KR0173546B1 - Electricity power saving paint containing nephrite powder - Google Patents

Abstract

The present invention is an epoxy resin alone having an epoxy group at both ends of a linear poly alcohol in which 1-5 mol of bisphenol and 2-6 mol of epichlorohydrin are ether-bonded. And a petroleum resin and an amino resin, to prepare a paint in which a nephrite powder is mixed with a known liquid epoxy resin paint or to a coating film of the known epoxy resin coating material, and to mixing the nephrite powder upon coating. As it is deposited, it has excellent power saving effect, and can improve water quality and heavy metal removal ability as a synergistic effect.

Description

Energy-saving paints containing jade powder

FIG. 1 is a diagram showing the purgatory powder crystal structure used in the paint of the present invention shown by a scanning electron microscope (SEM).

2 is a far-infrared emissivity measurement diagram of the FT-IR Spectrometer for purgatory powder of the present invention.

Figure 3a is a graph showing the effect of purgatory on the juice outflow when the pork is stored in the glass container containing the purgatory powder used in the present invention.

3b is a graph showing the effect of purgatory on the same pH.

3c is a graph showing the effect of purgatory on the VBH inclination.

3d is a graph showing the effect of purgatory on the TBA value.

Figure 3e is a graph showing the effect of purgatory on the color (delta E) of copper meat.

Figure 4a is a diagram showing the effect of purgatory on the plasma glucose in the diabetes mellitus test mice (rat) used in the present invention.

4b shows the effect of purgatory on hydroxybutyrate in the same plasma.

Figure 4c shows the effect of purgatory on free fatty acids in the same plasma.

Figure 4d is a diagram showing the effect of purgatory on cholesterol in the blood cholesterol.

Figure 4e shows the effect of purgatory on triglycerides in the same plasma.

Figure 4f shows the effect of purgatory on HDL-cholesterol in the same plasma.

Figure 5a is a diagram showing the effect of purgatory on the weight change of essential hypertension rats (SHR) of the nephrite tile used in the present invention.

Figure 5b is a diagram showing the effect of purgatory on the systolic blood pressure of the same SHR.

Figure 5c is a diagram showing the effect of purgatory on the blood pressure lowering action.

The present invention relates to a power saving paint made by containing fine powder of nephrite.

More specifically, the present invention relates to a fine powder of nephrite jadeite, which has a very fine structure of a hollow fiber of fine-grain granite-Yang-Yi-seok-based fibers, for example, a thermosetting acrylic resin coating material. , In the manufacture of paints containing amino acid resins, phenolic resins, especially epoxy resins, or the preparation of paints containing nephrite powders, or these paints on the interior and exterior surfaces of household appliances such as electric refrigerators, electric washing machines and vacuum cleaners. When coating, the nephrite powder is mixed and coated free of charge, so it is not only excellent in power saving effect, but especially in refrigerators, household goods having excellent effects such as impurities removal (heavy metal removal) and water quality improvement. It relates to power saving paint which made it possible to obtain.

As is well known, jade is roughly divided into jadeite and nephtite, and jadeite is a lead stone mineral belonging to the pyroxene family. Monoclinic system made of aluminum and soda. Hardness is a dense mass like crystal. Light is black, cyan and green, transparent or semi-transparent, usually called jade. Refers to this jadeite.

Nephthite is a monolithic ore mineral of Inosilicates, which is divided into purgatory and serpentine superbasic purgatory in high-quality surrogate. Its quality is determined by the fine structure of its hollow structure, that is, the granules of caterpillar-positive stone sperm, which are made of fastenings and fibers, and it is known that the thinner the fiber, the better the quality (Mining Promotion, 1993). Promotion Corporation).

According to a report published in the German medical literature (KRAFF der KRISTALLE und der EDELSTEINE by Mauda Palmer Die Verborgene), jadeite and jadeite are two different ores that contain silicon and oxygen like most gemstones, but jadeite is a granular crystal The jadeite is composed of a myriad of crystals and fine aggregates such as fiber and hair, while the jadeite has three minerals, namely calcium and magnesium, which are beneficial to the human body, unlike natrium and aluminum in jadeite. It has been reported to have a major effect on the healing of diseases caused by high blood pressure, diabetes, circulatory disorders, heart disease and kidney disorders when worn purgatory.

