JPS63153132A - Laminated sheet for molding vessel and manufacture thereof - Google Patents
Laminated sheet for molding vessel and manufacture thereofInfo
- Publication number
- JPS63153132A JPS63153132A JP29882686A JP29882686A JPS63153132A JP S63153132 A JPS63153132 A JP S63153132A JP 29882686 A JP29882686 A JP 29882686A JP 29882686 A JP29882686 A JP 29882686A JP S63153132 A JPS63153132 A JP S63153132A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin layer
- polyolefin resin
- polyvinylidene chloride
- laminated sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は酸素等のガス不透過性と防水・耐湿性とヒート
シール特性とを有する容器成形用の積層シートとその製
造方法とに関するものであり、前記諸特性を具備する容
器に容易に成形され得る積層シート及びその製造方法を
提供するものである。[Detailed Description of the Invention] [Industrial Application Field] The present invention relates to a laminated sheet for forming containers that is impermeable to gases such as oxygen, waterproof/moisture resistant, and has heat-sealing properties, and a method for manufacturing the same. The present invention provides a laminated sheet that can be easily formed into a container having the above characteristics, and a method for manufacturing the same.
紙層による剛性と熱可塑性樹脂層による防水性やヒート
シール特性とを兼備する容器成形用積層シートとして、
紙層とポリオレフィン系樹脂層との積層シートが諸種の
内填物封入用の容器を得るための容器成形用積層シート
として多用されている。As a laminated sheet for container molding, it combines the rigidity of the paper layer with the waterproof and heat-sealing properties of the thermoplastic resin layer.
A laminated sheet of a paper layer and a polyolefin resin layer is frequently used as a laminated sheet for forming containers to obtain containers for encapsulating various types of fillers.
ところで、前記従来の紙層とポリオレフィン系樹脂層と
の積層シートからなる容器成形用積層シートによって得
られる容器は、酸素等のガス不透過性の点における性能
が劣るものであることから、食品等の種類によっては品
質劣化などが生ずるため、その保存性能が悪く、封入さ
れる内填物の種類が大幅に制限されなければならないと
いう欠点を有している。By the way, containers obtained using the conventional laminated sheet for container molding, which is a laminated sheet of a paper layer and a polyolefin resin layer, have poor performance in terms of impermeability to gases such as oxygen, so they cannot be used for foods, etc. Depending on the type, quality deterioration may occur, resulting in poor storage performance and the disadvantage that the types of fillers to be encapsulated must be greatly restricted.
これに対して本第１の発明は、前記従来の容器成形用積
層シートと同様の防水性とヒートシール特性とを具備す
るばかりでなく、酸素等のガス不透過性及び耐湿性の点
においても十分に満足される性質を発揮し、且つ、容易
、安価に得られるという特質を有する容器成形用の積層
シートを提供するものであり、また、本第２の発明は、
前記緒特性を有する本第１の発明の容器成形用の積層シ
ートを容易、且つ確実に得る方法を提供するものである
。In contrast, the first invention not only has the same waterproof properties and heat-sealing properties as the conventional laminated sheet for forming containers, but also has good impermeability to gases such as oxygen and moisture resistance. The second invention provides a laminated sheet for container molding that exhibits sufficiently satisfactory properties and can be obtained easily and inexpensively.
The present invention provides a method for easily and reliably obtaining the laminated sheet for container molding of the first invention having the above-mentioned properties.
本第１の発明の容器成形用の積層シートは、紙層もしく
はポリオレフィン系樹脂被覆層を有する紙層と、前記紙
層に直接形成されているポリオレフィン系樹脂による目
止め樹脂層と、該ポリオレフィン系樹脂による目止め樹
脂層を介して前記紙層に積層されているポリ塩化ビニリ
デン樹脂層と、該ポリ塩化ビニリデン樹脂層に積層され
ているポリオレフィン系樹脂層とからなるものである。The laminated sheet for container molding of the first invention comprises a paper layer having a paper layer or a polyolefin-based resin coating layer, a sealing resin layer made of a polyolefin-based resin directly formed on the paper layer, and a sealing resin layer made of a polyolefin-based resin formed directly on the paper layer; It consists of a polyvinylidene chloride resin layer laminated on the paper layer via a sealing resin layer made of resin, and a polyolefin resin layer laminated on the polyvinylidene chloride resin layer.
