JPH1120393A - Thermal transfer sheet and method for temporarily fastening the transfer sheet - Google Patents
Thermal transfer sheet and method for temporarily fastening the transfer sheetInfo
- Publication number
- JPH1120393A JPH1120393A JP9181542A JP18154297A JPH1120393A JP H1120393 A JPH1120393 A JP H1120393A JP 9181542 A JP9181542 A JP 9181542A JP 18154297 A JP18154297 A JP 18154297A JP H1120393 A JPH1120393 A JP H1120393A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- transfer sheet
- thermal transfer
- image forming
- image
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、加熱により被接着
物に画像を転写する熱転写シート及び熱転写シート仮止
め方法に関し、特に、インクジェット記録用として画像
記録が可能な熱転写シート及び熱転写シート仮止め方法
に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thermal transfer sheet and a thermal transfer sheet temporary fixing method for transferring an image to an adherend by heating, and more particularly to a thermal transfer sheet and a thermal transfer sheet temporary fixing method capable of recording an image for ink jet recording. About.
【０００２】[0002]
【従来の技術】従来より、文字や図柄（以下、文字や図
柄を総称して「画像」と云う）などの画像が形成された
転写シートを用いて、該画像を所望するもの（被接着
物）に転写することが行われている。2. Description of the Related Art Conventionally, a transfer sheet on which an image such as a character or a pattern (hereinafter, a character or a pattern is collectively referred to as an "image") is formed on a transfer sheet on which a desired image (an object to be adhered) is formed. ) Is performed.
【０００３】この種の転写シートにおいては、該転写シ
ートを加熱することによって、画像を被接着物へ転写・
固定する所謂熱転写シートがある。この加熱による転写
は、画像の固定が極めて強固かつ確実であることから、
例えば、ハンカチや衣類のように、洗濯など比較的荒い
使用形態のものに適しており、衣類などに多用されてき
ている。[0003] In this type of transfer sheet, an image is transferred to an adherend by heating the transfer sheet.
There is a so-called thermal transfer sheet to be fixed. The transfer by this heating is very strong and reliable in fixing the image.
For example, it is suitable for a relatively rough use form such as washing, such as a handkerchief or clothes, and has been frequently used for clothes.
【０００４】この熱転写シートについて、図６の断面図
を参照して説明する。図６に示すように、熱転写シート
４０は、画像の形成された画像形成層４２および該画像
形成層４２の上に設けられた接着層４３が基材４１上に
設けられた構成である。[0004] This thermal transfer sheet will be described with reference to the sectional view of FIG. As shown in FIG. 6, the thermal transfer sheet 40 has a configuration in which an image forming layer 42 on which an image is formed and an adhesive layer 43 provided on the image forming layer 42 are provided on a base material 41.
【０００５】そして、画像形成層４２を衣類等の被接着
物３０に転写するときは、図６に示すように、接着層４
３を被接着物３０の上に重ね合わせ、その後、加熱手段
である例えばアイロンを用いて、少なくとも転写領域に
対応する基材４１の表面全体を加熱する。この加熱操作
は、普通、非接着物３０に対してアイロンを適宜加圧し
つつ擦り(例えば、矢印Ｘ0方向の擦り)つける。When the image forming layer 42 is transferred to the adherend 30 such as clothing, as shown in FIG.
3 is superimposed on the object 30 to be bonded, and thereafter, at least the entire surface of the base material 41 corresponding to the transfer area is heated using a heating means, for example, an iron. In this heating operation, the iron is usually rubbed against the non-adhesive 30 while appropriately pressing (for example, rubbing in the direction of arrow X0).
【０００６】このような加熱操作によって、被接着物３
０と画像形成層４２とは、熱によって温度が上昇して接
着力を生じた接着層４３により接着される。その後、基
材４１を画像形成層４２から剥離することにより、被接
着物３０上に所定の画像を形成したように、画像形成層
４２が転写される。[0006] By such a heating operation, the adherend 3
0 and the image forming layer 42 are bonded by the bonding layer 43 whose temperature has been raised by heat to generate bonding force. Thereafter, the image forming layer 42 is transferred as if a predetermined image was formed on the adherend 30 by peeling the base material 41 from the image forming layer 42.
【０００７】[0007]
【発明が解決しようとする課題】前掲の図６に示した従
来の熱転写シート４０においては、上記加熱操作によっ
て画像形成層４２を被接着物３０に強固に転写すること
ができる。しかし、加熱する前において、被接着物３０
上に熱転写シート４０を載置した状態では、動き易いた
めに、所望の位置からずれることがある。In the conventional thermal transfer sheet 40 shown in FIG. 6, the image forming layer 42 can be firmly transferred to the adherend 30 by the above-mentioned heating operation. However, before heating, the object 30
In a state where the thermal transfer sheet 40 is placed thereon, it may be shifted from a desired position because the thermal transfer sheet 40 is easily moved.
【０００８】特に、被接着物３０が比較的伸びちじみす
るような素材(例えば、生地や伸縮性の部材)にて構成さ
れている場合には、アイロンやホットプレス等により擦
る(矢印Ｘ0方向)ように加熱操作することから、熱が伝
わって接着層４３が接着力を発揮するまでは、加熱操作
中の熱源（アイロンやホットプレス）の動きに引きずら
れるように熱転写シート自体も移動(矢印Ｘ1方向)して
しまい、転写位置が所望の位置からずれてしまう問題が
あった。In particular, when the adherend 30 is made of a material (for example, cloth or elastic member) that is relatively stretchable, it is rubbed with an iron or hot press (in the direction of arrow X0). ), The heat transfer sheet itself moves (arrow) until the heat is transmitted and the adhesive layer 43 exerts the adhesive force, so that it is dragged by the movement of the heat source (iron or hot press) during the heating operation. (X1 direction), and the transfer position is deviated from a desired position.
【０００９】また、転写画像の位置を決定する場合、特
に被接着物３０が衣類であるときは、被接着物３０に熱
転写シートを当ててハンガー等に吊るした状態等の実際
の状態に近い状態として見ることが最も良い。そこで、
従来においては、洗濯バサミや粘着テープで止めたり、
あるいは他の人に持ってもらうなどの方法をとっている
のが現状であった。しかしながら、洗濯バサミや粘着テ
ープでは、アイロンやホットプレス等による加熱操作の
とき邪魔になると云う問題があった。Further, when the position of the transferred image is determined, particularly when the object 30 is clothing, a state close to the actual state such as a state in which a heat transfer sheet is applied to the object 30 and hung on a hanger or the like. As best to see. Therefore,
Conventionally, with clothespins or adhesive tape,
At the present time, it is a method of taking another person to take it. However, there is a problem in that clothespins and adhesive tapes hinder a heating operation using an iron or a hot press.
【００１０】本発明は、上記問題点に鑑み成されたもの
であって、その目的とするところは、アイロン等の熱源
により擦るような加熱操作をしたときでも、熱転写シー
トが熱源の動きに引きずられるような現象を防止して、
転写位置を正確にすることができ、かつ転写位置を決定
する時の仮止め操作が容易にできる熱転写シート及び熱
転写シート仮止め方法を提供することである。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems, and has as its object the object of the present invention in that even when a heating operation such as rubbing with a heat source such as an iron is performed, the heat transfer sheet slides with the movement of the heat source. To prevent the phenomenon
An object of the present invention is to provide a thermal transfer sheet and a thermal transfer sheet temporary fixing method that can make the transfer position accurate and facilitate a temporary fixing operation when determining the transfer position.
