JPS63248380A - Radical catching agent for tobacco smoke - Google Patents
Radical catching agent for tobacco smokeInfo
- Publication number
- JPS63248380A JPS63248380A JP8286387A JP8286387A JPS63248380A JP S63248380 A JPS63248380 A JP S63248380A JP 8286387 A JP8286387 A JP 8286387A JP 8286387 A JP8286387 A JP 8286387A JP S63248380 A JPS63248380 A JP S63248380A
- Authority
- JP
- Japan
- Prior art keywords
- activated carbon
- zeolite
- filter
- present
- radical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】 皇呈上辺肌ユ分互 本発明は、煙草連用ラジカル捕捉剤に関する。[Detailed description of the invention] Emperor's upper side skin Yu division The present invention relates to a radical scavenger for continuous use in cigarettes.
更に詳しくは、ゼオライトと活性炭とからなるラジカル
捕捉剤およびこれらを用いた煙草用フィルターに関する
。More specifically, the present invention relates to a radical scavenger made of zeolite and activated carbon, and a cigarette filter using these.
皿米二孜土
煙草の喫煙が人体に有害であることは、たとえば、喫煙
量と癌発生率等の多くの統計的な報告から、間接的に証
明されている。しかし、その有害性の真の原因について
はまだ明らかにされていない。It has been indirectly proven that smoking cigarettes is harmful to the human body, for example, from many statistical reports on the amount of tobacco smoked and the incidence of cancer. However, the true cause of its toxicity has not yet been clarified.
今までは、喫煙の有害性を軽減するために煙草の煙の中
に含まれる有害物質の除去を目的としたフィルターが数
多く製造され、市販されている。Until now, many filters have been manufactured and commercially available for the purpose of removing harmful substances contained in cigarette smoke in order to reduce the harmful effects of smoking.
たとえば、アセテートフィルターのようにタールやニコ
チン等の粒状物質の除去を目的としたフィルター、ある
いは、活性炭のようにアセトアルデヒド、シアン化水素
等のガス状物質の除去を目的としたフィルターである。For example, a filter such as an acetate filter is used to remove particulate substances such as tar and nicotine, or a filter such as activated carbon is used to remove gaseous substances such as acetaldehyde and hydrogen cyanide.
このように、煙草の有害物質を軽減しうるフィルターが
広く普及しているにもかかわらず、煙草の有害性が軽減
されていないのが現状である。これは、いいかえれば、
タールやニコチンあるいはアセトアルデヒド等は有害物
質の一種ではあるが、現存しているフィルターを使用し
てこれらを軽減しても、煙草の煙の中に存在する他の有
害物質を除去することができないためである。As described above, despite the widespread use of filters that can reduce the harmful substances in cigarettes, the current situation is that the harmfulness of cigarettes has not been reduced. In other words,
Tar, nicotine, acetaldehyde, etc. are types of harmful substances, but even if existing filters are used to reduce these substances, other harmful substances present in cigarette smoke cannot be removed. It is.
最近の煙草と人体に及ぼす影響の研究から、煙草の煙に
はラジカル、主に、アルコキシラジカルが存在し、この
ラジカルが今までに知られているフィルターを通過し、
人体の、特に、遺伝子に重大な悪影響を与えることが明
らかになってきた（たとえば、Ｃｈｕｒｃｈ Ｄ、Ｆ、
ａｎｄ Ｐｒｙｏｒ Ｗ、Ａ、、 Ｅｎｖｉｒｏｎｍ
ｅｎｔａｌ ｈｅａｌｔｈ ｐｅｒｓｐｅｃｔｉｖｅｓ
、１９８４＋１−３６）、この有害物質の一つである煙
草のラジカルは、喫煙者が直接吸引する煙草の煙、すな
わち、主流煙中にも、また、煙草の立ち昇る煙、すなわ
ち、副流煙中にも存在する０通常、ラジカルは高活性で
あればある程、そのラジカルの寿命は短い、しかし煙草
の煙に存在するラジカルは極めて高活性であるにもかか
わらず、数分間も安定に存在している。Recent research on cigarette smoke and its effects on the human body has revealed that cigarette smoke contains radicals, mainly alkoxy radicals, and that these radicals pass through known filters.
