JPS6228298A - Pen point made of synthetic resin - Google Patents
Pen point made of synthetic resinInfo
- Publication number
- JPS6228298A JPS6228298A JP60168840A JP16884085A JPS6228298A JP S6228298 A JPS6228298 A JP S6228298A JP 60168840 A JP60168840 A JP 60168840A JP 16884085 A JP16884085 A JP 16884085A JP S6228298 A JPS6228298 A JP S6228298A
- Authority
- JP
- Japan
- Prior art keywords
- synthetic resin
- pen
- nib
- reinforcing
- pen point
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】 (産業上の利用分野) この発明は合成樹脂製のペン先に関する。[Detailed description of the invention] (Industrial application field) This invention relates to a pen nib made of synthetic resin.
(従来の技術)
合成樹脂製ペン先を補強するため、金属や種類の異なる
合成樹脂を補強体として使用することは2例えば特開昭
47−41930号公報に開示されている。ちなみに、
該公報における特許請求の範囲の記載は、「毛細管作用
を為すスリットを有“するか又は有しない著しく細径の
杆体を金属又は硬質合成樹脂等の著しく薄手にして且つ
細径の耐摩耗性パイプに圧入し且つ杆体の外面とパイプ
の内面間に毛細管作用を為す間隙を形成することを特徴
とするペン先。」となっている。(Prior Art) In order to reinforce a synthetic resin pen nib, the use of metal or different types of synthetic resin as a reinforcing body is disclosed in, for example, Japanese Patent Laid-Open No. 47-41930. By the way,
The scope of claims in this publication is ``A wear-resistant pipe of extremely thin diameter made of extremely thin rods made of metal or hard synthetic resin, with or without slits for capillary action.'' A pen nib, which is press-fitted into the rod and forms a gap between the outer surface of the rod and the inner surface of the pipe to create a capillary action. ”.
(発明が解決しようとする問題点) 補強体に求められる条件は次のとおりである。(Problem that the invention attempts to solve) The conditions required for the reinforcement are as follows.
O合成樹脂特有の滑らかな書き味を維持すること。O To maintain the smooth writing feel characteristic of synthetic resin.
0筆圧が加えられたとき、撓みにぐ〈、かつ。When 0 pen pressure is applied, there is no deflection.
折れにくくすること。Make it difficult to break.
O耐摩耗性を向上すること。O Improving wear resistance.
0筆跡を安定させるため、自らのインキ濡れ性が良いこ
と。0 Good ink wettability to stabilize handwriting.
O補強される部分との一体化成形が容易なこと。O Easily molded into one piece with the part to be reinforced.
しかるに、これら全てを同時に満足する補強体は今迄知
られていない。例えば、金属を補強体として使用すると
、何よりも合成樹脂特有の書き味が損われてしまう。ま
た、ポリアセタールやポリアミドなど通常使用されてい
るものに対して他の種類の合成樹脂を補強体として使用
することも2例えば、耐摩耗性を向上させること一つを
とってみても9選ぶことのできるものは限られてしまう
。However, until now, no reinforcing body has been known that satisfies all of these requirements at the same time. For example, if metal is used as a reinforcing material, the writing quality unique to synthetic resin will be impaired. In addition, it is also possible to use other types of synthetic resins as reinforcing materials for commonly used materials such as polyacetal and polyamide. What you can do is limited.
換言すると、従来の補強体を有する合成樹脂製ペン先は
、補強体による良好な補強がなされていなかった訳であ
る。In other words, conventional synthetic resin pen nibs with reinforcing bodies have not been adequately reinforced by the reinforcing bodies.
(問題点を解決するための手段) 本発明者らが鋭意研究の結果に知見したのは。(Means for solving problems) The inventors of the present invention have discovered the following as a result of intensive research.
ポリエーテルエーテルケトンを補強体として使用すれば
、前述した全ての条件を満足することができ、従って、
良好な補強がなされた合成樹脂製ペン先たらしめられる
ことである。即ち。If polyetheretherketone is used as a reinforcing body, all the conditions mentioned above can be satisfied, and therefore,
The pen nib is made of synthetic resin and has good reinforcement. That is.
本発明は、補強体を有する合成樹脂製ペン先であって、
前記補強体がポリエーテルエーテルケトンよシなること
を特徴とする合成樹脂製ペン先を要旨とする。The present invention is a synthetic resin pen nib having a reinforcing body,
The gist of the present invention is a synthetic resin pen nib, characterized in that the reinforcing body is made of polyetheretherketone.
