JPS591348A - Vessel with spout, adhesive strength thereof is controlled - Google Patents
Vessel with spout, adhesive strength thereof is controlledInfo
- Publication number
- JPS591348A JPS591348A JP57106230A JP10623082A JPS591348A JP S591348 A JPS591348 A JP S591348A JP 57106230 A JP57106230 A JP 57106230A JP 10623082 A JP10623082 A JP 10623082A JP S591348 A JPS591348 A JP S591348A
- Authority
- JP
- Japan
- Prior art keywords
- spout
- resin
- adhesive strength
- container
- controlled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
近年、牛乳、酒、塩など液体あるいは粉体容器として、
ポリエチレンなどの可塑性樹脂層を有する板紙を素材と
する密封容器が用いられている。[Detailed Description of the Invention] In recent years, containers for liquids or powders such as milk, alcohol, salt, etc.
Sealed containers made of paperboard with a layer of plastic resin such as polyethylene are used.
この容器は熱圧着によって形成されるために、注出口も
強く接着される。このため、開口時に相当の力が必要で
あり、捷た・注出口部分を損傷して醜くなったり、板紙
のカスが内容物に混入するなどの欠点があった。この欠
点を改善するために注出口となるべき個所にポリシロキ
サン、環化ゴムと微量のポリシロキサン、環化ゴムとリ
ン脂質などの芳香族系、ケトン系、エステル系などの有
機溶媒浴液を塗布し、接着力を制御する試みがなされて
いる(例えば、特公昭44−15076号公報、特公昭
51−30831号公報、特公昭51−35466号公
報)。Since this container is formed by thermocompression bonding, the spout is also strongly bonded. Therefore, a considerable amount of force is required to open the container, and there are disadvantages such as damage to the spout and the unsightly portion of the spout, and paperboard scraps getting mixed into the contents. In order to improve this drawback, use an organic solvent bath liquid such as polysiloxane, cyclized rubber and a trace amount of polysiloxane, cyclized rubber and aromatic, ketone, ester, etc. Attempts have been made to control the adhesion force by coating (for example, Japanese Patent Publication No. 44-15076, Japanese Patent Publication No. 51-30831, and Japanese Patent Publication No. 51-35466).
しかしながら、上記のような芳香族系などの有機溶剤の
残留により、特に内容物が食品である場合に味覚を損な
うおそれがあり、また接着力の制御機能も不十分である
という問題点が残っていた。However, there remain problems such as the residual aromatic and other organic solvents mentioned above may impair the taste, especially when the content is food, and the ability to control adhesive strength is insufficient. Ta.
本発明は上記問題点の解決のため研究によって完成され
−たものであり、内外面に熱可塑性樹脂層を有する板紙
を素材とする容器であり、熱圧着により容器を作製する
にあたり、注出口となるべき個所に、アルコール可溶性
耐熱性樹脂皮膜を施してなることを特徴とする接着強度
′r副制御た注出口を有する容器を提供するものである
。The present invention was completed through research to solve the above problems, and is a container made of paperboard with thermoplastic resin layers on the inner and outer surfaces. The purpose of the present invention is to provide a container having a pouring spout whose adhesive strength 'r is sub-controlled, which is characterized by being coated with an alcohol-soluble heat-resistant resin film at the desired location.
本発明におけるアルコール可溶性耐熱性樹脂トシテは、
ニトロセルロースなどの繊維素系樹脂、ポリビニルエー
テル、マレイン酸系樹脂、ブチラール系樹脂、ケトン樹
脂、フェノール系tff4 脂、アルキド系樹脂、ポリ
ウレタン系樹脂、ポリアミド系樹脂などが単独もしくは
併用して用いられるが、特にニトロセルロース、ブチラ
ール樹脂、アルキド樹脂が、作業性の面から好ましい。The alcohol-soluble heat-resistant resin toshite in the present invention is
Cellulose resins such as nitrocellulose, polyvinyl ether, maleic acid resins, butyral resins, ketone resins, phenolic TFF4 resins, alkyd resins, polyurethane resins, polyamide resins, etc. are used alone or in combination. In particular, nitrocellulose, butyral resin, and alkyd resin are preferred from the viewpoint of workability.
これらの樹脂は、板紙上の熱可塑性樹脂の融点よりも5
0℃以上、好ましくは100℃以上の高い融点を有する
ものから選択することが好捷しい。These resins have a melting point of 5
It is preferable to select from those having a high melting point of 0°C or higher, preferably 100°C or higher.
これらの樹脂はアルコール系溶剤に固型分10〜40重
量%、好ましくは15〜30重量%の溶液となるよう調
製し、印刷によって注出口となるべき部分に施す。この
溶液には脂肪酸ワックス、ポリエチレンワ、クスf:3
0重量%以下、オルガノボリンロキサンなどを5重量%
以下を溶lIJイもしくは微分散状態で添加することが
できる。These resins are prepared as a solution in an alcoholic solvent with a solid content of 10 to 40% by weight, preferably 15 to 30% by weight, and applied by printing to the area to be used as the spout. This solution contains fatty acid wax, polyethylene wax,
0% by weight or less, 5% by weight of organoborin loxane etc.
The following can be added in a dissolved or finely dispersed state.
上記樹脂溶液を容器口部に施すには自体公知の印刷方式
、塗布方式が適用できる、例えばグラビアコーター、フ
レキソコーター、ロールコータ−などがある。塗布量は
成分によっても異なるが乾燥量で、0.5〜59/lr
?、好捷しくは1.5〜3.597m″である。In order to apply the above-mentioned resin solution to the mouth of the container, a printing method or a coating method known per se can be applied, such as a gravure coater, a flexo coater, a roll coater, and the like. The amount applied varies depending on the ingredients, but the dry amount is 0.5 to 59/lr.