【００１１】[0011]
【課題を解決するための手段】本発明に係る熱転写シー
トは、基材上に、画像保持機能を有する画像形成層およ
び被接着物との接着機能を有する接着層もしくは画像保
持機能とともに接着機能を有する画像形成層を有してお
り、加熱によって前記被接着物へ前記画像形成層を転写
可能とする熱転写シートであって、前記接着層が水分の
付与によって、前記被接着物に対して仮止め用粘着力が
生じるように構成されたことを特徴とし(請求項１)、こ
れにより、上記目的を達成することができる。The thermal transfer sheet according to the present invention has an image forming layer having an image holding function and an adhesive layer or an image holding function having an adhesive function with an adherend on a substrate. A heat transfer sheet having an image forming layer having the image transfer layer, the image transfer layer being capable of transferring the image forming layer to the object by heating, wherein the adhesive layer is temporarily fixed to the object by applying moisture. The present invention is characterized in that it is configured to generate an adhesive force for use (claim 1), whereby the above object can be achieved.
【００１２】また、本発明に係る上記熱転写シートにお
いて、 ・前記接着層もしくは接着機能を有する前記画像形成層
は、加熱により接着力が生じる成分と、水分の付与によ
り粘着力が生じる成分とが混合されていること(請求項
２)、 ・前記接着層は、加熱により接着力が生じる熱接着層
と、該熱接着層の上に水分付与により粘着力が生じる仮
止め層とを有していること(請求項３)、 ・前記基材と前記画像形成層との間に易剥離手段が設け
られたこと(請求項４)、 ・前記画像形成層が、インクジェット記録方式により画
像形成可能なインク受容層により構成されたこと(請求
項５)、 ・シート端部が前記仮止め用接着力を生じるように構成
されたこと(請求項６)、 を特徴とする。Further, in the thermal transfer sheet according to the present invention, the adhesive layer or the image forming layer having an adhesive function is obtained by mixing a component that generates an adhesive force by heating and a component that generates an adhesive force by applying moisture. (Claim 2) The adhesive layer has a thermal adhesive layer that generates an adhesive force by heating, and a temporary fixing layer that generates an adhesive force by applying moisture on the thermal adhesive layer. (Claim 3) ・ An easy peeling means is provided between the base material and the image forming layer (Claim 4) ・ The ink in which the image forming layer can form an image by an ink jet recording system A receiving layer (claim 5); and an end portion of the sheet is configured to generate the adhesive force for temporary fixing (claim 6).
【００１３】本発明に係る熱転写シート仮止め方法は、
基材上に、画像保持機能を有する画像形成層および被接
着物との接着機能を有する接着層もしくは画像保持機能
とともに接着機能を有する画像形成層を有し、加熱によ
って前記被接着物へ前記画像形成層を転写可能とする熱
転写シートを用いて、前記画像形成層を前記被接着物へ
転写するときに、加熱前に、前記画像形成層に供給する
インクにより画像を形成し、該インクの水分によって、
前記被接着物に対して仮止め可能な粘着力を生じさせる
こととし(請求項７)、これにより上記目的を達成するこ
とができる。[0013] The method for temporarily fixing a thermal transfer sheet according to the present invention comprises:
An image formation layer having an image holding function and an image formation layer having an adhesion function together with an image holding function or an image holding function on a substrate, and the image is applied to the object by heating. When transferring the image forming layer to the adherend using a thermal transfer sheet capable of transferring the forming layer, an image is formed with the ink supplied to the image forming layer before heating, and the water content of the ink is controlled. By
An adhesive force that can be temporarily fixed to the adherend is generated (claim 7), whereby the above object can be achieved.
【００１４】また、本発明に係る上記熱転写シート仮止
め方法において、 ・前記画像形成層へのインク供給を、インクジェットプ
リンタによること(請求項８)、を特徴とする。Further, in the above-mentioned method of temporarily fixing a thermal transfer sheet according to the present invention, it is preferable that the ink supply to the image forming layer is performed by an ink jet printer.
【００１５】（作用）本発明に係る熱転写シートによれ
ば、接着層や画像形成層の接着領域が水分の付与によっ
て粘着力が生じるように構成されたことで、転写操作に
際して、加熱する前に、接着領域に水分を付与してか
ら、被接着物への転写位置に熱転写シートを載置するこ
とで、熱転写シートを、接着領域の仮止め用粘着力によ
り所定の位置に仮止めすることができる。この仮止め力
により、アイロン等の熱源により擦るような加熱操作に
伴う引きずり力に対抗することができ、この仮止め状態
から、加熱の熱により最終的に所望の位置に強固に固定
することができる。(Function) According to the thermal transfer sheet of the present invention, the adhesive area of the adhesive layer or the image forming layer is configured so that the adhesive force is generated by the application of moisture. By applying moisture to the bonding area, and placing the thermal transfer sheet at the transfer position to the object to be bonded, the thermal transfer sheet can be temporarily fixed at a predetermined position by the temporary fixing adhesive force of the bonding area. it can. With this temporary fixing force, it is possible to counter the drag force accompanying a heating operation such as rubbing with a heat source such as an iron, and from this temporary fixing state, it is possible to firmly fix the final position to a desired position by the heat of heating. it can.
【００１６】なお、ここで云う“仮止め用粘着力”と
は、被接着物への染料等の染み込みや転写画像の最終的
な固定に関与する粘着力ではなく、被接着物に対して熱
転写シートを仮に保持しておくことができれば良く、転
写位置を決めるときの貼り替え操作の際に、被接着物に
損傷を与えない程度の粘着力である。The term "adhesive force for temporary fixing" as used herein is not the adhesive force involved in the penetration of a dye or the like into the adherend or the final fixation of the transferred image, but rather the thermal transfer to the adherend. It is sufficient that the sheet can be temporarily held, and the adhesive strength is such that the adherend is not damaged during the re-placing operation when determining the transfer position.
【００１７】また、本発明に係る熱転写シートによれ
ば、前記接着層或いは前記画像形成層が、加熱により接
着力を生じるとともに、水分の付与により粘着力を生じ
るように構成されていることで、接着層を単層にて両機
能を生じさせることができ、層構成が複雑化しない(請
求項２)。Further, according to the thermal transfer sheet of the present invention, the adhesive layer or the image forming layer is configured to generate an adhesive force by heating and to generate an adhesive force by applying moisture, Both functions can be provided by a single layer of the adhesive layer, and the layer configuration is not complicated (claim 2).
【００１８】本発明に係る熱転写シートによれば、前記
接着層が、加熱により接着力が生じる熱接着層と、該熱
接着層の上に水分の付与により粘着力が生じる仮止め層
との二層構造を有することで、各層の機能をより確実に
発揮することが容易になる(請求項３)。According to the thermal transfer sheet of the present invention, the adhesive layer is composed of a thermal adhesive layer having an adhesive force by heating, and a temporary fixing layer having an adhesive force by applying moisture on the thermal adhesive layer. By having a layer structure, it is easy to more reliably exhibit the function of each layer (claim 3).
【００１９】本発明に係る熱転写シートによれば、前記
基材と前記画像形成層との間に易剥離手段が設けられた
ことにより、該基材と画像形成層との剥離がより容易に
なる(請求項４)。According to the thermal transfer sheet of the present invention, the easy peeling means is provided between the substrate and the image forming layer, so that the substrate and the image forming layer can be more easily peeled. (Claim 4).
【００２０】本発明に係る熱転写シートによれば、前記
画像形成層が、インクジェット記録方式により画像形成
可能なインク受容層により構成されたことにより、水分
付与前においては、粘着性を有しないことからインクジ
ェットプリンター内を通過することができ、ユーザーの
所望する様々な画像を簡易に形成でき、画像形成後に
は、水分の付与により位置ズレすることなく正確に転写
することができる(請求項５)。According to the thermal transfer sheet of the present invention, since the image forming layer is constituted by the ink receiving layer capable of forming an image by an ink jet recording method, it does not have tackiness before water is applied. Various images desired by the user can be easily formed by passing through the inside of the ink jet printer, and after the image formation, the image can be accurately transferred without displacement due to the application of moisture (claim 5).
