JPS6231889B2 - - Google Patents
Info
- Publication number
- JPS6231889B2 JPS6231889B2 JP54077123A JP7712379A JPS6231889B2 JP S6231889 B2 JPS6231889 B2 JP S6231889B2 JP 54077123 A JP54077123 A JP 54077123A JP 7712379 A JP7712379 A JP 7712379A JP S6231889 B2 JPS6231889 B2 JP S6231889B2
- Authority
- JP
- Japan
- Prior art keywords
- fishing line
- polymer
- monofilament
- terephthalate polymer
- butylene terephthalate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
本発明は釣糸に関するものである。
従来魚釣を行なう際に用いる釣糸は、通常、比
較的太くて強力の高い釣糸（みち糸）の先端に、
このみち糸より強力の若干小さな細い釣糸（はり
す）をつなぎ、このはりすに釣針を取付けて用い
ている。本発明はこのはりすに用いて特に好適な
釣糸に関するものである。
はりすとして用いる釣糸の性質としては、あま
り過大な力が加わつた場合にみち糸が切断する前
に切断してみち糸の切断するのを防止するため、
みち糸より若干その強力が低くなければならない
が、釣針に掛かつた魚が暴れ回る場合には、はり
すは引張られることは勿論屈曲されたり、ねじら
れたりする。すなわち、はりすに用いる釣糸は、
このような種々の応力に対しての強度や、使用状
態に応じた特性、例えば引張強度、結節強度、屈
曲強度、耐水性、曲げ剛性等がバランス良く具備
されていなければならない。
つまり、例えば他の強度や特性に優れていたと
しても結節強度が低い場合には、掛かつた魚が暴
れた場合、はりすと釣針との結節部から切断して
しまうし、屈曲強度が低い場合には魚が暴れては
りすが屈曲された場合にその屈曲部から切断して
しまうこととなる。
このようにはりすとして用いる釣糸の性質とし
ては、ある特定の強度や、特性のみが優れている
ものより、あらゆる強度が平均してある水準以上
に優れたものとされなければならないことは勿
論、特に水中で強度低下を起さないものであるこ
とが必要である。
従来、釣糸として多く用いられているナイロン
６、ナイロン６−10等のポリアミド系樹脂は、そ
の固有特性である吸水性により吸水し、その結果
引張強度、結節強度が低下して切断しやすくな
り、また、曲げ剛性が低下する（柔軟化する）の
で、糸が絡まる等の欠陥がある。
本発明者等はこのような従来のはりすの欠点を
解消し、釣糸、特にはりすとして必要な諸強度、
諸特性に優れ、かつ、該強度、特性がバランス良
く具備された釣糸を提供すべく種々検討を重ねた
結果、ブチレンテレフタレート重合体、又はブチ
レンテレフタレート重合体とエチレンテレフタレ
ート重合体を特定割合で混合した重合体組成物を
用い、特定の伸び率と弾性率との関係を有するモ
ノフイラメントとして釣糸とすれば問題を解決し
得ることを見出し、本発明を完成した。
すなわち、本発明の要旨はブチレンテレフタレ
ート重合体70〜100重量％、エチレンテレフタレ
ート重合体０〜30重量％の割合で混合された重合
体組成物を成形してなるつり糸であつて、該つり
糸は太さ100〜2000デニールのモノフイラメント
で構成され、伸び率と弾性率との関係において、
伸び率が15％に至る間に弾性率が一旦低下する部
分を有することを特徴とする釣糸に存する。
本発明の釣糸は、ブチレンテレフタレート重合
体単独、もしくはブチレンテレフタレート重合体
とエチレンテレフタレート重合体との重合体混合
物からなるものである。
ブチレンテレフタレート重合体とは、重合体の
少なくとも75モル％が
FIELD OF THE INVENTION The present invention relates to fishing lines. Traditionally, the fishing line used for fishing is usually a relatively thick and strong fishing line (michiito) with a wire attached at the tip.
A thin fishing line (harisu), which is slightly smaller and stronger than this michi line, is tied together, and a fishhook is attached to this string. The present invention relates to a fishing line particularly suitable for use with this fishing rod. The characteristics of the fishing line used as a fishing line are such that if too much force is applied, the line will break before the line is cut, thus preventing the line from breaking.