It has become clear that it has a serious negative effect on the human body, especially on genes (for example, Church D, F,
and Pryor W, A., Environm.
mental health perspectives
, 1984+1-36), cigarette radicals, which are one of these harmful substances, are present both in the cigarette smoke directly inhaled by smokers, i.e., mainstream smoke, and in the rising smoke of cigarettes, i.e., sidestream smoke. Normally, the more active a radical is, the shorter its life span is.However, the radicals present in cigarette smoke remain stable for several minutes, even though they are extremely active. are doing.
この事実はラジカルについてのこれまでの常識から考え
て驚くべきことである。This fact is surprising considering the conventional wisdom about radicals.
ラジカルによる癌発生機構が注目されている（たとえば
、がん発生機構−分子および電子レベルからみたー、Ｐ
、６７〜８４．１９８３、サイエンス社発行）、ラジカ
ルとは不対電子を持ったものの総称であり、煙草の煙に
存在するラジカルが癌の発生をもたらすことは直接的に
は証明されていない。The mechanism of cancer development by radicals is attracting attention (for example, cancer development mechanism - from the molecular and electronic level, P.
, 67-84, 1983, published by Science Inc.) Radical is a general term for things with unpaired electrons, and it has not been directly proven that the radicals present in cigarette smoke cause cancer.
しかし、煙草の煙に存在するラジカルは極めて高活性で
あるために人体への悪影響が十分に予想される。しかし
、このような煙草の煙に存在するラジカルを除去するフ
ィルターは全く知られていないのが現状であり、このラ
ジカルを除去しろるフィルターが特に切望される。However, since the radicals present in cigarette smoke are extremely active, it is fully expected that they will have an adverse effect on the human body. However, at present, there is no known filter that removes such radicals present in cigarette smoke, and a filter that can remove these radicals is particularly desired.
活性炭を使用したフィルターは広く普及しているが、ラ
ジカルの軽減効果はほとんどない、これを証明するため
に、本発明者らは市販されている数種のフィルター付き
煙草について、これらの煙草をフィルター付きのまま燃
焼させた場合とフィルターを除いて燃焼させた場合のそ
れぞれのラジカル通過量をＥＳＲ装置を用いて測定した
。その結果、両者間のラジカル通過量にはほとんど有意
差は認められなかつた。また、煙草の種類によらず、そ
のラジカル量はほぼ等しいという結果が得られた。これ
らの結果から、アセテ−日銭維だけのもの、活性炭を含
有したもの、乳性蛋白を含有しているものなど、現在普
及しているフィルターにはラジカルの軽減効果はほとん
ど見い出せないことがわかった。Although filters using activated carbon are widely used, they have little effect in reducing radicals.To prove this, the present inventors tested several types of filtered cigarettes on the market. The amount of radicals passed was measured using an ESR device when the fuel was burned with the filter attached and when it was burned without the filter. As a result, almost no significant difference was observed in the amount of radicals passing between the two. Furthermore, the results showed that the amount of radicals was almost the same regardless of the type of cigarette. These results show that the currently popular filters, such as those containing only acetate fiber, those containing activated carbon, and those containing milk protein, have almost no radical reduction effect. Ta.
本発明者らは活性炭の形状、使用量、充填方法の検討を
行い、活性炭のラジカル捕捉効果の大きい条件を既に見
い出している。この条件としては平均粒子径の小さい活
性炭を一定量以上使用することが必要である。しかし、
ラジカル捕捉剤として活性炭だけを使用した場合、人に
よっては活性炭の臭いを強く怒し、実用的ではないとい
う問題点がある。The present inventors have studied the shape, amount used, and filling method of activated carbon, and have already found conditions under which activated carbon has a large radical scavenging effect. This condition requires that a certain amount or more of activated carbon with a small average particle size be used. but,
When only activated carbon is used as a radical scavenger, there is a problem that some people are offended by the smell of activated carbon, making it impractical.
