JPH1159743A - Packaging material - Google Patents
Packaging materialInfo
- Publication number
- JPH1159743A JPH1159743A JP22502697A JP22502697A JPH1159743A JP H1159743 A JPH1159743 A JP H1159743A JP 22502697 A JP22502697 A JP 22502697A JP 22502697 A JP22502697 A JP 22502697A JP H1159743 A JPH1159743 A JP H1159743A
- Authority
- JP
- Japan
- Prior art keywords
- packaging material
- desiccant
- film
- layer
- sealant layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、包装材料自体に水
分吸収能力を持たせた包装材料とその包装材料を用いて
作製した包装袋に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a packaging material in which the packaging material itself has a water absorbing ability, and a packaging bag produced using the packaging material.
【０００２】[0002]
【従来の技術】従来、海苔等の乾燥製品を包装する場合
には、包装体内にシリカゲル、塩化カルシウム、酸化カ
ルシウム等の乾燥物質を小袋に包装した、いわゆる乾燥
剤を同封する手法が一般的であった。乾燥剤を同封する
手法は包装体内の水分を完全に除去できるが、子袋の投
入自体が面倒であり、また、食品と混在するため誤って
食品と共に調理される可能性もある。2. Description of the Related Art Conventionally, when packaging dried products such as laver, a method of enclosing a so-called desiccant in which a dry substance such as silica gel, calcium chloride, or calcium oxide is packaged in a small bag in a package. there were. Although the method of enclosing the desiccant can completely remove the moisture in the package, it is troublesome to put the child bag itself, and may be erroneously cooked together with the food because it is mixed with the food.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、乾燥剤（子
袋）入りの包装体に関する上記のような問題点に着目し
てなされたもので、乾燥剤入りの子袋を同封せずに、乾
燥効果を出す包装材料とそれを使用した包装袋を提供す
ることを目的とする。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems relating to a package containing a desiccant (child bag). It is an object of the present invention to provide a packaging material exhibiting a drying effect and a packaging bag using the same.
【０００４】[0004]
【課題を解決するための手段】本発明の第１の発明は、
基材フィルムとシーラント層が積層された包装材料であ
って、基材フィルムのシーラント層と対向する側に水分
吸収層を設けた包装材料である。Means for Solving the Problems A first invention of the present invention is:
It is a packaging material in which a base film and a sealant layer are laminated, wherein the moisture absorption layer is provided on a side of the base film facing the sealant layer.
【０００５】また、第２の発明は、第１の発明におい
て、前記水分吸収層が、乾燥剤をビヒクル中に分散さ
せ、該乾燥剤が分散されたビヒクルを溶剤で希釈し、基
材フィルム上に塗布して塗膜状にした包装材料である。According to a second aspect of the present invention, in the first aspect, the moisture absorption layer disperses a desiccant in a vehicle, dilutes the vehicle in which the desiccant is dispersed with a solvent, and forms This is a packaging material that is applied to a coating film.
【０００６】さらにまた、第３の発明は、第１および第
２の発明において、前記乾燥剤が、シリカゲル、酸化カ
ルシウム、モレキュラーシーブのいずれかである包装材
料である。A third invention is a packaging material according to the first and second inventions, wherein the desiccant is any one of silica gel, calcium oxide, and molecular sieve.
【０００７】さらにまた、第４の発明は、第１、第２お
よび第３の発明において、前記基材フィルムは、透湿度
が１０ｇ／ｍ2 ・２４ｈｒｓ．／２５μｍ以下のプラス
チックフィルムである包装材料である。Further, in a fourth invention based on the first, second and third inventions, the base film has a moisture permeability of 10 g / m 2 · 24 hrs. / 25 μm or less is a packaging material that is a plastic film.
【０００８】さらにまた、第５の発明は、第１、第２、
第３および第４の発明において、前記シーラント層は、
透湿度が１５ｇ／ｍ2 ・２４ｈｒｓ．／２５μｍ以上の
プラスチックフィルム層である包装材料である。[0008] Further, a fifth invention is directed to the first, second, and third aspects.
In the third and fourth inventions, the sealant layer comprises:
The moisture permeability is 15 g / m 2 · 24 hrs. / Packaging material which is a plastic film layer of 25 μm or more.
【０００９】さらにまた、第６の発明は、第１ないし第
５の発明のいずれかに記載の包装材料を用いた包装袋で
ある。Furthermore, a sixth invention is a packaging bag using the packaging material according to any one of the first to fifth inventions.
