JPS61172709A - Manufacture of resin mold for synthetic resin molding - Google Patents
Manufacture of resin mold for synthetic resin moldingInfo
- Publication number
- JPS61172709A JPS61172709A JP1409385A JP1409385A JPS61172709A JP S61172709 A JPS61172709 A JP S61172709A JP 1409385 A JP1409385 A JP 1409385A JP 1409385 A JP1409385 A JP 1409385A JP S61172709 A JPS61172709 A JP S61172709A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- powder
- mold
- casting
- cooling pipes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は射出成形用簡易樹脂型の製造法に関するもので
あり、試作成形品または少量成形品製作用の射出成形用
簡易樹脂型の製造法として利用される。Detailed Description of the Invention (Field of Industrial Application) The present invention relates to a method for manufacturing a simple resin mold for injection molding, and a method for manufacturing a simple resin mold for injection molding for producing trial molded products or small quantity molded products. used as.
(従来の技術)
従来から一般に5試作成形品用樹脂型、あるいは成形個
数の少ない樹脂型は、木型または金属型などの製品モデ
ル(成形品と同形状)に金属粉入り樹脂1例えば、鉄粉
、銅粉、アルミ粉などを含有するエポキシ系樹脂を注型
して、キャビティ部を形成する方法で製造していた(例
えば、特公昭58−54971号公報)。(Prior art) Conventionally, resin molds for 5 trial molded products or resin molds for a small number of molded products are made by placing a resin mold containing metal powder into a product model (same shape as the molded product) such as a wooden or metal mold. The cavity was manufactured by casting an epoxy resin containing powder, copper powder, aluminum powder, etc. (for example, Japanese Patent Publication No. 58-54971).
(発明が解決しようとする問題点)
従来の方法では、成形品を形成する樹脂型の表面は、成
形用型としての必要特性、例えば耐圧力、耐熱性、離型
性などが劣り、たとえ簡易樹脂型としても満足すべき成
形品を得ることが困難であった・
本発明が解決しようとする問題点は、樹脂型の耐圧力、
耐熱性、離型性などを向上させることである。(Problems to be Solved by the Invention) In the conventional method, the surface of the resin mold for forming the molded product has poor characteristics necessary for a molding mold, such as pressure resistance, heat resistance, mold releasability, etc. It was difficult to obtain a satisfactory molded product even with a resin mold.The problems that the present invention aims to solve are the pressure resistance of the resin mold,
The aim is to improve heat resistance, mold releasability, etc.
(問題点を解決するための手段)
上記問題点を解決するための手段は、冷却用管および熱
伝導性の高い長尺金属材が装入された型枠内に磁化しや
すい金属粉が混在した樹脂を充填し、該樹脂を磁界中で
固化せしめることである。(Means for solving the problem) The means for solving the above problem is that metal powder that is easily magnetized is mixed in the formwork in which the cooling tube and the long metal material with high thermal conductivity are charged. The method is to fill the container with a resin and solidify the resin in a magnetic field.
(作用) 上記手段は次のように作用する。(effect) The above means works as follows.
型枠内に磁化しやすい金属粉が混在した樹脂を充填した
後、定盤および/または型枠を磁化すると、樹脂中に埋
設された冷却用管および長尺金属材は樹脂と一体結合し
、かつ磁化しやすい金属粉は指向性を持って配設され、
次いで樹脂が固化する。After filling the formwork with a resin mixed with easily magnetized metal powder, when the surface plate and/or the formwork are magnetized, the cooling pipe and long metal material embedded in the resin are integrally bonded to the resin. The metal powder, which is easily magnetized, is arranged in a directional manner.
The resin then solidifies.
(実施例)
以下、上記手段の一具体例を示す実施例について説明す
る。(Example) Hereinafter, an example showing a specific example of the above means will be described.
第1図に合成樹脂成形用樹脂型の製造装置、第2図に本
発明方法により製作された樹脂型を示す。マスターモデ
ル1を具備した定盤2上に型枠3が載置され、型枠3内
に冷却水、油等の令媒の通る金属製冷却用管4.4およ
び熱伝導性の高い棒状部材および/または管状部材から
形成された長尺金属材5,5が多数個装入されている。FIG. 1 shows an apparatus for manufacturing a resin mold for synthetic resin molding, and FIG. 2 shows a resin mold manufactured by the method of the present invention. A formwork 3 is placed on a surface plate 2 equipped with a master model 1, and inside the formwork 3 are metal cooling pipes 4.4 through which coolants such as cooling water and oil pass, and rod-shaped members with high thermal conductivity. A large number of elongated metal materials 5, 5 formed from and/or tubular members are charged.
