JPH11246838A - Adhesive composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain an adhesive composition capable of solving the problem of hardening retardation caused by decrease of formaldehyde in an amino resin, capable of improving productivity and economy, and useful for adhesion of a veneer, a sliced veneer or the like by including a specific amino resin and a specified hardening accelerator. SOLUTION: This adhesive composition comprises (A) an amino resin having a molar ratio of formaldehyde to an amino group regulated so as to be 0.4-0.9, and (B) a hardening accelerator comprising one or more kinds of a persulfuric acid salt, a peroxide and an azo compound, [e.g. ammonium persulfate, hydroperoxide and 2,2'-azobis(2-amidinopropane) hydrochloride], preferably in an proportion of 0.05-20 pts.wt. component B based on 100 pts.wt. component A (expressed in terms of solid).

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention relates to plywood, veneer plywood,
The present invention relates to an adhesive composition containing a low-molar-ratio amino resin as a main component, which is used without lowering productivity at the time of bonding a laminated wood, a wood fiber board or the like.

[0002]

2. Description of the Related Art Conventionally, when plywood, veneer plywood, laminated wood, wood fiber board, etc. are adhesively molded, urea resin, melamine resin,
Generally, an amino resin such as a urea-melamine co-condensation resin is used as a main component, and an ammonium salt is added as a curing agent to form an adhesive composition, which is generally applied to an adherend and used.

However, when an adhesive composition containing a formaldehyde-based amino resin as a main component is used, the amount of free formaldehyde in the adhesive composition is reduced, so that even when an ammonium salt is added as a curing agent, the curing property is not increased. There is a disadvantage that it cannot be promoted.

[0004]

SUMMARY OF THE INVENTION The present invention is intended to solve the problem of retardation of curing by reducing formaldehyde of amino resin and to improve the economic efficiency by accelerating the curing.

[0005]

According to the present invention, it has been found that the curing is accelerated by using a specific compound to solve the curing delay due to the reduction of formaldehyde in the amino resin.

That is, the present invention relates to an amino resin in which the molar ratio of formaldehyde (F) to amino group (NH ₂ ) (F / NH ₂ ) is adjusted to 0.4 to 0.8, and a persulfate as a curing accelerator. The present invention relates to an adhesive composition using at least one, or two or more of a peroxide, an azo compound and a peroxide.

[0007]

DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail.
Conventionally, when adhesively molding plywood, veneer plywood, glued laminated wood, wood fiber board, etc., an urea resin, a melamine resin, an amino resin such as a urea-melamine co-condensation resin as a main component, and an extender such as flour and water are added. It is a common practice to mix well and further add an ammonium salt as a curing agent to form an adhesive composition, which is applied to an adherend and used.

However, plywood, veneer plywood, laminated wood, wood fiber board, and the like using an adhesive composition containing an amino resin as a formalin resin as a main component use formaldehyde as a part of the raw material. Unreacted formaldehyde remains in these during curing by hot pressure, and the cured product also releases formaldehyde due to the progress of hydrolysis and condensation reactions. These formaldehyde move to the surface and are released from the plate surface or side surface. This is the so-called formalin odor, which causes irritation and discomfort. In recent years, particularly, formaldehyde to be released has become a serious social problem, and various measures for reducing formaldehyde in resin have been studied in order to solve these problems of formaldehyde emission. Therefore, it is conceivable to use a urethane resin containing no formaldehyde at all, an aqueous vinyl urethane resin, or the like, but it is obviously difficult to use it as a general-purpose resin in practice, and it will increase the cost significantly.

Therefore, an adhesive composition containing as a main component a resin obtained by reducing formaldehyde of an amino resin which is a general-purpose resin has been studied. However, in this adhesive composition, formaldehyde remaining in the composition and ammonium chloride, which is usually used as a curing agent, are cured by lowering the pH with hydrochloric acid generated by the reaction. For this reason, amino resins satisfying the Japanese Agriculture and Forestry Standard and the formaldehyde emission test F1 standard specified for ordinary plywood lack formaldehyde and do not generate a sufficient amount of hydrochloric acid, and the curing of the resin is delayed and the adhesive strength cannot be satisfied. The problem remains. Further, the time for hot pressing must be extended in order to obtain sufficient adhesive strength, which is disadvantageous in terms of productivity.