【００１０】上記のように本発明によれば、基材フィル
ムのシーラント層と接する側に水分吸収層を設けたの
で、包装材料自体で水分吸収能力を有することが可能と
なった。As described above, according to the present invention, since the moisture absorbing layer is provided on the side of the base film which is in contact with the sealant layer, the packaging material itself can have the moisture absorbing ability.
【００１１】[0011]
【発明の実施の形態】以下実施例により本発明を詳細に
説明する。本発明の包装材料は、図１に示すように、基
材フィルム１１とシーラント層１２が積層された包装材
料であって、基材フィルムのシーラント層と対向する側
に水分吸収層１３を設けた構成である。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in detail below with reference to embodiments. As shown in FIG. 1, the packaging material of the present invention is a packaging material in which a base film 11 and a sealant layer 12 are laminated, and a moisture absorption layer 13 is provided on the side of the base film facing the sealant layer. Configuration.
【００１２】基材フィルム１１としては、透湿度が１０
ｇ／ｍ2 ・２４ｈｒｓ．／２５μｍ以下のプラスチック
フィルム、具体的には従来包装材料として使用されてい
る二軸延伸ポリプロピレンフィルム（ＯＰＰ）、二軸延
伸ポリエチレンテレフタレートフィルム（ＰＥＴ）、二
軸延伸ナイロンフィルム（ＯＮ）等のプラスチックフィ
ルムないしはシートが好ましく使用できる。なお、金属
や無機物質を真空蒸着などの方法により上記のプラスチ
ックフィルムないしはシートに形成したもの、ポリ塩化
ビニリデン、エチレン−ビニルアルコールなどの樹脂を
上記プラスチックフィルムないしはシートに塗布したも
のも好ましく使用できる。また、単層に限定されるもの
ではなく、上述したプラスチックフィルムないしはシー
トに紙、金属箔等を適宜に組み合わせ複合した多層構造
であってもよい。さらに、基材フィルム１１の上に必要
に応じて印刷インキ等により絵柄層（図示せず）を設け
てもよい。The base film 11 has a moisture permeability of 10
g / m 2 · 24 hrs. / 25 μm or less plastic film, specifically, plastic films such as biaxially oriented polypropylene film (OPP), biaxially oriented polyethylene terephthalate film (PET), and biaxially oriented nylon film (ON) conventionally used as packaging materials Or a sheet can be preferably used. In addition, those in which a metal or an inorganic substance is formed on the above-mentioned plastic film or sheet by a method such as vacuum deposition, and those in which a resin such as polyvinylidene chloride or ethylene-vinyl alcohol is applied to the above-mentioned plastic film or sheet can be preferably used. In addition, the present invention is not limited to a single layer, and may have a multilayer structure in which paper, metal foil, and the like are appropriately combined with the above-described plastic film or sheet. Further, a picture layer (not shown) may be provided on the base film 11 with printing ink or the like as necessary.
【００１３】なお、透湿度が１０ｇ／ｍ2 ・２４ｈｒ
ｓ．／２５μｍ以上のプラスチックフィルムを用いる
と、水分吸収層が内容物の水分を吸収しないで、外部
（外気）の水分を吸収してしまうなどの問題を生じるこ
とがあるので、避けなければならない。The moisture permeability is 10 g / m 2 · 24 hr.
s. If a plastic film having a thickness of / 25 μm or more is used, the moisture absorbing layer may not absorb moisture in the contents but may absorb moisture from the outside (outside air).
【００１４】また、基材フィルムの厚さは５〜３０μｍ
程度のものが好ましく使用できる。Further, the thickness of the base film is 5 to 30 μm.
Of these can be preferably used.
【００１５】シーラント層１２は、従来包装材料のシー
ラント層として使用される種々の材料のうち、透湿度が
１５ｇ／ｍ2 ・２４ｈｒｓ．／２５μｍ以上ある熱接着
性樹脂フィルムが使用できる。具体的には、ポリエチレ
ン（ＰＥ）、エチレン−酢酸ビニール共重合体、未延伸
ポリプロピレン（ＣＰＰ）などのポリオレフィン、ヒー
トシール性ポリエステル等のフィルムが使用できる。The sealant layer 12 has a moisture permeability of 15 g / m 2 · 24 hrs. Of various materials conventionally used as a sealant layer of a packaging material. / 25 μm or more can be used. Specifically, films such as polyethylene (PE), ethylene-vinyl acetate copolymer, polyolefin such as undrawn polypropylene (CPP), and heat sealable polyester can be used.
