JPH11336846A - Belt for motive power transmission and double-sided toothed belt - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a belt for motive power transmission which can provide marks by printing them securely. SOLUTION: This belt A for motive power transmission consists of a compression rubber layer 1, an extension rubber layer 2, and an adhesive rubber layer 3 between both rubber layers 1 and 2, and in this belt A, a core wire 4 is buried in the adhesive rubber layer 4, cog parts 5 are provided at least to one side of the surface of the compression rubber layer 1 and the surface of the extension rubber layer 2, and marks 8 are printed to the cog summits 6 of one side cog parts 5 by copying from the copying film. Plural lines of mark lines 9 where the plural marks 8 are formed continuously in the continuing direction of cog summits 6 are printed by slipping the mark lines 9 in a specific size in the line direction. On the plural mark lines 9, even though the marks of one part mark line 9 are slipped from the position of the cog summit 6, and no printing is applied on the cog summits 6, the marks of the other part mark line 9 can be printed by making coinside on the cog summits.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cog-attached power transmission belt on which marks are printed by transfer and a double-sided toothed belt.

[0002]

2. Description of the Related Art As shown in FIG. 12, a cord 4 is embedded in a rubber layer comprising a compressed rubber layer 1, an extended rubber layer 2, and an adhesive rubber layer 3 between the two rubber layers 1 and 2, and a compressed rubber layer is formed. In a power transmission belt A provided with a cog portion 5 on at least one surface of the elastic rubber layer 1 and the extended rubber layer 2, for example, a low edge single cog belt or a low edge double cog belt, a method for printing a mark on the cog portion 5 is as follows. There is a method of transferring a mark from a transfer film during vulcanization for producing A. However, in this method, vulcanization is performed in a state where the transfer films are stacked, and thus there is a problem that the shape of the cog may not be correctly formed.

For this reason, a mark is printed on the surface of the cog portion 5 of the power transmission belt A after vulcanization. As a printing method, for example, Japanese Patent Application Laid-Open No. 8-152
Ink jet printing such as that disclosed in Japanese Patent Application Publication No. 048 is conceivable. However, in the case of ink jet printing, there is a problem that it is difficult to print fine characters.
In addition, it is conceivable to print a mark one by one on the cog peak 6 of the cog portion 5 by a stamp, but there is a problem that the printing is too time-consuming.

Therefore, it has been studied to transfer a mark from a transfer film onto the surface of the cog portion 5 of the vulcanized power transmission belt A and print the mark.

However, the cog portion 5 has a cog peak 6 and a cog groove 17.
Are formed alternately and continuously, so that the mark is transferred only from the transfer film onto the cog ridge 6, and the mark is divided by the cog groove 17 to make it difficult to determine the character of the mark. For this purpose, it has been considered to increase the size of one character of the mark so that the mark can be distinguished. However, since the size of one character of the mark is limited to the width of the power transmission belt A, It is difficult to make the mark distinguishable.

Therefore, the size of one character of the transfer mark 18 is made smaller than the width dimension of the cog ridge 6 of the cog portion 5 of the power transmission belt A, and the transfer marks 18 are arranged in a line at an interval equal to the pitch of the cog ridge 6. It has been studied to form a transfer film 7 as shown in FIG. 13 by continuously providing a transfer mark string 19 having a character string having a predetermined meaning, and to perform transfer using this transfer film 7. Transfer film 7 of FIG.
In FIG. 13, a plurality of rows of transfer mark rows 19 are provided with their heads aligned (FIG. 13 shows a state in which the transfer marks 18 are printed on the back surface of the transparent transfer film 7 and a state seen through the transfer film 7. Shown). Then, the transfer film 7 is superimposed on the surface of the cog portion 5 of the power transmission belt A after vulcanization, and heated and pressed to transfer each transfer mark 18 of the transfer mark row 19 from the transfer film 7 to the cog peak 6 of the cog portion 5. Transfer onto Each transfer mark 18 of the transfer mark row 19 is transferred onto each cog peak 6 of the cog portion 5, and the mark 8 can be printed on each cog peak 6 of the cog portion 5 as shown in FIG. In addition, the characters of the individual marks 8 printed on the individual cog peaks 6 can be identified, and the mark name 9 in which the marks 4 printed on the respective cog peaks 6 are arranged in a line, the manufacturer name and the like are displayed. A predetermined meaning such as a product number can be determined.

[0007]

However, in this case,
The position of the transfer film 7 overlapping the surface of the cog portion 5 of the power transmission belt A is shifted, and the transfer mark 1 on the transfer film 7 is shifted.
If the mark 8 does not correspond to the position of the cog ridge 6 but corresponds to the position of the cog groove 17, the transfer mark 18 will not be transferred onto the cog ridge 6 at all, and the product on which the mark 4 is not printed at all will be obtained. There was a problem that it could be completed.

[0008] Such a problem also occurs when a mark is printed by transfer from a transfer film to each tooth portion in a double-sided toothed belt provided with a plurality of tooth portions on the inside and outside along the longitudinal direction. It occurs in.