[0010] Further, since chlorinated hydrochloric acid generated by the decomposition of ammonium chloride remains on the obtained plywood or the like,
When burning and discarding, etc., there is a concern about environmental problems. Further, there is a method of using an acid substance such as hydrochloric acid or sulfuric acid as a pH adjuster in order to accelerate the curing of the adhesive composition and satisfy the adhesive strength. Can not be satisfied. Under the condition where the amount of addition is large, sufficient adhesive strength can be satisfied, but the viscosity of the adhesive composition increases sharply with the lapse of time, and the pot life, which is the actual use time, is short, leaving a problem. There are also problems such as a narrow range for obtaining an appropriate amount of addition.

On the other hand, in the case of the Japanese Agriculture and Forestry Standard, which contains a large amount of formaldehyde, the formaldehyde emission test F3 standard, which is specified for ordinary plywood, or an amino resin exceeding this, sufficient formaldehyde is present and the adhesive strength is satisfied, but it is generated in the manufacturing process. Problems remain such that the formaldehyde odor becomes strong, the working environment deteriorates, and the amount of emitted formaldehyde is large.

The amino resin of the present invention comprises one or more compounds having an amino group in a molecule such as urea, thiourea, melamine, benzoguanamine, dicyandiamine and the like, and an aldehyde such as formaldehyde. Refers to reacted oligomers and / or polymers.

In particular, melamine is mixed or co-condensed with a urea resin to impart water resistance to form a urea-melamine resin, so that a decrease in strength in a high humidity environment can be avoided. In addition, it may be mixed with other polymers such as polyvinyl alcohol and cellulose derivatives to impart various properties at the time of amino resin production, or, if necessary, at the time of use, a water emitting agent, a flame retardant, an insect repellent, a preservative. And the like.

The amino resin used in the present invention is a resin in which the molar ratio of formaldehyde (F) to amino group (NH ₂ ) (F / NH ₂ ) is adjusted to 0.4 to 0.8. If the molar ratio of formaldehyde to amino group is less than 0.4, sufficient adhesive strength and water-resistant adhesive strength cannot be obtained,
On the other hand, if it exceeds 0.8, a resin having a low required emission formaldehyde cannot be obtained although the adhesive strength is high. Also,
The ratio of amino groups related to melamine in the amino groups is 0.3
Molar% or more is preferable because stable water resistance can be obtained.

[0015] The production method and properties of the amino resin are not particularly limited, and ordinary production methods may be used. Amino resins are desirable because they use a catalyst or form a cured product which is polymerized by heating and partially crosslinked to form a high-hardness adhesive layer, which increases the bending strength and rigidity of the plywood and the like obtained.

In the present invention, persulfates, peroxides or azo compounds are used as a curing accelerator. Examples of persulfates include ammonium persulfate, potassium persulfate, sodium persulfate, barium persulfate and the like. Also,
Examples of the peroxide include ketone peroxide, peroxyketal, hydroperoxide, dialkyl peroxide, diacyl peroxide, peroxyester, peroxydicarbonate, and the like.

Further, as the azo compound, 2,2'-
Azobisisobutyronitrile, 2,2′-azobis (4
-Methoxy-2,4-dimethylpentanenitrile),
Azonitrile type such as 2,2′-azobis (2,4-dimethylpentanenitrile) and 2,2′-azobis (2-methylbutanenitrile), azoamidine type [V-50
Wako Pure Chemical Industries K. K, 2,2'-azobis (2-amidinopropane) hydrochloride], azodicarbonamide, 2,2'-azobis (azoamides such as 2-methylpropanimidamide, 2,2'-azobis (2-
The azoalkyl type of acetoxypropane can be listed.
One or more of these persulfates, peroxides and azo compounds may be used.

