JPH1118627A - Fishing matter having decorative layer - Google Patents
Fishing matter having decorative layerInfo
- Publication number
- JPH1118627A JPH1118627A JP17997997A JP17997997A JPH1118627A JP H1118627 A JPH1118627 A JP H1118627A JP 17997997 A JP17997997 A JP 17997997A JP 17997997 A JP17997997 A JP 17997997A JP H1118627 A JPH1118627 A JP H1118627A
- Authority
- JP
- Japan
- Prior art keywords
- main body
- layer
- matter
- fishing
- decorative layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、リール、釣り竿、
小物用品等に用いられる装飾層を有する釣り用部材に関
する。The present invention relates to a reel, a fishing rod,
The present invention relates to a fishing member having a decorative layer used for accessories and the like.
【０００２】[0002]
【従来の技術】近年、釣り竿やリール等の釣り用具に
は、釣り人の趣味に訴え、また高級感や重宝感を出すた
めに、様々な装飾を施して優れた外観を得ている。この
ため、これらに用いられる釣り用部材には、優れた外観
を示すように、種々の装飾層が設けられている。2. Description of the Related Art In recent years, fishing gear such as fishing rods and reels have been provided with various decorations to obtain an excellent appearance in order to appeal to the hobby of anglers and to give a sense of quality and usefulness. For this reason, various decorative layers are provided on the fishing member used for them so as to show an excellent appearance.
【０００３】一方、近年の釣り用具は軽量化を図ること
が重要であり、種々の部材の軽量化がなされている。し
たがって、部材本体の重量が軽くなってきているので、
部材重量における塗装層の割合が大きくなってきてい
る。このため、塗装層や装飾層は、上述した釣り用具の
軽量化を妨げる大きな原因となっている。そこで、特開
平７−３１３３７号公報では、アルミニウムやマグネシ
ウム等の金属製部材上に塗装層を形成し、その上に干渉
薄膜を装飾層として用いたものが開示されている。On the other hand, it is important to reduce the weight of recent fishing gear, and various members have been reduced in weight. Therefore, since the weight of the member body is becoming lighter,
The proportion of the coating layer in the member weight has been increasing. For this reason, the painted layer and the decorative layer are a major factor that hinders the weight reduction of the fishing gear described above. Therefore, Japanese Patent Application Laid-Open No. Hei 7-31337 discloses a technique in which a coating layer is formed on a metal member such as aluminum or magnesium and an interference thin film is used as a decorative layer thereon.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、釣り用
具は、海水や水等が付着し易い厳しい環境下で使用され
るので、この干渉薄膜だけでは、耐食性に問題がある。
このため、金属製部材の腐食により変色が起こり、外観
を損なうことになる。However, since fishing equipment is used in a severe environment where seawater, water and the like easily adhere, there is a problem in corrosion resistance using only the interference thin film.
For this reason, discoloration occurs due to corrosion of the metal member, and the appearance is impaired.
【０００５】また、干渉薄膜は、虹色を呈するので、下
地の塗装層との間の色調差が大きい。さらに、干渉薄膜
は、柔らかい塗装層上に形成しているので、傷が付き易
い。このため、干渉薄膜に傷が入ると、下地の塗装層が
露出して、傷が目立ってしまうという問題がある。Further, since the interference thin film exhibits a rainbow color, the color tone difference between the interference thin film and the underlying coating layer is large. Further, since the interference thin film is formed on the soft coating layer, it is easily scratched. For this reason, when the interference thin film is damaged, there is a problem that the underlying coating layer is exposed and the damage is conspicuous.
【０００６】本発明はかかる点に鑑みてなされたもので
あり、優れた外観を示し、耐食性に優れ、しかも軽量で
ある装飾層を有する釣り用部材を提供することを目的と
する。The present invention has been made in view of the above circumstances, and has as its object to provide a fishing member having a decorative layer which has an excellent appearance, is excellent in corrosion resistance, and is lightweight.