【００２１】本発明に係る熱転写シートによれば、シー
ト端部が前記仮止め用接着力を生じるように構成された
ことにより、画像転写の位置合わせをするときに、この
シート端部のみ接着させることで、位置合わせを容易に
できる。また、仮止めをし直すときには、接着部分がシ
ート端部であることから操作性がよい。さらに、シート
端部が非画像領域(インクジェットプリンタによる形成
画像の場合はシート端部が非画像領域となる余白部分が
形成される)である場合には、仮止め操作の時に画像領
域を手指にて触ること無くでき、画像への油分やゴミの
付着等を避けることができる(請求項６)。According to the thermal transfer sheet of the present invention, since the sheet edge portion is configured to generate the adhesive force for temporary fixing, only the sheet edge portion is adhered at the time of image transfer position adjustment. This facilitates alignment. Further, when the temporary fixing is performed again, the operability is good because the adhesive portion is the end of the sheet. Further, when the sheet edge is a non-image area (in the case of an image formed by an ink jet printer, a margin is formed where the sheet edge is a non-image area), the image area is manually held during the temporary fixing operation. This makes it possible to avoid touching the image and to prevent oil and dust from adhering to the image (claim 6).
【００２２】本発明に係る熱転写シート仮止め方法によ
れば、前記画像形成層を前記被接着物へ転写するとき
に、加熱前に、前記画像形成層に供給するインクにより
画像を形成し、該インクの水分によって、前記被接着物
に対して仮止め可能な粘着力を生じさせるので、熱転写
シートを、接着領域の仮止め用粘着力により所定の位置
に仮止めすることができ、転写位置を決めるときの操作
性が向上し、さらに、例えば、アイロン等の熱源により
擦るような加熱操作に伴う引きずり力に対抗することが
でき、この仮止め状態から、加熱の熱により最終的に所
望の位置に強固に固定することができる(請求項７)。According to the thermal transfer sheet temporary fixing method of the present invention, when the image forming layer is transferred to the adherend, an image is formed with ink supplied to the image forming layer before heating. Due to the water content of the ink, an adhesive force that can be temporarily fixed to the adherend is generated, so that the thermal transfer sheet can be temporarily fixed to a predetermined position by the temporary fixing adhesive force of the bonding area, and the transfer position can be set. The operability when deciding is improved, and further, for example, it is possible to counter the drag force accompanying a heating operation such as rubbing with a heat source such as an iron. (Claim 7).
【００２３】本発明に係る熱転写シート仮止め方法によ
れば、前記画像形成層へのインク供給を、インクジェッ
トプリンタによることで、画像形成によって、自動的に
仮止め用粘着力を発生させることができる(請求項８)。According to the thermal transfer sheet temporary fixing method of the present invention, the ink supply to the image forming layer is performed by the ink jet printer, so that the adhesive force for temporary fixing can be automatically generated by image formation. (Claim 8).
【００２４】[0024]
【発明の実施の形態】以下、本発明に係る熱転写シート
及び熱転写シート仮止め方法の一実施の形態について、
添付図に基づいて詳細に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, one embodiment of a thermal transfer sheet and a thermal transfer sheet temporary fixing method according to the present invention will be described.
This will be described in detail based on the accompanying drawings.
【００２５】（第１の実施の形態）図１は、本発明の第
１の実施の形態を示す熱転写シートを被接着物に重ね合
わせた状態における断面図であり、図２は第１の実施の
形態を示す熱転写シートの断面図である。なお、第１の
実施の形態の説明にあたっては、先ず、図２を参照して
熱転写シートを説明し、引き続いて図１を参照して転写
操作を説明する。(First Embodiment) FIG. 1 is a cross-sectional view showing a state in which a thermal transfer sheet according to a first embodiment of the present invention is superimposed on an object to be bonded, and FIG. FIG. 3 is a cross-sectional view of the thermal transfer sheet showing the embodiment. In the description of the first embodiment, first, the thermal transfer sheet will be described with reference to FIG. 2, and subsequently, the transfer operation will be described with reference to FIG.
【００２６】図２に示すように、転写シート１０は、画
像形成層２と該画像形成層２の上(図面においては下側)
に設けられた接着層３とが基材１上に易剥離手段４を介
して設けられた構成である。As shown in FIG. 2, the transfer sheet 10 is composed of an image forming layer 2 and the upper side (the lower side in the drawing) of the image forming layer 2.
And the adhesive layer 3 provided on the base material 1 via the easy peeling means 4.
【００２７】そして、画像形成層２を衣類等の被接着物
３０に転写するときは、図１に示すように、接着層３を
被接着物３０の上に重ね合わせる前に、接着層３の表面
に水を適量塗布する。この水の塗布により、接着層３の
表面に粘着力を有する粘着部５が形成される(接着層３
全体が粘着部５として機能してもよい)。この後、接着
層３を被接着物３０の上に重ね合わせる。その後、加熱
手段である例えばアイロンにより、転写領域に対応する
基材１の表面全体を加熱するように該アイロンを適当な
圧力により加圧しつつ擦り(矢印Ｘ0方向)つける。When the image forming layer 2 is to be transferred to the object 30 such as clothing, as shown in FIG. Apply an appropriate amount of water to the surface. By this application of water, an adhesive portion 5 having an adhesive force is formed on the surface of the adhesive layer 3.
The whole may function as the adhesive portion 5). Thereafter, the adhesive layer 3 is overlaid on the adherend 30. Thereafter, the iron is rubbed (in the direction of arrow X0) while being pressed with an appropriate pressure so as to heat the entire surface of the base material 1 corresponding to the transfer area by a heating means, for example, an iron.
【００２８】このように、接着層３が水の塗布によって
粘着力が生じるように構成されたことで、加熱する前
に、接着層に水分を付与してから、図１に示すように被
接着物３０への転写位置に熱転写シート１０を載置する
ことで、熱転写シート１０は、接着層３の粘着力により
所定の位置に仮止めされる。As described above, since the adhesive layer 3 is configured to have an adhesive force by application of water, water is applied to the adhesive layer before heating, and then, as shown in FIG. By placing the thermal transfer sheet 10 at the transfer position to the object 30, the thermal transfer sheet 10 is temporarily fixed at a predetermined position by the adhesive force of the adhesive layer 3.
【００２９】この仮止め用粘着力が作用することによ
り、アイロン等の熱源により擦る(矢印Ｘ0方向)ような
加熱操作に伴う引きずり力が大きくても、この引きずり
力に対抗することができ、転写位置の位置ずれを回避し
た状態で、被接着物３０と画像形成層２とは、熱によっ
て温度が上昇して接着力を生じた接着層３により最終的
に接着される。By the action of the temporary tacking adhesive force, even if the drag force accompanying a heating operation such as rubbing with a heat source such as an iron (in the direction of arrow X0) is large, the drag force can be countered. In a state in which the positional displacement is avoided, the object 30 and the image forming layer 2 are finally bonded by the bonding layer 3 whose temperature has been increased by heat to generate bonding force.
【００３０】その後、基材１を画像形成層２から離すよ
うに力を加えることにより、易剥離手段４により容易に
剥離することができ、被接着物３０上に画像形成層２が
転写される。Thereafter, by applying a force to separate the substrate 1 from the image forming layer 2, the substrate 1 can be easily peeled off by the easy peeling means 4, and the image forming layer 2 is transferred onto the adherend 30. .
【００３１】基材１としては、特に限定するものではな
く、合成樹脂、紙、合成紙等、従来知られているものを
用いることができる。The substrate 1 is not particularly limited, and conventionally known materials such as synthetic resin, paper, and synthetic paper can be used.
