JPS6145670B2 - - Google Patents
Info
- Publication number
- JPS6145670B2 JPS6145670B2 JP14997078A JP14997078A JPS6145670B2 JP S6145670 B2 JPS6145670 B2 JP S6145670B2 JP 14997078 A JP14997078 A JP 14997078A JP 14997078 A JP14997078 A JP 14997078A JP S6145670 B2 JPS6145670 B2 JP S6145670B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- volatile
- acid
- salt
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は錆の認められない金属は勿論、浮いた
錆が機械的に除去された金属、特に鋼板に対する
腐食を防止する為の水性塗料組成物に関するもの
である。
錆が機械的に除去された金属、特に鋼板に対する
腐食を防止する為の水性塗料組成物に関するもの
である。
タンニン、没食子酸、サリチル酸、アナカルド酸
誘導体などのフエノールカルボン酸を利用した塗
料は鉄と直接キレート化し、付着性、防錆性が向
上することは公知である。
誘導体などのフエノールカルボン酸を利用した塗
料は鉄と直接キレート化し、付着性、防錆性が向
上することは公知である。
本発明者等は特開昭49―96033号に記載された
炭酸亜鉛アンモン、リン酸亜鉛アンモン等を含有
するエマルシヨン系塗料の優れた防食効果に着目
し、多価金属カチオン特に無公害と言う観点から
亜鉛錯塩に付き詳細に検討した結果、フエノール
カルボン酸と揮発性錯化剤による多価金属なかん
ずく亜鉛華が水溶性塩を形成し、これをエチレン
性不飽和カルボン酸と他の共重合可能な単量体と
を共重合せしめることにより得られる共重合体の
揮発性アルカリ塩水溶液又は水分散液に添加して
作成した塗料は該錯塩無添加樹脂に対比出来ない
優れたソルトスプレー性を示す事を見出し、先に
特願昭53―40264号（特開昭54―132632号参照）
として出願したが、その後フエノールカルボン酸
の中でも特に非水溶性であり、アルカリ性で可溶
なフミン酸が亜鉛華及び揮発性錯化剤とで水溶性
錯塩を形成する事を認め、該水溶性錯塩をカルボ
キシル基を有する樹脂の揮発性アルカリ塩水溶液
又は水分散液に添加して作成した塗料は更に優れ
た防食効果を示し、ソルトスプレー性も優れてい
る事を見出した。
炭酸亜鉛アンモン、リン酸亜鉛アンモン等を含有
するエマルシヨン系塗料の優れた防食効果に着目
し、多価金属カチオン特に無公害と言う観点から
亜鉛錯塩に付き詳細に検討した結果、フエノール
カルボン酸と揮発性錯化剤による多価金属なかん
ずく亜鉛華が水溶性塩を形成し、これをエチレン
性不飽和カルボン酸と他の共重合可能な単量体と
を共重合せしめることにより得られる共重合体の
揮発性アルカリ塩水溶液又は水分散液に添加して
作成した塗料は該錯塩無添加樹脂に対比出来ない
優れたソルトスプレー性を示す事を見出し、先に
特願昭53―40264号（特開昭54―132632号参照）
として出願したが、その後フエノールカルボン酸
の中でも特に非水溶性であり、アルカリ性で可溶
なフミン酸が亜鉛華及び揮発性錯化剤とで水溶性
錯塩を形成する事を認め、該水溶性錯塩をカルボ
キシル基を有する樹脂の揮発性アルカリ塩水溶液
又は水分散液に添加して作成した塗料は更に優れ