【０００７】[0007]
【課題を解決するための手段】本発明は、上記課題を解
決するために以下の手段を講じた。すなわち、本発明
は、部材本体と、この部材本体上に形成された塗装層
と、この塗装層上に設けられ、無色透明な無機物を含み
光沢を有する装飾層とを具備することを特徴とする装飾
層を有する釣り用部材を提供する。According to the present invention, the following means are provided to solve the above-mentioned problems. That is, the present invention is characterized by comprising a member main body, a coating layer formed on the member main body, and a decorative layer provided on the coating layer and containing a colorless and transparent inorganic substance and having luster. A fishing member having a decorative layer is provided.
【０００８】また、本発明は、部材本体と、この部材本
体上に形成された塗装層と、この塗装層上に設けられ、
白色光の反射率が２０％を超える装飾層とを具備するこ
とを特徴とする装飾層を有する釣り用部材を提供する。Further, the present invention provides a member main body, a coating layer formed on the member main body, and provided on the coating layer.
A fishing member having a decorative layer, comprising: a decorative layer having a reflectance of white light of more than 20%.
【０００９】これらの構成によれば、単色で下地塗装層
の色との間の色調差がなくなる。このため、表面に傷が
付いても傷が目立たない。その結果、長期間にわたって
装飾外観を維持することができる。According to these configurations, there is no difference in color tone between the single color and the color of the undercoat layer. Therefore, even if the surface is scratched, the scratch is not noticeable. As a result, the decorative appearance can be maintained for a long time.
【００１０】上記発明においては、部材本体は、金属製
部材上に防食被膜が形成されてなることが好ましい。こ
の構成によれば、上記発明に加えてさらに、海水、水、
魚のぬめり、異物等が付着した場合、巻取り操作中に他
物に衝突した場合、誤って落下した場合、強負荷巻取り
時に局部的に負荷が加わった場合等が想定される釣り場
での使用においても、金属製部材の防食により、部材本
体の強度維持を図りながら、装飾層による優れた外観を
維持することができる。In the above invention, the member main body is preferably formed by forming an anticorrosion coating on a metal member. According to this configuration, in addition to the above-described invention, seawater, water,
Use at fishing spots where it is assumed that the fish is slimmed, foreign matter is attached, collides with other objects during the winding operation, falls accidentally, or if a load is locally applied during winding with heavy load. In this case, the corrosion prevention of the metal member can also maintain the strength of the member body and maintain the excellent appearance of the decorative layer.
【００１１】また、本発明は、部材本体と、この部材本
体上に形成された金属被膜で構成された装飾層と、この
装飾層上に設けられた防食被膜とを具備することを特徴
とする装飾層を有する釣り用部材を提供する。Further, the present invention is characterized by comprising a member main body, a decorative layer composed of a metal film formed on the member main body, and an anticorrosion coating provided on the decorative layer. A fishing member having a decorative layer is provided.
【００１２】この構成によれば、装飾層である金属被膜
上に防食被膜を形成するので、金属被膜の腐食を防止す
ることができ、これにより装飾性能を維持することがで
きる。また、この構成では、塗装層よりも硬度が高くな
るので、上述したように、厳しい環境である釣り場での
使用においても傷が付きにくいものとなる。According to this structure, since the anticorrosion film is formed on the metal film serving as the decoration layer, the corrosion of the metal film can be prevented, whereby the decoration performance can be maintained. Further, in this configuration, since the hardness is higher than that of the coating layer, as described above, it is difficult to be damaged even when used in a fishing environment where the environment is severe.
【００１３】[0013]
【発明の実施の形態】以下、本発明の実施の形態を図面
を参照して具体的に説明する。図１は本発明の装飾層を
有する釣り用部材の一実施形態を示す断面図である。図
中１は部材本体を示す。部材本体１上には、塗装層２が
設けられている。塗装層２上には、無色透明な薄膜で構
成された装飾層３が形成されている。Embodiments of the present invention will be specifically described below with reference to the drawings. FIG. 1 is a sectional view showing an embodiment of a fishing member having a decorative layer according to the present invention. In the drawing, reference numeral 1 denotes a member main body. A coating layer 2 is provided on the member body 1. On the coating layer 2, a decorative layer 3 composed of a colorless and transparent thin film is formed.