(実施例)
添付第1図、第2図に第1実施例を示す。ペン先Aは、
全体として円柱状の形状を有するペン先本体1と、この
ペン先本体1の外側壁を覆い、ペン先本体1とともに先
端整形された補強体2とよりなっている。ここで、ペン
先本体1はポリアセタールとかポリアミドなどの合成樹
脂よりなり、補強体2はポリエーテルエーテルケトンよ
りなる。尚、参照符号3はインキ通路である。(Example) A first example is shown in the attached FIGS. 1 and 2. Pen nib A is
The pen tip body 1 is composed of a pen tip body 1 having a cylindrical shape as a whole, and a reinforcing body 2 which covers the outer wall of the pen tip body 1 and has a tip shaped together with the pen tip body 1. Here, the pen tip body 1 is made of synthetic resin such as polyacetal or polyamide, and the reinforcing body 2 is made of polyether ether ketone. Note that reference numeral 3 is an ink passage.
この例は最近特に細径化の傾向にある一般的な合成樹脂
製ペン先の一例を示している。即ち補強体による補強が
特に切望されているものの一例である。This example shows an example of a general synthetic resin nib, which has recently become particularly thin in diameter. That is, this is an example of a material in which reinforcement by a reinforcing body is particularly desired.
しかし、ペン先形状は円柱状でなくてもよいし、tた。However, the shape of the pen tip may not be cylindrical.
補強体も外壁に存在しなければならない訳でもない。こ
の−例を第5図、第4図に示す第2実施例で説明する。The reinforcement body also does not have to be present on the outer wall. This example will be explained with reference to a second embodiment shown in FIGS. 5 and 4.
ペン先Bは、全体として4角柱状の形状を有するペン先
本体4と。The pen tip B includes a pen tip main body 4 that has a quadrangular prism shape as a whole.
このペン先本体4の2つの幅狭な面の近傍に埋込状態で
位置する補強体5とよりなっている。A reinforcing body 5 is embedded in the vicinity of the two narrow surfaces of the pen tip body 4.
尚、参照符号6はインキ通路であシ、また。ペン先Bの
先部は4つの面をテーパー化して、補強体5が両側端に
位置するようなしであるが。Incidentally, reference numeral 6 is an ink passage. The tip of the pen nib B has four tapered surfaces so that the reinforcing bodies 5 are located at both ends.
これは、このペン先Bが幅広にして一定の筆跡を得られ
ることを意図したものであって、長期にわたる筆跡安定
性を維持する上で好ましいためである。This is because the pen tip B is intended to be wide enough to obtain a constant handwriting, which is preferable for maintaining handwriting stability over a long period of time.
このように、ポリエーテルエーテルケトンよりなる補強
体は適宜形状、適宜配置状態で使用される。In this way, the reinforcing body made of polyether ether ketone is used in an appropriate shape and in an appropriate arrangement.
(発明の効果)
前述した第1実施例のペン先人を製造する場合の一例を
通して説明する。(Effects of the Invention) An example of manufacturing the nib of the first embodiment described above will be explained.
先端に151m径のダイスを付けた押出成形機よシ溶融
したジュラコンU10−01(ポリプラスチックス■製
のポリアセタール)を押出し。Molten Duracon U10-01 (polyacetal manufactured by Polyplastics ■) was extruded using an extrusion molding machine equipped with a 151 m diameter die at the tip.
引っ張りながら冷却固化して直径約0.5 mの細線状
物を得た。ペン先本体1の基材であり、断面測定したと
ころ、インキ通路6の全体とじての直径は約0.35鵡
であった。次に、外径0.8態内径α5顛のリング状の
吐出口を有するダイスを付けた押出成形機より溶融した
ピクトレックス450G(インペリアルケミカルインダ
ストリー社製のポリエーテルエーテルケトン〕ヲ押出し
、引っ張りながら冷却固化した。このとき。The mixture was cooled and solidified while being pulled to obtain a thin wire-like material with a diameter of about 0.5 m. This is the base material of the pen nib body 1, and when the cross section was measured, the overall diameter of the ink passage 6 was about 0.35 mm. Next, molten Pictrex 450G (polyether ether ketone manufactured by Imperial Chemical Industries) was extruded using an extruder equipped with a die having a ring-shaped discharge port with an outer diameter of 0.8 and an inner diameter of α5, and while being pulled. Cooled and solidified.At this time.
ペン先本体1の基材であるポリアセタール類の細線状物
はポリエーテルエーテルケトンの内側に配しておいた。A thin polyacetal filament, which is the base material of the pen nib body 1, was placed inside the polyetheretherketone.