た防食効果を示し、ソルトスプレー性も優れてい
る事を見出した。
本発明で使用するカルボキシル基を含有する樹
脂としては例えば無水トリメリツト酸、無水ピロ
メリツト酸、トリメジン酸、ロジンー無水マレイ
ン酸付加物等の多塩基酸を用いたアルキツド樹
脂、（メタ）アクリル酸、無水マレイン酸、イタ
コン酸等のエチレン性不飽和カルボン酸と他の共
重合可能な単量体との共重合体が挙げられる。多
塩性性酸及びエチレン性不飽和カルボン酸の使用
量は0.1〜30重量％で0.1％以下の場合は多価金属
水溶性錯塩との架橋が不充分であり、耐水性、耐
溶剤性、造膜性が悪くなり、又30％以上では耐水
性が悪く実用上使用に耐えない。好ましい量は
1.5〜５％の範囲である。他の共重合可能な単量
体としては、（メタ）アクリル酸のメチル、エチ
ル、プロピル、ブチル又は２―エチルヘキシルエ
ステルの如き（メタ）アクリル酸アルキルエステ
ル、（メタ）アクリル酸グリシジルエステル、（メ
タ）アクリロニトリル、（メタ）アクリルアミ
ド、スチレン、α―又はβ―メチルスチレン、α
―又はβ―エチルスチレン、酢酸ビニル、プロピ
オン酸ビニル等が挙げられる。
脂としては例えば無水トリメリツト酸、無水ピロ
メリツト酸、トリメジン酸、ロジンー無水マレイ
ン酸付加物等の多塩基酸を用いたアルキツド樹
脂、（メタ）アクリル酸、無水マレイン酸、イタ
コン酸等のエチレン性不飽和カルボン酸と他の共
重合可能な単量体との共重合体が挙げられる。多
塩性性酸及びエチレン性不飽和カルボン酸の使用
量は0.1〜30重量％で0.1％以下の場合は多価金属
水溶性錯塩との架橋が不充分であり、耐水性、耐
溶剤性、造膜性が悪くなり、又30％以上では耐水
性が悪く実用上使用に耐えない。好ましい量は
1.5〜５％の範囲である。他の共重合可能な単量
体としては、（メタ）アクリル酸のメチル、エチ
ル、プロピル、ブチル又は２―エチルヘキシルエ
ステルの如き（メタ）アクリル酸アルキルエステ
ル、（メタ）アクリル酸グリシジルエステル、（メ
タ）アクリロニトリル、（メタ）アクリルアミ
ド、スチレン、α―又はβ―メチルスチレン、α
―又はβ―エチルスチレン、酢酸ビニル、プロピ
オン酸ビニル等が挙げられる。
これ等のエチレン性不飽和カルボン酸と他の共
重合性単量体は通常の溶液重合あるいは乳化重合
によつて共重合されるが水溶性の溶剤、例えばメ
タノール、イソプロパノール、セロソルブ等を含
有させても何等差支えない。
重合性単量体は通常の溶液重合あるいは乳化重合
によつて共重合されるが水溶性の溶剤、例えばメ
タノール、イソプロパノール、セロソルブ等を含
有させても何等差支えない。
上記カルボキシル基を有する樹脂を中和するた
め、アンモニヤ水或いは揮発性アミンが使用され
る。揮発性アミンとしてはメチルアミン、エチル
アミン、ジメチルアミン、ジエチルアミン、トリ
エチルアミン、モルホリン等が挙げられる。
め、アンモニヤ水或いは揮発性アミンが使用され
る。揮発性アミンとしてはメチルアミン、エチル
アミン、ジメチルアミン、ジエチルアミン、トリ
エチルアミン、モルホリン等が挙げられる。
上記樹脂は水溶液又は水分散液の何れでも差支
えない。水溶液の場合は水溶性にする為過剰のカ
ルボキシル基の導入が必要となり、乾燥塗膜の耐
水性に於いて不利となるが適度のカルボキシル基
の導入で耐水性も向上出来る。水分散液に本発明
を適用した場合、従来エマルシヨン型はソルトス
プレー性が悪いとされていたものが本発明の適用
により200時間以上のソルトスプレーも容易に可
能である。
えない。水溶液の場合は水溶性にする為過剰のカ