一方、ゼオライトは有害成分の吸着量として広（知られ
ている。しかし、ゼオライトにラジカルの捕捉効果があ
ることは全く知られていない。On the other hand, zeolite is widely known for its ability to adsorb harmful components. However, it is completely unknown that zeolite has a radical scavenging effect.
また、ゼオライトを煙草のフィルターに使用する方法も
知られている。たとえば、ゼオラ・イトを使用し、ｃｏ
、Ｃｏｔを除去するフィルターは特開昭５３−３９２６
６に開示されている。しかし、この明細書からはゼオラ
イトの効果を見い出すことはできない、たとえば、Ｃ０
１ｃｏ２の吸着量を示した具体的な実施例には十分な記
載がなく、当業者間の常識的な範囲から判断する限りに
おいて、実際に煙草を燃焼させて、その煙を用い、それ
をゼオライトに吸着させる方法で実施したとは考えられ
ない、その理由としては、煙草の埋に存在するＣ０１Ｃ
Ｏ，がそれぞれ、１３，２００ｐｐｍ 、 ５６ｐｐ１
ｍｍであり、それらを同時にほぼ完全に吸着したのであ
れば、ゼオライトの単位重量あたりのＣＯおよびＣＯ□
の吸着量の容積比は１３．２００：５６となるばずであ
る。しかし、合成ゼオライトおよび天然モルデナイトの
その比はそれぞれ１７゜］：６１および２０，５： ４
２．０であり、前記ＣＯとＣｏｔの比１．３．２００：
５６とは大幅に異なる。また、天然モルデナイトの吸−
Ｖ温度は吸着ガスがＣＯの場合とＣｏ２の場合ではそれ
ぞれ２３℃と２２℃と異なっている。したがって、実施
例で開示されている方法はＣＯガスあるいはＣｏ８ガス
をＮ２等の不活性ガスで希釈したものを使用して実施し
たものと判断される。このような方法で実施されたゼオ
ライトの吸着効果は、実際の煙草を燃焼させた煙の中か
ら生成するＣＯとＣＯ□を吸着除去する効果とは大幅に
異なる。It is also known to use zeolite in cigarette filters. For example, using zeolaite and co
, a filter for removing Cot is disclosed in Japanese Patent Application Laid-Open No. 53-3926.
6. However, the effect of zeolite cannot be found from this specification, for example, CO
There is no sufficient description in the specific examples showing the adsorption amount of 1 co2, and as far as it can be judged from the common sense among those skilled in the art, it is possible to actually burn cigarettes, use the smoke, and apply it to zeolite. It is unlikely that the method was used to adsorb CO1C to the cigarettes.
O, is 13,200 ppm and 56 ppm, respectively.
mm, and if they are almost completely adsorbed at the same time, CO and CO□ per unit weight of zeolite
The volume ratio of the amount of adsorption should be 13.200:56. However, the ratios for synthetic zeolite and natural mordenite are 17°]:61 and 20,5:4, respectively.
2.0, and the ratio of CO and Cot is 1.3.200:
It is significantly different from 56. In addition, natural mordenite absorption
The V temperature is 23° C. and 22° C. when the adsorbed gas is CO and Co2, respectively. Therefore, it is considered that the method disclosed in the Examples was carried out using CO gas or Co8 gas diluted with an inert gas such as N2. The adsorption effect of zeolite carried out in this manner is significantly different from the effect of adsorbing and removing CO and CO□ produced from actual smoke from burning cigarettes.