In Dongbobogam, a classic of oriental medicine, jade is added to Omiju and Jiyuju, and it turns into water, and it is good to eat when it is put in Hwangjangsu. When eaten in the same size as 배출 大), the waste is discharged to the outside of the body, 1 oxol 1 jijicho (地 楡 草), 1 bream (滔 米) 1, egret (白露) 3 Dori together and cooked in a copper bowl Okseol turns into water, and it is called oxal (玉液), so-called Shinseonokjang (神仙 玉 漿), and according to Sinnonboncho, Dangboncho, and the main herbaceous trees, If you take jade powder to make it enlightening, it will not only make the five intestines flesh clean and completely discharge the wastes in the body, but also remove the heat in the stomach, which is effective for the digestive system. Good for asthma, fever and stuffy chest It will quench your thirst, and if you wear sesame-like clothes, your body will fly and become lighter and longer, lubricating your lungs, helping your vocal cords nourish your throat, nourish your hair, and nourish your hair. It nourishes and changes the neurological disorders, especially during stress.In addition, when the muscles are tense and the rats fly, they can eat white jade powder as powder.When there are scar marks on the face and body, rubbing the wounds with purgatory for several days will eliminate the scars. The main ingredient of Eundeung Purgne has been known for its excellent effects on the human body with little side effects (Engbobom, Bon Cha).

Although purgatory has been known to have such excellent medical effects due to its scarcity, it has been limited to its use as some jewelry for jewelry, such as necklaces, rings, and bracelets. It is not economically disadvantaged to be able to work without skilled workers with oren experience because it requires careful attention, and it is economically disadvantageous, so there is almost no development as general household goods using purgatory. Therefore, its research and development is urgently required. At this point.

The present inventors pay attention to the excellent medical efficacy of purgatory as described above, and at the end of each decade of research experiments, each article such as electrical appliances, especially home appliances, purgatory stones, especially hollow granite in high-quality surrogate rock As a method of preparing and applying a paint containing jadeite powder, which is defined as butch σ ¹⁸ 0, or during the manufacturing process of an electrical appliance such as insulator, jadeite powder is added to the raw materials of these articles, and then mixed and In the case of molding, the electrical appliances and the home appliances coated with the jade powder containing paint have excellent power-saving effect, as well as synergistic effects such as water quality improvement and heavy metal removal in kitchen appliances. It was completed.

Therefore, the present invention is to provide a paint having excellent power saving effect, which can be widely used, such as household appliances such as kitchen appliances, automobiles, exterior appliances, electrical appliances, etc., by using the excellent effects of purgatory and purgatory as described above. There is a purpose.

Another object of the present invention is to maximize the use of jade powder treated with residues or wastes derived from mining or jewel processing of volatile jadeite with a specific composition.

Other objects and advantages of the invention will be apparent from the following specification, and will be apparent from the examples and experimental examples.

As a characteristic element of the present invention, a bisphenol 1-5 mol (mole) and epichlorohydrin (2-6 mol) is an ether-bonded linear polyalcohol with an epoxy group at both ends of the molecule. Prepare a paint obtained by mixing a jade powder with a known liquid epoxy resin paint by mixing a resin alone or / and a phenolic resin and an amizo resin, or by mixing a known epoxide coating material with a coating film and coating the jade powder upon coating. As it is deposited in (貿 狀), it has excellent power saving effect, and it is possible to express water quality improvement ability and heavy metal removal ability as a rising table.

As the paint in the present invention is a non-limiting meaning, the epoxy resin paint is a thermosetting acrylic resin paint made of epoxy resin as a crosslinking agent. Therefore, the paint according to the present invention may be used alone or in combination of amino resins and phenol resins in addition to the epoxy resin paint. Any of these can be applied as long as it is a thermosetting acrylic resin coating material having a blend of as a crosslinking agent.

In addition, the liquid epoxy resin is preferably a polymer epoxy resin having a large increase in the following formulas (1) and (2).

