JPS63295738A - Fabric having embossed pattern - Google Patents
Fabric having embossed patternInfo
- Publication number
- JPS63295738A JPS63295738A JP62129660A JP12966087A JPS63295738A JP S63295738 A JPS63295738 A JP S63295738A JP 62129660 A JP62129660 A JP 62129660A JP 12966087 A JP12966087 A JP 12966087A JP S63295738 A JPS63295738 A JP S63295738A
- Authority
- JP
- Japan
- Prior art keywords
- woven
- fabric
- knitted fabric
- embossed pattern
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、エンボス模様付き織編物に関し、詳しくは、
しわ模様が立体的に見えるエンボス模様付き織編物に関
する。[Detailed Description of the Invention] [Industrial Application Field] The present invention relates to a woven or knitted fabric with an embossed pattern, and in detail,
This invention relates to a woven or knitted fabric with an embossed pattern that makes the wrinkle pattern look three-dimensional.
従来のエンボス模様付き織編物は、織編物を拡布して加
熱エンボス型ローラと弾性ローラの挟圧の間に通すこと
により得られるものであり、表面に一様にエンボス模様
を有するようなものであった。Conventional woven or knitted fabrics with embossed patterns are obtained by spreading a woven or knitted fabric and passing it between a heated embossing roller and an elastic roller, and the fabric has an embossed pattern uniformly on its surface. there were.
本発明者らは、織編物を折れ重なり部分が多数分布して
生ずるような状態で加熱エンボス型ローラと弾性ローラ
の挟圧の間に通すと、表面にしわ線模様とエンボス模様
とを有し、しわ模様がエンボス模様によって立体的に見
えるようになる織編物が得ら共ることを見出した。The present inventors have discovered that when a woven or knitted fabric is passed between a heated embossing roller and an elastic roller in a state where a large number of folded parts are distributed, the fabric has a wrinkle line pattern and an embossed pattern on the surface. It was discovered that woven or knitted fabrics with wrinkled patterns that appear three-dimensional due to the embossed patterns can be obtained.
本発明は、上述の知見に基いてなされたものであり、表
面にしわ線模様とエンボス模様とを有して、しわ模様が
立体′的に見えるエンボス模様付きｉｉ物の提供を目的
とする。The present invention has been made based on the above-mentioned findings, and aims to provide a product with an embossed pattern, which has a wrinkle line pattern and an embossed pattern on the surface, so that the wrinkled pattern appears three-dimensional.
本発明は、表面にしわ線模様と、しわ線の片側のしわ線
に沿った比較的狭い幅部分を除いてエンボス模様とを有
することを特徴とするエンボス模様付き織編物にあり、
この構成によって前記目的を達成する。The present invention resides in a woven or knitted fabric with an embossed pattern, characterized in that it has a wrinkle line pattern on the surface and an embossed pattern except for a relatively narrow width part along the wrinkle line on one side of the wrinkle line,
This configuration achieves the above object.
本発明のエンボス模様付き織編物には、熱可塑性合成繊
維から成る糸を用いた！ｔｉｉ物が耐久性に優れたしわ
線模様やエンボス模様を付与できるので好ましく用いら
れる。また、表面が凹凸になるふくれ織編物、タンク織
編物、しぼ織編物あるいはプリーツ加工やしわ加工を施
した織編物が、本発明のエンボス模様付き織編物を比較
的容易に得ることができるので、好ましく用いられる。The embossed patterned woven or knitted fabric of the present invention uses threads made of thermoplastic synthetic fibers! tii products are preferably used because they can provide wrinkle line patterns and embossed patterns with excellent durability. In addition, the embossed patterned woven or knitted fabric of the present invention can be obtained relatively easily from a bulge-woven fabric, a tank-woven fabric, a wrinkled-knitted fabric, or a pleated or wrinkled woven fabric that has an uneven surface. Preferably used.
これに対し、通常のプレーンな織編物から本発明のエン
ボス模様付き織編物を得ようとした場合は、加熱エンボ
ス型ローラと弾性ローラの挟圧の間に織編物を折れ重な
り部分が多数分布して生ずるように通すために、特別の
幅寄せ手段やオーバフィード手段等を必要とする。On the other hand, when attempting to obtain a woven or knitted fabric with an embossed pattern according to the present invention from a normal plain woven or knitted fabric, the woven or knitted fabric has many folded and overlapping parts between the pressure of the heated embossing type roller and the elastic roller. In order to allow the material to pass through in such a way as to occur, a special width adjustment means, overfeed means, etc. are required.
