JPH11204838A - Semiconductor light emitting device and its manufacture - Google Patents

Semiconductor light emitting device and its manufacture

Info

Publication number
JPH11204838A
JPH11204838A JP10006423A JP642398A JPH11204838A JP H11204838 A JPH11204838 A JP H11204838A JP 10006423 A JP10006423 A JP 10006423A JP 642398 A JP642398 A JP 642398A JP H11204838 A JPH11204838 A JP H11204838A
Authority
JP
Japan
Prior art keywords
light emitting
semiconductor light
glass layer
emitting diode
emitting device
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP10006423A
Other languages
Japanese (ja)
Other versions
JP2924961B1 (en
Inventor
Takeshi Sano
武志 佐野
Original Assignee
Sanken Electric Co Ltd
サンケン電気株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sanken Electric Co Ltd, サンケン電気株式会社 filed Critical Sanken Electric Co Ltd
Priority to JP10006423A priority Critical patent/JP2924961B1/en
Application granted granted Critical
Publication of JP2924961B1 publication Critical patent/JP2924961B1/en
Publication of JPH11204838A publication Critical patent/JPH11204838A/en
Application status is Expired - Fee Related legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To improve environmental resistance and ultraviolet-ray resistance of a semiconductor light emitting device. SOLUTION: In a semiconductor light emitting device provided with a pair of wiring conductors (3, 4), a semiconductor light emitting device (2) fixed to one end part of the pair of wiring conductor (3, 4), and a light-transmittive insulating seal body covering the semiconductor light emitting device (2), the insulating seal body is constructed of a glass layer (10). A fluorescent material (10a), which has light-transmittivity to the light from the semiconductor light emitting device (2), and which absorbs the light from the semiconductor light emitting device (2) and converts it into other wavelength of light emission, is mixed into the glass layer (10). The light emitted by the semiconductor light emitting device (2) is converted into a desired wavelength of light emission by the fluorescent material (10a) in the glass layer (10), and is emitted outside through the glass layer (10) surrounding the semiconductor light emitting device (2).

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、発光ダイオード装置、特に半導体発光素子から照射される光を波長変換して外部に放出する半導体発光装置に関する。 The present invention relates to a light-emitting diode device, a semiconductor light emitting device that emits to the outside, especially wavelength conversion of light emitted from the semiconductor light emitting element.

【0002】 [0002]

【従来の技術】図5は、発光ダイオードチップから照射される光の波長を蛍光体によって変換する従来の発光ダイオード装置の断面図を示す。 BACKGROUND OF THE INVENTION Figure 5 shows a cross-sectional view of a conventional light emitting diode device that converts a wavelength of light emitted from the light emitting diode chip by the phosphor. 図5に示す発光ダイオード装置(1)では、カソード側のリードとしての配線導体(3)のカップ部(3a)の底面(3b)に発光ダイオードチップ(2)が固着され、ボンディングワイヤ(5)により発光ダイオードチップ(2)のカソード電極はカソード側の配線導体(3)の上端部(9a)に接続される。 In the light-emitting diode device shown in FIG. 5 (1), the cup portion of the cathode side of the lead as the wiring conductor (3) light-emitting diode chip (2) to the bottom (3b) of (3a) is fixed, the bonding wire (5) the cathode electrode of the LED chip (2) is connected to the upper end portion of the cathode side of the wiring conductor (3) (9a) by. また、発光ダイオードチップ(2)のアノード電極はボンディングワイヤ(6)によりアノード側のリードとしての配線導体(4)の上端部(9b)に接続される。 Also connected to the upper end portion of the anode electrode wiring conductor as a bonding wire (6) of the anode-side lead of the light emitting diode chip (2) (4) (9b). カップ部(3a)に固着された発光ダイオードチップ(2)は、カップ部(3a)内に充填され且つ蛍光物質が混入された光透過性の保護樹脂(7)により被覆される。 LED chip fixed to the cup portion (3a) (2) is and the fluorescent substance is filled into the cup portion (3a) is covered by a mixed light transparent protective resin (7). 発光ダイオードチップ(2)、カソード側の配線導体(3)のカップ部(3a)及び上端部(9 Light emitting diode chip (2), the cup portion of the cathode side of the wiring conductor (3) (3a) and the upper end (9
a)、アノード側の配線導体(4)の上端部(9b)、 a), the upper end portion of the anode side of the wiring conductor (4) (9b),
ボンディングワイヤ(5、6)は、更に光透過性の封止樹脂(8)内に封入される。 Bonding wires (5, 6) is further encapsulated in optically transparent sealing resin (8) within.

【0003】発光ダイオード装置(1)のカソード側の配線導体(3)とアノード側の配線導体(4)との間に電圧を印加し、発光ダイオードチップ(2)に通電すると、発光ダイオードチップ(2)から照射される光は、 [0003] applying a voltage between the cathode side of the wiring conductor (3) and the anode side of the wiring conductor of the light emitting diode device (1) (4), when energized light emitting diode chip (2), the light emitting diode chip ( light emitted from the 2)
保護樹脂(7)内を通り配線導体(3)のカップ部(3 Cup portion of the protective resin (7) in the street wiring conductor (3) (3
a)の側壁(3c)で反射した後に、透明な封止樹脂(8)を通り発光ダイオード装置(1)の外部に放出される。 After being reflected by the side walls of a) (3c), is discharged to the outside of the light-emission diode device a transparent sealing resin (8) (1). また、発光ダイオードチップ(2)の上面から放射されてカップ部(3a)の側壁(3c)で反射されずに直接に保護樹脂(7)及び封止樹脂(8)を通って発光ダイオード装置(1)の外部に放出される光もある。 The light emitting diode device through a direct protection resin (7) and the sealing resin (8) without being reflected by the side walls (3c) of the light emitting diode chip is radiated from the upper surface cup portion (2) (3a) ( light emitted outside of 1) also.
封止樹脂(8)の先端にはレンズ部(8a)が形成され、封止樹脂(8)内を通過する光は、レンズ部(8 The distal end of the sealing resin (8) lens unit (8a) is formed, the light, a lens portion that passes through the sealing resin (8) (8
a)によって集光されて指向性が高められる。 Directivity is condensed by a) is enhanced. 発光ダイオードチップ(2)の発光時に、発光ダイオードチップ(2)から照射される光は保護樹脂(7)内に混入された蛍光物質によって異なる波長に変換されて放出される。 During light emission of the light emitting diode chip (2), the light emitted from the light emitting diode chip (2) is released is converted to a different wavelength by the fluorescent material mixed into the protective resin (7) within. この結果、発光ダイオードチップ(2)から照射された光とは異なる波長の光が発光ダイオード装置(1) As a result, light having a wavelength different from the light emitted from the light emitting diode chip (2) is a light emitting diode device (1)
から放出される。 It is released from.

【0004】複数の発光ダイオード装置(1)が互いに隣接して配置されるとき、通電され且つ点灯された発光ダイオード装置(1)からの放射光によって隣接する他の発光ダイオード装置(1)の保護樹脂(7)中の蛍光体が励起されて、非通電時でも、あたかも点灯しているように見える不具合(偽灯)が生じるおそれがある。 [0004] When a plurality of light emitting diode device (1) are arranged adjacent to each other, the protection of the other light emitting diode device adjacent the radiation from the energized and illuminated light emitting diodes device (1) (1) phosphor in the resin (7) is excited, even when de-energized, there is a possibility that though seem lit failure (false light) occurs. 保護樹脂(7)がカップ部(3a)の上端部(9a)より上方に突出しないように保護樹脂(7)の充填量を調整すると、保護樹脂(7)により光の波長変換を行いつつ外部光による偽灯も防止できる。 When the protective resin (7) to adjust the filling amount of the upper end portion (9a) from the protective resin so as not to protrude upward (7) of the cup portion (3a), outside while performing wavelength conversion of light by the protective resin (7) false light by light can be prevented.

【0005】 [0005]

【発明が解決しようとする課題】蛍光体を含有する保護樹脂(7)で発光ダイオードチップ(2)を包囲し、更に全体を封止樹脂(8)で包囲する従来の発光ダイオード装置(1)では、実用上種々の問題が生ずる。 Surrounding the light emitting diode chip (2) with a protective resin containing a phosphor [0006] (7), further the whole conventional light-emitting diode device which surrounds a sealing resin (8) (1) in practical various problems. 第1 First
に、保護樹脂(7)及び封止樹脂(8)の耐環境性が必ずしも十分でないとき、保護樹脂(7)に配合できる蛍光体が特定の種類に限定される。 , When environmental resistance of the protective resin (7) and the sealing resin (8) is not necessarily sufficient, a phosphor that can be blended in the protective resin (7) is limited to a particular type. 即ち、一般に樹脂は水分を透過し、高湿度の雰囲気中に放置されると、時間の経過とともに樹脂の内部に水分が浸透する。 That is, in general the resin passes through the water, if left in an atmosphere of high humidity, moisture penetrates into the interior of the resin over time. この場合、 in this case,
侵入する水分によって分解又は変質して光波長変換機能が低下し又は消失する耐湿性の悪い蛍光体もある。 Decomposed or altered by the optical wavelength converting function by the moisture entering there is also moisture resistant poor phosphor reduced or eliminated. 例えば、水分によって加水分解する公知の代表的な硫化カルシュウム系の蛍光体は従来の発光ダイオード装置(1) For example, the phosphor of hydrolyzing known representative sulfide calcium system by moisture conventional light emitting diode device (1)
に使用できない。 Can not be used to.

【0006】また、水分のみならずナトリウム又は塩素等の不純物イオンも樹脂を透過し、発光ダイオードチップに有害な影響を与える。 [0006] Also, the impurity ions of sodium or chlorine or the like not only water passes through the resin, adversely affecting the light emitting diode chip. 従って、清浄な環境で製造された発光ダイオード装置(1)でも、不純物イオンを含む雰囲気中に放置すると、不純物イオンが樹脂の内部に次第に浸透して発光ダイオードチップ(2)の電気的特性が劣化する難点がある。 Accordingly, the light emitting diode device (1) which is manufactured in a clean environment But if left in an atmosphere containing an impurity ion, the electrical characteristics of the impurity ions is gradually penetrate into the resin-emitting diode chips (2) the degradation there is a drawback to. 特に、重大な問題は、有害不純物イオンが遊離する化学的に不安定な有機蛍光体も少なくない点である。 Particularly, serious problems is that harmful impurity ions is not less chemically unstable organic phosphors free. 従って従来の発光ダイオード装置(1)では、この種の有機蛍光体を使用することができない。 Therefore, in the conventional light emitting diode device (1), it is not possible to use an organic fluorescent material of this kind.

【0007】次に、発光ダイオードチップ(2)から発生する紫外線成分によって被覆樹脂及び蛍光体が劣化する問題がある。 [0007] Next, the light emitting diode chip (2) the coating resin and the phosphor with ultraviolet component generated from there is a problem of deterioration. 一般に、炭素、水素、酸素、窒素等の元素が網目状に結合した有機高分子化合物によって構成される保護樹脂(7)及び封止樹脂(8)は、紫外線が照射されると、有機高分子の繋ぎ目が切断され、各種の光学的特性及び化学的特性が劣化することが知られている。 In general, carbon, hydrogen, oxygen, and protects the resin by an organic polymer compound elements such as nitrogen is bound in a network form (7) and the sealing resin (8), when ultraviolet rays are irradiated, an organic polymer the joint of the cutting, various optical and chemical properties has been known to degrade. 例えばGaN(窒化ガリウム)の青色発光ダイオードチップは、可視光成分以外にも波長380nm以下の紫外波長域に発光成分を持つため、被覆樹脂は光強度の強い発光ダイオードチップの周囲から次第に黄変し、着色現象が発生する。 For example blue light emitting diode chip GaN (gallium nitride), in order to have a light-emitting component in the ultraviolet wavelength region of less than the wavelength 380nm other than visible light component, the coating resin gradually yellowed from the periphery of the strong emission diode chip light intensity , coloring phenomenon occurs. このため、発光ダイオードチップが発した可視光は着色部で吸収され減衰する。 Therefore, the visible light emitting diode chip is emitted is absorbed by the colored portion is attenuated. 更に、被覆樹脂の劣化に伴って耐湿性が低下すると共にイオン透過性が増大するため、発光ダイオードチップ自体も劣化し、その結果、発光ダイオード装置(1)の発光強度は相乗的に低減する。 Furthermore, since the ion permeability increases with moisture resistance decreases with deterioration of the coating resin, also deteriorates the light-emitting diode chip itself, as a result, light emission intensity of the light emitting diode device (1) is synergistically reduced.

