JPS614750A - Polyvinylidene fluoride polymer composition - Google Patents
Polyvinylidene fluoride polymer compositionInfo
- Publication number
- JPS614750A JPS614750A JP12621784A JP12621784A JPS614750A JP S614750 A JPS614750 A JP S614750A JP 12621784 A JP12621784 A JP 12621784A JP 12621784 A JP12621784 A JP 12621784A JP S614750 A JPS614750 A JP S614750A
- Authority
- JP
- Japan
- Prior art keywords
- polymer composition
- fluorine
- polymer
- polyvinylidene fluoride
- containing organic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は溶融成形性が良好で、優れた物性の成形物を与
えるポリ弗化ビニリデン(PV叶という)系重合体組成
物に関するものである。Detailed Description of the Invention (Industrial Field of Application) The present invention relates to a polyvinylidene fluoride (PV Kano) polymer composition that has good melt moldability and provides molded products with excellent physical properties. .
(従来技術)
PVDFは融点が160〜180°Cで比較的低く、溶
融成形可能な重合体であり、ポリオレフィン、ポリアミ
ド、ポリエステル等に比べて、比重が大きい。(Prior Art) PVDF is a melt-moldable polymer with a relatively low melting point of 160 to 180°C, and has a higher specific gravity than polyolefins, polyamides, polyesters, and the like.
表面張力が小さい、吸水率が低い、誘電率が高い。Low surface tension, low water absorption, high dielectric constant.
屈折率が低い、耐候性に優れている。難燃性であるとい
った性質を有するため、これから得られるフィルム、シ
ート、繊維等の成形物に特異な性質を与え3種々の用途
に展開されている。Low refractive index and excellent weather resistance. Because it has properties such as flame retardancy, it imparts unique properties to molded products such as films, sheets, and fibers that are obtained from it, and is used for a variety of purposes.
しかし、 pv叶底成形物物性、特に強度を十分にする
には高分子量のものを使用する必要があり。However, it is necessary to use a material with a high molecular weight in order to obtain sufficient physical properties, especially strength, of the PV molded product.
■溶融粘度が著しく高くなって、流動性が低下し。■The melt viscosity becomes significantly high and the fluidity decreases.
成形物表面に凹凸が発生しやすいこと、■流動性を上げ
るべく成形を高温で行うと、Pv叶が分解し。Irregularities are likely to occur on the surface of the molded product. ■ If molding is performed at high temperatures to increase fluidity, Pv leaves will decompose.
有毒な弗化水素ガスを発生すること等の問題がある。There are problems such as generation of toxic hydrogen fluoride gas.
このため、Pv叶の成形性を向上させるべく1種々検討
されており1例えば特公昭43−12012号公報によ
ればポリメチルメタクリレートを配合することが有効で
あるとされているが、十分満足できる段階には達してい
ないのが実状である。For this reason, various studies have been made to improve the moldability of Pv leaves.1 For example, according to Japanese Patent Publication No. 12012/1983, it is said that it is effective to blend polymethyl methacrylate, but this is not fully satisfactory. The reality is that we have not yet reached that stage.
(発明の目的) 本発明は、溶融成形性が良好で、優れた物性。(Purpose of the invention) The present invention has good melt moldability and excellent physical properties.
特に優れた強度特性を有する成形物を与えるPVDF系
重合体組成物を提供することを目的とするものである。It is an object of the present invention to provide a PVDF polymer composition that provides molded articles with particularly excellent strength properties.
(発明の構成)
本発明は上記目的を達成するもので、 pv叶系重合体
と含弗素有機ポリシロキサンとからなる重合体組成物を
要旨とするものである。(Structure of the Invention) The present invention achieves the above objects, and its gist is a polymer composition comprising a PV leaf-based polymer and a fluorine-containing organic polysiloxane.
