JPS6099694A - Colored composition for recording sheet - Google Patents
Colored composition for recording sheetInfo
- Publication number
- JPS6099694A JPS6099694A JP58207538A JP20753883A JPS6099694A JP S6099694 A JPS6099694 A JP S6099694A JP 58207538 A JP58207538 A JP 58207538A JP 20753883 A JP20753883 A JP 20753883A JP S6099694 A JPS6099694 A JP S6099694A
- Authority
- JP
- Japan
- Prior art keywords
- composition
- wax
- paper
- leuco dye
- recording sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
らに詳細に1lま、感圧記録シートやカーボン紙とは、
種類を異にする新規な記録シート用着色組成物に関する
。[Detailed Description of the Invention] In more detail, what is a pressure-sensitive recording sheet or carbon paper?
This invention relates to different types of novel coloring compositions for recording sheets.
記録シートとしては、感圧複写紙、感熱記録紙及びカー
ボン紙に大別される。感圧複写紙は,無色または淡色の
ロイコ染料をアルキル化ナフタレン等の溶媒に溶解させ
て得た溶液をコアセルベーション法、界jji重仕法等
の各種カプセル製造法によりロイコ染料をマイクロカプ
セル中Vこ3゛イ1きぜ、このマイクロカプセルを爪等
の支持体上に塗布することにより製造される。感熱記録
紙は、微粒子化シたロイコ染料、ビスフェノールA等の
凸・夕性物質及びノミインダー等の分散液を支持体J.
: I/C塗布することにより製造されている。1だカ
ーボン紙は、炭素と油丑たはロウとの混合物を薄い支持
体の片面または両面に塗被したものである。しかしこれ
ら記録シート、例えば感圧複写紙では、複雑なマイクロ
カプセル化工程を経る為に高価であり、さらに不測の加
圧によってマイクロカプセルが破壊され着色してしまう
欠点が、又感熱記録紙1・・よびカーボン紙では、地肌
の汚れ,さらには不測のひつかき摩擦によって着色する
等の欠点があった。Recording sheets are broadly classified into pressure-sensitive copying paper, heat-sensitive recording paper, and carbon paper. Pressure-sensitive copying paper is made by dissolving a colorless or light-colored leuco dye in a solvent such as alkylated naphthalene, and then using various capsule manufacturing methods such as the coacervation method and the kaiju method to inject the leuco dye into microcapsules. Step 3: The microcapsules are manufactured by coating them on a support such as a nail. The thermosensitive recording paper is prepared by dispersing a micronized leuco dye, a convex/evening substance such as bisphenol A, and a dispersion of a chiselinder as a support.
: Manufactured by I/C coating. Single carbon paper is a thin support coated on one or both sides with a mixture of carbon and oil or wax. However, these recording sheets, such as pressure-sensitive copying paper, are expensive because they go through a complicated microencapsulation process, and they also have the disadvantage that the microcapsules are destroyed and colored by unexpected pressure. - Carbon paper had drawbacks such as dirt on the background and coloring due to unexpected rubbing.
本発明は、このような従来の記録ノートQ)欠点を改良
したうえ、非常に簡単な操作によって支44体上に塗布
できる新規な記録ノート用の着色組成物に関する。すな
わち、本発明は、
a.無色または淡色のロイコ染料
b,溶媒
C・ 体質顔料
(+、高級脂肪族アルキレンジアミン、およびC・ ワ
ックス
からなる記録シート用着色組成物である。本発明の着色
組成物は本来無色であるが、酸性物質と接触することに
より着色する組成物である。The present invention relates to a novel coloring composition for a recording notebook which improves the drawbacks of the conventional recording notebook Q) and which can be applied onto the support 44 by a very simple operation. That is, the present invention comprises a. This is a coloring composition for a recording sheet consisting of a colorless or light-colored leuco dye B, a solvent C, an extender pigment (+), a higher aliphatic alkylene diamine, and a wax C.The coloring composition of the present invention is originally colorless, but It is a composition that becomes colored when it comes into contact with an acidic substance.
本発明で1史用するロイコ染料は、従来の感圧、熱記録
紙に用いられるものであって、トリアリールメタン系化
合物、ジフェニルメタン系化合物、キサンチン系化分゛
吻、チアジン系化合物、オキサジン系化合物などが知ら
れている。The leuco dyes used in the present invention are those used in conventional pressure-sensitive and thermal recording papers, including triarylmethane compounds, diphenylmethane compounds, xanthine compounds, thiazine compounds, and oxazine compounds. Compounds are known.