なぜならば、煙草の煙にはＣＯ，、ＣＯｔの他に主に、
水、タールまたはニコチン等が存在し、これらのゼオラ
イトへの影響は無視できないためである。したがって、
これらの共存下においても、実施例に示された条件下で
Ｃ０５ＣＯｔが吸着除去できるかははなはだ疑問である
。This is because, in addition to CO, COt, cigarette smoke mainly contains
This is because water, tar, nicotine, etc. are present, and their influence on zeolite cannot be ignored. therefore,
It is highly questionable whether CO5COt can be adsorbed and removed under the conditions shown in the examples even under these coexistence conditions.
このように、ゼオライトが煙草の煙の存置成分の吸着に
対し、特に効果があることは具体的には実証されていな
い。Thus, it has not been specifically demonstrated that zeolite is particularly effective in adsorbing residual components of cigarette smoke.
Ｉがｊ！” しようとする− 占
このように現存するフィルターはラジカルを捕捉する効
果はなく、また、このラジカルを捕捉する捕捉剤も全く
知られていないのが実状である。I is j! In this way, existing filters are not effective in capturing radicals, and the reality is that there are no known scavengers that can capture these radicals.
したがって、煙草の煙に存在するラジカルを軽減するフ
ィルターが強く切望される。Therefore, there is a strong need for a filter that reduces the radicals present in cigarette smoke.
本発明者らの課題は、煙草の煙に存在するラジカルを喫
煙する条件で除去するラジカル捕（ｙ剤を提供するもの
である。The object of the present inventors is to provide a radical scavenger that removes radicals present in cigarette smoke under smoking conditions.
ル 占を”°するための び
本発明者らは煙草の煙に存在するラジカルを除去しつる
捕捉剤について、鋭意検討した。その結果、ゼオライト
がラジカル捕捉効果の大きいことを見い出した。さらに
、このゼオライトと活性炭とを含有したフィルターが喫
煙する条件下においても、その除去効果が大きく、さら
に、活性炭の臭いも抑制されることを見い出し、本発明
を完成するに至った。The present inventors have conducted intensive studies on scavengers that remove radicals present in cigarette smoke.As a result, they have discovered that zeolite has a large radical scavenging effect.Furthermore, The present inventors have discovered that a filter containing zeolite and activated carbon has a great removal effect even under smoking conditions, and further suppresses the odor of activated carbon, leading to the completion of the present invention.
即ち、本発明はゼオラ、イトと活性炭とからなる煙草連
用ラジカル捕捉剤である。That is, the present invention is a radical scavenger for continuous use in cigarettes, which is composed of zeola, light and activated carbon.
本発明の方法におけるゼオライトの例としてはゼオライ
トＡ、ゼオライトＸまたはゼオライトＹのような合成ゼ
オライトが挙げられる。また天然ゼオライトも使用する
ことができる。Examples of zeolites in the method of the invention include synthetic zeolites such as zeolite A, zeolite X or zeolite Y. Natural zeolites can also be used.
本発明の方法で使用するゼオライトの平均粒径は小さい
ほどそのラジカル捕捉効果が大きいが、圧損失を考慮す
ればゼオライトの平均粒径は０．０１〜１．５Ｎが好ま
しい。The smaller the average particle size of the zeolite used in the method of the present invention, the greater its radical scavenging effect, but in consideration of pressure loss, the average particle size of the zeolite is preferably 0.01 to 1.5N.
また、本発明の方法で使用するゼオライトは通常の方法
で乾燥、すなわち、８０℃以上で１時間程度加熱乾燥し
たものを用いる方が好ましい。Further, it is preferable that the zeolite used in the method of the present invention be dried by a conventional method, that is, dried by heating at 80° C. or higher for about 1 hour.
