JPH11219082A - Cleaning blade and its manufacture - Google Patents
Cleaning blade and its manufactureInfo
- Publication number
- JPH11219082A JPH11219082A JP10020600A JP2060098A JPH11219082A JP H11219082 A JPH11219082 A JP H11219082A JP 10020600 A JP10020600 A JP 10020600A JP 2060098 A JP2060098 A JP 2060098A JP H11219082 A JPH11219082 A JP H11219082A
- Authority
- JP
- Japan
- Prior art keywords
- plate
- blade member
- cleaning blade
- metal plate
- resin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、クリーニングブレ
ード及びその製造方法に関し、さらに詳しくは、電子写
真装置における画像形成体の表面に残留するトナーを掻
き取るために用いられ、かつその板状ブレード部材の圧
縮永久歪が小さく、クリーニング性能に優れたクリーニ
ングブレード、及びこれを効率よく製造する方法に関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cleaning blade and a method for manufacturing the same, and more particularly, to a cleaning blade and a plate-like blade member used for scraping toner remaining on the surface of an image forming body in an electrophotographic apparatus. The present invention relates to a cleaning blade having a small compression set and excellent cleaning performance, and a method for efficiently producing the same.
【０００２】[0002]
【従来の技術】従来、複写機，ファクシミリ，プリンタ
ー等の電子写真装置等においては、一般にまず、光導電
性物質〔例えばＺｎＯ，ＣｄＳ，Ｓｅ，ＯＰＣ（有機半
導体），α−Ｓｉなど〕を用いた画像形成体（感光体）
の表面を一様に帯電させ、これに光学系から映像を投射
して、光の当たった部分の帯電を消去することによって
潜像を形成し、さらにトナーの付着（現像）、紙などの
転写材（記録媒体）へのトナー画像の転写により、複写
を行う方法がとられている。このような電子写真装置に
おいては、トナー像の転写後に、画像形成体外周面上に
トナーが残留するため、例えば図１（ａ）の斜視図及び
（ｂ）の断面図で示されるような板状ブレード部材１と
支持部材２とを有するクリーニングブレードを用い、前
記画像形成体外周面に、板状ブレード部材１の先端部３
を摺接させ、残留トナーを掻き取り、除去することが行
われている。2. Description of the Related Art Conventionally, in an electrophotographic apparatus such as a copying machine, a facsimile, and a printer, a photoconductive substance (for example, ZnO, CdS, Se, OPC (organic semiconductor), α-Si, etc.) is generally used. Image forming body (photoreceptor)
Surface is uniformly charged, an image is projected from the optical system onto the surface, a latent image is formed by erasing the charged portion of the light, a toner is attached (developed), and paper is transferred. A method of performing copying by transferring a toner image to a material (recording medium) has been adopted. In such an electrophotographic apparatus, since the toner remains on the outer peripheral surface of the image forming body after the transfer of the toner image, for example, a plate as shown in the perspective view of FIG. A cleaning blade having a plate-shaped blade member 1 and a support member 2 is used, and a tip 3 of the plate-shaped blade member 1 is formed on the outer peripheral surface of the image forming body.
Are slid in contact with each other to scrape and remove residual toner.
【０００３】このような機能を有するクリーニングブレ
ードにおいては、その板状ブレード部材は、一般に
（１）画像形成体を汚染したり、傷付けたりしない、
（２）耐摩耗性に優れる、（３）圧縮永久歪が小さい、
などの性能が要求される。このクリーニングブレード
は、通常、その板状ブレード部材として、画像形成体を
傷付けることがなく、かつ耐摩耗性に優れることから、
熱可塑性エラストマーなどが用いられており、そして、
金型を使用する注入成形によって作製されている。すな
わち、クリーニングブレード用金型内に支持部材を配置
したのち、金型内に板状ブレード部材成形材料を注入
し、硬化させることにより、板状ブレード部材と支持部
材とを一体化したクリーニングブレードを得ている。し
かしながら、上記板状ブレード部材として用いられる従
来の熱可塑性エラストマーは、適度の硬度を有し、画像
形成体を傷付けたりすることが少なく、かつ耐摩耗性に
優れるなどの長所を有しているが、圧縮永久歪が比較的
大きく、画像形成体に対して必要な面圧が充分に得られ
ない場合があり、クリーニングブレード性能について
は、必ずしも満足しうるものではなかった。In a cleaning blade having such a function, the plate-like blade member generally (1) does not contaminate or damage the image forming body.
