JPS59179734A - Sliding contact material - Google Patents

Sliding contact material

Info

Publication number
JPS59179734A
JPS59179734A JP58052866A JP5286683A JPS59179734A JP S59179734 A JPS59179734 A JP S59179734A JP 58052866 A JP58052866 A JP 58052866A JP 5286683 A JP5286683 A JP 5286683A JP S59179734 A JPS59179734 A JP S59179734A
Authority
JP
Japan
Prior art keywords
weight
sliding contact
contact material
contact
alloy material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP58052866A
Other languages
Japanese (ja)
Other versions
JPH0259226B2 (en
Inventor
Susumu Fujishima
藤嶋 進
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tanaka Kikinzoku Kogyo KK
Original Assignee
Tanaka Kikinzoku Kogyo KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tanaka Kikinzoku Kogyo KK filed Critical Tanaka Kikinzoku Kogyo KK
Priority to JP58052866A priority Critical patent/JPS59179734A/en
Publication of JPS59179734A publication Critical patent/JPS59179734A/en
Publication of JPH0259226B2 publication Critical patent/JPH0259226B2/ja
Granted legal-status Critical Current

Abstract

PURPOSE:To improve the wear resistance of the resulting sliding contact material by adding small amounts of Sb and one or more among Si, Bi, Ge and Ga to an alloy material having a specified composition consisting of Au, Ag and Cu. CONSTITUTION:This sliding contact material is obtd. by adding, by weight, 1- 10% Sb and 0.1-3% one or more among Si, Bi, Ge and Ga to an alloy material consisting of 61.5-63.5% Au, 28-30% AG and 7.5-9.5% Cu without changing the ratio in the composition. To the alloy material may be further added 0.01- 0.5% Fe group metal. This sliding contact material can give a brush contact which causes a smaller extent of wear than a brush contact made of a conventional sliding contact material and has comparably low and stable contact resistance.

Description

【発明の詳細な説明】 本発明は、摺動接点材料の改良に関する。[Detailed description of the invention] The present invention relates to improvements in sliding contact materials.

従来、摺動接点材料としては各種材料が用いられ、とり
わけ刷子接点用の材料としては、A u 61.5〜6
3.5重量%、A328〜30重量%、  Cu 7.
5〜9.5重量%より成る合金材料が広く用いられてい
た。
Conventionally, various materials have been used as sliding contact materials, and in particular, as materials for brush contacts, A u 61.5-6
3.5% by weight, A328-30% by weight, Cu 7.
Alloy materials consisting of 5-9.5% by weight were widely used.

然し乍ら、この合金材料で製作した刷子接点では、整流
子との摺動時の耐摩耗性が劣り、摩耗粉が生じ易く、ノ
イズ発生の原因となっζいた。
However, brush contacts made of this alloy material have poor abrasion resistance when sliding with the commutator, and are likely to generate abrasion powder, causing noise.

本発明は、斯かる欠点を解消すべくなされものであり、
前記合金材料を基材としてこれに特定の材料を僅かに添
加させて、耐摩耗性を向」―させた摺動接点材料を提供
せんとするものである。
The present invention has been made to eliminate such drawbacks,
The present invention aims to provide a sliding contact material whose wear resistance is improved by adding a small amount of a specific material to the alloy material as a base material.

本発明の摺動接点材料の1つは、A u 61.5〜6
3.5重量%、Ag28〜30重量%、 Cu 7.5
〜9.5重量%より成る合金材料に、その組成比に変更
を加えずに、sbを1〜10重量%とSi、Bi、Ge
One of the sliding contact materials of the present invention has an A u of 61.5 to 6
3.5% by weight, Ag28-30% by weight, Cu 7.5
~9.5% by weight of sb and Si, Bi, Ge without changing the composition ratio.
.

Gaの少なくとも一種を0.1〜3市量重量加して成る
ものである。
It is made by adding at least one type of Ga in an amount of 0.1 to 3 by weight.

