JPS63219592A - Rust preventive treatment for separator - Google Patents
Rust preventive treatment for separatorInfo
- Publication number
- JPS63219592A JPS63219592A JP5492987A JP5492987A JPS63219592A JP S63219592 A JPS63219592 A JP S63219592A JP 5492987 A JP5492987 A JP 5492987A JP 5492987 A JP5492987 A JP 5492987A JP S63219592 A JPS63219592 A JP S63219592A
- Authority
- JP
- Japan
- Prior art keywords
- separator
- concrete
- cement paste
- cone
- tip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
［発 明 の 目 的］
（産業上の利用分野）
本発明は、鉄筋コンクリート建造物において、コンクリ
ート壁内に残されたセパレーターの防錆に好適なセパレ
ーター防錆処理方法に関する。[Detailed description of the invention] [Object of the invention] (Industrial application field) The present invention relates to a separator rust prevention treatment method suitable for rust prevention of separators left in concrete walls in reinforced concrete buildings. .
（従来の技術）
従来、コンクリート壁等を形成する場合、相対向した型
枠相互間にセパレーターを介在し、型枠内に打設したコ
ンクリートが硬化した後に型枠を取り外す。この時、コ
ンクリート壁面には、コンクリート壁内に埋設されたセ
パレーターの先端部分が突出すると共に、この突出した
セパレーター先端の周囲に、プラスチックや本コーン等
のコーンの跡が凹設される。そこで、壁面の体裁を良好
にすると共に、セパレーターの防錆を図るため、セパレ
ーターの先端部が突出したコーン跡に、モルタル等を埋
め戻すなどの方法が取られていた。(Prior Art) Conventionally, when forming a concrete wall or the like, a separator is interposed between opposing formworks, and the formworks are removed after the concrete poured in the formworks has hardened. At this time, the tip portion of the separator buried in the concrete wall protrudes from the concrete wall surface, and the remains of a cone such as plastic or real cone are recessed around the protruding tip of the separator. Therefore, in order to improve the appearance of the wall surface and to prevent the separators from rusting, methods such as backfilling the cone marks where the tips of the separators protruded with mortar have been used.
また、コーン跡を埋め戻した後、コンクリート壁面上に
高分子ディスパージョンを混入したセメントペーストを
塗布する保護方法等もある。Another protection method involves backfilling the cone scars and then applying cement paste mixed with a polymer dispersion onto the concrete wall surface.
（発明が解決しようとする問題点）
ところが、モルタル等を埋め戻し、セパレーター先端が
高アルカリ性材で防錆された状態になっていでも、壁体
表面から侵入する空気中の炭酸ガスや水等により、壁面
近傍のコンクリートから徐々に中性化されるので、この
セパレーター先端部分の発錆は少なくない。(Problem to be solved by the invention) However, even if the tip of the separator is rust-proofed with a highly alkaline material after being backfilled with mortar, etc., carbon dioxide and water in the air that enters from the wall surface can cause corrosion. Since the concrete near the wall surface is gradually neutralized, there is considerable rusting at the tip of the separator.
また、セメントコンクリートは、長期に亘り硬化が進行
し、経年により岩石化して、極めて堅牢な材料となるが
、一旦、コンクリート内部で発錆すると、コンクリート
壁に亀裂が入り、この結果、防水性が低下し、発錆が更
に内部にまで進行して短期間でも著しい耐久性の劣化が
生じる虞があった。In addition, cement concrete hardens over a long period of time and turns into rock over time, making it an extremely strong material. However, once rust develops inside the concrete, cracks appear in the concrete wall, resulting in loss of waterproof properties. There was a risk that rust would progress further into the interior, resulting in significant deterioration of durability even in a short period of time.
一方、従来では、高分子ディスバージ日ンを混入したセ
メントペーストを、コンクリート壁面上に塗布被覆する
方法もあるが、このようなセメントペーストをコンクリ
ート壁面上に塗布しただけでは、コンクリート内部への
浸透性がなく、経年によるコーン跡部付着力の低下が生
じ、コンクリート内のセパレーター防蝕には役立たない
欠点があった。On the other hand, conventionally, there is a method of coating concrete walls with cement paste mixed with polymeric disverging sun, but if such cement paste is simply applied on concrete walls, it will not penetrate into the concrete. This has the disadvantage that the adhesion of the cone traces decreases over time, making it useless for preventing corrosion of separators in concrete.