(2) excellent wear resistance, (3) small compression set,
Such performance is required. This cleaning blade, as its plate-shaped blade member, usually does not damage the image forming body, and is excellent in abrasion resistance.
Thermoplastic elastomers and the like are used, and
It is made by injection molding using a mold. That is, after the support member is disposed in the cleaning blade mold, the plate blade member molding material is injected into the mold and cured to form a cleaning blade in which the plate blade member and the support member are integrated. It has gained. However, conventional thermoplastic elastomers used as the plate-like blade members have advantages such as having appropriate hardness, less damage to the image forming body, and excellent wear resistance. In some cases, the compression set was relatively large, and the required surface pressure on the image forming body could not be sufficiently obtained, and the cleaning blade performance was not always satisfactory.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、このような
状況下で、特に圧縮永久歪の小さい部材を板状ブレード
部材として用いてなる、クリーニング性能に優れたクリ
ーニングブレードを提供することを目的とするものであ
る。SUMMARY OF THE INVENTION It is an object of the present invention to provide a cleaning blade having excellent cleaning performance, in which a member having a particularly small compression set is used as a plate-like blade member under such circumstances. It is assumed that.
【０００５】[0005]
【課題を解決するための手段】本発明者らは、特に圧縮
永久歪の小さい板状ブレード部材をもつクリーニング性
能に優れるクリーニングブレードを開発すべく鋭意研究
を重ねた結果、金属板上に樹脂層を設けた積層体を、板
状ブレード部材として用いることにより、その目的を達
成しうることを見出した。本発明は、かかる知見に基づ
いて完成したものである。すなわち、本発明、板状ブレ
ード部材とこれを支持する支持部材を有し、かつ該板状
ブレード部材を画像形成体に当接させ、その表面に残留
するトナーを除去するクリーニングブレードにおいて、
前記板状ブレード部材が、金属板上に樹脂層を設けた積
層体であることを特徴とするクリーニングブレードを提
供するものである。また、このクリーニングブレード
は、（Ａ）金属板上に樹脂層を設け積層体を作製する工
程、（Ｂ）上記積層体を所定形状の板状ブレード部材に
加工する工程及び（Ｃ）この板状ブレード部材と支持部
材とを一体化させる工程を順次行うことにより、製造す
ることができる。Means for Solving the Problems The inventors of the present invention have conducted intensive studies to develop a cleaning blade having a plate blade member having a small compression set and excellent cleaning performance, and as a result, a resin layer is formed on a metal plate. It has been found that the object can be achieved by using a laminated body provided with as a plate-like blade member. The present invention has been completed based on such findings. That is, the present invention provides a cleaning blade having a plate-shaped blade member and a support member for supporting the plate-shaped blade member, and contacting the plate-shaped blade member with an image forming body to remove toner remaining on the surface thereof.
A cleaning blade is provided, wherein the plate-shaped blade member is a laminate in which a resin layer is provided on a metal plate. Further, the cleaning blade comprises: (A) a step of providing a resin layer on a metal plate to form a laminate; (B) a step of processing the laminate into a plate-like blade member having a predetermined shape; It can be manufactured by sequentially performing a process of integrating the blade member and the support member.
