JPH11315500A - Highly sebum-absorbing cleansing paper for cosmetic and its production - Google Patents
Highly sebum-absorbing cleansing paper for cosmetic and its productionInfo
- Publication number
- JPH11315500A JPH11315500A JP11021441A JP2144199A JPH11315500A JP H11315500 A JPH11315500 A JP H11315500A JP 11021441 A JP11021441 A JP 11021441A JP 2144199 A JP2144199 A JP 2144199A JP H11315500 A JPH11315500 A JP H11315500A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- absorbing
- mesh
- cosmetic
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】この発明は、高吸化粧用脂取
り紙及びその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a high-absorbency cosmetic absorbent paper and a method for producing the same.
【0002】[0002]
【従来の技術】人間の顔面、特に鼻、頬、額、眉毛間等
は皮脂の分泌が盛んで油っぽくなり易く、従って、その
部分では化粧崩れを起こし易い。一般に皮脂が浮いたま
ま化粧をすると、皮膚に化粧料が馴染まないため、顔面
の脂分を化粧用脂取り紙にて取り除いてから化粧し、効
果を上げている。これは化粧直しの場合も同様である。
従来の化粧用脂取り紙は古くから箔打紙が使われてお
り、名塩紙が有名である。この紙は、西宮市名塩産で、
三椏、楮、雁皮に特殊な泥、例えば、金箔打ちには東久
保土と呼ぶ白色のもの、銀箔打ちには蛇豆土という茶褐
色のものを混入して漉いた紙である。2. Description of the Related Art The face of a human, particularly between the nose, cheeks, forehead, and eyebrows, tends to become greasy due to the secretion of sebum, and the makeup tends to be lost in that part. In general, if makeup is applied while sebum is floating, cosmetics do not fit into the skin. Therefore, makeup is applied after removing fat on the face with a cosmetic fat removing paper. This is the same in the case of makeup correction.
Foil paper has been used as a conventional fat removing paper for cosmetics, and famous salt paper is famous. This paper is from Nishinomiya City
It is a paper made by mixing mitsumata, mulberry, and goosepicks with special mud, for example, gold leafing with a white thing called Higashikubo soil, and silver leafing with a brownish one called snake bean soil.
【0003】又、箔打紙は箔打ちを15回ほど使用する
と、箔を打ちを延ばす働きがなくなり、これを女性の脂
取り化粧紙として用いられている。名塩紙は箱打ち後、
密度が0.94kg/cm3常に高くなり、これを脂取
り化粧紙として用いると、顔面の油脂分が除かれ、風呂
に浴したようになるので、またの名を風呂屋紙として早
くから用いられてきた。[0003] When the foil stamping is used about 15 times, the function of extending the foil is lost, and the foil stamping paper is used as a grease-absorbing decorative paper for women. After salting paper,
The density is always 0.94 kg / cm 3, and when it is used as a grease-removing decorative paper, the grease on the face is removed and it is like taking a bath. .
【0004】[0004]
【発明が解決しようとする課題】従来の技術で使用され
ている、化粧用脂取り紙は手漉きのため量産するには限
界があり、最近では靭皮繊維に特殊な無機填料、例え
ば、クレー、タルク、カオリン、炭酸カルシウム、酸化
チタン等を混合させた後、特殊な定着剤を投入した後、
抄紙し更に化粧紙として使用後の透明性を上げるため、
名塩紙のような高密度になるようにキャレンダー等によ
り処理を行い、量産使用されている。The cosmetic fat removing paper used in the prior art has a limit in mass production due to hand-making, and recently, a special inorganic filler such as clay, After mixing talc, kaolin, calcium carbonate, titanium oxide, etc., after adding a special fixing agent,
In order to increase the transparency after making paper and also as decorative paper,
It is processed by a calender or the like so as to have a high density like Meishio paper, and is used in mass production.
【0005】しかし現行の化粧用脂取り紙では、使用後
の透明性が高く油脂分が取れた様に見えるが、2回、3
回と繰り返しても完全に顔面の油脂分が取れない問題点
がある。[0005] However, with the current cosmetic fat removing paper, the transparency after use is high and it seems that oil and fat are removed.
There is a problem that the oil and fat on the face cannot be completely removed even if it is repeated many times.