本発明の方法で用いる活性炭はその原料が植物であって
もまた鉱物であっても用いることができる。活性炭の平
均粒径が１．５Ｎ以上であると、活性炭と煙草の煙との
接触効率が悪くなり、活性炭の単位重量あたりのラジカ
ル捕捉効率が低下し、多量の活性炭を必要とする。した
がって、活性炭の平均粒径は１．５ｆｌ以下、特に、１
ｆｌ以下が好ましい。The activated carbon used in the method of the present invention can be used regardless of whether its raw material is a plant or a mineral. If the average particle size of the activated carbon is 1.5N or more, the contact efficiency between the activated carbon and cigarette smoke will be poor, the radical trapping efficiency per unit weight of the activated carbon will be reduced, and a large amount of activated carbon will be required. Therefore, the average particle size of activated carbon is 1.5 fl or less, especially 1
It is preferably less than fl.
本発明の方法で使用するゼオライトはそれだけでラジカ
ルの捕捉効果があることを見い出した。It has been found that the zeolite used in the method of the present invention has a radical scavenging effect by itself.
平均粒径が１ｆｉのゼオライ目ＯＸを４００ Ｎ煙草の
フィルターとして使用した場合、そのラジカル軽減効果
は約５０％である。したがって、ラジカル捕捉効果のあ
る活性炭とは任意に混合してもラジカル捕捉効果は維持
される。ゼオライトの活性炭に対する含有量が多くなる
と同じラジカル捕捉効果を得るためにはゼオライトと活
性炭の総量が多くなるが活性炭の臭いは抑制される。し
たがって、これらを考慮した実用的なゼオライトの使用
量は重量比で活性炭の１７３〜３の範囲である。When Zeolite OX having an average particle size of 1 fi is used as a filter for 400 N cigarettes, its radical reduction effect is about 50%. Therefore, even if it is optionally mixed with activated carbon that has a radical-scavenging effect, the radical-scavenging effect is maintained. As the content of zeolite to activated carbon increases, the total amount of zeolite and activated carbon increases to obtain the same radical scavenging effect, but the odor of activated carbon is suppressed. Therefore, taking these into consideration, the practical amount of zeolite to be used is in the range of 173 to 3 parts by weight of activated carbon.
本発明の方法を煙草のフィルターとして使用する場合に
は、ゼオライトと活性炭の総重量が問題となる。圧損失
、あるいは、煙草のフィルターとしての使い易さを考慮
すれば、その総重量は５００■以下が好ましい。When using the method of the invention as a cigarette filter, the total weight of zeolite and activated carbon becomes a problem. Considering pressure loss or ease of use as a cigarette filter, the total weight is preferably 500 square meters or less.
ある程度のラジカル捕捉率がないと実用的ではない、こ
のためには、ゼオライトだけを煙草のフィルターとして
充填して使用するにはその充填量が多くなりすぎて好ま
しくない、この結果、ラジカル捕捉効果の大きい活性炭
と併用することが好ましい。It is not practical unless there is a certain degree of radical scavenging efficiency.For this reason, filling only zeolite as a cigarette filter would be undesirable because the amount of zeolite packed would be too large.As a result, the radical scavenging effect would be reduced. Preferably used in combination with large activated carbon.
本発明の方法で使用する活性炭の量は煙草１本あたり、
２００■以上あればラジカルの捕捉率は９０％以上にな
る。しかし、個人差あるいは活性炭の種類にもよるが、
活性炭を１．００ Ｑｒ以上使用した場合では、活性炭
の臭いが問題となる場合がある。The amount of activated carbon used in the method of the present invention is per cigarette;
If it is 200 or more, the radical capture rate will be 90% or more. However, depending on individual differences and the type of activated carbon,
When 1.00 Qr or more of activated carbon is used, the odor of the activated carbon may become a problem.
しかし、この場合、ゼオライトを併用すればゼオライト
自身のラジカル捕捉効果により活性炭の使用量を減少さ
せることができる上に、活性炭の臭いを抑制する効果も
ある。However, in this case, if zeolite is used in combination, the amount of activated carbon used can be reduced due to the radical scavenging effect of zeolite itself, and it is also effective in suppressing the odor of activated carbon.
したがって、活性炭の使用量は煙草１本あたり１００
ｆｆｇ以上２００■以下の範囲が好ましい。Therefore, the amount of activated carbon used is 100 per cigarette.