冷却用管4.4は型枠3により支持され、長尺金属材5
.5は支持部材6を介して型枠3内に並設され、定盤2
および型枠3は磁化しやすい金属材料より形成される。The cooling pipe 4.4 is supported by the formwork 3, and the long metal material 5
.. 5 are arranged in parallel in the formwork 3 via the support member 6, and the surface plate 2
The formwork 3 is made of a metal material that is easily magnetized.
冷却用管4.4および長尺金属材5,5が装入された型
枠3内にキャビティ7を形成する表装樹脂8を注型し1
次いで磁化しやすい金属粉が混在した注型樹脂91例え
ばアルミ粉と銅粉と鉄粉とを含有したエポキシ系樹脂、
を充填した後、定盤2と型枠3とを磁化すると、冷却用
管4.4および長尺部材5,5は注型樹脂9と一体結合
し、かつ注型樹脂9内で鉄粉は磁界方向に指向性をもっ
て配設され、次いで注型樹脂9が固化する。A facing resin 8 is poured into a mold 3 into which a cooling pipe 4.4 and long metal materials 5, 5 are charged, and a cavity 7 is formed therein.
Next, cast resin 91 mixed with easily magnetized metal powder, for example, an epoxy resin containing aluminum powder, copper powder, and iron powder,
When the surface plate 2 and the formwork 3 are magnetized, the cooling tube 4.4 and the elongated members 5, 5 are integrally combined with the casting resin 9, and the iron powder is removed in the casting resin 9. The casting resin 9 is disposed with directionality in the direction of the magnetic field, and then the casting resin 9 is solidified.
(発明の効果) 本発明は次の効果を生ずる。(Effect of the invention) The present invention produces the following effects.
磁化しやすい金属粉が混在した樹脂中に冷却用管および
長尺金属材を埋設し、かつ磁界中で樹脂を固化させるか
ら、冷却用管および長尺金属材と樹脂とが一体結合し、
かつ磁化しやすい金属粉が指向性をもって配設されるの
で、樹脂型の機械的強度が大きくなるとともに耐熱性が
向上する。The cooling tube and the long metal material are embedded in the resin mixed with easily magnetized metal powder, and the resin is solidified in a magnetic field, so the cooling tube and the long metal material and the resin are integrally bonded.
In addition, since the metal powder that is easily magnetized is arranged in a directional manner, the mechanical strength of the resin mold is increased and the heat resistance is improved.
樹脂層中に冷却用管および長尺金属材が多数個埋設され
、かつ樹脂と一体結合されるから、樹脂型および樹脂型
内に注入された溶融樹脂を強制的に冷却することができ
るので、成形品の固化が早くなるとともに成形品の離型
性°が向上する。Since a large number of cooling tubes and long metal materials are embedded in the resin layer and are integrally bonded to the resin, the resin mold and the molten resin injected into the resin mold can be forcibly cooled. The solidification of the molded product becomes faster and the releasability of the molded product improves.
第1図は本発明方法を実施する装置を示す断面図、第2
図は本発明方法により製作された樹脂型の断面図である
。
3・・・型枠 4・・・冷却用管 5・・・長尺金属材
9・・・注型樹脂FIG. 1 is a sectional view showing an apparatus for carrying out the method of the present invention, and FIG.
The figure is a sectional view of a resin mold manufactured by the method of the present invention. 3... Formwork 4... Cooling pipe 5... Long metal material 9... Casting resin
Claims (1)
型枠内に磁化しやすい金属粉が混在した樹脂を充填し、
該樹脂を磁界中で固化せしめることを特徴とする合成樹
脂成形用樹脂型の製造法。A mold containing cooling tubes and long metal materials with high thermal conductivity is filled with resin mixed with metal powder that is easily magnetized.
A method for producing a resin mold for molding a synthetic resin, which comprises solidifying the resin in a magnetic field.