JPS60147446A - Antifogging treatment of cellulose triacetate plastic sheet material - Google Patents
Antifogging treatment of cellulose triacetate plastic sheet materialInfo
- Publication number
- JPS60147446A JPS60147446A JP241584A JP241584A JPS60147446A JP S60147446 A JPS60147446 A JP S60147446A JP 241584 A JP241584 A JP 241584A JP 241584 A JP241584 A JP 241584A JP S60147446 A JPS60147446 A JP S60147446A
- Authority
- JP
- Japan
- Prior art keywords
- sheet material
- cellulose triacetate
- plastic sheet
- cellulose
- pref
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
この発明はセルローストリアレデートプラスデックシー
ト状物の防曇処理方法に関りるものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for antifogging treatment of cellulose trialedate plus deck sheets.
最近一般用ゴーグル、防塵メガネ、Ａ−トパイ用ゴーグ
ル、風防メガネ、水中メガネ等多くの分野で防曇性能を
有するプラスデック成形物が使用されている。これらの
大部分はセルロースジアセテートのシート状物またはセ
ルロースプロピオネートのシート状物を公知の方法（例
えばＵＳＰ３、７００，４６７＞で鹸化することにより
、該シート状物の吸水性を高め、半永久的な防曇性を附
与したものを使用している。Recently, PlusDeck molded products having anti-fog properties have been used in many fields such as general goggles, dust-proof glasses, A-topie goggles, windshield glasses, and underwater glasses. Most of these are made by saponifying a sheet of cellulose diacetate or cellulose propionate using a known method (for example, US Pat. A material with anti-fog properties is used.
しかしながら、セルロースジアセテートやセルロースプ
ロピオネートは耐水性、寸法安定性に劣っており、時に
高温多湿の条件下で長時間使用した場合に成形物の変形
が起り易い欠点がある。However, cellulose diacetate and cellulose propionate are inferior in water resistance and dimensional stability, and sometimes have the disadvantage that molded products tend to deform when used for long periods of time under hot and humid conditions.
このような観点から本発明者は従来用いられているセル
ロースジアセテートやセルロースプロピ・オネートに代
り、耐水性、寸法安定性、さらには耐熱性にすぐれたセ
ルロー支トリアセテートのシート状物の防曇処理法につ
いて研究した結果、この発明に至ったものである。また
この発明は防曇性能を附与できないプラスチック成形物
、例えばポリカーボネート成形物、アクリル成形物、ポ
リ塩化ビニル成形物等にセルローストリアセテートシー
ト状物を積層することにより防曇性を附与することをも
目的どしている。From this point of view, the present inventor developed an antifogging treatment for cellulose triacetate sheets, which have excellent water resistance, dimensional stability, and heat resistance, in place of the conventionally used cellulose diacetate and cellulose propionate. This invention was arrived at as a result of research on the law. The present invention also proposes that anti-fog properties can be imparted to plastic molded products that cannot be provided with anti-fog properties, such as polycarbonate molded products, acrylic molded products, polyvinyl chloride molded products, etc., by laminating cellulose triacetate sheet materials. I also have a purpose.
しかして従来セルローストリアレデートは従来公知とさ
れる鹸化方゛法ではセルロースジアセデートやセルロー
スプロビオネートに比べて鹸化されにり＜、従って十分
な防曇性を与えることができなかった。However, conventionally, cellulose trialedate was less saponified than cellulose diacedate or cellulose probionate by the conventionally known saponification methods, and therefore it was not possible to provide sufficient antifogging properties.
本発明者はこのようなセルロースジアセデートにういそ
いかに経済的に期待する防曇性を削りすることができる
かを鋭意研究を行なった結果、本発明を得たものである
。The present inventors have conducted intensive research to find out how cellulose diacedate can be economically improved in its expected antifogging properties, and as a result, the present invention was obtained.
