JPS6041630B2 - Air entraining agent composition - Google Patents
Air entraining agent compositionInfo
- Publication number
- JPS6041630B2 JPS6041630B2 JP54099022A JP9902279A JPS6041630B2 JP S6041630 B2 JPS6041630 B2 JP S6041630B2 JP 54099022 A JP54099022 A JP 54099022A JP 9902279 A JP9902279 A JP 9902279A JP S6041630 B2 JPS6041630 B2 JP S6041630B2
- Authority
- JP
- Japan
- Prior art keywords
- ether
- entraining agent
- agent composition
- air entraining
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は気硬性セメントまたは水硬性セメントに使用し
て多孔性コンクリートを得るための空気連行剤組成物に
関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to an air entraining agent composition for use in pneumatic or hydraulic cements to obtain porous concrete.
多孔性コンクリートは気硬性セメントまたは水硬性セメ
ントに界面活性剤を加え、その起泡力を利用して製造さ
れる。Porous concrete is manufactured by adding a surfactant to air or hydraulic cement and utilizing its foaming power.
そして、軽量で断熱効果も大きいことから、建築用資材
として多く用いられている。界面活性剤としては主に起
泡力の大きいアニオン界面活性剤が用いられているが、
さらに起泡力を大きくするために起泡助剤としてイソプ
ロパノールなどの低級アルコールが併用される。Because it is lightweight and has great heat insulation effects, it is often used as a construction material. Anionic surfactants with high foaming power are mainly used as surfactants.
Further, in order to increase the foaming power, a lower alcohol such as isopropanol is used in combination as a foaming aid.
しかし、低級アルコールは引火点が低いために取り扱い
上の注意を要する。本発明者らはアニオン界面活性剤の
起泡力を向上させるとともに取り扱い上も安全な起泡助
剤について鋭意検討を重ねた結果本発明を完成した。However, lower alcohols require care when handling because of their low flash points. The present inventors have completed the present invention as a result of intensive studies on foaming aids that improve the foaming power of anionic surfactants and are also safe to handle.
すなわち、本発明はアニオン界面活性剤と一般式（１）
のグリコールエーテルとからなる多孔性コンクリートを
得るための空気連行剤組成物である。ＲＯ（ＣＨ２ＣＨ
２Ｏ）ｎＨ・・・・・・田（Ｒは炭素数１〜６のアルキ
ル基、フェニル基またはベンジル基、ｎは１〜５の整数
である。）本発明の空気連行剤組成物が適用されるセメ
ントには、気硬性セメントとして焼石こう、マグネシア
セメントなどがあり、水硬性セメントとしてボルトラン
ドセメント、シリカセメント、フライアッシュセメント
、アルミナセメント、高炉セメントなどがある。また骨
材として、気硬性セメントにはパルプかす、砂等、水硬
性セメントには砂、砂利、砕石、軽石、スラグ、人工骨
材等、通常セメントに使用される骨材を併用することが
できる。本発明に使用するアニオン界面活性剤はコンク
リート用の空気連行剤として通常用いられているもので
、たとえばつぎのものがあり、１種または２種以上の混
合物として使用される。That is, the present invention provides anionic surfactants and general formula (1)
This is an air entraining agent composition for obtaining porous concrete consisting of glycol ether. RO(CH2CH
2O) nH... (R is an alkyl group having 1 to 6 carbon atoms, a phenyl group, or a benzyl group, and n is an integer of 1 to 5.) The air entraining agent composition of the present invention is applied. Air-hardening cements include calcined gypsum and magnesia cement, while hydraulic cements include boltland cement, silica cement, fly ash cement, alumina cement, and blast furnace cement. In addition, as aggregates, aggregates normally used for cement can be used together, such as pulp waste, sand, etc. for air hard cement, and sand, gravel, crushed stone, pumice, slag, artificial aggregate, etc. for hydraulic cement. . The anionic surfactants used in the present invention are commonly used as air entraining agents for concrete, and include, for example, the following, and are used singly or as a mixture of two or more.
（ａ）樹脂酸塩
（ｂ）アルカンスルホン酸塩
”（ｃ）オレフィンスルホン酸塩
（ｄ）アルキルベンゼンスルホン酸塩
（ｅ）アルキル硫酸エステル塩
（ｆ）ポリオキシエチレンアルキルエーテル硫酸エステ
ル塩・ （ｇ）ポリオキシエチレンアルキルフェニルエ
ーテル硫酸エステル塩これらのアニオン界面活性剤の塩
の種類は、ナトリウム塩、カリウム塩、アンモニウム塩
、モノエタノールアミン塩、ジエタノールアミン塩、ト
りエタノールアミン塩などである。(a) Resinates (b) Alkanesulfonates (c) Olefinsulfonates (d) Alkylbenzenesulfonates (e) Alkyl sulfates (f) Polyoxyethylene alkyl ether sulfates (g) Polyoxyethylene alkyl phenyl ether sulfate ester salt Types of salts of these anionic surfactants include sodium salt, potassium salt, ammonium salt, monoethanolamine salt, diethanolamine salt, and triethanolamine salt.