【0008】また、被覆樹脂と同様に、紫外線によって劣化する蛍光体もある。 [0008] Similarly to the coating resin, there is also a phosphor to degradation by ultraviolet radiation. 例えば、硫化亜鉛系の蛍光体は放射線や紫外線によって光分解を起こし亜鉛が遊離するいわゆる「黒化」現象を起こすことが知られている。 For example, it is known to cause so-called "blackening" phenomenon zinc cause phosphors photolysis by radiation or ultraviolet zinc sulfide is liberated. 被覆樹脂中の蛍光体が光分解を生ずると、発光ダイオード装置(1)の発光強度は著しく低下する。 When the phosphor in the coating resin is caused to photolysis, the light emission intensity of the light emitting diode device (1) is significantly reduced.

【0009】紫外線による被覆樹脂及び蛍光体の劣化を防止するため、被覆樹脂中に紫外線吸収物質を混入する方法も考えられるが、可視光成分自体を吸収せず、被覆樹脂本来の特性に悪影響を与えない紫外線吸収物質を慎重に選定しなければならない。 [0009] In order to prevent degradation of the coating resin and the phosphor by UV is considered a method of mixing an ultraviolet absorbing material in the coating resin does not absorb visible light component itself, affect the coating resin intrinsic properties UV-absorbing material which does not give must be carefully selected. また、紫外線吸収物質を採用する際に、付加的に使用する材料及び作業工程が増加するので、製品価格が上昇する難点がある。 Further, when employing an ultraviolet absorbing material, because the material and the working step of additionally used is increased, there is a drawback that product prices rise.

【0010】更に、紫外線を発する紫外線発光ダイオードチップを使用できないため、蛍光体の材料選択と発光ダイオード装置の発光特性が大きな制限を受けることが第三の問題である。 Furthermore, since no available ultraviolet light-emitting diode chip that emits UV, it is the third problem which the emission characteristics of the light-emitting diode device and material selection of the phosphor is subjected to significant limitations. 蛍光ランプ又は水銀ランプに使用する紫外線で励起される紫外線用の蛍光体は、古くから開発・改良が行われた結果、現在では様々な発光波長分布を持つ安価で光変換効率の高い数多くの蛍光体が実用化されている。 Phosphor for UV excited by ultraviolet rays to be used for fluorescent lamps or mercury lamps as a result of development and improvements were made for a long time, a large number of fluorescent high light conversion efficiency at low cost with a variety of emission wavelength distribution in the current body has been put into practical use. 紫外線発光ダイオードチップと紫外線用の蛍光体を組み合わせると、一層明るく且つ変化に富む色調の発光ダイオード装置が得られると予想される。 Combining ultraviolet light emitting diode chip and a phosphor for UV, it is expected color tone of the light emitting diode device can be obtained rich in brighter and changes. しかしながら、紫外線により樹脂が劣化する従来の発光ダイオード装置では、紫外線発光ダイオードチップを使用できず、優れた蛍光体を利用できない。 However, the conventional light emitting diode device in which the resin is deteriorated by ultraviolet rays can not be used an ultraviolet light emitting diode chip, unavailable excellent phosphor.

【0011】第四の問題は、耐熱性が低い被覆樹脂が黄変・着色するため、発光ダイオードチップから照射された光が被覆樹脂を通過する際に減衰する点にある。 [0011] The fourth problem is that heat resistance is low coating resin is yellow-colored, in that the light emitted from the light emitting diode chip is attenuated when passing through the coating resin. 例えば順方向電圧が高いGaN(窒化ガリウム)の青色発光ダイオードチップは、比較的低い順方向電流でも電力損失が大きく、作動時にチップ温度はかなり上昇する。 For example blue light emitting diode chip of the forward voltage is high GaN (gallium nitride), the power loss at a relatively low forward current is large, the chip temperature is considerably increased during operation. 一般に、樹脂は高温に加熱されると次第に劣化して黄変・ In general, varying the resin is deteriorated gradually when heated to a high temperature yellow,
着色を起こすことが知られている。 To cause coloring is known. 従ってGaNの発光ダイオードチップを従来の発光ダイオード装置に用いると、高温の発光ダイオードチップと接する部分から樹脂が次第に黄変・着色するため、発光ダイオード装置(1)の外観品質と発光強度は次第に低下する。 Therefore the use of GaN light emitting diode chip to a conventional light emitting diode device, since the resin from the portion in contact with the hot emitting diode chip gradually yellow coloring, appearance quality and emission intensity of the light emitting diode device (1) gradually decreases to. このように、従来の発光ダイオード装置では、蛍光体を樹脂中に配合すると前記問題が生じ、このため選択する材料種類の減少、信頼性の低下、光変換機能の不完全性、製品価格の上昇を招来する原因となる。 Thus, in the conventional light-emitting diode device, the phosphor occurs the and blended into the resin problems, material type of reduction that selected for this, decrease in reliability, imperfection of light conversion function, increase product prices cause to lead to.

【0012】本発明は、耐環境性及び耐紫外線性を有する半導体発光装置を提供することを目的とする。 The present invention aims to provide a semiconductor light-emitting device having environmental resistance and UV resistance.

【0013】 [0013]

【課題を解決するための手段】本発明による半導体発光装置は、一対の配線導体(3、4)と、一対の配線導体(3、4)の一方の端部に固着された半導体発光素子(2)と、半導体発光素子(2)を被覆する光透過性の絶縁物封止体とを備えている。 The semiconductor light-emitting device according to the present invention SUMMARY OF] The pair of the wiring conductor (3, 4), a pair of wiring conductors (3, 4) of one of the semiconductor light emitting element fixed to an end portion ( and 2), and a light-transmitting insulating material sealing body covering the semiconductor light emitting element (2). ガラス層(10)により構成される。 Composed of glass layer (10). 半導体発光素子(2)から照射される光に対して光透過性を有し且つ半導体発光素子(2)から照射される光を吸収して他の発光波長に変換する蛍光物質(10a)をガラス層(10)中に混入させる。 Glass phosphor (10a) for converting the other emission wavelength by absorbing the light emitted from and semiconductor light-emitting device having a light transparent to light irradiated (2) from the semiconductor light emitting element (2) It is mixed into the layer (10). 半導体発光素子(2)の発光をガラス層(10)中の蛍光物質(10a)によって所望の発光波長に変換し、半導体発光素子(2)を包囲するガラス層(10)を通して外部に放出される。 The light emission of the semiconductor light emitting element (2) into a desired emission wavelength by the fluorescent material in the glass layer (10) (10a), is emitted to the outside through the glass layer surrounding the semiconductor light emitting element (2) (10) .

【0014】金属アルコキシド(テトラメトキシシラン、テトラエトキシシラン等)を出発原料とする塗布形ガラス材料又はセラミック前駆体ポリマー(ペルヒドロポリシラザン等)等から成る塗布型ガラス材料は、摂氏150度前後で焼成可能であり、低温領域でのガラス層の形成が可能である。 [0014] Metal alkoxide (tetramethoxysilane, tetraethoxysilane, etc.) coating type glass material consisting of a coating-type glass material or a ceramic precursor polymer as a starting material (perhydropolysilazane etc.) or the like, calcination at about 150 ° C is possible, it is possible to form a glass layer in a low temperature range. これらの塗布型ガラス材料は通常は液状であるが、空気中又は酸素雰囲気中で加熱すると、成分の分解又は酸素の吸収によりSiO 2 (酸化珪素)のシロキサン(siloxane)結合を主体とした透明な固形ガラス層を生成する。 These coating type glass material generally is a liquid, but when heated in air or an oxygen atmosphere, a clear composed mainly of siloxane (siloxane) bonds of SiO 2 (silicon oxide) by absorption of decomposition or oxygen components to produce a solid glass layer. これらのガラス材料に蛍光物質(10a)粉末を混合して半導体発光素子(2)の周囲に塗布すれば、光変換作用のみならず、下記の優れた特性を兼ねそなえた蛍光物質(10a)含有ガラス層(10)を形成することができる。 If applied around these glass materials to the fluorescent substance (10a) semiconductor light emitting device by mixing powders (2), not only light conversion effect only, fluorescent substance (10a) containing equipped serves excellent characteristics below it is possible to form the glass layer (10). [1] 耐湿性に優れ、内部に水分を浸透させず、半導体発光素子(2)及び蛍光物質(10a)を劣化させない。 [1] excellent moisture resistance, internal without penetration of moisture, does not degrade the semiconductor light emitting element (2) and fluorescent substance (10a). [2] 有害イオンの浸透を防ぐイオンバリア効果が高いため、発光ダイオード装置の外部や蛍光物質(10a) [2] prevents the penetration of harmful ion has high ion barrier effect, light-emitting diode device of the external and fluorescent substance (10a)
からの有害イオンで発光ダイオードチップを劣化させない。 It does not degrade the light emitting diode chip harmful ions from. [3] 紫外線耐性に優れ、高温環境下又は紫外線発光下でも黄変・着色を起こさず、半導体発光素子(2)の発光を減衰させない。 [3] excellent UV resistance, without causing yellowing coloring even under high temperature environment or ultraviolet light, does not attenuate the light emission of the semiconductor light emitting element (2). [4] ガラス中の珪素原子が金属又はセラミックの表面酸化物層の酸素原子と強固に結合するので、半導体発光素子(2)、配線導体(3、4)又は酸化物系無機蛍光物質(10a)との密着性がよい。 [4] Since the silicon atoms in the glass is strongly bonded with an oxygen atom of a metal or ceramic surface oxide layer, the semiconductor light emitting element (2), the wiring conductor (3, 4) or oxide inorganic fluorescent substance (10a ) good adhesion to the. [5] 配線導体(3、4)のカップ部(3a)内全体に塗布した塗布型ガラス材料が固化する時、添加した蛍光物質(10a)粉末が核となるので、厚塗りをしてもクラックが生じにくい。 [5] When the cup portion (3a) in coating type glass material applied to the entire of the wiring conductor (3, 4) is solidified, the fluorescent substance (10a) powder added is the core, even if the thick coating crack is less likely to occur.

【0015】このように、ガラス層(10)を使用することにより従来の発光ダイオード装置の種々の弱点を克服でき、安価で信頼性の高い、蛍光物質(10a)による波長変換機能を有する半導体発光装置を得ることができる。 [0015] Thus, various weaknesses of the conventional light-emitting diode device by using glass layer (10) can be overcome, and reliable low cost, a semiconductor light emission having a wavelength converting function by the fluorescent substance (10a) it can be obtained device.

【0016】本発明の実施の形態では、ガラス層(1 [0016] In the embodiment of the present invention, the glass layer (1
0)は、金属アルコキシドを出発原料とする塗布形ガラス材料又はセラミック前駆体ポリマー等から成る塗布形ガラス材料より選択され、摂氏150度前後の温度で焼成可能である。 0) is selected from the applied-shaped glass material formed of the metal alkoxide from the coating-shaped glass material or a ceramic precursor polymer or the like as the starting material, it is possible calcined at a temperature of around 150 degrees Celsius. ガラス層(10)は、シロキサン(silo Glass layer (10) is a siloxane (silo
xane)結合を主体とする透明な固形ガラス層で、空気中又は酸素雰囲気中で加熱されたとき、成分の分解又は酸素の吸収によりSiO 2 (酸化珪素)のシロキサン結合を発生する。 Xane) a transparent solid glass layer mainly comprising binding, when heated in air or an oxygen atmosphere to produce a siloxane bond of SiO 2 (silicon oxide) by absorption of decomposition or oxygen components. 半導体発光素子(2)の上面に形成された電極(2a、2b)と一対の配線導体(3、4)とはボンディングワイヤ(5、6)により電気的に接続され、ガラス層(10)は半導体発光素子(2)、電極(2a、 Top electrodes formed of the semiconductor light emitting element (2) (2a, 2b) and the pair of the wiring conductor (3, 4) are electrically connected by bonding wires (5,6), the glass layer (10) The semiconductor light emitting element (2), electrodes (2a,
2b)及び電極(2a、2b)に接続されたボンディングワイヤ(5、6)の端部を被覆する。 2b) and the electrodes (2a, covering the end of the bonding wire connected to 2b) (5, 6). 一対の配線導体(3、4)の一方の端部にカップ部(3a)が形成され、半導体発光素子(2)はカップ部(3a)の底部(3b)に接着される。 A pair of cup portions (3a) is formed at one end portion of the wiring conductor (3, 4), the semiconductor light emitting element (2) is glued to the bottom of the cup portion (3a) (3b).

【0017】絶縁性基板(11)の一方の主面にカップ部(3a)と、絶縁性基板(11)の一方の主面に沿って互いに反対方向に延びる一対の配線導体(3、4)とが形成され、カップ部(3a)の底部(3b)にて一対の配線導体(3、4)の一方に半導体発光素子(2)が固着される。 The cup portion on one principal surface of the insulating substrate (11) and (3a), along one of the main surfaces of the insulating substrate (11) extending in opposite directions a pair of wiring conductors (3,4) : it is formed, while the semiconductor light emitting element (2) is fixed to the bottom of the cup portion (3a) (3b) a pair of wire conductors at (3,4). ガラス層(10)はカップ部(3a)の上端部(3d)から突出しない。 Glass layer (10) does not protrude from the upper end of the cup portion (3a) (3d). 配線導体(3、4)は絶縁性基板(11)の一方の主面から側面に沿って他方の主面に延びる。 Wiring conductors (3, 4) extends on the other main surface along the sides from one main surface of the insulating substrate (11). ガラス層(10)は更に封止樹脂(8) Glass layer (10) further sealing resin (8)
により封止され、半導体発光素子(2)から照射される光は、ガラス層(10)内を通過した後、封止樹脂(8)の外部に放出される。 Sealed with, light emitted from the semiconductor light emitting element (2) passes through the glass layer (10), it is discharged to the outside of the sealing resin (8).