【００１６】なお、透湿度が１５ｇ／ｍ2 ・２４ｈｒ
ｓ．／２５μｍ以下の熱接着性樹脂フィルムを用いる
と、水分吸収層での内容物の水分吸収に時間がかかるな
どの問題を生じることがあるので、避けなければならな
い。The moisture permeability is 15 g / m 2 · 24 hr
s. If a heat-adhesive resin film having a thickness of / 25 μm or less is used, it may cause a problem such as taking a long time to absorb the moisture of the contents in the moisture-absorbing layer.
【００１７】また、シーラント層１２の厚さは２０〜５
０μｍ程度のものが好ましく使用できる。The thickness of the sealant layer 12 is 20 to 5
Those having a thickness of about 0 μm can be preferably used.
【００１８】水分吸収層１３は、乾燥剤２１をビヒクル
２２中に分散させ、この乾燥剤が分散されたビヒクルを
溶剤２３で希釈し（乾燥剤分散液という）、この乾燥剤
分散液を基材フィルム１１面に塗布して溶剤２３を飛散
させ塗膜状にしたものである。The moisture absorbing layer 13 is formed by dispersing a desiccant 21 in a vehicle 22, diluting the vehicle in which the desiccant is dispersed with a solvent 23 (referred to as a desiccant dispersion), and using the desiccant dispersion as a base material. It is applied to the surface of the film 11 to scatter the solvent 23 to form a coating film.
【００１９】乾燥剤２１としては、シリカゲル、酸化カ
ルシウム、モレキュラーシーブが容易に粉末化でき、ビ
ヒクル中に分散させ易いなどの理由から好ましく使用で
きる。As the desiccant 21, silica gel, calcium oxide, and molecular sieve can be preferably used because they can be easily pulverized and easily dispersed in a vehicle.
【００２０】ビヒクル２２は、乾燥剤を均一に分散さ
せ、基材フィルム面に乾燥剤を固着させる役目を担う液
状成分で、乾燥剤との分散性に優れ、各種の耐性を有す
るウレタン樹脂、硝化綿、塩素化ポリプロピレン等の溶
液が好ましく使用できる。The vehicle 22 is a liquid component having a role of uniformly dispersing the desiccant and fixing the desiccant on the surface of the substrate film. The vehicle 22 has excellent dispersibility with the desiccant and has various resistances such as urethane resin, Solutions such as cotton and chlorinated polypropylene can be preferably used.
【００２１】溶剤２３は、ビヒクルとの相溶性がよい酢
酸エチル、イソプロピルアルコール、トルエン、あるい
はこれらの混合溶剤等が好ましく使用できる。As the solvent 23, ethyl acetate, isopropyl alcohol, toluene, or a mixed solvent thereof having good compatibility with the vehicle can be preferably used.
【００２２】水分吸収層１３を形成させるための乾燥剤
分散液の基材フィルム１１への塗布は、グラビアコー
タ、ブレードコータ等周知の塗工機を用いて行えばよ
い。乾燥剤２１の塗布量は、０．１〜１０ｇ／ｍ2 （固
形分）程度が適量である。適量より多いと、基材フィル
ムとシーラント層間で接着強度不足となり層間で剥離現
象が発生することが多くなり、適量より少ないと、水分
吸収能力が不足することになる。The application of the desiccant dispersion to the base film 11 to form the moisture absorbing layer 13 may be performed using a well-known coating machine such as a gravure coater or a blade coater. An appropriate amount of the drying agent 21 applied is about 0.1 to 10 g / m 2 (solid content). If the amount is more than the appropriate amount, the adhesive strength between the base film and the sealant layer will be insufficient, and the peeling phenomenon will often occur between the layers. If the amount is less than the appropriate amount, the water absorbing ability will be insufficient.
【００２３】基材フィルム１１の水分吸収層１３面への
シーラント層１２の積層は、接着剤１４を用いて積層す
る。この接着剤は周知の任意のものが使用できる。具体
的には、周知のドライラミネ−ト用接着剤（例えばポリ
エステル系、ポリウレタン系の接着剤）が使用できる。
このようにして、本発明の包装材料を作製することがで
きる。The sealant layer 12 is laminated on the surface of the moisture absorbing layer 13 of the base film 11 using an adhesive 14. As the adhesive, any known adhesive can be used. Specifically, a well-known adhesive for dry laminate (for example, a polyester-based or polyurethane-based adhesive) can be used.