SUMMARY OF THE INVENTION The present invention has been made in view of the above points, and has as its object to provide a power transmission belt and a double-sided toothed belt which can reliably print and provide marks.

[0010]

The power transmission belt according to the present invention comprises a compression rubber layer 1, an extension rubber layer 2, an adhesive rubber layer 3 between the two rubber layers 1 and 2, and a center for the adhesive rubber layer 3. The wire 4 is embedded and the surface of the compression rubber layer 1 and the extension rubber layer 2
A power transmission belt A in which a cog portion 5 is provided on at least one of the surfaces of the power transmission belt 5 and a mark 8 is printed on each cog peak 6 of at least one cog portion 5 by transfer from a transfer film 7,
A mark row 9 formed by connecting a plurality of marks 8 in the direction in which the cog ridges 6 are connected is printed in a plurality of rows, and each mark row 9 is printed by being shifted by a predetermined dimension in the column direction.

In the double-sided toothed belt according to the present invention, a plurality of teeth 11 are provided on the inside and outside along the longitudinal direction, and a core wire 12 is embedded between the inside and outside teeth 11, and In the double-sided toothed belt B in which the marks 8 are printed on at least one of the outer teeth 11 by transfer from the transfer film 7, a mark row 9 formed by connecting a plurality of marks 8 in the direction in which the teeth 11 are connected. Are printed in a plurality of rows, each mark column 9 being shifted by a predetermined dimension in the column direction.

[0012]

Embodiments of the present invention will be described below.

FIG. 1 shows an example of a power transmission belt A with cogs. An inner compression rubber layer 1 and an outer extension rubber layer 2 and an adhesive rubber layer 3 between the two rubber layers 1 and 2 are shown. And the adhesive rubber layer 3 has a core 4
Is embedded. Further, a reinforcing cloth 21 is laminated on the surface of the compressed rubber layer 1 and the surface of the stretched rubber layer 2 in order to increase the resistance to bending fatigue and the resistance to shearing force and tearing force. Then, the surface of the compression rubber layer 1 and the extension rubber layer 2
A cog portion 5 in which cog peaks 6 and cog grooves 17 are alternately continuous at a constant pitch in the longitudinal direction of the belt is provided on at least one of the surfaces. The power transmission belt A in FIG. 1 is a low edge double cog belt provided with cog portions 5 on both sides.

The above-mentioned compressed rubber layer 1 and extended rubber layer 2 include
Rubber material such as natural rubber, styrene-butadiene rubber, chloroprene rubber, alkylated chlorosulfonated polyethylene, hydrogenated nitrile rubber, mixed polymer of hydrogenated nitrile rubber and unsaturated metal salt of carboxylic acid, or a mixture thereof. For example, para-aramid fibers (trade names "Twaron", "Kevlar", "Technola", etc.) alone, or para-aramid fibers and nylon, polyester, vinylon, cotton, meta-aramid fibers (trade name "Cornex" ), Etc., which are mixed so as to be oriented in the belt width direction. The amount of the short fibers added is 5 to 4 parts per 100 parts by weight of rubber.
0 parts by weight is preferable, and 8 to 15 parts by weight is particularly preferable.
Specifically, the short fiber is preferably a mixture of para-aramid fiber and nylon.

The adhesive rubber layer 3 may be the same as that used for the compressed rubber layer 1 and the expanded rubber layer 2, but the short fibers may or may not be mixed. .

The cord 4 can be made of a cord made of fibers such as polyester fiber, nylon fiber, aramid fiber, glass fiber and the like.

As the reinforcing cloth 21, a cloth made of cotton, polyester fiber, nylon or the like such as plain weave, twill weave and satin weave can be used.
A wide-angle canvas of about 120 ° may be used. This reinforcing cloth 21
It is preferable that the rubber composition is treated with an RFL solution and then subjected to fiction coating to use as a canvas with rubber. The RFL solution is obtained by mixing a latex with an initial condensate of resorcinol and formalin. As the latex, a latex such as chloroprene, styrene / butadiene / vinylpyridine terpolymer, hydrogenated nitrile rubber, or NBR can be used. it can.

Next, an example of manufacturing the power transmission belt A will be described. First, ridges 23 and concave grooves 24 are alternately provided at predetermined constant intervals on the outer circumference at predetermined intervals, and a cylindrical inner mold 25 whose surface is covered with canvas is nitrified. Fit into the outer periphery of the cylindrical mold 26. Meanwhile, 1
One to several reinforcing cloths 21, an unvulcanized rubber sheet 27 to be the compressed rubber layer 1, and an unvulcanized rubber sheet 28 to be the adhesive rubber layer 3 are laminated in this order, and these are separately prepared. The reinforcing cloth 21 is placed on a flat die having alternately formed concave grooves with the reinforcing cloth 21 facing downward, and is pressed to form the cog peaks 6 and the cog grooves 17 of the cog portion 5 by the ridges and the concave grooves. The cog pad 29 is manufactured by shaping the convex portion 6a and the concave portion 17a. Next, a mold 26 into which the inner mold 25 is fitted is mounted on a molding machine, and the concave portions 17a and the convex portions 6a are fitted into the ridges 23 and the concave grooves 24 of the inner mold 25 as shown in FIG. Then, a cog pad 27 of a predetermined length is wound around the circumference once and both ends are brought together.