また、本第２の発明の容器成形用の積層シートの製造方
法は、ポリオレフィン系樹脂による目止め樹脂層を、厚
紙もしくはポリオレフィン系樹脂被覆層を有する厚紙に
おける紙層に直接押出しコート法にて形成する工程と、
前記ポリオレフィン系樹脂による目止め樹脂層にコロナ
放電処理を施す工程と、コロナ放電処理が施されている
前記ポリオレフィン系樹脂による目止め樹脂層に、ポリ
塩化ビニリデン樹脂エマルジョ／を塗布、乾燥、加熱し
てポリ塩化ビニリデン樹脂層を形成する工程と、前記得
られたポリ塩化ビニリデン樹脂層にコロナ放電処理を施
す工程と、前記コロナ放電処理が施されているポリ塩化
ビニリデン樹脂層にポリオレフィン系樹脂の押出しコー
ト層を形成する工程とからなるものである。Further, in the method for manufacturing a laminated sheet for container molding according to the second invention, a sealing resin layer made of polyolefin resin is formed directly on a paper layer of cardboard or cardboard having a polyolefin resin coating layer by an extrusion coating method. The process of
A step of applying a corona discharge treatment to the sealing resin layer made of the polyolefin resin, and applying a polyvinylidene chloride resin emulsion/to the sealing resin layer made of the polyolefin resin that has been subjected to the corona discharge treatment, drying, and heating. a step of forming a polyvinylidene chloride resin layer by applying a corona discharge treatment to the obtained polyvinylidene chloride resin layer, and extruding a polyolefin resin to the polyvinylidene chloride resin layer that has been subjected to the corona discharge treatment. It consists of a step of forming a coat layer.
前記構成から成る本書発明の容器成形用の積層シート及
びその製造方法において、紙層もしくはポリオレフィン
系樹脂被覆層を有する紙層は、積層シートに剛性を与え
るもので、前記積層シートによって得られる成形容器に
剛性と形状保持性とを具備させるものであって、通常、
紙容器成形用の機械加工適性を有する厚紙が利用される
のが一般的である。In the laminated sheet for container molding of the present invention having the above-mentioned structure and the method for producing the same, the paper layer or the paper layer having a polyolefin resin coating layer provides rigidity to the laminated sheet, and the molded container obtained by the laminated sheet It provides rigidity and shape retention, and usually,
It is common to use cardboard that is suitable for machining to form paper containers.
紙層に直接形成されているポリオレフィン系樹脂による
目止め樹脂層は、前記紙層に積層されているポリ塩化ビ
ニリゾ／樹脂層と紙層との間の接着強度を向上させるも
のであり、且つ、均一な厚さのポリ塩化ビニＩＪデン樹
脂層を得るだめのものである。The sealing resin layer made of polyolefin resin that is directly formed on the paper layer improves the adhesive strength between the polyvinyl chloride/resin layer laminated on the paper layer and the paper layer, and This is to obtain a polyvinyl chloride IJ resin layer of uniform thickness.
前記紙層に積層されているポリ塩化ビニリデン樹脂層は
′、本発明の容器成形用の積層シートに酸素等のガス不
透過性と耐湿性とをもたらすものである。The polyvinylidene chloride resin layer laminated on the paper layer provides impermeability to gases such as oxygen and moisture resistance to the laminated sheet for forming containers of the present invention.
また、前記ポリ塩化ビニリデン樹脂層に積層されている
ポリオレフィン系樹脂層は、本発明の容器成形用の積層
シートにヒートシール性能を付与するものであり、本発
明の容器成形用の積層シートによって成形された容器と
別製の蓋材とが、ヒートシールによって溶着、固着され
得る特性が得られるものであると共に、前記容器成形用
の積層シートは前記ポリオレフィン系樹脂層が容器内周
面層となるようにして容器に成形されるものであること
から、容器内に封入される内填物に対する衛生特性（例
えば、内填物の鮮度保持や内填物中に存在していること
が必要とされる嫌気性菌の生存日数の延長等）もが導入
されるものである。Further, the polyolefin resin layer laminated on the polyvinylidene chloride resin layer imparts heat sealing performance to the laminated sheet for container molding of the present invention, and is molded by the laminated sheet for container molding of the present invention. In addition, the polyolefin resin layer of the laminated sheet for container molding serves as a layer on the inner peripheral surface of the container. Since the container is formed into a container in this way, sanitary properties for the filler sealed in the container (for example, maintaining the freshness of the filler and its presence in the filler are required. (e.g., extending the survival period of anaerobic bacteria).