本発明において、Pv叶系重合体としてはPv叶ホモポ
リマーのほか、弗化ビニリデンを主成分(80重量%以
上が好ましい。)とし、これにテトラフルオロエチレン
、モノクロロトリフルオロエチル7、 弗化ビニル、ヘ
キサフルオロプロピレン、パーフルオロイソプロポキシ
エチレンなどを共重合成分としたPVDF系コポリマー
が用いられる。In the present invention, in addition to the Pv leaf homopolymer, the Pv leaf-based polymer contains vinylidene fluoride as a main component (preferably 80% by weight or more), in addition to tetrafluoroethylene, monochlorotrifluoroethyl 7, and vinyl fluoride. , hexafluoropropylene, perfluoroisopropoxyethylene, and the like are used as PVDF-based copolymers.
そして、十分な強度特性を発揮させるためには。And in order to demonstrate sufficient strength characteristics.
対数粘度数ηinh (ジメチルホルムアミド′中で
。Logarithmic viscosity number ηinh (in dimethylformamide'.
0.5g/diの濃度で30℃で測定)が0.8以上の
ものを用いることが望ましい。It is desirable to use a material whose value (measured at 30° C. at a concentration of 0.5 g/di) is 0.8 or more.
次に9本発明において含弗素有機ポリシロキサンとは次
の一般式で示される構造単位を含むポリマーである。Next, in the present invention, a fluorine-containing organic polysiloxane is a polymer containing a structural unit represented by the following general formula.
(ここでR,、R2は炭素原子数1〜15の1価の有機
基で、R+ 、R2のうち少なくとも一方が炭素原子上
の水素原子の一部又は全部が弗素原子で置換されている
ものである。)
特に好ましい含弗素有機ポリシロキサンは、ビス(2−
パーフルオロアルキルエチル)シロキサン単位、すなわ
ち、前記一般式におけるR、、R2が−(CH2) z
Rf (Rfは炭素原子数1〜8のパーフルオロアルキ
基)である単位を有するもの及びアルキル(又はアリー
ル)−2−パーフルオロアルキルエチルシロキサン単位
、すなわち、前記一般式におけるR1が炭素原子数1〜
10のアルキル基又は了り−ル基で、R2が−(CH2
)ZRfである単位を有するものである。(Here, R, and R2 are monovalent organic groups having 1 to 15 carbon atoms, and at least one of R+ and R2 has a part or all of the hydrogen atoms on the carbon atoms substituted with fluorine atoms. ) A particularly preferred fluorine-containing organopolysiloxane is bis(2-
perfluoroalkylethyl) siloxane unit, that is, R in the above general formula, R2 is -(CH2) z
Rf (Rf is a perfluoroalkyl group having 1 to 8 carbon atoms) and an alkyl (or aryl)-2-perfluoroalkylethylsiloxane unit, that is, R1 in the above general formula has 1 carbon atom ~
R2 is -(CH2
) ZRf.
含弗素有機ポリシロキサンは公知の方法で得られるもの
であり2弗素含量が5〜30重景%重量のが好ましく用
いられる。The fluorine-containing organic polysiloxane can be obtained by a known method, and preferably has a difluorine content of 5 to 30% by weight.
本発明の重合体組成物は公知の方法で得られる。The polymer composition of the present invention can be obtained by a known method.
すなわち溶融成形以前の任意の段階でPVDF系重合体
と含弗素有機ポリシロキサンとを動的あるいは静的混合
する方法である。この際、配合比は成形性及び成形物の
物性を考慮すると9組成物中の含弗素有機ポリシロキサ
ンの量が0.1〜10重量%。That is, this is a method of dynamically or statically mixing the PVDF polymer and the fluorine-containing organic polysiloxane at any stage prior to melt molding. At this time, the blending ratio is such that the amount of fluorine-containing organic polysiloxane in the 9 composition is 0.1 to 10% by weight, considering moldability and physical properties of the molded product.
好ましくは0.3〜7重量%となるようにすることが望
ましい。また、配合温度あるいは成形温度は200〜3
00°C1好ましくは220〜280℃が適当である。The content is preferably 0.3 to 7% by weight. In addition, the compounding temperature or molding temperature is 200 to 3
00°C, preferably 220 to 280°C.
本発明の重合体組成物はフィルム、シート、繊維、その
他の成形物として有用な製品を提供し。The polymer composition of the present invention provides products useful as films, sheets, fibers, and other molded articles.