本発明の摺動接点材料の他の1つば、A u 61.5
〜63.5重量%、Ag28〜30重量%、CIJ7.
5〜9.5重量%より成る合金材料に、その組成比に変
更を加えずに、sbを1〜10重量%とSi、Bi、G
e−Gaの少なくとも一種を0.1〜3重量%添加し、
さらにFe族金属を0.01〜0.5重量%添加して成
を超えてもそれ以上の効果が(Mられないからである。
Another member of the sliding contact material of the present invention, A u 61.5
~63.5% by weight, Ag28-30% by weight, CIJ7.
Adding 1 to 10% by weight of sb and Si, Bi, G to an alloy material consisting of 5 to 9.5% by weight without changing the composition ratio.
Adding 0.1 to 3% by weight of at least one type of e-Ga,
Furthermore, even if 0.01 to 0.5% by weight of Fe group metal is added, no further effect can be obtained.

次に下記の左欄に示す成分組成の本発明による摺動接点
材料と従来の摺動接点材料を用いて夫々線径0.7mm
の刷子線材を作り、これを各々長ざ8mmに切断し、2
本並列させて一端を柘ロQmm、長さ13fi、厚さ0
.2鶴の含料に熔接し、他端に2Rの円弧状の接触部を
曲成して刷子接点を作った。そして夫々の刷子接点を円
盤状の整流子に接触させ、整流子を正逆回転させて下記
の試験条件にて摺動試験を行い、摩耗量及び接触抵抗を
測定した処、下記の表の右欄に示すような結果を得た。
Next, using the sliding contact material according to the present invention and the conventional sliding contact material having the compositions shown in the left column below, each wire diameter was 0.7 mm.
Make brush wire rods, cut each into 8 mm length, and
These are placed in parallel and one end is 4mm long, 13fi long, and 0 thick.
.. A brush contact was made by welding to the 2-tsuru material and bending a 2R arc-shaped contact portion at the other end. Then, each brush contact was brought into contact with a disk-shaped commutator, and the commutator was rotated in forward and reverse directions to perform a sliding test under the following test conditions, and the wear amount and contact resistance were measured. The results shown in the column were obtained.

試験条件 電   流 :   0.6A 電    圧  :  12■ 負    荷  :  抵抗負荷 回転速度  :  ]、000r p m周    速
  :    130〜120 m/min接触カニ 
 100g 試験時間  :  7時間
Test conditions Current: 0.6 A Voltage: 12 ■ Load: Resistance load Rotational speed: ], 000 rpm Peripheral speed: 130-120 m/min Contact crab
100g Test time: 7 hours

Claims (1)

【特許請求の範囲】 1 )  A u 61.5〜63.5重量%、Ag2
8〜30重量%。 CLl 7.5〜9.5重量%より成る合金材料に、そ
の組成比に変更を加えずにsbを1〜10重量%と3i
。 Bi、Ge、Gaの少なくとも一種を0.1〜3重量%
添加して成る摺動接点材料。 2 )  A u 61.5〜63.5重量%、Ag2
8〜30重量%。 Cu 7.5〜9.5重量%より成る合金材料に、その
組成比に変更を加えずにSbを1〜10重量%と3i。 Bi、Ge、Gaの少なくとも一種を0.1〜3重量%
添加し、さらにFe族金属を0.01〜0,5重量%添
加して成る摺動接点材料。
[Claims] 1) A u 61.5-63.5% by weight, Ag2
8-30% by weight. 3i is added to an alloy material consisting of 7.5 to 9.5 wt% of CLl with 1 to 10 wt% of sb without changing the composition ratio.
. 0.1 to 3% by weight of at least one of Bi, Ge, and Ga
Sliding contact material made of additives. 2) Au 61.5-63.5% by weight, Ag2
8-30% by weight. 3i, an alloy material consisting of 7.5 to 9.5% by weight of Cu and 1 to 10% by weight of Sb without changing the composition ratio. 0.1 to 3% by weight of at least one of Bi, Ge, and Ga
A sliding contact material made by adding Fe group metal in an amount of 0.01 to 0.5% by weight.
JP58052866A 1983-03-29 1983-03-29 Sliding contact material Granted JPS59179734A (en)