これらの一部を例示すれば、トリアリールメタン系化合
物として、3,3ビス(p−ジメチルアミノフェニル)
−6−ジメチルアミノフタリドCOV L ]、3,3
−ビス(p−ジメチルアミノフタリド)、3−(p−ツ
メチルアミノフェニル)3(1,3−ジメチルインドー
ル−
フタリド,3−(p−ツメチルアミノフェニル)−3−
(2−メチルインドール−3−イル)フタリド等があり
キサンチン系化合物としては、ローダミンB−アニリノ
ラクタム、ローダミン( 1)ニトロアニリノ)ラクタ
ム、ローダミン+( ( +) −クロロアニリノ)ラ
クタム、2−ジインノルアミノ−6−ジエチルアミノフ
ルオラン、2−アニリノ−6−ジニチルアミノフルオラ
ン、2−アニリノ−3−メチル−6−ジニチルアミノフ
ルオラン、2−アニリノ−3〜メチル−6−(N−シク
ロへキシル−N−メチル)アミノフルオラン、2−。Some examples of these include 3,3 bis(p-dimethylaminophenyl) as a triarylmethane compound.
-6-dimethylaminophthalide COV L ], 3,3
-bis(p-dimethylaminophthalide), 3-(p-trimethylaminophenyl)3(1,3-dimethylindole-phthalide, 3-(p-trimethylaminophenyl)-3-
(2-methylindol-3-yl) phthalide, etc., and xanthine compounds include rhodamine B-anilinolactam, rhodamine (1) nitroanilino)lactam, rhodamine + ( (+) -chloroanilino)lactam, 2-diynnoramino- 6-diethylaminofluorane, 2-anilino-6-dinithylaminofluorane, 2-anilino-3-methyl-6-dinithylaminofluorane, 2-anilino-3-methyl-6-(N-cyclohexyl -N-methyl)aminofluorane, 2-.
−クロロアニリノ−6−ジニチルアミノフルオラン、2
−0−クロロアニリノ−6−シブチルアミノフルオラン
、2−アニリノ−3−メトキシ−6−シブチルアミノフ
ルオラン等がちシ、チアジン系化合物としてはベンゾイ
ルロイコメチレンブルー、p−ニトロベンジルロイコメ
チレンブルー等があり、オキサジン系化合物としては、
3,7ービス(ジエチルアミノ)−10−ベンゾイル−
フェノキサジン、3,7ービス(ジエチルアミノ)−1
0−アセチルフェノキサジン等があり、スピロ系化合物
としては、3−メチルスピロジナフトピラン、3−ベン
ジルスピロ−ジナフトピラン、3−プロピル−スピロ−
ジペンゾビラン等がある。-chloroanilino-6-dinithylaminofluorane, 2
-0-Chloroanilino-6-sibutylaminofluoran, 2-anilino-3-methoxy-6-sibutylaminofluoran, etc., and thiazine compounds include benzoylleucomethylene blue, p-nitrobenzylleucomethylene blue, etc. , as oxazine compounds,
3,7-bis(diethylamino)-10-benzoyl-
Phenoxazine, 3,7-bis(diethylamino)-1
0-acetylphenoxazine, etc., and spiro compounds include 3-methylspirodinaphthopyran, 3-benzylspiro-dinaphthopyran, and 3-propylspiro-dinaphthopyran.
Examples include dipenzobilan.
これらは、単独もしくは混合して用いられる。These may be used alone or in combination.
また本発明で使用する溶媒とは、上記のロイコ染料を溶
解して液状または半固体状にしつるものであシ、通常、
感圧記録紙で用いられるアルキル化ナフタレン、アルキ
ル化ジフェニル、アルキル化ジフェニルメタン、アルキ
ル化ターフェニル、モーピル油、塩素化ノミラフイン等
の合成油、木綿油、ヒマシ油等の植物油、動物油、鉱物
油或はこれらの混合物である。Further, the solvent used in the present invention is one that dissolves the above-mentioned leuco dye and makes it into a liquid or semi-solid state, and usually,
Synthetic oils such as alkylated naphthalene, alkylated diphenyl, alkylated diphenylmethane, alkylated terphenyl, mopil oil, and chlorinated chilafin used in pressure-sensitive recording paper, vegetable oils such as cotton oil and castor oil, animal oils, mineral oils, or It is a mixture of these.