Next, the core wire 4 is spirally wound around the outer periphery of the cog pad 27. Further, an unvulcanized rubber sheet 30 to be an extended rubber layer 2 and zero to several reinforcing cloths 2
, And a molded body 31 composed of the reinforcing cloth 21, unvulcanized rubber sheets 27, 28, 30, and the core wire 4.
Is prepared.

After that, the plurality of guide rods 33 are
1 on the outer surface. The guide rod 33 is a fixed piece 34 at the end.
Is inserted into a fixing hole 35 provided in the mold 26 to be mounted. Next, an outer matrix 38 formed in a cylindrical shape with vulcanized rubber by alternately providing ridges 36 and concave grooves 37 at predetermined constant intervals on the inner circumference at predetermined intervals is used as a guide rod 3.
As shown in FIG. 8, the molded body 31 is fitted along the outer periphery of the molded body 31 and attached. The ridge 23 of the inner matrix 25 is formed by the guide rod 33.
The outer mold 38 can be mounted in a state where the ridges 36 and the concave grooves 37 of the outer mold 38 are aligned with the concave grooves 24.

Next, after removing the guide rod 33, the guide rod 33 is transferred to a vulcanizing can for vulcanization. After vulcanization in this manner, the outer mold 38 is extracted, and a sleeve-shaped molded product obtained by vulcanizing the molded body 31 is extracted, and the sleeve-shaped molded product is cut into a predetermined width to obtain a ring. , The ridge 23 and the concave groove 24 of the inner mold 25 and the ridge 3 of the outer mold 38
The power transmission belt A as shown in FIG. 1 in which the cog portion 5 is formed by the groove 6 and the concave groove 37 can be obtained.

FIG. 2 shows an example of a double-sided toothed belt B. A plurality of tooth portions 11 and tooth grooves 42 are alternately provided at a constant pitch inside and outside a rubber layer 41 along the longitudinal direction, respectively. It is formed by embedding a core wire 12 between the inner and outer teeth 11. In addition, the inner and outer teeth 1
A tooth cloth 43 is laminated on the surfaces of the tooth grooves 1 and the tooth grooves 42.

The rubber layer 41 is formed of rubber such as chloroprene, natural rubber, millable urethane rubber, hydrogenated nitrile rubber, chlorosulfonated ethylene (CSM), and alkylated chlorosulfonated polyethylene (ACSM). Is preferred. The hydrogenated nitrile rubber preferably has a hydrogenation rate of 80% or more, and has a hydrogenation rate of 90% in order to exhibit heat resistance and ozone resistance.
% Or more is good. A hydrogenated nitrile rubber having a hydrogenation rate of less than 80% has extremely low heat resistance and ozone resistance. These rubbers are added with carbon black, zinc white, stearic acid, a plasticizer, an antioxidant, etc. as a compounding agent, and sulfur and an organic peroxide are further compounded as a vulcanizing agent. The types of these additives and vulcanizing agents are not particularly limited.

The above-mentioned core wire 12 is made of polyester, aliphatic polyamide, aromatic polyamide, rayon,
Low elongation and high strength materials such as glass fiber and steel wire can be used.

Further, as the canvas used as the above-mentioned tooth cloth 43, a cloth formed of fibers such as 6 nylon, 66 nylon, polyester, aramid, etc., alone or in combination can be used. The configuration of the weft along the longitudinal direction of the belt or the warp along the width direction of the belt is a filament yarn or spun yarn of these fibers, and the woven configuration may be any of plain weave, twill weave, and satin weave. In addition, it is preferable to use a weft obtained by twisting crimped yarn or elastic urethane yarn having elasticity. Further, as the tooth cloth 43, it is preferable to use an RFL solution that has been treated with an RFL solution and has a solid content of 10 to 50% by weight obtained by drying the RFL solution. The solid content of the RFL solution is R
It is made of (resorcinol) F (formalin) resin and a solid component, and has an effect of preventing the rubber component oozing out from the rubber layer 41 to the surface of the tooth portion 11 from scattering as rubber powder during belt running. As described above, this RFL liquid is obtained by mixing the latex with the initial condensate of resorcinol and formalin, and the molar ratio of resorcinol to formalin is 1 to 1 to 3. The weight ratio of the initial condensate of resorcinol and formalin to latex is 1: 1 to 10. The latex used here is a latex such as styrene / butadiene / vinylpyridine terpolymer, hydrogenated nitrile rubber, chlorosulfonated polyethylene, epichlorohydrin and the like.