【0018】半導体発光素子(2)から放射された光成分の一部がガラス層(10)に達してガラス層(10) The glass layer reaches the glass layer portion of the emitted light ingredient from the semiconductor light emitting element (2) (10) (10)
内で異なる波長に波長変換された光と、波長変換されない半導体発光素子(2)からの光成分とが混合して封止樹脂(8)を通して外部に放出される。 A light whose wavelength is converted into a different wavelength in the inner, is discharged to the outside through the sealing resin (8) and the optical components are mixed from the semiconductor light emitting element which is not wavelength-converted (2). 特定の発光波長を吸収する光吸収物質、半導体発光素子(2)の発光を散乱する光散乱物質又はガラス層(10)のクラックを防止する結合材をガラス層(10)内に配合してもよい。 Light absorbing material that absorbs a specific emission wavelength, even if the light-scattering material or a glass layer to scatter the light emission of the semiconductor light emitting element (2) a coupling member for preventing the crack (10) incorporated into the glass layer (10) good.

【0019】 [0019]

【発明の実施の形態】以下、発光ダイオード装置に適用した本発明による半導体発光装置の実施の形態を図1〜 DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, FIG. 1 to the embodiment of the semiconductor light-emitting device according to the present invention applied to a light emitting diode device
図4について説明する。 Figure 4 will be described. 図1〜図4に示す実施の形態では、図5に示す箇所と同一の部分には同一の符号を付し、説明を省略する。 In the embodiment shown in FIGS. 1 to 4, the same reference numerals are assigned to portions that are the same as the parts shown in FIG. 5, the description thereof is omitted.

【0020】図1は、本発明による発光ダイオード装置(20)の第1の実施の形態を示す断面図である。 [0020] Figure 1 is a sectional view showing a first embodiment of a light emitting diode device according to the present invention (20). 発光ダイオード装置(20)ではカップ部(3a)に固着された発光ダイオードチップ(2)は、絶縁物封止体として蛍光物質(10a)を含有するガラス層(10)により被覆され、更に封止樹脂(8)により被覆される。 Light emitting diode device (20) in the light-emitting diode chip is secured to the cup portion (3a) (2) is covered by a glass layer containing a fluorescent substance (10a) as the insulator sealing body (10), further sealing It is covered with a resin (8). 製造の際に、発光ダイオードチップ(2)の上部より蛍光物質(10a)を含む塗布型ガラス材料をカップ部(3 During manufacture, the cup portion coating type glass material including phosphor (10a) from the upper portion of the LED chip (2) (3
a)内に注入して、約摂氏150度の温度で焼成し、蛍光物質(10a)を含有するガラス層(10)を固化形成した後に、配線導体(3、4)の端部全体を透明な封止樹脂(8)で封止する。 Was injected into a), about fired at a temperature of 150 degrees Celsius, after the glass layer containing a fluorescent substance (10a) and (10) solidified form, transparent the entire end of the wiring conductor (3, 4) sealed with a sealing resin (8), such. ガラス層(10)の焼成温度は発光ダイオードチップ(2)の融点よりも十分に低い。 Baking temperature of the glass layer (10) is sufficiently lower than the melting point of the light emitting diode chip (2).

【0021】発光ダイオード装置(20)の配線導体(3、4)間に電圧を印加して発光ダイオードチップ(2)に通電して発光ダイオードチップ(2)を発光させると、ガラス層(10)内の蛍光物質(10a)によってその一部又は全部がその発光波長と異なる他の波長に変換された後、封止樹脂(8)の先端部に形成されたレンズ部(8a)によって集光されて発光ダイオード装置(20)の外部に放出される。 [0021] When the light emitting diode is a light-emitting device (20) of the wiring conductor (3, 4) light emitting diode chip is energized by applying a voltage to a light-emitting diode chip (2) between (2), the glass layer (10) after fluorescent substance (10a) partially or entirely by the inner is converted into other different wavelengths and the emission wavelength, is condensed by the lens portion formed on the tip portion of the sealing resin (8) (8a) It is discharged to the outside of the light emitting diode device (20) Te. 例えば、半導体発光素子には発光波長のピークが約440nmから約470n For example, about the peak of the emission wavelength of about 440nm in the semiconductor light emitting element 470n
mのGaN系の青色の発光ダイオードチップ(2)を用い、蛍光物質(10a)には付活剤としてCe(セリウム)を約6mol%添加したYAG(イットリウム・アルミニウム・ガーネット、化学式Y 3 Al 512 、励起波長のピーク約450nm、発光波長のピーク約540n using m of GaN-based blue light emitting diode chip (2), YAG is a fluorescent substance (10a) was added Ce (the cerium) about 6 mol% as an activator (yttrium aluminum garnet, formula Y 3 Al 5 O 12, the peak excitation wavelength of approximately 450 nm, the peak emission wavelength of about 540n
mの黄緑色光)を用いる。 m using the yellow-green light).

【0022】ガラス層(10)は、YAG蛍光物質(1 The glass layer (10) is, YAG fluorescent substance (1
0a)の粉末状微細結晶粒を塗布型ガラス材料に適量混合して成るガラス混合物を作成し、これをカップ部(3 Powdery fine crystal grains to create a glass mixture formed by appropriate amount to the coating type glass material, which cup portion 0a) (3
a)内にカップ部(3a)の上端部(3d)から突出しない量で注入した後に焼成して得られる。 Obtained by baking after implantation in an amount that does not protrude from the upper end (3d) of the cup portion (3a) in a).

【0023】一方、封止樹脂(8)は、液状で透明なエポキシ樹脂を成形型に注入した後に発光ダイオードチップ(2)、ボンディングワイヤ(5、6)、ガラス層(10)を固着した配線導体(3、4)の端部をこのエポキシ樹脂中に浸漬し且つ位置決め治具によりエポキシ樹脂中の所定の位置に固定し、エポキシ樹脂を加熱し硬化して得られる。 On the other hand, the sealing resin (8), the light emitting diode chip transparent epoxy resin in liquid state after injection into the mold (2), bonding wires (5, 6), wiring fixed glass layer (10) conductors (3, 4) end is fixed in place in the epoxy resin by the immersed and positioning jig in this epoxy resin, obtained by curing by heating the epoxy resin. 発光ダイオード装置(20)から外部に放出される光の指向角を広げるため、必要に応じて粉末シリカ等の散乱剤を封止樹脂(8)に混合させてもよい。 To broaden the directivity angle of light emitted from the light emitting diode device (20) to the outside, scattering agent in powder such as silica may be mixed in the sealing resin (8) as required. 本実施の形態では、YAG蛍光物質(10a)の波長変換効率の最大値が比較的高く、発光ダイオードチップ(2)の発光波長とYAG蛍光物質(10a)の励起波長とが約450nmのピークでほぼ一致するため、実効波長変換効率の高い明るい発光ダイオード装置(2 In this embodiment, the maximum value of the wavelength conversion efficiency of the YAG phosphor (10a) is relatively high, the emission wavelength and a peak excitation wavelength of about 450nm of YAG fluorescent substance (10a) of the light-emitting diode chips (2) to approximately match the effective wavelength conversion efficient bright light emitting diode device (2
0)が得られる。 0) is obtained. また、YAG蛍光物質(10a)の結晶粒がガラス層(10)中に分散しているので、発光ダイオード装置(20)から外部に放出される光は、蛍光物質(10a)で波長変換された光成分以外に蛍光物質(10a)の結晶粒を透過せず波長変換されない本来の発光成分即ち発光ダイオードチップ(2)から照射された光成分も含まれる。 The crystal grains of the YAG fluorescent substance (10a) is so dispersed in the glass layer (10), light emitted outside from the light emitting diode device (20) is subjected to wavelength conversion by the fluorescent material (10a) original light emission component or light components emitted from the light emitting diode chip (2) are not wavelength-converted without transmitting the crystal grains of the fluorescent material (10a) in addition to the optical components are also included.

【0024】従って、発光波長ピーク約440nm〜約470nmの青色光である発光ダイオードチップ(2) [0024] Thus, a blue light emission wavelength peak of about 440nm~ about 470nm light emitting diode chips (2)
の発光成分と、半値幅約130nmの幅広い波長分布を持った発光波長ピーク約540nmの黄緑色光であるY A light emitting component, a yellow-green light emission wavelength peak of about 540nm having a broad wavelength distribution half width of about 130 nm Y of
AG蛍光物質(10a)の発光成分とが混合された白色光が発光ダイオード装置(20)から外部に放出される。 The white light emitting components are mixed AG fluorescent substance (10a) is released to the outside from the light emitting diode device (20). この場合、塗布型ガラス材料に混合するYAG蛍光物質(10a)粉末の量を調整し、ガラス層(10)内の分布濃度を変更することにより発光ダイオード装置(20)の発光色の色調を調整することができる。 In this case, by adjusting the amount of YAG fluorescent substance (10a) powder to be mixed with the coating type glass material, adjust the color tone of the emission color of the light-emitting diode device by changing the distribution density of the glass layer (10) (20) can do. また、YAG蛍光物質(10a)の製造時に適当な添加物を適量添加して結晶構造を一部変更して発光波長分布をシフトすると、発光ダイオード装置(20)の発光色を更に異なる色調に調整することができる。 Further, when shifting the emission wavelength distribution partially modified the appropriate amount to the crystal structure of suitable additives in the production of YAG fluorescent substance (10a), adjusted to further different shades the light emission color of the light emitting diode device (20) can do. 例えばGa For example, Ga
(ガリウム)又はLu(ルテチウム)を添加して短波長側にシフトし、Gd(ガドリニウム)を添加して長波長側にシフトすることができる。 (Gallium) or shifted by adding to the short wavelength side of Lu (lutetium) can be shifted to the long wavelength side by adding Gd (gadolinium).

【0025】本発明では更に光学的特性や作業性を向上するため、例えば下記の改善も可能である。 [0025] To further improve the optical characteristics and workability in the present invention, for example, can be improved below. [1] ガラス層(10)内に散乱剤を混入することで発光ダイオードチップ(2)の光を散乱させることにより蛍光物質(10a)に当たる発光ダイオードチップ(2)の光量が増加し、波長変換効率を向上すると共に、発光ダイオード装置(20)から外部に放出される光の指向角を広げることができる。 [1] glass layer (10) amount of the fluorescent material by scattering the light emitting diode chip (2) by the incorporation of scattering agent emitting diode chip striking the (10a) (2) is increased in the wavelength conversion with improved efficiency, it is possible to widen the beam angle of light emitted outside from the light emitting diode device (20). [2] ガラス層(10)のクラックを防止する結合材を配合する。 [2] formulating a binder to prevent cracking of the glass layer (10). [3] 塗布型ガラス材料の粘度を高くする。 [3] increasing the viscosity of the coating type glass material. [4] 塗布型ガラス材料の使用量を減らす。 [4] reduce the amount of coating type glass material.

【0026】このような場合は、図2に示すように、塗布型ガラス材料に蛍光物質(10a)の粉末とともにシリカ、酸化チタン等のセラミック粉末(10b)を目的に応じて適量混合すればよい。 [0026] In this case, as shown in FIG. 2, the silica together with the powder of the fluorescent material (10a) on the coating type glass material, a ceramic powder (10b) such as titanium oxide may be mixed with an appropriate amount in accordance with the intended .

【0027】図2に示す本発明の第2の実施の形態では、混合するセラミック粉末の種類及び量によって得られる効果が異なる。 [0027] In the second embodiment of the present invention shown in FIG. 2, the effect obtained by the type and amount of the ceramic powder to be mixed are different. 例えばセラミック粉末がシリカの場合は本来ガラス層(10)と同じ物質なので[1]の効果は少なく[2][3]の効果が大きい。 For example the effect of the effect of so original when the ceramic powder is silica is the same material as the glass layer (10) [1] is less [2] [3] is large. しかしセラミック粉末が酸化チタンの場合は[1]〜[3]の効果とも大きい。 However the ceramic powder is greater with the effect of the case of titanium oxide [1] to [3].
従って混合するセラミック粉末は目的によって単一でも複数の種類を組み合わせても良い。 Therefore the ceramic powder to be mixed may be used in combination of two or more kinds in a single depending on the purpose.