体質顔料としては,炭酸カルシウム、ケイ酸アルミニウ
ム、ケイ酸カルシウム、ケイ酸マグネシウム、水酸化ア
ルミニウム、亜鉛華、硫酸バリウム、珪藻土、ソリ力等
があげられる。Examples of extender pigments include calcium carbonate, aluminum silicate, calcium silicate, magnesium silicate, aluminum hydroxide, zinc white, barium sulfate, diatomaceous earth, and warping force.
高級脂肪族アルキレンジアミンとしては,例えばN−ア
ルギルトリメチレンジアミン、N−アルキルテトラメチ
レンジアミン、N−アルキルペンタメチレンジアミン、
N−アルキルへキサメチレンジアミン等があげられ、ア
ルキル基の炭素数は12ないし20のものであって、例
えば牛脂,大豆オレイルヤシ油から得られるアルキル基
てある。Examples of higher aliphatic alkylene diamines include N-algyl trimethylene diamine, N-alkyltetramethylene diamine, N-alkylpentamethylene diamine,
Examples include N-alkylhexamethylene diamine, and the alkyl group has 12 to 20 carbon atoms, such as those obtained from beef tallow, soybean oleyl and coconut oil.
また、本発明で使用するワックス類としては、密ロウ、
セラックロウなどの動物性ワックス類、カルナウノセロ
ウなどの植物性ワックス類パラフィンワックス、微晶ワ
ックスなどの石油ワックス類、ポリエチレンワックスそ
の他会成ワックス類が使用される。In addition, waxes used in the present invention include beeswax,
Animal waxes such as shellac wax, vegetable waxes such as carnanocellulose, paraffin waxes, petroleum waxes such as microcrystalline wax, polyethylene wax and other synthetic waxes are used.
更に、本発明では必要に応じてこれらの分散を良好にす
るため、分散剤f:使用する場合があり、分散剤として
はステアリン酸などが用いられる。Furthermore, in the present invention, in order to improve the dispersion of these materials, a dispersant f may be used as necessary, and stearic acid or the like is used as the dispersant.
本発明の記録シート用着色組成物は、捷ず(a)ロイコ
染料を(b)溶媒に溶解あるいはけX7濁し、次に(c
)体質顔料、(d)高級脂肪族アルキレンジアミンおよ
び(e)ワックス類を加え、例えば、三本ロール等の混
線手段により良く分散混和し、必要応じて加熱し溶融混
和したのち冷却してワックス状にして得られる。これら
(a)〜(e)からなる成分の割合は、支持体の種類に
よっても、また使用する塗布機によっても異なるが、約
(a) : (b) : (C) : (d) : I
C)は、1:10〜50:10〜50:1〜10:10
〜70である。The coloring composition for a recording sheet of the present invention is prepared by dissolving (a) a leuco dye in (b) a solvent or clouding it with X7, and then (c)
) Extender pigment, (d) higher aliphatic alkylene diamine, and (e) waxes are added, dispersed and mixed well using a mixing means such as a triple roll, heated as necessary to melt and mix, and then cooled to form a wax-like mixture. It can be obtained by The ratio of these components (a) to (e) varies depending on the type of support and the coating machine used, but is approximately (a): (b): (C): (d): I
C) is 1:10-50:10-50:1-10:10
~70.
本発明の着色組成物は、感圧記録紙にみらhるようなマ
イクロカプセル化のための複雑な操作を必要とせず、ま
た、本発明では体質顔料の表面にロイコ染料を保持させ
たのち、ワックス類と混和して一体化しであるので、支
持体への塗布手段としては従来のマイクロカプセル液f
:塗布する方法とは異り、 fMi単な裏カーボン紙を
製造する機器で極めて容易に塗布できるのである。特に
、支持体として紙を使用した場合には従来のマイクロカ
プセル液塗布方式では紙に皺が生じるため、塗布乾燥後
に高速カレンダーかけを行って皺を除去するなど行って
いたが、本発明ではこのような操作を心安とせず、速乾
性にて乾燥工程を必要とせず前述のように夷カーボン紙
用のft11jliな機器を用いて印刷すればよいため
便利且つ簡単に塗布できるものである。又、本発明の利
点は感圧記録紙のように、かならずしも支持体の全面に
塗布する必要性はなく、又部分部に減感インキを使用し
てスポット記録をする必要もなく、必要に応じて本発明
の組成物を部分的に簡便に塗布しうることにある。The coloring composition of the present invention does not require complicated operations for microencapsulation as seen in pressure-sensitive recording paper, and in the present invention, the leuco dye is retained on the surface of the extender pigment. Since it is mixed with waxes and integrated, conventional microcapsule liquid f can be used as a means of coating it on the support.