更に、本第２の発明におけるポリオレフィン系樹脂によ
る目止め樹脂層に施されるコロナ放電処理と、ポリ塩化
ビニリゾ／樹脂層に施されるコロナ放電処理とは、ポリ
オレフィン系樹脂による目止め樹脂層とポリ塩化ビニリ
デン樹脂層との間の接着強度、及びポリ塩化ビニリデン
樹脂層と該樹脂層に積層されるポリオレフィン系樹脂層
との間の接着強度をそれぞれ向上させるためのもので、
好ましくはコロナ放電処理面が３８〜４４ ｄｙｎｅ／
ｃＩＩＬ程度となるようなコロナ放電処理されるもので
ある。Furthermore, the corona discharge treatment applied to the sealing resin layer made of polyolefin resin and the corona discharge treatment applied to the polyvinylchloride/resin layer in the second invention are different from the corona discharge treatment applied to the sealing resin layer made of polyolefin resin. This is for improving the adhesive strength between the polyvinylidene chloride resin layer and the polyolefin resin layer laminated on the polyvinylidene chloride resin layer, respectively.
Preferably, the corona discharge treated surface has 38 to 44 dyne/
It is subjected to corona discharge treatment to achieve a level of cIIL.
また、本第２の発明の方法におけるポリ塩化ビニリデン
樹脂層の形成は、ポリ塩化ビニＩＪデ／樹脂エマルジョ
ンを、例えば、エアーナイフ。Further, in the method of the second invention, the polyvinylidene chloride resin layer is formed by using a polyvinylidene chloride IJ resin emulsion, for example, with an air knife.
マイヤーロッド、グラビアロール等の塗布方法で塗布、
乾燥後、加熱処理することによって達成されるものであ
る。尚、前記ポリ塩化ビニリデン樹脂層の形成工程にお
けるポリ塩化ビニリデン樹脂エマルジョンの塗布、乾燥
後に実施される加熱工程は、ポリ塩化ビニ＋７デ／樹脂
エマルジヨンによる塗工樹脂層が、前記エマルジョンの
塗布、乾燥後に１００−１２０℃程度の加熱処理（熟成
処理）に付されることにより、被塗工面との間に優れた
接着強度を有する樹脂層となる性質を有していることに
よるものであり、前記加熱工程は１００〜１２０’Ｃ程
度で実施されるものである。Apply using Meyer rod, gravure roll, etc.
This is achieved by heat treatment after drying. In addition, the heating step carried out after coating and drying the polyvinylidene chloride resin emulsion in the step of forming the polyvinylidene chloride resin layer is such that the coated resin layer of the polyvinylidene + 7 de/resin emulsion is coated with the emulsion and dried. This is because it has the property of forming a resin layer with excellent adhesive strength with the surface to be coated when it is subsequently subjected to heat treatment (aging treatment) at about 100-120°C. The heating step is carried out at about 100 to 120'C.
尚、前記本書発明の容器成形用の積層シート及びその製
造方法において、ポリオレフィン系樹脂層は、例えばポ
リエチレン、ポリプロピレン、エチレン・酢酸ビニル共
重合体またはこれらの変性樹脂等で形成されるが、最も
好ましくはポリエチレン樹脂で形成されるものである。In the laminated sheet for container molding and the manufacturing method thereof of the present invention, the polyolefin resin layer is formed of, for example, polyethylene, polypropylene, an ethylene/vinyl acetate copolymer, or a modified resin thereof, but most preferably. is made of polyethylene resin.
以下、本発明の容器成形用の積層シート及びその製造方
法の具体的な構成を実施例に基いて説明する。Hereinafter, the specific structure of the laminated sheet for container molding and the manufacturing method thereof of the present invention will be explained based on Examples.
実施例
片側表面がポリオレフィン系樹脂で被覆さ・れている紙
容器成形原紙の紙層面に、押出しコート法にてポリエチ
レン樹脂の目止め樹脂層を形成する第１工程と、前記ポ
リエチレン樹脂の目止め樹脂層面にコロナ放電処理加工
を施す第２工程と、前記コロナ放電処理面に、ポリ塩化
ビニリデン樹脂エマルジョン〔固型分：５０チ、比重：
１．２５４、粘度： ３０ ｃｐｓ （ブルックフィー
ルドＲＶＴ ”１ ）、表面長カニ ５０ ｄｙｎｅ／
ａｎｓｐ）Ｉ：１．８）に、よるコーティング剤を、マ
イヤーロッドコート法にて、７２（固形成分）／Ｗ？
の割合にて塗布後、１１０°Ｃ１３０秒間の乾燥。Example A first step of forming a sealing resin layer of polyethylene resin by an extrusion coating method on the paper layer surface of paper container forming base paper whose one side surface is coated with a polyolefin resin, and a sealing layer of polyethylene resin. A second step of applying corona discharge treatment to the surface of the resin layer, and applying a polyvinylidene chloride resin emulsion [solid content: 50 cm, specific gravity:
1.254, viscosity: 30 cps (Brookfield RVT "1"), surface length crab 50 dyne/
Ansp) I: 1.8) was coated with a coating agent of 72 (solid component)/W? using the Mayer rod coating method.