[Equation 1]

[Equation 2]

Where n = 1

In the present invention, the coating material to which the paint of the present invention is applied in the specification has been mentioned to focus on home appliances, but the paint of the present invention is not limited to home appliances, of course.

In the case of household appliances, electric appliances, electric refrigerators, electric washing machines, electric dehydrators, electric irons, electric stoves, electric furnaces, electric blankets, electric blankets, electric furnaces, electric ranges, electric toasters, electric furnace clay , Hair dryer, electric fan, luum courer, electric kettle, electric mixer, electric massager, electric shaver, electric barrican, messenger, electric iron, electric can opener, electric toothbrush, TV game set, electric cushion, electric coffee pot Applicable to electric foot warmer, humidifier, clothes dryer, electric refrigeration showcase, electric vending machine, electric frying pan, electric cooker, vacuum cleaner, electric mosquito collector, electric briquette gas discharger, automatic bowl washer, DC generator, AC Generator, DC Motor, AC Motor, Rotary Current Transformer, Rectifier, Transformer, Induction Voltage Regulator, Switchgear, Relay, Electric Switch, Circuit Breaker, Disconnector, Current Controller, Current Limiter, Resistance , Distribution of capacitors, Electrical appliances for control and electrical insulation insulator, Electrical insulation tube, Electrical insulation cloth, Electrical insulation paper, Electrical insulation rubber products, Electrical insulation mixture, Mica products for electrical insulation, Electrical machinery carbon, Insulation It can be applied to electrical materials of tapes. When the coating is used on the interior and exterior materials of T.V, the sharpness of the screen can be improved.

In addition, in vehicles, ships, and aircrafts, passenger cars, trucks, buses, trailers, tractors, ambulances, fire trucks, sprinklers, dump cars, forklift cars, race cars, hearse, amphibians, armored vehicles, tanks, and tricycles. , Wheel, motorcycle, sweeper, ladder truck, freezer, tank lorry, snowplow, armored vehicle, unmanned van, remicon truck, bulk car, excavator, payloader, bulldozer, grader, ferry, cargo ship, fishing vessel, tugboat, icebreaker Turbowoone, yacht cable laying boat, dredger, boat, canoe, lanch, sailboat, lifeboat, warship, propeller, mooring, signal ship for ship, drilling ship, tanker, container ship, amphibian, apparatus, airship, Glider, helicopter, auto gyro, airplane, rocket, spacecraft, satellite, steam locomotive, electric locomotive, internal combustion electric locomotive, internal combustion locomotive, storage battery, locomotive, tram, internal combustion car, passenger car, wagon, k Blocks can be applied.

The particle size of the jade powder mixed and used in the paint of the present invention is selected in consideration of the shape of the object to be coated, etc., generally, 100-350 mesh is suitable. When ductility needs to be increased, such as when the shape of the object is complicated or a thin item, it is more advantageous to use fine particles of 250-300 mesh, which are finer particles. It is mixed and used. If the grain size of the jade powder is larger than the above range, the surface roughness of the product becomes severe, which is not preferable, and finer particles than the above range are not preferable because it is difficult to grind.

In addition, when the nephrite powder is added to the paint prepared by mixing the nephrite powder or the freely dispersed paint, the addition amount thereof is appropriately 5-15%, and if the addition amount is less than 5%, the effect due to the nephrite addition cannot be expected. However, the higher the added amount of jade, the higher the inherent efficacy of the jade, but the higher the added amount, the lower the coating resin properties, especially adhesion, resulting in poor adherence and the higher price of the jade powder increases the paint price. 15% or less of the total weight of the raw material is appropriate.

Purgatory powder used in the paint of the present invention can be used to make products such as jewelry, bowls, sculptures and the like, and to crush the remaining residues, which is economically advantageous in terms of cost reduction, and in particular, various products with excellent power saving effect. It is highly economically evaluated in that it can be obtained.

In the present invention, the nephrite powder used as a composite material of the paint is defined as butch σ ¹⁸ 0 as a hollowstone in high-quality surrogate rock, and it is effective to have a composition ratio as shown in Table 1 below. Most preferred.

The effect shown in the manufacture of the paint to which the jade powder used for the coating of this invention was added, and the application of this coating is demonstrated in detail in the following Example.

