JPH11217910A - Modification structure and method for sheet waterproof structure and multiple layer sheet therefor - Google Patents
Modification structure and method for sheet waterproof structure and multiple layer sheet thereforInfo
- Publication number
- JPH11217910A JPH11217910A JP10226095A JP22609598A JPH11217910A JP H11217910 A JPH11217910 A JP H11217910A JP 10226095 A JP10226095 A JP 10226095A JP 22609598 A JP22609598 A JP 22609598A JP H11217910 A JPH11217910 A JP H11217910A
- Authority
- JP
- Japan
- Prior art keywords
- plasticizer
- sheet
- waterproof sheet
- repair
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、構造物の防水す
べき表面に張設されたシート防水構造物の改修構造及び
改修方法並びに改修用複層シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a repair structure and a repair method for a waterproof sheet structure stretched on a surface of a structure to be waterproofed, and a repair multi-layer sheet.
【０００２】なお、この明細書において、「積層」の語
は、接合状態での積層はもちろん、非接合状態での積層
（単なる積み重ね状の配置）をも含む意味で用いる。[0002] In this specification, the term "lamination" is used to mean not only lamination in a joined state but also lamination in a non-joined state (merely a stacked arrangement).
【０００３】[0003]
【従来の技術】従来より、ビルや家屋等の防水を必要と
する屋外側の躯体表面には、雨水等の侵入を防ぐため
に、合成樹脂からなる防水シートを絶縁工法や密着工法
等のシート防水工法により張設することが一般的に行わ
れている。2. Description of the Related Art Conventionally, a waterproof sheet made of a synthetic resin is applied to a surface of a building or a house, which requires waterproofing, to prevent the intrusion of rainwater or the like by a waterproofing method such as an insulation method or a close contact method. It is common practice to stretch by the construction method.
【０００４】絶縁工法とは、例えば図８及び図９に示す
ように、構造物（１１）の表面に、塩化ビニル樹脂被覆
鋼板からなる円板状の接合片（１２）が開脚釘、カール
プラグ等の固着具（１３）により点在状態に多数固定さ
れ、軟質塩化ビニル樹脂からなる防水シート（１４）
が、構造物（１１）の表面上に張り渡されるようにし
て、接合片（１２）に溶剤や熱により接着されるか、あ
るいは接着剤により接着されるものである。また、密着
工法とは、図１２に示すように、防水すべき構造物（１
１）の表面に、防水シート（１４）が接着剤層（３０）
を介して全面的に接合固定されるものである。As shown in FIGS. 8 and 9, for example, an insulating construction method is a method in which a disc-shaped joining piece (12) made of a vinyl chloride resin-coated steel sheet is formed on a surface of a structure (11) by a nail, a curling leg, or the like. Waterproof sheet (14) made of soft vinyl chloride resin, which is fixed in a large number in a dotted state by fasteners (13) such as plugs
Is bonded to the joining piece (12) by a solvent or heat, or is bonded by an adhesive so as to be stretched over the surface of the structure (11). In addition, as shown in FIG. 12, the contact construction method refers to a structure (1) to be waterproofed.
On the surface of 1), a waterproof sheet (14) is provided with an adhesive layer (30).
And is entirely fixed by bonding.
【０００５】いずれの工法を採用するにせよ、このよう
なシート防水構造物は、長期の使用により劣化すると、
防水シート（１４）の張力バランスが乱れて局部的に伸
び縮みが生じ、防水シート（１４）に剥離や膨れが生じ
て美観を損ねるとともに、場合によっては亀裂が発生し
て漏水する恐れがある。このためシート防水構造物は、
経年劣化すると補修が必要となるが、従来、その補修方
法としては、既設の防水シート（１４）をすべて撤去し
た後、構造物（１）の表面に、新たな防水シートを施工
するという方法が一般に行われている。Regardless of which construction method is adopted, such a waterproof sheet structure deteriorates due to long-term use.
The tension balance of the waterproof sheet (14) is disturbed to cause local expansion and contraction, and the waterproof sheet (14) may be peeled or swelled to impair the aesthetic appearance, and in some cases, cracks may occur to leak water. For this reason, the sheet waterproof structure is
Repairing is required if it deteriorates over time. Conventionally, the repair method is to remove all existing waterproof sheets (14) and then install a new waterproof sheet on the surface of the structure (1). Generally done.
【０００６】[0006]
【発明が解決しようとする課題】しかしながら、上記従
来の改修方法においては、経年劣化した防水シート（１
４）をすべて撤去する必要があり、その撤去作業に多大
な労力を必要とし、作業効率の低下を来して、改修期間
の長期化及びコストの増大を招くという問題が発生す
る。しかも改修期間が長くなると、改修期間中に雨等に
より漏水が生じるという不具合もあった。更に撤去され
た防水シート（１４）は、産業廃棄物として処理する必
要があるので、自然環境保護の面においても不安を抱え
ている。However, in the above conventional repair method, the waterproof sheet (1
It is necessary to remove all of 4), and a great deal of labor is required for the removal work, resulting in a problem that the work efficiency is reduced, and the repair period is prolonged and the cost is increased. In addition, when the repair period is long, there is a problem that water leaks due to rain or the like during the repair period. Furthermore, since the removed waterproof sheet (14) needs to be disposed of as industrial waste, there is anxiety also in terms of protecting the natural environment.
【０００７】一方、上記以外のシート防水構造物の改修
方法として、例えば経年劣化した防水シート（１４）上
に新たな防水シートを、直接、接着剤により接合する工
法も採用されている。この改修方法においては、既設の
防水シート（１４）を撤去する必要がなく、作業効率の
向上等を図ることができる。[0007] On the other hand, as a method of repairing a waterproof sheet structure other than the above, for example, a method of directly bonding a new waterproof sheet to an aged waterproof sheet (14) with an adhesive has been adopted. In this repair method, it is not necessary to remove the existing waterproof sheet (14), and it is possible to improve work efficiency and the like.
【０００８】ところが、既設の防水シート（１４）は、
長期の使用により表面状態が悪化しているため、その劣
悪な表面に新防水シートを接着することは非常に困難で
ある。しかも劣化した既設防水シート（１４）は、剥離
や膨れが存在しているため、その既設防水シート（１
４）に接着する新防水シートにも膨れ等が生じ易く、良
好な美観が得られないという問題があった。更に劣化し
た既設防水シートに新防水シートが接触状態に配置され
るものであるため、新防水シートから既設防水シート
に、可塑剤等の必要成分が移行してしまい、新防水シー
トが早期に劣化して、十分な耐久性が得られないという
問題もあった。However, the existing waterproof sheet (14) is
Since the surface condition has deteriorated due to long-term use, it is very difficult to bond a new waterproof sheet to the poor surface. In addition, since the existing waterproof sheet (14) that has deteriorated has peeling or swelling, the existing waterproof sheet (1)
There is a problem that the new waterproof sheet adhered to 4) is liable to swell and the like, and good aesthetic appearance cannot be obtained. Further, since the new waterproof sheet is placed in contact with the deteriorated existing waterproof sheet, necessary components such as plasticizers are transferred from the new waterproof sheet to the existing waterproof sheet, and the new waterproof sheet deteriorates quickly. Thus, there is a problem that sufficient durability cannot be obtained.
【０００９】また従来において、既設防水シート（１
４）上に新防水シートを絶縁工法により張設する改修方
法、すなわち既設防水シート（１４）上から新たに接合
片を固定し、既設防水シート（１４）上に新防水シート
を張り渡した状態で上記新設の接合片に接着する改修方
法も採用されている。Conventionally, existing waterproof sheets (1)
4) A repair method in which a new waterproof sheet is stretched on the existing waterproof sheet (14), that is, a new joint piece is fixed from the existing waterproof sheet (14), and the new waterproof sheet is stretched over the existing waterproof sheet (14). Therefore, a refurbishment method of bonding to the newly-installed joint piece is also adopted.
【００１０】しかしながらこの改修方法においては、改
修作業完了後に、既設防水シート（１４）が熱等の影響
により、劣化が更に進行すると、既設防水シート（１
４）に縮みや皺が発生して新設の接合片が浮き上がり、
ひいては新防水シートも浮き上がって、良好な美観を維
持できないことが起こりうるという問題が発生する。However, in this repair method, after the repair work is completed, if the existing waterproof sheet (14) further deteriorates due to the influence of heat or the like, the existing waterproof sheet (1) is deteriorated.
4) Shrinkage and wrinkles occur, and the newly-installed joint piece rises,
Eventually, the new waterproof sheet also rises, and a problem arises that a good aesthetic cannot be maintained.
【００１１】更にこの改修方法においては、既設防水シ
ート（１４）に新防水シートが接触状態に配置されるも
のであるため、上記と同様、新防水シートから既設防水
シート（１４）に可塑剤等の必要成分が移行するのを防
止できず、上記した早期劣化の問題を十分に解消できる
ものではない。Further, in this repair method, since the new waterproof sheet is placed in contact with the existing waterproof sheet (14), the plastic sheet or the like is transferred from the new waterproof sheet to the existing waterproof sheet (14) in the same manner as described above. Cannot be prevented from shifting, and the above-mentioned problem of early deterioration cannot be sufficiently solved.
【００１２】この発明は、上記従来技術の問題を解消
し、効率良く確実に改修することができて、改修期間の
短縮及びコストの削減を図ることができ、改修期間中に
降雨があっても漏水を生じることが全くなく、かつ産業
廃棄物を発生させることがなく、更に改修された構造物
において、良好な美観を長期維持できるとともに、早期
劣化を防止できて十分な耐久性を得ることができるシー
ト防水構造物の改修構造及び改修方法並びにこのような
改修を行うための改修用複層シートを提供することを目
的とする。[0012] The present invention solves the above-mentioned problems of the prior art, enables efficient and reliable repair, shortens the repair period and reduces costs, and prevents rainfall during the repair period. With no water leakage and no generation of industrial waste, the renovated structure can maintain good aesthetics for a long period of time, prevent early deterioration and obtain sufficient durability. It is an object of the present invention to provide a repair structure and a repair method for a waterproof sheet structure, and a repair multilayer sheet for performing such repair.
【００１３】[0013]
【課題を解決するための手段】上記目的を達成するた
め、この発明に係るシート防水構造物の改修構造は、構
造物の防水すべき表面に絶縁工法や密着工法等により敷
設された既設防水シートにより防水施工されたシート防
水構造物の改修構造であって、前記既設防水シート表面
の一部ないし全面に、可塑剤を多量に含有した塩化ビニ
ル系樹脂組成物からなる可塑剤供給層が積層され、該可
塑剤供給層が積層された既設防水シート上に改修用防水
シートが積層されると共に、改修用接合片が前記既設防
水シートと改修用防水シートとの間に又は改修用防水シ
ートの上に配置された状態で前記構造物に固定され、か
つこの改修用接合片に前記改修用防水シートの一部が接
合されていることを特徴とするものである。In order to achieve the above object, a modified structure of a waterproof sheet structure according to the present invention comprises an existing waterproof sheet laid on the surface of the structure to be waterproof by an insulation method or a close contact method. A modified structure of a sheet waterproof structure subjected to waterproofing, wherein a plasticizer supply layer made of a vinyl chloride resin composition containing a large amount of a plasticizer is laminated on a part or the entire surface of the existing waterproof sheet. The renovation waterproof sheet is laminated on the existing waterproof sheet on which the plasticizer supply layer is laminated, and the renovation joint piece is located between the existing waterproof sheet and the renovation waterproof sheet or on the renovation waterproof sheet. And a part of the repairing waterproof sheet is joined to the repairing joint piece.