【００３２】基材１と画像形成層２との剥離性を高める
易剥離手段４は、剥離性樹脂層として形成することがで
き、例えばアクリル樹脂、メラミン樹脂、ビニル樹脂、
塩化オレフィン樹脂等を単独もしくは混合しても良い。
また、易剥離手段４としては、基材１の表面に、剥離性
をより高めるためにシリコンコーティングを施す構成で
あってもよい。更に、基材１との剥離を容易にするもの
として、例えば、植物ロウであるカルナバロウ,木ロウ,
オウリキュリーロウ,エスバルロウ、動物ロウである蜜
ロウ,昆虫ロウ,セラックロウ,鯨ロウ、石油ロウである
パラフィンワックス,マイクロクリスタルワックス,ポリ
エチレンワックス,エステルワックス,酸ワックス、鉱物
ロウであるモンタンロウ,オゾケライト,セレシン等のワ
ックス類を挙げることができる。The easy peeling means 4 for improving the peelability between the substrate 1 and the image forming layer 2 can be formed as a peelable resin layer, for example, an acrylic resin, a melamine resin, a vinyl resin,
A chlorinated olefin resin or the like may be used alone or in combination.
Further, the easy peeling means 4 may have a configuration in which a silicon coating is applied to the surface of the base material 1 in order to further enhance the peelability. Further, as materials that facilitate peeling from the substrate 1, for example, carnauba wax, wood wax,
Ouricy wax, esbal wax, beeswax which is animal wax, insect wax, shellac wax, whale wax, paraffin wax which is petroleum wax, micro crystal wax, polyethylene wax, ester wax, acid wax, montan wax which is mineral wax, ozokerite, ceresin And the like.
【００３３】本発明に係る熱転写シート１０において、
画像形成層２は、画像が形成された既製品として構成さ
れていてもよいが、インクジェットプリンター等の画像
形成装置により平易に画像を形成することのできるイン
ク受容層にて形成されていることが望ましい。In the thermal transfer sheet 10 according to the present invention,
The image forming layer 2 may be configured as a ready-made product on which an image is formed, but may be formed of an ink receiving layer that can easily form an image by an image forming apparatus such as an inkjet printer. desirable.
【００３４】画像形成層２がインク受容層にて構成され
ている場合、例えばインクジェットプリンタにより画像
を形成(画像形成層２にインクを供給)することにより、
このインクの水分によって、被接着物３０に対して仮止
め可能な粘着力を生じさせることができる。すなわち、
画像形成層２へのインク供給を、インクジェットプリン
タによることで、画像形成によって自動的に仮止め用粘
着力を発生させることができる。さらにシート端部が非
画像領域であるため、仮止め操作の時に粘着力が生じて
いる画像領域を手指にて触ることなくできる。さらに、
インクジェット印刷によって生じた粘着力が、インク中
の水分の蒸発によって低下した時には、非画像領域に水
分を付与させることによって、印刷領域に水分を付与す
ることなく仮止め操作を行なう事ができる。When the image forming layer 2 is composed of an ink receiving layer, for example, an image is formed by an ink jet printer (ink is supplied to the image forming layer 2).
By the moisture of the ink, an adhesive force that can be temporarily fixed to the adherend 30 can be generated. That is,
By supplying the ink to the image forming layer 2 by an ink jet printer, it is possible to automatically generate a temporary fixing adhesive force by image formation. Further, since the sheet end is a non-image area, the image area where the adhesive force is generated during the temporary fixing operation can be prevented from being touched by a finger. further,
When the adhesive force generated by the ink jet printing is reduced due to evaporation of the water in the ink, the temporary fixing operation can be performed without applying the water to the printing area by applying the water to the non-image area.
【００３５】接着層３に用いる接着剤は、例えばナイロ
ンホットメルトパウダーを用いることができるが、要
は、加熱によって接着性を付与できるものであれば、熱
硬化性樹脂でも熱可塑性樹脂であってもよい。熱硬化性
樹脂として、ポリウレタン,メラミン樹脂,エポキシ樹
脂,ユリア樹脂などを挙げることができる。熱可塑性樹
脂として、石油系樹脂類では、エチレン系共重合体,ポ
リアミド系樹脂,ポリエステル系樹脂,ポリウレタン系樹
脂,ポリアクリル系樹脂,酢酸ビニル樹脂,アイオノマー
樹脂,ポリオレフィン系樹脂,塩化ビニル系樹脂,セルロ
ース系樹脂,ロジン系樹脂など、エラストマー類では、
天然ゴム,スチレンブタジエンゴム,イソプレンゴム,ク
ロロプレンゴム,ジエン系コポリマーなど、ロジン誘導
体では、エステルガム,ロジンマレイン酸樹脂,ロジンフ
ェノール樹脂,水添ロジンなど、芳香族系炭化水素樹脂
では、フェノール樹脂,テルペン樹脂,シクロペンタジエ
ン樹脂などを挙げることができる。As the adhesive used for the adhesive layer 3, for example, nylon hot melt powder can be used. The point is that a thermosetting resin or a thermoplastic resin can be used as long as the adhesive can be imparted by heating. Is also good. Examples of the thermosetting resin include polyurethane, melamine resin, epoxy resin, and urea resin. As thermoplastic resins, petroleum resins include ethylene copolymers, polyamide resins, polyester resins, polyurethane resins, polyacrylic resins, vinyl acetate resins, ionomer resins, polyolefin resins, vinyl chloride resins, For elastomers such as cellulose resin and rosin resin,
For rosin derivatives such as natural rubber, styrene butadiene rubber, isoprene rubber, chloroprene rubber, and diene copolymers, ester gum for rosin derivatives, rosin maleic acid resin, rosin phenol resin, hydrogenated rosin, and for aromatic hydrocarbon resins, phenol resin, Terpene resins, cyclopentadiene resins and the like can be mentioned.
【００３６】水分の付与によって粘着力が生じる接着剤
としては、特にその種類を問わないが、接着剤の好まし
い例としては、にかわ、ゼラチン、カゼイン、アルブミ
ン、大豆タンパク等の蛋白質系、でんぷん、デキストリ
ン等の含水炭素系、メチルセルロース、ヒドロキシエチ
ルセルロース、エチルヒドロキシエチルセルロース、カ
ルボキシメチルセルロース、ビスロース等のセルロース
系、アラビアゴム、トラガントゴム、アルギン酸ソーダ
等の水溶性接着剤が用いられ、これらは単独あるいは２
種以上を混合して用いてもよい。また、接着性向上・塗
工性・安定性等の目的でポリビニルエチルエーテル、グ
リセリン、カセイカリや多価アルコール等を適宜配合し
てもよい。The type of adhesive which produces adhesive force by the provision of moisture is not particularly limited. Preferred examples of the adhesive include glues, gelatin, casein, albumin, protein-based proteins such as soybean protein, starch, and dextrin. And water-soluble adhesives such as cellulose cellulose such as methylcellulose, hydroxyethylcellulose, ethylhydroxyethylcellulose, carboxymethylcellulose and bisulose, gum arabic, tragacanth gum, sodium alginate and the like.
Mixtures of more than one species may be used. In addition, polyvinyl ethyl ether, glycerin, caustic potash, polyhydric alcohol, and the like may be appropriately blended for the purpose of improving adhesion, coating properties, and stability.
【００３７】加熱によって接着力を生じる成分と、水分
の付与によって接着力を生じる成分との混合比率は、そ
の成分によって種々変わるものであり、例えば９：１〜
１：９とする事ができる。The mixing ratio of the component that produces an adhesive force by heating and the component that produces the adhesive force by the provision of moisture varies depending on the component.
1: 9.
【００３８】また、インク受容層に添加する材料として
は、例えば、シリカ,炭酸カルシウム,水酸化カルシウ
ム,水酸化マグネシウム,タルク,クレー,カオリン,ケイ
ソウ土,硫酸バリウム,酸化チタン,酸化亜鉛,サチンホワ
イト,ケイ酸アルミニウム,リトポン等を挙げることがで
きる。Materials added to the ink receiving layer include, for example, silica, calcium carbonate, calcium hydroxide, magnesium hydroxide, talc, clay, kaolin, diatomaceous earth, barium sulfate, titanium oxide, zinc oxide, and satin white. , Aluminum silicate, lithopone and the like.