EXAMPLE

1 mol of bisphenol and 2 mol of apichlor hydrin are ether-linked linear polyalcohols, in which 10-20 parts by weight of phenol resin is mixed with 80-90 parts by weight of an epoxy resin having epoxy groups at both ends of the molecule. 75-25 weight part of epoxy resin paints and 15-25 weight part of nephrite powder were stirred and mixed, and the liquid paint which concerns on this invention was obtained.

The spray coating was applied to the freezer compartment and the refrigerating compartment inside the electric refrigerator to measure the amount of heat consumed. As shown in Table 2, the power saving effect was about 25%.

Experimental Example 1

The following experiments tested the presence of lead, heavy metals and other toxic components of purgatory powder used as a mixture of paints in the Examples of the present invention (US FDA Registration No. 2022038, Bio-Science Research Institute. Inc)

ND = concentration is below detection limit or not detected

As shown in the above experimental results, purgatory powder used as a mixture of paints in the present invention was proved to be safe when used as a coating material for refrigerator interior since no harmful lead, heavy metal, or other toxic components were detected.

Experimental Example 2

In this experimental example, the test cup prepared by the purgatory powder of the present invention and the control cup (polyethylene) were filled with homogeneous Class A milk, and left for 48 hours at ambient temperature before the milk was analyzed. The results are shown in Table 6 below.

CONCLUSIONS: Reduction of harmful microorganisms.

Experimental Example 3

In this experiment, the anion content test for the jade purge impregnated cotton (duvet) used in the paint of the present invention was commissioned by the Korea Yarn Textile Testing Institute.

As a result, it can be seen that the anion generated beneficial to the human body as follows.

Test Item Test Result

(1) Ionchromatography: (ppm)

C1 54.8

NO Not detected

SO Not detected

Note) Extraction condition: Extraction for 2 hours in distilled water at room temperature.

(2) Antibacterial (KS K 0693): (Reduction rate of bacteria:%) 99.9

Note) Used strain: Staphylococcus aureus (ATCC 6538)

(3) Antibacterial (KS K 0692): (Segun Reservoir: mm) 4

Note) Used strain: Staphylococcus aureus (ATCC 6538)

Experimental Example 4

In this experiment, it was performed by requesting the Korea Food Research Institute to determine the effect on the freshness change over time when the pork is stored in the bowl (bowl) made of purgatory powder used in the embodiment of the present invention. The results of the research are described in detail below (leading evaluation of pork stored in purgatory containers: Korea Food Research Institute).

Pork was stored in purgatory and general (control). The storage temperature was 0 ℃ and 4 ℃, it was stored for 0, 4, 7, 14, 21 days. The ham portion of pork cut about 100g and stored, while the loss (Drip loss), meat color (Meat color), pH, volatile basic nitrogen (VBN; protein decay). Fatty acidity (TBA) was measured. The measurement results are shown in Table 7 below.

(A) of FIG. 3 shows the effect of the purgatory container on the drip loss (%) when the pork is stored at 0 ° C. or 4 ° C. for 21 days. Shows the effect of the purgatory container on the change of pH when stored for 21 days at 0 ℃ or 4 ℃, Figure 3 (c) shows the VBN content when pork is stored at 0 ℃ or 4 ℃ 21 days Figure 3 shows the effect of the purgatory container, and Figure 3 (d) shows the effect of the purgatory container on the TBA content when the pork is stored at 0 ° C or 4 ° C for 21 days. ) Shows the effect of the purgatory container on the change of meat color when pork is stored at 0 ° C or 4 ° C for 21 days.

As shown in the above results, the juicy outflow rate of pork stored in the purgatory tablets was much lower than that of the control group, and especially, as the storage period elapsed, the juicy outflow amount was decreased in the purgatory tablet regardless of the storage temperature. The pH as an important index of post-mortem change in muscles remained high at 6.5-6.8 after a slight drop in pH at first, following livestock. In this leading assessment, the pH at 4 ° C was higher than at 0 ° C, but there was no significant difference. It was not found and there was no direct effect on the VBN value indicating protein deterioration. However, the TBA values indicating fatty acid plaques were kept low at the jade purge regardless of the storage temperature. Meat color is caused by pigments in meat absorbing light of a certain wavelength and reflecting light of other wavelengths. In this test, the ΔE value measured by a color difference meter is 0 ° C. Control) was lower than that of purgatory, and 4 ° C was slightly higher in ΔE than 0 ° C, but there was no tendency. This is because the dehydration drying of the meat surface becomes black when stored at 4 ° C. rather than 0 ° C. to increase the pigment concentration, thereby promoting the formation of metmyoglobin.