Next, an example of the production of the double-sided toothed belt B will be described. First, as a core wire 12, approximately 600 glass fiber filaments having a wire system of 9 μm are bundled to form a strand, and the strand is immersed in an RFL solution shown in Table 1 to obtain a core 2.
After drying at 00 ° C. for 2 minutes, a twisting is performed at a twist number of 16 times / 10 cm to form a small rope, and 10 small ropes are collected and twisted to use a 0.5 mm diameter glass cord. .

[0027]

[Table 1] Further, as the tooth cloth 43, the canvas is immersed in the RFL solution shown in Table 1, and a squeezing pressure of about 0.3 to 0.8 kgf is applied by a pair of rolls.
/ Cm ² (gauge pressure), followed by drying, and then treated with RFL solution in the same manner to adjust the solid content of the RFL solution to canvas to 10 to 50% by weight. If the solid content of the RFL liquid is less than 10% by weight, the contact portion between the warp and the weft of the canvas is easy to move, the opening between the yarns is enlarged, and the rubber of the rubber layer 41 is removed from the opening of the tooth cloth 43 through the opening. May be exposed on the surface and RF
If the solid content of the liquid L exceeds 50% by weight, the solid content may be so large that the shape of the tooth portion 11 may not appear correctly. On the inner surface of the tooth cloth 43 thus treated with the RFL solution, a rubber paste obtained by dissolving a rubber composition mainly composed of raw rubber used for the rubber layer 41 in a solvent is subjected to a spreading process (coating process). Attached, 100 ~
Dry at a temperature of 160 ° C. for 30-60 seconds to obtain 0.1-0.
A coated rubber layer having a thickness of 3 mm is formed. If the thickness of the coat rubber layer is less than 0.1 mm, the rubber of the rubber layer 41 may ooze onto the surface of the tooth cloth 43 during the final molding step described below, and if the thickness of the coat rubber layer exceeds 0.3 mm, Even if the bleeding of the rubber layer 41 onto the surface of the tooth cloth 43 is prevented, the PLD values of the inner and outer teeth 11 (distance from the tooth bottom to the pitch line, which is the center of the core wire) are different. Become. This is because the core wire 1 is applied to the coated rubber layer of the tooth cloth 43 to be coated on the inner teeth 11 during molding.
This is because the coat rubber layer is likely to be deformed when winding No. 2. Providing a coat rubber layer on the inner surface of each tooth cloth 43 to be covered by the inner tooth portion 11 and the outer tooth portion 11 is also preferable in order to make the PLD values of both tooth portions 11 coincide. Note that the tooth cloth 43 has the R
In addition to FL treatment, epoxy treatment, isocyanate treatment,
An adhesive treatment such as a soaking treatment can also be performed. Further, in order to improve the air flow in the constituent yarns of the canvas of the tooth cloth 43 and between the constituent yarns and to improve the air bleeding at the time of molding the surface of the rubber layer 41, these processes are not performed. Can also be used.

Then, as shown in FIG. 10, a cylindrical grooved mold 48 in which ridges 46 and concave grooves 47 are alternately provided on the outer periphery along the circumferential direction at predetermined constant intervals is mounted on a molding machine. A possible cylindrical tooth cloth 43 is wound along the outer peripheral surface of the grooved mold 48, and the core wire 12 is spirally wound thereon. Furthermore, a rubber layer 41 of a certain thickness having a volume (thickness) on which the teeth 11 on both sides can be formed.
An unvulcanized rubber sheet 49 for forming is wound and the tooth cloth 43 is wound thereon to form a molded body 50.

Then, a plurality of guide rods 33 are mounted on the outer surface of the molded body 50 in the same manner as in the case of FIG. The guide rod 33 is mounted by inserting a fixing piece 34 at the end into a fixing hole 35 provided in a grooved mold 48. Next, an outer matrix 38 formed of vulcanized rubber in a cylindrical shape by alternately providing ridges 36 and concave grooves 37 at predetermined constant intervals on the inner circumference along the circumferential direction is formed along the guide rod 33. 9 in the same manner as in FIG. The outer mold 38 can be mounted in a state where the ridges 36 and the concave grooves 37 of the outer mold 38 are aligned with the ridges 46 and the concave grooves 47 of the grooved mold 48 by the guide rods 33. is there.

Next, after the guide rod 33 is removed, the grooved mold 48 on which the molded body 50 and the outer mold 38 are mounted is transferred to a pre-molding step, and a jacket is fitted on the outer mold 38 and semi-vulcanized. Perform For semi-vulcanization, put this in a vulcanizer
This is performed by introducing steam of ² kgf / cm ² into the vulcanization can (not shown). During this semi-vulcanization, the unvulcanized rubber sheet 49 flows due to heating and pressing, and flows into the concave groove 47 of the grooved mold 48 while extending the inner tooth cloth 43 from the gap between the core wires 12 to flow into the inner groove. The teeth 11 are formed and the outer teeth 11 are formed by flowing into the concave grooves 37 of the outer mold 38 while extending the outer tooth cloth 43. When approaching the state of semi-vulcanization, the internal pressure and temperature of the vulcan can are lowered so that vulcanization does not proceed any more so that complete vulcanization does not occur. Here, semi-vulcanized means a state where each physical property value reaches 1 to 5 when each physical property value such as tensile strength, modulus, elongation and the like at the time of final optimal vulcanization is 100. . In this case, the optimal vulcanization is estimated at a point where the tensile strength is slightly past the maximum value, a modulus is a point slightly before the maximum value, and an elongation is a point slightly before the minimum value, and these are determined by the vulcanization curve. Is done.