【0006】この発明は1回の使用で真の皮脂の高吸収
性があり更に使用後の透明性が高い特性が得られる高吸
油化粧用脂取り紙及びその製造方法を提供することにあ
る。SUMMARY OF THE INVENTION An object of the present invention is to provide a highly oil-absorbing cosmetic fat-absorbing paper, which has a high absorbency of true sebum in one use and a property of high transparency after use, and a method for producing the same.
【0007】[0007]
【課題を解決するための手段】上記の目的を達成するた
めに、この請求項1の発明においては、植物繊維を主成
分とする原料により、一層の抄紙からなり、抄紙時、線
経0.1〜1.0mmで5〜40メッシュの抄網にて片
面に凹凸層を設けた高吸油化粧用脂取り紙をその要旨と
している。In order to achieve the above-mentioned object, the invention according to claim 1 comprises a single layer of paper made from a raw material mainly composed of vegetable fiber. The gist of the present invention is a highly oil-absorbing cosmetic grease-absorbing paper provided with a concavo-convex layer on one surface by a paper net of 1 to 1.0 mm and 5 to 40 mesh.
【0008】この発明での植物繊維は、マニラ麻、亜
麻、黄麻、サイザル麻、ケナフ、雁皮、楮、バナナ繊
維、或は三椏からなる靱皮繊維又は木材パルプから選ば
れた少なくとも一種をいい、主成分とは、前記植物繊維
を50重量部%以上を含むことをいう。[0008] The plant fiber in the present invention refers to at least one selected from bast fiber or wood pulp composed of Manila hemp, flax, jute, sisal, kenaf, ganpi, kozo, banana fiber, mitsumata, Means that the plant fiber is contained at 50% by weight or more.
【0009】凹凸層がない脂取り紙の場合、紙の厚さ方
向のみで吸油するため、紙の厚さにより吸油量が制限さ
れる。又、使用時の肌触り・強度(使用時破けにくい)
・使い易さより、紙の坪量は15〜25g/m2の範囲
であり、使用時の吸油量には制限があり、特に顔面等の
皮脂の多い場合一枚のみの使用では十分に取れないた
め、2〜3枚使用する場合も生ずる。紙の片面に凹凸層
がある場合には、その凹部に皮脂が吸収され、凹凸層面
の表層部並びに紙の厚さ方向にて吸油され高い吸油量が
得られるため、特に顔面等の皮脂の多い場合一枚のみの
使用でも十分な効果が得られる。In the case of a grease-absorbing paper having no uneven layer, oil is absorbed only in the thickness direction of the paper, so that the amount of oil absorption is limited by the thickness of the paper. Also, feel and strength when used (hard to break when used)
-Due to ease of use, the basis weight of the paper is in the range of 15 to 25 g / m 2 , and the amount of oil absorbed during use is limited. Therefore, a case where two or three sheets are used also occurs. When there is an uneven layer on one side of the paper, sebum is absorbed in the concave portion, and oil is absorbed in the surface layer portion of the uneven layer surface and in the thickness direction of the paper, so that a high oil absorption amount is obtained. In this case, a sufficient effect can be obtained by using only one sheet.
【0010】前記凹凸層は、抄紙の段階で抄紙機のシリ
ンダーワイヤー上に金網又はプラスチックワイヤー又は
シリンダーワイヤー上に部分的に目止めを行うことによ
り、一層から形成される。[0010] The uneven layer is formed from a single layer by partially filling a wire net or a plastic wire or a cylinder wire on a cylinder wire of a paper machine at a paper making stage.
【0011】線径0.1mmから1.0mmの範囲で、
かつ5メッシュ〜40メッシュの範囲の抄網を使用する
と、凹凸層による吸油量及び紙層形成の点で好ましい。
0.1mm未満の線径では、吸油量が増加しないため好
ましくなく、1.0mmを越すと、紙層形成及び強度の
点でよくない。又、5メッシュ未満では、吸油量の点で
好ましくなく、40メッシュを越えると、凹凸層が形成
できず好ましくない。In the range of wire diameter from 0.1 mm to 1.0 mm,
It is preferable to use a mesh having a mesh size of 5 to 40 meshes in terms of oil absorption by the uneven layer and formation of the paper layer.
A wire diameter of less than 0.1 mm is not preferable because the oil absorption does not increase, and a wire diameter of more than 1.0 mm is not good in terms of paper layer formation and strength. On the other hand, if it is less than 5 meshes, it is not preferable in terms of oil absorption, and if it exceeds 40 meshes, it is not preferable because an uneven layer cannot be formed.