To summarize the results of the experiment, when oxalic powder as well as jade powder is coated on packaging materials such as vinyl and coagulated for food storage, hygiene and quality are preserved in the distribution of highly perishable foods, thus prolonging shelf life and safety. It is sure to be able to increase.

Experimental Example 5

In the present experimental example, an infrared experiment was performed on the jade dust used in the present invention (Fig. 2).

Note: The result of black body comparison using FT-IR Spectrometer (Korea Institute of Construction Materials).

Experimental Example 6

In this Experimental Example, experiments were conducted on chemical and biological oxygen demand of the oxidized samples of the present invention (US F.D.A accredited laboratory).

Experimental Example 7

In this experimental example, the effect on the taste and related properties when the coffee was put into the jade mug (jade mug) prepared by the purgatory powder used in the present invention was investigated. The experiment was conducted jointly by the Department of Food and Nutrition, Chung-Ang University and Korea Food Research Institute. The details are described below.

1 test purpose

The purpose of this study was to examine the effects of drinking coffee on purgatory and plain mugs on the variables such as taste, aroma, aftertaste and color of coffee.

2 Sensory test method: Paired Preference Test

Using a method that selects another sample that is more preferred for one sample.

-Evaluation Items: Taste, Flavor, Aftertaste, Color

3 sensory inspector

-20-25 students in 4th grade, Department of Food and Nutrition, Chung-Ang University (Experienced sensory tests)

4 Sensory test period

-March 1996 to June

-Once a week

-A total of 10 times

5 Test containers and tasting materials

-Purgatory mug and general mug: Appearance was same.

Types of drink: Instant Coffee (Taster's Choice)

6 Sample Preparation

-Prepare 1 teaspoon of coffee in each cup and add 1/2 cup boiled water to 100 ℃

7 Statistical Processing:

T-test (p≤0.05)

[result]

1. Taste: Coffee taste in purgatory cups was much milder than coffee in regular cups (p≤0.05).

2. Color and aftertaste: Coffee color and aftertaste of purgatory glass are preferred, but there is no statistical benefit.

3. Fragrance: Common cup coffee was better than purgatory cup, but there was no statistical significance.

The figure below shows the effect of the nephrite cup on the sensory properties of coffee.

[conclusion]

Purgatory cups were found to have a milder taste, which was statistically significant. On the other hand, aftertaste and color tended to be similar or better than regular cups, but there was no statistical benefit, and coffee flavors were better. However, no statistical significance was observed.

Experimental Example 8

In this experimental example, the experiment was commissioned by the Korea Food Research Institute to determine the effect on the breeding and growth rate of rats when treated with chalcedony-containing tiles and chalcedony powder. Details are as follows.

Nine-week-old Sprague Dawley rats were prepared for 30 males and females. The rats of group A were allowed to drink tap water in the cage with purgatory tiles, and the rats of group B were allowed to drink the supernatant after dipping the purgatory powder (2 mg / ml tap water), but did not leave the purp tile. Group C was used as a control without jade tiles or corn. All treatments were seeded for 9 days and males were isolated and slaughtered for sperm seedling and vitality tests. The results are shown in Table 10 below.

Experimental results showed better results in purgatory tile (Group A) and Agate (Group B) treatments than the control group. The powder rate was 90% in the A and B treatment groups and 80% in the C treatment group, and the number of pups was 3-8 in the A and B treatment groups, although there were 6-8 more in the control group. More. The days to postpartum delivery were significantly shorter in the A treatment group.

In addition, sperm concentration and sperm vitality were excellent in group A treated with octagonal tiles. However, the effect of simultaneous treatment with purgatory tile and corn was not studied in this experiment.