ふくれ織編物は、織物ではふくれの二重部分が共に経、
！ＩＩ糸の組織から成るものが、ふくれの浮きや織物の
耐久性等の点から好ましいが、二重部分の一方の張り部
分が緯糸あるいは経糸のみから成るものでもよい、また
、編物ではブリスター組織をベースにしたダブルニット
によるふくれ編物が好ましい。しぼ織編物は、織物では
揚柳しぼ織物の方が縮緬しぼ織物よりも一般にしぼが深
（て大きいので、本発明の効果に優れたエンボス模様付
き織物を得易＜、編物では緯糸挿入による経編物で緯糸
に片強撚糸を用いたクインズコード組織のものが好まし
い、プリーツ加工は、金属加熱ローラとフェルトベルト
のずれ回動の間に織編物を通すようにしたプリーツ機を
用いる方法、あるいは織編物を型付は紙で挟んで型付は
紙と共に折り畳み加熱セットする方法等、従来公知のプ
リーツ加工法によって行うことができる。また、しわ加
工は、織編物をローブ状に絞って鎖編にし、鎖編を網袋
等の袋に詰めて、その袋をワッシャー機等で加熱する鎖
編法、織編物を幅狭く絞ってビームに巻取り、そのビー
ムを蒸熱缶で加熱する幅寄せ 法、織編物をローブ状に
して撚掛けしたものをビームに巻取り、そのビームを蒸
熱缶で加熱する撚掛は法、織編物の幅を絞って細長い網
袋等に押し込み、その袋を蒸熱缶やワッシャー機等で加
熱する詰め込み法等の従来公知のしわ加工法で行うこと
ができる。In woven fabrics, the double parts of the bulges are warped,
! A structure made of II yarn is preferable from the viewpoint of lifting the bulge and durability of the fabric, but one tension part of the double part may be made of only the weft or warp. A puffy knit fabric based on double knit is preferred. As for the wrinkled knitted fabric, since the wrinkles of the willow-grained fabric are generally deeper and larger than the crepe-grained fabric, it is easier to obtain a fabric with an embossed pattern that is excellent in the effect of the present invention. A warp-knitted fabric with a queen's cord structure using one-sidedly twisted yarns for the weft is preferable.The pleating process is performed by using a pleating machine in which the woven or knitted fabric is passed between a metal heating roller and a felt belt that are rotated in an offset manner, or The woven or knitted fabric can be formed using a conventional pleating method, such as sandwiching the woven or knitted fabric between paper sheets, folding the woven or knitted fabric together with the paper, and heating and setting the woven or knitted fabric.Wrinkle processing can also be done by squeezing the woven or knitted fabric into a lobe shape and chain stitching. Chain stitch method, in which the chain stitch is packed into a net bag or other bag, and the bag is heated with a washer machine, etc., and the width-aligning method, in which the woven or knitted fabric is squeezed narrowly and wound into a beam, and the beam is heated in a steamer can. The twisting method involves twisting the woven or knitted fabric into a lobe and winding it around a beam, and then heating the beam in a steam can.The twisting method involves squeezing the width of the woven or knit fabric into a long, thin net bag, etc., and then heating the beam in a steam can. This can be done by a conventionally known wrinkle processing method such as a heating method using a washer machine or the like.
第１図は、ふくれ織編物、あるいはプリーツの屈曲形状
が完全には伸ばされない状態でプリーツ加工織編物を、
加熱エンボス型ローラと弾性ローラの挟圧の間に通して
得られる、本発明エンボス模様付き織編物の表面模様を
模式的に示した部分平面図であり、第２図は、しわ加工
織編物あるいは揚柳しぼｔａ＆Ｉ物をしわやしぼが完全
には伸ばされない状態で加熱エンボス型ローラと弾性ロ
ーラの挟圧の間に通して得られる、本発明エンボス模様
付き織編物の表面模様を模式的に示した部分平面図であ
る。Figure 1 shows a pleated woven or knitted fabric, or a pleated woven or knitted fabric with the bent shape of the pleats not fully stretched.
