JPH11299940A - Iron club head - Google Patents

Iron club head

Info

Publication number
JPH11299940A
JPH11299940A JP10109175A JP10917598A JPH11299940A JP H11299940 A JPH11299940 A JP H11299940A JP 10109175 A JP10109175 A JP 10109175A JP 10917598 A JP10917598 A JP 10917598A JP H11299940 A JPH11299940 A JP H11299940A
Authority
JP
Japan
Prior art keywords
copper alloy
plate
head
iron club
alloy member
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP10109175A
Other languages
Japanese (ja)
Inventor
Naoki Asakawa
直己 浅川
Original Assignee
Sumitomo Rubber Ind Ltd
住友ゴム工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Rubber Ind Ltd, 住友ゴム工業株式会社 filed Critical Sumitomo Rubber Ind Ltd
Priority to JP10109175A priority Critical patent/JPH11299940A/en
Publication of JPH11299940A publication Critical patent/JPH11299940A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To make full use of the soft feeling natural to titanium by integrally fixing a copper alloy-made member having a specified weight composition ratio of Pb, Sn, Ni, and Cu and a specified specific gravity to a titanium head body.
SOLUTION: The weight composition of a plate copper alloy-made member 1 is set to 14.0-18.0% Pb, 6.0-10.0% Sn, 0.4-1.0% Ni, and the remainder of Cu, and the specific gravity is set to 9.0-9.5 A plate-like recessed part is formed on the back surface 3 of a titanium head body constituting the essential part of an iron club head, and the plate copper alloy-made member 1 has an outer form corresponding to the inside circumferential surface form of the plate-like recessed part of the back surface 3 of the head body. The copper alloy-made member 1 is fitted to the plate-like recessed part, and integrally fixed to the head body by adhesion or crushing plastic deformation. The weight ratio of the copper alloy-made member 1 to the whole head is set to 45.0-55.0%.
COPYRIGHT: (C)1999,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、アイアンクラブヘッドに関する。 The present invention relates to relates to an iron club head.

【0002】 [0002]

【従来の技術】従来、チタンあるいはチタン合金製アイアンクラブヘッドは、単一素材で製作すると大きくなりすぎるので、アイアンクラブヘッドの大きさを縮小するために、チタンあるいはチタン合金より十分に比重の大きい、真鍮・タングステン・銅─タングステン等の合金をチタンあるいはチタン合金製ゴルフクラブアイアンヘッド本体と複合化させていた。 Conventionally, titanium or a titanium alloy iron club head, since too large when manufactured in a single material, in order to reduce the size of the iron club head, large enough specific gravity than titanium or titanium alloy , an alloy such as brass, tungsten, copper ─ tungsten had not complexed with a titanium or titanium alloy golf club iron head body.

【0003】 [0003]

【発明が解決しようとする課題】しかしながら、従来の(上述のように)複合化させたアイアンクラブヘッドでは打球感が非常に硬く、打球時のチタン本来のソフトなフィーリングを生かせなかった。 The object of the invention is to be Solved However, the conventional (as described above) very hard and the shot feeling in the iron club head, which was composite, did not Ikase the titanium original soft feeling of the time of hitting the ball. そこで、本発明は、チタン本来のソフトなフィーリングを生かせるアイアンクラブヘッドを提供することを目的とする。 Therefore, an object of the present invention to provide an iron club head to capitalize the original soft feeling titanium.

【0004】 [0004]

【課題を解決するための手段】上述の目的を解決するために、本発明に係るアイアンクラブヘッドは、重量組成が14.0〜18.0%Pb,6.0 〜10.0%Sn,0.4 〜1.0 % To solve the above object, according to the solution to ## iron club head according to the present invention, the weight composition 14.0~18.0% Pb, 6.0 ~10.0% Sn, 0.4 ~1.0%
Ni,残部Cuから成る比重が9.0 〜9.5 の銅合金製部材を、チタン系のヘッド本体に、一体状に固着したことを特徴とするものである。 Ni, a copper alloy member having a specific gravity of 9.0 to 9.5 and the balance Cu, the head main body of titanium-based, and is characterized in that fixed to one piece.