【0012】請求項2の発明は、請求項1において、凹
凸層に填料が混在することをその要旨としている。填料
とは、クレー、タルク、カオリン、炭酸カルシウム、酸
化チタン、あるいはホワイトカーボン等の填料をいい、
この填料が混在することにより、高吸油し、更に使用後
透明性が上がるものをいう。The gist of the invention of claim 2 is that, in claim 1, the filler is mixed in the uneven layer. Filler refers to a filler such as clay, talc, kaolin, calcium carbonate, titanium oxide, or white carbon.
When the filler is mixed, it means that the oil absorption is high and the transparency increases after use.
【0013】請求項3の発明は、請求項1又は請求項2
において、紙密度が0.7〜1.2g/cm3であるこ
とをその要旨としている。0.7〜1.2g/cm3の
範囲であると、高吸油し、更に使用後非常に透明性が上
がる。紙密度が0.7g/cm3未満の場合は、使用後
の透明性が悪くなり、1.2g/cm3を越えると、生
産が困難となるため好ましくない。[0013] The invention of claim 3 is claim 1 or claim 2.
, The gist is that the paper density is 0.7 to 1.2 g / cm 3 . When the amount is in the range of 0.7 to 1.2 g / cm 3 , the oil absorption is high, and the transparency is extremely increased after use. When the paper density is less than 0.7 g / cm 3 , the transparency after use becomes poor, and when it exceeds 1.2 g / cm 3 , production becomes difficult, which is not preferable.
【0014】請求項4の発明は、植物繊維を主成分とす
る原料を抄紙機にて1層を抄紙し、前記抄紙機は線経
0.1〜1.0mmで5〜40メッシュの抄網で片面に
凹凸層を形成することを特徴とする高吸油化粧用脂取り
紙の製造方法をその要旨としている。According to a fourth aspect of the present invention, one layer is formed from a raw material mainly composed of vegetable fiber by a paper machine, and the paper machine has a wire mesh of 0.1 to 1.0 mm and a mesh of 5 to 40 mesh. The gist of the present invention is a method for producing a highly oil-absorbing cosmetic grease-absorbing paper, characterized by forming an uneven layer on one surface.
【0015】(製造方法)原料は、マニラ麻、亜麻、黄
麻、サイザル麻、ケナフ、雁皮、楮、バナナ繊維あるい
は三椏から成る靭皮繊維又は木材パルプから選ばれた少
なくとも一種を50重量部%以上を用いることが望まし
い。50重量部%を下回ると、使用時の脂の取れ方の点
で好ましくない。(Production method) The raw material is at least 50% by weight of at least one selected from bast fiber or wood pulp consisting of manila hemp, flax, jute, sisal, kenaf, ganpi, kozo, banana fiber or mitsumata. It is desirable to use. If the amount is less than 50 parts by weight, it is not preferable in terms of removing fats during use.
【0016】ビー夕ー等の叩解機にて所定の叩解度に調
成し、更にタルク等の無機質填料を0.5〜40重量部
混合して均一分散する。そして、そのまま抄紙すると、
繊維への填料定着が悪く、排水の問題並びに工程の汚れ
が発生するため、その後定着剤としてファイレックスR
C104及びファイレックスM(ともに、明成化学工業
株式会社製)等を用い、繊維への定着性を向上する。そ
の後、丸網抄紙機、短網抄紙機、長網抄紙機等の抄き網
であって、線径0.1〜1.0mmで5〜40メッシュ
のものを使用して網目模様にて一層の凹凸紙を形成す
る、又は抄き網に部分的に金網の目を詰めることにより
その部分は原料が乗らず一層の凹凸紙を形成できる。The mixture is adjusted to a predetermined degree of beating with a beating machine such as Bee-Bee, and 0.5 to 40 parts by weight of an inorganic filler such as talc is mixed and uniformly dispersed. And if you make the paper as it is,
The filler fixation to the fiber is poor, causing drainage problems and process contamination.
Using C104 and Filex M (both manufactured by Meisei Chemical Industry Co., Ltd.), etc., the fixability to fibers is improved. Then, using a netting machine such as a round netting machine, a short netting machine, a long netting machine, etc., having a wire diameter of 0.1 to 1.0 mm and a mesh of 5 to 40 mesh, using a mesh pattern. By forming the irregular paper of the above, or by partially filling the mesh of the wire netting with the mesh, a portion of the irregular mesh paper can be formed without the raw material on that part.
