JPS60177145A - Golden copper alloy for ornamentation - Google Patents
Golden copper alloy for ornamentationInfo
- Publication number
- JPS60177145A JPS60177145A JP3289684A JP3289684A JPS60177145A JP S60177145 A JPS60177145 A JP S60177145A JP 3289684 A JP3289684 A JP 3289684A JP 3289684 A JP3289684 A JP 3289684A JP S60177145 A JPS60177145 A JP S60177145A
- Authority
- JP
- Japan
- Prior art keywords
- golden
- copper alloy
- alloy
- decorative
- ornamentation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
本発明は、装飾用金合金の代用として用いられる黄金色
系銅合金に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a golden copper alloy used as a substitute for decorative gold alloys.
近年の省資源化に伴い、装飾用金合金の代用として黄金
色系合金材料が要求されている。With the recent efforts to save resources, golden alloy materials are required as a substitute for decorative gold alloys.
一般に装飾品に於いては、耐食性が良好であることが具
備条件の一つとされている。更には、これ等の装飾品は
装飾性の面がら、複雑な加工が施される為、その加工が
容易であること、さらにその色が黄金色に近いことも併
せて要求されている。In general, one of the requirements for decorative items is good corrosion resistance. Furthermore, since these ornaments undergo complicated processing for their decorative nature, they are also required to be easy to process and to have a color close to golden yellow.
ところで、装飾用黄金色系材料として用いられている合
金としてはＺ ｎ ３０ｗｔ％、残部Ｃｕより成る黄銅
合金があるが、この合金は耐食性が悪く、複雑な形状に
加工しづらいという欠点があった。Incidentally, an alloy used as a decorative golden-colored material is a brass alloy consisting of 30 wt% Zn and the balance Cu, but this alloy has the disadvantage of poor corrosion resistance and difficulty in processing into complex shapes. .
本発明は、上記の欠点を解消せんが為になされたもので
あり、銅系合金で耐食性、加工性に優れ、かつ黄金色を
有する装飾用黄金色系銅合金を提供せんとするものであ
る。The present invention was made in order to eliminate the above-mentioned drawbacks, and aims to provide a decorative golden-colored copper alloy that is a copper-based alloy and has excellent corrosion resistance and workability, and has a golden color. .
本発明による装飾用黄金色系銅合金はＡ１２〜１０−ｔ
％＋ Ｚ ｎ Ｏ，１〜２ ｗｔ％、貴金属０．０１〜
１．８ｗｔ％、残部Ｃｕより成る合金である。The decorative golden copper alloy according to the present invention is A12-10-t.
%+ZnO, 1-2 wt%, noble metal 0.01-
It is an alloy consisting of 1.8 wt% and the balance Cu.
本発明による装飾用黄金色系銅合金に於いて、Ａ１を添
加した理由は、ＡｔはＣｕと合金を作った際に表面に安
定な酸化被膜を作り、耐食性を向上すると共に、黄金色
の合金が得られる為であり、２ｗｔ％未満ではその効果
が薄く、１０ｗｔ％を超えると金属間化合物を作り、薄
板に加工することが困難になる為である。The reason for adding A1 to the decorative golden-colored copper alloy according to the present invention is that when At is alloyed with Cu, it forms a stable oxide film on the surface, improving corrosion resistance and producing a golden-colored alloy. This is because if it is less than 2 wt%, the effect will be weak, and if it exceeds 10 wt%, intermetallic compounds will be formed, making it difficult to process into a thin plate.
また、Ｚｎを添加した理由は、Ｚｎの添加によりＣｕ−
Ａ１合金の黄金色をさらに彩やかにすると共に機械的強
度を増加させる為であり、０．１ｗｔ％未満ではその効
果が薄く、２ｗｔ％を超えると耐食性が低下してくる為
である。Moreover, the reason why Zn was added is that the addition of Zn makes Cu-
This is to make the golden color of the A1 alloy more colorful and to increase its mechanical strength.If it is less than 0.1 wt%, the effect will be weak, and if it exceeds 2 wt%, the corrosion resistance will decrease.
また、貴金属を添加した理由は、貴金属の微量添加によ
りＣｕ−Ａｌ合金の耐食性をさらに向上させる為であり
、Ｏ，Ｏｈｔ％未満ではその効果が薄く、 １．８ｗｔ
％を超えてもあまり顕著な変化が見られなくなる為であ
る。ここで言う貴金属とは、Ａｕ。In addition, the reason for adding precious metals is to further improve the corrosion resistance of the Cu-Al alloy by adding a small amount of precious metals, and if it is less than 1.8wt%, the effect is weak.
This is because even if it exceeds %, no noticeable change is observed. The precious metal referred to here is Au.
Ａｇ、ＰＬ、Ｐｄ、Ｒ’ｈ、）マｕ、ｌｒ、Ｑｓを含め
てのことである。This includes Ag, PL, Pd, R'h, ) mu, lr, and Qs.
以下本発明による装飾用黄金色系銅合金の効果を明瞭な
らしめる為に実施例及び従来例について述べる。Examples and conventional examples will be described below in order to clarify the effects of the decorative golden copper alloy according to the present invention.
第１表に示す成分組成の実施例１〜４の装飾用黄金色系
銅合金と従来例１，２の装飾用黄金色系銅合金の色、加
工性、耐汗性についてテストしたところ第２表のような
結果を得た。The color, workability, and sweat resistance of the decorative golden copper alloys of Examples 1 to 4 and the conventional examples 1 and 2 with the compositions shown in Table 1 were tested. The results shown in the table were obtained.
（以下余白） 第１表 第２表 なお、人工汗試験はＮ Ｈ４ＣＩ １５．５ｇ ／β。(Margin below) Table 1 Table 2 In addition, the artificial sweat test is NH4CI 15.5g/β.
ＮａＣｌ２０ｇ／Ｉｌ、酢酸２．５ｇ ／ ｌ 、尿素
５ｇ／Ｃ乳酸１５ｇ／ｊ！、ＰＨ，４，７の液組成で液
温４０℃、２４０時間浸漬後判定した。NaCl 20g/Il, acetic acid 2.5g/l, urea 5g/C lactic acid 15g/j! Judgment was made after immersion for 240 hours at a liquid temperature of 40°C with a liquid composition of , PH, 4, 7.
上記で明らかなように本発明による装飾用黄金色系銅合
金は従来の装飾用黄金色系銅合金に比し、耐汗性、加工
性が優れ、かつ黄金色を有していることが判る。As is clear from the above, the decorative golden-colored copper alloy according to the present invention has superior sweat resistance and processability, and has a golden color, compared to conventional decorative golden-colored copper alloys. .
以上詳記した通り、本発明の装飾用黄金色系銅合金は、
耐汗性、加工性が優れかつ黄金色を有しているので、従
来の装飾用黄金色系銅合金にとって代わることのできる
画期的なものと言える。As detailed above, the decorative golden copper alloy of the present invention is
Because it has excellent sweat resistance, workability, and a golden color, it can be said to be an epoch-making product that can replace conventional decorative golden copper alloys.
出願人 田中貴金属工業株式会社Applicant: Tanaka Kikinzoku Kogyo Co., Ltd.
Claims (1)
飾用黄金色系銅合金。[Claims] 2 to 10 wt% aluminum, 0.1 to 2 wt% zinc. Kikai 11 = Decorative golden copper alloy consisting of 0.01 to 1.8 wt%, the balance being copper.