Thus, the packaging material of the present invention can be manufactured.
【００２４】[0024]
【実施例】以下に本発明の実施例をさらに具体的に説明
する。 〈実施例１〉基材フィルム１１として、厚さ２０μｍの
ＯＰＰ（透湿度；５ｇ／ｍ2 ・２４ｈｒｓ．／２５μ
ｍ）を、また、シーラント層として、厚さ３０μｍのＰ
Ｅ（透湿度；２５ｇ／ｍ2 ・２４ｈｒｓ．／２５μｍ）
をそれぞれ準備する。EXAMPLES Examples of the present invention will be described below more specifically. <Example 1> As a substrate film 11, an OPP having a thickness of 20 µm (moisture permeability; 5 g / m 2 · 24 hrs./25 µm)
m), and as a sealant layer, a 30 μm thick P
E (moisture permeability; 25 g / m 2 · 24 hrs./25 μm)
Prepare each.
【００２５】次に、下記処方からなる薬剤をオートクレ
ーブ等でよく混練して乾燥剤をビヒクル中に均一に分散
させ、乾燥剤分散液とする。 シリカゲル（乾燥剤） １５重量部 ウレタン樹脂溶液（ビヒクル） （固形分５０％、溶媒；酢酸エチル） １０重量部（固形分換算） 酢酸エチル（溶剤） ７５重量部Next, a medicine having the following formulation is kneaded well in an autoclave or the like, and the desiccant is uniformly dispersed in the vehicle to obtain a desiccant dispersion. Silica gel (desiccant) 15 parts by weight Urethane resin solution (vehicle) (solid content 50%, solvent: ethyl acetate) 10 parts by weight (solid content conversion) Ethyl acetate (solvent) 75 parts by weight
【００２６】この乾燥剤分散液を基材フィルムであるＯ
ＰＰに、グラビアコータを用いて乾燥剤の塗布量が１０
ｇ／ｍ2 （固形分換算）になるように塗布し、溶剤を乾
燥させ、水分吸収層１３を形成させた。The desiccant dispersion liquid is applied to a substrate film O
The amount of the desiccant applied to PP is 10 using a gravure coater.
g / m 2 (in terms of solid content), and the solvent was dried to form a water absorbing layer 13.
【００２７】最後に、ＯＰＰの水分吸収層１３を形成さ
せた面に、予め準備しておいた３０μｍ厚のＰＥをウレ
タン系接着剤を用いてドライラミネートし、本発明の包
装材料とした。Finally, a 30 μm-thick PE prepared in advance was dry-laminated on the surface on which the moisture absorbing layer 13 of OPP was formed using a urethane-based adhesive to obtain a packaging material of the present invention.
【００２８】この包装材料の水分吸収能力を下記の方法
により測定した。その結果を図２に示す。The moisture absorption capacity of this packaging material was measured by the following method. The result is shown in FIG.
【００２９】すなわち、上記包装材料を１０ｃｍ×１０
ｃｍの大きさに断裁し適宜に曲げて試料びんに入れ、こ
れを３０°Ｃで７９％ＲＨ．になる湿度調整液（ＮＨ4
Ｃｌ飽和水溶液）５０ｍｌ、空気２５０ｍｌの入ってい
る２５０ｍｌ容量のガラス容器に入れ密栓し、３０°
Ｃ、７９％ＲＨ．の条件下で包装材料の経時による重量
変化を測定し包装材料の水分吸収能力（ｇ／ｄａｙ）を
求めた。その結果を図２にグラフ化して示した。That is, the above packaging material is 10 cm × 10
cm in size, bent appropriately and placed in a sample bottle, and placed in a 79% RH. Humidity adjustment liquid (NH 4
Cl-saturated aqueous solution) into a 250 ml glass container containing 50 ml and 250 ml of air, and tightly stoppered.
C, 79% RH. The weight change of the packaging material with the passage of time was measured under the conditions described in (1) to determine the moisture absorption capacity (g / day) of the packaging material. The results are shown in a graph in FIG.