【００１４】また、この発明に係るシート防水構造物の
改修方法は、構造物の防水すべき表面に絶縁工法や密着
工法等により敷設された既設防水シートにより防水施工
されたシート防水構造物の改修方法であって、前記既設
防水シート表面の一部ないし全面に、可塑剤を多量に含
有した塩化ビニル系樹脂組成物からなる可塑剤供給層を
密着状態に被覆形成する工程と、前記可塑剤供給層が形
成された既設防水シート上に可塑剤移行防止シートを敷
設する工程と、前記可塑剤移行防止シート上に改修用接
合片を配置し前記構造物に固定する工程と、改修用防水
シートを前記可塑剤移行防止シート上に張り渡して前記
改修用接合片に接着する工程とを含むことを特徴とする
ものである。A method for repairing a waterproof sheet structure according to the present invention is a method for repairing a waterproof sheet structure which is waterproofed by an existing waterproof sheet laid on a surface to be waterproofed of the structure by an insulation method or a close contact method. A step of: forming a plasticizer supply layer made of a vinyl chloride resin composition containing a large amount of a plasticizer on a part or the entire surface of the existing waterproof sheet in an intimate contact state; A step of laying a plasticizer migration prevention sheet on the existing waterproof sheet on which the layer is formed, a step of arranging a repairing joint piece on the plasticizer migration prevention sheet and fixing it to the structure, and a repair waterproofing sheet. Stretching over the plasticizer transfer prevention sheet and adhering to the repairing joint piece.
【００１５】上記改修構造及び改修方法によれば、経年
劣化した既設防水シートをすべて撤去するというような
負担の大きい作業を行わなくとも良い。また、経年劣化
した既設防水シートの表面を被覆するのみであり、該既
設防水シートをすべて撤去したり、あるいは部分的に撤
去するような工程等がないから、改修期間中の雨により
漏水することが全くない。更に既設防水シートは新規の
改修用防水シートの下側に配置されるものであるため、
劣化した既設防水シートを廃棄することは全くなく、従
って廃棄物が発生することはない。According to the above-described repair structure and repair method, it is not necessary to perform a heavy work such as removing all the existing waterproof sheets that have deteriorated over time. In addition, since it only covers the surface of the existing waterproof sheet that has deteriorated over time, there is no step to remove or remove the existing waterproof sheet entirely, so water leakage due to rain during the renovation period There is no. In addition, the existing tarpaulin is located below the new renovation tarpaulin,
There is no disposal of the deteriorated existing tarpaulin, and no waste is generated.
【００１６】また新たな改修用防水シートを、新設の改
修用接合片を介して構造物に取り付けるものであるた
め、劣化防水シートがどのような表面状態にあろうと
も、新防水シートを支障なく取り付けることができ、し
かも劣化防水シートの表面に被覆形成された可塑剤供給
層から劣化防水シートに徐々に可塑剤が供給され、該劣
化防水シート中に欠乏していた可塑剤が補充されて、劣
化防水シートの物性、特に柔軟性が回復するとともに張
力が取り除かれるから、劣化防水シートの張力に起因す
る悪影響が新防水シートに及ぶことはない。In addition, since a new waterproof sheet for repair is attached to a structure via a newly installed joint piece for repair, the new waterproof sheet can be used regardless of the surface condition of the deteriorated waterproof sheet. A plasticizer can be attached to the deteriorated waterproof sheet, and a plasticizer is gradually supplied to the deteriorated waterproof sheet from a plasticizer supply layer formed on the surface of the deteriorated waterproof sheet, and the plasticizer lacking in the deteriorated waterproof sheet is replenished. Since the physical properties of the deteriorated waterproof sheet, particularly the flexibility, are restored and the tension is removed, the adverse effect due to the tension of the deteriorated waterproof sheet does not affect the new waterproof sheet.
【００１７】上記において、改修用接合片は、可塑剤供
給層が形成された領域に対応する上部位置に配置される
のが望ましく、これにより既設防水シートにおける改修
用接合片を支持する領域に確実にかつ早期に可塑剤が供
給されるから、劣化防水シートの張力による悪影響が改
修用接合片にまで及ぶことが確実に防止されて改修用接
合片の浮き上がりが確実に防止される。In the above, it is desirable that the repairing joint piece is disposed at an upper position corresponding to the area where the plasticizer supply layer is formed, and thereby the area for supporting the repairing joint piece in the existing waterproof sheet is surely provided. Since the plasticizer is supplied quickly and at an early stage, the adverse effect due to the tension of the deteriorated waterproof sheet is reliably prevented from reaching the repairing joint piece, and the repairing joint piece is reliably prevented from rising.
【００１８】また、上記改修構造において、可塑剤供給
層が積層された既設防水シートと改修用防水シートとの
間に可塑剤移行防止層が積層されているのが望ましく、
この場合には改修用防水シートから劣化既設防水シート
側に可塑剤等の必要成分が移行するのを確実に防止する
ことができる。In the above-mentioned renovation structure, it is preferable that a plasticizer migration prevention layer is laminated between the existing waterproof sheet on which the plasticizer supply layer is laminated and the renovation waterproof sheet.
In this case, it is possible to reliably prevent a necessary component such as a plasticizer from being transferred from the renovation waterproof sheet to the deteriorated existing waterproof sheet.
【００１９】また、この発明の改修用複層シートは、可
塑剤移行防止層、可塑剤供給層が予め積層一体化された
ものであるから、上記改修構造を形成するに際しその構
成材として用いれば、改修を容易に行うことができ、施
工時間、施工労力ともに少なくて済み、改修の施工性を
向上させることができる。Further, since the repairing multi-layer sheet of the present invention has a plasticizer transfer prevention layer and a plasticizer supply layer previously laminated and integrated, it can be used as a constituent material when forming the repaired structure. In addition, the renovation can be easily performed, and the construction time and labor can be reduced, and the renovation workability can be improved.
【００２０】また、この発明の別の改修用複層シート
は、防水層、可塑剤移行防止層、可塑剤供給層が予め積
層一体化されたものであり、この複層防水シートを経年
劣化した既設防水シート上に、可塑剤供給層から既設防
水シートへ可塑剤が供給可能となる態様で敷設施工する
だけで改修施工が完了するから、改修が容易であり、施
工時間、施工労力ともに少なくて済み、施工性に極めて
優れている。そして、可塑剤供給層から劣化既設防水シ
ートに徐々に可塑剤が供給され、該劣化防水シート中に
欠乏していた可塑剤が補充されて、劣化既設防水シート
の物性、特に柔軟性が回復するとともに張力が取り除か
れるから、劣化既設防水シートの張力に起因する悪影響
がこの改修用複層シートに及ぶことはない。また防水層
と可塑剤供給層の間に可塑剤移行防止層が介装されてい
るから、この複層シートの防水層から劣化既設防水シー
ト側に可塑剤等の必要成分が移行するのを確実に防止す
ることができる。Another modified multi-layer sheet of the present invention is one in which a waterproof layer, a plasticizer migration preventing layer, and a plasticizer supply layer are previously laminated and integrated, and this multi-layer waterproof sheet has been deteriorated over time. On the existing waterproof sheet, the repair work is completed only by laying and constructing in such a manner that the plasticizer can be supplied from the plasticizer supply layer to the existing waterproof sheet, so the repair is easy, the construction time and the construction labor are small. It is extremely excellent in workability. Then, the plasticizer is gradually supplied from the plasticizer supply layer to the deteriorated existing waterproof sheet, and the plasticizer lacking in the deteriorated waterproof sheet is replenished, and the physical properties of the deteriorated existing waterproof sheet, particularly the flexibility, are restored. At the same time, the tension is removed, so that adverse effects caused by the tension of the deteriorated existing waterproof sheet do not affect the repair multi-layer sheet. In addition, since a plasticizer migration prevention layer is interposed between the waterproof layer and the plasticizer supply layer, it is ensured that necessary components such as plasticizer migrate from the waterproof layer of the multilayer sheet to the deteriorated existing waterproof sheet side. Can be prevented.
【００２１】[0021]
【発明の実施の形態】以下、この発明に係るシート防水
構造物の改修構造の一実施形態を図面を参照しつつ説明
する。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is an exploded perspective view showing a modified structure of a waterproof sheet structure according to the present invention.
【００２２】本実施形態が適用されたシート防水構造物
は、絶縁工法により防水施工されたものである。すなわ
ち図８及び図９に示すように、ビルディング等の構造物
（１１）における陸屋根のような防水すべき表面に、部
分的に、多数の円板状の第１接合片（１２）が、開脚
釘、カールプラグ等の機械的固着手段からなる第１固着
具（１３）を用いて構造物（１１）の躯体に固定される
と共に、防水シート（以下、「既設防水シート」とい
う）（１４）が、構造物表面上に張り渡された状態で、
各第１接合片（１２）に接着剤により接着されて、シー
ト防水構造物が形成されている。The waterproof sheet structure to which this embodiment is applied is waterproofed by an insulation method. That is, as shown in FIGS. 8 and 9, a large number of disc-shaped first joint pieces (12) are partially opened on a surface to be waterproofed such as a flat roof of a structure (11) such as a building. It is fixed to the frame of the structure (11) using a first fixing tool (13) comprising mechanical fixing means such as a leg nail, a curl plug, and a waterproof sheet (hereinafter referred to as an "existing waterproof sheet") (14). ) Is stretched over the structure surface,
Each of the first joint pieces (12) is bonded with an adhesive to form a waterproof sheet structure.
【００２３】そしてこのようなシート防水構造物におい
て、長期使用により既設防水シート（１４）が劣化した
際等に、この発明に係る改修構造が適用される。In such a waterproof sheet structure, the renovation structure according to the present invention is applied when the existing waterproof sheet (14) is deteriorated due to long-term use.
【００２４】本実施形態の改修構造においては、前記既
設防水シート（１４）表面の一部または全面に、可塑剤
を多量に含有した塩化ビニル系樹脂組成物からなる可塑
剤供給層（１５）が被覆形成されている。In the modified structure of this embodiment, a plasticizer supply layer (15) made of a vinyl chloride resin composition containing a large amount of a plasticizer is provided on a part or the entire surface of the existing waterproof sheet (14). The coating is formed.
【００２５】この可塑剤供給層（１５）は、図７に示す
ように既設防水シート（１４）表面の全面に被覆形成さ
れるのが望ましいが、作業効率の一層の向上および材料
コストの低減等の観点から部分的に被覆形成される場合
には、既設防水シート（１４）表面のうち、後述する改
修用接合片が固定される領域に対応する位置に、少なく
とも被覆形成されるのが望ましい。既設防水シート（１
４）における、改修用接合片が配置される領域に対応す
る位置に確実に可塑剤が供給されるから、劣化防水シー
ト（１４）の張力に起因する悪影響が改修用接合片（２
２）にまで及ぶようなことはなく、改修用接合片（２
２）の浮き上がりを確実に防止することができ、ひいて
は良好な美観を長期維持することができる。本実施形態
においては、図１に示すように後述する改修用接合片
（２２）が固定される領域である第１接合片（１２）間
の所定領域に可塑剤供給層（１５）が形成されている。The plasticizer supply layer (15) is desirably formed so as to cover the entire surface of the existing waterproof sheet (14) as shown in FIG. 7. However, the work efficiency is further improved and the material cost is reduced. In the case where the coating is partially formed from the viewpoint of the above, it is desirable that the coating is formed at least at a position corresponding to a region where a repairing joint piece to be described later is fixed on the surface of the existing waterproof sheet (14). Existing tarpaulin (1
Since the plasticizer is reliably supplied to the position corresponding to the area where the repairing joint piece is disposed in 4), the adverse effect due to the tension of the deteriorated waterproof sheet (14) is adversely affected.