【0028】また、本発明では紫外線で劣化しないガラスを用いるので、半導体発光素子に紫外線発光ダイオードチップ(2)も用いることができる。 Further, since a glass which is not degraded by ultraviolet rays in the present invention, the ultraviolet light emitting diode chip (2) to the semiconductor light-emitting device can also be used. 従って、従来の発光ダイオード装置よりも明るく且つ変化に富む色調の発光ダイオード装置(20)を実現することができる。 Accordingly, it is possible to realize the light emitting diode device of the color-rich and change brighter than conventional LED device (20).

【0029】本発明による発光ダイオード装置(20) The light emitting diode device according to the present invention (20)
の第3の実施の形態を図3に示す。 It shows a third embodiment of Figure 3.

【0030】例えば、約360nm〜380nmの発光ピーク波長を有する紫外線を発生するGaN系発光ダイオードチップ(2)と、励起ピーク波長約360nm、 [0030] For example, a GaN-based light emitting diode chip which generates ultraviolet radiation having a peak emission wavelength of about 360nm~380nm (2), excitation peak wavelength of about 360 nm,
発光ピーク波長約543nmのGa及びTb(テルビウム)付活のY 2 SiO 5の蛍光物質(10a)とを使用すると、半値幅約12nmの非常にシャープな発光分布を持つ緑色発光ダイオード装置(20)が得られる。 Emission peak wavelength of about 543nm of Ga and Tb (terbium) Using the activated of Y 2 SiO 5 phosphor (10a), a green light-emitting diode device having a very sharp emission distribution half width of about 12 nm (20) It is obtained.

【0031】発光ダイオードチップと蛍光物質(10 The light emitting diode chip and a fluorescent substance (10
a)の前記組合わせは例示に過ぎず、紫外線発光ダイオードチップ(2)の発光波長に適合する励起波長分布を持ち且つ波長変換効率が高ければ、いかなる蛍光物質(10a)でも使用できる。 The combination of a) are illustrative only, higher and the wavelength conversion efficiency have compatible excitation wavelength distribution to the emission wavelength of the ultraviolet light emitting diode chip (2), it can be used in any fluorescent material (10a). 例えばハロ燐酸カルシュウム系、燐酸カルシュウム系、珪酸塩系、アルミン酸塩系、タングステン酸塩系等の蛍光物質(10a)から所望の特性を持つ蛍光物質(10a)を選択することができる。 For example halophosphate calcium-based phosphate calcium-based, silicate, aluminate, can be selected fluorescent substance (10a) having the desired characteristics from the fluorescent substance (10a) of tungstate-based and the like.

【0032】また、第2の実施の形態と同様に、第3の実施の形態の発光ダイオード装置(20)のガラス層(10)にもセラミック粉末を混合することは可能である。 Further, as in the second embodiment, it is possible to mix the ceramic powder to the glass layer of the third embodiment of the light emitting diode device (20) (10).

【0033】前記の実施の形態では、カップ部(3a) [0033] In the above embodiment, the cup portion (3a)
の上端部より上方に突出しないようにガラス層(10) Glass layer so as not to protrude above the upper end of (10)
の充填量を調整すれば、隣接して他の発光ダイオード装置(20)を設置しても偽灯を発生しない。 By adjusting the filling amount, does not generate false lighting even adjacent installing another light-emitting diode device (20).

【0034】図4は、チップ形発光ダイオード装置(2 [0034] Figure 4 is a chip type light emitting diode device (2
0)に適用した本発明の他の実施の形態を示す。 Shows another embodiment of the present invention applied to 0). チップ形発光ダイオード装置(20)では、絶縁性基板(1 In Chip emitting diode device (20), an insulating substrate (1
1)の一方の主面にカップ部(3a)と、相互に離間した配線導体(3、4)とが形成され、配線導体(3、 Cup portion on one principal surface of 1) and (3a), mutually spaced wire conductors and (3,4) are formed, the wiring conductor (3,
4)の一方の端部は、カップ部(3a)内に配置される。 One end of the 4) is disposed in the cup portion (3a). 発光ダイオードチップ(2)はカップ部(3a)の底部(3b)にて配線導体(3)に接着剤(12)を介して固着される。 Light emitting diode chip (2) is secured with an adhesive (12) the bottom of the cup portion (3a) at (3b) to the wiring conductor (3). 配線導体(3、4)の他方の端部は、 The other end of the wiring conductor (3, 4),
絶縁性基板(11)の側面及び他方の主面に延びて配置される。 They are arranged to extend on the side surface and the other main surface of the insulating substrate (11). 発光ダイオードチップ(2)のカソード電極(2a)及びアノード電極(2b)はそれぞれボンディングワイヤ(5、6)により配線導体(3、4)に接続される。 A cathode electrode (2a) and an anode electrode of the LED chip (2) (2b) is connected to the wiring conductor (3, 4) by bonding wires (5, 6), respectively. 発光ダイオードチップ(2)、カップ部(3 Light emitting diode chip (2), the cup portion (3
a)、ボンディングワイヤ(5、6)、配線導体(3、 a), bonding wires (5, 6), the wiring conductor (3,
4)の一方の端部側はガラス層(10)により被覆され、絶縁性基板(11)の一方の主面に形成された台形状断面の封止樹脂(8)によって更に被覆される。 One end side of 4) is covered by a glass layer (10) is further covered by an insulating substrate (11) one main surface to the formed trapezoidal cross-section of the sealing resin (8). 図4 Figure 4
の発光ダイオード装置(20)でも、発光ダイオードチップ(2)から照射された光の一部がガラス層(10) Emitting diode device (20) also emitting diode chips (2) glass layer part of the light emitted from (10)
の蛍光物質(10a)によって発光波長が変換され、図1の発光ダイオード装置と同様の作用効果が得られる。 Fluorescence emission wavelength depending on the material (10a) is converted to the same effects as the light emitting diode device of FIG. 1 can be obtained.
尚、図4の発光ダイオードにおいても、ガラス層(1 Also in the light emitting diode of FIG. 4, the glass layer (1
0)にセラミック粉末を混入することができる。 0) can be mixed with the ceramic powder. また、 Also,
図1〜図4の発光ダイオードでは、蛍光物質(10a) The light emitting diode of FIGS. 1-4, a fluorescent substance (10a)
をガラス層(10)内に均一に分散させているが、不均一に分散させることもできる。 The but was uniformly dispersed in the glass layer (10) can also be unevenly distributed. 例えば、LEDチップ(3a)側で蛍光物質(10a)の混入濃度を増加してもよい。 For example, the LED chip (3a) side may be increased contamination concentration of the fluorescent substance (10a).

【0035】 [0035]

【発明の効果】前記のように、本発明では、有害物質の浸透を防ぎ且つ紫外線耐性に優れるガラス層により半導体発光素子を被覆するので、湿度、温度又は紫外線等によってガラス層や半導体発光素子に劣化を起こさず、耐環境性が向上し、蛍光物質による発光波長変換機能を有しつつも信頼性が高く安価な半導体発光装置を得ることができる。 [Effect of the Invention] As described above, in the present invention, since covering the semiconductor light-emitting element by a glass layer which is excellent in and UV-resistant to prevent penetration of harmful substances, humidity, the glass layer and the semiconductor light-emitting device by temperature or UV rays without causing degradation, improved environmental resistance, while having an emission wavelength converting function by the fluorescent substance can also be reliable obtain highly inexpensive semiconductor light-emitting device.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】 発光ダイオード装置に適用した本発明による半導体発光装置の断面図 Figure 1 is a cross-sectional view of a semiconductor light-emitting device according to the present invention applied to a light emitting diode device

【図2】 本発明の第2の実施の形態を示す部分断面図 Partial cross-sectional view showing a second embodiment of the present invention; FIG

【図3】 本発明の第3の実施の形態を示す部分断面図 3 partial cross-sectional view showing the embodiment of the invention; FIG

【図4】 チップ型発光ダイオード装置に適用した本発明の実施の形態を示す断面図 4 is a cross-sectional view showing an embodiment of the present invention applied to a chip type light emitting diode device

【図5】 従来の発光ダイオード装置の断面図 FIG. 5 is a cross-sectional view of a conventional light emitting diode device

【符号の説明】 DESCRIPTION OF SYMBOLS

(2)・・半導体発光素子、 (2a、2b)・・電極、 (3、4)・・配線導体、 (3a)・・カップ部、 (3b)・・底部、 (3c)・・側壁、(3 (2) ... semiconductor light-emitting element, (2a, 2b) ... electrode, (3,4) ... wiring conductors, (3a) ... cup portion, (3b) ... the bottom, (3c) ... side wall, (3
d)・・上端部、 (5、6)・・ボンディングワイヤ、 (8)・・封止樹脂、 (10)・・ガラス層、 d) ... upper end, (5,6) ... bonding wire (8) ... sealing resin (10) .. glass layer,
(11)・・絶縁性基板、 (11) ... the insulating substrate,

───────────────────────────────────────────────────── ────────────────────────────────────────────────── ───

【手続補正書】 [Procedure amendment]

【提出日】平成11年2月12日 [Filing date] 1999 February 12,

【手続補正1】 [Amendment 1]

【補正対象書類名】明細書 [Correction target document name] specification

【補正対象項目名】全文 [Correction target item name] full text

【補正方法】変更 [Correction method] change

【補正内容】 [Correction contents]

【書類名】 明細書 [Document name] specification

【発明の名称】 半導体発光装置及びその製法 [Title of the Invention A semiconductor light-emitting device and its manufacturing method

【特許請求の範囲】 [The claims]

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、発光ダイオード装置、特に半導体発光素子から照射される光を波長変換して外部に放出する半導体発光装置に関する。 The present invention relates to a light-emitting diode device, a semiconductor light emitting device that emits to the outside, especially wavelength conversion of light emitted from the semiconductor light emitting element.

【0002】 [0002]

【従来の技術】図5は、発光ダイオードチップから照射される光の波長を蛍光体によって変換する従来の発光ダイオード装置の断面図を示す。 BACKGROUND OF THE INVENTION Figure 5 shows a cross-sectional view of a conventional light emitting diode device that converts a wavelength of light emitted from the light emitting diode chip by the phosphor. 図5に示す発光ダイオード装置(1)では、カソード側のリードとしての配線導体(3)のカップ部(3a)の底面(3b)に発光ダイオードチップ(2)が固着され、ボンディングワイヤ(5)により発光ダイオードチップ(2)のカソード電極はカソード側の配線導体(3)の上端部(9a)に接続される。 In the light-emitting diode device shown in FIG. 5 (1), the cup portion of the cathode side of the lead as the wiring conductor (3) light-emitting diode chip (2) to the bottom (3b) of (3a) is fixed, the bonding wire (5) the cathode electrode of the LED chip (2) is connected to the upper end portion of the cathode side of the wiring conductor (3) (9a) by. また、発光ダイオードチップ(2)のアノード電極はボンディングワイヤ(6)によりアノード側のリードとしての配線導体(4)の上端部(9b)に接続される。 Also connected to the upper end portion of the anode electrode wiring conductor as a bonding wire (6) of the anode-side lead of the light emitting diode chip (2) (4) (9b). カップ部(3a)に固着された発光ダイオードチップ(2)は、カップ部(3a)内に充填され且つ蛍光物質が混入された光透過性の保護樹脂(7)により被覆される。 LED chip fixed to the cup portion (3a) (2) is and the fluorescent substance is filled into the cup portion (3a) is covered by a mixed light transparent protective resin (7). 発光ダイオードチップ(2)、カソード側の配線導体(3)のカップ部(3a)及び上端部(9 Light emitting diode chip (2), the cup portion of the cathode side of the wiring conductor (3) (3a) and the upper end (9
a)、アノード側の配線導体(4)の上端部(9b)、 a), the upper end portion of the anode side of the wiring conductor (4) (9b),
ボンディングワイヤ(5、6)は、更に光透過性の封止樹脂(8)内に封入される。 Bonding wires (5, 6) is further encapsulated in optically transparent sealing resin (8) within.

【0003】発光ダイオード装置(1)のカソード側の配線導体(3)とアノード側の配線導体(4)との間に電圧を印加し、発光ダイオードチップ(2)に通電すると、発光ダイオードチップ(2)から照射される光は、 [0003] applying a voltage between the cathode side of the wiring conductor (3) and the anode side of the wiring conductor of the light emitting diode device (1) (4), when energized light emitting diode chip (2), the light emitting diode chip ( light emitted from the 2)
保護樹脂(7)内を通り配線導体(3)のカップ部(3 Cup portion of the protective resin (7) in the street wiring conductor (3) (3
a)の側壁(3c)で反射した後に、透明な封止樹脂(8)を通り発光ダイオード装置(1)の外部に放出される。 After being reflected by the side walls of a) (3c), is discharged to the outside of the light-emission diode device a transparent sealing resin (8) (1). また、発光ダイオードチップ(2)の上面から放射されてカップ部(3a)の側壁(3c)で反射されずに直接に保護樹脂(7)及び封止樹脂(8)を通って発光ダイオード装置(1)の外部に放出される光もある。 The light emitting diode device through a direct protection resin (7) and the sealing resin (8) without being reflected by the side walls (3c) of the light emitting diode chip is radiated from the upper surface cup portion (2) (3a) ( light emitted outside of 1) also.
封止樹脂(8)の先端にはレンズ部(8a)が形成され、封止樹脂(8)内を通過する光は、レンズ部(8 The distal end of the sealing resin (8) lens unit (8a) is formed, the light, a lens portion that passes through the sealing resin (8) (8
a)によって集光されて指向性が高められる。 Directivity is condensed by a) is enhanced. 発光ダイオードチップ(2)の発光時に、発光ダイオードチップ(2)から照射される光は保護樹脂(7)内に混入された蛍光物質によって異なる波長に変換されて放出される。 During light emission of the light emitting diode chip (2), the light emitted from the light emitting diode chip (2) is released is converted to a different wavelength by the fluorescent material mixed into the protective resin (7) within. この結果、発光ダイオードチップ(2)から照射された光とは異なる波長の光が発光ダイオード装置(1) As a result, light having a wavelength different from the light emitted from the light emitting diode chip (2) is a light emitting diode device (1)
から放出される。 It is released from.