The range is preferably from ffg to 200 ■.
また、この時のゼオライトの使用量は３０■以上が好ま
しく、また、活性炭との合計が５００■以下の範囲が好
ましい。Further, the amount of zeolite used at this time is preferably 30 .mu. or more, and the total amount including activated carbon is preferably 500 .mu. or less.
本発明の方法で使用するゼオライトあるいは活性炭をフ
ィルターに含有させる方法としては、それぞれを混合す
ることなく、活性炭をアセテート繊維等のチップ間に充
填するトリプルフィルターとして使用してもよく、また
、アセテート繊維にｌ具入させるデュアルフィルターと
して使用してもよい。この場合、ゼオライトと活性炭の
充填のｉｌ１番は任意であり、また、ゼオライトと活性
炭を交互に充填しても効果がある。As a method of incorporating zeolite or activated carbon used in the method of the present invention into a filter, activated carbon may be used as a triple filter by filling between chips of acetate fibers etc. without mixing each. It may also be used as a dual filter. In this case, the filling number of zeolite and activated carbon is arbitrary, and it is also effective to fill zeolite and activated carbon alternately.
また、本発明の方法で使用するゼオライトあるいは活性
炭をフィルターに含有させる方法としては、それぞれを
あ°らかしめ混合し、この混合物をアセテート繊維等の
チップ間に充填するトリプルフィルターとして使用して
もよく、また、アセテート繊維に混入させるデュアルフ
ィルターとして使用してもよい、しかし、この他の方法
により、ゼオライトおよび活性炭をフィルターに含有さ
せても本発明の効果を得ることができるフィルターであ
ればその含有方法は同等制限されない。In addition, as a method for incorporating zeolite or activated carbon used in the method of the present invention into a filter, each may be thoroughly mixed and this mixture may be used as a triple filter by filling between chips of acetate fibers or the like. Also, it may be used as a dual filter by mixing it with acetate fibers. However, if the filter can obtain the effects of the present invention even if the filter contains zeolite and activated carbon by other methods, the filter may contain zeolite and activated carbon. The method is not equally limited.
また、本発明の方法によるラジカル充填剤をこれらの充
填方法を用いて煙草のパイプフィルターとしても使用す
ることもできる。Further, the radical filler prepared by the method of the present invention can also be used as a cigarette pipe filter using these filling methods.
また、本発明の方法によるラジカル捕捉剤を煙草埋用の
空気浄化用フィルターにも用いることができる。Furthermore, the radical scavenger prepared by the method of the present invention can also be used in air purifying filters for cigarettes.
大豆■
以下、実施例により本発明のフィルターを更に詳細に説
明する。Soybean ■ The filter of the present invention will be explained in more detail below with reference to Examples.
実施例１
ゼオライト１００■および活性炭２００■をあらかじめ
よく混合し、内径６．５Ｈのガラス管に少量の石英ウー
ルと共に充填したフィルターを作成した。Example 1 A filter was prepared by thoroughly mixing 100 μm of zeolite and 200 μm of activated carbon and filling it in a glass tube with an inner diameter of 6.5H together with a small amount of quartz wool.
このガラス管に市販の煙草（マイルドセブン）をフィル
ター付きのまま取り付け、空気中で燃焼させた。この煙
草の煙をガラス管から吸引ポンプを用いてＩＩ！／分で
吸引し、スピントラップ剤を調製した吸収液へ３０〜４
０秒で導入した。このスピン付加物をＥＳＲ装置で観察
し、本発明の方法によるラジカル捕捉剤を使用しない場
合との比較を行った結果、本発明の方法によるラジカル
捕捉剤を使用した場合のラジカル除去率は９０％であっ
た。A commercially available cigarette (Mild Seven) was attached to this glass tube with a filter attached, and it was burned in the air. This cigarette smoke is sucked from a glass tube using a pump II! 30 to 4 min to the absorbent solution prepared with spin trap agent.
