JPS5894403A - Manufacture of aggregate decorative veneer - Google Patents
Manufacture of aggregate decorative veneerInfo
- Publication number
- JPS5894403A JPS5894403A JP19317881A JP19317881A JPS5894403A JP S5894403 A JPS5894403 A JP S5894403A JP 19317881 A JP19317881 A JP 19317881A JP 19317881 A JP19317881 A JP 19317881A JP S5894403 A JPS5894403 A JP S5894403A
- Authority
- JP
- Japan
- Prior art keywords
- veneer
- modulus
- young
- veneers
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
〔発明の目的〕
圧力の不均一による接着不良・をなくすることのできる
集成化粧単板の製法を提供することを目的とする。[Detailed Description of the Invention] [Object of the Invention] An object of the invention is to provide a method for manufacturing a laminated decorative veneer that can eliminate poor adhesion due to uneven pressure.
従来より知られている集成化粧単板の製法は、単板を接
着剤を介して積層すると共に、一定の曲率を有する凹型
$よび凸型の対からなる型版に挾んで圧締し、フリッチ
を得て、ξれをスライスすることより成り立っている。The conventionally known manufacturing method for laminated decorative veneers involves laminating the veneers with an adhesive, sandwiching them between molds consisting of a pair of concave and convex shapes with a certain curvature, and pressing them together to form a flitch. It consists of obtaining ξ and slicing ξ.
第1図はその実例を示す略図であり、1は上型で下に凸
の型面を有する。2は下型であり、凹型の面を有してい
る。この上、下1対の型版の間に、単板を挾んで圧締す
ると、図のような端部の(A1部分では圧力が高く、中
央部の(111部分では圧力が低い。(〜部分で印加さ
れる圧力を支えてしまうからである。このような圧力の
不均一が生じると、(11部分が圧締不充分と匁り接着
不良の問題が生じる。FIG. 1 is a schematic diagram showing an example thereof, and 1 is an upper mold having a downwardly convex mold surface. 2 is a lower mold and has a concave surface. When a veneer is sandwiched and pressed between the upper and lower pair of mold plates, the pressure is high at the end (A1 part) and low at the central part (111 part) as shown in the figure. This is because the pressure applied to the part is supported. If such unevenness of pressure occurs, the problem arises that the part 11 is insufficiently pressed and has poor adhesion.
また圧力のかかり易い(II!部では単板の破壊が生じ
、良質の化粧単板が得られない欠点があった。In addition, pressure was easily applied (in the II! section, the veneer was destroyed, making it impossible to obtain a high-quality decorative veneer).
本発明は圧力のかかり易い部分に相当する単板の部分に
ヤング率の小さい材質のものを配置し、圧力のかかりに
くい部分く相当する単板の部分にヤング率の大きい材質
のものを配置して繋ぎ合わせてなる単板を用いることを
特徴とする以下詳しく説明する。第1図に基づいて説明
したよう番こ、型版内(〜部は圧力がかかり易いので、
本発明ではこの部分に配置される単板の部分はヤング率
が小さく、(B1部に位置する単板としてはヤング率の
大奮いものを使用する。つまり、そのような性質の単板
を繋ぎ合わせて1枚の単板となして用いるのである。In the present invention, a material with a small Young's modulus is arranged in the part of the veneer that corresponds to the part where pressure is easily applied, and a material with a large Young's modulus is arranged in the part of the veneer which corresponds to the part where pressure is not easily applied. This method is characterized by the use of veneers made by joining two pieces together, and will be described in detail below. As explained based on Fig. 1, pressure is easily applied to the inside of the plate and mold plate (~), so
In the present invention, the veneer placed in this part has a small Young's modulus (the veneer located in the B1 part is a veneer with a large Young's modulus. In other words, veneers with such properties are connected Together, they are used as a single veneer.
第2図は以上のような観点より形成された単板を示す斜
視図であり、この図で外側の(A1部がヤング率の小さ
い材質、中央の(B1部がヤング率の大きい材質の単板
を配置した例を示している。型版の形状によっては、こ
のような配置を取らない場合もある。このような繋いだ
単板を造るには、たとえば2種の材種の興なる単板をパ
ッチワークにより糸で縫い合わして造る。あるいは、角
材を予め接着剤で接着しておき、これをスライスして造
ってもよい。FIG. 2 is a perspective view showing a veneer formed from the above perspective. In this figure, the outer (A1 part) is made of a material with a small Young's modulus, and the central (B1 part) is made of a material with a large Young's modulus. An example of how the boards are arranged is shown.Depending on the shape of the template, this arrangement may not be possible.To make such a connected veneer, for example, it is necessary to It is made by sewing boards together with thread in a patchwork manner.Alternatively, it can be made by gluing square pieces of wood together in advance and slicing them.
なお、ヤング率の大小は相対的な問題であり、かつ材の
産地や含水率、厚みによって異なるので実状に合わせて
調整する。The magnitude of Young's modulus is a relative issue and varies depending on the production area, moisture content, and thickness of the material, so it should be adjusted according to the actual situation.