【0004】複数の発光ダイオード装置(1)が互いに隣接して配置されるとき、通電され且つ点灯された発光ダイオード装置(1)からの放射光によって隣接する他の発光ダイオード装置(1)の保護樹脂(7)中の蛍光体が励起されて、非通電時でも、あたかも点灯しているように見える不具合(偽灯)が生じるおそれがある。 [0004] When a plurality of light emitting diode device (1) are arranged adjacent to each other, the protection of the other light emitting diode device adjacent the radiation from the energized and illuminated light emitting diodes device (1) (1) phosphor in the resin (7) is excited, even when de-energized, there is a possibility that though seem lit failure (false light) occurs. 保護樹脂(7)がカップ部(3a)の上端部(9a)より上方に突出しないように保護樹脂(7)の充填量を調整すると、保護樹脂(7)により光の波長変換を行いつつ外部光による偽灯も防止できる。 When the protective resin (7) to adjust the filling amount of the upper end portion (9a) from the protective resin so as not to protrude upward (7) of the cup portion (3a), outside while performing wavelength conversion of light by the protective resin (7) false light by light can be prevented.

【0005】 [0005]

【発明が解決しようとする課題】蛍光体を含有する保護樹脂(7)で発光ダイオードチップ(2)を包囲し、更に全体を封止樹脂(8)で包囲する従来の発光ダイオード装置(1)では、実用上種々の問題が生ずる。 Surrounding the light emitting diode chip (2) with a protective resin containing a phosphor [0006] (7), further the whole conventional light-emitting diode device which surrounds a sealing resin (8) (1) in practical various problems. 第1 First
に、保護樹脂(7)及び封止樹脂(8)の耐環境性が必ずしも十分でないとき、保護樹脂(7)に配合できる蛍光体が特定の種類に限定される。 , When environmental resistance of the protective resin (7) and the sealing resin (8) is not necessarily sufficient, a phosphor that can be blended in the protective resin (7) is limited to a particular type. 即ち、一般に樹脂は水分を透過し、高湿度の雰囲気中に放置されると、時間の経過と共に樹脂の内部に水分が浸透する。 That is, in general the resin passes through the water, when it is left in a high-humidity atmosphere, moisture in the resin over time to penetrate. この場合、侵入する水分によって分解又は変質して光波長変換機能が低下し又は消失する耐湿性の悪い蛍光体もある。 In this case, there is also a moisture resistance poor phosphor decomposed or altered by the optical wavelength converting function is reduced or eliminated by moisture intrusion. 例えば、水分によって加水分解する公知の代表的な硫化カルシウム系の蛍光体は従来の発光ダイオード装置(1)に使用できない。 For example, the phosphor of the known typical calcium sulfide-based hydrolyzed by water can not be used in the conventional light emitting diode device (1).

【0006】また、水分のみならずナトリウム又は塩素等の不純物イオンも樹脂を透過し、発光ダイオードチップに有害な影響を与える。 [0006] Also, the impurity ions of sodium or chlorine or the like not only water passes through the resin, adversely affecting the light emitting diode chip. 従って、清浄な環境で製造された発光ダイオード装置(1)でも、不純物イオンを含む雰囲気中に放置すると、不純物イオンが樹脂の内部に次第に浸透して発光ダイオードチップ(2)の電気的特性が劣化する難点がある。 Accordingly, the light emitting diode device (1) which is manufactured in a clean environment But if left in an atmosphere containing an impurity ion, the electrical characteristics of the impurity ions is gradually penetrate into the resin-emitting diode chips (2) the degradation there is a drawback to. 特に、重大な問題は、有害不純物イオンが遊離する化学的に不安定な有機蛍光体も少なくない点である。 Particularly, serious problems is that harmful impurity ions is not less chemically unstable organic phosphors free. 従って、従来の発光ダイオード装置(1)では、この種の有機蛍光体を使用することができない。 Therefore, the conventional light emitting diode device (1), it is not possible to use an organic fluorescent material of this kind.

【0007】次に、発光ダイオードチップ(2)から発生する紫外線成分によって被覆樹脂及び蛍光体が劣化する問題がある。 [0007] Next, the light emitting diode chip (2) the coating resin and the phosphor with ultraviolet component generated from there is a problem of deterioration. 一般に、炭素、水素、酸素、窒素等の元素が網目状に結合した有機高分子化合物によって構成される保護樹脂(7)及び封止樹脂(8)は、紫外線が照射されると、有機高分子の繋ぎ目が切断され、各種の光学的特性及び化学的特性が劣化することが知られている。 In general, carbon, hydrogen, oxygen, and protects the resin by an organic polymer compound elements such as nitrogen is bound in a network form (7) and the sealing resin (8), when ultraviolet rays are irradiated, an organic polymer the joint of the cutting, various optical and chemical properties has been known to degrade. 例えばGaN(窒化ガリウム)の青色発光ダイオードチップは、可視光成分以外にも波長380nm以下の紫外波長域に発光成分を持つため、被覆樹脂は光強度の強い発光ダイオードチップの周囲から次第に黄変し、着色現象が発生する。 For example blue light emitting diode chip GaN (gallium nitride), in order to have a light-emitting component in the ultraviolet wavelength region of less than the wavelength 380nm other than visible light component, the coating resin gradually yellowed from the periphery of the strong emission diode chip light intensity , coloring phenomenon occurs. このため、発光ダイオードチップが発した可視光は着色部で吸収され減衰する。 Therefore, the visible light emitting diode chip is emitted is absorbed by the colored portion is attenuated. 更に、被覆樹脂の劣化に伴って耐湿性が低下すると共にイオン透過性が増大するため、発光ダイオードチップ自体も劣化し、その結果、発光ダイオード装置(1)の発光強度は相乗的に低減する。 Furthermore, since the ion permeability increases with moisture resistance decreases with deterioration of the coating resin, also deteriorates the light-emitting diode chip itself, as a result, light emission intensity of the light emitting diode device (1) is synergistically reduced.

【0008】また、被覆樹脂と同様に、紫外線によって劣化する蛍光体もある。 [0008] Similarly to the coating resin, there is also a phosphor to degradation by ultraviolet radiation. 例えば、硫化亜鉛系の蛍光体は放射線や紫外線によって光分解を起こし亜鉛が遊離するいわゆる「黒化」現象を起こすことが知られている。 For example, it is known to cause so-called "blackening" phenomenon zinc cause phosphors photolysis by radiation or ultraviolet zinc sulfide is liberated. 被覆樹脂中の蛍光体が光分解を生ずると、発光ダイオード装置(1)の発光強度は著しく低下する。 When the phosphor in the coating resin is caused to photolysis, the light emission intensity of the light emitting diode device (1) is significantly reduced.

【0009】紫外線による被覆樹脂及び蛍光体の劣化を防止するため、被覆樹脂中に紫外線吸収物質を混入する方法も考えられるが、可視光成分自体を吸収せず、被覆樹脂本来の特性に悪影響を与えない紫外線吸収物質を慎重に選定しなければならない。 [0009] In order to prevent degradation of the coating resin and the phosphor by UV is considered a method of mixing an ultraviolet absorbing material in the coating resin does not absorb visible light component itself, affect the coating resin intrinsic properties UV-absorbing material which does not give must be carefully selected. また、紫外線吸収物質を採用する際に、付加的に使用する材料及び作業工程が増加するので、製品価格が上昇する難点がある。 Further, when employing an ultraviolet absorbing material, because the material and the working step of additionally used is increased, there is a drawback that product prices rise.

【0010】更に、紫外線を発する紫外線発光ダイオードチップを使用できないため、蛍光体の材料選択と発光ダイオード装置の発光特性が大きな制限を受けることが第三の問題である。 Furthermore, since no available ultraviolet light-emitting diode chip that emits UV, it is the third problem which the emission characteristics of the light-emitting diode device and material selection of the phosphor is subjected to significant limitations. 蛍光ランプ又は水銀ランプに使用する紫外線で励起される紫外線用の蛍光体は、古くから開発・改良が行われた結果、現在では様々な発光波長分布を持つ安価で光変換効率の高い数多くの蛍光体が実用化されている。 Phosphor for UV excited by ultraviolet rays to be used for fluorescent lamps or mercury lamps as a result of development and improvements were made for a long time, a large number of fluorescent high light conversion efficiency at low cost with a variety of emission wavelength distribution in the current body has been put into practical use. 紫外線発光ダイオードチップと紫外線用の蛍光体を組み合わせると、一層明るく且つ変化に富む色調の発光ダイオード装置が得られると予想される。 Combining ultraviolet light emitting diode chip and a phosphor for UV, it is expected color tone of the light emitting diode device can be obtained rich in brighter and changes. しかしながら、紫外線により樹脂が劣化する従来の発光ダイオード装置では、紫外線発光ダイオードチップを使用できず、優れた蛍光体を利用できない。 However, the conventional light emitting diode device in which the resin is deteriorated by ultraviolet rays can not be used an ultraviolet light emitting diode chip, unavailable excellent phosphor.

【0011】第四の問題は、耐熱性が低い被覆樹脂が黄変・着色するため、発光ダイオードチップから照射された光が被覆樹脂を通過する際に減衰する点にある。 [0011] The fourth problem is that heat resistance is low coating resin is yellow-colored, in that the light emitted from the light emitting diode chip is attenuated when passing through the coating resin. 例えば順方向電圧が高いGaN(窒化ガリウム)の青色発光ダイオードチップは、比較的低い順方向電流でも電力損失が大きく、作動時にチップ温度はかなり上昇する。 For example blue light emitting diode chip of the forward voltage is high GaN (gallium nitride), the power loss at a relatively low forward current is large, the chip temperature is considerably increased during operation. 一般に、樹脂は高温に加熱されると次第に劣化して黄変・ In general, varying the resin is deteriorated gradually when heated to a high temperature yellow,
着色を起こすことが知られている。 To cause coloring is known. 従ってGaNの発光ダイオードチップを従来の発光ダイオード装置に用いると、高温の発光ダイオードチップと接する部分から樹脂が次第に黄変・着色するため、発光ダイオード装置(1)の外観品質と発光強度は次第に低下する。 Therefore the use of GaN light emitting diode chip to a conventional light emitting diode device, since the resin from the portion in contact with the hot emitting diode chip gradually yellow coloring, appearance quality and emission intensity of the light emitting diode device (1) gradually decreases to. このように、従来の発光ダイオード装置では、蛍光体を樹脂中に配合すると前記問題が生じ、このため選択する材料種類の減少、信頼性の低下、光変換機能の不完全性、製品価格の上昇を招来する原因となる。 Thus, in the conventional light-emitting diode device, the phosphor occurs the and blended into the resin problems, material type of reduction that selected for this, decrease in reliability, imperfection of light conversion function, increase product prices cause to lead to.

【0012】本発明は、耐環境性及び耐紫外線性を有する半導体発光装置を提供することを目的とする。 The present invention aims to provide a semiconductor light-emitting device having environmental resistance and UV resistance.