【００３９】又、易剥離手段４、画像形成層２、接着層
３を設ける方法としては、例えば、バーコーター、スピ
ンコーター、エアナイフコーター、ブレードコーター、
ロールコーターなどの公知装置を使用して塗布し乾燥す
る方法を採用することができる。Examples of the method of providing the easy peeling means 4, the image forming layer 2, and the adhesive layer 3 include a bar coater, a spin coater, an air knife coater, a blade coater, and the like.
A method of applying and drying using a known device such as a roll coater can be adopted.
【００４０】これら易剥離手段４、画像形成層２、接着
層３の厚さについては、厳密にいえば記録インク組成・
単位面積当りのインク打込み量等や他層との釣り合いが
取れるように設定するのが好ましいが、易剥離手段４は
１〜１５μｍ程度、接着層３は１〜２０μｍ程度、画像
形成層２(インク吸収層)は５〜４０μｍ程度が好まし
い。Strictly speaking, the thickness of the easy peeling means 4, the image forming layer 2, and the adhesive layer 3,
It is preferable to set the ink ejection amount per unit area or the like so as to be balanced with other layers, but the easy peeling means 4 is about 1 to 15 μm, the adhesive layer 3 is about 1 to 20 μm, and the image forming layer 2 (ink The absorption layer is preferably about 5 to 40 μm.
【００４１】前記画像形成層２がインク受容層にて構成
される場合は、該インク受容層に対応する記録インクの
インク組成物としては、着色剤、有機溶媒等で構成され
るものを用いることができる。なお、上記着色剤の好ま
しい例としては、顔料や直接染料、酸性染料、食料染
料、塩基性染料、反応性染料、分散染料、建築染料、可
溶性建築染料、反応分散染料、油性染料が挙げられ、い
ずれも使用できるが、中でも水溶性染料は記録液の性能
上好ましく使用される。When the image forming layer 2 is constituted by an ink receiving layer, an ink composition of a recording ink corresponding to the ink receiving layer may be constituted by a coloring agent, an organic solvent or the like. Can be. Preferred examples of the coloring agent include pigments and direct dyes, acid dyes, food dyes, basic dyes, reactive dyes, disperse dyes, building dyes, soluble building dyes, reactive disperse dyes, and oil dyes. Any of them can be used, and among them, a water-soluble dye is preferably used in terms of the performance of the recording liquid.
【００４２】顔料としては、特別な制限なしに無機顔
料、有機顔料を使用することができる。無機顔料として
は、酸化チタンおよび酸化鉄に加え、コンタクト法、フ
ァーネス法、サーマル法などの公知の方法によって製造
されたカーボンブラックを使用することができる。ま
た、有機顔料としては、アゾ顔料（アゾレーキ、不溶性
アゾ顔料、縮合アゾ顔料、キレートアゾ顔料などを含
む）、多環式顔料（例えば、フタロシアニン顔料、ベリ
レン顔料、ベリノン顔料、アントラキノン顔料、キナク
リドン顔料、ジオキサジン顔料、チオインジゴ顔料、イ
ソインドリノン顔料、キノフラロン顔料など）、染料キ
レート（例えば、塩基性染料型キレート、酸性染料型キ
レートなど）、ニトロ顔料、ニトロソ顔料、アニリンブ
ラックなどを使用できる。As the pigment, inorganic pigments and organic pigments can be used without any particular limitation. As the inorganic pigment, in addition to titanium oxide and iron oxide, carbon black produced by a known method such as a contact method, a furnace method, and a thermal method can be used. Examples of organic pigments include azo pigments (including azo lakes, insoluble azo pigments, condensed azo pigments, chelated azo pigments, etc.), and polycyclic pigments (for example, phthalocyanine pigments, berylen pigments, verinone pigments, anthraquinone pigments, quinacridone pigments, dioxazines) Pigments, thioindigo pigments, isoindolinone pigments, quinoflurone pigments, etc., dye chelates (eg, basic dye type chelates, acidic dye type chelates, etc.), nitro pigments, nitroso pigments, aniline black and the like can be used.
【００４３】これら染料の添加料は、染料の種類、溶媒
成分の種類、インクに対し要求されている特性等に依存
して決定されるが、一般にはインク全重量に対し0.2〜1
5ｗｔ％、好ましくは0.5〜10ｗｔ％の範囲が好ましい。
有機溶媒の好ましい例としては、グリセリン、エチレン
グリコール、ジエチレングリコール、トリエチレングリ
コール、プロピレングリコール、ジプロピレングリコー
ル、ヘキシレングリコール、ポリエチレングリコール、
ポリプロピレングリコール等の高沸点低揮発性の多価ア
ルコール類が用いられ、その他Ｎメチル２-ピロリド
ン、１,３-ジメチルイミダゾリジノン、モノエタノール
アミン、Ｎ，Ｎ-ジメチルエタノールアミン、Ｎ,Ｎ-ジ
メチルエタノールアミン、ジエタノールアミン、Ｎ-ｎ-
ブチルジエタノールアミン、トリイソプロパノールアミ
ン、トリエタノールアミン等の含窒素有機用剤等の水溶
性有機溶剤を印字のにじみが生じない範囲で添加するこ
とができる。更に必要なら、増粘剤、消泡剤、浸透剤、
蛍光増白剤、紫外線吸収剤、酸化防止剤、防腐剤等を適
宜配合することもできる。The additive of the dye is determined depending on the type of the dye, the type of the solvent component, the characteristics required for the ink, and the like.
A range of 5 wt%, preferably 0.5 to 10 wt% is preferred.
Preferred examples of the organic solvent include glycerin, ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, hexylene glycol, polyethylene glycol,
High-boiling, low-volatility polyhydric alcohols such as polypropylene glycol are used, and N-methyl 2-pyrrolidone, 1,3-dimethylimidazolidinone, monoethanolamine, N, N-dimethylethanolamine, N, N- Dimethylethanolamine, diethanolamine, Nn-
A water-soluble organic solvent such as a nitrogen-containing organic agent such as butyldiethanolamine, triisopropanolamine, and triethanolamine can be added to the extent that printing bleeding does not occur. If necessary, thickener, defoamer, penetrant,
A fluorescent whitening agent, an ultraviolet absorber, an antioxidant, a preservative, and the like can be appropriately blended.
【００４４】（第２の実施の形態）図３は、本発明の第
２の実施の形態を示す熱転写シートの断面図である。図
３に示す熱転写シート２０は、第１の実施の態様と同様
に、画像形成層２とこの画像形成層２の上(図面におい
ては下側)に設けられた接着層３とが基材１上に易剥離
手段４を介して設けられた構成である。しかし、本実施
の形態においては、接着層３は、加熱により接着力が生
じる熱接着層６と、該熱接着層６の上に水分付与により
粘着力が生じる仮止め層７とからなることを特徴として
いる。(Second Embodiment) FIG. 3 is a sectional view of a thermal transfer sheet showing a second embodiment of the present invention. As in the first embodiment, the thermal transfer sheet 20 shown in FIG. 3 includes the image forming layer 2 and the adhesive layer 3 provided on the image forming layer 2 (the lower side in the drawing). This is a configuration provided on the upper side via the easy peeling means 4. However, in the present embodiment, the adhesive layer 3 is composed of the thermal adhesive layer 6 whose adhesive force is generated by heating and the temporary fixing layer 7 whose adhesive force is formed on the thermal adhesive layer 6 by applying moisture. Features.