It does not extend to 2), and the repair joint (2
The lifting of 2) can be reliably prevented, and a good appearance can be maintained for a long time. In the present embodiment, as shown in FIG. 1, a plasticizer supply layer (15) is formed in a predetermined region between the first bonding pieces (12), which is a region where a repair bonding piece (22) described later is fixed. ing.
【００２６】そして、前記可塑剤供給層（１５）が形成
された既設防水シート（１４）上に、可塑剤移行防止シ
ート（１６）が敷設されると共に、この可塑剤移行防止
シート（１６）上に改修用防水シート（２４）が敷設さ
れている。更に、前記可塑剤移行防止シート（１６）と
改修用防水シート（２４）との間に改修用接合片（２
２）が配置され、この改修用接合片（２２）が前記構造
物（２２）に固定されている。即ち、可塑剤移行防止シ
ート（１６）上における前記可塑剤供給層（１５）が形
成された領域上に改修用接合片（２２）が配置されて、
その接合片（２２）及び可塑剤移行防止シート（１６）
に、開脚釘、カールプラグ等の機械的固着手段からなる
第２固着具（２３）が貫通して、構造物（１１）の躯体
に固定されることによって、改修用接合片（２２）が可
塑剤移行防止シート（１６）上に固定されるようになさ
れている。そして、改修用接合片（２２）の上面と改修
用防水シート（２４）が接着されることにより、改修用
防水シート（２４）が前記構造物（１１）に対して固定
されるものとなされている。A plasticizer migration preventing sheet (16) is laid on the existing waterproof sheet (14) on which the plasticizer supply layer (15) is formed, and the plasticizer migration preventing sheet (16) A waterproofing sheet (24) for repair is laid. Further, a repair joint piece (2) is provided between the plasticizer transfer prevention sheet (16) and the repair waterproof sheet (24).
2) is arranged, and the repairing joint piece (22) is fixed to the structure (22). That is, the repairing joint piece (22) is disposed on the area where the plasticizer supply layer (15) is formed on the plasticizer transfer prevention sheet (16),
The joint piece (22) and the plasticizer transfer prevention sheet (16)
Then, a second fixing tool (23) formed of a mechanical fixing means such as an open nail or a curl plug penetrates and is fixed to the frame of the structure (11), so that the repairing joint piece (22) is formed. It is adapted to be fixed on a plasticizer transfer prevention sheet (16). Then, the renovation waterproof sheet (24) is fixed to the structure (11) by bonding the upper surface of the renovation joint piece (22) and the renovation waterproof sheet (24). I have.
【００２７】この発明において、可塑剤供給層（１５）
を構成する塩化ビニル系樹脂組成物のうち、塩化ビニル
系樹脂は、特に限定されるものではないが、例えば塩化
ビニルの単独重合体のほか、塩化ビニルと、酢酸ビニ
ル、エチレン、プロピレン等との二元または三元以上の
共重合体等を好適に使用でき、また２種以上併用したも
のも支障なく使用することができる。In the present invention, the plasticizer supply layer (15)
Among the vinyl chloride-based resin compositions constituting the above, the vinyl chloride-based resin is not particularly limited, for example, other than a homopolymer of vinyl chloride, and vinyl chloride, vinyl acetate, ethylene, propylene and the like Binary or ternary or higher copolymers and the like can be suitably used, and two or more of them can be used without any problem.
【００２８】また、可塑剤供給層（１５）を構成する塩
化ビニル系樹脂組成物は、塩化ビニル系樹脂１００重量
部（固形分）に対し、可塑剤を５０〜３００重量部含む
ものとするのが好ましい。可塑剤量が５０重量部未満で
は、既設劣化防水シートへの可塑剤の十分な移行量を確
保することができず、ひいては当該劣化防水シートの柔
軟性の回復を十分に図れなくなるので好ましくない。一
方、可塑剤量が３００重量部を超えると、劣化防水シー
トの表面が著しく膨潤し、表面状態が悪化するととも
に、防水層の機械的強度が損なわれやすくなるので、好
ましくない。最も好ましい可塑剤の含有量は、塩化ビニ
ル系樹脂１００重量部に対し、１５０〜２５０重量部で
ある。The vinyl chloride resin composition constituting the plasticizer supply layer (15) preferably contains 50 to 300 parts by weight of a plasticizer with respect to 100 parts by weight (solid content) of the vinyl chloride resin. . If the amount of the plasticizer is less than 50 parts by weight, it is not possible to secure a sufficient amount of the plasticizer transferred to the existing deteriorated waterproof sheet, and it is not possible to sufficiently recover the flexibility of the deteriorated waterproof sheet. On the other hand, when the amount of the plasticizer exceeds 300 parts by weight, the surface of the deteriorated waterproof sheet is significantly swollen, the surface condition is deteriorated, and the mechanical strength of the waterproof layer is easily deteriorated. The most preferable content of the plasticizer is 150 to 250 parts by weight based on 100 parts by weight of the vinyl chloride resin.
【００２９】ここに使用する可塑剤の種類は、特に限定
されるものではなく、最も汎用的なＤＢＰ、ＤＨＰ、Ｄ
ＯＰ、ＤＩＯＰ、ＤＩＤＰ等のフタル酸エステル類、Ｄ
ＯＡ、ＤＯＺ、ＤＯＳ等の直鎖二塩基酸エステル類、Ｔ
ＣＰに代表されるリン酸エステル類等を任意に選択使用
することができる。The type of the plasticizer used here is not particularly limited, and the most general-purpose DBP, DHP, D
Phthalates such as OP, DIOP, and DIDP, D
Linear dibasic acid esters such as OA, DOZ, and DOS;
Phosphate esters represented by CP and the like can be arbitrarily selected and used.
【００３０】上記塩化ビニル系樹脂組成物には、上記成
分の他に酸化チタン、クレー、シリカ、炭酸カルシウム
等の充填剤、金属石鹸系、塩基性鉛系等の安定剤、着色
剤、難燃剤、繊維強化剤、改質剤等の添加剤を適宜配合
しても良い。In addition to the above-mentioned components, the above-mentioned vinyl chloride resin composition contains fillers such as titanium oxide, clay, silica and calcium carbonate, stabilizers such as metal soaps and basic lead, coloring agents and flame retardants. Further, additives such as a fiber reinforcing agent and a modifying agent may be appropriately compounded.
【００３１】本発明において、可塑剤移行防止シート
（１６）としては、後述の改修用防水シートから既設防
水シート（１４）へ可塑剤等の必要成分の移行を防止で
きるもの、具体的にはポリエチレン樹脂、ポリプロピレ
ン樹脂等のポリオレフィン系樹脂、ポリエステル樹脂な
どからなるものを好適に使用することができる。また可
塑剤移行防止シート（１６）は、そのシート上から前記
可塑剤供給層（１５）が形成された領域を容易に判別で
きるように、透明又は半透明のものを使用するのが良
い。In the present invention, as the plasticizer migration preventing sheet (16), a sheet capable of preventing migration of necessary components such as a plasticizer from a renovation waterproof sheet (described later) to an existing waterproof sheet (14), specifically polyethylene. Resins, polyolefin resins such as polypropylene resins, polyester resins, and the like can be suitably used. The plasticizer transfer preventing sheet (16) is preferably a transparent or translucent one so that the region where the plasticizer supply layer (15) is formed can be easily identified from the sheet.
【００３２】また、改修用防水シート（２４）として
は、軟質ポリ塩化ビニル樹脂、ポリエチレン樹脂、ポリ
プロピレン樹脂等の熱可塑性樹脂シートからなるものの
他、非加硫ゴム系シート、ゴムアスファルト系シート等
を好適に使用でき、中でも特に、軟質ポリ塩化ビニル樹
脂シートからなるものは、優れた接着性が得られるた
め、より一層、好適に使用することができる。更に防水
シート（１４）（２４）は厚みが１．０〜２．５ｍｍの
ものを使用するのが一般的である。The renovation waterproofing sheet (24) may be made of a thermoplastic resin sheet such as a soft polyvinyl chloride resin, a polyethylene resin or a polypropylene resin, or a non-vulcanized rubber sheet or a rubber asphalt sheet. It can be suitably used, and especially, those made of a soft polyvinyl chloride resin sheet can be more preferably used because excellent adhesiveness is obtained. Further, the waterproof sheets (14) and (24) generally have a thickness of 1.0 to 2.5 mm.
【００３３】この発明において、改修用接合片（２２）
としては、上記第１接合片（１２）と同様で、硬質、ま
たは半硬質の合成樹脂板、金属板、あるいは防水シート
との接着性を向上させるために塩化ビニル樹脂が片面も
しくは両面に被覆された鋼板（塩ビ鋼板）等の板材から
なる円板状のものを好適に使用することができる。また
本発明においては、接合片（２２）と固着具（２３）と
が一体に形成されたものを使用しても良い。In the present invention, the repairing joint piece (22)
As in the case of the first joining piece (12), a vinyl chloride resin is coated on one or both sides to improve the adhesion to a hard or semi-hard synthetic resin plate, a metal plate, or a waterproof sheet. A disk-shaped plate made of a plate material such as a steel plate (PVC steel plate) can be suitably used. Further, in the present invention, the one in which the joining piece (22) and the fixing tool (23) are integrally formed may be used.
【００３４】また改修用防水シート（２４）を改修用接
合片（２２）に接着するための接着剤としては、既設防
水シート（１４）を第１接合片（１２）に接着するため
の接着剤と同様で、例えばエポキシ系、ウレタン系、ゴ
ム系接着剤等を好適に使用することができる。特に防水
シート（２４）と、接合片（２２）の接合面とが塩化ビ
ニル樹脂からなる場合には、テトラヒドロフラン（ＴＨ
Ｆ）単独、あるいはＴＨＦに塩化ビニル樹脂を溶解した
溶剤型接着剤を使用するのが望ましく、その使用によ
り、耐久性に優れた接着効果を得ることができる。The adhesive for bonding the waterproof sheet for repair (24) to the joint piece (22) for repair is an adhesive for bonding the existing waterproof sheet (14) to the first joint piece (12). Similarly to the above, for example, an epoxy-based, urethane-based, rubber-based adhesive, or the like can be suitably used. Particularly, when the waterproof sheet (24) and the joining surface of the joining piece (22) are made of a vinyl chloride resin, tetrahydrofuran (TH
F) It is desirable to use a solvent-type adhesive alone or a solvent obtained by dissolving a vinyl chloride resin in THF, and by using this, an adhesive effect with excellent durability can be obtained.
【００３５】上記のような改修構造によれば、劣化防水
シート（１４）をすべて撤去したり、あるいは一部撤去
する必要がないから、改修期間中の雨により漏水するこ
とが全くない。また、劣化既設防水シート（１４）を廃
棄することは全くなく、産業廃棄物の発生がないので、
環境保全にも貢献することができる。According to the above-mentioned repair structure, it is not necessary to remove all or a part of the deteriorated waterproof sheet (14), so that there is no water leakage due to rain during the repair period. Also, since the deteriorated existing waterproof sheet (14) is never discarded and no industrial waste is generated,
It can also contribute to environmental conservation.
【００３６】また、新たな改修用防水シート（２４）
を、新設の改修用接合片（２２）を介して構造物（１
１）に取り付けるものであるため、劣化防水シート（１
４）がどのような表面状態にあろうとも、新たな改修用
防水シート（２４）に悪影響が及ぶことがなく、新たな
改修用防水シート（２４）を確実に取り付けることがで
きるとともに、新たな改修用防水シート（２４）に部分
的に剥離や膨れが生じるようなことがなく、良好な美観
を得ることができる。A new renovation waterproofing sheet (24)
To the structure (1) via the newly installed repair piece (22).