【0017】なお、使用される無機質填料はクレー、タ
ルク、カオリン、炭酸カルシウム、酸化チタンあるいは
ホワイトカーボンの中から選ばれたものが使用できる
が、皮脂の吸油量を多くするには、マイクロタルクを使
用し平均粒子径2.5μ以下で表面積13.0 BET
m2/g以上のものが望ましい。The inorganic filler used may be selected from clay, talc, kaolin, calcium carbonate, titanium oxide and white carbon. To increase the oil absorption of sebum, use micro talc. Used with an average particle size of 2.5μ or less and a surface area of 13.0 BET
Those having m 2 / g or more are desirable.
【0018】使用後の透明性を上げるには密度を0.7
〜1.2g/cm3と高密度化する必要があり、所定の
寸法に裁断した後、箔打ち工程で数百回〜数千回の処理
を行う。なお、箔打ち工程の代りにスーパーキャレンダ
ー及び高圧プレス等により紙の密度を向上する方法もあ
る。To increase the transparency after use, a density of 0.7
It is necessary to increase the density to 1.21.2 g / cm 3, and after cutting to a predetermined size, several hundred to several thousand treatments are performed in the foiling step. It should be noted that there is a method of increasing the density of the paper by using a super calender, a high-pressure press or the like instead of the foiling step.
【0019】[0019]
【実施例】以下、実施例及び比較例について説明する。 (実施例1)実施例1では、下記の紙料、無機填料、及
び定着剤を使用した。EXAMPLES Examples and comparative examples will be described below. (Example 1) In Example 1, the following stock, inorganic filler, and fixing agent were used.
【0020】 マニラ麻 叩解度SR30゜ 100部 マイクロタルク 平均粒子径 1.7μ 20部 表面積 16.0 BETm2/g 定着剤 ファィレックスRC−104 0.5% ファイレックスM 0.3% すなわち、マニラ麻をビーターにて所定の叩解度に調成
し、マイクロタルクを20.0重量部を混合して均一分
散とした。そして、その後、定着剤としてファイレック
スRC−104及びファイレックスM(ともに、明成化
学工業株式会社製)を用いて、繊維へ定着させ、その
後、丸網抄紙機にて抄造した。Manila hemp beating degree SR30 ゜ 100 parts Microtalc Average particle size 1.7 μ 20 parts Surface area 16.0 BETm 2 / g Fixing agent Filex RC-104 0.5% Filex M 0.3% That is, Manila hemp is beater The mixture was adjusted to a predetermined degree of beating, and 20.0 parts by weight of microtalc were mixed to form a uniform dispersion. Then, using Firex RC-104 and Firex M (both manufactured by Meisei Chemical Industry Co., Ltd.) as fixing agents, the fibers were fixed to the fiber, and then the paper was formed by a round mesh paper machine.
【0021】丸網抄紙機の抄き網は線径0.2mmで1
6メッシュのものを使用し、1本バットにて坪量22g
/m2で片面側に凹凸層を抄紙した後、スーパーキャレ
ンダーにて密度1.0g/cm3にして化粧用脂取り紙
とした。The net of the round net paper machine has a wire diameter of 0.2 mm and a diameter of 1 mm.
Use a mesh of 6 mesh and weigh 22 g with one bat
/ M 2 , after making a concavo-convex layer on one side with a density of 1.0 g / cm 3 using a super calender, to obtain a cosmetic grease-absorbing paper.
【0022】(比較例1)比較例1では、実施例1と同
一の原料・薬品にてスラリーを調成し、抄き網は線径
0.132mmで90メッシュを使用し、1本バットに
て坪量22g/m2で両面ともに凹凸層のない紙を抄紙
した後、スーパーキャレンダーにて密度1.0g/cm
3の化粧用脂取り紙とした。(Comparative Example 1) In Comparative Example 1, a slurry was prepared from the same raw materials and chemicals as in Example 1, and a 90 mm mesh wire net having a diameter of 0.132 mm was used. After making a paper having a basis weight of 22 g / m 2 and having no uneven layer on both sides, the density was 1.0 g / cm by a super calender.
3 was used as a fat-absorbing paper for cosmetics.
【0023】(実施例2)比較例1及び実施例1の化粧
用脂取り紙を使用して下記試験方法にて吸油量を測定し
た。(Example 2) The oil absorption was measured by the following test method using the decorative grease-absorbing paper of Comparative Example 1 and Example 1.