本発明は上述の不都合を解消すべく創出されたもので、
特に、セパレーター先端部分の防錆を強化し、コンクリ
ート建造物の耐久性を高めるセパレーター防錆処理方法
の提供を目的とする。The present invention was created to solve the above-mentioned disadvantages.
In particular, the present invention aims to provide a separator rust prevention treatment method that strengthens the rust prevention of the tip of the separator and increases the durability of concrete buildings.
［発 明 の 構 成］
（問題点を解決するための手段）
上述の目的を達成すべく本発明は、鉄筋コンクリート造
のセパレーター防錆処理方法において、型枠解体後に、
セパレーターの先端からセパレーター突出部の基端に至
るセパレーター全表面とコンクリート表面に残るコーン
跡の底部全面とに、高分子ディスパージョンを混入した
セメントペーストを付着させることを問題解決のための
手段とする。[Structure of the Invention] (Means for Solving the Problems) In order to achieve the above-mentioned object, the present invention provides a separator rust prevention treatment method for a reinforced concrete structure, in which after the formwork is dismantled,
A means to solve the problem is to apply cement paste mixed with a polymer dispersion to the entire surface of the separator from the tip of the separator to the base end of the separator protrusion and the entire bottom of the cone marks left on the concrete surface. .
（実施例）
以下、セパレーター防錆処理方法を図面によって詳細に
説明する。(Example) Hereinafter, a separator rust prevention treatment method will be explained in detail with reference to the drawings.
図中、符号１はセパレーターである。セパレーター１は
、コンクリート２内に埋設されており、このセパレータ
ー１の先端部分はコーン跡３内部で突出している。In the figure, numeral 1 is a separator. The separator 1 is buried in the concrete 2, and the tip portion of the separator 1 protrudes inside the cone mark 3.
次に、コーン跡３内のセパレーター１の先端部分からセ
パレーター１の突出した部分の表面全体とコーン跡３の
底部全面とに、高分子ディスパージョンを混入したセメ
ントペースト４を被覆する。Next, the entire surface of the protruding portion of the separator 1 from the tip of the separator 1 within the cone mark 3 and the entire bottom of the cone mark 3 are coated with cement paste 4 mixed with a polymer dispersion.
セメントペースト４は、ポルトランドセメント等の各種
セメントに、ＳＢＲやＮＢＲ等のゴムラテックス、アク
リル樹脂、ポリエチレン等の合成樹脂エマルジョンや、
その共重合物、及びその混合物等の高分子ディスパージ
ョンを混入したものである。Cement paste 4 is made of various cements such as Portland cement, rubber latex such as SBR or NBR, synthetic resin emulsion such as acrylic resin, polyethylene, etc.
Polymer dispersions such as copolymers thereof and mixtures thereof are mixed therein.
この際、セメントペーストにカルシウムニトロ基等の鉄
筋コンクリート用防錆剤や、その他の防錆剤を混入する
ことで、防錆効果を更に高めることができる。尤も、Ｓ
ＢＲやＮＢＲ等のゴムラテックス、アクリル樹脂、ポリ
エチレン等の合成樹脂エマルジョンや、その共重合物、
及びその混合物のみを混合したセメントペースト４でも
コンクリートの中性化を充分防止し得ることは言うまで
もない。At this time, the rust preventive effect can be further enhanced by mixing a reinforced concrete rust preventive agent such as a calcium nitro group or other rust preventive agent into the cement paste. Of course, S
Rubber latex such as BR and NBR, synthetic resin emulsions such as acrylic resin and polyethylene, and their copolymers,
It goes without saying that cement paste 4, which is made by mixing only the above mixtures, can also sufficiently prevent the neutralization of concrete.
セメントペースト４の塗布は、主にスプレーガン使用に
よる吹付は塗布を予定しているが、塗布の手段として、
この他、刷毛塗りによるものや、鏝などを利用するなど
、セメントペースト４の活性度に応じた適宜な手段を用
いる。また、セメントペースト４塗布後のコンクリート
２表面加工などは、従来通りに施工するもので、セメン
トペースト４を塗布した状態で次の仕上げ工程に及ぶも
、或いは、セメントペースト４塗布後にコーン跡３を埋
め戻すも施工目的により任意に選択する。ただ、コーン
跡３を埋め戻す場合には、粘度の高いセメントペースト
４自体をコーン跡３内に埋設することで、更に中性化防
止力を強化し得ることは言うまでもない。The application of cement paste 4 is mainly planned to be done by spraying using a spray gun, but as a means of application,
In addition, an appropriate method depending on the activity level of the cement paste 4 is used, such as applying with a brush or using a trowel. In addition, the surface treatment of the concrete 2 after applying the cement paste 4 is performed in the conventional manner, and the next finishing process is carried out with the cement paste 4 applied, or the cone mark 3 is removed after the cement paste 4 is applied. Backfilling can also be selected arbitrarily depending on the purpose of construction. However, when backfilling the cone mark 3, it goes without saying that by burying the highly viscous cement paste 4 itself in the cone mark 3, the neutralization prevention ability can be further strengthened.