Because it is attached to 1), the deteriorated waterproof sheet (1
Regardless of the surface condition of 4), the new waterproofing sheet (24) is not adversely affected, the new waterproofing sheet (24) can be securely attached, and the new waterproofing sheet (24) can be securely attached. A good aesthetic appearance can be obtained without partial peeling or swelling of the waterproofing sheet for repair (24).
【００３７】また、劣化防水シート（１４）の表面に被
覆形成された可塑剤供給層（１５）から、可塑剤が欠乏
している劣化防水シートに徐々に可塑剤が供給されて、
劣化防水シートの物性、特に柔軟性が回復するとともに
張力が取り除かれるから、劣化防水シート（１４）上に
張設される新たな改修用防水シート（２４）が、劣化防
水シート（１４）の張力に起因する悪影響を受けること
がなく、この点からも新たな改修用防水シート（２４）
に剥離や膨れが生じるのを防止でき、より一層、良好な
美観を得ることができる。The plasticizer is gradually supplied from the plasticizer supply layer (15) coated on the surface of the deteriorated waterproof sheet (14) to the deteriorated waterproof sheet lacking the plasticizer.
Since the physical properties of the deteriorated waterproof sheet, in particular, the flexibility are restored and the tension is removed, the new waterproofing sheet (24) stretched over the deteriorated waterproof sheet (14) is not changed in tension. The renovation tarpaulin (24) does not suffer from the adverse effects of
This can prevent exfoliation and swelling from occurring, and can provide a better aesthetic appearance.
【００３８】更に、劣化防水シート（１４）と改修用防
水シート（２４）との間に可塑剤移行防止シート（１
６）が介装された構成であるので、改修用防水シート
（２４）から劣化防水シート（１４）側に可塑剤等の必
要成分が移行するのを確実に防止して、改修用防水シー
ト（２４）の劣化を抑えることができ、十分な耐久性を
得ることができる。Further, a plasticizer migration preventing sheet (1) is provided between the deteriorated waterproof sheet (14) and the repair waterproof sheet (24).
6), the necessary components such as the plasticizer are reliably prevented from migrating from the waterproofing sheet for repair (24) to the deteriorated waterproofing sheet (14), and the waterproofing sheet for repair ( 24) can be suppressed, and sufficient durability can be obtained.
【００３９】また、本実施形態においては、改修用接合
片（２２）が、可塑剤移行防止シート（１６）上におけ
る可塑剤供給層が形成された領域に対応する位置に配置
されるから、劣化防水シート（１４）における改修用接
合片（２２）を支持する領域に確実にかつ早期に可塑剤
が供給されて、劣化防水シートの張力による悪影響が改
修用接合片（２２）にまで及ぶようなことが確実に防止
され、改修用接合片（２２）の浮き上がり、すなわち新
たな改修用防水シート（２４）の浮き上がりを確実に防
止することができ、良好な美観を長期維持することがで
きる。Further, in this embodiment, since the repairing joint piece (22) is disposed at a position corresponding to the area where the plasticizer supply layer is formed on the plasticizer migration preventing sheet (16), deterioration occurs. The plasticizer is reliably and early supplied to the area of the waterproof sheet (14) that supports the repair joint piece (22), so that the adverse effect of the tension of the deteriorated waterproof sheet reaches the repair joint piece (22). Therefore, it is possible to reliably prevent the repairing joint piece (22) from lifting, that is, a new repairing waterproof sheet (24), and to maintain a good appearance for a long time.
【００４０】なお、本実施形態においては、既設防水シ
ート（１４）上に可塑剤供給層（１５）が接合状態で積
層されているが、非接合状態で積層される態様であって
も良い。即ち、単に既設防水シート（１４）上に接触状
態に敷設された態様であっても良い。In the present embodiment, the plasticizer supply layer (15) is laminated on the existing waterproof sheet (14) in a joined state, but may be laminated in a non-joined state. That is, a mode in which it is simply laid in contact with the existing waterproof sheet (14) may be used.
【００４１】また、本実施形態においては、可塑剤供給
層（１５）上に可塑剤移行防止シート（１６）が非接合
状態で積層されているが、接合状態で積層される態様で
あっても良い。即ち、可塑剤供給層（１５）と可塑剤移
行防止シート（１６）が一体化された態様でも良い。こ
のような一体化された構成は、具体的には、例えば図１
０に示すような可塑剤供給層（５２）と可塑剤移行防止
層（５３）とが積層一体化されてなる改修用複層シート
（５１）を敷設することにより得ることができ、このよ
うな改修用複層シート（５１）を用いて改修施工する場
合には、改修を容易に行うことができ、施工時間、施工
労力ともに少なくて済み、改修の施工性を向上させるこ
とができる利点がある。In the present embodiment, the plasticizer transfer preventing sheet (16) is laminated on the plasticizer supply layer (15) in a non-joined state. good. That is, the plasticizer supply layer (15) and the plasticizer transfer prevention sheet (16) may be integrated. Such an integrated configuration is specifically described in, for example, FIG.
0 and a plasticizer supply layer (52) and a plasticizer transfer prevention layer (53) as shown in FIG. When the renovation is performed using the multi-layered sheet for renovation (51), the renovation can be easily performed, the construction time and the construction labor can be reduced, and the renovation workability can be improved. .
【００４２】更に、本実施形態においては、可塑剤移行
防止シート（１６）上に改修用防水シート（２４）が非
接合状態で積層されているが、接合状態で積層される態
様であっても良い。即ち、例えば可塑剤移行防止シート
（１６）と改修用防水シート（２４）が一体化された態
様でも良い。Further, in the present embodiment, the repairing waterproof sheet (24) is laminated on the plasticizer migration preventing sheet (16) in a non-joined state. good. That is, for example, a mode in which the plasticizer transfer prevention sheet (16) and the waterproofing sheet for repair (24) are integrated may be used.
【００４３】また、本実施形態においては、可塑剤供給
層（１５）が積層された既設防水シート（１４）上の全
面に、可塑剤移行防止層が積層されているが、このよう
な可塑剤移行防止層は部分的に積層される構成であって
も良い。なお、部分的に積層される場合には、少なくと
も可塑剤供給層（１５）の上には可塑剤移行防止層が設
けられるのが望ましい。In this embodiment, the plasticizer migration preventing layer is laminated on the entire surface of the existing waterproof sheet (14) on which the plasticizer supply layer (15) is laminated. The migration prevention layer may be configured to be partially laminated. In the case of partial lamination, it is desirable to provide a plasticizer transfer prevention layer at least on the plasticizer supply layer (15).
【００４４】また、本実施形態においては、改修用接合
片（２２）が既設防水シート（１４）と改修用防水シー
ト（２４）との間に配置されて構造物（１１）駆体に固
定されているが、改修用防水シート（２４）の上に配置
された状態で構造物（１１）駆体に固定される構成であ
っても良い。また、改修用接合片（２２）と改修用防水
シート（２４）の接合は、接着剤により行われている
が、特にこれに限定されるものではなく、例えば改修用
接合片（２２）が改修用防水シート（２４）の上に配置
された状態で構造物（１１）駆体に固定される場合にお
いて、該接合片（２２）上面より幾分大きい樹脂シート
（好ましくは改修用防水シートと同材料からなるもの）
で該接合片（２２）上面を覆うと共に、その樹脂シート
の周縁部を改修用防水シート（２４）上面に接着するこ
とにより両者（２２）（２４）の接合を行うものであっ
ても良い。In this embodiment, the repairing joint piece (22) is disposed between the existing waterproof sheet (14) and the repairing waterproof sheet (24), and is fixed to the structure (11) body. However, the structure may be such that it is fixed to the vehicle of the structure (11) while being placed on the renovation waterproof sheet (24). Further, the joining of the repairing joint piece (22) and the repairing waterproof sheet (24) is performed by an adhesive, but is not particularly limited thereto. For example, the repairing jointing piece (22) is repaired. When it is fixed to the structure (11) vehicle while being placed on the waterproof sheet (24), a resin sheet slightly larger than the upper surface of the joint piece (22) (preferably the same as the renovation waterproof sheet) is used. Made of material)
In addition, the upper surface of the joining piece (22) may be covered, and the periphery of the resin sheet may be adhered to the upper surface of the waterproofing sheet for repair (24) to join the two (22) and (24).
【００４５】なお、本実施形態の改修構造は、絶縁工法
により防水施工されたシート防水構造物に適用されたも
のであるが、特にこのような工法のものに限定されるも
のではなく、例えば密着工法等のその他の工法により防
水施工されたシート防水構造物にも適用することができ
るものである。The modified structure according to the present embodiment is applied to a waterproof sheet structure which is waterproofed by an insulating method, but is not particularly limited to such a method. The present invention can also be applied to a sheet waterproof structure waterproofed by another method such as a method of construction.
【００４６】上記のような改修構造は、例えば次に示す
ような改修方法によって施工することができる。The above-mentioned repair structure can be constructed by the following repair method, for example.
【００４７】即ち、まず経年劣化した既設防水シート
（１４）の表面を必要に応じて簡単に清浄し、表面に付
着した砂などの異物を取り除く。That is, first, the surface of the existing waterproof sheet (14) that has deteriorated over time is easily cleaned as necessary to remove foreign substances such as sand adhering to the surface.
【００４８】次に、図１及び図５（ａ）に示すように、
既設防水シート（１４）表面の一部または全面に、可塑
剤を多量に含有した塩化ビニル系樹脂組成物からなる可
塑剤供給層（１５）を密着状態に被覆形成する。Next, as shown in FIG. 1 and FIG.
A plasticizer supply layer (15) made of a vinyl chloride resin composition containing a large amount of a plasticizer is formed on a part or the entire surface of the existing waterproof sheet (14) in a tightly adhered state.
【００４９】次に図２及び図５（ｂ）に示すように、前
記可塑剤供給層（１５）が形成された既設防水シート
（１４）を上方から被覆するようにして、可塑剤移行防
止シート（１６）を敷設する。Next, as shown in FIGS. 2 and 5 (b), the existing waterproof sheet (14) on which the plasticizer supply layer (15) is formed is covered from above, so that the plasticizer transfer prevention sheet is covered. Lay (16).
【００５０】次いで、図３及び図６（ａ）に示すよう
に、可塑剤移行防止シート（１６）上に、改修用接合片
（２２）を固定する。即ち可塑剤移行防止シート（１
６）上における前記可塑剤供給層（１５）が形成された
領域上に改修用接合片（２２）を配置して、その接合片
（２２）及び可塑剤移行防止シート（１６）に、開脚
釘、カールプラグ等の機械的固着手段からなる第２固着
具（２３）を貫通して、構造物（１１）の躯体に固定す
ることにより、改修用接合片（２２）を可塑剤移行防止
シート（１６）上に固定する。Next, as shown in FIG. 3 and FIG. 6A, the repairing joint piece (22) is fixed on the plasticizer migration preventing sheet (16). That is, the plasticizer transfer prevention sheet (1)
6) A repair joint piece (22) is arranged on the area where the plasticizer supply layer (15) is formed, and the joint piece (22) and the plasticizer transfer prevention sheet (16) are opened. The repairing joint piece (22) is fixed to the frame of the structure (11) by penetrating through a second fixing tool (23) made of a mechanical fixing means such as a nail or a curl plug, so that the plasticizer transfer prevention sheet is formed. (16) Fix on top.
【００５１】続いて、図４及び図６（ｂ）に示すよう
に、改修用防水シート（２４）を、可塑剤移行防止シー
ト（１６）を上方から被覆するように配置し、更にその
改修用防水シート（２４）を張り渡した状態で、防水シ
ート（２４）の所要領域を、改修用接合片（２２）に接
着剤によりそれぞれ接着し、こうして改修作業が完了す
る。Subsequently, as shown in FIGS. 4 and 6 (b), a waterproofing sheet for repair (24) is arranged so as to cover the plasticizer migration preventing sheet (16) from above, and the repairing sheet is further provided. In a state where the waterproof sheet (24) is stretched, the required area of the waterproof sheet (24) is bonded to the repair joint piece (22) with an adhesive, and thus the repair work is completed.