【０００６】[0006]
【発明の実施の形態】本発明のクリーニングブレード
は、板状ブレード部材とこれを支持する支持部材を有す
るものであって、該板状ブレード部材を感光ドラムなど
の画像形成体に当接させ、その表面に残留するトナーを
除去するのに用いられる。本発明においては、このクリ
ーニングブレードにおける板状ブレード部材として、金
属板上に樹脂層が設けられた積層体が用いられる。上記
積層体における金属板としては、適度の機械的強度及び
たわみ性などを有するものであればよく、特に制限され
ず、様々な材料からなるものの中から、状況に応じて適
宜選択して用いることができる。この金属板の例として
は、ＳＳ系などの一般的な鋼板，ＳＵＳ３００系やＳＵ
Ｓ４００系などのステンレス鋼板，銅板，亜鉛めっき鋼
板，アルミニウム／亜鉛合金めっき鋼板，真鍮板，アル
ミニウム板，アルミニウム合金板などが挙げられる。こ
れらの金属板の厚さは、得られる積層体の圧縮永久歪，
機械的強度，たわみ性，弾性率などを考慮し、使用する
材料の種類などに応じて適宜選定されるが、一般的には
0.０２〜0.５ｍｍの範囲である。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A cleaning blade according to the present invention has a plate-shaped blade member and a support member for supporting the plate-shaped blade member. The plate blade member is brought into contact with an image forming body such as a photosensitive drum. It is used to remove toner remaining on the surface. In the present invention, a laminate in which a resin layer is provided on a metal plate is used as the plate-like blade member of the cleaning blade. The metal plate in the laminate is not particularly limited as long as it has appropriate mechanical strength and flexibility, and is appropriately selected from those made of various materials depending on the situation. Can be. Examples of the metal plate include a general steel plate such as an SS type, a SUS300 type and a SU type.
Examples include stainless steel plates such as S400 series, copper plates, galvanized steel plates, aluminum / zinc alloy-plated steel plates, brass plates, aluminum plates, aluminum alloy plates, and the like. The thickness of these metal plates depends on the compression set of the resulting laminate,
Considering mechanical strength, flexibility, elastic modulus, etc., it is appropriately selected according to the type of material used, etc.
It is in the range of 0.02 to 0.5 mm.
【０００７】また、この金属板の物性については、ＪＩ
Ｓ Ｚ２２４１による測定において、引張強さが３０〜
４０ｋｇ／ｍｍ2 、降伏点が２０ｋｇ／ｍｍ2 以上、Ｊ
ＩＳＫ６３０１による測定において、伸びが２０％以上
であるのが好ましい。一方、この金属板上に設けられる
樹脂層を構成する樹脂としては、ＪＩＳ Ｋ６３０１に
よる測定において、硬度〔スプリング式硬さ試験（Ａ
型）〕が６０〜８０、伸びが３００〜３５０％、永久伸
びが1.０〜5.０％、３００％モジュラスが１３０〜２５
０ｋｇ／ｃｍ2 の範囲にあるものが好ましく用いられ
る。このような樹脂としては、上記物性を有するもので
あればよく、特に制限されず、従来板状ブレード部材に
おいて慣用されている樹脂、例えばウレタン系，スチレ
ン系，オレフィン系，塩化ビニル系，ポリエステル系，
ポリアミド系，フッ素系樹脂などの熱可塑性樹脂の中か
ら適宜選択して用いることができるが、これらの中で、
前記物性、さらには耐摩耗性や経済性などの面から、特
に熱可塑性ウレタン樹脂が好適である。Regarding the physical properties of this metal plate, see JI
In the measurement by SZ2241, the tensile strength is 30 to
40 kg / mm 2 , yield point 20 kg / mm 2 or more, J
In the measurement by ISK6301, the elongation is preferably 20% or more. On the other hand, as the resin constituting the resin layer provided on the metal plate, the hardness [spring hardness test (A
Mold)] of 60 to 80, elongation of 300 to 350%, permanent elongation of 1.0 to 5.0%, and 300% modulus of 130 to 25.