In conclusion, the results of the fertilization suggest that purgatory tiles and agate affect rats' reproduction and growth: Purgatory tiles and agate treatment groups showed better reproduction and growth indices. The results are also valuable as a basis for improving fertility and enhancing sperm concentration and motility.

Experimental Example 9

This experiment was performed by the Korea Food Research Institute to investigate the effects of various purgatory products on the symptoms of streptozotoin-induced diabetes in rats. Details are as follows (abcdef in Figure 4).

32 spragdogly rats, weighing 252-292 grams, induced diabetes mellitus intraperitoneally with ST (streptozotocin) (35-40 mg / kg body weight dissolved in 0.1 M citric acid in pH 4.0) . Seven days after ST administration, using only europaper (Eiken Chemical Co. Ltd., Japan), only rats with a urine glucose of 25 mg / dI or more were selected and placed in 5 water groups per 50 days. Animals in group A were intraperitoneally injected with 1.0 ml of oxalate solution (pH 6.40) daily. Group B was raised in a cage with purgatory tiles on the floor. Group C was fed daily with supernatant of maize as a negative water after precipitation of the gemstone powder, Group D was administered only ST as a control.

Experimental feed was fed commercially available feed, the breeding method was in accordance with the usual practice. Mice were sacrificed at the end of the experiment (50 days) and blood was collected from the abdominal aorta. Blood was left at room temperature for 30 minutes and then centrifuged at 5,000 rpm for 15 minutes to obtain plasma. The weights of organs, such as isolated liver and kidneys, were weighed and recorded. On-site plasma β-hydroxybutyrate (HBA), free fatty acids (FFA), cholesterol, HDL-cholesterol and triglycerides were measured. HBA inclusion was quantified by measuring the absorbance (OD) increase at 340 nm of NADH produced by the oxidation reaction with β-hydroxybutyrate dehydrogenase, and blood lipid was measured in a clinical laboratory kit (Eiken Chemical co., Ltd., Japan). ).

s0.05

^a β-hydroxybutyrate (ketone body)

^b free fatty acid

^c total cholesterol

^d triglycerides (neutral lipids)

^e high density lipoprotein cholesterol

Body weight was increased in corn group C, but decreased or maintained in other groups (B, D). (A) In diabetic rats, hypertrophy of the kidneys is known to be common. Kidney weight of group C was the smallest among treatment groups except control group. Hepatomegaly was also seen due to diabetes, but liver weight was the lowest in rats fed corn. The concentrations of blood glucose, ketone bodies and FFA were highest in the order of A, B, C, and D treatment groups. Plasma cholesterol and triglyceride concentrations showed the same trend (ABCD). From the above results, the rats fed the corn (group C) showed relatively lower values of all the indexes than the other two experimental groups, and the blood cholesterol and FFA concentrations showed lower values than the control group without the nephrite treatment.

Blood cholesterol and TCG concentrations were generally higher in the order of A, B, C, and D treatment groups. When the glycemic index is determined by the post-prandial blood glucose response, the experimental results may vary depending on the researcher.However, in this experiment, a commercially available complete formula (TMR) was obtained without considering the glycemic index of cereals in the experimental feed. Even though it was fed, the treatment group (a group C) fed agate improved the hyperlipidemia, one of the symptoms of diabetes. HDL-cholesterol content did not differ between treatment groups.

In conclusion, supplementation of agate with streptozotocin-induced diabetic rats prevented weight loss, prevented hypertrophy of the kidneys and liver, and improved hyperlipidemia, a type of diabetes.

Experimental Example 10

This experiment was commissioned by the Korea Food Research Institute to investigate the effect of bedding (bedding), a nephrite product, on the blood pressure of spontaneous hypertensive rats.

Details are as follows.