【0024】(試験方法) 1.試験片は5cm × 5cmにする。 2.調湿後(JISP8111の条件)の試験片の重量
を測定する。(Test Method) The test piece is 5 cm x 5 cm. 2. After the humidity control (under the conditions of JISP 8111), the weight of the test piece is measured.
【0025】3.容器の中に入れた亜麻仁油の中に試験
片をどぶ漬けして5分間浸漬する。 4.試験片の一角をピンセットでつかみ、つかんだ角の
対角以外の対角線が平衡となるようにして5分間つる
す。3. The test piece is soaked in linseed oil in a container and immersed for 5 minutes. 4. Grasp one corner of the test piece with tweezers and suspend for 5 minutes so that the diagonal lines other than the diagonal of the gripped corner are in equilibrium.
【0026】5.5分間つるし終わった試験片を、カッ
プ容器に入れて計量する。 6.下式にて吸油率を演算する。 吸油率(%)= 吸油量(g)/吸油前試験片重量
(g)× 100 なお、吸油量(g)は、吸油後試験片重量(g)から吸
油前試験片重量(g)の差にて求める。The test specimen which has been suspended for 5.5 minutes is put into a cup container and weighed. 6. Calculate the oil absorption by the following formula. Oil absorption (%) = Oil absorption (g) / weight of test piece before oil absorption (g) x 100 The oil absorption (g) is the difference between the weight of the test piece after oil absorption (g) and the weight of the test piece before oil absorption (g). Ask at.
【0027】(試験結果)試験結果を表1に示す。(Test Results) The test results are shown in Table 1.
【0028】[0028]
【表1】 上記の表1のごとく比較例1に対して実施例1の方が吸
油率が35.9%も向上した。[Table 1] As shown in Table 1 above, the oil absorption of Example 1 was improved by 35.9% as compared with Comparative Example 1.
【0029】なお、この発明は、前記実施例に限定され
るものではなく、この発明から逸脱しない範囲で任意に
変更可能である。The present invention is not limited to the above embodiment, but can be arbitrarily changed without departing from the present invention.
【0030】[0030]
【発明の効果】以上詳述したようにこの発明は、化粧用
脂取り紙の片面又は両面に網目等の凹凸層を設けたこと
により、その凹部にて吸油量が大幅に増大し従来使用さ
れている化粧用脂取り紙に比べて真の皮脂量を増大し、
特に皮脂の発生量が多い場合の使用枚数を低減でき更に
使用後の透明感が非常に高いので使用後の満足感が得ら
れる化粧用脂取り紙とすることができる。As described above in detail, according to the present invention, the unevenness layer such as a mesh is provided on one side or both sides of the decorative fat-removing paper, so that the oil absorption in the concave portion is greatly increased, so that the present invention has been used conventionally. Increases the amount of true sebum compared to cosmetic fat-absorbing paper,
In particular, when the amount of generated sebum is large, the number of sheets used can be reduced, and the transparency after use is very high.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 FI D21H 5/24 Z ──────────────────────────────────────────────────の Continued on front page (51) Int.Cl. 6 Identification code FI D21H 5/24 Z
Claims (4)
層の抄紙からなり、抄紙時、線経0.1〜1.0mmで
5〜40メッシュの抄網にて片面に凹凸層を設けたこと
を特徴とする高吸油化粧用脂取り紙。1. A layer of paper made from a raw material mainly composed of vegetable fibers, and a paper-forming layer having a roughness of 0.1 to 1.0 mm and a mesh of 5 to 40 mesh on one side. A highly oil-absorbing cosmetic fat-absorbing paper, characterized in that:
の高吸油化粧用脂取り紙。2. The superabsorbent grease-absorbing paper according to claim 1, wherein a filler is mixed in the uneven layer.
求項1又は請求項2に記載の高吸油化粧用脂取り紙。3. The highly oil-absorbing cosmetic fat-removing paper according to claim 1, wherein the paper density is 0.7 to 1.2 g / cm 3 .
て1層を抄紙し、前記抄紙機は線経0.1〜1.0mm
で5〜40メッシュの抄網で片面に凹凸層を形成するこ
とを特徴とする高吸油化粧用脂取り紙の製造方法。4. A paper machine is used to make one layer of a raw material mainly composed of vegetable fiber by a paper machine, and the paper machine has a meridian of 0.1 to 1.0 mm.
A method for producing a highly oil-absorbing cosmetic grease-absorbing paper, characterized in that an uneven layer is formed on one side with a paper net of 5 to 40 mesh.