【0005】また、ヘッド本体の背面に、板状の銅合金製部材を、一体状に固着したものである。 Further, on the back of the head body, a plate-like copper alloy member is obtained by integrally adhered to shape. また、ヘッド本体のソール面側に、銅合金製部材を一体状に固着したものである。 Moreover, the sole surface side of the head main body is obtained by integrally fixed to form the copper alloy member. また、ヘッド本体の背面及びソール面側に、銅合金製部材を一体状に夫々固着したものである。 Further, the back and the sole surface side of the head main body is obtained by fixing each integrally form the copper alloy member.
銅合金製部材のヘッド全体に占める重量比率を45.0〜5 The weight ratio of total head of the copper alloy member from 45.0 to 5
5.0%としたものである。 In which was 5.0%. また、ヘッド本体のフェース部肉厚を2.0 〜3.0 mmに設定し、かつ、板状の銅合金製部材の肉厚を3.0 〜6.0 mmに設定したものである。 Also, the face portion wall thickness of the head main body is set to 2.0 to 3.0 mm, and is obtained by setting the thickness of the plate-like copper alloy member in 3.0 ~6.0 mm.

【0006】 [0006]

【発明の実施の形態】以下、実施の形態を示す図面に基づき、本発明を詳説する。 DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, with reference to the drawings showing an embodiment of the present invention will now be described with.

【0007】図1は、銅合金製部材1を示す。 [0007] Figure 1 illustrates a copper alloy member 1. この銅合金製部材1は板状であって、その重量組成は14.0〜18.0 The copper alloy member 1 is a plate-like, its composition by weight is 14.0 to 18.0
%Pb,6.0 〜10.0%Sn,0.4 〜1.0 %Ni,残部C % Pb, 6.0 ~10.0% Sn, 0.4 ~1.0% Ni, balance C
uから成り、比重が9.0 〜9.5 である。 It consists of u, a specific gravity of 9.0 to 9.5. ただし、他の元素が多少含まれても良い。 However, it may be included other elements somewhat. 図2は、アイアンクラブヘッドの主要部を構成するチタン系のヘッド本体2を示し、 Figure 2 shows a head main body 2 of the titanium-based which constitutes the main part of the iron club head,
このヘッド本体2の背面3には浅皿状の凹所が形成されている。 Shallow dish-like recess is formed in the rear surface 3 of the head main body 2. なお、チタン系とは、純チタン又は僅かの他の元素を含有したチタン、若しくはチタン合金をいう。 Here, the titanium-based, titanium containing pure titanium or a slightly of other elements, or refers to a titanium alloy.

【0008】この板状の銅合金製部材1は、ヘッド本体2の背面3の浅皿状凹所の内周面形状に対応した外形を有し、この銅合金製部材1を浅皿状凹所に嵌着して、接着又は圧潰塑性変形等によりヘッド本体2に一体状に固着される。 [0008] Copper alloy member 1 of this plate has a contour corresponding to the inner peripheral shape of the shallow dish-shaped recess of the back 3 of the head main body 2, a shallow dish-shaped concave of the copper alloy member 1 and fitted in place, it is integrally fixed to form the head body 2 by bonding or crushing plastic deformation. 図3は、そのような固着後の(完成品の)縦断面図を示している。 3, such fixing post (PVC) shows a longitudinal sectional view. また、銅合金製部材1がヘッド全体に占める重量比率Pは45.0〜55.0%に設定されている。 Further, the copper alloy member 1 weight ratio P of the total head is set to 45.0 to 55.0%. 即ち重量比率Pを45.0%未満にすると、(ヘッド全体を必要重量にするためには)ヘッド全体の体積が大きくなり過ぎ、また、55.0%を越えると、打球感が硬くなってしまう。 That is, when the weight ratio P to less than 45.0%, (in order to require weight whole head) total volume head becomes too large, it exceeds 55.0% shot feel becomes hard.

【0009】さらに、図3に於いて、ヘッド本体2のフェース部肉厚tは、2.0 〜3.0 mmに設定されている。 Furthermore, in FIG. 3, the face portion thickness t of the head main body 2 is set to 2.0 to 3.0 mm. かつ、板状の銅合金製部材1の肉厚sは、3.0 〜6.0 mmに設定される。 And, the wall thickness s of the plate-like copper alloy member 1 is set to 3.0 ~6.0 mm. これらの肉厚t,sの範囲を外れると、強度不足、又は、重量(容積)が過大となるという問題があり、このような範囲の肉厚t,sの組み合わせが最も優れた打球感が得られる。 These wall thickness t, when outside the range of s, insufficient strength or there is a problem that the weight (volume) becomes excessive, the thickness t of this range, the combination is best shot feeling s can get.