【００１４】部材本体１の材料としては、アルミニウム
合金、マグネシウム合金、純チタン、チタン合金、亜鉛
合金、鉄合金等の金属；ポリアミド樹脂、ガラス繊維強
化ポリアミド樹脂、ＡＢＳ（アクリロニトリル−ブタジ
エン−スチレン）樹脂、ガラス繊維強化ＡＢＳ樹脂、ポ
リカーボネート樹脂等の合成樹脂；酸化ジルコニウム、
酸化アルミニウム、炭化ケイ素、窒化ケイ素等のセラミ
ックス等を用いることができる。Examples of the material of the member body 1 include metals such as aluminum alloy, magnesium alloy, pure titanium, titanium alloy, zinc alloy, and iron alloy; polyamide resin, glass fiber reinforced polyamide resin, ABS (acrylonitrile-butadiene-styrene) resin. Synthetic resins such as glass fiber reinforced ABS resin and polycarbonate resin; zirconium oxide;
Ceramics such as aluminum oxide, silicon carbide, and silicon nitride can be used.
【００１５】部材本体１が金属である場合には、上記材
料で構成された金属製部材上に陽極酸化処理、クロム酸
処理、リン酸処理、すず酸処理等の化成処理により防食
被膜を設けても良い。この場合、防食被膜の厚さとして
は、耐食性を考慮して１〜１５μｍであることが好まし
い。このように、金属製部材上に防食被膜を形成してな
る部材本体を釣り用部材として用いることにより、釣り
用具の耐食性が向上するので、使用環境が厳しい釣り場
においても、部材の変色が防止され、優れた外観を維持
することができる。When the member body 1 is made of a metal, an anticorrosion coating is formed on the metal member made of the above-mentioned material by a chemical conversion treatment such as anodizing treatment, chromic acid treatment, phosphoric acid treatment, and stannic acid treatment. Is also good. In this case, the thickness of the anticorrosion coating is preferably 1 to 15 μm in consideration of corrosion resistance. As described above, since the corrosion resistance of the fishing gear is improved by using the member body obtained by forming the anticorrosion coating on the metal member as a fishing member, discoloration of the member is prevented even in a fishing environment where the use environment is severe. , Excellent appearance can be maintained.
【００１６】塗装層２としては、アクリル系塗料、ウレ
タン系塗料、エポキシ系塗料、シリコーン系塗料、フッ
素系塗料、フェノール系塗料等の塗料を塗布乾燥するこ
とにより得られた層を用いることができる。これらの塗
料は、用途に応じて適宜選択して使用する。また、塗装
層２の厚さとしては、耐食性及び寸法変化を考慮して５
〜５０μｍであることが好ましい。As the coating layer 2, a layer obtained by applying and drying a paint such as an acrylic paint, a urethane paint, an epoxy paint, a silicone paint, a fluorine paint or a phenol paint can be used. . These paints are appropriately selected and used according to the application. The thickness of the coating layer 2 is set to 5 in consideration of corrosion resistance and dimensional change.
It is preferably from 50 μm to 50 μm.
【００１７】装飾層３の無色透明の無機物としては、Ｔ
ｉＯ、ＴｉＯ2 、ＺｎＳ、ＳｉＯ、Ｉｎ2 Ｏ3 、ＭｇＦ
2 、Ａｌ2 Ｏ3 等の金属酸化物、金属弗化物を用いるこ
とができる。これらの無機物は、単層でも複数層でも良
い。The colorless and transparent inorganic substance of the decorative layer 3 includes T
iO, TiO 2 , ZnS, SiO, In 2 O 3 , MgF
2 , metal oxides such as Al 2 O 3 and metal fluorides can be used. These inorganic substances may be a single layer or a plurality of layers.