本発明に使用する一般式（１）のグリコールエーテルと
しては、エチレングリコールモノメチルエーテル、ジエ
チレングリコールモノメチルエーテル、トリエチレング
リコールモノメチルエーテル、エチレングリコールモノ
エチルエーテル、ジエチレングリコールモノエチルエー
テル、エチレングリコ−ルモノーｎ−プロピルエーテル
、エチレングリコールモノイソビルエーテル、エチレン
グリコ−ルモノーｎ−ブチルエーテル、ジエチレングリ
コ−ルモノーｎ−ブチルエーテル、トリエチレングリコ
−ルモノーｎ−ブチルエーテル、テトラエチレングリコ
−ルモノーｎ−ブチルエーテル、ペンタエチレングリコ
−ルモノーｎ−ブチルエーテル、エチレングリコ−ルモ
ノーｎ−アミルエーテル、エチレングリコ−ルモノーｎ
−ヘキシルエーテル、エチレングリコールモノフェニル
エーテル、エチレングリコールモノベンジルエーテルな
どがあり、とくにＲがブチル基またはフェニル基、ｎが
１〜３のものが好ましい。Examples of the glycol ether of general formula (1) used in the present invention include ethylene glycol monomethyl ether, diethylene glycol monomethyl ether, triethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monoethyl ether, and ethylene glycol monon-propyl ether. , ethylene glycol monoisobyl ether, ethylene glycol mono n-butyl ether, diethylene glycol mono n-butyl ether, triethylene glycol mono n-butyl ether, tetraethylene glycol mono n-butyl ether, pentaethylene glycol mono n-butyl ether, Ethylene glycol monon-amyl ether, ethylene glycol monon
-hexyl ether, ethylene glycol monophenyl ether, ethylene glycol monobenzyl ether, etc., and those in which R is a butyl group or phenyl group and n is 1 to 3 are particularly preferred.
アニオン界面活性剤と一般式（１）のグリコールエーテ
ルとの混合重量比は有効分として１：０．０１〜１０で
あり、この範囲ではアニオン界面活性剤の起泡力が向上
し、泡の安定性も改良される。The mixing weight ratio of the anionic surfactant and the glycol ether of general formula (1) is 1:0.01 to 10 as an effective component, and within this range, the foaming power of the anionic surfactant improves and the foam becomes stable. Sexuality is also improved.
アニオン界面活性剤の使用量は目的、使用条件，等によ
つて変化するが、空気連行剤として通常使用される範囲
であり、有効分として気硬性セメントに対して０．０１
〜１．０１！量％、水硬性セメントに対して０．００１
〜１．唾量％である。The amount of anionic surfactant to be used varies depending on the purpose, usage conditions, etc., but is within the range normally used as an air entraining agent, and the effective amount is 0.01 to air hardening cement.
~1.01! Volume %, 0.001 for hydraulic cement
~1. Saliva volume%.
本発明のアニオン界面活性剤とグリコールエーテルとか
らなる空気連行剤組成物は、従来のアニオン界面活性剤
と低級アルコールとからなる空気連行剤組成物よりも起
泡力が大きく、また引火点が高くて火災の危険性も小さ
い。The air entraining agent composition comprising an anionic surfactant and a glycol ether of the present invention has greater foaming power and a higher flash point than conventional air entraining agent compositions comprising an anionic surfactant and a lower alcohol. The risk of fire is also small.
また、従来の前記空気連行剤組成物と同様に、アニオン
界面活性剤が溶解して低粘度の流動物となるのて作業上
の取り扱いが容易であり、輸送や保管の面でも好都合で
ある。つぎに本発明を実施例により説明する。Further, like the conventional air entraining agent composition, the anionic surfactant is dissolved to form a low viscosity fluid, which is easy to handle and convenient for transportation and storage. Next, the present invention will be explained by examples.
％は重量％を表わす。実施例１
普通ボルトランドセメントまたは焼石こう１０ｙと空気
連行剤組成物水溶液（アニオン界面活性剤を含有）３０
０ｆとを容量２．４ｆの家庭用ミキサーにとり、回転数
毎分８０００回転て６＠間攪拌した。% represents weight %. Example 1 Ordinary Bortland cement or calcined gypsum 10y and air entraining agent composition aqueous solution (containing anionic surfactant) 30y
0f was placed in a household mixer with a capacity of 2.4f, and stirred for 6 hours at a rotational speed of 8000 rpm.