【0010】図4は第2の実施の形態を示す。 [0010] Figure 4 shows a second embodiment. 銅合金製部材1は、ヘッド本体のソール面4に設けられた凹部5 Copper alloy member 1, the recess 5 provided in the sole surface 4 of the head body
に対応した(ブロック状又は板状の)形状をしており、 Corresponding to and a (block-like or plate-like) shape,
この凹部5に圧入等で一体状に固着される(接着剤を併用してもよい)。 It is integrally fixed to form press-fitting or the like in the recess 5 (or in combination of adhesive). 図5は第3の実施の形態を示す。 Figure 5 shows a third embodiment. 銅合金製部材1は、ヘッド本体2の背面3及びソール面4の凹部5に夫々一体状に固着される。 Copper alloy member 1 is fixed to the respective integrally shaped in the recess 5 of the back 3 and the sole surface 4 of the head main body 2.

【0011】 [0011]

【実施例】次に、図1〜図3で説明したアイアンクラブヘッドを本発明の実施例1として製造した。 EXAMPLES Next, to produce the iron club head described in FIGS. 1 to 3 as a first embodiment of the present invention. その際、純チタン熱間鍛造によってアイアンクラブヘッド本体素材を製作し、その背面にミーリング加工を施し、重量 130 At that time, we made the iron club head body material by forging pure titanium heat is subjected to milling in the back, the weight 130
gの純チタン単一素材の5番アイアンヘッド本体(2) g pure titanium single material No. 5 iron head body (2)
を作製した。 It was produced. そして、図1に示すような板状の銅合金製部材1であって重量が 120gのものを作製し、背面3の浅皿状凹所に嵌着状に固定した。 Then, the weight a plate-like copper alloy member 1, as shown in FIG. 1 was produced ones 120 g, it was fixed in the loading form shallow dish-shaped recess of the back 3. この実施例1の銅合金製部材1の重量組成は、16.0%Pb,8.0 %Sn,0.7 The composition by weight of the copper alloy member 1 of this embodiment 1, 16.0% Pb, 8.0% Sn, 0.7
%Ni,残部がCuであって、比重が9.5 で、(ビッカース)硬度が120Hvのものを用いた。 % Ni, the balance being a Cu, a specific gravity of 9.5, (Vickers) hardness used was the 120 Hv.

【0012】また、比較例1,2,3としては、図6, [0012] As a comparative example 1, 2, 6,
図7,図8に示す如く、実施例1(図2)と同一の材質及び形状・寸法のヘッド本体12を使用したが、背面13に嵌着状に固着する板状部材6,7,8としては、次の表1に示すような材質(比重,硬度)のものを使用した。 7, as shown in FIG. 8, Example 1 was used (Figure 2) the same material and shape and size head body 12 with the plate-like member 6, 7, 8 fixed to the fitting shape to the back 13 as used was made of a material such as shown in the following Table 1 (specific gravity, hardness).
純チタン製ヘッド本体12の背面13の凹所(底面)との接触(接着)面積を同じくするため、各板状部材6,7, To contact (adhesion) area between the recess of the back 13 of the pure titanium head body 12 (bottom) Similarly, the plate members 6 and 7,
8の厚さ寸法uを(比重に反比例して)増減させ、各板状部材6,7,8の重量を 120g(一定)とした。 8 of the thickness u (in inverse proportion to the specific gravity) is increased or decreased, the weight of the plate members 6, 7, 8 was 120 g (constant).

【0013】 [0013]

【表1】 [Table 1]

【0014】実施例1(図3)、比較例1(図6)、比較例2(図7)、及び比較例3(図8)の各アイアンクラブヘッドに、同仕様のシャフト及びグリップを夫々装着したアイアンゴルフクラブA,B,C,Dを作製した。 [0014] Example 1 (FIG. 3), Comparative Example 1 (FIG. 6), each iron club head of Comparative Example 2 (FIG. 7), and Comparative Example 3 (FIG. 8), respectively the shaft and the grip of the same specifications s mounting the iron golf club a, B, C, and D were prepared. 5人のテスターによる打球感の実打テストを行った。 By five testers were actual driving test of the feel at impact. その結果を、次の表2に示す。 The results are shown in the following Table 2. 評点は5段階のアンケート方式とし、打球感が柔らかい程、高得点とした。 Scores and questionnaire method out of 5, as the soft feel at impact, and a high score.

【0015】 [0015]

【表2】 [Table 2]

【0016】上記表2より、本発明の実施例1のアイアンクラブヘッド(アイアンゴルフクラブA)が明らかに打球感が良好(ソフトフィーリング)であることが分かる。 [0016] From the above Table 2, it can be seen iron club head (iron golf club A) is clearly feel at impact of the first embodiment of the present invention is good (soft feeling).

【0017】 [0017]

【発明の効果】本発明は上述の如く構成されるので、次に記載する効果を奏する。 According to the present invention because it is configured as described above, the effect which will be described.