Those in the range of 0 kg / cm 2 are preferably used. Such a resin is not particularly limited as long as it has the above-mentioned properties, and resins conventionally used in conventional plate-shaped blade members, for example, urethane-based, styrene-based, olefin-based, vinyl chloride-based, and polyester-based resins are used. ,
It can be used by appropriately selecting from thermoplastic resins such as polyamide-based and fluorine-based resins.
A thermoplastic urethane resin is particularly preferable from the viewpoint of the above-mentioned physical properties, wear resistance and economy.
【０００８】本発明においては、前記樹脂は一種用いて
もよく、二種以上を組み合わせて用いてもよい。本発明
のクリーニングブレードにおいて、板状ブレード部材と
して用いられる積層体は、前記金属板上に、これらの樹
脂からなる層が設けられたものであって、この樹脂層の
厚さは、通常0.１〜3.０ｍｍの範囲である。この厚さが
0.１ｍｍ未満ではブレード部材としての機能が充分に発
揮されないおそれがあり、また3.０ｍｍより厚くする必
要はなく、3.０ｍｍ以下の厚さでも、ブレード部材とし
ての機能が充分に発揮される。本発明においては、この
積層体からなる板状ブレード部材は、圧縮永久歪（ＪＩ
Ｓ Ｋ６３０１，６０℃，４８時間）が、通常0.１〜２
０％の範囲である。また、その他の物性としては、一般
に硬度（ＪＩＳ Ａ）が６０〜８０、１００％モジュラ
スが２０〜３０ｋｇ／ｃｍ2 、３００％モジュラスが１
００〜２００ｋｇ／ｃｍ2 、伸びが３００％程度、引張
強さ（ＪＩＳ Ｚ２２４１）が２００ｋｇ／ｃｍ2 以上
であるのが好ましい。In the present invention, one kind of the resin may be used, or two or more kinds may be used in combination. In the cleaning blade of the present invention, the laminate used as the plate-shaped blade member is provided with a layer made of these resins on the metal plate, and the thickness of the resin layer is usually 0.1. It is in the range of 1 to 3.0 mm. This thickness
If the thickness is less than 0.1 mm, the function as a blade member may not be sufficiently exhibited, and it is not necessary to make the thickness greater than 3.0 mm. Even with a thickness of 3.0 mm or less, the function as a blade member is sufficiently exhibited. . In the present invention, the plate-shaped blade member made of the laminated body has a compression set (JI
SK6301, 60 ° C, 48 hours) is usually 0.1 to 2
The range is 0%. As other physical properties, hardness (JIS A) is generally 60 to 80, 100% modulus is 20 to 30 kg / cm 2 , and 300% modulus is 1
It is preferable that the hardness is 100 to 200 kg / cm 2 , the elongation is about 300%, and the tensile strength (JIS Z2241) is 200 kg / cm 2 or more.
【０００９】本発明のクリーニングブレードは、前記積
層体からなる板状ブレード部材と支持部材とが一体化さ
れたものであり、図２にその一例の断面図を示す。この
クリーニングブレードは、金属板４上に樹脂層５が設け
られた積層体からなる板状ブレード部材１が、金属板４
を介して支持部材２に接合され一体化された構造を有し
ている。なお、３は画像形成体との接触部分である。前
記板状ブレード部材と一体化させる支持部材としては、
該板状ブレード部材を画像形成体にしっかりと正確に押
し付けなければならないので、剛性が充分高く、寸法精
度の良好なものであればよく、特に制限されず、従来、
電子写真装置における画像形成体用クリーニングブレー
ドにおいて慣用されているものの中から適宜選択して用
いることができる。例えば、鋼板をプレスにより打ち抜
いたものなどが、通常用いられる。The cleaning blade of the present invention is one in which a plate-like blade member made of the above-mentioned laminate and a support member are integrated, and FIG. 2 is a cross-sectional view of one example. The cleaning blade includes a plate-shaped blade member 1 made of a laminate in which a resin layer 5 is provided on a metal plate 4.