Further, ammonium salts are used as a curing agent. Examples of the ammonium salt include ammonium nitrate, ammonium sulfate, ammonium hydrochloride, ammonium phosphate, ammonium carbonate, and ammonium acetate. In addition, ammonium chloride which has been used conventionally can be used, but is not preferable because of environmental problems.

The amount of the persulfate, peroxide or azo compound used in the adhesive composition is 0.05 to 20 parts by weight (in terms of solid content) based on 100 parts by weight (in terms of solid content) of the amino resin used in the adhesive composition. 0.0 parts by weight, more preferably 0.2 to 10.0 parts by weight, and most preferably 0.1 part by weight.
3 to 7.0 parts by weight are preferred. If the addition amount is less than 0.05 parts by weight, the curability of the resin is hardly improved, which is not preferable. On the other hand, if the amount exceeds 20.0 parts by weight, the viscosity of the adhesive composition rises significantly with the passage of time. Not preferred.

The use of a persulfate, a peroxide or an azo compound in the amino resin of the present invention also has the effect of improving the tolerance of the moisture content of a single plate as an adherend. That is, by curing in a short time, the moisture contained in the veneer at the time of hot pressing forms an adhesive layer that can withstand the internal pressure of water vapor applied to the adhesive layer. Adhesion is possible even at the water content of the plate, and the shrinkage loss of the veneer as the adherend can be reduced, which is economically advantageous.

[0021]

Hereinafter, the present invention will be described in detail with reference to Examples.
The present invention is not limited to these examples. Parts and% represent parts by weight or% by weight unless otherwise specified. Example 1 A reaction vessel equipped with a stirrer, a reflux condenser, and a thermometer was charged with 750 parts of a 48% formaldehyde aqueous solution, the pH was adjusted to 8.0, and then 360 parts of primary urea was added. And reacted at 85 ° C. for 30 minutes. Thereafter, the pH was readjusted to 5.8, reacted for 15 minutes, and further adjusted to pH 7.5.
Was added and reacted for 30 minutes. Thereafter, the resultant was cooled to obtain an amino resin (hereinafter abbreviated as a1). As for a1, the molar ratio (F / NH ₂ ) of the amino group (NH ₂ ) in formaldehyde (F) and urea (U) was 0.6. The nonvolatile content was adjusted to 50.0%. Next, using a1, the curing time of the resin was measured under the following method and conditions. Resin 100
A part was weighed in a glass beaker, a curing accelerator was added to the resin, and mixed and stirred for 5 minutes to obtain a sample. Further, 5 g of the sample was weighed into a test tube, immersed in boiling water at 100 ° C., and the time required for curing was measured. Table 1 shows the results. Furthermore, a1
Plywood is made using the following conditions using JAS ordinary plywood,
An adhesion test by a hot and cold water immersion test was measured. Table 1 shows the evaluation results.

(Adhesion conditions) a1 resin 100 parts Wheat flour (Nisshin Flour Milling Co., Ltd., red flower) 25 parts Water 20 parts Ammonium persulfate 0.5 part The compounding viscosity was adjusted to 20 to 25 poise.

(Plywood manufacturing conditions) Material type: Rawan Single veneer configuration: 0.6 mm + 1.4 mm + 0.6 mm Veneer water content: 10% or less Coating amount: 30 g / m ² Deposition time: 15 minutes Cold pressure / time: 10 kg / ^cm 2 · 30 min heat-pressure pressure, temperature, ^{time: 8kg / cm 2 · 115 ℃} · 50 seconds

Example 2 An amino resin was prepared in the same manner as in Example 1 except that 360 parts of primary urea and 240 parts of secondary urea were changed to 510 parts and 390 parts, respectively (hereinafter abbreviated as a2). Obtained. In addition, a plywood was prepared in the same manner as in Example 1, and an adhesion test by a JAS ordinary plywood and a hot and cold water immersion test was measured. Table 1 shows the evaluation results. a2, the molar ratio of formaldehyde (F) and amino group _{(NH 2) (F / NH} 2) was 0.4. The nonvolatile content was adjusted to 50.0%.