It has to be slightly less strong than the fishing line, but if the fish on the hook goes wild, the line will not only be pulled, but it will also be bent or twisted. In other words, the fishing line used for Harisu is
It must have a well-balanced strength against such various stresses and properties depending on the usage conditions, such as tensile strength, knot strength, bending strength, water resistance, and bending rigidity. In other words, even if other strengths and properties are excellent, if the knot strength is low, if a hooked fish becomes violent, it will break off at the knot between the fishhook and the fishhook, and the bending strength will be low. In this case, if the fish becomes violent and bends the squirrel, it may be cut off at the bent part. It goes without saying that the properties of the fishing line used as a fishing line must be superior in all strengths to a certain level or higher on average, rather than being superior in just one particular strength or characteristic. In particular, it is necessary that the strength does not decrease in water. Conventionally, polyamide resins such as nylon 6 and nylon 6-10, which are often used as fishing lines, absorb water due to their inherent water absorption properties, resulting in a decrease in tensile strength and knot strength, making them easier to cut. In addition, since the bending rigidity is reduced (softened), there are defects such as thread entanglement. The present inventors have solved the drawbacks of the conventional fishing line, and have improved the various strengths necessary for a fishing line, especially a fishing line.
As a result of various studies in order to provide a fishing line with excellent properties and a well-balanced strength and properties, we have developed a mixture of butylene terephthalate polymer, or butylene terephthalate polymer and ethylene terephthalate polymer in a specific ratio. The present invention was completed based on the discovery that the problem could be solved by using a polymer composition and making it into a fishing line as a monofilament having a specific relationship between elongation and elastic modulus. That is, the gist of the present invention is a hanging thread formed by molding a polymer composition in which a butylene terephthalate polymer is mixed in a proportion of 70 to 100% by weight and an ethylene terephthalate polymer is mixed in a proportion of 0 to 30% by weight. is composed of monofilament with a thickness of 100 to 2000 deniers, and the relationship between elongation rate and elastic modulus is
The fishing line is characterized by having a portion where the elastic modulus temporarily decreases while the elongation rate reaches 15%. The fishing line of the present invention is made of a butylene terephthalate polymer alone or a polymer mixture of a butylene terephthalate polymer and an ethylene terephthalate polymer. Butylene terephthalate polymer means that at least 75 mole percent of the polymer is
【式】の繰り返しブチ
レンテレフタレート単位を含有する重合体であつ
て、共重合体の場合は、その25モル％、好ましく
は15モル％までの範囲でブチレンテレフタレート
重合体のグリコール部分をエチレングリコール、
ジエチレングリコール、プロパン−１・３−ジオ
ール、ポリテトラメチレングリコール、ポリエチ
レングリコール、ポリプロピレングリコール、
１・４−ヒドロキシメチルシクロヘキサン等に変
えたものや、あるいは共重合体の25モル％、好ま
しくは15モル％までの範囲でブチレンテレフタレ
ート重合体のテレフタル酸部分をイソフタル酸、
パラヒドロキシ安息香酸、バニリン酸、ビス安息
香酸、ナフタレン−１・４−ジカルボン酸、ナフ
タレン−２・６−ジカルボン酸、アジピン酸、セ
バチン酸、デカン−１・10−ジカルボン酸等に変
えたもの等を云う。
また、エチレンテレフタレート重合体とは、重
合体の少なくとも75モル％、好ましくは85モル％
がIn the case of a copolymer containing repeating butylene terephthalate units of the formula, the glycol portion of the butylene terephthalate polymer may be ethylene glycol or
Diethylene glycol, propane-1,3-diol, polytetramethylene glycol, polyethylene glycol, polypropylene glycol,
1,4-hydroxymethylcyclohexane, etc., or the terephthalic acid moiety of the butylene terephthalate polymer is replaced with isophthalic acid, up to 25 mol%, preferably up to 15 mol% of the copolymer.