【００３０】図２の結果から、この包装材料は３０°
Ｃ、７９％ＲＨ．の雰囲気下では、０．２ｇ／ｄａｙ・
１００ｃｍ2 の水分吸収能力を有することがわかる。海
苔を例にとると、ＯＰＰ（２０μｍ厚）／ＰＥ（３０μ
ｍ厚）構成からなる包装袋に乾燥剤入りの子袋と共に１
０グラムの海苔を入れて密封した場合、６０日間に約
１．１グラムの水分を吸収する（常温雰囲気下）。これ
に対して、本発明の包装材料を用いた包装袋に海苔を入
れた場合には海苔の重量変化がほとんどなく、湿気を十
分に防ぐことができることがわかる。From the results shown in FIG. 2, the packaging material was 30 °
C, 79% RH. In an atmosphere of 0.2 g / day ·
It can be seen that it has a water absorption capacity of 100 cm 2 . Taking seaweed as an example, OPP (20 μm thick) / PE (30 μm
m) with a desiccant-containing child bag in a packaging bag
When sealed with 0 gram of nori, it absorbs about 1.1 gram of water over 60 days (under normal temperature atmosphere). On the other hand, when laver is put in the packaging bag using the packaging material of the present invention, the weight of the laver hardly changes, and it can be seen that moisture can be sufficiently prevented.
【００３１】[0031]
【発明の効果】上記のように本発明によれば、包装材料
自体が水分吸収能力を有するので、本発明の包装材料を
用いた包装袋には、乾燥剤入りの子袋を同封する必要が
なくなり、包装体の簡素化、充填時間の短縮が図れる。
また、包装体の中に子袋を同封しないので、誤って食品
と共に調理されるようなことはなくなった。As described above, according to the present invention, since the packaging material itself has a water absorbing ability, it is necessary to enclose a child bag containing a desiccant in the packaging bag using the packaging material of the present invention. As a result, the package can be simplified and the filling time can be shortened.
In addition, since the child bag is not enclosed in the package, it is not accidentally cooked with food.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明の包装材料の構成例を示す断面説明図で
ある。FIG. 1 is a cross-sectional explanatory view showing a configuration example of a packaging material of the present invention.
【図２】シリカゲルを１０ｇ／ｍ2 塗布した包装材料の
１日当たりの水分吸収能力を測定した折れ線グラフであ
る。FIG. 2 is a line graph showing the measurement of the water absorption capacity per day of a packaging material coated with 10 g / m 2 of silica gel.
１０‥‥包装材料 １１‥‥基材フィルム １２‥‥シーラント層 １３‥‥水分吸収層 １４‥‥接着剤 ２１‥‥乾燥剤 ２２‥‥ビヒクル 10 packaging material 11 base film 12 sealant layer 13 moisture absorption layer 14 adhesive 21 desiccant 22 vehicle
Claims (6)
包装材料であって、 基材フィルムのシーラント層と対向する側に水分吸収層
を設けたことを特徴とする包装材料。1. A packaging material in which a base film and a sealant layer are laminated, wherein a moisture absorbing layer is provided on a side of the base film facing the sealant layer.
分散させ、該乾燥剤が分散されたビヒクルを溶剤で希釈
し、基材フィルム上に塗布して塗膜状にしたことを特徴
とする請求項１記載の包装材料。2. The water-absorbing layer is characterized in that a desiccant is dispersed in a vehicle, the vehicle in which the desiccant is dispersed is diluted with a solvent, and applied to a substrate film to form a coating film. The packaging material according to claim 1, wherein
ム、モレキュラーシーブのいずれかであることを特徴と
する請求項１または２記載の包装材料。3. The packaging material according to claim 1, wherein the desiccant is any one of silica gel, calcium oxide, and molecular sieve.
2 ・２４ｈｒｓ．／２５μｍ以下のプラスチックフィル
ムであることを特徴とする請求項１、２または３記載の
包装材料。4. The substrate film has a moisture permeability of 10 g / m.
2 · 24hrs. 4. The packaging material according to claim 1, wherein the packaging material is a plastic film having a thickness of not more than / 25 μm.
2 ・２４ｈｒｓ．／２５μｍ以上のプラスチックフィル
ム層であることを特徴とする請求項１、２、３または４
記載の包装材料。5. The sealant layer has a moisture permeability of 15 g / m.
2 · 24hrs. 5. A plastic film layer having a thickness of at least / 25 .mu.m.
Packaging material as described.
材料を用いたことを特徴とする包装袋。6. A packaging bag using the packaging material according to any one of claims 1 to 5.