実施例1
第2図(〜部にあたる単板として、パパヤト産(圧縮ヤ
ング率250〜4001、含水率45%、板厚1.01
)のアガチス(南洋材)を、第2図(B)部に相当する
単板としてハルマヘラ産(圧縮ヤング率100〜250
4/d 、含水率45%、板厚1.0 m )のアガチ
ス(南洋材)を、それぞれ使用し、パッチワークにより
繋いで1枚の単板に仕上げた。以下、常法に従い積層圧
締してフリッチを得、スライスして化粧単板を得た。Example 1 Figure 2 (~ section) The veneer from Papayato (compressive Young's modulus 250-4001, moisture content 45%, board thickness 1.01
) from Halmahera (compressive Young's modulus 100-250) as a veneer corresponding to the part (B) in Figure 2.
4/d, moisture content 45%, board thickness 1.0 m) agathis (South Sea wood) was used and connected by patchwork to form a single veneer. Thereafter, flitches were obtained by laminating and pressing according to a conventional method, and decorative veneers were obtained by slicing.
実施例2
第2図(〜部に当る単板としてアガチス(パパヤト産)
の含水率的45%の単板(圧縮ヤング率150〜400
1り、板厚1.0閤)を、(Bj部に当る単板として、
同じアガチスの含水率的25%の単板(圧縮ヤング率4
00〜60014/d 、板厚1.0■)を、それぞれ
使用し、パッチワークにより繋いで1枚の単板とし、常
法により積層圧締、スライスして化粧単板を得た。Example 2 Figure 2 (Agathis (from Papayato) as a veneer corresponding to ~ section
veneer with a moisture content of 45% (compressive Young's modulus 150-400
1, plate thickness 1.0 yen), (as a veneer corresponding to the Bj part,
The same agathis veneer with a moisture content of 25% (compressive Young's modulus of 4
00 to 60014/d, board thickness 1.0 square meters) were used, connected by patchwork to form a single veneer, laminated and pressed and sliced in a conventional manner to obtain a decorative veneer.
実施例3
第2図の四部に当る単板としてアガチス(パパヤ)II
)の含水率的45%、板厚0.8閣の単板(圧縮ヤング
率100〜250 */d )を、伜)部に当る単板と
して同じアガチスの含水率的45%、板厚1.0−の単
板(圧縮ヤング率250〜400曝4Dを、それぞれ使
用し、前述のようにして1枚の単板とし、常法Gこよっ
て積層、圧締、スライスして化粧単板を得た。Example 3 Agatis (Papaya) II as a veneer corresponding to the fourth part in Figure 2
) with a moisture content of 45% and a board thickness of 0.8 mm (compressive Young's modulus 100 to 250 */d ) is used as the same Agatis veneer as the veneer corresponding to the section (B) with a moisture content of 45% and a board thickness of 1 .0- veneer (compressive Young's modulus 250-400 exposure 4D) was made into one veneer as described above, laminated, pressed and sliced using the usual G method to make a decorative veneer. Obtained.
以上の各実施例で得られた化粧単板は中央部に接着不良
もなく、端部に単板破壊もなく良質のものであった。The decorative veneers obtained in each of the above examples were of good quality, with no adhesion failure in the center and no veneer breakage at the edges.
本発明は圧力のかかり易い部分に相当する単板の部分に
ヤング率の小さい材質のものを配置し、圧力のかかりに
くい部分に相当する単板の部分にヤング率の大きい材質
のものを配置して繋ぎ合わせ、てなる単板を用いること
を特徴とするので、圧締圧力が均一となり、接着不良の
ない化粧単板が得られた。In the present invention, a material with a small Young's modulus is arranged in the part of the veneer that corresponds to the part where pressure is easily applied, and a material with a large Young's modulus is arranged in the part of the veneer which corresponds to the part where pressure is not easily applied. Since this method uses veneers made of wood, the pressing pressure is uniform and a decorative veneer with no adhesion defects can be obtained.
第1図は単板の圧締過程を示す略図、第2図はパッチワ
ークにより、ヤング率の興なる単板を繋いで得た単板の
斜視図である。
(^)・・・・・−・圧力のかかりやすい部分向・・・
・・・・・・圧力のかかりにくい部分特許出願人
松下電工株式会社
代理人弁理士 竹 元 敏 丸
(ほか2名)
第1図
1
第2図FIG. 1 is a schematic diagram showing the pressing process of veneers, and FIG. 2 is a perspective view of a veneer obtained by connecting veneers with a high Young's modulus by patchwork. (^)・・・・・・-・Direction where pressure is easily applied...
...Partial patent applicant who is less pressured Toshimaru Takemoto (and 2 other people) Patent attorney representing Matsushita Electric Works Co., Ltd. Figure 1 Figure 2
Claims (1)
の曲率を有する凹型および凸型の対からなる型版に挾ん
で圧締しフリッチ化し、スライスすることにより集成化
粧単板を製造する方法において、圧力のかかり易い部分
に相当する単板の部分にヤング率の小さい材質のものを
配置し、圧力のかかりに(い部分に相当する単板の部分
にヤング率の大合い材質のものを配置して繋ぎ合わせて
なる単板を用いることを特徴とする集成化粧単板の製法
。(1) Laminated decorative veneers are manufactured by laminating veneers with adhesive interposed, sandwiching them between a pair of concave and convex templates with a certain curvature, pressing them together to form flitches, and slicing them. In the method of A method for producing laminated decorative veneer, which is characterized by using a veneer made by arranging and connecting objects.