FIG. 2 is a partial plan view schematically showing the surface pattern of a woven or knitted fabric with an embossed pattern of the present invention, which is obtained by passing between a heated embossing type roller and an elastic roller, and FIG. Schematic representation of the surface pattern of the woven and knitted fabric with embossed patterns of the present invention obtained by passing the Yanagi grained ta&I material between the pressure of a heated embossing type roller and an elastic roller in a state where the wrinkles and grains are not completely smoothed out. FIG.
図において、１はしわ線、斜影を施した部分２はエンボ
ス模様を賦形されたエンボス模様部分、３はしわ線ｌの
片側のしわ線に沿ったエンボス模様を賦形されていない
エンボス模様後は部分である。このエンボス模様後は部
分３は、加熱エンボス型ローラと弾性ローラの挟圧の間
をｖａ編物が通過する際に発生した折れ重なり部分の直
接加熱エンボス型ローラに押されることがなくなった部
分であり、この部分には他の部分と比較して例えば揚柳
しぼがよく残るようになる。このように、エンボス模様
後は部分３がしわ線１の片側でしわ線ｌに沿って比較的
狭い幅に生じ、しかも、しわ線１の反対側のしわ線１に
沿う部分には、折れ重なりによって加熱エンボス型ロー
ラが強く働いて、エンボス模様が特に明確に付くように
なるから、それによりしわ模様が立体的に見えるように
なる。In the figure, 1 is the wrinkle line, the shaded area 2 is the embossed pattern area where the embossed pattern has been formed, and 3 is the embossed pattern area where the embossed pattern is not formed along the wrinkle line on one side of the wrinkle line l. is a part. After this embossed pattern, part 3 is the folded part that occurs when the VA knitted fabric passes between the heating embossment roller and the elastic roller, and is no longer directly pressed by the heating embossment roller. , for example, the willow grain remains more often in this part than in other parts. In this way, after the embossed pattern, part 3 is formed in a relatively narrow width along the wrinkle line l on one side of the wrinkle line 1, and moreover, there are folds and overlaps in the part along the wrinkle line 1 on the opposite side of the wrinkle line 1. As a result, the heated embossing type roller works strongly and the embossed pattern becomes particularly clear, making the wrinkled pattern appear three-dimensional.
このためにも、加熱エンボス型ローラは、ブレーンな織
編物には全面的にエンボス模様を付けるようなものであ
ることが好ましい。そして、これに対する弾性ローラは
、圧接点で加熱エンボスローラの凹凸面に密着し、圧接
点を離れたら一周の間で平滑な面に復する弾性表面を有
するものであればよく、−周しても表面にエンボス模様
が残るようでは明確なエンボス模様を付けることができ
なくなる。For this reason as well, it is preferable that the heated embossing type roller is one that can apply an embossed pattern to the entire surface of a plain woven or knitted fabric. The elastic roller for this need only have an elastic surface that comes into close contact with the uneven surface of the heating embossing roller at the pressure contact point and returns to a smooth surface within one rotation after leaving the pressure contact point. However, if the embossed pattern remains on the surface, it will not be possible to form a clear embossed pattern.
以下、本発明の実施例について説明する。 Examples of the present invention will be described below.
実施例１゜
Ｓ 撚ｉｏｏ ７７ｍのポリエステルフィラメント糸ブ
ライ）１００ ｄｅ／７２ｆｉｌを表の経、緯糸に用い
、ポリエステルフィラメント糸セミダル７５ｄｅ／３６
ｆｉｌの仮撚加工糸にそれぞれＳ撚２７００Ｔ／ｍと
Ｚ撚２７００Ｔ／ｍを加えた糸を裏の経、緯糸に用いて
、ふくれ１３４ ａｍ）を１０分間沸点に近い熱水に浸
すボイルオフの予備リラックス処理した後、液流染色機
により１１０℃の熱水でリラックス処理した。これによ
ってふくれが発現した織物（幅１１０ ｃｉＩＩ）を１
５０℃。Example 1゜S polyester filament yarn with a twist of 77 m (Brain) 100 de/72 fil was used for the front warp and weft, and polyester filament yarn semi-dull 75 de/36
Preparation for boil-off by soaking 134 am) in hot water close to the boiling point for 10 minutes using the false twisted yarn of fil with 2700 T/m of S twist and 2700 T/m of Z twist for the back warp and weft. After the relaxation treatment, a relaxing treatment was performed using hot water at 110° C. using a jet dyeing machine. The woven fabric (width 110 cII) that has developed blisters as a result of this
50℃.