After the molded body 49 is semi-vulcanized into a sleeve-shaped preform 51 as described above, the preform 51 is taken out of the vulcanizer, and the sleeve-shaped preform 51 is removed from the grooved mold 48. In this case, since the sleeve-shaped preform 51 is in a semi-vulcanized state, it is necessary to remove the tooth portion 11 without significantly deforming the same. next,
The vulcanization is completed in the final molding step.

In the final molding step, as shown in FIG. 11, a pair of toothed pulleys 52, 52 capable of adjusting the distance between the shafts.
And a sleeve-shaped preform 51 is suspended on the inner teeth 11.
A pair of internal toothed molds 54, 54 provided with forming irregularities 53 that match with the inner surface of the sleeve-like preform 51, and the forming irregularities 53 that match with the outer teeth 11 are provided.
Are provided on the upper side and lower side of the sleeve-shaped preform 51. Each of the externally toothed molds 55, 55 is a press mold 56, 56 whose temperature can be adjusted.
, And are arranged so that each molding unevenness 53 faces the side of the sleeve-shaped preform 51. Then, the sleeve-shaped preform 51 is sandwiched and pressed between the mold 54 with the internal teeth and the mold 55 with the external teeth by the press die 56, so that the sleeve-shaped preform 5
1, the inner and outer teeth 11 can be molded and vulcanized, the inner and outer teeth 11 can be formed to the exact shape and dimensions, and the PLD values of the inner and outer teeth 11 can be matched. Things. The inner toothed mold 54 and the outer toothed mold 55
Final molding of the tooth portion 11 by the sleeve-shaped preform 5
1, the sleeve-shaped preform 51 is moved by the toothed pulley 52 and is sequentially and repeatedly performed to perform the final shaping of all the teeth 11 of the sleeve-shaped preform 51. Can be done.

As described above, the sleeve-shaped preform 5
After obtaining a sleeve-shaped molded product obtained by vulcanizing 1, the sleeve-shaped molded product is cut into a round slice with a predetermined width, so that, for example, as shown in FIGS. And a belt width of 12.7 mm and a belt length of 819.
A double-sided toothed belt B can be obtained as a 15 mm L-shaped timing belt.

Next, the printing of the marks 8 on the cog-attached power transmission belt A and the double-sided toothed belt B produced as described above will be described.

First, the transfer film 7 used for printing the mark 8 will be described. The transfer film 7 is made of polyester,
The base 61 is formed of a synthetic resin film such as nylon, polypropylene, cellophane, polyethylene naphthalate, or acetate, and the thickness of the base 61 is preferably about 30 to 60 μm. If the thickness of the base material 13 is less than 30 μm, after the transfer mark 18 is transferred, the power transmission belt A or the double-sided toothed belt B
When the base material 61 is peeled off, the possibility that the base material 61 is broken and adheres to the power transmission belt A or the double-sided toothed belt B increases. Conversely, if the thickness of the base material 61 exceeds 60 μm, the power transmission belt A or When pressing the base material 61 to transfer the transfer mark 18 to the double-sided toothed belt B, a step occurs between the area where the power transmission belt A or the double-sided toothed belt B is dented and the mark 8 is printed and the area where the mark 8 is not printed. There is a risk.

Transfer mark 1 provided on the surface of substrate 61
8 is a vulcanizing agent, a vulcanizing aid, an unvulcanized color rubber composition, for example, a rubber such as natural rubber, chloroprene rubber, or SBR.
A material containing a pigment or the like, or a resin composition
Can be formed by printing. The color of the transfer mark 18 is not particularly limited, but is preferably a color that is clearly different from the color of the base material 61 and the surface of the power transmission belt A and the double-sided toothed belt B.

Here, the size of one character of the transfer mark 18 provided on the surface of the base material 61 of the transfer film 7 is determined by the width P ₁ of the cog ridge 6 of the cog portion 5 of the power transmission belt 1 to be transferred. than the width P ₁ of the tooth portion 11 of the double-sided toothed belt B to be transferred, and is set such that the width dimension becomes smaller. By arranging the plurality of transfer marks 18 in a line, a transfer mark array 19 indicating a manufacturer name, a product number, and the like is formed. Transfer mark 18
Are set to match the pitch P of the cog peak 6 and the pitch P of the tooth portions 11. The transfer mark array 19 is provided in a plurality of rows on the surface of the base material 61 as shown in FIG. 5 (FIG. 5 shows the transfer mark 1 on the back surface of the transparent base material 61).
8 shows a state where 8 is printed through the base material 61).