ルボキシル基の導入が必要となり、乾燥塗膜の耐
水性に於いて不利となるが適度のカルボキシル基
の導入で耐水性も向上出来る。水分散液に本発明
を適用した場合、従来エマルシヨン型はソルトス
プレー性が悪いとされていたものが本発明の適用
により200時間以上のソルトスプレーも容易に可
能である。
フミン酸は市販のものをそのまゝで充分であ
り、揮発性錯化剤としてはアンモニヤ、メチルア
ミン、エチルアミン、ジメチルアミン、ジエチル
アミン、トリメチルアミン、トリエチルアミン、
モルホリン等の揮発性塩基が使用される。
り、揮発性錯化剤としてはアンモニヤ、メチルア
ミン、エチルアミン、ジメチルアミン、ジエチル
アミン、トリメチルアミン、トリエチルアミン、
モルホリン等の揮発性塩基が使用される。
水溶性錯塩の具体例として亜鉛フミン酸アンモ
ン水溶性錯塩の製造方法を記述すると、先づ亜鉛
華5g、水10g、25％アンモニヤ水15gでスラリー
を作り、撹拌し乍らフミン酸を少しずつ添加し、
亜鉛華が透明に溶解するまで加える。フミン酸が
約10g位必要である。
ン水溶性錯塩の製造方法を記述すると、先づ亜鉛
華5g、水10g、25％アンモニヤ水15gでスラリー
を作り、撹拌し乍らフミン酸を少しずつ添加し、
亜鉛華が透明に溶解するまで加える。フミン酸が
約10g位必要である。
本水溶性錯塩は樹脂のカルボキシル基１モル当
り0.1〜1.0モルの見当で使用される。
り0.1〜1.0モルの見当で使用される。
本発明の組成物には着色顔料、体質顔料、防錆
顔料等の添加剤を混合することも可能である。
顔料等の添加剤を混合することも可能である。
以下本発明の詳細を実施例及び参考例により説
明する。実施例中、部及び％は各々重量部及び重
量％を表わす。
明する。実施例中、部及び％は各々重量部及び重
量％を表わす。
実施例 １
サイビノールEC―701B（サイデン化学製：ア
クリル酸３％含有のアクリル系共重合体エマルシ
ヨン、濃度45％）100部に対しプチルセロソルブ
５部を添加し、次いで本文中のフミン酸亜鉛アン
モン錯塩水溶性を３部添加した塗料組成物をみが
き鋼板に乾燥塗膜20μになるように塗布する。７
日間常温乾燥後35℃で塩水噴霧試験を行う。
クリル酸３％含有のアクリル系共重合体エマルシ
ヨン、濃度45％）100部に対しプチルセロソルブ
５部を添加し、次いで本文中のフミン酸亜鉛アン
モン錯塩水溶性を３部添加した塗料組成物をみが
き鋼板に乾燥塗膜20μになるように塗布する。７
日間常温乾燥後35℃で塩水噴霧試験を行う。
参考例 １
サイビノールEC―701B100部に対しブチルセ
ロソルブ５部添加し炭酸亜鉛アンモンの15％亜鉛
華含量水溶性錯塩溶液を２部添加し、実施例１と
同様みがき鋼板に塗布、７日間放置後同様なテス
トを行う。
ロソルブ５部添加し炭酸亜鉛アンモンの15％亜鉛
華含量水溶性錯塩溶液を２部添加し、実施例１と
同様みがき鋼板に塗布、７日間放置後同様なテス
トを行う。
参考例 ２
サイビノールEC―701B100部に対してブチル
セロソラプ５部を添加し、実施例１と同様みがき
鋼板に塗布７日間放置後同様なテストを行う。
セロソラプ５部を添加し、実施例１と同様みがき
鋼板に塗布７日間放置後同様なテストを行う。
塩水噴霧性
実施例１ 960時間で点さび発生
参考例１ 500時間で点さび発生
参考例２ 100時間で全面点さび
註：塩水噴霧試験はJIS Z2371に準じて行う。
Claims (1)
- １ カルボキシル基を有する樹脂の揮発性アルカ
リ塩水溶液又は水分散液に対し、亜鉛華とフミン
酸及び揮発性錯化剤よりなる水溶性錯塩を加えて
なる防食用水性塗料組成物。