Parahydroxybenzoic acid, vanillic acid, bisbenzoic acid, naphthalene-1,4-dicarboxylic acid, naphthalene-2,6-dicarboxylic acid, adipic acid, sebacic acid, decane-1,10-dicarboxylic acid, etc. says. Also, ethylene terephthalate polymer means at least 75 mol%, preferably 85 mol% of the polymer.
but
【式】の繰り返しエチ
レンテレフタレート単位を含有する重合体であつ
て、共重合体の場合は、その25モル％、好ましく
は15モル％までの範囲でエチレンテレフタレート
重合体のグリコール部分をジエチレングリコー
ル、プロパン−１・３−ジオール、ブタン−１・
４−ジオール、ポリテトラメチレングリコール、
ポリエチレングリコール、ポリプロピレングリコ
ール、１・４−ヒドロキシメチルシクロヘキサン
等に変えたものや、あるいは共重合体の25モル
％、好ましくは15モル％までの範囲でエチレンテ
レフタレート重合体のテレフタル酸部分を前述し
たと同様の酸に変えたもの等を云う。
またこれらのブチレンテレフタレート重合体や
ブチレンテレフタレート重合体とエチレンテレフ
タレート重合体との重合体混合物には酸化防止
剤、紫外線吸収剤、熱安定剤、帯電防止剤、難燃
剤、染料、顔料、有機充填剤、無機充填剤等を添
加、混合して用いても良いことは勿論である。
本発明の釣糸は上述したようなブチレンテレフ
タレート重合体とエチレンテレフタレート重合体
との重合体混合物より構成されるが、その割合は
ブチレンテレフタレート重合体70〜100重量％、
好ましくは85〜95重量％、エチレンテレフタレー
ト重合体０〜30重量％、好ましくは５〜15重量％
である。
上述の範囲よりエチレンテレフタレート重合体
を多量に用いると耐屈曲性が低下し、また少量で
あれば引張強度が低下する。
本発明の釣糸は上述のような重合体混合物を押
出成形等の方法により通常は断面形状が円形のモ
ノフイラメントに成形する。モノフイラメントの
太さとしては100〜2000デニール(d)、より好まし
くは150〜1000dである。
また、本発明に用いるブチレンテレフタレート
重合体は、所望の強度や特性を得るため、少くと
も0.8の固有粘度を有することが望ましく、より
望ましくは少くとも0.5の固有粘度を有するもの
である。また、エチレンテレフタレート重合体は
少くとも0.5の固有粘度を有することが望まし
い。
固有粘度〔η〕は、上記重合体をテトラクロロ
エタン37.5重合部とフエノール62.5重合部とから
なる溶剤中に１重合部の割合で溶解し、
Ｃ：溶液100ml当りの重合体のｇ数の式により求
められたものである。
また、ブチレンテレフタレート重合体の密度も
得ようとする釣糸の物性に影響を与える一要素と
なるが、この密度としては、望ましくは1.3〜1.4
ｇ／cm3、より望ましくは1.3〜1.35ｇ／cm3であ
り、エチレンテレフタレート重合体の密度は1.3
〜1.4ｇ／cm3であることが望ましい。
密度（ｇ／cm3）はASTM1505に示されている
「密度勾配法」により測定した価である。
上記の密度は使用する重合体の結晶化度により
変化し、結晶化が高ければ、高い密度を示す。
すなわち、密度と結晶化度には相関関係が成立
し、結晶化度（％）は次式
結晶化度（％）＝Ｐｓ−Ｐａ／Ｐｃ−Ｐａ×100
Ps：結晶化度を得ようとする試料の密度
Pa：同一重合体（混合物）における結晶化度０
％の際の密度
Pc：同一重合体（混合物）における結晶化度100
％の際の密度（単位格子をＸ線回折で得、これ
より計算した結晶の密度）
により計算される。
本発明の釣糸に用いられるブチレンテレフタレ
ート重合体もしくはブチレンテレフタレート重合
体とエチレンテレフタレート重合体との重合体混
合物からなるモノフイラメントの結晶化度は、望
ましくは15％以上、より望ましくは20％以上であ
る。
上記の重合体混合物からなるモノフイラメント
はその配向、結晶化の状態により諸物性が変化す
る。モノフイラメントに分子配向を行なわせると
高度に結晶化し引張強度、結節強度に優れたもの
となる。
更に本発明の釣糸を構成するブチレンテレフタ
レート重合体とエチレンテレフタレート重合体と
の重合体混合物を成形してなるモノフイラメント
は、上述した延伸により特異の弾性回復率を示
す。
すなわち、このようなモノフイラメントは、伸
び率と弾性率との関係において、伸び率が15％に
至る間に弾性率が一旦低下する部分を有するもの
となる。
また、このモノフイラメントはヤング率が260
〜700Kg／mm2程度となり、しかも引張強度が４
ｇ／ｄ以上（JIS−L0702に示された方法により
測定）結節強度が３ｇ／ｄ以上（JIS−L0702に
順ずる方法により測定）と云う高い値を示す。
更に本発明の釣糸の特異の性質として極めて高
い耐屈曲性を有する。
耐屈曲性は、測定するモノフイラメントの一端
に200ｇの錘りを取付け30cm上部をチヤツクで挾
持し、該チヤツクの挾持部の先端を中心に垂直位
置から両側に90゜（水平位置）まで180゜回転
（半回転）を繰り返し、（往復１秒）モノフイラメ
ントが切断するまでの往復回数を数え、その数で
表わす。
この耐屈性試験の結果、0.2mm±0.02mmのモノ
フイラメントでは、ナイロン６は5000〜7000回、
エチレンテレフタレート重合体は1000〜2000回で