After coating at a ratio of , dry for 130 seconds at 110°C.
熱処理を施し、ポリ塩化ビニリゾ／樹脂層を形成する第
３工程と、前記得られたポリ塩化ビニリゾ／樹脂層面に
コロナ放電処理加工を施す第４工程と、前記コロナ放電
処理面に押出しコート法にてポリエチレン樹脂層を形成
する第５工程とを施すことにより、本発明の容器成形用
の積層シートの１実施例品を得た。A third step of applying heat treatment to form a polyvinylizo-chloride/resin layer, a fourth step of applying corona discharge treatment to the surface of the obtained polyvinylchloride/resin layer, and applying an extrusion coating method to the corona discharge-treated surface. By performing the fifth step of forming a polyethylene resin layer, an example product of a laminated sheet for container molding of the present invention was obtained.
得られた容器成形用の積層シートは、図に示される通り
、ポリオレフィン系樹脂被覆層１を有する紙層２と、該
紙層２に直接形成されているポリオレフィン系樹脂によ
る目止め樹脂層３と、該目止め樹脂層３を介して前記紙
層２に積層されているポリ塩化ビニリデン樹脂層４と、
該ポリ塩化ビニリデン樹脂層４に積層されているポリオ
レフィン系樹脂層５とからなる積層シートであり、ポリ
オレフィン系樹脂層５が容器の内周面層となるようにし
て容器に成形されるものである。As shown in the figure, the obtained laminated sheet for container molding includes a paper layer 2 having a polyolefin resin coating layer 1, a sealing resin layer 3 made of a polyolefin resin directly formed on the paper layer 2, and , a polyvinylidene chloride resin layer 4 laminated on the paper layer 2 via the sealing resin layer 3;
It is a laminated sheet consisting of the polyvinylidene chloride resin layer 4 and a polyolefin resin layer 5 laminated thereon, and is molded into a container so that the polyolefin resin layer 5 becomes the inner peripheral surface layer of the container. .
本第１の発明の容器成形用の積層シートは、紙層もしく
はポリオレフィン系樹脂被覆層を有する紙層と、前記紙
層に直接形成されているポリオレフィン系樹脂による目
止め樹脂層を介して前記紙層に積層されているポリ塩化
ビニリデン樹脂層と、該ポリ塩化ビニリデン樹脂層に積
層されているポリオレフィン系樹脂層とからなるもので
、紙層の有する剛性と、ポリオレフィン系樹脂層の有す
る防水性と、ポリ塩化ビニリデン樹脂層の有する酸素等
のガス不透過性と耐湿性と、成形された容器における容
器内周面層をなすポリオレフィン系樹脂層の有するヒー
トンール特性と内填物に対する衛生特性（例えば、内填
物の鮮度保持や内填物中に存在していることが必要とさ
れる嫌気性菌の生存日数の延長等）とを具備すると共に
、簡単且つ廉価に製造され得る等の作用、効果を奏する
ものである。The laminated sheet for container molding according to the first aspect of the present invention includes a paper layer having a paper layer or a polyolefin resin coating layer, and a sealing resin layer made of a polyolefin resin formed directly on the paper layer. It consists of a polyvinylidene chloride resin layer laminated to a layer and a polyolefin resin layer laminated to the polyvinylidene chloride resin layer, and has the rigidity of the paper layer and the waterproofness of the polyolefin resin layer. The polyvinylidene chloride resin layer has impermeability to gases such as oxygen and moisture resistance, and the polyolefin resin layer that forms the inner circumferential surface layer of the molded container has heat roll properties and sanitary properties for the inner filling (for example, It has functions and effects such as maintaining the freshness of the inner filler and extending the survival period of anaerobic bacteria that are required to be present in the inner filler, etc., and can be easily and inexpensively manufactured. It is something that plays.