Then, each transfer mark column 19 in a plurality of rows is
The adjacent transfer mark rows 19 are provided on the surface of the base material 61 such that the adjacent transfer mark rows 19 are shifted by a predetermined dimension in the row direction. This shift dimension D can be set, for example, as follows. P ₁ : the width dimension of the cog peak 6 (or the width dimension of the tooth portion 11), P ₂ : the width dimension of the cog groove 17 (the width dimension of the tooth groove 42), W: the lateral width dimension perpendicular to the belt longitudinal direction, N: Number of rows of transfer mark rows 19 that can be printed on power transmission belt A or double-sided toothed belt B, L: row spacing of transfer mark rows 19 (= height L _{1 of} mark 4 + between transfer mark rows 6) If the interval is L ₂ ), D ≒ (P ₁ + P ₂ ) / N and N ≒ W / L, so that D ≒ L (P ₁ + P ₂ ) / W The numerical value obtained in this manner is rounded and shifted. Can be a substitute.

As shown in FIG. 5 (a), the transfer mark columns 19 of a plurality of rows are arranged in a shifted manner, as shown in FIG. 5D from the top of the first row, on the contrary, it is shifted to the left by D dimensions, and as shown in FIG. 5B, the top row is shifted to the right by D dimensions from the first row. When there is a deviation of a predetermined dimension (for example, 5 mm) from the leading end of the first line, the transfer mark 18 is transferred to the power transmission belt A or the double-sided toothed belt B. The appearance when printing mark 8
The embodiment of FIG. 5B is better.

FIG. 6 shows the use of the transfer film 7 formed by providing the transfer marks 18 on the surface of the base material 61 as described above.
This shows an example of a method of printing the mark 8 by transferring the transfer mark 18 to the cog portion 5 of the power transmission belt A. In FIG. 6, reference numeral 63 denotes a sleeve-like molded product obtained by vulcanizing the above-mentioned molded body 31. By cutting the sleeve-like molded product 63 into ring-shaped sections, a power transmission belt with a cog as a final product is provided. A can be obtained. Then, the sleeve-shaped molded product 63 is placed on the lower press 65, and the transfer film 7 is overlapped on the surface of the sleeve-shaped molded product 63 on the side where the transfer mark 18 is provided. The transfer film 7 is formed such that the direction of the transfer mark row 19 is formed on the cog portion 5 of the cog portion 5 formed on the sleeve-shaped molded product 63.
Are arranged so as to coincide with the continuous direction of the sleeve-shaped molded product 63, that is, to coincide with the circumferential direction of the sleeve-shaped molded product 63. Thereafter, the transfer film 7 is pressed from above by an upper press 64, and is heated to 100 to 140 ° C., preferably 120 to 13 ° C.
The transfer film 7 is heated and pressed by the upper and lower presses 64 and 65 for 10 to 30 seconds, preferably for 15 to 25 seconds under a temperature condition of 0 ° C. and a pressure condition of 2.0 to 3.0 kg / cm ² . By transferring the transfer mark 18, the mark 8 can be printed on the cog peak 6 of the cog portion 5 of the sleeve-shaped molded product 63.

After the transfer is performed in this manner, the sleeve-shaped molded product 63 is cut into a ring to obtain a power transmission belt A with a cog as shown in FIGS. 1 (a) and 1 (b). A mark 8 is printed on the cog ridge 6 of the cog portion 5 of the power transmission belt A, and a row of marks transferred from the transfer mark row 19 of the transfer film 7 to each of the cog ridges 6 is formed. The mark 8 printed on the cog peak 6 in FIGS. 1 (a) and 1 (b) can be identified by a solid line and a cog mark. Marks 8 that are not transferred corresponding to grooves 7 are indicated by broken lines). Here, as described above, the transfer film 7 is provided with a plurality of transfer mark rows 19 including the transfer marks 18 in which the pitch of the cog ridges 6 and the character spacing are made to coincide with each other by a predetermined dimension in the column direction. Therefore, the transfer mark column 1 of some of the transfer mark columns 19 of the plurality of rows
Even if each of the transfer marks 18 is not transferred onto each of the cog hills 6 from the position of the cog ridge 6, as shown in FIG. Reference numeral 18 indicates that the mark 4 can be printed by being transferred onto each of the cog peaks 6, and the mark row 9 of the mark 4 transferred and printed on each of the cog peaks 6 is a predetermined number such as a manufacturer name and a product number. The meaning can be determined.

Mark 8 on power transmission belt A with cogs
Here is a specific example of printing.