１５ｓｅｃの条件でテンターに通して仮セット（幅１１
３０）シた後、１５Ｔｏｎの圧力で弾性ローラに押し付
けられる１８０℃の加熱エンボス型ローラに通してエン
ボス模様の賦形を行った。この織物（幅１１３ｃｍ）を
１８０℃、 ２０ｓｅｃの条件でブリセント（幅１１２
ｃＩＩ＋）シ、１０５℃のアルカリ浴を用いて１５％減
量させる処理を行い、１３０℃で染色した後、１７０℃
。Tentatively set by passing it through a tenter under the condition of 15 seconds (width 11
30) After the printing, an embossed pattern was formed by passing it through a 180° C. heated embossing roller that was pressed against an elastic roller with a pressure of 15 tons. This fabric (width 113cm) was heated to Briscent (width 112cm) at 180℃ for 20 seconds.
cII+), treated to reduce weight by 15% using an alkaline bath at 105°C, dyed at 130°C, and then dyed at 170°C.
.
２０ｓｅｃの条件でファイナルセット（幅１１３ （Ｊ
）を行った。Final set (width 113 (J
) was carried out.
得られた織物は、表面に第１図に示したようなしわ線模
様としわ線の片側のしわ線に沿った比較的狭い幅部分を
除いたエンボス模様とを有して、しわ模様がエンボス模
様によって立体的に見え、しわ線模様もエンボス模様も
、Ｊ ｌ５−Ｌ−１０４２Ｇ法の洗濯試験で、ランドリ
ー５回では殆ど変わらないと言う優れた耐久性を示した
。The obtained fabric has a wrinkle line pattern on the surface as shown in FIG. The pattern gives a three-dimensional appearance, and both the wrinkle line pattern and the embossed pattern showed excellent durability in a washing test using the J15-L-1042G method, with almost no change after washing five times.
実施例２゜
経糸にＳ 撚３００７７ｍのポリエステルフィラメント
糸ブライト５０ｄｅ／３６ｆｉｌを用い、緯糸にＳ撚３
０００Ｔ／ｍのポリエステルフィラメント糸セミダル５
０ｄｅ／２４ ｆｉｌを用いて、平織物を製織した。こ
の生機（幅１３６ｃｍ）を液流染色機により１１０℃で
リラックス処理して、揚柳しぼ織物（幅８０ｃｍ＋）を
イ静にた。Example 2゜ Polyester filament yarn Bright 50de/36fil with S twist of 30077 m was used for the warp, and S twist of 3 was used for the weft.
000T/m polyester filament yarn semi-dull 5
A plain woven fabric was woven using 0de/24 fil. This gray fabric (width 136 cm) was subjected to a relaxing treatment at 110° C. using a jet dyeing machine, and a Yanagi grained fabric (width 80 cm+) was made into a relaxed state.
このしぼ織物を８０ｃｍの幅で実施例１と同じ条件の加
熱エンボス型ローラに通した後、幅８０ｃｍで実施例１
と同様プリセットを行い、さらに１５％のアルカリ減量
処理を行った。このアルカリ減量処理において織物幅は
９０口となった。この織物を１３０℃で染色し、幅９０
ｃ１１で実施例１と同じ条件でファイナルセットを行っ
た。This embossed fabric was passed through a heated embossing roller under the same conditions as in Example 1 with a width of 80 cm, and then with a width of 80 cm in Example 1.
Presetting was performed in the same manner as above, and further alkali weight reduction treatment was performed by 15%. In this alkali weight loss treatment, the fabric width became 90 openings. This fabric was dyed at 130℃ and the width was 90℃.
At c11, a final set was performed under the same conditions as in Example 1.