? , preferably 1.5 to 3.597 m''.
本発明に係る容器は、衛生性、臭気などの面知おいて改
善され、口部の剥離強度を0.05〜0、15 Kf
/ crlの容易に引き剥がせるよう調整することがで
きる。The container according to the present invention has improved hygiene and odor, and has a peel strength of 0.05 to 0.15 Kf at the mouth.
/ It can be adjusted so that the crl can be easily peeled off.
以下実施例によって本発明を具体的に説明する。例中部
は重量部を示す。EXAMPLES The present invention will be specifically explained below with reference to Examples. The middle part of the example shows parts by weight.
実施例1
下記各々の処方の樹脂組成物をポリエチレンによってサ
ンドウィッチされた板紙に塗布し、乾燥して膜厚約2.
Of/n?の樹脂皮膜を設けた、。Example 1 A resin composition having each of the following formulations was applied to a paperboard sandwiched with polyethylene and dried to a film thickness of about 2.5 mm.
Of/n? with a resin film.
この樹脂皮膜面に他のポリエチレンにサントウィッチさ
れた板紙とを重ね合わせ、230℃、40ボンド/cA
、3秒の条件で加熱圧着した。A paperboard sandwiched with other polyethylene was superimposed on this resin film surface at 230°C, 40 bonds/cA.
The bonding was carried out under heat and pressure for 3 seconds.
この剥離強度はT剥離試験で測定した。剥離において板
紙の損傷はなかった。This peel strength was measured by a T peel test. There was no damage to the paperboard during peeling.
処 方1
ニトロセルロース 10部
ブチラール樹脂 2〃
アルキド樹脂 14#
エタノール 40〃
メタノール 24#
エチルセロソルブ 10〃
剥離強度 0.10 Kg/crl
処 方2
ニトロセルロース 10 部
ウレタン樹脂 10 〃
ヒマシ油 0,5〃エタノール
50 〃
メタノール 19.5#
工チル七日ソルブ 10 〃
剥離強度 0.11に?/ca
処 方3
ブチラール樹脂 lO部
ポリアミド拉1脂 10 部エタノール
10 〃
n−グロパノール 40 〃
ブチルセロソルブ 5 〃
消 泡 剤 0.5〃イ
ソプロパツール 24.5#
剥離強度 0.07 Kg/lri
処 方4
ニトロセルロース 10 部
アルキド樹脂 10 〃
ブチラール樹脂 5 〃
ポリエチレンワックス 2 〃
ジメチルポリシロキサン 0.01 〃メチルセロ
ソルブ 10 〃
メタノール 23 〃
エタノール 40 〃
剥離強度 0.08 K9/crl
処 方5
ニトロセルロース 20 部
アルキド樹脂 10 〃
ウレタン樹脂 5 部
ポリエチレンワックス 2 〃レンチン
0.1〃メチルセロソルブ
10 〃
メタノール 13 I
エタノール 40 〃
剥離強度 0.10 Kg/crl
処 方6
ポリアミド樹脂 20 部
ニトロセルロース 7 〃
ポリエチレンワックス 2 〃脂肪酸ワック
ス 1.5〃ブチルセロソルブ
5 〃
n−プロパツール 50 #
エタノール 15 〃
離剥強度 0.08Kg/ca
特許出願人 東洋インキ製造株式会社Formula 1 Nitrocellulose 10 parts Butyral resin 2 Alkyd resin 14# Ethanol 40 Methanol 24# Ethyl cellosolve 10 Peel strength 0.10 Kg/crl Recipe 2 Nitrocellulose 10 parts Urethane resin 10 Castor oil 0.5 ethanol
50 〃 Methanol 19.5# Kochiru Seven Day Solve 10 〃 Peel strength 0.11? /ca Prescription 3 Butyral resin 10 parts Polyamide 1 fat 10 parts Ethanol
10 N-gropanol 40 Butyl cellosolve 5 Antifoaming agent 0.5 Isopropanol 24.5# Peel strength 0.07 Kg/lri Formula 4 Nitrocellulose 10 parts Alkyd resin 10 Butyral resin 5 Polyethylene wax 2 Dimethylpolysiloxane 0.01 Methyl cellosolve 10 Methanol 23 Ethanol 40 Peel strength 0.08 K9/crl Formula 5 Nitrocellulose 20 parts Alkyd resin 10 Urethane resin 5 parts Polyethylene wax 2 Lentin
0.1〃Methyl cellosolve
10 Methanol 13 I Ethanol 40 Peel strength 0.10 Kg/crl Formula 6 Polyamide resin 20 parts Nitrocellulose 7 Polyethylene wax 2 Fatty acid wax 1.5 Butyl cellosolve
5 〃 n-propatool 50 # Ethanol 15 〃 Peeling strength 0.08Kg/ca Patent applicant Toyo Ink Mfg. Co., Ltd.
Claims (1)
る容器であり、熱圧着により容器を作製するにあたり、
注出口となるべき個所に、アルコール可溶性耐熱性樹脂
皮膜を施してなることを特徴とする接着強度を制御した
注出口を有する容器。(1) A container made of paperboard with thermoplastic resin layers on the inner and outer surfaces, and when producing the container by thermocompression bonding,
A container having a pouring spout with controlled adhesive strength, characterized in that a portion of the spout is coated with an alcohol-soluble heat-resistant resin film.