【００１８】ここで、無色透明とは、完全に無色透明で
ある必要はなく、下地の色が認識できる程度に僅かに着
色されている場合や半透明である場合を含む意味であ
る。また、光沢を有するとは、金属の様な光沢であるこ
とを意味する。Here, "colorless and transparent" does not need to be completely colorless and transparent, but includes a case where the base is slightly colored to a recognizable color or a case where it is translucent. Also, having gloss means having a luster like a metal.
【００１９】装飾層３を形成する方法としては、真空蒸
着法、スパッタリング法、イオンプレーティング法等の
ＰＶＤ（物理的気相成長）法や、Ｐ−ＣＶＤ（プラズマ
ＣＶＤ）、ＭＯＣＶＤ（有機金属ＣＶＤ）法等のＣＶＤ
（化学的気相成長）法が挙げられる。As a method for forming the decorative layer 3, a PVD (physical vapor deposition) method such as a vacuum evaporation method, a sputtering method, an ion plating method, P-CVD (plasma CVD), and MOCVD (organic metal CVD) ) CVD etc.
(Chemical vapor deposition) method.
【００２０】装飾層３の厚さとしては、無色透明にする
ことを考慮して１ｎｍ〜１μｍであることが好ましい。
このように、装飾層３の厚さは、比較的薄いので、部材
における寸法の厳しい部分に装飾層３を問題なく設ける
ことができる。The thickness of the decorative layer 3 is preferably 1 nm to 1 μm in consideration of making the layer colorless and transparent.
As described above, since the thickness of the decorative layer 3 is relatively thin, the decorative layer 3 can be provided in a portion where the dimension is severe in the member without any problem.
【００２１】装飾層３の白色光に対する反射率は２０
％、好ましくは５０％を超えるように設定する。これに
より、外観を金属の様に見せることができる。このよう
に、図１に示す実施形態は、塗装層２上に無色透明な無
機物を含む光沢を有する装飾層３を設けたことを特徴と
しており、装飾層３の色調と下地である塗装層２との間
の色調差がほとんどない。したがって、取り扱い中に誤
って落下したり、他物が衝突して装飾層に傷が付いて
も、傷が目立たなく、優れた外観を常時維持することが
できる。The reflectivity of the decorative layer 3 for white light is 20.
%, Preferably more than 50%. Thereby, the appearance can be made to look like a metal. As described above, the embodiment shown in FIG. 1 is characterized in that the decorative layer 3 having luster containing a colorless and transparent inorganic substance is provided on the coating layer 2, and the color tone of the decorative layer 3 and the coating layer 2 serving as a base are provided. There is almost no color difference between Therefore, even if the decorative layer is accidentally dropped during handling, or collides with another object to scratch the decorative layer, the scratch is not noticeable and an excellent appearance can be always maintained.
【００２２】図２は本発明の装飾層を有する釣り用部材
の他の実施形態を示す断面図である。部材本体１上に
は、金属被膜４が形成されている。金属被膜４上には、
防食被膜５が形成されている。FIG. 2 is a sectional view showing another embodiment of a fishing member having a decorative layer according to the present invention. On the member main body 1, a metal coating 4 is formed. On the metal coating 4,
An anticorrosion coating 5 is formed.
【００２３】部材本体１は、図１に示す実施形態で使用
するものと同じであるので、その詳細な説明は省略す
る。金属被膜４の材料としては、Ｃｒ，Ｚｎ，Ｓｎ，Ａ
ｌ，Ｎｉ，Ｔｉ，Ｆｅ等を用いることができる。金属被
膜４の形成方法としては、湿式メッキ法、ＰＶＤ法、Ｃ
ＶＤ法等を挙げることができる。これらの方法は、金属
被膜４の材料に応じて適宜選択する。また、金属被膜４
の厚さとしては、後工程で防食処理をすることを考慮し
て０．１〜１０μｍであることが好ましい。The member main body 1 is the same as that used in the embodiment shown in FIG. 1, and a detailed description thereof will be omitted. The material of the metal coating 4 may be Cr, Zn, Sn, A
1, Ni, Ti, Fe, etc. can be used. Examples of the method for forming the metal film 4 include a wet plating method, a PVD method, and a C method.