【0013】 [0013]

【課題を解決するための手段】本発明による半導体発光装置は、一対の配線導体(3、4)と、一対の配線導体(3、4)の一方の端部に固着された半導体発光素子(2)と、半導体発光素子(2)を被覆する光透過性のガラス層(10)とを備えている。 The semiconductor light-emitting device according to the present invention SUMMARY OF] The pair of the wiring conductor (3, 4), a pair of wiring conductors (3, 4) of one of the semiconductor light emitting element fixed to an end portion ( and 2) is provided with light-transmitting glass layer covering the semiconductor light emitting element (2) and (10). ガラス層(10) Glass layer (10)
は、半導体発光素子(2)から照射される光に対して光透過性を有し且つ半導体発光素子(2)から照射される光を吸収して他の発光波長に変換する蛍光物質(10 A fluorescent substance (10 converted to other emission wavelength by absorbing the light emitted from and semiconductor light-emitting device having a light transparent to light irradiated (2) from the semiconductor light emitting element (2)
a)を含み且つ金属アルコキシド(例えば、テトラメトキシシラン、テトラエトキシシラン等)又はセラミック前駆体ポリマー(例えば、ペルヒドロポリシラザン等) And the metal alkoxide comprises a) (e.g., tetramethoxysilane, tetraethoxysilane, etc.) or a ceramic precursor polymer (e.g., perhydropolysilazane, etc.)
から成るガラス材料を焼成して形成されると共に、半導体発光素子(2)及び配線導体(3、4)と強固に密着する。 Together they are formed by firing a glass material consisting of firmly adhered to the semiconductor light emitting element (2) and wiring conductors (3, 4). 半導体発光素子(2)の発光をガラス層(10) Glass layer light emission of the semiconductor light emitting element (2) (10)
中の蛍光物質(10a)によって所望の発光波長に変換し、半導体発光素子(2)を包囲するガラス層(10) Fluorescent substances in the (10a) into a desired emission wavelength, the glass layer surrounding the semiconductor light emitting element (2) (10)
を通して外部に放出させる。 To be discharged to the outside through.

【0014】金属アルコキシドから成る塗布型ガラス材料又はセラミック前駆体ポリマーから成る塗布型ガラス材料は、半導体発光素子(2)の融点よりも低い温度である150℃前後で焼成可能であり、低温領域でのガラス層の形成が可能である。 [0014] coating type glass material consisting of a coating type glass material or ceramic precursor polymer composed of a metal alkoxide is capable baked at 0.99 ° C. before and after a temperature lower than the melting point of the semiconductor light emitting element (2), in a low temperature region it is possible to form the glass layer is. これらの塗布型ガラス材料は通常は液状であるが、空気中又は酸素雰囲気中で加熱すると、成分の分解又は酸素の吸収によりSiO 2 (酸化珪素)のシロキサン(siloxane)結合を主体とした透明な固形ガラス層を生成する。 These coating type glass material generally is a liquid, but when heated in air or an oxygen atmosphere, a clear composed mainly of siloxane (siloxane) bonds of SiO 2 (silicon oxide) by absorption of decomposition or oxygen components to produce a solid glass layer. これらのガラス材料に蛍光物質(10a)粉末を混合して半導体発光素子(2)の周囲に塗布すれば、光変換作用を発揮する蛍光物質(1 If applied around these glass materials to the fluorescent substance (10a) semiconductor light emitting device by mixing powders (2), a fluorescent substance which exhibits light conversion action (1
0a)含有ガラス層(10)を形成することができる。 Can be formed 0a) containing glass layer (10).

【0015】形成されたガラス層(10)は、光変換作用のみならず、下記の優れた特性を備えている。 [0015] glass layer formed (10) is not light conversion effect only, has excellent characteristics described below. [1] 耐湿性に優れ、内部に水分を浸透させず、半導体発光素子(2)及び蛍光物質(10a)を劣化させない。 [1] excellent moisture resistance, internal without penetration of moisture, does not degrade the semiconductor light emitting element (2) and fluorescent substance (10a). [2] 有害イオンの浸透を防ぐイオンバリア効果が高いため、半導体発光装置の外部や蛍光物質(10a)からの有害イオンで半導体発光素子(2)を劣化させない。 [2] because of the high ionic barrier effect of preventing the penetration of harmful ion, not degrade the semiconductor light emitting element (2) harmful ions from the outside and the fluorescent substance of the semiconductor light-emitting device (10a). [3] 紫外線耐性に優れ、高温環境下又は紫外線発光下でも黄変・着色を起こさず、半導体発光素子(2)の発光を減衰させない。 [3] excellent UV resistance, without causing yellowing coloring even under high temperature environment or ultraviolet light, does not attenuate the light emission of the semiconductor light emitting element (2). [4] ガラス中の珪素原子が金属又はセラミックの表面酸化物層の酸素原子と強固に結合するので、半導体発光素子(2)、配線導体(3、4)又は酸化物系無機蛍光物質(10a)との密着性がよい。 [4] Since the silicon atoms in the glass is strongly bonded with an oxygen atom of a metal or ceramic surface oxide layer, the semiconductor light emitting element (2), the wiring conductor (3, 4) or oxide inorganic fluorescent substance (10a ) good adhesion to the. [5] 配線導体(3、4)のカップ部(3a)内全体に塗布した塗布型ガラス材料が固化する時、添加した蛍光物質(10a)粉末が核となるので、厚塗りをしてもクラックが生じにくい。 [5] When the cup portion (3a) in coating type glass material applied to the entire of the wiring conductor (3, 4) is solidified, the fluorescent substance (10a) powder added is the core, even if the thick coating crack is less likely to occur. このように、ガラス層(10)を使用することにより従来の半導体発光装置の種々の弱点を克服でき、安価で信頼性の高い、蛍光物質(10a)による波長変換機能を有する半導体発光装置を得ることができる。 Thus, it is possible to overcome the various weaknesses of the conventional semiconductor light emitting device by using a glass layer (10), to obtain a reliable inexpensive, the semiconductor light-emitting device having a wavelength converting function by the fluorescent substance (10a) be able to.

【0016】本発明の実施の形態では、半導体発光素子(2)の上面に形成された電極(2a、2b)と一対の配線導体(3、4)とはボンディングワイヤ(5、6) [0016] In the embodiment of the present invention, the upper surface electrodes formed on the semiconductor light emitting element (2) (2a, 2b) and a pair of wiring conductors (3,4) bonding wires to the (5,6)
により電気的に接続され、半導体発光素子(2)、電極(2a、2b)及び電極(2a、2b)に接続されたボンディングワイヤ(5、6)の端部をガラス層(10) It is electrically connected by the semiconductor light emitting element (2), electrodes (2a, 2b) and the electrodes (2a, 2b) glass layer the ends of the bonding wires connected to the (5,6) (10)
により被覆する。 By covering. 一対の配線導体(3、4)の一方の端部にカップ部(3a)が形成され、半導体発光素子(2)はカップ部(3a)の底部(3b)に固着される。 A pair of cup portions (3a) is formed at one end portion of the wiring conductor (3, 4), the semiconductor light emitting element (2) is secured to the bottom of the cup portion (3a) (3b). 絶縁性基板(11)を備えた半導体発光装置の場合、絶縁性基板(11)の一方の主面にカップ部(3 If the semiconductor light-emitting device having an insulating substrate (11), the cup portion (3 on one principal surface of the insulating substrate (11)
a)を形成し、絶縁性基板(11)の一方の主面に沿って互いに反対方向に延びる一対の配線導体(3、4)を形成し、カップ部(3a)の底部(3b)にて一対の配線導体(3、4)の一方に半導体発光素子(2)を固着する。 a) to form, along one main surface of the insulating substrate (11) to form a pair of wiring conductors (3, 4) extending in opposite directions, at the bottom of the cup portion (3a) (3b) fixing the semiconductor light emitting element (2) to one of the pair of the wiring conductor (3, 4). この場合、配線導体(3、4)は絶縁性基板(1 In this case, the wiring conductor (3, 4) an insulating substrate (1
1)の一方の主面から側面に沿って他方の主面に延びる。 From one main surface of 1) along the sides extending in the other main surface.

【0017】ガラス層(10)はカップ部(3a)の上端部(3d)から突出しない。 The glass layer (10) does not protrude from the upper end of the cup portion (3a) (3d). ガラス層(10)は更に封止樹脂(8)により封止され、半導体発光素子(2) Glass layer (10) is sealed further sealed with a sealing resin (8), the semiconductor light emitting element (2)
から照射される光は、ガラス層(10)内を通過した後、封止樹脂(8)の外部に放出される。 Light emitted from, after passing through the glass layer (10), it is discharged to the outside of the sealing resin (8). 半導体発光素子(2)から放射された光成分の一部がガラス層(1 Glass layer portion of the emitted light ingredient from the semiconductor light emitting element (2) (1
0)に達してガラス層(10)内で異なる波長に波長変換された光と、波長変換されない半導体発光素子(2) Glass layer reached 0) (10) and light whose wavelength is converted to a different wavelength, are not wavelength-converted semiconductor light emitting element (2)
からの光成分とが混合して封止樹脂(8)を通して外部に放出される。 It was mixed and the light component from being released to the outside through the sealing resin (8). 特定の発光波長を吸収する光吸収物質、 Light absorbing material that absorbs a specific emission wavelength,
半導体発光素子(2)の発光を散乱する光散乱物質又はガラス層(10)のクラックを防止する結合材をガラス層(10)内に配合してもよい。 Light scattering material or a glass layer to scatter the light emission of the semiconductor light emitting element (2) a coupling member for preventing the crack (10) may be blended with the glass layer (10).

【0018】本発明による半導体発光装置の製法は、一対の配線導体(3、4)の一方の端部にカップ部(3 The method of the semiconductor light-emitting device according to the invention, the cup portion at one end of the pair of the wiring conductor (3, 4) (3
a)を形成する工程と、カップ部(3a)の底部(3 Forming an a), the bottom of the cup portion (3a) (3
b)に半導体発光素子(2)を固着する工程と、半導体発光素子(2)の上面に形成された電極(2a、2b) A step of fixing the semiconductor light emitting element (2) in b), electrodes formed on the upper surface of the semiconductor light emitting element (2) (2a, 2b)
と一対の配線導体(3、4)とをボンディングワイヤ(5、6)により電気的に接続する工程と、半導体発光素子(2)から照射される光に対して光透過性を有し且つ半導体発光素子(2)から照射される光を吸収して他の発光波長に変換する蛍光物質(10a)を含み且つ金属アルコキシド又はセラミック前駆体ポリマーから成るガラス材料をカップ部(3a)内に注入して、半導体発光素子(2)、電極(2a、2b)及び電極(2a、2 And the semiconductor has and a step of electrically connecting the pair of wire conductors (3, 4) by bonding wires (5,6), a light transmissive to the light emitted from the semiconductor light emitting element (2) absorbs the light emitted from the light emitting element (2) injecting a glass material consisting of and a metal alkoxide or a ceramic precursor polymer containing a fluorescent substance for converting the other of the emission wavelength (10a) into the cup portion (3a) Te, semiconductor light emitting element (2), electrodes (2a, 2b) and the electrodes (2a, 2
b)に接続されたボンディングワイヤ(5、6)の端部を被覆する工程と、ガラス材料を焼成してガラス層(1 A step of covering the ends of the bonding wires (5, 6) which is connected to b), the glass layer by firing a glass material (1
0)を形成する工程と、ガラス層(10)を更に封止樹脂(8)により封止する工程とを含む。 0) forming a, and a step of sealing with a glass layer (10) further sealing resin (8). ガラス層(1 Glass layer (1
0)は、半導体発光素子(2)及び配線導体(3、4) 0), the semiconductor light emitting element (2) and wiring conductors (3,4)
と強固に密着する。 To be firmly adhered. 絶縁性基板(11)を備えた半導体発光装置を製造する場合は、絶縁性基板(11)の一方の主面にカップ部(3a)を形成する工程と、絶縁性基板(11)の一方の主面に沿って互いに反対方向に延びる一対の配線導体(3、4)を形成する工程と、カップ部(3a)の底部(3b)にて一対の配線導体(3、 When manufacturing the semiconductor light-emitting device having an insulating substrate (11), forming a cup portion (3a) on one main surface of the insulating substrate (11), an insulating substrate of one of the (11) forming a pair of wire conductors (3, 4) extending in opposite directions along the main surface, the bottom (3b) by a pair of the wiring conductor (3 of the cup portion (3a),
4)の一方に半導体発光素子(2)を固着する工程とを含む。 One of 4) a step of fixing the semiconductor light emitting element (2).

【0019】 [0019]

【発明の実施の形態】以下、発光ダイオード装置に適用した本発明による半導体発光装置の実施の形態を図1〜 DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, FIG. 1 to the embodiment of the semiconductor light-emitting device according to the present invention applied to a light emitting diode device
図4について説明する。 Figure 4 will be described. 図1〜図4に示す実施の形態では、図5に示す箇所と同一の部分には同一の符号を付し、説明を省略する。 In the embodiment shown in FIGS. 1 to 4, the same reference numerals are assigned to portions that are the same as the parts shown in FIG. 5, the description thereof is omitted.

