JPH11152477A - Production of granular asphalt - Google Patents

Production of granular asphalt

Info

Publication number
JPH11152477A
JPH11152477A JP36246297A JP36246297A JPH11152477A JP H11152477 A JPH11152477 A JP H11152477A JP 36246297 A JP36246297 A JP 36246297A JP 36246297 A JP36246297 A JP 36246297A JP H11152477 A JPH11152477 A JP H11152477A
Authority
JP
Japan
Prior art keywords
asphalt
solution
granular
stirring
adhesion agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP36246297A
Other languages
Japanese (ja)
Inventor
Naotada Hasegawa
直忠 長谷川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to JP36246297A priority Critical patent/JPH11152477A/en
Publication of JPH11152477A publication Critical patent/JPH11152477A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To simply produce a granular asphalt excellent in anti-adhesion properties by dropping and bringing a thermally molten asphalt into contact with a solution under cooling and stirring. SOLUTION: The thermally molten asphalt is dropped and brought into contact with a solution under cooling and stirring. The melting temperature of the asphalt is preferably about 120-200 deg.C. The dropping of the asphalt is preferably carried out in the form of a drip, a thread or the like. A lower alcohol such as methyl alcohol is preferred as the solution from the aspects of low viscosity and excellent volatility. The solution is preferably cooled to <=10 deg.C with a usual cooling device and preferably stirred at 100-500 r.p.m. with a usual stirring device. When the use of an anti-adhesion agent is required, the anti-adhesion agent in an amount of 0.5-5 pts.wt. based on 100 pts.wt. granular asphalt is preferably used. For example, silica or calcium carbonate is cited as the anti-adhesion agent.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【産業上の利用分野】本発明は、貯蔵、包装、輸送など
の取り扱いが簡便な粒状アスファルトの製造方法に関す
るものである。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing granular asphalt which is easy to handle such as storage, packaging and transportation.

【0002】[0002]

【従来の技術】アスファルトは、その安価さと、その接
着力、結合力、防水性、防錆性、電気絶縁性などの特性
を有していることから、道路舗装材、防水材、防錆材、
電気絶縁材、防振材、防音材等として広く使用されてい
る。しかし、このアスファルトは、用途によって、加熱
して使用するストレートアスファルトや、ブローンアス
ファルトといったものや、常温で使用されるカットバッ
クアスファルトやアスファルト乳剤といったような、液
体アスファルトによるものがあるが、しかし、加熱して
使用するストレートアスファルトやブローンアスファル
ト等によるものは、常温では固体または半固体であるた
め、その使用に際しては、作業に適した粘度に絶えず加
熱しておく必要があり、これが貯蔵、輸送時での不便さ
と相俟って、アスファルトの熱劣化によることも問題で
あった。
2. Description of the Related Art Asphalt has properties such as low cost, adhesive strength, bonding strength, waterproofness, rustproofness, and electrical insulation. ,
It is widely used as an electrical insulating material, a vibration proof material, a sound proof material and the like. However, this asphalt, depending on the application, such as straight asphalt and blown asphalt to be used by heating, and liquid asphalt such as cutback asphalt and asphalt emulsion used at room temperature, but, Since straight or blown asphalt is used as a solid or semi-solid at room temperature, it must be constantly heated to a viscosity suitable for work. Combined with the inconvenience of the above, there is also a problem that the asphalt is thermally degraded.

【0003】そこで、これらの欠点を解消するためにア
スファルトを石油系溶剤に溶かしてカットバックアスフ
ァルトとしたものや、アスファルトを水中に乳化、分散
させてアスファルト乳剤とした液体アスファルトによる
ものがあるが、しかし、前者のカットバックアスファル
トによるものは、ストレートアスファルトやブローンア
スファルトのように常時アスファルトを、加熱、溶融し
ておかなければならないといったことはないので、その
取り扱いや施工は簡単であるが、施工後溶剤が蒸発する
までに長期養生が必要であるといったことや、その溶剤
のもつ、毒性、火災性、環境汚染等といったことが問題
であった。また後者のアスファルト乳剤によるものは、
上述のカットバックアスファルトによるものと同様、そ
の取り扱いや施工は容易であるが、しかしその反面アス
ファルトの乳化に際しては、多量の乳化剤や安定剤を用
いていることや水が介在している等のことから、乳化後
のアスファルトの諸物性は、元のアスファルトの諸物性
に比して劣るといったことや、乳剤が長期保存に適しな
いといったことや、施工後水分の蒸発に長期養生が必要
であるといったことが問題であった。
[0003] In order to solve these drawbacks, there are a cut asphalt obtained by dissolving asphalt in a petroleum solvent, and a liquid asphalt obtained by emulsifying and dispersing asphalt in water to obtain an asphalt emulsion. However, as for the former cutback asphalt, asphalt does not have to be heated and melted constantly like straight asphalt and blown asphalt, so its handling and construction is easy, but after construction There have been problems in that long-term curing is required before the solvent evaporates, and that the solvent has toxicity, fire, environmental pollution, and the like. In the case of the latter asphalt emulsion,
As with the cutback asphalt described above, it is easy to handle and construct, but on the other hand, when emulsifying asphalt, a large amount of emulsifiers and stabilizers are used and water is interposed Therefore, the physical properties of the asphalt after emulsification are inferior to the physical properties of the original asphalt, that the emulsion is not suitable for long-term storage, and that long-term curing is required for evaporation of water after construction That was the problem.