［発 明 の 効 果］
本発明は、上述の如く鉄筋コンクリート造のセパレータ
ー１防錆処理方法において、型枠解体後に、セパレータ
ー１の先端からセパレータ−１突出部の基端に至るセパ
レータ−１全表面とコンクリート表面に残るコーン跡３
の底部全面とに、高分子ディスパージョンを混入したセ
メントペースト４を付着させることことにより、尤も発
錆が生じやすいセパレーター１の先端部分を確実に防錆
することができる。[Effects of the Invention] The present invention provides a rust prevention treatment method for a separator 1 made of reinforced concrete as described above, in which the entire surface of the separator 1 from the tip of the separator 1 to the base end of the protruding portion of the separator 1 is treated after dismantling the formwork. and cone marks left on the concrete surface 3
By applying the cement paste 4 mixed with a polymer dispersion to the entire bottom surface of the separator 1, the tip portion of the separator 1, where rust is most likely to occur, can be reliably rust-proofed.
しかも、セメントペースト４は、コーン跡に残存するセ
パレーター１とコーン跡３の底部とに付着させるから、
セメントペースト４付着部分がコンクリート壁面上に表
出せずに済む。したがって、コンクリート全壁面上に高
分子ディスパーションを混入したセメントペーストを塗
布しただけの従来の保護方法等に比べ、経年による付着
力の低下防止を図ることができ、長期間に亘りコンクリ
ートの中性化を防止する。この結果、コンクリート構造
物内での発錆を防止し、コンクリート構造物の耐久性を
顕著に高めることができる。Moreover, since the cement paste 4 is attached to the separator 1 remaining on the cone mark and the bottom of the cone mark 3,
The adhering portion of the cement paste 4 is not exposed on the concrete wall surface. Therefore, compared to conventional protection methods that simply apply cement paste mixed with polymer dispersion on the entire concrete wall surface, it is possible to prevent the adhesive strength from decreasing over time, and the neutrality of the concrete can be maintained for a long period of time. to prevent As a result, rust can be prevented from forming within the concrete structure, and the durability of the concrete structure can be significantly improved.
このように本発明によれば、セパレーター先端部分の防
錆を強化し、コンクリート建造物の耐久性を高めるなど
の優れた諸効果を奏する。As described above, according to the present invention, various excellent effects such as strengthening the rust prevention of the tip portion of the separator and increasing the durability of concrete buildings are achieved.
図面は、本発明に係る鉄筋コンクリート造におけるコー
ン跡の防錆処理方法の実施例を示す断面図である。
１・・・セパレータ、２・・・コンクリート、３・・・
コーン跡、４・・・セメントペースト。
特許出願人 有限会社 銘木左官タイルエ店手続？ｒＤ
正書（自発）
昭和６３年 ２月、、−日The drawing is a cross-sectional view showing an embodiment of the rust prevention treatment method for cone marks in reinforced concrete construction according to the present invention. 1...Separator, 2...Concrete, 3...
Cone marks, 4...cement paste. Patent applicant Limited company Precious wood plastering tile store procedure? rD
Original text (spontaneous) February 1988, -Sun
Claims (1)
おいて、型枠解体後に、セパレーターの先端からセパレ
ーター突出部の基端に至るセパレーター全表面とコンク
リート表面に残るコーン跡の底部全面とに、高分子ディ
スパーションを混入したセメントペーストを付着させる
ことを特徴とするセパレーター防錆処理方法。 ２、セメントペーストは、防錆材を混入した特許請求の
範囲第１項記載のセパレーター防錆処理方法。[Scope of Claims] 1. In a method for rust-preventing a separator in a reinforced concrete structure, after the formwork is dismantled, the entire surface of the separator from the tip of the separator to the base end of the protruding part of the separator and the entire bottom of the cone trace remaining on the concrete surface are treated. , a separator rust prevention treatment method characterized by adhering a cement paste mixed with a polymer dispersion. 2. The separator rust prevention treatment method according to claim 1, wherein the cement paste contains a rust preventive material.