あるのに対し、ブチレンテレフタレート重合体単
独では800000回以上、ブチレンテレフタレート重
合体とエチレンテレフタレート重合体との８：２
の重合体混合物の場合は、50000〜70000回と云う
数十倍の耐屈曲性を示す。
このような特異の弾性及び耐屈曲性は魚が掛か
つた際に魚が暴れた場合の直接的な引張と屈曲に
よる糸切れを良好に防止することは云うまでもな
い。
本発明の釣糸は一軸延伸されたモノフイラメン
トからなるものであるが、その製法の一例につい
て述べれば、まず、ブチレンテレフタレート重合
体単独、もしくはブチレンテレフタレート重合体
とエチレンテレフタレート重合体とを所定割合で
混合した重合体混合物を押出成形機を用いて樹脂
温250〜300℃で溶融混練した後、ダイスから断面
形状が円形で太さ0.2〜1.2mmのモノフイラメント
状に押出す。押出されたモノフイラメントはダイ
スの直後に設けられた冷却槽（通常０〜90℃の水
が満されている。）により冷却固化し、実質的に
無定形（結晶化度９％以下）のモノフイラメント
を得る。
この実質的に無定形のブチレンテレフタレート
重合体又はブチレンテレフタレート重合体とエチ
レンテレフタレート重合体の重合体混合物を成形
してなるモノフイラメントを、45〜100℃の温水
浴中等で３〜４倍に延伸し、更に150〜250℃の加
熱空気中で1.05〜2.5倍好ましくは1.1〜2.1倍に二
段延伸する。その後、170〜250℃の加熱空気中で
0.85〜1.1倍好ましくは0.9〜1.0倍の倍率で熱処理
を行なう。
上記の延伸は通常２〜３段に分けて行なわれ、
その全延伸倍率は4.5倍以上であり、延伸時に切
断したり、他の物性を低下させたりしなければ可
及的に高倍率が望ましいが、通常は5.5倍程度ま
でであり、延伸終了時のモノフイラメントの結晶
化度は20〜30％であるのが好ましい。
このようにして得られた本発明の釣糸を構成す
るモノフイラメントは、伸び率と弾性率との関係
において、伸び率が15％に至る間に弾性率が一旦
低下する部分を有するものとなり、例えば魚が釣
針にかかつて暴れた場合、ある程度の力以上の引
張力が加わると釣糸が伸び初め、伸び率数％まで
は極めて軽くゴム状の伸びを示し、その後伸び率
の増加に伴い弾性率が大きくなる性質を示す。
このような伸び率と弾性率の関係は釣糸自身が
魚がかかつた際のシヨツクを良好に緩和するもの
であり大変特異の好ましい性質である。
また、本発明の釣糸を構成するモノフイラメン
トは10％伸長における弾性回復率が90％以上であ
り、引張強度４ｇ／ｄ以上、結節強度３ｇ／ｄ以
上、屈曲強度20000回以上（300dにおいて）のも
のとなり、更に、ブチレンテレフタレート重合体
又はブチレンテレフタレート重合体とエチレンテ
レフタレート重合体との重合体混合物からなるも
のであるから、水中で吸水して強度低下を起すよ
うなこともなく、しかも弾性回復率に優れてい
る、すなわち高弾性を有するものであるから魚が
暴れ回る際の引張、衝撃、屈曲等の応力を良好に
吸収し釣果を向上させるものである。
以下に実施例を挙げ本発明を更に説明するが本
発明はその要旨を越えない限り以下の実施例に限
定されるものではない。
実施例 １
ブチレンテレフタレート重合体（密度：1.31
ｇ／cm3、固有粘度〔η〕：1.0、三菱化成工業株
式会社製、ノバドウール5010）（ノバドウールは
三菱化成工業株式会社の登録商標）90重量部、エ
チレンテレフタレート重合体（密度：1.4ｇ／
cm3、固有粘度〔η〕：0.67、三菱化成工業株式会
社製、ノバペツト1065）（ノバペツトは三菱化成
工業株式会社の登録商標）10重量部を混合し、押
出成形機により溶融混練した後直径0.7mmの開孔
を有するダイスから、樹脂温270℃で押出し、ダ
イスの直後ダイス間距離50mmに設けられた４℃の
水が満された冷却槽を通して引き取り結晶化度２
％の実質的に無定形のモノフイラメントを得た。
得られたモノフイラメントを90℃の温水浴中で
3.5倍に延伸し、更に180℃の加熱空気中で1.46倍
に延伸した。次いで200℃の加熱空気中で0.98倍
の倍率で熱処理を行なつた。得られたモノフイラ
メントは直径0.2mm結晶化度50％のものであり、
10％伸長における弾性回復率93％、耐屈曲性
90000回、引張強度4.5ｇ／ｄ、結節強度3.5ｇ／
ｄ、であり、釣糸として用いて大変良好なバラン
スの良い強度、物性を備えたものであつた。
また、伸び率と弾性率との関係を測定した結果
添付第１図に示すような関係を示し、伸び率約５
％まで極めて軽く伸びその後また伸びなくなると
云う特異の性質を示し、釣糸として好適なもので
あることが分つた。なお、第１図において、
PBTはブチレンテレフタレート重合体を、また
PETはエチレンテレフタレート重合体を示す。
実施例 ２
ブチレンテレフタレート重合体とエチレンテレ
フタレート重合体との混合割合を80：20としたほ
かは実施例１と同様にしてモノフイラメントを得
た。得られたモノフイラメントは耐屈曲性60000
回以上引張強度4.8ｇ／ｄ、結節強度3.0ｇ／ｄと
釣糸として用いて良好なものであり、伸び率と弾
性率との関係も第１図に示したように大変良好な
ものであつた。In the case of a copolymer containing repeating ethylene terephthalate units of the formula, the glycol portion of the ethylene terephthalate polymer can be added to diethylene glycol, propane, etc. in an amount of up to 25 mol%, preferably 15 mol%. 1,3-diol, butane-1.