VD method and the like can be mentioned. These methods are appropriately selected according to the material of the metal coating 4. The metal coating 4
The thickness is preferably 0.1 to 10 μm in consideration of anticorrosion treatment in a later step.
【００２４】防食被膜５は、上記金属被膜４に陽極酸化
処理、クロム酸処理、リン酸処理、すず酸処理等の化成
処理を施して形成する。このように、図２に示す実施形
態は、防食被膜５により、部材本体及び金属被膜４が保
護された構成であるので、装飾層である金属被膜の腐食
を防止して、装飾性能の劣化を確実に防止でき、常時優
れた外観を保つことができる。The anticorrosion coating 5 is formed by subjecting the metal coating 4 to a chemical conversion treatment such as anodizing treatment, chromic acid treatment, phosphoric acid treatment, and stannic acid treatment. As described above, in the embodiment shown in FIG. 2, since the member main body and the metal coating 4 are protected by the anticorrosion coating 5, the corrosion of the metal coating serving as the decoration layer is prevented, and the deterioration of the decoration performance is prevented. Prevention can be reliably prevented, and excellent appearance can be always maintained.
【００２５】また、この構成では、塗装層よりも硬度が
高くなるので、落下や他物の衝突が想定される使用環境
が厳しい釣り場での使用においても傷が付きにくいもの
となる。Further, in this configuration, since the hardness is higher than that of the coating layer, it is unlikely to be damaged even when used in a fishing place where the use environment in which dropping or collision of other objects is assumed is severe.
【００２６】上記実施形態においては、必要に応じて最
外層や中間層に保護層や塗装層として、フッ素樹脂塗
料、エポキシ樹脂塗料等を塗布乾燥してなる層を設けて
も良い。それらの厚さには、特に制限はない。In the above embodiment, if necessary, a layer formed by applying and drying a fluororesin paint, an epoxy resin paint or the like may be provided as a protective layer or a coating layer on the outermost layer or the intermediate layer. There is no particular limitation on their thickness.
【００２７】次に、本発明の効果を明確にするために行
った実施例について説明する。 （実施例１)アルミニウム合金で成形したリールカバー
本体を陽極酸化処理して、リールカバー本体上に防食被
膜としてアルマイト被膜を厚さ３μｍで形成した。Next, an embodiment performed to clarify the effect of the present invention will be described. (Example 1) An anodizing treatment was performed on a reel cover body formed of an aluminum alloy to form an alumite film having a thickness of 3 µm on the reel cover body as an anticorrosion film.
【００２８】次いで、この上にウレタン系塗料を塗布
し、乾燥して厚さ２０μｍのメタリック塗装層を形成し
た。さらに、メタリック塗装層上に、無機物として酸化
チタンと酸化ケイ素を含有する光沢を有する装飾層をイ
オンプレーティング法により厚さ５００ｎｍで形成し
た。Next, a urethane-based paint was applied thereon and dried to form a metallic coating layer having a thickness of 20 μm. Further, a glossy decorative layer containing titanium oxide and silicon oxide as inorganic substances was formed to a thickness of 500 nm on the metallic coating layer by an ion plating method.
【００２９】このようにして得られたリールカバーを用
いたリールは、表面に傷が付いても傷が目立たなく、長
期間にわたって装飾外観を維持することができた。ま
た、部材本体には、アルマイト被膜が形成されているの
で、耐食性も向上して性能劣化や変色が起こらないもの
であった。The reel using the reel cover thus obtained was not noticeable even if the surface was damaged, and the decorative appearance could be maintained for a long period of time. Further, since the alumite film was formed on the member main body, the corrosion resistance was improved and the performance was not deteriorated or discolored.