It was introduced in 0 seconds. As a result of observing this spin adduct with an ESR device and comparing it with the method of the present invention without using the radical scavenger, the radical removal rate when using the method of the present invention with the radical scavenger was 90%. Met.
また、同じフィルターを作成し、喫煙者５名に喫煙して
もらい、活性炭の臭いの存無の判定を行った結果、活性
炭の臭いは認められなかった。結果を第１表に示す。In addition, the same filter was made and five smokers were asked to smoke it, and the presence or absence of activated carbon odor was determined.As a result, no activated carbon odor was detected. The results are shown in Table 1.
実施例２〜１２
実施例１と同様の方法で第１表の様にゼオライトの種類
、量および活性炭のｆｉＩｉ類、活性炭の量およびこれ
らの混合比を変化させた場合の結果を実施例１と共に第
１表に示す。Examples 2 to 12 In the same manner as in Example 1, the type and amount of zeolite, the fiIi type of activated carbon, the amount of activated carbon, and the mixing ratio of these were changed as shown in Table 1, and the results are shown together with Example 1. Shown in Table 1.
実施例１３
内径６．５ｆｌのガラス管に、ゼオライト１００■、活
性炭１５０躍およびゼオライト５０■を煙草の喫煙方向
へ順に、少量の石英ウールと共に充填したフィルターを
作成した。このガラス管にフィルタ一部分を除去した市
販の煙草（マイルドセブン）を取り付け、空気中で燃焼
させた。この煙草の煙をガラス管から吸引ポンプを用い
てｉｆｆ／分で吸引し、スピントラップ剤を調製した吸
収液へ３０〜４０秒で導入した。このスピン付加物をＥ
ＳＲ装置で観察し、本発明の方法によるラジカル捕捉剤
を使用しない場合と比較した結果、本発明の方法による
ラジカル捕捉剤を使用した場合のラジカル除去率は９０
％であった。また、活性炭の臭いは認められなかった。Example 13 A filter was prepared by filling a glass tube with an inner diameter of 6.5 fl with 100 mm of zeolite, 150 mm of activated carbon, and 50 mm of zeolite in the smoking direction of the cigarette, along with a small amount of quartz wool. A commercially available cigarette (Mild Seven) from which a portion of the filter had been removed was attached to this glass tube and burned in the air. The cigarette smoke was suctioned from the glass tube using a suction pump at iff/min, and the spin trap agent was introduced into the prepared absorption liquid in 30 to 40 seconds. This spin adduct is E
As a result of observation with an SR device and comparison with the case without using the radical scavenger according to the method of the present invention, the radical removal rate when using the radical scavenger according to the method of the present invention was 90.
%Met. Further, no odor of activated carbon was observed.
この結果を第２表に示す。The results are shown in Table 2.
実施例１４〜１６
実施例工３と同様の方法で第２表の様にゼオライトの種
類、量および活性炭の種類、活性炭の量およびこれらの
充填比率を変化させた場合の結果を実施例１３と共に第
２表に示す。Examples 14 to 16 The results when the type and amount of zeolite, the type of activated carbon, the amount of activated carbon, and their filling ratios were changed as shown in Table 2 in the same manner as in Example 3 are shown together with Example 13. Shown in Table 2.
実施例１７
第３図に示す装置において、３ツロフラスコの上方の口
から内径７１貫のガラス管を通じて１ｍａれた位置に２
００■の平均粒径０．８Ｉのゼオライト１０Ｘおよび３
００ ｒｒｔの平均粒径１ｍ塵のやし殻活性炭をよく混
合して調製したラジカル捕捉剤を充填し、煙を３００ｃ
ｃ／分でスピントラップ吸収液に導入した。このスピン
付加物をＥＳＲ装置で観察し、本発明の方法によるラジ
カル捕捉剤を使用しない場合と比較した結果、本発明の
方法によるラジカル捕捉剤を用いた場合のラジカル除去
率は９０％であった。また、活性炭の臭いは認められな
かった。Example 17 In the apparatus shown in Fig. 3, a 2-meter tube was placed 1 mm away from the upper mouth of the 3-tube flask through a glass tube with an inner diameter of 71 mm.