: Unlike the coating method, fMi can be applied extremely easily using equipment that produces simple back carbon paper. In particular, when paper is used as a support, the conventional microcapsule liquid coating method causes wrinkles in the paper, so high-speed calendering is performed after coating and drying to remove wrinkles. It is convenient and easy to apply, without worrying about such operations, because it dries quickly and does not require a drying process, and can be printed using the FT11JLI equipment for carbon paper as described above. Another advantage of the present invention is that unlike pressure-sensitive recording paper, it is not necessary to coat the entire surface of the support, and there is no need to perform spot recording using desensitizing ink in partial areas. The composition of the present invention can be easily applied locally.
そして、発色後の耐光堅ロウ度においても本発明の組成
物を使用した方がすぐれていた。史((、本発明は、裏
カーボン紙と比較して、被服の汚染等が皆無であり環境
衛生面からも優れている。またさらに、本発明の組成物
を感熱記録シートとして使用した場合、複数枚の重ね合
せによる複写が可能であり、この点も現在市販の感熱記
録シートに比べて優れている。Furthermore, the light fastness after color development was also superior when the composition of the present invention was used. (Compared to back carbon paper, the present invention does not cause any contamination of clothes and is superior in terms of environmental hygiene.Furthermore, when the composition of the present invention is used as a heat-sensitive recording sheet, It is possible to make copies by stacking multiple sheets, and this point is also superior to currently commercially available heat-sensitive recording sheets.
また、本発明の着色組成物を発色させるだめの酸性物質
としては、酸性白土、活性白土、ベントナイト、コロイ
ダルシリカ、珪酸アルミニウム等の無機物質或はシュウ
酸、マレイン酸、フェノール−ホルマリン樹脂などの有
機物質があるがこれらは感圧複写用の顕色紙として市販
されており、これらの市販品を好適に使用することがで
きる。In addition, as acidic substances for coloring the coloring composition of the present invention, inorganic substances such as acid clay, activated clay, bentonite, colloidal silica, aluminum silicate, etc., or organic substances such as oxalic acid, maleic acid, phenol-formalin resin, etc. Although there are materials, these are commercially available as color developer paper for pressure-sensitive copying, and these commercially available products can be suitably used.
次に実施例をあげて本発明をさらに詳細に説明するが、
部は重量部を表わす。Next, the present invention will be explained in more detail with reference to Examples.
Parts represent parts by weight.
実施例I
A液(染料含有固形物)
B′#、(ワックス混合物)
N液をロールにかけ、7昆台した後、130’Cで11
液を加え、約2時間湿分かくはんし良く分j′、!i混
オロした。このようにして得られた組成物を−h :g
紙」二に塗布し乾燥して記録シートラ得た。このd己録
シートヲ市販のクレー紙、レジン、i4(、またはす1
ノチル酸の金属塩を塗布した顕色紙とかさJα会J)せ
、上から筆記することにより、直しに青色の印字力・得
られた。この発色した印字は、各顕色紙とも+lj1九
性に優れており3ケ月間保存した結果でも、この印字は
鮮明であり、保存安定性の面からも実J「価値が充分で
あった。Example I Solution A (dye-containing solid) B'#, (wax mixture) Solution N was rolled, heated for 7 hours, and heated at 130'C for 11 hours.
Add the liquid and keep it moist for about 2 hours, stirring well for about 2 hours,! I was confused. The composition thus obtained is -h:g
It was coated on paper and dried to obtain a recording sheet. This self-recording sheet can be made from commercially available clay paper, resin, i4 (or
By writing on top of a sheet of color developing paper coated with a metal salt of notylic acid, blue printing power was immediately obtained. These colored prints had excellent +lj19 properties on each color developing paper, and even after being stored for 3 months, the prints were clear and had sufficient value in terms of storage stability.