また、本第２の発明の容器成形用の積層シートの製造方
法は、厚紙もしくはポリオレフィン系樹脂被覆層を有す
る厚紙における紙層に、ポリオレフィン系樹脂による目
止め樹脂層を直接押し出しコートする工程と、前記ポリ
オレフィン系樹脂による目止め樹脂層にコロナ放電処理
を施す工程と、コロナ放電処理が施されている前記ポリ
オレフィン系樹脂による目止め樹脂層に、ポリ塩化ビニ
リデン樹脂エマルジョ／を塗布、乾燥、加熱してポリ塩
化ビニリデン樹脂層を形成する工程と、前記得られたポ
リ塩化ビニリデン樹脂層にコロナ放電処理を施す工程と
、前記コロナ放電処理が施されているポリ塩化ビニリデ
ン樹脂層にポリオレフィン系樹脂の押出しコート層を形
成する工程とからなるものであり、前記本第１の発明の
緒特性を有する容器成形用の積層７−トが容易、且つ確
実に得られるという作用、効果を奏するものである。In addition, the method for manufacturing a laminated sheet for container molding according to the second invention includes a step of directly extruding and coating a sealing resin layer made of a polyolefin resin on a paper layer of cardboard or cardboard having a polyolefin resin coating layer; A step of applying a corona discharge treatment to the sealing resin layer made of the polyolefin resin, and applying a polyvinylidene chloride resin emulsion/to the sealing resin layer made of the polyolefin resin that has been subjected to the corona discharge treatment, drying, and heating. a step of forming a polyvinylidene chloride resin layer by applying a corona discharge treatment to the obtained polyvinylidene chloride resin layer, and extruding a polyolefin resin to the polyvinylidene chloride resin layer that has been subjected to the corona discharge treatment. This method consists of a step of forming a coating layer, and has the effect of easily and reliably obtaining a laminated sheet for container molding having the characteristics of the first aspect of the present invention.
図は本第１の発明の容器成形用の積層ノートの１例を模
型的に示す断面図である。
２：ポリオレフィン系樹脂被覆層１を有する紙層、３：
ポリオレフィン系樹脂による目止め樹脂層、４：ポリ塩
化ビニリデン樹脂層、５：（容器内周面層とな゛る）ポ
リオレフィン系樹脂層。The figure is a cross-sectional view schematically showing an example of a laminated notebook for container molding according to the first invention. 2: Paper layer having polyolefin resin coating layer 1, 3:
Sealing resin layer made of polyolefin resin, 4: polyvinylidene chloride resin layer, 5: polyolefin resin layer (which becomes the container inner peripheral surface layer).
Claims (2)
る紙層と、前記紙層に直接形成されているポリオレフィ
ン系樹脂による目止め樹脂層を介して前記紙層に積層さ
れているポリ塩化ビニリデン樹脂層と、該ポリ塩化ビニ
リデン樹脂層に積層されているポリオレフィン系樹脂層
とからなることを特徴とする容器成形用の積層シート。(1) A paper layer having a paper layer or a polyolefin resin coating layer, and a polyvinylidene chloride resin layer laminated on the paper layer via a sealing resin layer made of polyolefin resin that is directly formed on the paper layer. and a polyolefin resin layer laminated on the polyvinylidene chloride resin layer.
る厚紙における紙層に、ポリオレフィン樹脂による目止
め樹脂層を直接押し出しコートする工程と、前記ポリオ
レフィン系樹脂による目止め樹脂層にコロナ放電処理を
施す工程と、コロナ放電処理が施されている前記ポリオ
レフィン系樹脂による目止め樹脂層に、ポリ塩化ビニリ
デン樹脂エマルジョンを塗布、乾燥、加熱してポリ塩化
ビニリデン樹脂層を形成する工程と、前記得られたポリ
塩化ビニリデン樹脂層にコロナ放電処理を施す工程と、
前記コロナ放電処理が施されているポリ塩化ビニリデン
樹脂層にポリオレフィン系樹脂の押出しコート層を形成
する工程とからなることを特徴とする容器成形用の積層
シートの製造方法。(2) A step of directly extrusion coating a sealing resin layer made of a polyolefin resin onto a cardboard or a paper layer of cardboard having a polyolefin resin coating layer, and a step of subjecting the sealing resin layer made of the polyolefin resin to a corona discharge treatment. , forming a polyvinylidene chloride resin layer by applying a polyvinylidene chloride resin emulsion to the sealing resin layer made of the polyolefin resin that has been subjected to corona discharge treatment, drying and heating the polyvinylidene resin emulsion; A step of subjecting the vinylidene resin layer to corona discharge treatment,
A method for manufacturing a laminated sheet for container molding, comprising the step of forming an extrusion coat layer of a polyolefin resin on the polyvinylidene chloride resin layer that has been subjected to the corona discharge treatment.