【0020】図1は、本発明による発光ダイオード装置(20)の第1の実施の形態を示す断面図である。 [0020] Figure 1 is a sectional view showing a first embodiment of a light emitting diode device according to the present invention (20). 発光ダイオード装置(20)ではカップ部(3a)に固着された発光ダイオードチップ(2)は、絶縁物封止体として蛍光物質(10a)を含有するガラス層(10)により被覆され、更に封止樹脂(8)により被覆される。 Light emitting diode device (20) in the light-emitting diode chip is secured to the cup portion (3a) (2) is covered by a glass layer containing a fluorescent substance (10a) as the insulator sealing body (10), further sealing It is covered with a resin (8). 製造の際に、発光ダイオードチップ(2)の上部より蛍光物質(10a)を含む塗布型ガラス材料をカップ部(3 During manufacture, the cup portion coating type glass material including phosphor (10a) from the upper portion of the LED chip (2) (3
a)内に注入して、約150℃の温度で焼成し、蛍光物質(10a)を含有するガラス層(10)を固化形成した後に、配線導体(3、4)の端部全体を透明な封止樹脂(8)で封止する。 Was injected into a), the calcination at a temperature of from about 0.99 ° C., after the solidified form glass layer (10) containing a fluorescent material (10a), a clear overall end of the wiring conductor (3, 4) sealed with a sealing resin (8). ガラス層(10)の焼成温度は発光ダイオードチップ(2)の融点よりも十分に低い。 Baking temperature of the glass layer (10) is sufficiently lower than the melting point of the light emitting diode chip (2).

【0021】発光ダイオード装置(20)の配線導体(3、4)間に電圧を印加して発光ダイオードチップ(2)に通電して発光ダイオードチップ(2)を発光させると、ガラス層(10)内の蛍光物質(10a)によってその一部又は全部がその発光波長と異なる他の波長に変換された後、封止樹脂(8)の先端部に形成されたレンズ部(8a)によって集光されて発光ダイオード装置(20)の外部に放出される。 [0021] When the light emitting diode is a light-emitting device (20) of the wiring conductor (3, 4) light emitting diode chip is energized by applying a voltage to a light-emitting diode chip (2) between (2), the glass layer (10) after fluorescent substance (10a) partially or entirely by the inner is converted into other different wavelengths and the emission wavelength, is condensed by the lens portion formed on the tip portion of the sealing resin (8) (8a) It is discharged to the outside of the light emitting diode device (20) Te. 例えば、半導体発光素子には発光波長のピークが約440nmから約470n For example, about the peak of the emission wavelength of about 440nm in the semiconductor light emitting element 470n
mのGaN系の青色の発光ダイオードチップ(2)を用い、蛍光物質(10a)には付活剤としてCe(セリウム)を約6mol%添加したYAG(イットリウム・アルミニウム・ガーネット、化学式Y 3 Al 512 、励起波長のピーク約450nm、発光波長のピーク約540nm using m of GaN-based blue light emitting diode chip (2), YAG is a fluorescent substance (10a) was added Ce (the cerium) about 6 mol% as an activator (yttrium aluminum garnet, formula Y 3 Al 5 O 12, the peak excitation wavelength of approximately 450 nm, the peak emission wavelength of about 540nm
の黄緑色光)を用いる。 Using a yellow-green light).

【0022】ガラス層(10)は、YAG蛍光物質(1 The glass layer (10) is, YAG fluorescent substance (1
0a)の粉末状微細結晶粒を塗布型ガラス材料に適量混合して成るガラス混合物を作成し、これをカップ部(3 Powdery fine crystal grains to create a glass mixture formed by appropriate amount to the coating type glass material, which cup portion 0a) (3
a)内にカップ部(3a)の上端部(3d)から突出しない量で注入した後に焼成して得られる。 Obtained by baking after implantation in an amount that does not protrude from the upper end (3d) of the cup portion (3a) in a).

【0023】一方、封止樹脂(8)は、液状で透明なエポキシ樹脂を成形型に注入した後に発光ダイオードチップ(2)、ボンディングワイヤ(5、6)、ガラス層(10)を固着した配線導体(3、4)の端部をこのエポキシ樹脂中に浸漬し且つ位置決め治具によりエポキシ樹脂中の所定の位置に固定し、エポキシ樹脂を加熱し硬化して得られる。 On the other hand, the sealing resin (8), the light emitting diode chip transparent epoxy resin in liquid state after injection into the mold (2), bonding wires (5, 6), wiring fixed glass layer (10) conductors (3, 4) end is fixed in place in the epoxy resin by the immersed and positioning jig in this epoxy resin, obtained by curing by heating the epoxy resin. 発光ダイオード装置(20)から外部に放出される光の指向角を広げるため、必要に応じて粉末シリカ等の散乱剤を封止樹脂(8)に混合させてもよい。 To broaden the directivity angle of light emitted from the light emitting diode device (20) to the outside, scattering agent in powder such as silica may be mixed in the sealing resin (8) as required. 本実施の形態では、YAG蛍光物質(10a)の波長変換効率の最大値が比較的高く、発光ダイオードチップ(2)の発光波長とYAG蛍光物質(10a)の励起波長とが約450nmのピークでほぼ一致するため、実効波長変換効率の高い明るい発光ダイオード装置(2 In this embodiment, the maximum value of the wavelength conversion efficiency of the YAG phosphor (10a) is relatively high, the emission wavelength and a peak excitation wavelength of about 450nm of YAG fluorescent substance (10a) of the light-emitting diode chips (2) to approximately match the effective wavelength conversion efficient bright light emitting diode device (2
0)が得られる。 0) is obtained. また、YAG蛍光物質(10a)の結晶粒がガラス層(10)中に分散しているので、発光ダイオード装置(20)から外部に放出される光は、蛍光物質(10a)で波長変換された光成分以外に蛍光物質(10a)の結晶粒を透過せず波長変換されない本来の発光成分即ち発光ダイオードチップ(2)から照射された光成分も含まれる。 The crystal grains of the YAG fluorescent substance (10a) is so dispersed in the glass layer (10), light emitted outside from the light emitting diode device (20) is subjected to wavelength conversion by the fluorescent material (10a) original light emission component or light components emitted from the light emitting diode chip (2) are not wavelength-converted without transmitting the crystal grains of the fluorescent material (10a) in addition to the optical components are also included.

【0024】従って、発光波長ピーク約440nm〜約470nmの青色光である発光ダイオードチップ(2) [0024] Thus, a blue light emission wavelength peak of about 440nm~ about 470nm light emitting diode chips (2)
の発光成分と、半値幅約130nmの幅広い波長分布を持った発光波長ピーク約540nmの黄緑色光であるY A light emitting component, a yellow-green light emission wavelength peak of about 540nm having a broad wavelength distribution half width of about 130 nm Y of
AG蛍光物質(10a)の発光成分とが混合された白色光が発光ダイオード装置(20)から外部に放出される。 The white light emitting components are mixed AG fluorescent substance (10a) is released to the outside from the light emitting diode device (20). この場合、塗布型ガラス材料に混合するYAG蛍光物質(10a)粉末の量を調整し、ガラス層(10)内の分布濃度を変更することにより発光ダイオード装置(20)の発光色の色調を調整することができる。 In this case, by adjusting the amount of YAG fluorescent substance (10a) powder to be mixed with the coating type glass material, adjust the color tone of the emission color of the light-emitting diode device by changing the distribution density of the glass layer (10) (20) can do. また、YAG蛍光物質(10a)の製造時に適当な添加物を適量添加して結晶構造を一部変更して発光波長分布をシフトすると、発光ダイオード装置(20)の発光色を更に異なる色調に調整することができる。 Further, when shifting the emission wavelength distribution partially modified the appropriate amount to the crystal structure of suitable additives in the production of YAG fluorescent substance (10a), adjusted to further different shades the light emission color of the light emitting diode device (20) can do. 例えばGa For example, Ga
(ガリウム)又はLu(ルテチウム)を添加して短波長側にシフトし、Gd(ガドリニウム)を添加して長波長側にシフトすることができる。 (Gallium) or shifted by adding to the short wavelength side of Lu (lutetium) can be shifted to the long wavelength side by adding Gd (gadolinium).

【0025】本発明では更に光学的特性や作業性を向上するため、例えば下記の改善も可能である。 [0025] To further improve the optical characteristics and workability in the present invention, for example, can be improved below. [1] ガラス層(10)内に散乱剤を混入することで発光ダイオードチップ(2)の光を散乱させることにより蛍光物質(10a)に当たる発光ダイオードチップ(2)の光量が増加し、波長変換効率を向上すると共に、発光ダイオード装置(20)から外部に放出される光の指向角を広げることができる。 [1] glass layer (10) amount of the fluorescent material by scattering the light emitting diode chip (2) by the incorporation of scattering agent emitting diode chip striking the (10a) (2) is increased in the wavelength conversion with improved efficiency, it is possible to widen the beam angle of light emitted outside from the light emitting diode device (20). [2] ガラス層(10)のクラックを防止する結合材を配合する。 [2] formulating a binder to prevent cracking of the glass layer (10). [3] 塗布型ガラス材料の粘度を高くする。 [3] increasing the viscosity of the coating type glass material. [4] 塗布型ガラス材料の使用量を減らす。 [4] reduce the amount of coating type glass material.

【0026】このような場合は、図2に示すように、塗布型ガラス材料に蛍光物質(10a)の粉末と共にシリカ、酸化チタン等のセラミック粉末(10b)を目的に応じて適量混合すればよい。 [0026] In this case, as shown in FIG. 2, the silica with the powder of the fluorescent material (10a) on the coating type glass material, a ceramic powder (10b) such as titanium oxide may be mixed with an appropriate amount in accordance with the intended .

【0027】図2に示す本発明の第2の実施の形態では、混合するセラミック粉末の種類及び量によって得られる効果が異なる。 [0027] In the second embodiment of the present invention shown in FIG. 2, the effect obtained by the type and amount of the ceramic powder to be mixed are different. 例えばセラミック粉末がシリカの場合は本来ガラス層(10)と同じ物質なので[1]の効果は少なく[2][3]の効果が大きい。 For example the effect of the effect of so original when the ceramic powder is silica is the same material as the glass layer (10) [1] is less [2] [3] is large. しかし、セラミック粉末が酸化チタンの場合は[1]〜[3]の効果とも大きい。 However, the ceramic powder is large with the effect of the case of titanium oxide [1] to [3]. 従って、混合するセラミック粉末は目的によって単一でも複数の種類を組み合わせても良い。 Accordingly, the ceramic powder to be mixed may be used in combination of two or more kinds in a single depending on the purpose.

【0028】また、本発明では紫外線で劣化しないガラスを用いるので、半導体発光素子に紫外線発光ダイオードチップ(2)も用いることができる。 Further, since a glass which is not degraded by ultraviolet rays in the present invention, the ultraviolet light emitting diode chip (2) to the semiconductor light-emitting device can also be used. 従って、従来の発光ダイオード装置よりも明るく且つ変化に富む色調の発光ダイオード装置(20)を実現することができる。 Accordingly, it is possible to realize the light emitting diode device of the color-rich and change brighter than conventional LED device (20).

【0029】本発明による発光ダイオード装置(20) The light emitting diode device according to the present invention (20)
の第3の実施の形態を図3に示す。 It shows a third embodiment of Figure 3. 例えば、約360n For example, about 360n
m〜380nmの発光ピーク波長を有する紫外線を発生するGaN系発光ダイオードチップ(2)と、励起ピーク波長約360nm、発光ピーク波長約543nmのG A GaN-based light-emitting diode chip (2) which generates ultraviolet rays having an emission peak wavelength of M~380nm, excitation peak wavelength of about 360 nm, emission peak wavelength of about 543nm for G
a及びTb(テルビウム)付活のY 2 SiO 5の蛍光物質(10a)とを使用すると、半値幅約12nmの非常にシャープな発光分布を持つ緑色発光ダイオード装置(2 Using the a and Tb (terbium) activated in Y 2 SiO 5 phosphor (10a), a green light-emitting diode device having a very sharp emission distribution of the half-value width approximately 12 nm (2
0)が得られる。 0) is obtained.

【0030】発光ダイオードチップと蛍光物質(10 The light emitting diode chip and a fluorescent substance (10
a)の前記組合わせは例示に過ぎず、紫外線発光ダイオードチップ(2)の発光波長に適合する励起波長分布を持ち且つ波長変換効率が高ければ、いかなる蛍光物質(10a)でも使用できる。 The combination of a) are illustrative only, higher and the wavelength conversion efficiency have compatible excitation wavelength distribution to the emission wavelength of the ultraviolet light emitting diode chip (2), it can be used in any fluorescent material (10a). 例えばハロ燐酸カルシウム系、燐酸カルシウム系、珪酸塩系、アルミン酸塩系、タングステン酸塩系等の蛍光物質(10a)から所望の特性を持つ蛍光物質(10a)を選択することができる。 Such as halo calcium phosphate-based, calcium phosphate-based, silicate, aluminate, can be selected fluorescent substance (10a) having the desired characteristics from the fluorescent substance (10a) of tungstate-based and the like.

【0031】また、第2の実施の形態と同様に、第3の実施の形態の発光ダイオード装置(20)のガラス層(10)にもセラミック粉末を混合することは可能である。 Further, as in the second embodiment, it is possible to mix the ceramic powder to the glass layer of the third embodiment of the light emitting diode device (20) (10). 前記の実施の形態では、カップ部(3a)の上端部より上方に突出しないようにガラス層(10)の充填量を調整すれば、隣接して他の発光ダイオード装置(2 In the embodiment described above, by adjusting the filling amount of the glass layer so as not to protrude upward from the upper end (10) of the cup portion (3a), adjacent to another light emitting diode device (2
0)を設置しても偽灯を発生しない。 0) it does not generate a false light be installed.