4-diol, polytetramethylene glycol,
Polyethylene glycol, polypropylene glycol, 1,4-hydroxymethylcyclohexane, etc., or the terephthalic acid moiety of the ethylene terephthalate polymer in the range of up to 25 mol%, preferably 15 mol% of the copolymer. It refers to those that have been changed to similar acids. In addition, these butylene terephthalate polymers and polymer mixtures of butylene terephthalate polymers and ethylene terephthalate polymers contain antioxidants, ultraviolet absorbers, heat stabilizers, antistatic agents, flame retardants, dyes, pigments, and organic fillers. Of course, inorganic fillers and the like may be added and mixed. The fishing line of the present invention is composed of a polymer mixture of butylene terephthalate polymer and ethylene terephthalate polymer as described above, and the proportion thereof is 70 to 100% by weight of butylene terephthalate polymer,
Preferably 85-95% by weight, 0-30% by weight of ethylene terephthalate polymer, preferably 5-15% by weight
It is. If the ethylene terephthalate polymer is used in a larger amount than the above-mentioned range, the bending resistance will decrease, and if it is used in a smaller amount, the tensile strength will decrease. The fishing line of the present invention is produced by molding the above-mentioned polymer mixture into a monofilament, usually having a circular cross-sectional shape, by a method such as extrusion molding. The thickness of the monofilament is 100 to 2000 denier (d), more preferably 150 to 1000 d. Further, the butylene terephthalate polymer used in the present invention preferably has an intrinsic viscosity of at least 0.8, more preferably at least 0.5, in order to obtain desired strength and properties. It is also desirable that the ethylene terephthalate polymer have an intrinsic viscosity of at least 0.5. Intrinsic viscosity [η] is calculated by dissolving the above polymer at a ratio of 1 polymerization part in a solvent consisting of 37.5 polymerization parts of tetrachloroethane and 62.5 polymerization parts of phenol. C: Calculated using the formula for the number of grams of polymer per 100 ml of solution. In addition, the density of the butylene terephthalate polymer is also a factor that affects the physical properties of the fishing line, and this density is preferably 1.3 to 1.4.