【００５２】上記改修方法において、可塑剤供給層（１
５）は、少なくとも経年劣化防水シートに含まれる可塑
剤量よりも多量に可塑剤を含む塩化ビニル系樹脂組成物
をもって形成するものであり、被覆作業の簡易性と、劣
化防水シートとの良好な密着性を得るために、塩化ビニ
ルペースト（プラスチゾルまたはオルガノゾル）あるい
は塩化ビニル塗料等の塗布材料を用い、劣化防水シート
の表面に塗布することによって形成するものとすること
が好ましく、中でも塩化ビニル塗料系の塗布材料を用い
て劣化防水シートの表面に塗布して形成するのがより好
ましい。もっとも、可塑剤を多量に配合した軟質塩化ビ
ニルシートを用い、これを劣化防水シート表面に密着状
態に被覆一体化するものとしても良い。In the above repair method, the plasticizer supply layer (1
5) is formed by using a vinyl chloride resin composition containing a plasticizer in a larger amount than at least the amount of the plasticizer contained in the aged water-proof sheet. In order to obtain adhesiveness, it is preferable to use a coating material such as a vinyl chloride paste (plastisol or organosol) or a vinyl chloride paint and apply it to the surface of the deteriorated waterproof sheet, and particularly to use a vinyl chloride paint system. It is more preferable to apply the coating material on the surface of the deteriorated waterproof sheet to form it. However, a soft vinyl chloride sheet containing a large amount of a plasticizer may be used, and this may be integrally coated on the surface of the deteriorated waterproof sheet in a state of being adhered thereto.
【００５３】そして、塩化ビニルペーストを用いる場
合、例えば、これを１００℃以上、好ましくは１７５〜
１８０℃程度の高温に加熱し、溶融した状態で劣化防水
シートの表面に塗布し、塗布後放冷固化せしめて可塑剤
供給層（１５）を形成する。かかる工法においては、塗
布直後にペーストが冷却固化するため作業時間を短縮で
きるとともに、塗布時に劣化防水シートが加熱されるた
めアニーリング効果によりそれに内在する残留応力が緩
和されるという利点がある。具体的には、特開平８−３
５３０４号公報に記載されているように、ペースト供給
機、ペースト輸送用ポンプ、輸送路、ゲル化用ヒータ、
塗布用金型等からなる施工装置を用い、ペースト供給機
から順次送られてくる塩化ビニルペーストを加熱しなが
ら塗布用金型から吐出するとともに、この金型を塗布面
上を移動させることにより塗布施工する。When a vinyl chloride paste is used, for example, it is heated to 100 ° C. or higher, preferably 175 to 175 ° C.
It is heated to a high temperature of about 180 ° C., applied to the surface of the deteriorated waterproof sheet in a molten state, and allowed to cool and solidify after application to form a plasticizer supply layer (15). This method has the advantage that the working time can be reduced because the paste is cooled and solidified immediately after the application, and the residual stress inherent in the deteriorated waterproof sheet is reduced by the annealing effect because the deteriorated waterproof sheet is heated during the application. Specifically, JP-A-8-3
As described in JP-A-5304, a paste supply machine, a paste transportation pump, a transportation path, a gelling heater,
Using a construction device consisting of a coating die, etc., the vinyl chloride paste sequentially sent from the paste feeder is discharged from the coating die while heating, and the die is moved on the coating surface to perform coating. Execute.
【００５４】一方、塩化ビニル塗料系としては、塩化ビ
ニル系樹脂および可塑剤の混合物を溶媒に溶かした流動
性のある液状樹脂組成物、あるいは特開平８−２０７１
５４号公報に記載されるような、塩化ビニル系樹脂およ
び可塑剤を配合したゲル化物を溶媒中に膨潤分散させた
流動性のある樹脂組成物などが挙げられ、これを例えば
ローラや刷毛で塗布する。塗布後は、溶媒の揮発により
可塑剤供給層（１５）が形成される。中でも、後者の塩
化ビニル系樹脂および可塑剤を配合したゲル化物を溶媒
中に膨潤分散させた樹脂組成物を用いて塗布するのが好
ましく、この場合にはゲル化物において塩化ビニル系樹
脂が可塑剤を強く保持した状態となっているため、塗布
後に溶媒の揮発に伴って失われる可塑剤量は少なく、高
濃度に可塑剤を含有する塗膜を形成することができる。On the other hand, as the vinyl chloride coating system, a liquid resin composition having a fluidity obtained by dissolving a mixture of a vinyl chloride resin and a plasticizer in a solvent, or JP-A-8-2071
No. 54, a fluid resin composition obtained by swelling and dispersing a gelled product obtained by mixing a vinyl chloride resin and a plasticizer in a solvent, and the like, and applying this by, for example, a roller or a brush I do. After the application, the plasticizer supply layer (15) is formed by volatilization of the solvent. Above all, it is preferable to apply a resin composition obtained by swelling and dispersing a gelled product containing the latter vinyl chloride resin and a plasticizer in a solvent, and in this case, the vinyl chloride resin is used as a plasticizer in the gelled product. Is strongly retained, so that the amount of plasticizer lost due to the volatilization of the solvent after coating is small, and a coating film containing a high concentration of plasticizer can be formed.
【００５５】前記ゲル化物は、塩化ビニル系樹脂および
可塑剤を配合した塩化ビニルペーストを１４０〜１５０
℃以上に加熱することにより容易に得られる。前記ゲル
化物はそのままでは流動性がなく塗布により施工できな
いため、該ゲル化物を溶媒に分散させることによって系
に流動性を与え塗布施工を可能にしている。具体的に
は、ゲル化物を溶媒に浸漬して十分に膨潤させた後に、
撹拌して均一に分散させる。ここで使用する溶媒とはゲ
ル化物の良溶媒であり、エステル類、ケトン類、シクロ
ヘキサノン、テトラヒドロフラン、ニトロプロパン等を
例示できる。ゲル化物と溶媒の配合は、重量比で６０：
４０よりも溶媒が少なくなると、ゲル化物が十分に分散
せず流動性が不足して塗布作業が困難となる。一方、４
０：６０よりも溶媒が多くなると、分散性は向上するも
のの系の粘度が低下して塗膜厚みが薄くなり、防水性回
復効果が低下するばかりか、使用する溶媒は塩化ビニル
系樹脂の良溶媒であるため、被塗布物である防水シート
を溶解するおそれがある。従って、ゲル化物と溶媒の配
合は、重量比で６０：４０〜４０：６０とするのが好ま
しく、より好ましい下限値は５０：５０であり、より好
ましい上限値は４５：５５である。The gelled product is obtained by mixing a vinyl chloride paste containing a vinyl chloride-based resin and a plasticizer with 140-150.
It can be easily obtained by heating to above ℃. The gelled material has no fluidity as it is and cannot be applied by coating. Therefore, by dispersing the gelled material in a solvent, fluidity is given to the system to enable coating and application. Specifically, after swelling the gelled product sufficiently by immersing it in a solvent,
Stir to disperse evenly. The solvent used here is a good solvent for a gelled product, and examples thereof include esters, ketones, cyclohexanone, tetrahydrofuran, and nitropropane. The mixing ratio of the gelled product and the solvent is 60:
When the amount of the solvent is less than 40, the gelled product is not sufficiently dispersed and the fluidity is insufficient, so that the coating operation becomes difficult. Meanwhile, 4
When the amount of the solvent is larger than 0:60, the dispersibility is improved, but the viscosity of the system is reduced, the thickness of the coating film is reduced, and the effect of restoring waterproofness is reduced. Since it is a solvent, there is a possibility that the waterproof sheet which is an object to be coated is dissolved. Accordingly, the weight ratio of the gelled product and the solvent is preferably 60:40 to 40:60, more preferably the lower limit is 50:50, and the more preferred upper limit is 45:55.
【００５６】塗布材料（塩化ビニル系樹脂組成物）の塗
布量は、１０〜２４０００ｇ／ｍ2程度、塗布厚みにお
いて乾燥時０．３〜２．０ｍｍ程度とするのが適当であ
る。塗布量が少なすぎるときは、前記の可塑剤量が少な
すぎる場合と同様に、この発明の効果を十分に達成する
ことができず、逆に多すぎるときは、材料コストの増
大、塗布作業性の低下の不利益を招く。It is appropriate that the coating amount of the coating material (vinyl chloride resin composition) is about 10 to 24000 g / m 2 , and the coating thickness is about 0.3 to 2.0 mm when dried. When the coating amount is too small, the effect of the present invention cannot be sufficiently achieved as in the case where the plasticizer amount is too small. Conversely, when the coating amount is too large, the material cost increases and the coating workability increases. The disadvantage of the decline.
【００５７】次に、この発明の改修用複層シートについ
て説明する。図１１に本発明の一実施形態に係る改修用
複層シート（６１）の断面図を示す。この改修用複層シ
ート（６１）は、合成樹脂からなる防水層（６２）と、
可塑剤を多量に含有した塩化ビニル系樹脂組成物からな
る可塑剤供給層（６３）とが、可塑剤移行防止層（６
４）を介して積層一体化されたものである。Next, the repaired multilayer sheet of the present invention will be described. FIG. 11 shows a cross-sectional view of a repair multilayer sheet (61) according to an embodiment of the present invention. The repair multi-layer sheet (61) includes a waterproof layer (62) made of a synthetic resin,
A plasticizer supply layer (63) made of a vinyl chloride resin composition containing a large amount of a plasticizer;
4) through lamination and integration.
【００５８】上記防水層（６２）を構成する材料として
は、前記改修構造における改修用防水シート（２４）と
して挙示したものと同様のものが好適に用いられ、中で
も、軟質ポリ塩化ビニル樹脂からなるものは優れた接着
性、施工性、難燃性が得られるため、特に好適に用いら
れる。この防水層（６２）の厚さは、通常１．０〜２．
０ｍｍである。As the material constituting the waterproof layer (62), the same materials as those listed as the waterproof sheet for repair (24) in the repair structure are preferably used. These are particularly preferably used because excellent adhesiveness, workability and flame retardancy can be obtained. The thickness of the waterproof layer (62) is usually 1.0 to 2.
0 mm.
【００５９】また、可塑剤移行防止層（６４）として
は、前記防水層（６２）から劣化既設防水シートへの可
塑剤等の移行を防止できるもの、具体的にはポリエチレ
ン樹脂、ポリプロピレン樹脂等のポリオレフィン系樹
脂、ポリエステル樹脂などからなるものが好適に使用さ
れる。この可塑剤移行防止層（６４）の厚さは、通常
０．２〜１．０ｍｍである。なお、可塑剤移行防止層
（６４）は、防水層（６２）と可塑剤供給層（６３）の
間の全面に設けられるのが望ましいが、もちろん部分的
に設けられる構成であっても良い。The plasticizer migration preventing layer (64) can prevent migration of a plasticizer or the like from the waterproofing layer (62) to the deteriorated existing waterproofing sheet, specifically, a polyethylene resin, a polypropylene resin or the like. Those made of a polyolefin-based resin, a polyester resin or the like are preferably used. The thickness of the plasticizer migration preventing layer (64) is usually 0.2 to 1.0 mm. The plasticizer migration preventing layer (64) is desirably provided on the entire surface between the waterproof layer (62) and the plasticizer supply layer (63), but may be partially provided.