実施例2
入滅(染料含有固形物)
クリスタルノ々イオレットラクトン 3部ペンソイルロ
イコメチレンブルー 2部炭酸カルシウム 150部
アルキルナフタレン
(KMO呉羽化学工業(株)製品) 150部ラノリン
50部
N−アルキルトリメチレンジアミン
(デオミンライオン・アクゾ社製品) 30部Bi(ワ
ックス混合物)
カルナバろう 50部
モンタンろう ]、 00部
ステアリン酸 20バ13
A液KBfiを添加して三本ロールを用いて室温で3時
間混練し良く分散混和した。このようにして得られた着
色組成物を上質紙上に塗布乾燥して記録シートを得た。Example 2 Decomposition (dye-containing solid material) Crystalline iolet lactone 3 parts Pensoyl leucomethylene blue 2 parts Calcium carbonate 150 parts Alkylnaphthalene (product of KMO Kureha Chemical Co., Ltd.) 150 parts Lanolin 50 parts N-alkyl trimethylene Diamine (Deomin Lion Akzo product) 30 parts Bi (wax mixture) Carnauba wax 50 parts Montan wax], 00 parts Stearic acid 20 parts 13 Added Part A KBfi and kneaded for 3 hours at room temperature using a triple roll. It was well dispersed and mixed. The thus obtained colored composition was coated on high-quality paper and dried to obtain a recording sheet.
この記録シートを市販の1駿性白土を塗布した市販の顕
色用紙とかさね合せ、上かう筆記することにより、直ち
vc y(色の印字が得られた。この発色した印字は1
llII光性に優れており13)):月間保存した結果
でも、この印字は鮮明であり、保存安定性の面からも実
用価値が充分であった。By stacking this recording sheet with commercially available color developing paper coated with commercially available white clay and writing on it, a vcy (color print) was immediately obtained.
13)): Even after being stored for months, the print was clear and had sufficient practical value in terms of storage stability.
実施例3
実施例2のクリスタルバイオレットラクトンおよびベン
ゾイルロイコメチレンブルーのかわりに2−アニリノ−
3−メチル−6−ジニチルアミノフルオラン5部を使用
し、実施例2と同腫な方法により分散混和し顕色紙と重
ね合わ拷、」二から筆記することによシ直ちに、黒色の
印字が得られた。Example 3 2-anilino- in place of crystal violet lactone and benzoylleucomethylene blue in Example 2
Using 5 parts of 3-methyl-6-dinithylaminofluorane, it was dispersed and mixed in the same manner as in Example 2, and then layered with developer paper. Obtained.
この発色した印字は、耐光性に優れており、3ケ月間保
存した結果でも、この印字は鮮明であり、保存安定性の
面からも実用価値が充分であった。This colored print had excellent light resistance, and even after being stored for 3 months, the print was clear and had sufficient practical value in terms of storage stability.
実栴例4
実施例1のクリスタルバイオレットラクトンおよびベン
ゾイルロイコメチレンブルーのかわりに2−(2−クロ
ロアニリノ) −6−n−ジブチルアミノ−フルオラン
20部を使用し実施例1と同様に処理し顕色紙に印字す
ると黒色の像が1jtらJした。この発色した印字は面
」光性に優れてisす1.3ケ月間保存した結果でもこ
の印字は魚工明であり、保存安定性の面からも実用r1
1Ti 血が充分てあった。Practical Example 4 20 parts of 2-(2-chloroanilino)-6-n-dibutylamino-fluoran was used in place of the crystal violet lactone and benzoylleucomethylene blue of Example 1, and the same process as in Example 1 was carried out to produce color developing paper. When printed, a black image appeared. This colored print has excellent luminosity, and even after being stored for 1.3 months, this print is clear, and from the perspective of storage stability, it is practical.
1Ti There was enough blood.
出願人 保土谷化学工業株式会社 代理人 1) 中 宏Applicant: Hodogaya Chemical Industry Co., Ltd. Agent 1) Hiroshi Naka
Claims (1)
ス からなる記録シート用着色組成物。[Scope of Claims] A coloring composition for a recording sheet, comprising: (a) a colorless or light-colored leuco dye 1], a solvent C0 extender pigment (d), a higher aliphatic alkylene diamine, and (e) a wax.