g/cm 3 , more preferably 1.3 to 1.35 g/cm 3 , and the density of the ethylene terephthalate polymer is 1.3
It is desirable that it be ~1.4 g/cm 3 . Density (g/cm 3 ) is a value measured by the "density gradient method" specified in ASTM1505. The above density varies depending on the degree of crystallinity of the polymer used, and the higher the crystallinity, the higher the density. In other words, there is a correlation between density and crystallinity, and the crystallinity (%) can be calculated using the following formula: Crystallinity (%) = Ps-Pa/Pc-Pa x 100 Ps: Crystallinity Sample density Pa: Crystallinity of the same polymer (mixture) is 0
Density Pc in %: Crystallinity of the same polymer (mixture) 100
% density (crystal density calculated from a unit cell obtained by X-ray diffraction). The crystallinity of the monofilament made of a butylene terephthalate polymer or a polymer mixture of a butylene terephthalate polymer and an ethylene terephthalate polymer used in the fishing line of the present invention is preferably 15% or more, more preferably 20% or more. . A monofilament made of the above polymer mixture has various physical properties depending on its orientation and crystallization state. When a monofilament is subjected to molecular orientation, it becomes highly crystallized and has excellent tensile strength and knot strength. Furthermore, the monofilament formed from a polymer mixture of a butylene terephthalate polymer and an ethylene terephthalate polymer, which constitutes the fishing line of the present invention, exhibits a unique elastic recovery rate when stretched as described above. That is, in the relationship between the elongation rate and the elastic modulus, such a monofilament has a portion where the elastic modulus temporarily decreases while the elongation rate reaches 15%. In addition, this monofilament has a Young's modulus of 260
~700Kg/ mm2 , and the tensile strength is 4
g/d or more (measured by the method shown in JIS-L0702) The nodule strength shows a high value of 3 g/d or more (measured by the method shown in JIS-L0702). Furthermore, the fishing line of the present invention has extremely high bending resistance as a unique property. For bending resistance, attach a 200g weight to one end of the monofilament to be measured, clamp the 30cm top part with a chuck, and bend the chuck from a vertical position to 90° on both sides (horizontal position) to 180° around the tip of the clamping part of the chuck. Repeat the rotation (half rotation), count the number of reciprocations until the monofilament breaks (reciprocating for 1 second), and express the number of reciprocations. As a result of this bending resistance test, with a monofilament of 0.2 mm ± 0.02 mm, nylon 6 was
Ethylene terephthalate polymer has 1000 to 2000 times, but butylene terephthalate polymer alone has more than 800000 times, and the ratio of butylene terephthalate polymer to ethylene terephthalate polymer is 8:2.