攪拌停止後５秒経過した時点で泡の高さが一定になるの
で、ミキサーの底からの泡の高さを測定した。空気連行
剤組成物水溶液の組成と泡の高さの測定結果を表１に示
す。アニオン界面活性剤としては（４）ドデシルベンゼ
ンスルホン酸ナトリウム、（Ｂ）ｎ−ドデシル硫酸エス
テルナトリウムおよび（Ｃ）ポリオキシエチレン（３）
−ｎ−ドデシルエーテル硫酸エステルナトリウムを用い
、起泡助剤としてはイソプロパノールおよび各種のグル
コールエーテルを用いた。Since the height of the foam became constant 5 seconds after the stirring was stopped, the height of the foam from the bottom of the mixer was measured. Table 1 shows the composition of the air entraining agent composition aqueous solution and the measurement results of the foam height. Anionic surfactants include (4) sodium dodecylbenzenesulfonate, (B) sodium n-dodecyl sulfate, and (C) polyoxyethylene (3)
-n-dodecyl ether sodium sulfate was used, and isopropanol and various glycol ethers were used as foaming aids.
なお、起泡させない状態ではミキサーの底から液面まで
の高さは２８ＴｆＵｎであつた。In addition, the height from the bottom of the mixer to the liquid level was 28 TfUn in a state without foaming.
表１より、本発明のアニオン界面活性剤とグリコールエ
ーテルとを併用した空気連行剤組成物は、アニオン界面
活性剤とイソプロパノールとを．併用した空気連行剤組
成物よりも起泡力が大きいことが明らかである。From Table 1, it can be seen that the air entraining agent composition of the present invention that uses an anionic surfactant and a glycol ether in combination uses an anionic surfactant and isopropanol. It is clear that the foaming power is greater than that of the air entraining agent composition used in combination.
実施例２
実施例１と同様な空気連行剤組成物を用いて普通ボルト
ランドセメントと川砂（径１．ｈ以下）．一との混合重
量比１：３、水／ボルトランドセメント比６０％のセメ
ントモルタルを調製し、ＡＳＴＭＣｌ８５−５８Ｔに記
載の方法で空気量を測定した。Example 2 Using the same air-entraining agent composition as in Example 1, ordinary Bortland cement and river sand (diameter 1.h or less) were prepared. A cement mortar with a mixing weight ratio of 1:3 and a water/Boltland cement ratio of 60% was prepared, and the amount of air was measured by the method described in ASTM Cl85-58T.
測定時の温度は２（３Ｃである。結果を表２に示すが、
本発明のアニオン界面活性剤とグリコールエーテルとを
併用した空気連行剤組成物の場合は空気量が大きいこと
が明らかである。The temperature at the time of measurement was 2 (3C).The results are shown in Table 2,
It is clear that the air entraining agent composition using the anionic surfactant and glycol ether of the present invention has a large amount of air.
実施例３
ポリオキシエチレン（２）デシルエーテル硫酸エステル
ナトリウムと水との等量混合物は高粘度で取り扱いにく
い。Example 3 A mixture of equal amounts of sodium polyoxyethylene (2) decyl ether sulfate and water has a high viscosity and is difficult to handle.
この水の一部をイソプロパノールまたはエチレングリコ
−ルモノーｎ−ブチルエーテルで置換し、ポリオキシエ
チレン（２）デシルエーテル硫酸エステルナトリウム５
０％、水３５％、イソプロパノールまたはエチレングリ
コ−ルモノーｎ−ブチルエーテル１５％にすると十分な
流動性を示すようになる。Part of this water is replaced with isopropanol or ethylene glycol monon-butyl ether, and polyoxyethylene (2) decyl ether sulfate sodium 5
0%, water 35%, and isopropanol or ethylene glycol monon-butyl ether 15%, sufficient fluidity will be exhibited.
この引火点を測定すると（測定法：ＪＩＳＫ一２２６５
）、イソプロパノールを含有するものは？℃で危険性が
大きいのに対し、エチレングリコ−ルモノーｎ−ブチル
エーテルを含有するものは沸点の９１℃においても引火
しなかつた。このように、本発明のアニオン界面活性剤
とグリコールエーテルとからなる空気連行剤組成物はｌ
引火点が高くて安全であるとともに、水に対する溶解性
にもすぐれているので取り扱いが容易である。When this flash point is measured (Measurement method: JISK-2265
), which ones contain isopropanol? While the danger is high at 91°C, those containing ethylene glycol mono n-butyl ether did not catch fire even at the boiling point of 91°C. Thus, the air entraining agent composition comprising the anionic surfactant and glycol ether of the present invention is l
It has a high flash point, making it safe, and it also has excellent solubility in water, making it easy to handle.
Claims (1)
ーテルとからなり、混合重量比が有効分として１：０．
０１〜１０であるコンクリート用空気連行剤組成物。 ＲＯ（ＣＨ＿２ＣＨ＿２Ｏ）＿ｎＨ・・・・・・（１）
（Ｒは炭素数１〜６のアルキル基、フェニル基またはベ
ンジル基、ｎは１〜５の整数である。 ）[Scope of Claims] 1 Consists of an anionic surfactant and a glycol ether of general formula (1), with a mixing weight ratio of 1:0 as effective components.
An air entraining agent composition for concrete having numbers 01 to 10. RO(CH_2CH_2O)_nH...(1)
(R is an alkyl group having 1 to 6 carbon atoms, a phenyl group, or a benzyl group, and n is an integer of 1 to 5.)