【００４５】したがって、画像形成層２を衣類等の被接
着物３０に転写するときは、第１の実施の形態の場合と
同様(図１参照)に、接着層３の仮止め層７に適量の水を
塗布する。この水の塗布により、仮止め層７は、その表
面若しくは全体が粘着力を有する層として機能し始め
る。この後、仮止め層７を被接着物３０の上に重ね合わ
せる。この後の操作については、第１の実施の形態と同
様にすることができる。Therefore, when transferring the image forming layer 2 to the adherend 30 such as clothing, an appropriate amount is applied to the temporary fixing layer 7 of the adhesive layer 3 in the same manner as in the first embodiment (see FIG. 1). Apply water. By this application of the water, the temporary fixing layer 7 starts to function as a layer having an adhesive force on the surface or the whole. Thereafter, the temporary fixing layer 7 is overlaid on the adherend 30. Subsequent operations can be performed in the same manner as in the first embodiment.
【００４６】本実施の形態の熱転写シート２０によれ
ば、接着層３が、加熱により接着力が生じる熱接着層６
と、該熱接着層６の上に水分の付与により粘着力が生じ
る仮止め層７とからなる二層構造となっていることか
ら、両層の機能(加熱により最終的に接着する機能と、
水付与に伴う粘着力による仮止め機能)をより確実に発
揮することができる。According to the thermal transfer sheet 20 of the present embodiment, the adhesive layer 3 is formed by the thermal adhesive layer 6 which generates an adhesive force by heating.
And a two-layer structure comprising a temporary fixing layer 7 that generates an adhesive force due to the provision of moisture on the heat bonding layer 6, so that the functions of both layers (the function of finally bonding by heating,
(Temporary fixing function by adhesive force accompanying water application) can be more reliably exhibited.
【００４７】（第３の実施の形態）図４は、本発明の第
３の実施の形態を示す熱転写シートの断面図である。図
４に示す熱転写シート１０aは、第１の実施の態様とは
異なり、画像形成層２aが基材１上に易剥離手段４を介
して設けられた構成である。そして、本実施の形態にお
いては、画像形成層２aは、画像保持層としての機能を
有し、さらに、加熱により接着力が生じる材料と、水分
付与により粘着力が生じる材料とを有している。(Third Embodiment) FIG. 4 is a sectional view of a thermal transfer sheet according to a third embodiment of the present invention. Unlike the first embodiment, the thermal transfer sheet 10a shown in FIG. 4 has a configuration in which the image forming layer 2a is provided on the substrate 1 via the easy peeling means 4. In the present embodiment, the image forming layer 2a has a function as an image holding layer, and further has a material that generates an adhesive force by heating and a material that generates an adhesive force by applying moisture. .
【００４８】したがって、画像形成層２aを衣類等の被
接着物３０に転写するときは、第１の実施の形態の場合
と同様(図１参照)に、接着面側に適量の水を塗布する。
この水の塗布により、画像形成層１０aは、その表面が
粘着力を有する層として機能し始める。この後、被接着
物３０の上に重ね合わせる。この後の操作については、
第１の実施の形態と同様にすることができる。Therefore, when transferring the image forming layer 2a to the adherend 30 such as clothing, an appropriate amount of water is applied to the adhesive surface side in the same manner as in the first embodiment (see FIG. 1). .
Due to the application of the water, the image forming layer 10a starts to function as a layer having an adhesive surface. Then, it is superimposed on the adherend 30. For subsequent operations,
This can be the same as in the first embodiment.
【００４９】本実施の形態の熱転写シート１０aによれ
ば、画像形成層２aは、画像保持機能（インク受容性）
に加えて、加熱により接着力が生じる機能と、水分の付
与により粘着力が生じる仮止め機能との三つの機能を有
しているので、前記両実施の形態のように、層構造にし
なくてもよく、層間の分離を考慮しなくてもよく、ま
た、層の形成工程も簡略化される。According to the thermal transfer sheet 10a of the present embodiment, the image forming layer 2a has an image holding function (ink receiving property).
In addition, since it has three functions of a function of generating an adhesive force by heating and a temporary fixing function of generating an adhesive force by applying moisture, it is not necessary to form a layer structure as in the above-described two embodiments. It is not necessary to consider the separation between the layers, and the step of forming the layers is simplified.
【００５０】なお、インク受容性と密着性(加熱により
発生する接着機能)を兼ねるものとしては、酢酸ビニル
樹脂,エチレン−酢酸ビニル共重合体、アイオノマー樹
脂,ポリエチレン,アクリル系樹脂,ポリスチレンおよび
その重合体,ポリイソプレン樹脂,ポリプロピレン,ポリ
エチレン−ポリプロピレン共重合体エラストマー,ポリ
アミド樹脂,ポリエステル系樹脂,ポリウレタン系樹脂な
どを挙げることができる。さらに、水分の付与によって
粘着力が発生する材料としては、前掲の第１の実施の形
態に示した材料を適宜用いることができる。Incidentally, those having both ink receptivity and adhesiveness (adhesion function generated by heating) include vinyl acetate resin, ethylene-vinyl acetate copolymer, ionomer resin, polyethylene, acrylic resin, polystyrene and its weight. Coalesced resin, polyisoprene resin, polypropylene, polyethylene-polypropylene copolymer elastomer, polyamide resin, polyester resin, polyurethane resin and the like. Further, as a material that generates adhesive force by the provision of moisture, the material described in the first embodiment can be appropriately used.
【００５１】（第４の実施の形態）図５は、本発明の第
４の実施の形態を示す熱転写シートの平面図である。図
５に示す熱転写シート１５は、図中において下側のシー
ト端部に仮止め用接着力を生じる仮止め部９ａが設けら
れている。本実施の形態においては、図示しないが、仮
止め部９ａの構造は、前掲の第１の実施の形態、第２の
実施の形態或いは第３の実施の形態と同様にすることが
できる。(Fourth Embodiment) FIG. 5 is a plan view of a thermal transfer sheet according to a fourth embodiment of the present invention. The thermal transfer sheet 15 shown in FIG. 5 has a temporary fixing portion 9a for generating a temporary fixing adhesive force at a lower sheet end in the drawing. In the present embodiment, although not shown, the structure of the temporary fixing portion 9a can be the same as that of the above-described first, second, or third embodiment.
【００５２】この熱転写シート１５は、例えばインクジ
ェットプリンタにより画像を形成するときには、図５に
示す矢印Ｙ方向に搬送されるように、該プリンタにセッ
トする。そして、画像形成領域８に所定の画像が形成さ
れる。この結果、非画像領域９に仮止め部９ａが位置す
ることになる。(熱転写シート１５は予め画像が形成さ
れたものであっても良い。)When an image is formed by, for example, an ink jet printer, the thermal transfer sheet 15 is set on the printer so that it is conveyed in the direction of arrow Y shown in FIG. Then, a predetermined image is formed in the image forming area 8. As a result, the temporary fixing portion 9a is located in the non-image area 9. (The thermal transfer sheet 15 may have an image formed in advance.)
【００５３】このように構成された熱転写シート１５
は、画像転写の位置合わせをするときに、仮止め部９ａ
に水を塗布する。このようにすることにより、シート端
部のみを非接着物に仮止め接着させることができ、転写
画像の位置合わせを容易にできる。また、アイロン等に
より加熱するときにおいて、仮止め部側から反対方向
(図中における矢印Ｙ方向)に擦るようにすることによ
り、シート皺等が発生することなく操作性がよい。更に
また、仮止めをし直すときには、接着部分がシート端部
の仮止め部９ａであることから、画像形成領域８を触る
ことなく再接着の操作をすることができ、本実施の形態
の構成の熱転写シート１５は、転写作業における操作性
が良い。The thermal transfer sheet 15 thus configured
The temporary fixing portion 9a is used when positioning the image transfer.
