JPS60177154A - Golden copper alloy for ornamentation - Google Patents
Golden copper alloy for ornamentationInfo
- Publication number
- JPS60177154A JPS60177154A JP3290384A JP3290384A JPS60177154A JP S60177154 A JPS60177154 A JP S60177154A JP 3290384 A JP3290384 A JP 3290384A JP 3290384 A JP3290384 A JP 3290384A JP S60177154 A JPS60177154 A JP S60177154A
- Authority
- JP
- Japan
- Prior art keywords
- golden
- ornamentation
- decorative
- copper alloy
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
本発明は、装飾用金合金の代用として用いられる黄金色
系銅合金に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a golden copper alloy used as a substitute for decorative gold alloys.
近年の省資源化に伴い、装飾用金合金の代用として黄金
色系合金材料が要求されている。With the recent efforts to save resources, golden alloy materials are required as a substitute for decorative gold alloys.
一般に装飾品に於いては、耐食性1機械的性質が良好で
あることが具備条件の一つとされている。In general, one of the requirements for decorative items is to have good corrosion resistance and mechanical properties.
更には、これ等の装飾品は装飾性の面から、複雑な加工
が施される為、その加工が容易であること、さらにその
色が黄金色に近いことも併せて要求されている。Furthermore, since these ornaments are subjected to complex processing for decorative purposes, they are also required to be easy to process and to have a color close to golden yellow.
ところで、装飾用黄金色系材料として用いられている合
金としてはZ n 3Qwt%、残部Cuより成る黄銅
合金があるが、この合金は耐食性1機械的性質が悪く、
複雑な形状に加工しづらいという欠点があった。By the way, as an alloy used as a decorative golden-colored material, there is a brass alloy consisting of 3Qwt% Z n and the balance Cu, but this alloy has poor corrosion resistance and poor mechanical properties.
The drawback was that it was difficult to process into complex shapes.
本発明は、上記の欠点を解消せんが為になされたもので
あり、銅系合金で耐食性、加工性2機械的性質(耐疲労
性)に優れ、かつ黄金色を有する装飾用黄金色系銅合金
を提供せんとするものである。The present invention was made in order to eliminate the above-mentioned drawbacks, and is a copper-based alloy that has excellent corrosion resistance, workability, mechanical properties (fatigue resistance), and has a golden color. The purpose is to provide alloys.
本発明による装飾用黄金色系銅合金はZn7〜45iv
t%、S i O,1〜7 wt%、貴金属0.01〜
2 wt%。The decorative golden copper alloy according to the present invention is Zn7~45iv
t%, S i O, 1-7 wt%, noble metal 0.01-
2 wt%.
残部Cuより成る合金である。This is an alloy with the remainder being Cu.
本発明による装飾用黄金色系銅合金に於いて、Znを添
加した理由は、ZnはCLJと合金を作った際に、黄金
色が得られる為であり、7wt%未満ではその効果が薄
く、45ivt%を超えるとβ相が現われ、薄板に加工
することが困難になる為である。The reason why Zn is added to the decorative golden-colored copper alloy according to the present invention is that Zn produces a golden color when alloyed with CLJ, and if it is less than 7 wt%, the effect is weak. This is because if it exceeds 45 ivt%, β phase will appear and it will be difficult to process it into a thin plate.
また、Siを添加した理由は、StはCuと合金するこ
とにより結晶粒を微細化させ、繰り返し変形に対する耐
疲労性が向上するためであり、0.1wt%未満ではそ
の効果が薄く、7ivt%を超えると、相が析出し、加
工性が低下してくる為である。Furthermore, the reason for adding Si is that by alloying with Cu, St refines the crystal grains and improves the fatigue resistance against repeated deformation. This is because if it exceeds this, phases will precipitate and workability will deteriorate.
また、貴金属を添加した理由は、貴金属の微量添加によ
りCu−Zn−5t合金の耐食性をさらに向上させる為
であり、0.01wt%未満ではその効果が薄く、2w
t%を超えてもあまり顕著な変化が見られなくなる為で
ある。ここで言う貴金属とば、Au、Ag、P t、p
d、Rh、Ru、l r、Osを含めてのことである。In addition, the reason for adding precious metals is to further improve the corrosion resistance of the Cu-Zn-5t alloy by adding a small amount of precious metals, and if it is less than 0.01wt%, the effect is weak;
This is because even if it exceeds t%, no significant change is observed. The precious metals mentioned here are Au, Ag, Pt, p
This includes d, Rh, Ru, l r, and Os.
以下本発明による装飾用黄金色系鋼合金の効果を明瞭な
らしめる為に実施例及び従来例について述べる。Examples and conventional examples will be described below in order to clarify the effects of the decorative golden-colored steel alloy according to the present invention.
第1表に示す成分組成の実施例1〜4の装飾用黄金色系
銅合金と従来例1,2の装飾用黄金色系鋼合金の色、加
工性、耐汗性、耐疲労性についてテストしたところ第2
表のような結果を得た。Tests on the color, workability, sweat resistance, and fatigue resistance of the decorative golden-colored copper alloys of Examples 1 to 4 and the decorative golden-colored steel alloys of Conventional Examples 1 and 2 having the compositions shown in Table 1. Then the second
The results shown in the table were obtained.
第1表
第2表
ナオ、人工汗試験はN H4Cl 15.51T /
ji 。Table 1 Table 2 Nao, artificial sweat test is N H4Cl 15.51T /
ji.
NaCl20g/C酢ill 2.5g / I! 、
尿$5 g/it。NaCl20g/C vinegarill 2.5g/I! ,
Urine $5 g/it.
乳酸15g/β、I)8 4.7の液組成で液温40℃
、240時間浸?13後判定した。Lactic acid 15g/β, liquid composition I)8 4.7, liquid temperature 40℃
, soaked for 240 hours? Judgment was made after 13 days.
また、疲労試験はシャルピー試験機を用い、4号試験片
に15kg−amの衝撃エネルギーを繰り返し加えて試
験片が破壊するまでの回数で評価した。The fatigue test was performed using a Charpy tester, and the impact energy of 15 kg-am was repeatedly applied to the No. 4 test piece, and the test piece was evaluated by the number of times it took to break.
上記で明らかなように本発明による装飾用黄金色系銅合
金は従来の装飾用黄金色系銅合金に比し、耐汗性、加工
性2機械的性質(耐疲労性)が優れ、かつ黄金色を有し
ていることが判る。As is clear from the above, the decorative golden-colored copper alloy according to the present invention has excellent sweat resistance, workability, mechanical properties (fatigue resistance), and is superior to conventional decorative golden-colored copper alloys. It can be seen that it has a color.
以上詳記した通り、本発明の装飾用黄金色系銅合金は、
耐汗性、加工性1機械的性質(−(疲労性)が優れかつ
黄金色を有しているので、従来の装飾用黄金色系銅合金
にとって代わることのできる画期的なものと言える。As detailed above, the decorative golden copper alloy of the present invention is
It has excellent sweat resistance, processability, mechanical properties (-(fatigue resistance)), and has a golden color, so it can be said to be an epoch-making product that can replace conventional decorative golden copper alloys.
出願人 田中貴金属工業株式会社Applicant: Tanaka Kikinzoku Kogyo Co., Ltd.
Claims (1)
JffiO,01〜2wt%、残部銅より成る装飾用黄
金色系銅合金。A decorative golden copper alloy consisting of 7-45t% zinc, 0.1-7wt% silicon, 01-2wt% silicon, and the balance copper.