Twelve male SHRs, 8 weeks old, were prepared. The experiments were arranged in six groups, each of which was treated as two treatment groups of jade treatment group (A) and control group (B) treated with bedding. Group A lays bedding on the floor of the cage, while Group B lays out the traditional wooden litter. The experimental feed was fed the Extrusion blended feed of Samyang Oil Feed Co., Ltd., and the conditions for raising such as daylighting were in accordance with the general breeding method. The experiment was conducted for a total of five weeks, including one week of adaptation in the measuring holder for blood pressure measurement. Body weight and blood pressure were measured at weekly intervals during the test period. The blood pressure was placed in the rat holder and stabilized for 10 minutes in a silver tube, which was adjusted to 29 ± 1 ° C., and then from the unveined vein to the non-vascular sphygmomanometer (IITC Inc.). , Woodland Hills, California). Changes in blood pressure were applied to this test using the criteria commonly used in clinical trials.

Changes in body weight of SHR mice during the test period tended to increase over time as shown in (a) of FIG. 5, and the average growth rate was 1.43 ± 1.04g in group A and 1.50 ± 0.27g in group B, and there was no significant difference between treatment groups. . In general, the growth rate of SHR is known to be lower than that of normal rats.

Table 13 below shows weekly changes in cardiac contractile blood pressure (mmHg) of SHR treated with jade products.

Systolic blood pressure of group A treated with nephrite products showed a tendency to decrease with time as shown in Table 13 and FIG. 5 (b), and the measured value of 202.6 mmHg at baseline decreased about 10 mmHg at 1 week after the test. It was. From the 3rd week of testing, 187mmHg was maintained without significant change, and the dropping effect was about 16mmHg compared to the start of the test. This decrease is considered to be a significant change as a result far exceeding the determination of blood pressure change in clinical trials, 10 mmHg. On the other hand, systolic blood pressure of the control group B was increased from about 200mmHg at baseline to the first half of the test, and then increased to 213mmHg, and then slightly decreased until the second half of the test, which was somewhat stable as about 209mmHg at the fourth week of the test. In (c) of FIG. 5, in the group A, blood pressure was significantly decreased in the first half of the test (-10.5 mmHg), while in the group B, the blood pressure was increased in the first half (+13.4 mmHg), and in the second half of the test, both treatment groups decreased slightly. (-4.6, -4.5 mmHg) tended.

As in the experimental examples described above, the purgatory powder used in the paint of the present invention is, firstly, in the freshness evaluation test of pork, the drip loss in the purgatory container irrespective of the storage temperature as the storage period elapses. Much lower than in normal containers. Protein variability (VBN) and fatty acid opacity (TBA 覇) were also generally low in jade tablets.

Second, in the sensory evaluation related to the taste, purgatory coffee mug was statistically significantly verified to have a milder taste than coffee (p0.05).

Third, as a result of evaluating the effect on the reproductive ability by treating the nephrite product in SD rats, the results of labor, sperm concentration, and sperm vitality (sperm concentration) motility was higher than general breeding (control).

Fourth, in the experiment of diabetic relaxation effect in rats that induced experimental diabetes by administration of Streptozotcin (ST), blood lipid level was better in corn feeding group than other treatment groups, which improved hyperlipidemia of purgatory products. May have been suggested.

Fifth, in the experiment to investigate the effect of nephrite products on blood pressure, the systolic blood pressure was measured while breeding the high-strength hypertensive rat (SHR) in the bedding of the jade tablets, which showed a significant blood pressure-lowering effect. That is, it was confirmed that systolic blood pressure dropped about 16 mmHg in the bedding treatment of the purgatory agent compared to the start of the test.

In particular, it was confirmed that there is an excellent power saving effect when mixed with the paint as shown in Table 2 of the Examples.

Claims (3)

A well-known liquid epoxy resin obtained by combining an epoxy resin having an epoxy group alone or / and a phenol resin and an amizo resin in a linear polyalcohol in which 1-5 mol of bisphenol and 2-6 mol of apichlor hydrin are ether-bonded. An energy-saving paint containing jade powder, characterized in that it is applied by stirring and mixing 15-25 parts by weight of 150-300 mesh jade powder into 75-85 parts by weight. According to claim 1, Epoxy resin coating material 75-85 parts by weight 15-25 parts by weight of 150-300 mesh nephrite powder immediately before the coating of the coating material, characterized in that the spray coating by spray mixing by stirring. The power saving chart according to claim 1 or 2, wherein the workpiece is a household appliance, an electrical appliance, or a transportation machine appliance.