Apply water to. This makes it possible to temporarily fix only the sheet end portion to the non-adhesive, thereby facilitating the alignment of the transferred image. In addition, when heating with an iron etc., the opposite direction from the temporary fixing part side
By rubbing in the direction of arrow Y in the figure, the operability is good without generating sheet wrinkles or the like. Furthermore, when the temporary fixing is performed again, since the bonding portion is the temporary fixing portion 9a at the end of the sheet, the re-adhering operation can be performed without touching the image forming area 8, and the configuration of the present embodiment The heat transfer sheet 15 has good operability in the transfer operation.
【００５４】本実施の形態においては、図５に示すよう
に、仮止め部９ａは、熱転写シート１５の短辺に沿った
全域に形成しなくてもよく、シート角部分に設けるよう
な構成でもよい。In the present embodiment, as shown in FIG. 5, the temporary fixing portion 9a does not have to be formed over the entire area along the short side of the thermal transfer sheet 15, and may be provided at the corner of the sheet. Good.
【００５５】[0055]
【実施例】次に、本発明の実施例を比較例と共に挙げ、
本発明に係る熱転写シートについて具体的に説明する。
なお、以下の実施例および比較例を説明するにあたっ
て、前掲の図２を参照している。即ち、各実施例，比較
例で作製されたサンプルは、図２に示すように、熱転写
シート１０は、画像形成層２と該画像形成層２の上(図
面においては下側)に設けられた接着層３とが基材１上
に易剥離手段４を介して設けられた構成である。Next, examples of the present invention will be described together with comparative examples.
The thermal transfer sheet according to the present invention will be specifically described.
In describing the following examples and comparative examples, reference is made to FIG. 2 described above. That is, as shown in FIG. 2, in the samples manufactured in each of the examples and the comparative examples, the thermal transfer sheet 10 was provided on the image forming layer 2 and on the image forming layer 2 (the lower side in the drawing). In this configuration, the adhesive layer 3 is provided on the base material 1 via the easy peeling means 4.
【００５６】（実施例１）本実施例１では、基材１とし
て上質紙（１１０ｋｇ／ｍ2）の表面にシリコンコーテ
ィングを施し、さらに その上に易剥離手段４としてア
クリル樹脂コートされた基材シートを作成した。さら
に、易剥離手段４の上に画像形成層２としてエチレン・
酢酸ビニル共重合体をトルエンで溶解させた溶液をバー
コータで塗布し、乾燥させて３０μｍ形成した。接着層
３として、アラビアゴムと粒径１００μｍのナイロンホ
ットメルトパウダー１：９の比で混合し５ｇ／ｍ2にな
るようにして熱転写シート１０の実施例サンプルを作成
した。Example 1 In Example 1, a high-quality paper (110 kg / m 2 ) was coated with a silicon coating on the surface of a base material 1, and an acrylic resin-coated base material was further coated thereon as an easy-peeling means 4. Created a sheet. Further, the image forming layer 2 on the easy peeling means 4 is made of ethylene.
A solution prepared by dissolving the vinyl acetate copolymer in toluene was applied using a bar coater and dried to form a film having a thickness of 30 μm. As the adhesive layer 3, an example sample of the thermal transfer sheet 10 was prepared by mixing gum arabic and nylon hot melt powder having a particle size of 100 μm at a ratio of 1: 9 to 5 g / m 2 .
【００５７】（比較例１）比較例１として、実施例１で
作成した基材シートの接着層３にナイロンホットメルト
パウダーを５ｇ／ｍ2 塗布する以外は同じ方法で熱転写
シート１０の比較例サンプルを作成した。(Comparative Example 1) As Comparative Example 1, a comparative sample of the thermal transfer sheet 10 was prepared in the same manner except that 5 g / m 2 of nylon hot melt powder was applied to the adhesive layer 3 of the base sheet prepared in Example 1. It was created.
【００５８】これらの熱転写シート１０の実施例及び比
較例のサンプルに、セイコーエプソン株式会社製のイン
クジェットプリンターＭＪ−９１０Ｃを使用してプリン
ト図柄の印刷を行った。次に、この熱転写シートの印刷
物を、実施例サンプルでは水を塗布した状態で、比較例
サンプルではそのままで、綿１００％の生地片の上に印
刷面を生地片に密着するように設置し、その上にアイロ
ンを置き１８０℃で９０秒間ヒートプレスを行い転写生
地片を熱接着した後、基材１を剥離除去し、プリント図
柄入り転写物を、各サンプル１０個ずつ形成した。Print samples were printed on the samples of Examples and Comparative Examples of the thermal transfer sheet 10 using an inkjet printer MJ-910C manufactured by Seiko Epson Corporation. Next, the printed matter of the thermal transfer sheet was placed on a 100% cotton piece of cloth in a state where water was applied in the sample of the example, and in the sample of the comparative example so that the printing surface was in close contact with the piece of cloth, An iron was placed thereon and heat-pressed at 180 ° C. for 90 seconds to thermally bond the transfer cloth pieces. Then, the base material 1 was peeled off, and 10 prints each containing a printed pattern were formed.
【００５９】実施例サンプルの熱転写シート１０では、
転写操作を開始する当初の位置決め箇所の位置から殆ど
ズレることなくに固定することができたが、比較例サン
プルにおいては、全てのサンプルにおいて、加熱中に熱
転写シートのずれが発生してしまった。In the thermal transfer sheet 10 of the embodiment sample,
Although it was possible to fix the position of the positioning portion at the beginning of the transfer operation with little deviation from the initial position, in all of the comparative samples, the thermal transfer sheet was displaced during heating.
【００６０】[0060]
【発明の効果】以上詳記したとおり、本発明に係る熱転
写シートは、水分の付与によって仮止め用粘着力が生じ
るように構成されたので、転写操作を行う時に、所定の
領域に水分を付与してから、転写位置に熱転写シートを
接触させることで、熱転写シートを、水付与による粘着
力により所定の位置に仮止めでき、アイロンやホットプ
レス等の熱源により不測の外力による位置ズレを効果的
に防止することができ、加熱の熱により最終的な固定を
正確な位置決め下にて実施することができる。As described above in detail, the thermal transfer sheet according to the present invention is configured so that the adhesive force for temporary fixing is generated by the application of moisture. After that, by bringing the thermal transfer sheet into contact with the transfer position, the thermal transfer sheet can be temporarily fixed to a predetermined position by the adhesive force by applying water, and the positional deviation due to unexpected external force by a heat source such as an iron or a hot press is effectively performed. The final fixing can be performed under accurate positioning by the heat of heating.
【００６１】また、本発明に係る熱転写シートは、接着
層を有し、該接着層が加熱により接着力を生じるととも
に、水分の付与により粘着力を生じるように構成されて
いる場合には、接着層を単層として極めて平易な層構成
にて、仮止め機能並びに最終適な強固な固定機能の両機
能を生じさせることができる。The thermal transfer sheet according to the present invention has an adhesive layer. When the adhesive layer is configured to generate an adhesive force by heating and to generate an adhesive force by applying moisture, With a very simple layer configuration with a single layer, both the temporary fixing function and the finally suitable strong fixing function can be generated.
【００６２】本発明に係る熱転写シートは、前記接着層
が、加熱により接着力が生じる熱接着層と、水分の付与
により粘着力が生じる仮止め層とからなる二層構造とし
た場合には、層成分の調整が容易であり、両層の異なっ
た機能をより確実に発揮することができる。In the thermal transfer sheet according to the present invention, when the adhesive layer has a two-layer structure composed of a thermal adhesive layer having an adhesive force by heating and a temporary fixing layer having an adhesive force by applying moisture, Adjustment of layer components is easy, and different functions of both layers can be more reliably exhibited.
【００６３】本発明に係る熱転写シートは、基材と画像
形成層との間に易剥離手段が設けられた場合において
は、該基材と画像形成層との剥離がより容易である。In the thermal transfer sheet according to the present invention, when the easy peeling means is provided between the substrate and the image forming layer, the substrate and the image forming layer are more easily peeled.