And is integrated with the support member 2 via the. Reference numeral 3 denotes a contact portion with the image forming body. As a support member integrated with the plate-like blade member,
Since the plate-shaped blade member must be firmly and accurately pressed against the image forming body, the rigidity is sufficiently high and any one having good dimensional accuracy may be used.
It can be appropriately selected from those commonly used in cleaning blades for image forming bodies in electrophotographic apparatuses. For example, a steel plate punched out by a press is usually used.
【００１０】このような構成の本発明のクリーニングブ
レードは、特に板状ブレード部材の圧縮永久歪が低く、
画像形成体に対して所定の面圧がかかり、クリーニング
性能に優れており、また、金属板として適度のたわみ性
を有するものが用いられているので、画像形成体を傷付
けることも少ない。このクリーニングブレードの製造方
法としては、前記構成を有するクリーニングブレードが
得られる方法であればよく、特に制限はないが、以下に
示す本発明の方法に従えば、効率よく製造することがで
きる。本発明のクリーニングブレードの製造方法は、
（Ａ）積層体を作製する工程、（Ｂ）板状ブレード部材
に加工する工程及び（Ｃ）板状ブレード部材と支持部材
とを一体化させる工程から構成されている。まず、
（Ａ）工程、すなわち、積層体を作製する工程について
説明する。この（Ａ）工程においては、金属板上に前記
樹脂からなる層が形成されるが、樹脂層と金属板との密
着性などを向上させる目的で、樹脂層の形成に先立っ
て、所望により、金属板の表面に脱脂処理や粗面化処理
を施したのち、化成処理を施すことができる。この化成
処理方法としては、従来金属板の塗装において使用され
ている方法でよく、例えばリン酸亜鉛処理、塗布型又は
反応型のクロメート処理などの方法の中から、金属板の
種類に応じて適宜選択して用いることができる。[0010] The cleaning blade of the present invention having such a configuration has a low compression set, particularly of the plate-like blade member,
Since a predetermined surface pressure is applied to the image forming body, the cleaning performance is excellent, and a metal plate having an appropriate flexibility is used, the image forming body is hardly damaged. The method for manufacturing the cleaning blade is not particularly limited as long as the cleaning blade having the above-described configuration can be obtained, and can be efficiently manufactured according to the method of the present invention described below. The manufacturing method of the cleaning blade of the present invention,
It comprises (A) a step of producing a laminate, (B) a step of processing into a plate-like blade member, and (C) a step of integrating the plate-like blade member and the support member. First,
The step (A), that is, the step of manufacturing a laminate will be described. In the step (A), a layer made of the resin is formed on a metal plate. For the purpose of improving the adhesion between the resin layer and the metal plate and the like, prior to the formation of the resin layer, if desired, After subjecting the surface of the metal plate to a degreasing treatment or a roughening treatment, a chemical conversion treatment can be applied. As the chemical conversion treatment method, a method conventionally used in coating of a metal plate may be used.For example, a method of zinc phosphate treatment, a coating type or a reaction type chromate treatment, or the like, appropriately depending on the type of the metal plate. Can be selected and used.