【0032】図4は、チップ形発光ダイオード装置(2 [0032] Figure 4 is a chip type light emitting diode device (2
0)に適用した本発明の他の実施の形態を示す。 Shows another embodiment of the present invention applied to 0). チップ形発光ダイオード装置(20)では、絶縁性基板(1 In Chip emitting diode device (20), an insulating substrate (1
1)の一方の主面にカップ部(3a)と、相互に離間した配線導体(3、4)とが形成され、配線導体(3、 Cup portion on one principal surface of 1) and (3a), mutually spaced wire conductors and (3,4) are formed, the wiring conductor (3,
4)の一方の端部は、カップ部(3a)内に配置される。 One end of the 4) is disposed in the cup portion (3a). 発光ダイオードチップ(2)はカップ部(3a)の底部(3b)にて配線導体(3)に接着剤(12)を介して固着される。 Light emitting diode chip (2) is secured with an adhesive (12) the bottom of the cup portion (3a) at (3b) to the wiring conductor (3). 配線導体(3、4)の他方の端部は、 The other end of the wiring conductor (3, 4),
絶縁性基板(11)の側面及び他方の主面に延びて配置される。 They are arranged to extend on the side surface and the other main surface of the insulating substrate (11). 発光ダイオードチップ(2)のカソード電極(2a)及びアノード電極(2b)はそれぞれボンディングワイヤ(5、6)により配線導体(3、4)に接続される。 A cathode electrode (2a) and an anode electrode of the LED chip (2) (2b) is connected to the wiring conductor (3, 4) by bonding wires (5, 6), respectively. 発光ダイオードチップ(2)、カップ部(3 Light emitting diode chip (2), the cup portion (3
a)、ボンディングワイヤ(5、6)、配線導体(3、 a), bonding wires (5, 6), the wiring conductor (3,
4)の一方の端部側はガラス層(10)により被覆され、絶縁性基板(11)の一方の主面に形成された台形状断面の封止樹脂(8)によって更に被覆される。 One end side of 4) is covered by a glass layer (10) is further covered by an insulating substrate (11) one main surface to the formed trapezoidal cross-section of the sealing resin (8). 図4 Figure 4
の発光ダイオード装置(20)でも、発光ダイオードチップ(2)から照射された光の一部がガラス層(10) Emitting diode device (20) also emitting diode chips (2) glass layer part of the light emitted from (10)
の蛍光物質(10a)によって発光波長が変換され、図1の発光ダイオード装置と同様の作用効果が得られる。 Fluorescence emission wavelength depending on the material (10a) is converted to the same effects as the light emitting diode device of FIG. 1 can be obtained.
尚、図4の発光ダイオードにおいても、ガラス層(1 Also in the light emitting diode of FIG. 4, the glass layer (1
0)にセラミック粉末を混入することができる。 0) can be mixed with the ceramic powder. また、 Also,
図1〜図4の発光ダイオードでは、蛍光物質(10a) The light emitting diode of FIGS. 1-4, a fluorescent substance (10a)
をガラス層(10)内に均一に分散させているが、不均一に分散させることもできる。 The but was uniformly dispersed in the glass layer (10) can also be unevenly distributed. 例えば、発光ダイオードチップ(2)側で蛍光物質(10a)の混入濃度を増加してもよい。 For example, it may increase the contamination concentration of the fluorescent substance (10a) in the light-emitting diode chips (2) side.

【0033】 [0033]

【発明の効果】前記のように、本発明では、有害物質の浸透を防ぎ且つ紫外線耐性に優れるガラス層により半導体発光素子を被覆するので、湿度、温度又は紫外線等によってガラス層や半導体発光素子に劣化を起こさず、耐環境性が向上し、蛍光物質による発光波長変換機能を有しつつも信頼性が高く安価な半導体発光装置を得ることができる。 [Effect of the Invention] As described above, in the present invention, since covering the semiconductor light-emitting element by a glass layer which is excellent in and UV-resistant to prevent penetration of harmful substances, humidity, the glass layer and the semiconductor light-emitting device by temperature or UV rays without causing degradation, improved environmental resistance, while having an emission wavelength converting function by the fluorescent substance can also be reliable obtain highly inexpensive semiconductor light-emitting device.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】 発光ダイオード装置に適用した本発明による半導体発光装置の断面図 Figure 1 is a cross-sectional view of a semiconductor light-emitting device according to the present invention applied to a light emitting diode device

【図2】 本発明の第2の実施の形態を示す部分断面図 Partial cross-sectional view showing a second embodiment of the present invention; FIG

【図3】 本発明の第3の実施の形態を示す部分断面図 3 partial cross-sectional view showing the embodiment of the invention; FIG

【図4】 チップ型発光ダイオード装置に適用した本発明の実施の形態を示す断面図 4 is a cross-sectional view showing an embodiment of the present invention applied to a chip type light emitting diode device

【図5】 従来の発光ダイオード装置の断面図 FIG. 5 is a cross-sectional view of a conventional light emitting diode device

【符号の説明】 (2)・・半導体発光素子、 (2a、2b)・・電極、 (3、4)・・配線導体、 (3a)・・カップ部、 (3b)・・底部、 (3c)・・側壁、(3 [Description of Reference Numerals] (2) ... semiconductor light-emitting element, (2a, 2b) ... electrode, (3,4) ... wiring conductors, (3a) ... cup portion, (3b) ... the bottom, (3c ) ... side wall, (3
d)・・上端部、 (5、6)・・ボンディングワイヤ、 (8)・・封止樹脂、 (10)・・ガラス層、 d) ... upper end, (5,6) ... bonding wire (8) ... sealing resin (10) .. glass layer,
(11)・・絶縁性基板、 (11) ... the insulating substrate,

Claims (12)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 一対の配線導体(3、4)と、該一対の配線導体(3、4)の一方の端部に固着された半導体発光素子(2)と、前記半導体発光素子(2)を被覆する光透過性の絶縁物封止体とを備えた半導体発光装置において、 前記絶縁物封止体は、ガラス層(10)により構成され、 該ガラス層(10)は前記半導体発光素子(2)から照射される光に対して光透過性を有し且つ前記半導体発光素子(2)から照射される光を吸収して他の発光波長に変換する蛍光物質(10a)が混入されていることを特徴とする半導体発光装置。 And 1. A pair of the wiring conductor (3, 4), a semiconductor light emitting element (2) fixed to one end of the pair of the wiring conductor (3, 4), the semiconductor light emitting element (2) in the semiconductor light-emitting device having a light-transmitting insulating material sealing body covering, said insulator sealing body is composed of a glass layer (10), the glass layer (10) is a semiconductor light emitting device ( by absorbing light emitted from and the semiconductor light emitting device has a light-transmitting (2) a fluorescent material which converts to other emission wavelengths (10a) is mixed with respect to light emitted from the 2) the semiconductor light-emitting device, characterized in that.
  2. 【請求項2】 前記ガラス層(10)はガラス材料を前記半導体発光素子(2)の融点よりも低い温度で焼成して形成された請求項1に記載の半導体発光装置。 2. A semiconductor light emitting device according to claim 1 which is formed by firing at a temperature lower than the melting point of the glass layer (10) the semiconductor light-emitting element a glass material (2).
  3. 【請求項3】 前記ガラス層(10)は、金属アルコキシドを出発原料とするガラス材料又はセラミック前駆体ポリマーから成るガラス材料を焼成して形成された請求項1又は請求項2に記載の半導体発光装置。 Wherein the glass layer (10) is a semiconductor light emitting according to claim 1 or claim 2 which is formed by firing a glass material made of a glass material or a ceramic precursor polymer to a metal alkoxide as a starting material apparatus.
  4. 【請求項4】 前記ガラス層(10)は、シロキサン(siloxane)結合を主体とする透明な固形ガラス層である請求項1〜請求項3のいずれか1項に記載の半導体発光装置。 Wherein said glass layer (10) is a siloxane (siloxane) semiconductor light emitting device according to any one of claims 1 to 3 which is a transparent solid glass layer mainly comprising binding.
  5. 【請求項5】 前記半導体発光素子(2)の上面に形成された電極(2a、2b)と前記一対の配線導体(3、 Wherein said semiconductor light emitting element (2) formed on the upper surface electrodes (2a, 2b) and the pair of the wiring conductor (3,
    4)とをボンディングワイヤ(5、6)により電気的に接続し、前記ガラス層(10)は前記半導体発光素子(2)、電極(2a、2b)及び該電極(2a、2b) 4) and electrically connected by bonding wires (5,6), said glass layer (10) is a semiconductor light emitting element (2), electrodes (2a, 2b) and the electrodes (2a, 2b)
    に接続された前記ボンディングワイヤ(5、6)の端部を被覆する請求項1〜請求項4のいずれか1項に記載の半導体発光装置。 The semiconductor light emitting device according to any one of claims 1 to 4 for covering the ends of the connected the bonding wires (5, 6) to.
  6. 【請求項6】 前記一対の配線導体(3、4)の一方の端部にカップ部(3a)を形成し、前記半導体発光素子(2)を前記カップ部(3a)の底部(3b)に固着した請求項1〜請求項5のいずれか1項に記載の半導体発光装置。 6. form a cup portion (3a) at one end of said pair of wiring conductors (3,4), the bottom of the cup portion of the semiconductor light emitting element (2) (3a) to (3b) the semiconductor light emitting device according to any one of the fixed claims 1 to claim 5.
  7. 【請求項7】 絶縁性基板(11)の一方の主面にカップ部(3a)と、前記絶縁性基板(11)の一方の主面に沿って互いに反対方向に延びる前記一対の配線導体(3、4)とを形成し、前記カップ部(3a)の底部(3b)にて前記一対の配線導体(3、4)の一方に前記半導体発光素子(2)を固着した請求項1〜請求項6 7. cup portion on one principal surface of the insulating substrate (11) and (3a), along said one main surface of the insulating substrate (11) extending in opposite directions of the pair of wire conductors ( 3, 4) and to form, according to claim 1 wherein the bottom in (3b) was fixed to the semiconductor light emitting element (2) on one of the pair of the wiring conductor (3, 4) of said cup portion (3a) section 6
    のいずれか1項に記載の半導体発光装置。 The semiconductor light emitting device according to any one of.
  8. 【請求項8】 前記ガラス層(10)は前記カップ部(3a)の上端部(3d)から突出しない請求項2〜請求項7の何れか1項に記載の半導体発光装置。 8. The semiconductor light emitting device according to any one of claims 2 7 does not project above the glass layer (10) from the upper end of the cup portion (3a) (3d).
  9. 【請求項9】 前記配線導体(3、4)は前記絶縁性基板(11)の一方の主面から側面に沿って他方の主面に延びる請求項7に記載の半導体発光装置。 Wherein said wiring conductor (3, 4) is a semiconductor light emitting device according to claim 7 extending on the other main surface along the sides from one main surface of the insulating substrate (11).
  10. 【請求項10】 前記ガラス層(10)は更に封止樹脂(8)により封止され、前記半導体発光素子(2)から照射される光は、前記ガラス層(10)内を通過した後、前記封止樹脂(8)の外部に放出される請求項1〜 Wherein said glass layer (10) is sealed further sealed with a sealing resin (8), the light emitted from the semiconductor light emitting element (2) is passed through the glass layer (10), claim 1, which is discharged to the outside of the sealing resin (8)
    請求項9に記載の半導体発光装置。 The semiconductor light emitting device according to claim 9.
  11. 【請求項11】 前記半導体発光素子(2)から放射された光成分の一部が前記ガラス層(10)に達して前記ガラス層(10)内で異なる波長に波長変換された光と、波長変換されない前記半導体発光素子(2)からの光成分とが混合して前記封止樹脂(8)を通して外部に放出される請求項10に記載の半導体発光装置。 11. A light part of the light component wavelength has been converted to a different wavelength in the glass layer (10) reached the glass layer (10) emitted from the semiconductor light emitting element (2), the wavelength the semiconductor light emitting device according to claim 10 which is released to the outside through the sealing resin and the light components are mixed (8) from unconverted the semiconductor light emitting element (2).
  12. 【請求項12】 特定の発光波長を吸収する光吸収物質、前記半導体発光素子(2)の発光を散乱する光散乱物質又はガラス層(10)のクラックを防止する結合材を前記ガラス層(10)内に配合した請求項1〜請求項11に記載の半導体発光装置。 12. The light-absorbing material that absorbs a specific emission wavelength, wherein the glass layer bonding material to prevent cracking of the semiconductor light emitting element light scattering material or a glass layer to scatter the light emission (2) (10) (10 ) the semiconductor light emitting device according to claims 1 to 11 formulated into.
JP10006423A 1998-01-16 1998-01-16 The semiconductor light emitting device and its manufacturing method Expired - Fee Related JP2924961B1 (en)