JPS6017067A - Method for providing gold color of plastic surface - Google Patents
Method for providing gold color of plastic surfaceInfo
- Publication number
- JPS6017067A JPS6017067A JP12376183A JP12376183A JPS6017067A JP S6017067 A JPS6017067 A JP S6017067A JP 12376183 A JP12376183 A JP 12376183A JP 12376183 A JP12376183 A JP 12376183A JP S6017067 A JPS6017067 A JP S6017067A
- Authority
- JP
- Japan
- Prior art keywords
- plastic surface
- yellow
- plastic
- gaseous
- gold color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
本発明け、プラスチック表面(黄金色を与える方法に関
する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for imparting a golden color to plastic surfaces.
装飾品またけ時計等のケースにおいて、プラスチックの
表面に黄金色の光沢を与える場合、一般にはプラスチッ
クの素地上にアルミニウムを蒸着又はスパッタリングに
より形成し、その上でその上に黄色の塗料を塗装し、最
後に透明の侶謹コーティング膜を形成する方法が一般的
である。しかしこの方法は工程数が多い欠点があった。To give the plastic surface a golden luster in the cases of ornamental watches, etc., aluminum is generally formed on the plastic base by vapor deposition or sputtering, and then a yellow paint is applied on top of that. A common method is to finally form a transparent coating film. However, this method had the drawback of requiring a large number of steps.
本発明け、プラスチック表面に黄金色の光沢が簡単VC
得られるようにすることを目的とするものである。With this invention, it is easy to create a golden luster on the plastic surface.
The purpose is to make it possible to obtain.
実施例について押切すると、プラスチック素材としては
黄色のABS樹脂を使用し、その上にアルゴンと少量の
酸素とを導入ガスとして、真空ベルジャ内で上記プラス
チック表面にチタンの反応性スパ・ツタリングを行った
。In the example, yellow ABS resin was used as the plastic material, and titanium was reactively sputtered onto the surface of the plastic in a vacuum belljar using argon and a small amount of oxygen as gases introduced thereon. .
反応性ユバ9タリングの条件
ターゲ・ノド チタン
真空II 5x10−’Toττ以下
0圧 (2〜B) x 10−’ TorrAr圧 5
×10″′BTorr
高周波入力パワー 800W
処理時間 〜 mtn
この反応性スパー74リングによってプラスチッり表面
VC200〜300オン〃°ヌトロームの酸化チlン購
が形成され、黄金色の光沢を呈17た。これ−酸化チタ
ン嘩が薄青味がかった透明をし、それが金属党派を有[
7ていることと、プラスチック素材の色とが融合して黄
金色の光沢を呈するものと思わhる。Conditions for reactive Yuva9taling Target/nod Titanium vacuum II 5x10-'Toττ or less 0 pressure (2~B) x 10-'TorrAr pressure 5
×10″'BTorr High frequency input power 800W Processing time ~ mtn This reactive spar 74 ring formed a tin oxide layer on the plastic surface with a VC of 200 to 300 on, giving it a golden luster17. -Titanium oxide is transparent with a bluish tinge, and it has metallic particles [
I believe that the combination of the color of the plastic material and the color of the plastic material gives it a golden luster.
またチ〃ン旬外にも二・ソケル、銅につ(ハても十5ビ
とほぼ回等の冬作で黄金色の光沢が得られることを確認
した。プラスチ9りけAB’S以外で本黄色士たけそれ
に近い色のものであれば適用可能である。また上記条件
において、入力パワーと処理時間け200〜300オン
グストロームの膜厚ヲ得る一例に過ぎず、適宜に変更す
ることができる。It has also been confirmed that a golden luster can be obtained with winter crops such as 2, Sokel, and Copper Nitsu (at least 15 Bis). It can be applied as long as the color is close to that of the actual yellow color.In addition, under the above conditions, the input power and processing time are only an example of obtaining a film thickness of 200 to 300 angstroms, and can be changed as appropriate. .
この発明によれば、スパッタリングの工程だけでプラス
チック表面に全光沢を簡単に与えることができ、金メ・
ツキの代替として装飾品や時計ケースに低コストで利用
できる。According to this invention, full gloss can be easily imparted to the plastic surface with just the sputtering process, and gold plated and
It can be used as a low-cost substitute for decorations and watch cases.
以 上 出願人 株式会社 精 工 舎 代理人 弁理士 最上 務 3−that's all Applicant Seikosha Co., Ltd. Agent Patent Attorney Mogami 3-
Claims (1)
ッケル、銅の中のいずれかの金属を、黄色またはそれに
近い色のプラスチック表面に反応性スパッタリングし、
上記プラスチック表面に上記金属の酸化膜を200〜3
00オングストロームの厚さで形成することを特徴とす
るプラスチック表面に黄金色を与える方法、Argon and a small amount of oxygen are introduced as gases to reactively sputter a metal among titanium, nickel, and copper onto a yellow or nearly yellow plastic surface.
An oxide film of the above metal is applied to the surface of the above plastic by 200 to 3
A method for imparting a golden color to a plastic surface, the method comprising: forming a plastic surface with a thickness of 0.00 angstroms;