【００１１】このようにして、所望により、表面処理さ
れた金属板の表面に樹脂層を形成させるには、例えば適
当な溶剤を用いて、塗工可能な最適粘度に調整した樹脂
含有塗工液を調製し、これをはけ塗り，吹付塗り，スプ
レー塗り，ローラ塗り、あるいはスクリーン印刷などに
より、金属板の表面に、乾燥膜厚が所望の値になるよう
に塗工したのち、加熱し、乾燥すればよい。なお、上記
塗工液には、本発明の目的が損なわれない範囲で、必要
に応じ各種添加成分、例えば酸化防止剤，熱安定剤，紫
外線吸収剤，光安定剤，難燃剤，難燃助剤，フィラーな
どを添加することができる。このようにして、金属板上
に樹脂層が設けられた積層体が得られる。次に、（Ｂ）
工程において、前記（Ａ）工程で得られた積層体を所定
形状の板状ブレード部材に加工する。この加工方法とし
ては所定形状に加工できる方法であればよく、特に制限
されず、様々な方法を用いることができるが、一般的に
は、ギロティンカッターなどを用いたプレスなどによる
打抜き加工、あるいはノコ盤などによる切断加工などの
加工方法が好ましく用いられる。In order to form a resin layer on the surface of the surface-treated metal plate as required in this manner, for example, a resin-containing coating liquid adjusted to an optimum coatable viscosity using an appropriate solvent is used. Is coated on the surface of a metal plate by brushing, spray coating, spray coating, roller coating, screen printing, or the like so that the dry film thickness becomes a desired value, and then heating, It may be dried. In the above-mentioned coating liquid, various additives such as an antioxidant, a heat stabilizer, an ultraviolet absorber, a light stabilizer, a flame retardant, and a Agents, fillers and the like can be added. Thus, a laminate in which the resin layer is provided on the metal plate is obtained. Next, (B)
In the step, the laminate obtained in the step (A) is processed into a plate-shaped blade member having a predetermined shape. This processing method is not particularly limited as long as it can be processed into a predetermined shape, and various methods can be used. In general, punching by a press using a guillotine cutter or the like, or sawing A processing method such as cutting with a board or the like is preferably used.
【００１２】また、このようにして所定形状に加工した
のち、所望により、エッジ部にヤスリや砥石などによる
研磨加工を施すことができる。このようにして、所定形
状の板状ブレード部材が得られる。最後に、（Ｃ）工程
において、上記（Ｂ）工程で得られた板状ブレード部材
の金属板側を支持部材と対面させ、両者を接合させて前
記図２で示すように一体化させる。この接合方法として
は特に制限はなく、例えばネジ止め，スポット溶接、あ
るいは瞬間接着剤や嫌気性接着剤などの接着剤による方
法などが挙げられるが、これらの方法の中で、リサイク
ルを考えるとネジ止めによる接合方法が有利である。こ
のようにして、本発明のクリーニングブレードを効率よ
く製造することができる。After processing into a predetermined shape in this way, the edge portion can be polished with a file or a grindstone if desired. Thus, a plate-shaped blade member having a predetermined shape is obtained. Finally, in the step (C), the metal plate side of the plate-shaped blade member obtained in the step (B) faces the support member, and the two are joined and integrated as shown in FIG. The joining method is not particularly limited, and examples thereof include a screwing method, a spot welding method, and a method using an adhesive such as an instantaneous adhesive or an anaerobic adhesive. A joining method with a stop is advantageous. Thus, the cleaning blade of the present invention can be manufactured efficiently.
【００１３】[0013]
【実施例】次に、本発明を実施例により、さらに詳しく
説明するが、本発明は、これらの例によってなんら限定
されるものではない。 実施例１ 熱可塑性ウレタン樹脂〔日本ポリウレタン（株）製，商
品名：パラプレン〕１００重量部に対し、溶剤としてメ
チルエチルケトンを２０重量部の割合で配合し、塗工液
を調製した。次に、厚さ0.１ｍｍの板バネ（鋼板）の片
面に、上記塗工液をロールコータにより塗工し、乾燥し
て厚さ0.１ｍｍの熱可塑性ウレタン樹脂層を形成したの
ち、所定形状にプレスにより打抜き、板状ブレード部材
を作製した。この板状ブレード部材の６０℃における圧
縮永久歪を第１表に示す。 比較例１ 実施例１で用いた熱可塑性ウレタン樹脂を射出成形し
て、実施例１で得られた板状ブレード部材と同じ形状の
シートからなる板状ブレード部材を作製した。この板状
ブレード部材の６０℃における圧縮永久歪を第１表に示
す。Next, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples. Example 1 A coating liquid was prepared by mixing 20 parts by weight of methyl ethyl ketone as a solvent with 100 parts by weight of a thermoplastic urethane resin (trade name: Paraprene, manufactured by Nippon Polyurethane Co., Ltd.). Next, the above coating liquid is applied to one side of a leaf spring (steel plate) having a thickness of 0.1 mm by a roll coater and dried to form a thermoplastic urethane resin layer having a thickness of 0.1 mm. The sheet was punched into a shape to produce a plate-shaped blade member. Table 1 shows the permanent compression set of this plate-shaped blade member at 60 ° C. Comparative Example 1 The thermoplastic urethane resin used in Example 1 was injection-molded to produce a plate-shaped blade member made of a sheet having the same shape as the plate-shaped blade member obtained in Example 1. Table 1 shows the permanent compression set of this plate-shaped blade member at 60 ° C.