【0004】これらのことから近年アスファルトの粒状
化による試みがなされている。これには、アスファルト
を凍結させて後、機械的に粉砕する方法やアスファルト
をスプレードライして粒状化した後マイクロカプセル化
する方法や、アスファルトをシート状やストランド状に
成形冷却後、所定の形状に切断してペレット化する方法
等が知られている。しかし、アスファルトを凍結した後
粉砕させる方法によるものは、アスファルトや粉砕機を
−10℃〜−20℃といったような極低温下にしておか
ないと、アスファルトが粉砕機の摩擦熱によって粉砕で
きないとか、また、たとえそれが粉砕できたとしても、
貯蔵時そのアスファルト粉の付着防止をどうするかとい
ったことが問題であった。また、アスファルトをマイク
ロカプセル化する方法によるものは、上述の凍結粉砕に
よる方法に比べて、粉状アスファルトの付着防止といっ
たことでは、優れているが、しかし、アスファルトを1
00μm以下の微粒子にしてカプセル化するというのは
極めて特殊な設備が必要となるため、経済性に劣るもの
であった。また一方ペレット化による方法であるが、こ
れは高温時のアスファルトが引張り強さに欠けることか
ら、アスファルトをシート状はストランド状にうまく引
き出せないとか、たとえうまく引き出せたととしても、
アスファルトが有する粘着性によって、うまくペレット
状に、切断できないとか、ペレット化したアスファルト
の付着防止を、どうするかといった事が問題であった。
[0004] For these reasons, attempts have recently been made to granulate asphalt. This includes freezing the asphalt and then mechanically pulverizing it, spray-drying the asphalt into granules after granulation, and forming the asphalt into a sheet or strand, cooling it into a predetermined shape, There is known a method of cutting into pellets. However, according to the method of crushing after asphalt is frozen, unless the asphalt or the crusher is kept at an extremely low temperature such as -10 ° C to -20 ° C, the asphalt cannot be crushed by friction heat of the crusher, Also, even if it can be crushed,
The problem was how to prevent the asphalt powder from adhering during storage. The method of microencapsulating asphalt is superior to the above-mentioned method of freeze pulverization in terms of preventing powdery asphalt from adhering.
Encapsulation into fine particles of not more than 00 μm requires very special equipment, and is inferior in economical efficiency. On the other hand, it is a method by pelletization, but this is because asphalt at high temperature lacks tensile strength, so that asphalt can not be pulled out into a sheet shape well as a strand, or even if it can be pulled out well,
Due to the tackiness of the asphalt, there were problems in that it could not be cut into pellets well, and how to prevent adhesion of the pelletized asphalt.

【0005】[0005]

【発明が解決しようとする課題】そこで、本発明は、防
着性に優れた粒状アスファルトを簡便に製造する方法を
提供することにある。
Accordingly, an object of the present invention is to provide a method for easily producing granular asphalt having excellent anti-adhesion properties.

【0006】[0006]

【課題を解決するための手段】本発明者らは、上記事情
に鑑みて、鋭意研究を重ねた結果、加熱溶融させたアス
ファルトを冷却撹拌下にある溶液中に滴下接触させてい
くことにより粒状化アスファルトが得られることを見出
し、本発明を完成した。
Means for Solving the Problems In view of the above circumstances, the inventors of the present invention have conducted intensive studies and as a result, found that asphalt that has been heated and melted is brought into contact with a solution under cooling and agitation to obtain a granular material. The present inventors have found that a modified asphalt can be obtained and completed the present invention.

【0007】以下、本発明の内容を詳細に説明する。本
発明で使用されるアスファルトとは、ストレートアスフ
ァルト、セミブローンアスファルト、ブローンアスファ
ルト等の石油アスファルト、ロックアスファルト、レー
キアスファルト、グランスピッチ、ギルソナイト等の天
然アスファルト、脱色アスファルトのような合成アスフ
ァルト、それに、これらを樹脂やゴム等で改質を図った
改質アスファルト等によるものを指すがこれらは単独で
使用することもできるが、混合して使用することもでき
る。
Hereinafter, the contents of the present invention will be described in detail. The asphalt used in the present invention is straight asphalt, semi-blown asphalt, petroleum asphalt such as blown asphalt, rock asphalt, lake asphalt, glan pitch, natural asphalt such as Gilsonite, synthetic asphalt such as decolorized asphalt, and these Refers to a modified asphalt or the like which is modified with a resin, rubber, or the like. These can be used alone or in a mixture.