【００３０】（実施例２）アルミニウム合金で成形した
リールカバー本体にスパッタリング法により装飾層であ
るＴｉ被膜を厚さ２μｍで形成した。Example 2 A Ti coating as a decorative layer was formed to a thickness of 2 μm on a reel cover body formed of an aluminum alloy by a sputtering method.
【００３１】次いで、このＴｉ被膜に陽極酸化処理を施
すことにより、防食被膜であるＴｉＯ2 被膜を厚さ１μ
ｍで形成した。このようにして得られたリールカバーを
用いたリールは、部材本体の腐食を防止することがで
き、これにより装飾性能を維持することができる。ま
た、厳しい環境である釣り場で使用しても傷が付きにく
いものであった。Next, by subjecting the Ti film to an anodic oxidation treatment, a TiO 2 film serving as an anticorrosion film having a thickness of 1 μm was formed.
m. The reel using the reel cover obtained in this manner can prevent the corrosion of the member main body, thereby maintaining the decorative performance. In addition, even when used in a fishing environment where the environment is harsh, it is difficult to damage.
【００３２】なお、上記実施例においては、装飾層を有
する釣り用部材がリールカバーである場合について説明
しているが、本発明は、リール以外の釣り竿、ルアー、
釣り道具箱、友舟等の釣り用具全般に使用することがで
きる。In the above embodiment, the case where the fishing member having the decorative layer is a reel cover has been described. However, the present invention relates to a fishing rod other than a reel, a lure,
It can be used for all fishing equipment such as fishing equipment boxes and friendships.
【００３３】[0033]
【発明の効果】以上説明したように本発明の装飾層を有
する釣り用部材は、優れた外観を示し、耐食性に優れ、
しかも軽量である装飾層を有するものである。As described above, the fishing member having the decorative layer according to the present invention has an excellent appearance, excellent corrosion resistance,
Moreover, it has a lightweight decorative layer.
【図１】本発明に係る装飾層を有する部材の一実施形態
を示す断面図。FIG. 1 is a sectional view showing an embodiment of a member having a decorative layer according to the present invention.
【図２】本発明に係る装飾層を有する部材の他の実施形
態を示す断面図。FIG. 2 is a sectional view showing another embodiment of a member having a decorative layer according to the present invention.
１ 部材本体 ２ 塗装層 ３ 装飾層 ４ 金属被膜 ５ 防食被膜 DESCRIPTION OF SYMBOLS 1 Member main body 2 Painting layer 3 Decorative layer 4 Metal coating 5 Corrosion-resistant coating
Claims (4)
た塗装層と、この塗装層上に設けられ、無色透明な無機
物を含み光沢を有する装飾層とを具備することを特徴と
する装飾層を有する釣り用部材。1. A decoration comprising a member main body, a coating layer formed on the member main body, and a decoration layer provided on the coating layer and containing a colorless and transparent inorganic substance and having a gloss. A fishing member having a layer.
た塗装層と、この塗装層上に設けられ、白色光の反射率
が２０％を超える装飾層とを具備することを特徴とする
装飾層を有する釣り用部材。2. A member comprising: a member main body; a coating layer formed on the member main body; and a decorative layer provided on the coating layer and having a reflectance of white light exceeding 20%. A fishing member having a decorative layer.
形成されてなる請求項１または請求項２に記載の装飾層
を有する釣り用部材。3. The fishing member having a decorative layer according to claim 1, wherein the member main body has a corrosion-resistant coating formed on a metal member.
た金属被膜で構成された装飾層と、この装飾層上に設け
られた防食被膜とを具備することを特徴とする装飾層を
有する釣り用部材。4. A decorative layer comprising: a member main body; a decorative layer formed of a metal film formed on the member main body; and an anticorrosion coating provided on the decorative layer. Fishing parts.