(Specific Example 1) As the power transmission belt A,
Width W = 35.9 mm, thickness 16.0 mm, circumference 111
3 mm, the height of the cog peak 6 of the cog portion 5 on the outer peripheral side is 5.0 m.
m, pitch P of cog peak 6 = 5.6 mm, width P of cog peak 6
A low-edge cog belt having ₁ = 2.0 mm and a width P ₂ of the cog groove 17 of 3.6 mm was used. On the other hand, a transfer mark row 19 in which transfer marks 18 each having a size of 4 mm in length and 2 mm in width were arranged in a line at a character interval of 5.6 mm was provided on the surface of the film of the base material 61 to produce the transfer film 7. . Each transfer mark row 19 is shifted by D = 1 mm at a time in FIG.
They were arranged as in (b). Using the transfer film 7, the transfer mark 18 is formed on the cog 5 of the power transmission belt A.
Is transferred and printing is performed, so that each transfer mark 18 of at least one row of transfer mark rows 19 can be transferred onto each cog peak 6 of the cog portion 5 and printed on each cog peak 6 of the cog portion 5. Among the marks 4, the marks 4 in at least one mark row 9 could be determined.

(Specific Example 2) As the power transmission belt A,
Width W = 36.5 mm, thickness 16.5 mm, circumference 131
0 mm, the height of the cog ridges 6 of the cog portions 5 on the outer peripheral side and the inner peripheral side is 5.0 mm, the pitch P of the cog ridges 6 of each of the cog portions 5 on the outer peripheral side and the inner peripheral side is 10.7 mm, and each cog ridge 6 width P ₁ =
A low edge double cog belt of 5.7 mm and a width P ₂ of each cog groove 17 of 5 mm was used. On the other hand, on the surface of the film of the base material 61, a transfer mark row 19 in which transfer marks 18 each having a size of 6 mm in length and 4.7 mm in width are arranged in a line at a character interval of 10.7 mm is provided to transfer the transfer film 7. Produced. These transfer mark rows 19 were arranged as shown in FIG. 5B with a shift of D = 2 mm. Then, the transfer marks 18 were transferred to the cog portions 5 on the outer and inner peripheral sides of the power transmission belt A by using the transfer film 7, and printing was performed. 18 can be transferred onto each of the cog ridges 6 of the cog portion 5, and among the marks 4 printed on each of the cog ridges 6 of the cog portion 5, at least one of the marks 4 in the mark row 9 can be determined. did it.

The transfer of the transfer marks 18 from the transfer film 7 to the teeth 11 of the double-sided toothed belt B to print the marks 8 can be performed in the same manner as described above. That is, in FIG. 6, 66 is the sleeve-shaped preform 5
1 is a sleeve-shaped molded product obtained by vulcanization of 1. The sleeve-shaped molded product 66 is cut into slices,
A double-sided toothed belt B as a final product can be obtained. Then, the sleeve-shaped molded product 66 is placed on the lower press 65, and the transfer film 7 is overlaid on the surface of the sleeve-shaped molded product 66 on the side where the transfer mark 18 is provided. The transfer film 7 is arranged such that the row direction of the transfer mark row 19 coincides with the continuous direction of the teeth 11 formed on the sleeve-shaped molded product 66, that is, the circumferential direction of the sleeve-shaped molded product 66. Things. Thereafter, the transfer film 7 is pressed from above with an upper press 64, and is heated at a temperature of 100 to 140 ° C., preferably 120 to 130 ° C. under a pressure of 2.0 to 3.0 kg / cm ² ,
The transfer mark 18 of the transfer film 7 is transferred by heating and pressing the upper and lower presses 64 and 65 for 10 to 30 seconds, preferably 15 to 25 seconds, and the mark 8 is placed on the tooth portion 11 of the sleeve-shaped molded product 66. It can be printed.

After the transfer is performed in this manner, the double-sided toothed belt B as shown in FIG.
The mark 8 is printed on the tooth portion 11 of the double-sided toothed belt B, and the name of the manufacturer and the name of the manufacturing company are indicated by the mark line 9 of one line of the mark 8 transferred from the transfer mark line 19 of the transfer film 7 to each tooth portion 11. It is possible to determine a predetermined meaning such as a product number (in FIG. 2, a mark 8 printed on the tooth portion 11 is indicated by a solid line, and a mark 8 that is not transferred corresponding to the tooth groove 42 is indicated by a broken line). Here, as described above, the transfer film 7 is provided with a plurality of transfer mark rows 19 including the transfer marks 18 in which the pitch of the tooth portions 11 and the character spacing are made to coincide with each other by a predetermined dimension in the column direction. Therefore, of the transfer mark columns 19 of the plurality of rows,
Even if each of the transfer marks 18 is not transferred onto each of the tooth portions 11 by being shifted from the position of the tooth portion 11, as shown in FIG. Can be transferred onto each tooth portion 11 to print the mark 4, and the mark row 9 of the mark 4 transferred and printed on each tooth portion 11 has a predetermined meaning such as a manufacturer name and a product number. Can be determined.

A specific example of printing the mark 8 on the double-sided toothed belt B will be described.