即ちこの発明は水１ｏｏｏ’ｔに対し、水酸化ナトリウ
ムまたは／および水酸化カリ？ムを５０７乃、至。That is, this invention uses sodium hydroxide and/or potassium hydroxide per 100' of water. From 507 to 507.
４００Ｇ 、ベンジルアルコールを、１０２乃至１０Ｈ
添加した溶液を３０℃から９０℃に維持し、この溶液に
セルローストリアセテートプラスデックシー１〜状物を
５分から６０分間浸漬することを特徴どするヒルロース
トリアセテートプラスチックシート状物の防曇処理方法
である。400G, benzyl alcohol, 102 to 10H
A method for antifogging treatment of a hiluro triacetate plastic sheet, characterized by maintaining the added solution at a temperature of 30°C to 90°C, and immersing a cellulose triacetate plus deck sheet in this solution for 5 to 60 minutes. be.
本発明者はこの発明に至るまでに水酸化ナトリウムおよ
び／または水酸化カリウムの水溶液のみにセルロースト
リアセテートプラスチックシート状物を浸漬したのでは
期待する防曇性能が得られなかった。そこで水酸化すト
リウムおよび／または水酸化カリウムに各種のアルコー
ルおよびその化合物、さらにその他の湿潤剤、浸透剤等
を加えることにより目的の性能を短時間に（ｑられない
か研究奮行なったところ、ベンジルアルコールが最も良
いことが認められた。Until this invention, the inventors had discovered that the expected antifogging performance could not be obtained by immersing a cellulose triacetate plastic sheet only in an aqueous solution of sodium hydroxide and/or potassium hydroxide. Therefore, by adding various alcohols and their compounds, as well as other wetting agents and penetrants to thorium hydroxide and/or potassium hydroxide, we conducted extensive research to see if the desired performance could be achieved in a short period of time. Benzyl alcohol was found to be the best.
この発明において使用できるトリアセテートプラスチッ
クとしては、一般にトリアセテートと表示される。もの
□総てを含むものであり、またシート状に加エキ゛れた
ものであれば総てその中に含まれる。The triacetate plastic that can be used in this invention is generally referred to as triacetate. It includes everything, and anything that has been processed into a sheet is included in it.
水酸化ナトリウムまたは水酸化カリウムはそれぞれ単独
または併用で使用できるが、その量は水１ｏｏｏｓに対
し５０５＃以下では防曇性を十分に附与することができ
ず、また４００７以上ではセルローストリア０テートシ
ート状物０表面１肌荒れ８か縮 ｒみを発生させるため
、５０′）乃至４００２がよく、特に好ましくは１００
２乃至２５０２の範囲である。Sodium hydroxide or potassium hydroxide can be used alone or in combination, but if the amount is less than 505# per 1ooos of water, it will not be able to provide sufficient antifogging properties, and if it is more than 4007#, it will not be possible to impart sufficient antifogging properties. 50') to 4002 are preferred, particularly preferably 100 to cause surface roughness or shrinkage of the sheet material.
The range is from 2 to 2502.
またベンジルアルコールの添加ωは１０２以下では防曇
性を附与することができず、また １００′ｉ＃以上で
はセルローストリアレデートシー１〜状物を変形させる
と共に表面の肌を荒れさせ、商品価値を低下させてしま
うため１０′ｉＩ乃至１０’ｉがにり、特に３０２乃至
５０２が好ましい範囲である。さらにこの溶液温度は、
３０〜９０℃（好ましくは４５〜７５℃）の範囲が適当
である。なぜならこの温度が３０℃以下では十分な防曇
性能が得られず、まｌζ９（）℃以Ｊ−では縮みや変形
が生じるためである。また浸ＫＪ １１．？闇は５分以
下では十分な防曇性能が得られず、６０分以上ではセル
ローストリアセテ−１〜シーＩ・状物に白化が発生し、
更に変形が生じるため好ましくない。好ましくは１５〜
４０分の範囲が適当である。Furthermore, if the addition ω of benzyl alcohol is less than 102, it will not be possible to impart antifogging properties, and if it is more than 100'i#, it will deform the cellulose trialedate sheet 1~ and roughen the surface skin, making the product 10'iI to 10'i is preferable, and 302 to 502 is particularly preferable because it reduces the value. Furthermore, the temperature of this solution is
A range of 30 to 90°C (preferably 45 to 75°C) is suitable. This is because if the temperature is below 30°C, sufficient antifogging performance cannot be obtained, and if the temperature is below 9()°C, shrinkage or deformation occurs. Also soaked KJ 11. ? If the darkness is less than 5 minutes, sufficient antifogging performance cannot be obtained, and if it is more than 60 minutes, whitening will occur in the cellulose triacetate-1 to C-I.