Example 3 Example 1 was repeated except that 360 parts of primary urea and 240 parts of secondary urea were changed to 360 parts and 90 parts, respectively, and further to 15 parts of powdered melamine (hereinafter abbreviated as a3). And an amino resin was obtained. In addition, a plywood was prepared in the same manner as in Example 1, and an adhesion test by a JAS ordinary plywood and a hot and cold water immersion test was measured. Table 1 shows the evaluation results. a3 is the molar ratio of formaldehyde (F) to amino group (NH ₂ ) (F
/ NH ₂ ) was 0.78, and the ratio of amino groups related to melamine in the amino groups (NH ₂ ) was 2.3 mol%. The nonvolatile content was adjusted to 50.0%.

Example 4 The procedure of Example 1 was repeated except that 0.5 part of ammonium persulfate was changed to 1.0 part. Table 1 shows the evaluation results.

Example 5 The procedure of Example 1 was repeated except that ammonium persulfate in Example 1 was changed to hydroperoxide.
Table 1 shows the evaluation results.

Example 6 The same operation as in Example 1 was carried out except that the ammonium persulfate in Example 1 was changed to V-50. Table 1 shows the evaluation results.
Shown in

Comparative Example 1 The procedure of Example 1 was repeated, except that 0.5 part of ammonium persulfate was changed to 1.0 part of ammonium chloride. Table 1 shows the evaluation results.

Comparative Example 2 An amino resin was prepared in the same manner as in Example 1, except that 360 parts of primary urea and 240 parts of secondary urea were changed to 630 parts and 400 parts, respectively (hereinafter abbreviated as a4). Obtained. In addition, a plywood was prepared in the same manner as in Example 1, and an adhesion test by a JAS ordinary plywood and a hot and cold water immersion test was measured. Table 1 shows the evaluation results. a4, the molar ratio of formaldehyde (F) and amino group _{(NH 2) (F / NH} 2) was 0.35. The nonvolatile content was adjusted to 50.0%.

[0031]

[Table 1]

[0032]

According to the present invention, there is an advantage that the curing delay caused by using an amino resin having reduced formaldehyde can be solved and the productivity can be improved. That is, the present invention is to obtain a plywood and the like with less formaldehyde emission,
Formaldehyde in the adhesive composition must be reduced. As a result, it is necessary to add hydrochloric acid, sulfuric acid, or the like as a pH adjuster, or to extend the time during hot pressing. However, by using the specific curing accelerator of the present invention,
Improve productivity without changing conventional conditions,
All of these can be solved.

 ──────────────────────────────────────────────────続 き Continued on the front page (72) Inventor Nobuhiko Kotan 7-1-1, Hikoshimasako-cho, Shimonoseki-shi, Yamaguchi Prefecture Inside Mitsui Chemicals, Inc. No. 1 in Mitsui Chemicals, Inc.

Claims (4)

[Claims] 1. A molar ratio of formaldehyde (F) to amino group (NH ₂ ) (F / NH ₂ ) of 0.4 to 0.5.
An adhesive composition using an amino resin adjusted to 8 and at least one or two or more of a persulfate, a peroxide and an azo compound as a curing accelerator. 2. The adhesive composition according to claim 1, wherein the addition amount of the curing accelerator is 0.05 to 20 parts by weight based on 100 parts by weight (in terms of solid content) of the amino resin. 3. The adhesive composition according to claim 1, wherein the ratio of amino groups related to melamine in the amino groups of the amino resin is 0.3 mol% or more. 4. The adhesive composition according to claim 1, wherein an ammonium salt is used in combination with a persulfate, a peroxide or an azo compound.