In the case of a polymer mixture of , the bending resistance is several tens of times higher, 50,000 to 70,000 times. Needless to say, such unique elasticity and bending resistance effectively prevent the thread from breaking due to direct tension and bending when the fish is hooked and becomes violent. The fishing line of the present invention is made of a uniaxially stretched monofilament, and an example of its manufacturing method is first to mix a butylene terephthalate polymer alone or a butylene terephthalate polymer and an ethylene terephthalate polymer at a predetermined ratio. The resulting polymer mixture is melt-kneaded using an extruder at a resin temperature of 250 to 300°C, and then extruded from a die into a monofilament having a circular cross-section and a thickness of 0.2 to 1.2 mm. The extruded monofilament is cooled and solidified in a cooling tank (usually filled with water at 0 to 90°C) installed immediately after the die, and becomes a substantially amorphous monofilament (crystallinity of 9% or less). Get filament. A monofilament formed by molding this substantially amorphous butylene terephthalate polymer or a polymer mixture of butylene terephthalate polymer and ethylene terephthalate polymer is stretched 3 to 4 times in a hot water bath at 45 to 100°C. Then, the film is further stretched in two stages by 1.05 to 2.5 times, preferably 1.1 to 2.1 times, in heated air at 150 to 250°C. Then in heated air at 170-250℃
Heat treatment is performed at a magnification of 0.85 to 1.1 times, preferably 0.9 to 1.0 times. The above stretching is usually carried out in two to three stages,
The total stretching ratio is 4.5 times or more, and as long as it does not cause breakage or deterioration of other physical properties during stretching, it is desirable to have as high a ratio as possible, but it is usually up to about 5.5 times, and at the end of stretching Preferably, the crystallinity of the monofilament is between 20 and 30%. The monofilament constituting the fishing line of the present invention obtained in this way has a portion where the elastic modulus temporarily decreases while the elongation rate reaches 15% in the relationship between the elongation rate and the elastic modulus, for example. When a fish is caught on a fishing hook and becomes violent, the fishing line begins to stretch when a tensile force beyond a certain level is applied, exhibiting extremely light and rubber-like elongation until the elongation rate is a few percent, and then as the elongation rate increases, the elastic modulus decreases. Shows the property of becoming larger. Such a relationship between the elongation rate and the elastic modulus is a very unique and desirable property that allows the fishing line itself to satisfactorily cushion the shock when caught by a fish. Furthermore, the monofilament constituting the fishing line of the present invention has an elastic recovery rate of 90% or more at 10% elongation, a tensile strength of 4 g/d or more, a knot strength of 3 g/d or more, and a bending strength of 20,000 times or more (at 300 d). Furthermore, since it is made of a butylene terephthalate polymer or a polymer mixture of a butylene terephthalate polymer and an ethylene terephthalate polymer, it does not absorb water in water and cause a decrease in strength, and has a low elastic recovery rate. In other words, since it has high elasticity, it can absorb stresses such as tension, impact, and bending when fish move wildly, improving fishing results. The present invention will be further explained with reference to Examples below, but the present invention is not limited to the following Examples unless the gist of the invention is exceeded. Example 1 Butylene terephthalate polymer (density: 1.31
g/cm 3 , intrinsic viscosity [η]: 1.0, manufactured by Mitsubishi Chemical Industries, Ltd., Novad Wool 5010) (Novad Wool is a registered trademark of Mitsubishi Chemical Industries, Ltd.) 90 parts by weight, ethylene terephthalate polymer (density: 1.4 g/
cm 3 , intrinsic viscosity [η]: 0.67, Novapet 1065 (manufactured by Mitsubishi Chemical Industries, Ltd.) (Novapet is a registered trademark of Mitsubishi Chemical Industries, Ltd.) was mixed and melted and kneaded using an extruder to give a diameter of 0.7. The resin is extruded from a die with a hole of 270°C, and the crystallinity is 2.
% of substantially amorphous monofilament was obtained. The obtained monofilament was placed in a hot water bath at 90°C.
It was stretched 3.5 times, and further stretched 1.46 times in heated air at 180°C. Next, heat treatment was performed in heated air at 200°C at a magnification of 0.98. The obtained monofilament had a diameter of 0.2 mm and a crystallinity of 50%.
Elastic recovery rate of 93% at 10% elongation, bending resistance
90000 times, tensile strength 4.5g/d, knot strength 3.5g/
d, and it had well-balanced strength and physical properties that made it very suitable for use as a fishing line. In addition, as a result of measuring the relationship between elongation rate and elastic modulus, the relationship shown in attached Figure 1 was obtained, and the elongation rate was approximately 5.
It was found to be suitable as a fishing line because it exhibits the unique property of stretching extremely lightly up to 100% and then not stretching again. In addition, in Figure 1,
PBT is butylene terephthalate polymer, also
PET stands for ethylene terephthalate polymer. Example 2 A monofilament was obtained in the same manner as in Example 1, except that the mixing ratio of the butylene terephthalate polymer and the ethylene terephthalate polymer was 80:20. The resulting monofilament has a bending resistance of 60000
It had a tensile strength of 4.8 g/d and a knot strength of 3.0 g/d, making it suitable for use as a fishing line, and the relationship between elongation and elastic modulus was also very good, as shown in Figure 1. .