【００６０】また、可塑剤供給層（６３）を構成する塩
化ビニル系樹脂としては、特に限定されるものではない
が、例えば塩化ビニルの単独重合体の他、塩化ビニル
と、酢酸ビニル、エチレン、プロピレン等との二元また
は三元以上の共重合体等を好適に使用でき、また２種以
上併用したものも支障なく使用できる。The vinyl chloride resin constituting the plasticizer supply layer (63) is not particularly limited. For example, in addition to a homopolymer of vinyl chloride, vinyl chloride, vinyl acetate, ethylene, Binary or ternary or more copolymers with propylene or the like can be suitably used, and those in which two or more kinds are used in combination can be used without any trouble.
【００６１】また、可塑剤供給層（６３）を構成する塩
化ビニル系樹脂組成物は、塩化ビニル系樹脂１００重量
部（固形分）に対し、可塑剤を５０〜３００重量部含有
させるのが好ましい。この数値限定理由については前記
改修構造における理由と全く同一である。最も好ましい
可塑剤の含有量は、塩化ビニル系樹脂１００重量部に対
し、可塑剤１５０〜２５０重量部である。また、可塑剤
についても、前記改修構造において例示したものと同様
のものを例示できる。更に、配合し得る各種添加剤につ
いても前記同様である。The vinyl chloride resin composition constituting the plasticizer supply layer (63) preferably contains 50 to 300 parts by weight of a plasticizer based on 100 parts by weight (solid content) of the vinyl chloride resin. . The reason for this numerical limitation is exactly the same as the reason for the above-mentioned renovation structure. The most preferable content of the plasticizer is 150 to 250 parts by weight of the plasticizer based on 100 parts by weight of the vinyl chloride resin. Further, the same plasticizers as those exemplified in the above-mentioned modified structure can be exemplified. Further, the same applies to the various additives that can be blended.
【００６２】この可塑剤供給層（６３）は、前記可塑剤
移行防止層（６４）表面の全面に積層一体化されたもの
でも良いし、あるいは該表面に部分的に積層一体化され
たものであっても良いが、劣化既設防水シートに早期に
可塑剤を十分に供給補充する観点から、全面に積層一体
化されるのが望ましい。この可塑剤供給層（６３）の厚
さは、前記改修構造における理由と同様の理由から、
０．３〜２．０ｍｍ程度とするのが適当である。The plasticizer supply layer (63) may be laminated and integrated on the entire surface of the plasticizer migration preventing layer (64), or may be partially laminated and integrated on the surface. It may be present, but from the viewpoint of sufficiently supplying and replenishing the plasticizer to the deteriorated existing waterproof sheet at an early stage, it is preferable that the waterproof sheet is laminated and integrated over the entire surface. The thickness of the plasticizer supply layer (63) is determined for the same reason as in the above-mentioned remodeled structure,
Suitably, it is about 0.3 to 2.0 mm.
【００６３】この発明の改修用複層シート（６１）を得
るに際し、防水層（６２）、可塑剤供給層（６３）、可
塑剤移行防止層（６４）の各層を積層一体化する手段と
しては、特に限定されないが、例えばラミネート法、プ
レス法等の通常適用される積層方法を用いれば良い。In order to obtain the repair multi-layer sheet (61) of the present invention, means for laminating and integrating the waterproof layer (62), the plasticizer supply layer (63), and the plasticizer migration preventing layer (64) are as follows. Although not particularly limited, a commonly applied laminating method such as a laminating method and a pressing method may be used.
【００６４】この発明の改修用複層シート（６１）を用
いて既設防水シートの改修を行うにあたっては、この複
層シート（６１）を、可塑剤供給層（６３）が既設防水
シートと接する態様で敷設施工するか、あるいは直接に
接していなくても可塑剤供給層（６３）から既設防水シ
ートへ可塑剤が供給可能となる態様で敷設施工すれば良
い。具体的には、例えば可塑剤供給層（６３）と既設防
水シートとを部分的に接着剤により接着して敷設施工し
ても良いし、あるいは可塑剤の移行が可能となる接着層
を介して可塑剤供給層（６３）と既設防水シートとを接
合するものとしても良いし、あるいはまた前述したよう
な接合片（２２）を用いてこの改修用複層シート（６
１）を、防水構造物（既設防水シートの防水対象である
構造物）に固定するものとしても良い。このような改修
用複層シート（６１）を用いて改修を行うものとすれ
ば、可塑剤供給層（６３）から既設防水シートへ可塑剤
が供給可能となる態様で敷設施工するだけで改修施工が
完了するから、改修が容易であり、施工時間、施工労力
ともに少なくて済み、施工性に極めて優れるという利点
がある。そして、可塑剤供給層（６３）から劣化既設防
水シートに徐々に可塑剤が供給補充されて、劣化既設防
水シートの物性、特に柔軟性が回復するとともに張力が
取り除かれるから、劣化既設防水シートの張力に起因す
る悪影響がこの改修用複層シート（６１）に及ぶことは
ない。また可塑剤移行防止層（６４）が中間層として介
装されているから、この複層シートの防水層（６２）か
ら劣化既設防水シート側に可塑剤が移行するのを確実に
防止することができる。In repairing an existing waterproof sheet using the repairing multi-layer sheet (61) of the present invention, the multi-layer sheet (61) is brought into contact with the plasticizer supply layer (63) in contact with the existing waterproof sheet. The plasticizer may be laid or constructed in such a manner that the plasticizer can be supplied from the plasticizer supply layer (63) to the existing waterproof sheet even if the plasticizer is not in direct contact. Specifically, for example, the plasticizer supply layer (63) and the existing waterproof sheet may be partially laid and adhered with an adhesive, or the plasticizer supply layer (63) may be connected to the existing waterproof sheet through an adhesive layer capable of transferring the plasticizer. The plasticizer supply layer (63) may be joined to the existing waterproof sheet, or the repaired multilayer sheet (6) may be joined using the joint piece (22) as described above.
1) may be fixed to a waterproof structure (a structure to be waterproofed by an existing waterproof sheet). If the renovation is performed using such a multi-layer sheet for renovation (61), the renovation can be performed simply by laying the plasticizer from the plasticizer supply layer (63) to the existing waterproof sheet in such a manner that the plasticizer can be supplied. Thus, there is an advantage that the renovation is easy, the construction time and labor are small, and the workability is extremely excellent. Then, the plasticizer is gradually supplied and replenished from the plasticizer supply layer (63) to the deteriorated existing waterproof sheet, and the physical properties, particularly flexibility, of the deteriorated existing waterproof sheet are restored and the tension is removed. The adverse effect due to the tension does not affect the repair multi-layer sheet (61). Further, since the plasticizer transfer prevention layer (64) is interposed as an intermediate layer, it is possible to reliably prevent the transfer of the plasticizer from the waterproof layer (62) of the multilayer sheet to the deteriorated existing waterproof sheet side. it can.
【００６５】なお、この発明の改修用複層シート（６
１）は、上記のように、既設防水シート上に敷設施工す
るだけで改修を完了できるものであるから、絶縁工法に
より施工された防水シートのみならず、密着工法により
施工された防水シート、あるいはその他の工法により施
工された防水シートにも適用することができる。The repaired multi-layer sheet (6
1) As described above, since the repair can be completed simply by laying on the existing waterproof sheet, not only the waterproof sheet constructed by the insulation method, but also the waterproof sheet constructed by the close contact method, or The present invention can be applied to a waterproof sheet constructed by another method.
【００６６】[0066]
【実施例】次に、この発明の具体的実施例について説明
する。Next, specific embodiments of the present invention will be described.
【００６７】＜実施例１＞建築物の屋上に絶縁工法によ
り張設施工された軟質塩化ビニル樹脂製防水シート（厚
さ１．５ｍｍ）であって、施工後陽光暴露下に約１５年
を経過した防水シートを経年劣化防水シートのサンプル
として使用し、これの表面に図１に示すように部分的に
下記配合および調製法により調製した修復用樹脂組成物
をローラ刷毛により１２００ｇ／ｍ2 の割合に塗布し、
可塑剤供給層を形成した。次いで、図２に示すように上
方から被覆するようにしてポリエチレン樹脂からなる可
塑剤移行防止シートを敷設した後、この可塑剤移行防止
シート上の前記可塑剤供給層の上方に対応する位置にそ
れぞれディスク状の塩化ビニル鋼鈑からなる改修用接合
片を固定し（図３）、更に軟質ポリ塩化ビニル樹脂から
なる改修用防水シートを、可塑剤移行防止シートを上方
から被覆するように配置して張り渡した状態で、この改
修用防水シートの所要領域を改修用接合片に接着剤（テ
トラヒドロフラン）によりそれぞれ接着して（図４）、
改修を行った。<Example 1> A waterproof sheet made of a soft vinyl chloride resin (1.5 mm thick) stretched and installed on the roof of a building by an insulation method, and about 15 years have passed since the construction was exposed to sunlight. The obtained waterproof sheet was used as a sample of an aged waterproof sheet, and a repairing resin composition partially prepared by the following formulation and preparation method as shown in FIG. 1 was applied to the surface of the sample with a roller brush at a rate of 1200 g / m 2 . And apply
A plasticizer supply layer was formed. Next, as shown in FIG. 2, after laying a plasticizer migration prevention sheet made of polyethylene resin so as to cover from above, each of the plasticizer migration prevention sheets is positioned on the plasticizer migration prevention sheet at a position corresponding to above the plasticizer supply layer. A repair piece made of a disc-shaped polyvinyl chloride steel plate is fixed (FIG. 3), and a repair waterproof sheet made of a soft polyvinyl chloride resin is arranged so as to cover the plasticizer migration prevention sheet from above. In the stretched state, the required area of the repairing waterproof sheet is bonded to the repairing joint piece with an adhesive (tetrahydrofuran), respectively (FIG. 4).
Renovated.
【００６８】（修復用樹脂組成物）塩化ビニル樹脂１０
０重量部、可塑剤（ＤＯＰ）２００重量部、充填材（酸
化チタン）１０重量部、安定剤（金属せっけん）５重量
部を配合して得られる塩化ビニル樹脂組成物と、溶媒と
してメチルエチルケトン（ＭＥＫ）とを、塩化ビニル樹
脂組成物：ＭＥＫが重量比で４０：６０の割合となるよ
うに加え、室温で１日放置して塩化ビニル樹脂組成物を
十分に膨潤させてゲル化物を得て、撹拌して系が均一と
なるように分散させた。(Repairing Resin Composition) Vinyl Chloride Resin 10
0 parts by weight, 200 parts by weight of a plasticizer (DOP), 10 parts by weight of a filler (titanium oxide), and 5 parts by weight of a stabilizer (metal soap), and methyl ethyl ketone (MEK) as a solvent. ) Was added so that the weight ratio of the vinyl chloride resin composition: MEK was 40:60, and the mixture was left at room temperature for 1 day to sufficiently swell the vinyl chloride resin composition to obtain a gelled product. The system was stirred and dispersed so as to be uniform.
【００６９】＜実施例２＞下記配合により調製した修復
用樹脂組成物を１２００ｇ／ｍ2 の割合に塗布して可塑
剤供給層を形成した以外は、実施例１と同様にして改修
を行った。<Example 2> A repair was performed in the same manner as in Example 1 except that a repairing resin composition prepared according to the following formulation was applied at a rate of 1200 g / m 2 to form a plasticizer supply layer. .