【0008】ここに、本アスファルトを加熱溶融する場
合における、その溶融温度であるが、通常120〜20
0℃前後とするのが好ましい。
Here, the melting temperature when the asphalt is heated and melted is usually 120 to 20.
Preferably, the temperature is around 0 ° C.

【0009】ここにこのような溶融温度にあるアスファ
ルトの滴下であるが、これは点滴状、糸状、霧状のよう
な形で行うのが好ましい。
[0009] The asphalt dripping at such a melting temperature is preferably performed in the form of a drip, a thread or a mist.

【0010】ここに、アスファルトを滴下接触させてい
く、溶液であるが、これは、アスファルトを殆ど溶かす
ことのない、炭化水素の水素原子を水素基で置換した化
合物からなるアルコール溶液によるものを指す。具体例
を挙げればメチルアルコール、エチルアルコールなどの
脂肪族飽和一価アルコール、エチレングリコールのよう
な脂肪族飽和二価アルコール、グリセリンのような脂肪
族飽和三価アルコールといったものからアリルアルコー
ルのような脂肪族不飽和アルコール、ミクロペンタノー
ルのような指環式アルコール、ベンジンアルコールのよ
うな芳香族アルコール、フルフリルアルコールのような
複素環式アルコールといったようなものがある。しか
し、これらアルコールの中でもメチルアルコールやエチ
ルアルコールのような低級アルコールによるものは粘性
が低く、揮発性に優れているといったことから好適に用
いることが出来る。
[0010] Here, the asphalt is a solution in which asphalt is dropped and contacted, and this refers to an alcohol solution consisting of a compound in which a hydrogen atom of a hydrocarbon is substituted with a hydrogen group, which hardly dissolves asphalt. . Specific examples include aliphatic saturated monohydric alcohols such as methyl alcohol and ethyl alcohol, aliphatic saturated dihydric alcohols such as ethylene glycol, aliphatic saturated trihydric alcohols such as glycerin to fats such as allyl alcohol. Examples include group-unsaturated alcohols, finger-ring alcohols such as micropentanol, aromatic alcohols such as benzene alcohol, and heterocyclic alcohols such as furfuryl alcohol. However, among these alcohols, those based on lower alcohols such as methyl alcohol and ethyl alcohol can be suitably used because of their low viscosity and excellent volatility.

【0011】ここに、該溶液の冷却であるが、汎用の冷
却装置を用いて10℃以下に冷却するのが好ましい。
Here, the cooling of the solution is preferably performed by cooling the solution to 10 ° C. or less using a general-purpose cooling device.

【0012】ここに該溶液の撹拌であるが、汎用の撹拌
装置を用いて、100〜500r.p.m.程度の撹拌
を与えるのが好ましい。但し、これ以外の撹拌速度によ
る使用を防げるものではない。
Here, the stirring of the solution is performed using a general-purpose stirring device at 100 to 500 rpm. p. m. It is preferred to provide a degree of agitation. However, use at other stirring speeds is not prevented.

【0013】ここに、溶液中に生成した粒状アスファル
トの乾燥であるが、これについては、粒状アスファルト
を溶液中から取り出して、この粒状アスファルト表面に
付着する溶液を自然下または加熱下に蒸発させることで
よい。ところでこの溶液の蒸発であるが、完全に蒸発さ
せることでもよいが、また少しこの溶液を残すようにし
てもよい。ここにこの溶液を少し残すことによる理由は
それが粒状アスファルトの付着防止に役立つからであ
る。またここに、付着防止剤の使用が必要であれば、粒
状アスファルト100重量部当たり、この付着防止剤
を、通常0.1〜10重量部、好ましくは0.5〜5重
量部用いるとよい。ところで、ここにいう付着防止剤で
あるが、これには、シリカ、炭酸カルシウム、炭酸マグ
ネシウム、タルク、酸化亜鉛、水酸化アルミニウム、ク
レー等によるものが挙げられる。これら付着防止剤は単
独で使用することもできるが、これらはまた2種以上組
み合わせて用いることもできる。ここに、またこれらは
付着防止剤の添加方法であるが、これらは溶液中に添加
することも、また直接、粒状アスファルト表面をまぶす
ような形で添加することもできる。
[0013] Here, the drying of granular asphalt generated in the solution is performed by removing the granular asphalt from the solution and evaporating the solution adhering to the surface of the granular asphalt naturally or under heating. Is fine. By the way, the evaporation of the solution may be completely evaporated, or the solution may be left a little. The reason for leaving this solution a little here is that it helps to prevent the adhesion of particulate asphalt. If it is necessary to use an anti-adhesion agent, the anti-adhesion agent is usually used in an amount of 0.1 to 10 parts by weight, preferably 0.5 to 5 parts by weight, per 100 parts by weight of the granular asphalt. By the way, the anti-adhesion agent referred to here includes silica, calcium carbonate, magnesium carbonate, talc, zinc oxide, aluminum hydroxide, clay and the like. These anti-adhesion agents can be used alone, but they can also be used in combination of two or more. Here, these are also methods of adding an anti-adhesion agent, and they can be added in a solution or directly in such a manner as to dust the surface of the granular asphalt.