Zeolite 10X and 3 with an average particle size of 0.8I
Filled with a radical scavenger prepared by thoroughly mixing coconut shell activated carbon with an average particle size of 1 m dust of 00 rrt, the smoke was
c/min into the spin trap absorption liquid. The results of observing this spin adduct using an ESR device and comparing it with the method of the present invention without using the radical scavenger showed that the radical removal rate when using the method of the present invention with the radical scavenger was 90%. . Further, no odor of activated carbon was observed.
この実施例は本発明の方法によるラジカル捕捉剤を用い
て、煙草の副流煙中のラジカルが軽減できることを実証
したものである。すなわち、本発明の方法によるラジカ
ル捕捉剤を煙草煙用の空気浄化装置に使用できることを
示したものである。This example demonstrates that radicals in sidestream smoke of cigarettes can be reduced using the radical scavenger according to the method of the present invention. That is, this shows that the radical scavenger produced by the method of the present invention can be used in an air purification device for cigarette smoke.
１里（２）四王
実施例１〜１７で明かなように、本発明の方法によるラ
ジカル捕捉剤を使用した場合、使用しない場合に比べ、
煙草連中のラジカルは８５〜９５％除去され、また、活
性炭の臭いも認められなかった。1 Ri (2) Four Kings As is clear from Examples 1 to 17, when the radical scavenger according to the method of the present invention is used, compared to when it is not used,
85-95% of the radicals from cigarette smokers were removed, and no odor of activated carbon was observed.
第１図および第２図は本発明の方法を煙草のフィルター
に使用した場合の一例を示す断面図である。実施例１〜
１２及び１７では第１図に示したフィルターを使用し、
また、実施例１３〜１６では第２図に示したフィルター
を使用した。第３図は副流煙中のラジカル捕捉効果を試
験するための装置である。
各図において符号は以下の通りである。
１、煙草 ２．煙草に付属したフィルター３、石英ウ
ール ４．ラジカル捕捉剤（１）５、ラジカル捕捉剤
（２） ６．ラジカル捕捉剤（３）７．３ツロフラス
コ ８．吸引ポンプ
９、ケンブフリジフィルターFIGS. 1 and 2 are cross-sectional views showing an example of the use of the method of the present invention in a cigarette filter. Example 1~
12 and 17 use the filter shown in Figure 1,
Further, in Examples 13 to 16, the filter shown in FIG. 2 was used. Figure 3 shows an apparatus for testing the radical scavenging effect in sidestream smoke. In each figure, the symbols are as follows. 1. Cigarettes 2. Filter attached to cigarettes 3, quartz wool 4. Radical scavenger (1) 5, Radical scavenger (2) 6. Radical scavenger (3) 7.3 Tulo flask 8. Suction pump 9, Kenbufuriji filter
Claims (4)
捕捉剤。(1) A radical scavenger for cigarette smoke consisting of zeolite and activated carbon.
３〜３：１である特許請求の範囲第１項に記載の煙草煙
用ラジカル捕捉剤。(2) The content ratio of zeolite and activated carbon is 1:1 by weight.
The radical scavenger for cigarette smoke according to claim 1, which has a ratio of 3 to 3:1.
許請求の範囲第１項または第２項に記載の煙草煙用ラジ
カル捕捉剤。(3) The radical scavenger for cigarette smoke according to claim 1 or 2, wherein the zeolite has an average particle size of 1.5 mm or less.
範囲第１項または第２項に記載の煙草煙用ラジカル捕捉
剤。(4) The radical scavenger for cigarette smoke according to claim 1 or 2, wherein the activated carbon has an average particle size of 1 mm or less.