【００７０】（修復用樹脂組成物）塩化ビニル樹脂１０
０重量部、可塑剤（ＤＯＰ）２００重量部、充填剤（酸
化チタン）１０重量部、安定剤（Ｂａ−Ｚｎ）５重量
部、溶媒（テトラヒドロフラン８５％、シクロヘキサノ
ン１５％）３３０重量部を配合して得られる塩化ビニル
塗料。(Repairing Resin Composition) Vinyl Chloride Resin 10
0 parts by weight, plasticizer (DOP) 200 parts by weight, filler (titanium oxide) 10 parts by weight, stabilizer (Ba-Zn) 5 parts by weight, solvent (tetrahydrofuran 85%, cyclohexanone 15%) 330 parts by weight PVC paint obtained by
【００７１】＜実施例３＞下記配合により調製した修復
用樹脂組成物を、１７０℃に加熱溶融した状態で１２０
０ｇ／ｍ2 の割合に塗布し、放冷固化させて可塑剤供給
層を形成した以外は、実施例１と同様にして改修を行っ
た。Example 3 A repairing resin composition prepared according to the following formulation was heated to 170 ° C. and melted to obtain a resin composition.
The modification was carried out in the same manner as in Example 1 except that a plasticizer supply layer was formed by applying the mixture at a rate of 0 g / m 2 and allowing it to cool and solidify.
【００７２】（修復用樹脂組成物）塩化ビニルペースト
（プラスチゾル）１００重量部、可塑剤（ＤＯＰ）２０
０重量部、充填剤（酸化チタン）１０重量部、安定剤
（金属せっけん）５重量部を配合して得られる塩化ビニ
ルペースト。(Resin Resin Composition) 100 parts by weight of vinyl chloride paste (plastisol), plasticizer (DOP) 20
A vinyl chloride paste obtained by mixing 0 parts by weight, 10 parts by weight of a filler (titanium oxide), and 5 parts by weight of a stabilizer (metal soap).
【００７３】＜実施例４＞塩化ビニル樹脂１００重量
部、可塑剤（ＤＯＰ）２００重量部、充填材（酸化チタ
ン）１０重量部、安定剤（金属せっけん）５重量部を配
合して得られる塩化ビニル樹脂組成物からなる可塑剤供
給層と、ポリエチレン樹脂からなる可塑剤移行防止層と
が一体化された改修用複層シートを、ラミネート法によ
り得た。Example 4 Chloride obtained by blending 100 parts by weight of a vinyl chloride resin, 200 parts by weight of a plasticizer (DOP), 10 parts by weight of a filler (titanium oxide), and 5 parts by weight of a stabilizer (metal soap). A multilayer sheet for repair in which a plasticizer supply layer made of a vinyl resin composition and a plasticizer migration preventing layer made of a polyethylene resin were integrated was obtained by a laminating method.
【００７４】この改修用複層シートを、可塑剤供給層を
下にして、実施例１と同様の経年劣化防水シート上に接
触状態に敷設し、次いでこれの上方からディスク状の塩
化ビニル鋼鈑からなる改修用接合片を固定し、更に軟質
ポリ塩化ビニル樹脂からなる改修用防水シートを、改修
用複層シートを上方から被覆するように配置して張り渡
した状態で、この改修用防水シートの所要領域を改修用
接合片に接着剤（テトラヒドロフラン）によりそれぞれ
接着して、改修を行った。The repaired multi-layer sheet is laid in contact with the aging waterproof sheet similar to that of Example 1 with the plasticizer supply layer facing down, and then a disc-shaped vinyl chloride steel sheet is placed from above. The repairing waterproofing sheet made of soft polyvinyl chloride resin is fixed, and the repairing waterproof sheet made of a soft polyvinyl chloride resin is arranged so as to cover the repairing multi-layer sheet from above. The required area was repaired by bonding it to the repaired joint piece with an adhesive (tetrahydrofuran).
【００７５】＜実施例５＞塩化ビニル樹脂１００重量
部、可塑剤（ＤＯＰ）２００重量部、充填材（酸化チタ
ン）１０重量部、安定剤（金属せっけん）５重量部を配
合して得られる塩化ビニル樹脂組成物からなる可塑剤供
給シート（可塑剤供給層を形成するもの）に、ポリエチ
レン樹脂からなる可塑剤移行防止シート（可塑剤移行防
止層を形成するもの）をラミネート法により積層し、更
にこの可塑剤移行防止シートの上に軟質塩化ビニル樹脂
からなる防水シート（防水層を形成するもの）をラミネ
ート法により積層して、改修用複層シートを得た。<Example 5> Chloride obtained by blending 100 parts by weight of a vinyl chloride resin, 200 parts by weight of a plasticizer (DOP), 10 parts by weight of a filler (titanium oxide), and 5 parts by weight of a stabilizer (metal soap). A plasticizer transfer preventing sheet (forming a plasticizer transfer preventing layer) made of a polyethylene resin is laminated on a plasticizer supply sheet (forming a plasticizer supply layer) made of a vinyl resin composition by a laminating method. A waterproof sheet made of a soft vinyl chloride resin (forming a waterproof layer) was laminated on the plasticizer transfer prevention sheet by a laminating method to obtain a multi-layer sheet for repair.
【００７６】次に、建築物の屋上に絶縁工法により張設
施工された軟質塩化ビニル樹脂製防水シート（厚さ１．
５ｍｍ）であって、施工後陽光暴露下に約１５年を経過
した防水シートを経年劣化防水シートのサンプルとして
使用し、この劣化防水シートの上に、接着剤を用いて前
記改修用複層シートの可塑剤供給層を部分的に接着し
て、当該接着箇所を除いて可塑剤供給層と劣化防水シー
トとが接触する態様で改修用複層シートを敷設し、改修
を行った。Next, a soft vinyl chloride resin waterproof sheet (having a thickness of 1.times.) Stretched on the roof of a building by an insulation method.
5 mm), and a waterproof sheet that has passed about 15 years after being exposed to sunlight after construction is used as a sample of an aged deteriorated waterproof sheet. Of the plasticizer supply layer was partially adhered, and a repair multi-layer sheet was laid so that the plasticizer supply layer and the deteriorated waterproof sheet were in contact with each other except for the bonded portion, and the repair was performed.
【００７７】＜評価＞改修作業完了後３０日を経過した
時のシート防水構造物の上面、即ち最上層の新防水シー
トの外観（しわ発生の有無、膨れの有無、接合片の浮き
上がりの有無等）を観察した。<Evaluation> Appearance of the upper surface of the sheet waterproof structure, that is, the appearance of the new uppermost waterproof sheet 30 days after the completion of the repair work (whether there are wrinkles, whether there is swelling, or whether the joint pieces have risen, etc.) ) Was observed.
【００７８】一方、塗布後３０日を経過した時に可塑剤
供給層付き防水シート（供給層＋経年防水シートのみ）
を切り出し、これの機械的性質を測定し（ＪＩＳ Ａ６
００８）、防水シートの初期物性、及び経年劣化時の物
性と比較した。これらの結果を表１に示す。On the other hand, when 30 days have passed since the application, the waterproof sheet with the plasticizer supply layer (only the supply layer and the aged waterproof sheet)
Was cut out and its mechanical properties were measured (JIS A6
008), the initial physical properties of the waterproof sheet, and the physical properties after aging degradation were compared. Table 1 shows the results.
【００７９】[0079]
【表１】 [Table 1]
【００８０】表１に示されるとおり、改修後３０日を経
過した時点において既に、経年防水シートは伸び率を相
当程度に回復するとともに、改修後のシート防水構造物
の外観も、しわ発生や膨れ、浮き上がり等もなく良好な
ものであった。As shown in Table 1, the aged waterproof sheet has already recovered its elongation to a considerable extent 30 days after the renovation, and the appearance of the renovated sheet waterproof structure has become wrinkled or blistered. The product was good without any lifting.
【００８１】[0081]
【発明の効果】以上のように、この発明のシート防水構
造物の改修構造によれば、経年劣化した既設防水シート
をすべて撤去するという負担の大きい作業を行わなくと
もよく、その分、作業効率を向上させることができ、改
修期間の短縮及びコストの削減を図ることができる。し
かも既設防水シートをすべて撤去したり、あるいは部分
的に撤去するようなことがないから、改修期間中の雨に
より漏水することが全くない。更に劣化防水シートを廃
棄することは全くなく、産業廃棄物が発生せず、自然環
境保護に関しても適切に対処することができる。また本
発明においては新たな改修用防水シートを、新設の改修
用接合片を介して構造物に取り付けるものであるため、
劣化防水シートがどのような表面状態にあろうとも、改
修用防水シートを支障なく取り付けることができ、しか
も可塑剤供給層から劣化防水シートに徐々に可塑剤が供
給されて張力が取り除かれるから、劣化防水シートの張
力に起因する悪影響が新設の改修用防水シートに及ぶこ
とはない。従って改修用防水シートを確実に施工できる
とともに、改修用防水シートに剥離や膨れが生ずること
がなく、良好な美観を得ることができる。As described above, according to the repaired structure of the waterproof sheet structure of the present invention, it is not necessary to perform the burdensome work of removing all the existing waterproof sheets that have deteriorated over time. Can be improved, and the repair period can be shortened and the cost can be reduced. Moreover, since there is no need to completely or partially remove the existing waterproof sheet, there is no water leakage due to rain during the renovation period. Furthermore, the deteriorated waterproof sheet is never discarded, no industrial waste is generated, and appropriate measures can be taken for protecting the natural environment. Also, in the present invention, a new renovation waterproofing sheet is to be attached to the structure via the newly installed renovation joint piece,
Regardless of the surface condition of the deteriorated waterproofing sheet, the repairing waterproofing sheet can be installed without trouble, and the plasticizer is gradually supplied from the plasticizer supply layer to the deteriorated waterproofing sheet to remove the tension, The adverse effects caused by the tension of the deteriorated tarpaulin do not affect the newly installed renovation tarpaulin. Therefore, the repairing waterproof sheet can be reliably applied, and the repairing waterproof sheet does not peel off or swell, and a good appearance can be obtained.
【００８２】改修用接合片が、可塑剤供給層が形成され
た領域に対応する上部位置に配置される場合には、劣化
防水シートの張力による悪影響が改修用接合片にまで及
ぶことが確実に防止でき、改修用接合片の浮き上がりを
確実に防止できる。When the repair joint piece is disposed at an upper position corresponding to the area where the plasticizer supply layer is formed, it is ensured that the adverse effect due to the tension of the deteriorated waterproof sheet reaches the repair joint piece. It is possible to prevent the repairing piece from rising.
【００８３】また、可塑剤供給層が積層された既設防水
シートと、改修用防水シートとの間に、可塑剤移行防止
層が積層されている場合には、改修用防水シートから劣
化防水シート側に可塑剤等の必要成分が移行するのを確
実に防止でき、改修用防水シートの早期劣化を抑制して
耐久性の向上を図ることができるという効果が得られ
る。When a plasticizer migration preventing layer is laminated between the existing waterproof sheet on which the plasticizer supply layer is laminated and the renovation waterproof sheet, when the renovation waterproof sheet is replaced with the deteriorated waterproof sheet, In addition, it is possible to reliably prevent the necessary components such as the plasticizer from migrating, and to suppress the early deterioration of the waterproofing sheet for repair, thereby improving the durability.
【００８４】また、この発明のシート防水構造物の改修
方法により形成される構造は、上記発明の改修構造その
ものであるから、この方法により形成された改修構造
は、上記改修構造において記載したと同様の各種の優れ
た効果が得られることは言うまでもないが、加えて、こ
の改修方法によれば、可塑剤供給層が既設防水シートに
対して密着状態に被覆形成されるから、即ち両者が接合
状態となされるから、可塑剤供給層から既設防水シート
への可塑剤の供給がより早期に行われ、ひいては施工後
のより早い時期から改修用防水シートに剥離や膨れのな
い、良好な美観を確保することができる。Further, since the structure formed by the method for repairing a waterproof sheet structure of the present invention is the same as the repair structure of the present invention, the repair structure formed by this method is the same as that described in the above repair structure. Needless to say, various excellent effects can be obtained, but in addition, according to this repair method, the plasticizer supply layer is formed in close contact with the existing waterproof sheet, that is, the two are in a joined state. As a result, the supply of plasticizer from the plasticizer supply layer to the existing waterproof sheet is performed earlier, and as a result, a good appearance without peeling or swelling of the waterproofing sheet for repair is secured earlier from the construction. can do.
