JPH11192807A - Pneumatic tire - Google Patents

Abstract

PROBLEM TO BE SOLVED: To remove an inner line while maintaining a necessary anti air- permeability, to improve an adhesive property of a carcass cord and to enhance a durability. SOLUTION: A carcass ply 9 is formed by burrying carcass cords being disposed in arrangement and having rubber 12 coated with a peripheral rubber 11 in a topping rubber 13. The peripheral rubber layer 11 is comprised of a non-butyl mixed rubber which does not contain a butyl type rubber and a thickness T1 thereof is 0.1 mm or more and not more than a diameter D of the carcass code 10. The topping rubber 13 comprises a butyl mixed rubber which contains butyl mixed rubber.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pneumatic tire which is particularly suitable as a tubeless tire and which can achieve weight reduction while maintaining air permeability resistance.

[0002]

2. Description of the Related Art Generally, in a tubeless tire, a butyl rubber having excellent air impermeability is formed on an inner surface of a carcass facing a tire cavity in order to keep air at an internal pressure airtight. Inner liner is stuck inside.

[0003] However, even in such tubeless tires from which tubes are eliminated, further reduction in weight is desired in response to recent demands for resource saving and fuel efficiency reduction. 156007 proposes that in a carcass ply, a topping rubber covering both sides of a carcass cord is formed of butyl rubber. In this case, since the function of the inner liner can be performed by the carcass ply, the conventional inner liner can be omitted altogether, and a large weight reduction can be achieved.

[0004] However, butyl rubber has a property of being inferior in adhesiveness to diene rubber. Therefore, when this butyl rubber is used as the topping rubber, the adhesive strength between the carcass cord and the topping rubber becomes insufficient, and the durability is lowered such that peeling damage such as cord loose easily occurs. There's a problem.

Accordingly, the present invention uses a carcass cord with rubber in which the carcass cord is once covered with a peripheral rubber layer made of non-butyl compound rubber, and embeds the carcass cord with rubber in a topping rubber made of non-butyl compound rubber. It is an object of the present invention to provide a pneumatic tire in which the inner liner can be eliminated while maintaining the required air permeability, the adhesion of the carcass cord is improved, and the decrease in durability is suppressed.

[0006]

To achieve the above object, a pneumatic tire according to the present invention comprises a carcass ply in which a carcass cord is arranged from a tread portion to a bead core of a bead portion through a sidewall portion to a bead portion. A carcass is provided, and the carcass ply is formed by embedding a rubber carcass cord covered with a peripheral rubber layer around the periphery and burying the carcass cord in a topping rubber layer, and the peripheral rubber layer includes a butyl rubber in a compounded rubber. And the thickness T1 of the surrounding rubber layer is 0.1%.
mm and not more than the diameter D of the carcass cord, and the topping rubber layer is made of a butyl compound rubber containing a butyl rubber in the compound rubber.

In the topping rubber layer, the coating thickness T2 for the carcass cord with rubber is set to 0.2 to 0.2.
1.0 mm is preferable in order to reduce the weight while maintaining air permeability resistance and durability.

The natural rubber content in the butyl compound rubber is 30 to 85 phr, the butyl rubber content is 70 to 15 phr, the natural rubber content in the non-butyl compound rubber is 40 to 90 phr, and It is preferable that the content of the styrene / butadiene rubber is 60 to 10 phr, particularly from the viewpoint of air permeability resistance and durability.

[0009]

Embodiments of the present invention will be described below with reference to the drawings. In FIG. 1, a pneumatic tire 1
The tire (hereinafter referred to as a tire 1) is a radial tire for a passenger car in this example, and includes a tread portion 2, a sidewall portion 3 extending inward in a tire radial direction from both ends thereof, and an inner end of each sidewall portion 3. And a bead portion 4 located at The tire 1 has a carcass 6 extending along the tire bore H between the bead portions 4, and each bead portion 4 has a triangular cross-sectional bead extending radially outward from the bead core 5. Apex rubber 8 is provided.

The carcass 6 is formed of one or more carcass plies 9 in which carcass cords 10 are arranged at a cord angle of 75 to 90 degrees with respect to the tire equator C, in this embodiment, one carcass ply 9. The carcass ply 9 has a ply body 9A extending from the tread portion 2 to the bead core 5 of the bead portion 4 through the sidewall portion 3 and, in the present example, is connected to the ply body portion 9A and turns around the bead core 5 with a tire. It has a so-called 1-0 folded structure having a ply folded portion 9B that is folded inward from the outside in the axial direction. It should be noted that a 0-1 folded structure folded from the outside to the inside can be adopted as required.