【００６４】さらに又、本発明に係る熱転写シートは、
前記画像形成層が、インクジェット記録方式により画像
形成可能なインク受容層により構成された場合には、水
分付与前においては、粘着性を有しないことからインク
ジェットプリンター内を通過することができ、熱転写シ
ートのユーザーが所望する様々な画像を簡易に形成する
ことができ、画像形成後には水分の付与により位置ズレ
することなく正確に転写することができ、使い勝手に優
れた熱転写シートを提供することができる。Further, the thermal transfer sheet according to the present invention comprises:
When the image forming layer is constituted by an ink receiving layer capable of forming an image by an ink jet recording method, before water is applied, since the ink receiving layer does not have adhesiveness, it can pass through an ink jet printer, and a heat transfer sheet Various images desired by the user can be easily formed, and after the image formation, the transfer can be accurately performed without misalignment due to the application of moisture, and a heat transfer sheet excellent in usability can be provided. .
【００６５】本発明に係る熱転写シート仮止め方法は、
画像形成層を被接着物へ転写するときに、加熱前に、前
記画像形成層に供給するインクにより画像を形成し、こ
のインクの水分によって、前記被接着物に対して仮止め
可能な粘着力を生じさせるので、熱転写シートを、仮止
め用粘着力により所定の位置に仮止めすることができ、
転写位置を決めるときの操作性を良くすることができ
る。The method for temporarily fixing a thermal transfer sheet according to the present invention comprises:
When transferring the image forming layer to the adherend, an image is formed with the ink supplied to the image forming layer before heating, and the adhesive force that can be temporarily fixed to the adherend by the moisture of the ink. As a result, the thermal transfer sheet can be temporarily fixed at a predetermined position by the temporary fixing adhesive force,
Operability in determining the transfer position can be improved.
【００６６】また、本発明に係る熱転写シート仮止め方
法において、画像形成層へのインク供給を、インクジェ
ットプリンタにより行う場合には、該プリンタから取り
出された後に、自動的に仮止め用粘着力を発生させるこ
とができ、画像転写操作性を向上させることができる。In the thermal transfer sheet temporary fixing method according to the present invention, when the ink is supplied to the image forming layer by an ink jet printer, the adhesive force for temporary fixing is automatically reduced after the ink is taken out from the printer. Can be generated, and the image transfer operability can be improved.
【図１】本発明の一実施の形態(第１の実施の形態)であ
る熱転写シ−トの転写操作中段における断面図である。FIG. 1 is a cross-sectional view of a thermal transfer sheet according to an embodiment (a first embodiment) of the present invention at a middle stage of a transfer operation.
【図２】本発明の一実施形態(第１の実施の形態)である
熱転写シ−トの断面図である。FIG. 2 is a cross-sectional view of a thermal transfer sheet according to one embodiment (first embodiment) of the present invention.
【図３】本発明の他の実施の形態(第２の実施の態様)で
ある熱転写シ−トの断面図である。FIG. 3 is a cross-sectional view of a thermal transfer sheet according to another embodiment (second embodiment) of the present invention.
【図４】本発明の他の実施の形態(第３の実施の態様)で
ある熱転写シ−トの断面図である。FIG. 4 is a cross-sectional view of a thermal transfer sheet according to another embodiment (third embodiment) of the present invention.
【図５】本発明の他の実施の形態(第４の実施の態様)で
ある熱転写シ−トの平面図である。FIG. 5 is a plan view of a thermal transfer sheet according to another embodiment (fourth embodiment) of the present invention.
【図６】従来の熱転写シ−トの転写操作中段における断
面図である。FIG. 6 is a sectional view of a conventional thermal transfer sheet at a middle stage of a transfer operation.
１ 基材 ２ 画像記録層 ２a 画像記録層（接着機能を有した画像記録層） ３ 接着層 ４ 易剥離層 ５ 粘着部 ６ 熱接着層 ７ 仮止め層 ８ 画像形成領域 ９ 非画像領域 ９ａ 仮止め部 １０、１０a、２０、１５ 熱転写シ−ト ３０ 被接着物 DESCRIPTION OF SYMBOLS 1 Substrate 2 Image recording layer 2a Image recording layer (image recording layer having an adhesive function) 3 Adhesive layer 4 Easy peeling layer 5 Adhesive part 6 Thermal adhesive layer 7 Temporary fixing layer 8 Image forming area 9 Non-image area 9a Temporary fixing Part 10, 10a, 20, 15 Thermal transfer sheet 30 Adhesive
Claims (8)
成層および被接着物との接着機能を有する接着層もしく
は画像保持機能とともに接着機能を有する画像形成層を
有しており、加熱によって前記被接着物へ前記画像形成
層を転写可能とする熱転写シートであって、 前記接着層が水分の付与によって、前記被接着物に対し
て仮止め用粘着力が生じるように構成されたことを特徴
とする熱転写シート。An image forming layer having an image holding function and an image forming layer having an image holding function together with an image forming layer having an image holding function and an image holding function are provided on a substrate by heating. A thermal transfer sheet capable of transferring the image forming layer to the adherend, wherein the adhesive layer is configured to generate a temporary tack adhesive force to the adherend by applying moisture. Characteristic thermal transfer sheet.
記画像形成層は、加熱により接着力が生じる成分と、水
分の付与により粘着力が生じる成分とが混合されている
ことを特徴とする請求項１に記載の熱転写シート。2. The adhesive layer or the image forming layer having an adhesive function, wherein a component that produces an adhesive force by heating and a component that produces an adhesive force by applying moisture are mixed. 2. The thermal transfer sheet according to 1.
る熱接着層と、該熱接着層の上に水分付与により粘着力
が生じる仮止め層とを有していることを特徴とする請求
項１に記載の熱転写シート。3. The adhesive layer according to claim 1, wherein the adhesive layer has a thermal adhesive layer that generates an adhesive force by heating, and a temporary fixing layer that generates an adhesive force by applying moisture on the thermal adhesive layer. Item 2. The thermal transfer sheet according to Item 1.
離手段が設けられたことを特徴とする請求項１、２、又
は３に記載の熱転写シート。4. The thermal transfer sheet according to claim 1, wherein an easy peeling means is provided between the substrate and the image forming layer.
方式により画像形成可能なインク受容層により構成され
たことを特徴とする請求項１、２、３又は４に記載の熱
転写シート。5. The thermal transfer sheet according to claim 1, wherein the image forming layer comprises an ink receiving layer capable of forming an image by an ink jet recording method.
るように構成されたことを特徴とする請求項１から５の
いずれかに記載の熱転写シート。6. The thermal transfer sheet according to claim 1, wherein an end portion of the sheet is configured to generate the adhesive force for the temporary fixing.
成層および被接着物との接着機能を有する接着層もしく
は画像保持機能とともに接着機能を有する画像形成層を
有し、加熱によって前記被接着物へ前記画像形成層を転
写可能とする熱転写シートを用いて、前記画像形成層を
前記被接着物へ転写するときに、加熱前に、前記画像形
成層に供給するインクにより画像を形成し、該インクの
水分によって、前記被接着物に対して仮止め可能な粘着
力を生じさせることを特徴とする熱転写シート仮止め方
法。7. An image formation layer having an image holding function and an adhesion layer having an adhesion function to an object to be adhered or an image formation layer having an adhesion function together with an image holding function are provided on a base material. Using a thermal transfer sheet capable of transferring the image forming layer to an adhesive, when transferring the image forming layer to the adherend, before heating, forming an image with ink supplied to the image forming layer. A method of temporarily fixing a thermal transfer sheet, wherein the moisture of the ink causes an adhesive force to be temporarily fixed to the adherend.
クジェットプリンタによることを特徴とする請求項７に
記載の熱転写シート仮止め方法。8. The method according to claim 7, wherein the ink is supplied to the image forming layer by an ink jet printer.