Further, deformation occurs, which is not preferable. Preferably 15~
A range of 40 minutes is appropriate.
この発明によって得れたセル［Ｊ −２１−リア上テー
トプラスチックシート状物はセルロースジアレテートプ
ラスチック成形物のような耐水性、耐熱性の欠点がなく
、従って高温多湿の条件下であっても使用に耐え得るも
のである。このため用途も従来使用されているゴーグル
、風防メツＪネｔｑ、のみならず、水中メガネのレンズ
としても使用できる。The cell [J-21-Ria upper tate plastic sheet material obtained by this invention does not have the disadvantages of water resistance and heat resistance unlike cellulose dialtate plastic molded products, and therefore can be used even under hot and humid conditions. It is durable for use. Therefore, it can be used not only for conventional goggles and windshield glasses, but also as lenses for underwater glasses.
またセルローストリアレテートプラスデックシート状物
と他のプラスデックシートどの積層をすることにより浴
室や温室用ガラス、歯科医師用内Ｍ４＃１１あるいは歯
ブラシ他端に結句りる内視鏡等にも使用することができ
る。In addition, by laminating cellulose trialretate PlusDeck sheets with other PlusDeck sheets, it can be used for glass for bathrooms and greenhouses, M4 #11 for dentists, or endoscopes attached to the other end of toothbrushes. can do.
、次にこの発明を実施例を挙げて具体的に１２萌する。Next, this invention will be explained in detail by giving 12 examples.
実施例１〜３
セルローストリアセテートプラスチックフィルム（１５
０Ｘ １５０Ｘ’０．２ｍ４）を第１表に示す方法に°
Ｃ防曇処理を施した。これを温度４０℃、相対湿度９５
％の雰囲気中に置き、その表面に曇りが生ず゛るまでの
時間を測定した。ｔの結果は第１表の通りであった。Examples 1-3 Cellulose triacetate plastic film (15
0X 150X'0.2m4) according to the method shown in Table 1.
C anti-fog treatment was applied. This is done at a temperature of 40°C and a relative humidity of 95.
% atmosphere and the time required for the surface to become cloudy was measured. The results of t are shown in Table 1.
なお比較例１．２は第１表に示す処理液組成について実
施例と同様に処理したものである。In Comparative Example 1.2, the treatment was performed in the same manner as in the Example using the treatment liquid composition shown in Table 1.
Claims (1)
よび水酸化カリウムを５０〜４００牙、ベンジルアルコ
ールを１０〜１００牙添加した溶液を３０〜９０℃に紺
竺し、この溶液にセルローストリアレチードブシスナッ
クシート状物を５〜６０分間浸）６゛りることを特徴と
するセルローストリアセテ−１へプラスチックシート状
物の防曇処理方法。A solution of 1-lium hydroxide/and potassium hydroxide added at 50-400 g and benzyl alcohol at 10-100 g is heated to 30-90°C, and this solution is heated to iooo't. 1. A method for antifogging treatment of a plastic sheet material to cellulose triacetate, which comprises soaking the cellulose triacetate plastic sheet material for 5 to 60 minutes.