As shown in FIG. 2, the carcass ply 9 surrounds the carcass cord 10 with a surrounding rubber layer 11.
And a topping rubber 13 for embedding a cord aligned body formed by aligning the carcass cords 12 with rubber.

The carcass cord 10 includes a textile cord obtained by twisting a plurality of organic fiber filaments such as nylon, rayon, polyester, and aromatic polyamide; a monofilament cord composed of one organic fiber filament; A metal cord obtained by twisting a plurality of wires can be employed. In this example, a polyester fiber textile cord is used as the carcass cord 10. For example, a metal cord (steel cord) is suitably used for a heavy duty tire.

The peripheral rubber layer 11 does not contain butyl rubber and uses only diene rubber such as natural rubber (NR), butadiene rubber (BR), styrene / butadiene rubber (SBR) as raw rubber. The carcass cord 10 is formed of a non-butyl compound rubber and has a coating thickness T1 within a range of 0.1 mm or more and 1.0 times or less of the diameter D of the carcass cord 10.

As the butyl rubber, butyl rubber (IIR) which is a copolymer of isobutylene and a small amount of isoprene is used.
And derivatives thereof, that is, halogenated butyl rubbers such as chlorinated butyl rubber and brominated butyl rubber obtained by reacting butyl rubber with chlorine, bromine and the like.

In the present embodiment, the peripheral rubber layer 11 is provided with 40 to 90 phr of natural rubber and 60 to 10 phr of styrene / styrene in order to exhibit excellent adhesion to both the carcass cord 10 and the topping rubber 13. A compound rubber obtained by mixing butadiene rubber is used, and 20-60 phr of HAF type (average particle size of 26 to 30 nm) carbon black is added as a reinforcing agent. The carcass cord 10 may be provided with an adhesive, which is a dipping liquid adhered when dipping, between the carcass cord 10 and the surrounding rubber layer 11.

On the other hand, the topping rubber 13 is formed from a butyl compound rubber containing the butyl rubber in the raw rubber. In this embodiment, the coating thickness T2 of the carcass cord 12 with rubber, that is, the topping rubber 13 The minimum distance from the surface to the surrounding rubber layer 11 is 0.2 to 1.0 m
m.

The above-mentioned diene rubber can be compounded in the butyl compound rubber as the remainder of the raw rubber. In this example, in order to enhance the adhesiveness to the surrounding rubber layer 11 while exhibiting excellent air permeability resistance, a compounded rubber obtained by mixing 30 to 85 phr of natural rubber and 70 to 15 phr of butyl rubber is used. And 15 to 60 phr of HAF type carbon black is added as a reinforcing agent.

As in the case of the conventional topping rubber, known fillers such as a vulcanizing agent, a vulcanization accelerator and a softener can be added to the butyl compound rubber and the non-butyl compound rubber.

As described above, the butyl compound topping rubber 13 having high air permeability has a function of surrounding the tire cavity H, so that the carcass ply 9 can function as a conventional inner liner. Elimination can achieve a significant weight reduction. Further, in the topping rubber 13, each carcass cord 10 is covered with a non-butyl compound peripheral rubber layer 11, and a large contact area between the peripheral rubber layer 11 and the topping rubber 13 is ensured. The adhesiveness is maintained high in the ply, and the occurrence of peeling damage such as cord loose can be suppressed.

Here, if the thickness T1 of the peripheral rubber layer 11 is less than 0.1 mm, the adhesiveness becomes insufficient and the peeling damage cannot be suppressed, and on the contrary, it exceeds 1.0 times the diameter D of the carcass cord 10. In addition, not only the improvement in the adhesiveness cannot be expected, but also the unnecessary increase in the thickness of the ply, which hinders the weight reduction. If the coating thickness T2 of the topping rubber 13 is less than 0.2 mm, the air permeation resistance is reduced and it is difficult to maintain the filling internal pressure. Conversely, if it exceeds 1.0 mm, the weight is hindered.

In the butyl compound rubber, if the content of the butyl rubber is less than 15 phr, the air permeation resistance becomes insufficient, and if it exceeds 70 phr, the adhesion deteriorates. If the content of carbon black is less than 15 phr, the reinforcing property is insufficient, and if it exceeds 60 phr, the carbon black becomes hard and easily cracks or the like due to large deformation.