(Specific Example 3) As the double-sided toothed belt B, the width W = 12.7 mm, the belt length 819.15 mm, the tooth pitch P of each tooth portion 11 on the outer peripheral side and the inner peripheral side = 9.525.
An L-shape with a tooth shape of mm was used. On the other hand, the transfer film 7 was produced by providing a transfer mark row 19 in which transfer marks 18 each having a size of 4 mm in length and 2 mm in width were arranged in a line at a character interval of 9.525 mm on the surface of the film of the base material 61. . These transfer mark rows 19 were arranged as shown in FIG. 5B with a shift of D = 2 mm. The transfer marks 18 were transferred to the outer and inner teeth 11 of the double-sided toothed belt B by using the transfer film 7, and printing was performed. 18 can be transferred onto each tooth 11 and the tooth 1
Among the marks 4 printed on No. 1, marks 4 in at least one mark row 9 could be determined.

[0049]

As described above, the present invention comprises a compression rubber layer, an extension rubber layer and an adhesive rubber layer between both rubber layers, and a core wire is embedded in the adhesive rubber layer. In a power transmission belt in which a cog portion is provided on at least one of the surfaces of the power transmission belt and a mark is printed on each cog peak of at least one cog portion by transfer from a transfer film, a plurality of marks are formed in a continuous direction of the cog peaks. Since the mark rows to be printed are printed in a plurality of rows and each mark row is shifted by a predetermined dimension in the column direction, among the mark rows in the plurality of rows, each mark in some of the mark rows is shifted from the position of the cog peak. Even if the mark is not printed on each cog peak, each mark in some other mark row can be printed so as to match each cog peak. Can also It is.

According to the present invention, a plurality of teeth are provided on the inner side and the outer side in the longitudinal direction, and a core wire is buried between the inner and outer teeth, and at least one of the inner and outer teeth is provided. In a double-sided toothed belt on which marks are printed by transfer from a transfer film, a plurality of marks are formed by connecting a plurality of marks in a continuous direction of a tooth portion, and a plurality of rows of marks are formed. Since it is printed, even if each mark of a part of the mark rows is not printed on each tooth part because it is displaced from the position of the tooth part among the mark rows of a plurality of lines, Each mark can be printed so as to be coincident with each tooth, and the mark can be reliably printed and provided.

[Brief description of the drawings]

FIG. 1 shows a power transmission belt on which a mark according to the present invention is printed, and (a) and (b) are partially broken perspective views showing one example of each of them.

FIG. 2 is a partially broken perspective view showing an example of a double-sided toothed belt on which marks according to the present invention are printed.

FIG. 3 is a sectional view showing another example of the double-sided toothed belt of the above.

FIG. 4 is a plan view of a part of a power transmission belt (double-sided toothed belt) on which a mark according to the present invention is printed.

FIG. 5 shows a transfer film used for printing a mark, and (a) and (b) are partial plan views.

FIG. 6 is a perspective view showing a process of printing a mark.

FIG. 7 is a cross-sectional view in which a part of one process of manufacturing the power transmission belt is omitted.

FIG. 8 is a perspective view of one step of manufacturing the power transmission belt.

FIG. 9 is a perspective view of one step of manufacturing the power transmission belt.

FIG. 10 is a cross-sectional view of one process of manufacturing a double-sided toothed belt.

FIG. 11 is a cross-sectional view of one process of manufacturing a double-sided toothed belt.

FIG. 12 shows an example of a power transmission belt.
(A) is a partial perspective view, (b) is a partial front view.

FIG. 13 is a plan view showing an example of a conventional transfer film.

14 is a plan view of a part of a power transmission belt on which marks are printed using the transfer film of FIG. 13;

[Explanation of symbols]

 DESCRIPTION OF SYMBOLS 1 Compression rubber layer 2 Extension rubber layer 3 Adhesive rubber layer 4 Core wire 5 Cog part 6 Cog mountain 7 Transfer film 8 Mark 9 Mark row

Claims (2)

[Claims] 1. A compression rubber layer, an extension rubber layer, and an adhesive rubber layer between both rubber layers. A core wire is embedded in the adhesive rubber layer, and a cog portion is formed on at least one of the surface of the compression rubber layer and the surface of the extension rubber layer. In a power transmission belt in which at least one cog portion of each cog peak is printed with a mark by transfer from a transfer film, a mark row formed by connecting a plurality of marks in a continuous direction of the cog peaks has a plurality of rows, A power transmission belt, wherein each mark row is printed by being shifted by a predetermined dimension in the row direction. 2. A plurality of teeth are provided on an inner side and an outer side along a longitudinal direction, a core wire is buried between the inner side and the outer side, and a transfer film is provided on at least one of the inner side and the outer side. In a double-sided toothed belt on which marks are printed by transfer from a plurality of marks, a mark row formed by connecting a plurality of marks in a row of teeth is printed in a plurality of rows, and each mark row is printed by being shifted by a predetermined dimension in the row direction. A double-sided toothed belt.