【0014】[0014]

【実施例】以下、本発明を実施例を挙げてさらに詳述す
る。まず1リットルのホーロージョッキーに300gの
エチルアルコールを採り、これを5℃に冷却した水槽中
に浸漬させて、このエチルアルコールをプロペラ式の撹
拌機で、300r.p.m.の撹拌下に10℃以下に冷
却させておいた所に、これとは別に1リットルのホーロ
ージョッキー中に100g用意しておいた、針入度1
9、軟化点84℃の改質アスファルトを190℃に加熱
すると共に、該ジョッキーを傾けながら、改質アスファ
ルトを糸状で少しずつ滴下していって、1〜3m/m粒
径の粒状アスファルトを得た。ここに得られた粒状アス
ファルトは、その後840μのフルイ上に採り出して、
自然乾燥下にエチルアルコールを蒸発させた。そしてこ
の乾燥させた粒状アスファルトは、タルクを用いて、ま
ぶすとともにこのものをポリエチレン袋に入れて約1カ
月間その様子を見たが、アスファルト粒同志の付着は全
く見られなかった。
EXAMPLES Hereinafter, the present invention will be described in more detail with reference to examples. First, 300 g of ethyl alcohol is taken in a 1 liter hollow jockey, and immersed in a water bath cooled to 5 ° C., and the ethyl alcohol is removed with a propeller type stirrer at 300 rpm. p. m. 100 g was prepared separately in a 1 liter hollow jockey where it was cooled to 10 ° C. or less under stirring.
9. While heating the modified asphalt having a softening point of 84 ° C. to 190 ° C. and dropping the modified asphalt little by little in a thread form while tilting the jockey, a granular asphalt having a particle size of 1 to 3 m / m is obtained. Was. The granular asphalt obtained here is then taken out on a 840 μ sieve,
The ethyl alcohol was evaporated under air drying. The dried granular asphalt was sprinkled with talc and put in a polyethylene bag, and the state was observed for about one month. However, no adhesion of the asphalt particles was observed at all.

【0015】[0015]

【発明の効果】以上説明したように、この発明によれ
ば、極めて簡単な製造装置によって、粒状アスファルト
を得ることが出来るとともにアスファルトが粒状化され
ていることから輸送や包装に際してに取り扱いが極めて
容易であり、しかも防着性があることから貯蔵性に優れ
たものであるといえる。それに、加熱アスファルトに見
られたような熱劣化による物性の低下や、常温アスファ
ルトに見られるような、養生時間による問題や、アスフ
ァルトを常温化するための加工による物性の低下といっ
たようなこともないといえる。
As described above, according to the present invention, granular asphalt can be obtained with an extremely simple manufacturing apparatus, and handling is extremely easy during transportation and packaging because the asphalt is granulated. In addition, since it has anti-adhesion properties, it can be said that it has excellent storage properties. In addition, there is no deterioration in physical properties due to thermal degradation as seen in heated asphalt, no problem with curing time as seen in normal-temperature asphalt, and no decrease in physical properties due to processing for asphalt at normal temperature. It can be said that.

Claims (2)

【特許請求の範囲】[Claims] 【請求項1】加熱溶融させたアスファルトを冷却撹拌下
にある溶液中に滴下接触させていくことを特徴とした粒
状アスファルトの製造方法。
1. A method for producing granular asphalt, wherein asphalt melted by heating is dropped into a solution under cooling and stirring.
【請求項2】アスファルトを滴下接触させていく溶液
が、炭化水素原子を水酸基で置換した化合物からなるア
ルコール溶液であることを特徴とした請求項1記載の粒
状アスファルトの製造方法。
2. The method for producing granular asphalt according to claim 1, wherein the solution to which the asphalt is dropped is an alcohol solution comprising a compound in which a hydrocarbon atom is substituted with a hydroxyl group.
JP36246297A 1997-11-21 1997-11-21 Production of granular asphalt Pending JPH11152477A (en)