【００１４】[0014]
【表１】 [Table 1]
【００１５】圧縮永久歪：ＪＩＳ Ｋ６３０１に準拠
し、６０℃にて測定Compression set: Measured at 60 ° C. according to JIS K6301
【００１６】[0016]
【発明の効果】本発明のクリーニングブレードは、その
板状ブレード部材として、金属板上に樹脂層を有する積
層体からなるものを用いたものであって、圧縮永久歪が
極めて小さく、クリーニング性能に優れている。According to the cleaning blade of the present invention, a plate-shaped blade member made of a laminate having a resin layer on a metal plate is used. Are better.
【図１】 従来のクリーニングブレードの一例を示す斜
視図（ａ）及び断面図（ｂ）である。FIG. 1 is a perspective view (a) and a sectional view (b) showing an example of a conventional cleaning blade.
【図２】 本発明のクリーニングブレードの一例を示す
断面図である。FIG. 2 is a sectional view showing an example of the cleaning blade of the present invention.
１：板状ブレード部材 ２：支持部材 ３：画像形成体との接触部分 ４：金属板 ５：樹脂層 1: Plate-like blade member 2: Support member 3: Contact portion with image forming body 4: Metal plate 5: Resin layer
Claims (5)
部材を有し、かつ該板状ブレード部材を画像形成体に当
接させ、その表面に残留するトナーを除去するクリーニ
ングブレードにおいて、前記板状ブレード部材が、金属
板上に樹脂層を設けた積層体であることを特徴とするク
リーニングブレード。1. A cleaning blade having a plate-shaped blade member and a support member for supporting the plate-shaped blade member, wherein the plate-shaped blade member is brought into contact with an image forming body to remove toner remaining on the surface thereof. A cleaning blade, wherein the blade member is a laminate in which a resin layer is provided on a metal plate.
請求項１記載のクリーニングブレード。2. The cleaning blade according to claim 1, wherein the thickness of the metal plate is 0.02 to 0.5 mm.
求項１記載のクリーニングブレード。3. The cleaning blade according to claim 1, wherein the thickness of the resin layer is 0.1 to 3.0 mm.
請求項１又は３記載のクリーニングブレード。4. The cleaning blade according to claim 1, wherein the resin layer is a thermoplastic urethane resin layer.
部材を有し、かつ該板状ブレード部材を画像形成体に当
接させ、その表面に残留するトナーを除去するクリーニ
ングブレードを製造するに当たり、（Ａ）金属板上に樹
脂層を設け積層体を作製する工程、（Ｂ）上記積層体を
所定形状の板状ブレード部材に加工する工程及び（Ｃ）
この板状ブレード部材と支持部材とを一体化させる工程
を順次行うことを特徴とするクリーニングブレードの製
造方法。5. A method for manufacturing a cleaning blade having a plate-like blade member and a supporting member for supporting the plate-like blade member, wherein the plate-like blade member is brought into contact with an image forming body to remove toner remaining on the surface thereof. (A) a step of forming a laminate by providing a resin layer on a metal plate, (B) a step of processing the laminate into a plate-shaped blade member having a predetermined shape, and (C).
A method for manufacturing a cleaning blade, wherein the steps of integrating the plate-shaped blade member and the support member are sequentially performed.