【００８５】また、この発明の改修用複層シートは、可
塑剤移行防止層、可塑剤供給層が予め積層一体化された
ものであるから、上記改修構造を施工するに際しその構
成材として用いれば、改修を容易に行うことができ、施
工時間、施工労力ともに少なくて済み、改修の施工性を
向上させることができる。Further, the multi-layer sheet for renovation of the present invention has a plasticizer transfer prevention layer and a plasticizer supply layer previously laminated and integrated, so that it can be used as a constituent material when constructing the renovation structure. In addition, the renovation can be easily performed, and the construction time and labor can be reduced, and the renovation workability can be improved.
【００８６】また、この発明の別の改修用複層シート
は、防水層、可塑剤移行防止層、可塑剤供給層が予め積
層一体化されたものであるから、改修作業が容易であ
り、施工時間、施工労力ともに少なくて済み、施工性に
優れている。そして、劣化既設防水シートの上に敷設さ
れた可塑剤供給層から既設防水シートに可塑剤が供給補
充されるので、劣化既設防水シートの張力に起因する悪
影響がこの改修用複層防水シートに及ぶことがない。ま
た、可塑剤移行防止層が中間層として介装されているか
ら、この複層防水シートの防水層から既設防水シート側
に可塑剤が移行するのを確実に防止でき、ひいては防水
シートとしての耐久性の向上を図ることができる。Further, another repairing multi-layer sheet of the present invention has a waterproof layer, a plasticizer migration preventing layer, and a plasticizer supply layer previously laminated and integrated, so that the repair work is easy, and It requires less time and labor, and has excellent workability. Then, the plasticizer is supplied and replenished to the existing waterproof sheet from the plasticizer supply layer laid on the deteriorated existing waterproof sheet, so that the adverse effect due to the tension of the deteriorated existing waterproof sheet extends to this repair multi-layer waterproof sheet. Nothing. Further, since the plasticizer migration preventing layer is interposed as an intermediate layer, the migration of the plasticizer from the waterproof layer of the multi-layer waterproof sheet to the existing waterproof sheet side can be reliably prevented. Performance can be improved.
【図１】この発明の改修方法が適用されたシート防水構
造物を可塑剤供給層形成直後の状態で示す斜視図であ
る。FIG. 1 is a perspective view showing a waterproof sheet structure to which a repair method of the present invention has been applied, in a state immediately after forming a plasticizer supply layer.
【図２】上記シート防水構造物を可塑剤移行防止シート
敷設直後の状態で示す斜視図である。FIG. 2 is a perspective view showing the waterproof sheet structure immediately after a plasticizer transfer preventing sheet is laid.
【図３】上記シート防水構造物を改修用接合片固定直後
の状態で示す斜視図である。FIG. 3 is a perspective view showing the waterproof sheet structure in a state immediately after fixing a repairing joint piece.
【図４】上記シート防水構造物を改修施工完了後の状態
で示す斜視図である。FIG. 4 is a perspective view showing the waterproof sheet structure in a state after completion of repair work.
【図５】上記シート防水構造物を示す断面図であって、
同図（ａ）は可塑剤供給層形成直後の状態における断面
図、同図（ｂ）は可塑剤移行防止シート敷設直後の状態
における断面図である。FIG. 5 is a cross-sectional view showing the waterproof sheet structure.
FIG. 4A is a cross-sectional view in a state immediately after forming a plasticizer supply layer, and FIG. 4B is a cross-sectional view in a state immediately after laying a plasticizer transfer prevention sheet.
【図６】上記シート防水構造物を示す断面図であって、
同図（ａ）は改修用接合片固定直後の状態における断面
図、同図（ｂ）は改修施工完了後の状態における断面図
である。FIG. 6 is a cross-sectional view showing the waterproof sheet structure,
FIG. 3A is a cross-sectional view in a state immediately after fixing of the repairing joint piece, and FIG. 3B is a cross-sectional view in a state after completion of the repair work.
【図７】別の実施形態の改修方法が適用されたシート防
水構造物の改修施工完了後における断面図である。FIG. 7 is a cross-sectional view of a waterproof sheet structure to which the repair method according to another embodiment has been applied after repair work is completed.
【図８】絶縁工法により施工されたシート防水構造物を
示す斜視図である。FIG. 8 is a perspective view showing a waterproof sheet structure constructed by an insulation method.
【図９】絶縁工法により施工されたシート防水構造物を
示す断面図である。FIG. 9 is a cross-sectional view showing a waterproof sheet structure constructed by an insulating method.
【図１０】この発明の改修用複層シートを示す断面図で
ある。FIG. 10 is a cross-sectional view showing a repair multilayer sheet of the present invention.
【図１１】この発明の別の改修用複層シートを示す断面
図である。FIG. 11 is a cross-sectional view showing another modified multi-layer sheet of the present invention.
【図１２】密着工法により施工されたシート防水構造物
を示す断面図である。FIG. 12 is a cross-sectional view showing a waterproof sheet structure constructed by a close contact method.
１１…構造物 １２…第１接合片 １４…既設防水シート １５…可塑剤供給層 １６…可塑剤移行防止シート ２２…改修用接合片 ２４…改修用防水シート ５１…改修用複層シート ５２…可塑剤供給層 ５３…可塑剤移行防止層 ６１…改修用複層シート ６２…防水層 ６３…可塑剤供給層 ６４…可塑剤移行防止層 DESCRIPTION OF SYMBOLS 11 ... Structure 12 ... 1st joint piece 14 ... Existing waterproof sheet 15 ... Plasticizer supply layer 16 ... Plasticizer migration prevention sheet 22 ... Repair joint piece 24 ... Repair waterproof sheet 51 ... Repair multilayer sheet 52 ... Plastic Agent supply layer 53 ... Plasticizer migration prevention layer 61 ... Renovation multilayer sheet 62 ... Waterproof layer 63 ... Plasticizer supply layer 64 ... Plasticizer migration prevention layer
Claims (9)
着工法等により敷設された既設防水シートにより防水施
工されたシート防水構造物の改修構造であって、 前記既設防水シート表面の一部ないし全面に、可塑剤を
多量に含有した塩化ビニル系樹脂組成物からなる可塑剤
供給層が積層され、該可塑剤供給層が積層された既設防
水シート上に改修用防水シートが積層されると共に、改
修用接合片が前記既設防水シートと改修用防水シートと
の間に又は改修用防水シートの上に配置された状態で前
記構造物に固定され、かつこの改修用接合片に前記改修
用防水シートの一部が接合されていることを特徴とする
シート防水構造物の改修構造。1. A repair structure for a sheet waterproofing structure which is waterproofed by an existing waterproofing sheet laid on a surface of the structure to be waterproofed by an insulating method, a close contacting method, or the like, and a part of the surface of the existing waterproofing sheet. On the entire surface, a plasticizer supply layer made of a vinyl chloride resin composition containing a large amount of a plasticizer is laminated, and a renovation waterproof sheet is laminated on an existing waterproof sheet on which the plasticizer supply layer is laminated. The repair joint piece is fixed to the structure in a state where the repair joint piece is disposed between the existing waterproof sheet and the repair waterproof sheet or on the repair waterproof sheet, and the repair waterproof piece is attached to the repair joint piece. A repair structure for a waterproof sheet structure, wherein a part of the sheet is joined.
１００重量部（固形分）に対し、可塑剤５０〜３００重
量部を含有する塩化ビニル系樹脂組成物からなる請求項
１に記載のシート防水構造物の改修構造。2. The plasticizer supply layer according to claim 1, wherein the plasticizer supply layer comprises a vinyl chloride resin composition containing 50 to 300 parts by weight of a plasticizer with respect to 100 parts by weight (solid content) of the vinyl chloride resin. Renovation structure of waterproof sheet structure.
が形成された領域に対応する上部位置に配置されている
請求項１または２に記載のシート防水構造物の改修構
造。3. The repair structure for a waterproof sheet structure according to claim 1, wherein the repair piece is arranged at an upper position corresponding to a region where the plasticizer supply layer is formed.
シートと、改修用防水シートとの間に、可塑剤移行防止
層が積層されている請求項１〜３のいずれか１項に記載
のシート防水構造物の改修構造。4. The plasticizer migration preventing layer is laminated between an existing waterproof sheet on which the plasticizer supply layer is laminated and a renovation waterproof sheet. Renovation structure of waterproof sheet structure.
着工法等により敷設された既設防水シートにより防水施
工されたシート防水構造物の改修方法であって、 前記既設防水シート表面の一部ないし全面に、可塑剤を
多量に含有した塩化ビニル系樹脂組成物からなる可塑剤
供給層を密着状態に被覆形成する工程と、 前記可塑剤供給層が形成された既設防水シート上に可塑
剤移行防止シートを敷設する工程と、 前記可塑剤移行防止シート上に改修用接合片を配置し前
記構造物に固定する工程と、 改修用防水シートを前記可塑剤移行防止シート上に張り
渡して前記改修用接合片に接着する工程とを含むことを
特徴とするシート防水構造物の改修方法。5. A method for repairing a sheet waterproof structure waterproofed by an existing waterproof sheet laid on a surface of the structure to be waterproofed by an insulating method, a close contact method, or the like, wherein a part of the surface of the existing waterproof sheet is provided. Or forming a plasticizer supply layer composed of a vinyl chloride resin composition containing a large amount of a plasticizer on the entire surface in an intimate contact state, and transferring the plasticizer onto the existing waterproof sheet on which the plasticizer supply layer is formed. Laying a preventive sheet, arranging a repairing joint piece on the plasticizer transfer preventing sheet and fixing it to the structure, stretching the waterproofing sheet over the plasticizer transfer preventive sheet and performing the repair A method for repairing a waterproof sheet structure, the method comprising:
脂組成物からなる可塑剤供給層と、可塑剤移行防止層と
が積層一体化されてなるシート防水構造物の改修用複層
シート。6. A multi-layer sheet for repairing a waterproof sheet structure in which a plasticizer supply layer composed of a vinyl chloride resin composition containing a large amount of a plasticizer and a plasticizer migration preventing layer are integrally laminated.
１００重量部（固形分）に対し、可塑剤５０〜３００重
量部を含有する塩化ビニル系樹脂組成物からなる請求項
６に記載のシート防水構造物の改修用複層シート。7. The plasticizer supply layer according to claim 6, wherein the plasticizer supply layer comprises a vinyl chloride resin composition containing 50 to 300 parts by weight of a plasticizer with respect to 100 parts by weight (solid content) of the vinyl chloride resin. A multi-layer sheet for repairing sheet waterproof structures.
量に含有した塩化ビニル系樹脂組成物からなる可塑剤供
給層が、可塑剤移行防止層を介して積層一体化されてな
ることを特徴とするシート防水構造物の改修用複層シー
ト。8. A method in which a waterproof layer made of a synthetic resin and a plasticizer supply layer made of a vinyl chloride resin composition containing a large amount of a plasticizer are laminated and integrated via a plasticizer migration preventing layer. A multi-layer sheet for renovation of a sheet waterproof structure, which is a feature.
１００重量部（固形分）に対し、可塑剤５０〜３００重
量部を含有する塩化ビニル系樹脂組成物からなる請求項
８に記載のシート防水構造物の改修用複層シート。9. The plasticizer supply layer according to claim 8, wherein the plasticizer supply layer comprises a vinyl chloride resin composition containing 50 to 300 parts by weight of a plasticizer based on 100 parts by weight (solid content) of the vinyl chloride resin. A multi-layer sheet for repairing sheet waterproof structures.