その工業的価値は高い。Its industrial value is high.
なお2本発明の重合体組成物に熱安定剤1着色剤、抗酸
化剤、他の可塑剤等の添加剤を含有させてもよいことは
いうまでもない。It goes without saying that the polymer composition of the present invention may also contain additives such as a heat stabilizer, a coloring agent, an antioxidant, and other plasticizers.
(実施例) 以下実施例によって本発明をさらに具体的に説明する。(Example) The present invention will be explained in more detail below with reference to Examples.
実施例1〜4.比較例1
ηinh 1.23のPv叶ホモポリマーに第1表に示
した量の含弗素有機ポリシロキサンを添加し、250°
Cでン容融フ゛レントし、チップ化した。このチソフ。Examples 1-4. Comparative Example 1 Fluorine-containing organopolysiloxane in the amount shown in Table 1 was added to a Pv leaf homopolymer with ηinh 1.23, and the mixture was heated at 250°
The mixture was melted with C and made into chips. This Chisov.
をエクストル−ダニ型熔融紡糸機に供給し、紡糸温度2
60°Cで、1mmφ×6孔の紡糸口金より6木のモノ
フィラメントを紡出し、紡出モノフィラメントを40°
Cの水浴中で冷却し9次いで170°Cのグリセリン浴
中で延伸倍率5.3倍の第1段延伸を行い、さらに18
5°Cの気体雰囲気中で延伸倍率1.3倍の第2段延伸
を行い、約350デニールのモノフィラメント(6本)
を得た(スピンドロ一方式)。is supplied to an Extru-mite type melt spinning machine, and the spinning temperature is set to 2.
At 60°C, 6 wood monofilaments were spun from a spinneret with 1mmφ x 6 holes, and the spun monofilaments were heated at 40°C.
The film was cooled in a water bath at 9°C, then subjected to first-stage stretching at a stretching ratio of 5.3 times in a glycerin bath at 170°C, and further stretched at 18°C.
The second stage of stretching was carried out in a gas atmosphere at 5°C at a stretching ratio of 1.3 times to produce approximately 350 denier monofilaments (6 pieces).
(Spindro one-sided system).
未延伸モノフィラメントの表面の凹凸状態(顕微鏡で観
察)、延伸モノフィラメントの引張強度及び結節強度を
第1表に示す。なお、モノフィラメントには着色はほと
んど認められなかった。Table 1 shows the unevenness of the surface of the undrawn monofilament (observed with a microscope), the tensile strength and knot strength of the drawn monofilament. In addition, almost no coloring was observed in the monofilament.
第1表
実施例において使用した含弗素有機ポリシロキサンは、
ジメチルシロキサンとメチル−2−パーフルオロペンチ
ルエチルシロキサンとの等モル共重合体である。The fluorine-containing organopolysiloxane used in the Examples in Table 1 is:
It is an equimolar copolymer of dimethylsiloxane and methyl-2-perfluoropentylethylsiloxane.
(発明の効果)
以上のように9本発明によれば、溶融成形性が良好で゛
、物物性時に強度特性の優れた成形物を与えるPVDF
系重合体組成物が提供される。(Effects of the Invention) As described above, according to the present invention, PVDF has good melt formability and provides a molded product with excellent strength properties in terms of physical properties.
-based polymer compositions are provided.
Claims (3)
ロキサンとからなる重合体組成物。(1) A polymer composition comprising a polyvinylidene fluoride polymer and a fluorine-containing organic polysiloxane.
〜10重量%である特許請求の範囲第1項記載の重合体
組成物。(2) The amount of fluorine-containing organic polysiloxane is 0.1 of the composition.
10. The polymer composition of claim 1, wherein the amount is 10% by weight.
オロアルキルエチル)シロキサン又はアルキル(もしく
はアリール)−2−パーフルオロアルキルエチルシロキ
サン単位を含むものである特許請求の範囲第1項又は第
2項記載の重合体組成物。(3) The fluorine-containing organic polysiloxane includes bis(2-perfluoroalkylethyl)siloxane or alkyl (or aryl)-2-perfluoroalkylethylsiloxane units, according to claim 1 or 2. Polymer composition.