第１図は本発明の実施例１〜３におけるモノフ
イラメントの伸び率（％）と弾性率（Kg／mm2）と
の関係を示すものである。
FIG. 1 shows the relationship between elongation (%) and elastic modulus (Kg/mm 2 ) of monofilaments in Examples 1 to 3 of the present invention.
Claims (1)
レフタレート重合体が最高30重量％までの割合で
混合された重合体混合物を成形してなるつり糸で
あつて、該つり糸は太さ100〜2000デニールのモ
ノフイラメントで構成され、伸び率と弾性率との
関係において、伸び率が15％に至る間に弾性率が
一旦低下する部分を有することを特徴とする釣
糸。 ２ 重合体組成物は、ブチレンテレフタレート重
合体85〜95重量％、エチレンテレフタレート重合
体５〜15重量％の割合で混合された組成物である
ことを特徴とする特許請求の範囲第１項記載の釣
糸。 ３ ブチレンテレフタレート重合体は少なくとも
0.8の固有粘度を有し、エチレンテレフタート重
合体は少なくとも0.5の固有粘度を有することを
特徴とする特許請求の範囲第１項又は第２項記載
の釣糸。 ４ ブチレンテレフタレート重合体、またはエチ
レンテレフタレート重合体は1.3〜1.4ｇ／cm3の密
度を有することを特徴とする特許請求の範囲第１
項乃至第３項のいずれかに記載の釣糸。 ５ モノフイラメントは、該モノフイラメントが
切断に至るまでの伸び率が18〜25％であることを
特徴とする特許請求の範囲第１項乃至第４項のい
ずれかに記載の釣糸。 ６ モノフイラメントは260〜700Kg／mm2のヤング
率を有するものであることを特徴とする特許請求
の範囲第１項乃至第５項のいずれかに記載の釣
糸。 ７ モノフイラメントは引張強度が４ｇ／ｄ以上
であり、結節強度が３ｇ／ｄ以上であることを特
徴とする特許請求の範囲第１項乃至第６項のいず
れかに記載の釣糸。 ８ モノフイラメントは軸方向に4.5〜6.0倍に一
軸延伸されていることを特徴とする特許請求の範
囲第１項乃至第７項のいずれかに記載の釣糸。 ９ モノフイラメントは少なくとも15％結晶化し
ていることを特徴とする特許請求の範囲第１項乃
至第８項のいずれかに記載の釣糸。[Scope of Claims] 1. A hanging thread formed by molding a polymer mixture in which a butylene terephthalate polymer and an ethylene terephthalate polymer are mixed in a proportion of up to 30% by weight, the hanging thread having a thickness of 100 to 100% by weight. A fishing line composed of a 2000 denier monofilament and characterized in that, in the relationship between elongation rate and elastic modulus, it has a portion where the elastic modulus temporarily decreases while the elongation rate reaches 15%. 2. The polymer composition according to claim 1, wherein the polymer composition is a mixture of 85 to 95% by weight of butylene terephthalate polymer and 5 to 15% by weight of ethylene terephthalate polymer. fishing line. 3 The butylene terephthalate polymer is at least
A fishing line according to claim 1 or 2, characterized in that it has an intrinsic viscosity of 0.8, and the ethylene tereftate polymer has an intrinsic viscosity of at least 0.5. 4. Claim 1, wherein the butylene terephthalate polymer or ethylene terephthalate polymer has a density of 1.3 to 1.4 g/cm 3
The fishing line according to any one of Items 1 to 3. 5. The fishing line according to any one of claims 1 to 4, wherein the monofilament has an elongation rate of 18 to 25% before breaking. 6. The fishing line according to any one of claims 1 to 5, wherein the monofilament has a Young's modulus of 260 to 700 Kg/mm 2 . 7. The fishing line according to any one of claims 1 to 6, wherein the monofilament has a tensile strength of 4 g/d or more and a knot strength of 3 g/d or more. 8. The fishing line according to any one of claims 1 to 7, wherein the monofilament is uniaxially stretched 4.5 to 6.0 times in the axial direction. 9. A fishing line according to any one of claims 1 to 8, characterized in that the monofilament is at least 15% crystallized.