得られた織物は、表面に第２図に示したのとはり同様の
しわ線模様とエンボス模様とを有して、しわ模様が立体
的に見え、しわ線模様やエンボス模様の耐久性が実施例
１と同様に優れていた。なお、この織物の場合、しわ線
の片側のエンボス模様が抜けている部分でしぼの凹凸が
比較的よく残った。The obtained fabric has a wrinkle line pattern and an embossed pattern on the surface similar to those shown in Figure 2, the wrinkle pattern appears three-dimensional, and the durability of the wrinkle line pattern and embossed pattern is improved. Excellent as in Example 1. In addition, in the case of this fabric, the unevenness of the wrinkles remained relatively well in the part where the embossed pattern was missing on one side of the wrinkle line.
実施例３゜
経、緯糸にポリエステルフィラメント糸ブライト６０ｄ
ｅ／３６ ｆｉｔ 、 Ｓ撚３００７７ｍを用いた平
織物の幅１２４ ｃｍの生機を鎖編法でワッシャー機の
熱水による加熱温度を１２０℃としてしわ加工し、開度
した織物を幅９０Ｃ１ｍで実施例１と同じ条件の加熱エ
ンボス型ローラに通してエンボス加工を行い、得られた
織物を幅９０ＣＩ１１で実施例１と同じ条件によりプリ
セントし、さらに８％のアルカリＦ２世処理と１３０℃
の高圧染色処理とを行った後、幅１００ ｃｍで実施例
１と同じ条件によりファイナルセットを行った。Example 3: Polyester filament yarn bright 60d for warp and weft
Example: e/36 fit, S-twist 30077m plain woven gray fabric with a width of 124 cm was wrinkled using the chain knitting method using hot water in a washer machine at a heating temperature of 120°C, and the opened fabric was 90C1m wide. Embossing was carried out by passing it through a heated embossing roller under the same conditions as in Example 1, and the resulting fabric was prescented with a width of 90CI11 under the same conditions as in Example 1, and further treated with 8% alkali F2 and 130°C.
After high-pressure dyeing treatment, final setting was performed under the same conditions as in Example 1 with a width of 100 cm.
得られた織物は、表面に第２図に示したようなしわ線模
様とエンボス模様とを有し、実施例１で得られた織物と
同様、しわ模様が立体的に見えて、しわ線模様とエンボ
ス模様の耐久性が優れるものであった。The obtained woven fabric has a wrinkle line pattern and an embossed pattern on the surface as shown in FIG. The durability of the embossed pattern was excellent.
本発明の織編物は、しわ模様がエンボス模様によって立
体的に見えると言う効果を奏し、また、しわ付けやエン
ボス加工における加熱強度よりも高い温度の加熱があと
から行われているものでは、しわ線模様とエンボス模様
の耐久性も優れる。The woven or knitted fabric of the present invention has the effect that the wrinkle pattern looks three-dimensional due to the embossed pattern, and if the fabric is subsequently heated at a temperature higher than the heating intensity during the wrinkle forming or embossing process, the wrinkle pattern will appear three-dimensionally. The durability of line patterns and embossed patterns is also excellent.
第１図および第２図は、それぞれ本発明エンボス模様付
き織編物の表面模様を模式的に示した部分平面図である
。
１・・・しわ線、 ２・・・エンボス模様部分、
３・・・エンボス模様後は部分。
１８開口Ｕ６３−２９５７３８ （４）第 ｆ 図
マ
第ｚ図FIGS. 1 and 2 are partial plan views schematically showing the surface patterns of the embossed woven or knitted fabric of the present invention, respectively. 1...Wrinkle line, 2...Embossed pattern part,
3... After the embossed pattern is the part. 18 opening U63-295738 (4) Figure f Figure Z
Claims (4)
った比較的狭い幅部分を除いてエンボス模様とを有する
ことを特徴とするエンボス模様付き織編物。(1) A woven or knitted fabric with an embossed pattern, characterized by having a wrinkle line pattern on the surface and an embossed pattern except for a relatively narrow width part along the wrinkle line on one side of the wrinkle line.
のエンボス模様付き織編物。(2) A woven or knitted fabric with an embossed pattern according to claim 1, which comprises a puffy woven or knitted fabric.
載のエンボス模様付き織編物。(3) A woven or knitted fabric with an embossed pattern according to claim 1, which is made of a woven or knitted fabric made of Yanagi grain.
囲第１項記載のエンボス模様付き織編物。(4) The embossed patterned woven or knitted fabric according to claim 1, wherein the constituent threads are made of thermoplastic synthetic fibers.