When the content of the styrene / butadiene rubber is less than 10 phr in the non-butyl compound rubber, the strength becomes insufficient, and when it exceeds 60 phr, the flexibility is impaired.
Similarly, if the carbon black is less than 20 phr, the reinforcing property becomes insufficient, and if it exceeds 60 phr, the carbon black becomes too hard.

Further, from the viewpoint of peeling damage, the carcass ply 9 has its ply folded portion 9B extending radially outward from the bead apex rubber 8 so that the ply main portion 9A and the ply folded portion 9B are adjacent to each other. Is preferred. Thereby, the butyl compound topping rubber 13
Since the carcass ply 9 is fused together and restrains the movement of the carcass ply 9, the carcass cord itself or the peeling between the carcass ply 9 and an adjacent side wall rubber or the like is suppressed.

The belt layer 7 on the outer side in the tire radial direction of the carcass 6 is composed of a plurality of belt cords made of organic, inorganic, steel or the like arranged at a small angle of 0 ° to 70 ° with respect to the tire equator. In this example, two belt plies 7A and 7B are arranged so that the belt cords cross each other.

In this embodiment, an example of a tire for a passenger car has been described. However, the present invention can be modified in various modes such as a tire for a motorcycle or a tire for heavy loads.

[Example] The tire size is 195 / 65R15 and FIG.
Were manufactured based on the specifications in Table 1, and the air permeability, the tire weight, and the rolling resistance of each test tire were measured. The test results are shown in Table 1, and the rubber composition at that time is shown in Table 2. The test conditions are as follows.

Air resistance: The tire is mounted on a specified rim (6
JJ x 15) and the specified internal pressure (200 kp
a) was filled and left in an oven at 80 ° C. for 15 days to measure the rate of decrease in internal pressure of the tire.
The index was set to 00. The larger the value, the better the air permeation resistance. -Tire weight The weight per tire was measured, and the weight difference from the conventional product was measured. -Means lighter than conventional products.・ Rolling resistance Measure using a rolling resistance tester, and calculate the reciprocal
The index was set to 00. The larger the value, the smaller the rolling resistance and the better.

[0027]

[Table 1]

[0028]

[Table 2]

As a result of the test, the tires of the examples can exhibit excellent air permeation resistance even when the inner liner is eliminated, and can reduce the weight of the tire and improve the rolling resistance more than the conventional tire. . From Examples 1 and 3, it can be seen that the coating thickness T2 of the topping rubber needs to be 0.2 mm or more in order to make the air permeation resistance higher than that of the conventional tire.

[0030]

As described above, the pneumatic tire of the present invention has the following features.
A carcass cord with rubber is used in which the carcass cord is once covered with a surrounding rubber layer made of non-butyl compound rubber, and this rubber carcass cord is embedded in the topping rubber made of non-butyl compound rubber. While maintaining the air permeability, the inner liner can be eliminated, and the adhesion of the carcass cord can be improved and the decrease in durability can be suppressed.

[Brief description of the drawings]

FIG. 1 is a sectional view of a tire showing one embodiment of the present invention.

FIG. 2 is a sectional view illustrating a carcass ply.

[Explanation of symbols]

 2 Tread 3 Sidewall 4 Bead 5 Bead core 6 Carcass 9 Carcass ply 10 Carcass cord 11 Peripheral rubber layer 12 Carcass cord with rubber 13 Topping rubber

Claims (3)

[Claims] 1. A carcass comprising a carcass ply having a carcass cord arranged from a tread portion to a bead core of a bead portion extending from a tread portion to a side wall portion, wherein the carcass ply is provided with a rubber covered by a peripheral rubber layer. The carcass cords are aligned and buried in the topping rubber, and the surrounding rubber layer is made of non-butyl compound rubber containing no butyl rubber in the compound rubber, and the thickness T1 of the surrounding rubber layer is set to 0. 2. The pneumatic tire according to claim 1, wherein the topping rubber is 1 mm or more and a diameter D or less of the carcass cord, and the topping rubber is a butyl compound rubber containing a butyl rubber in the compound rubber. 2. The pneumatic tire according to claim 1, wherein the topping rubber has a coating thickness T2 of 0.2 to 1.0 mm with respect to the carcass cord with rubber. 3. The butyl compound rubber has a natural rubber content of 30 to 85 phr and a butyl rubber content of 70 to 70 phr.
3. The pneumatic device according to claim 1, wherein the non-butyl compound rubber has a natural rubber content of 40 to 90 phr and a styrene / butadiene rubber content of 60 to 10 phr. tire.