【0018】(請求項1、2、3又は4によれば)ゴルフボールを打撃したときの打球感を柔らかくすることができる。 [0018] it is possible to soften the feel at impact of the time you hit the golf ball (according to claim 1, 2, 3 or 4). (請求項2又は4によれば)ゴルフボールに直接接触するフェース面の裏側───背面3───に板状の銅合金製部材1を固着したので、打球感の一層の改善を図り得る。 Having secured the (Claim 2 or according to 4) Copper alloy member 1 to the back side ─── back 3─── plate-shaped face surface in direct contact with the golf ball, aim to further improve the feel at impact obtain. このように、ヘッド本体2の材質であるところのチタン本来のソフトなフィーリングを十分に活かし得る。 Thus, can leverage sufficient titanium inherent soft feel where a material of the head main body 2. (請求項5によれば)ヘッド全体の体積を小さく保ちながら、良好な打球感が得られる。 While keeping small head total volume (according to claim 5), good shot feeling is obtained. (請求項6によれば)強度を十分に維持しつつ、最も優れた打球感が得られる。 While maintaining sufficient strength (according to claim 6), the best shot feeling is obtained.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】銅合金製部材を示す斜視図である。 1 is a perspective view showing a copper alloy member.

【図2】ヘッド本体を示す背面側から見た斜視図である。 2 is a perspective view from the back side of a head main body.

【図3】本発明の実施の一形態を示す断面図である。 3 is a cross-sectional view showing an embodiment of the present invention.

【図4】本発明の実施の他の形態を示す断面図である。 4 is a sectional view showing another embodiment of the present invention.

【図5】本発明の実施の別の形態を示す断面図である。 5 is a cross-sectional view showing another embodiment of the present invention.

【図6】比較例1を示す断面図である。 6 is a sectional view showing a comparative example 1.

【図7】比較例2を示す断面図である。 7 is a sectional view showing a comparative example 2.

【図8】比較例3を示す断面図である。 8 is a sectional view showing a comparative example 3.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 銅合金製部材 2 ヘッド本体 3 背面 4 ソール面 1 Copper alloy member 2 head main body 3 back 4 sole surface

Claims (6)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 重量組成が14.0〜18.0%Pb,6.0 〜1 1. A weight composition 14.0~18.0% Pb, 6.0 ~1
    0.0%Sn,0.4 〜1.0%Ni,残部Cuから成る比重が 0.0% Sn, 0.4 ~1.0% Ni, specific gravity and the balance Cu
    9.0 〜9.5 の銅合金製部材1を、チタン系のヘッド本体2に、一体状に固着したことを特徴とするアイアンクラブヘッド。 Copper alloy member 1 of 9.0 to 9.5, to the head main body 2 of the titanium-based, iron club head is characterized in that fixed to one piece.
  2. 【請求項2】 ヘッド本体2の背面3に、板状の銅合金製部材1を、一体状に固着した請求項1記載のアイアンクラブヘッド。 Wherein the back 3 of the head main body 2, the copper alloy member 1 of the plate, an iron club head according to claim 1, wherein the fixed integrally form.
  3. 【請求項3】 ヘッド本体2のソール面4側に、銅合金製部材1を一体状に固着した請求項1記載のアイアンクラブヘッド。 Wherein the sole surface 4 side of the head main body 2, an iron club head according to claim 1, wherein the fixed copper alloy member 1 together form.
  4. 【請求項4】 ヘッド本体2の背面3及びソール面4側に、銅合金製部材1を一体状に夫々固着した請求項1記載のアイアンクラブヘッド。 4. A rear 3 and the sole surface 4 side of the head main body 2, an iron club head according to claim 1, wherein the copper alloy member 1 secured respectively to one piece.
  5. 【請求項5】 銅合金製部材1のヘッド全体に占める重量比率が45.0〜55.0%である請求項1,2,3又は4記載のアイアンクラブヘッド。 5. A method according to claim 1, 2, 3 or 4 iron club head, wherein the weight ratio of total head of the copper alloy member 1 is 45.0 to 55.0%.
  6. 【請求項6】 ヘッド本体2のフェース部肉厚を2.0 〜 6. The face portion wall thickness of the head main body 2 2.0 to
    3.0 mmに設定し、かつ、板状の銅合金製部材1の肉厚を Set 3.0 mm, and the thickness of the copper alloy member 1 plate
    3.0 〜6.0 mmに設定した請求項2又は4記載のアイアンクラブヘッド。 3.0 to 6.0 according to claim 2 or 4 iron club head according to set mm.
JP10109175A 1998-04-20 1998-04-20 Iron club head Pending JPH11299940A (en)