両者はポリエーテルエーテルケトンの冷却固化の途中段
階で互いに接触し合い、最終的に得た一体化物の径は約
0.6脇であった。これを切断し一端を半球状に整形し
てペン先人としたときの評価結果を表−1に示す。Both came into contact with each other during the cooling and solidification of the polyether ether ketone, and the diameter of the finally obtained integrated product was about 0.6 mm. Table 1 shows the evaluation results when this was cut and one end was shaped into a hemispherical shape to be used as a nib.
尚2表−1の中で比較例とあるのは、インキ通路の形状
を含め、全体形状・寸法をペン先人と同様にし、ただ上
記使用のポリアセタールのみで作製したペン先について
のものである。In addition, the comparative example in Table 2-1 refers to a pen nib whose overall shape and dimensions, including the shape of the ink passage, are the same as that of the nib, but made only of the polyacetal used above. .
表−1
(注1)値は、荷重100/−、筆記角度60゜でのも
のである。Table 1 (Note 1) Values are at a load of 100/- and a writing angle of 60°.
(注2)値は、ペン先突出長を1鶏にしてホルダーにセ
ットし、筆記面に対し1001の荷重をかけてすべわが
発生しないよう垂直に維持しながら、筆記面に対し平行
な荷重を5CIPかけたとき、ペン先先端が元の状態か
ら撓んだ量を示す。(Note 2) The value is when the pen is set in the holder with the protruding length of the pen tip set to 1, and a load of 1001 is applied to the writing surface, maintaining it vertically to prevent slippage, and applying a load parallel to the writing surface. This indicates the amount by which the tip of the pen tip flexes from its original state when 5CIP is applied.
(注3)値は、ペン先突出長を1鶏にしてホルダーにセ
ットし、筆記角度60°で折れるまでの最大荷重を示す
。(Note 3) Values indicate the maximum load required until the pen breaks at a writing angle of 60° when the pen tip is set in a holder with one length of protrusion.
(注4)値は、荷重100J’、 筆記速度7 cs
/秒でトレー/ングベーバー上を500m移動させたと
きのものである。(Note 4) Values are load 100J', writing speed 7cs
This is when moving 500 m on a tray/ngber at a speed of 500 m per second.
(注5)値は、荷ffi 100 、P 、筆記角度6
00゜筆記速度7(J/秒で上質紙に筆記したときの筆
跡を拡大観察しながら、筆跡の幅方向の端部における不
鮮明部の幅をランダムに50回測定し、その標準偏差を
計算したものである。(Note 5) Values are load ffi 100, P, writing angle 6
While observing the handwriting written on high-quality paper at 00° writing speed 7 (J/sec) under magnification, the width of the blurred part at the end of the handwriting in the width direction was randomly measured 50 times, and the standard deviation was calculated. It is something.
上記結果より判るように1本発明のペン先は合成樹脂特
有の滑らかな書き味を維持しつつ。As can be seen from the above results, the pen nib of the present invention maintains the smooth writing feel characteristic of synthetic resin.
撓みに<<、かつ、折れにくいので筆記安定感があり、
しかも耐摩耗性に優れ、その上、得られる筆跡の安定性
も良好である。また、金属を補強体とする場合、往々に
して必要となる面倒な一体化成形をすることなく容易に
製造することもできる。It does not bend easily and does not easily break, so it provides a sense of stability when writing.
Moreover, it has excellent abrasion resistance, and the resulting handwriting is also stable. Furthermore, when the reinforcing body is made of metal, it can be easily manufactured without the troublesome integral molding that is often required.
第1図は第1実施例を示す要部縦断面図、第2図は第1
図のI−r線機断面図、第3図は第2実施例を示す要部
斜視図、第4図は第3図のH−n線機断面図である。
A、B・・・・・・ペン先 1.4・・・・・・ヘン
先本体2.5・・・・・・補強体 6,6・山・・イ
ンキ通路。Fig. 1 is a vertical sectional view of the main part showing the first embodiment, and Fig. 2 is a longitudinal sectional view of the main part showing the first embodiment.
FIG. 3 is a perspective view of essential parts showing the second embodiment, and FIG. 4 is a sectional view of the H-n line machine in FIG. 3. A, B... Pen nib 1.4... Nib body 2.5... Reinforcement body 6, 6. Mountain... Ink passage.
Claims (1)
がポリエーテルエーテルケトンよりなることを特徴とす
る合成樹脂製ペン先。A synthetic resin pen nib having a reinforcing body, characterized in that the reinforcing body is made of polyether ether ketone.