JPH107997A - Tracking-resistant tacky adhesive tape - Google Patents
Tracking-resistant tacky adhesive tapeInfo
- Publication number
- JPH107997A JPH107997A JP8185376A JP18537696A JPH107997A JP H107997 A JPH107997 A JP H107997A JP 8185376 A JP8185376 A JP 8185376A JP 18537696 A JP18537696 A JP 18537696A JP H107997 A JPH107997 A JP H107997A
- Authority
- JP
- Japan
- Prior art keywords
- tracking
- synthetic resin
- sensitive adhesive
- adhesive tape
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、トランス用巻線な
どのように電気絶縁用に使用される耐トラッキング性難
燃性粘着テープに関する。特に本発明は、国際安全規格
であるＩＥＣ−１１２に記載された測定方法により測定
される比較トラッキング指数（ＣＴＩ値）が６００Ｖ以
上である耐トラッキング性粘着テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a tracking-resistant flame-retardant pressure-sensitive adhesive tape used for electrical insulation, such as a winding for a transformer. In particular, the present invention relates to a tracking-resistant pressure-sensitive adhesive tape having a comparative tracking index (CTI value) of 600 V or more as measured by a measurement method described in IEC-112, which is an international safety standard.
【０００２】[0002]
【従来の技術】情報機器の分野では、特に電源トランス
などの機器の安全性確保のために沿面距離及び空間距離
の確保、さらに使用絶縁材料の絶縁性等の基準が定めら
れていたが、近年情報機器の国際安全規格（ＩＥＣ）の
規格改訂により、新しい要求項目である比較トラッキン
グ指数（Ｃｏｍｐａｒａｔｉｖｅ ＴｒａｃｋｉｎｇＩ
ｎｄｅｘ：ＣＴＩ）の高い絶縁材料に対する需要が増加
してきている。特に、最近の電子機器の小型化、軽量化
の進行に伴い層間絶縁用として卷回使用する絶縁用粘着
テープについても高い耐トラッキング性が求められてき
ている。しかし、従来のポリエステル等を基材とする通
常の粘着テープの殆どは、ＣＴＩ値が４００Ｖ程度まで
であり、より以上のＣＴＩ値を示す絶縁用粘着テープは
少ない。2. Description of the Related Art In the field of information equipment, standards for securing creepage distances and clearances, and for insulating properties of insulating materials used, have been set, especially in order to ensure the safety of equipment such as power transformers. With the revision of the International Safety Standard (IEC) for information equipment, a new requirement, the Comparative Tracking Index (Comparative Tracking I)
There is an increasing demand for insulating materials having a high Ndex (CTI). In particular, with the progress of recent miniaturization and weight reduction of electronic devices, high tracking resistance is also required for insulating pressure-sensitive adhesive tapes used for winding for interlayer insulation. However, most of the conventional adhesive tapes using a conventional polyester or the like as a base material have a CTI value of up to about 400 V, and few insulating adhesive tapes exhibiting a higher CTI value.
【０００３】[0003]
【発明が解決しようとする課題】それ故、本願発明は、
粘着テープに対する新しい要求基準である高いＣＴＩ値
を示す絶縁用の粘着テープを提供することを目的とする
ものである。特に本発明は、ＣＴＩ値が６００以上であ
る耐トラッキング性粘着テープを提供することを目的と
するものである。SUMMARY OF THE INVENTION Therefore, the present invention
It is an object of the present invention to provide an insulating adhesive tape exhibiting a high CTI value, which is a new standard for adhesive tapes. In particular, an object of the present invention is to provide a tracking-resistant pressure-sensitive adhesive tape having a CTI value of 600 or more.
【０００４】[0004]
【課題を解決するための手段】前記課題を解決すること
のできる本発明の第一は、絶縁性基材と粘着剤層の間
に、ポリウレタン系合成樹脂、塩酢ビ系合成樹脂、アク
リル系合成樹脂及びポリオレフィン系合成樹脂から選ば
れた少なくとも１種の合成樹脂を主成分とする中間層を
設けたことを特徴とする耐トラッキング性粘着テープに
関する。Means for Solving the Problems The first aspect of the present invention which can solve the above-mentioned problems is that a polyurethane-based synthetic resin, a polyvinyl chloride-based synthetic resin, an acrylic-based resin is provided between an insulating substrate and an adhesive layer. The present invention relates to a tracking-resistant pressure-sensitive adhesive tape provided with an intermediate layer containing at least one synthetic resin selected from a synthetic resin and a polyolefin-based synthetic resin as a main component.
【０００５】また本発明の第二は、ＩＥＣ−１１２に準
じて測定される比較トラッキング指数（ＣＴＩ値）が６
００Ｖ以上であることを特徴とする前記の耐トラッキン
グ性粘着テープに関する。同様に、本発明の第三は、前
記粘着剤層がアクリル系粘着剤からなることを特徴とす
る前記の耐トラッキング性粘着テープに関するものであ
る。同様に、本発明の第四は、絶縁性基材がポリエステ
ルフィルムからなることを特徴とする前記の耐トラッキ
ング性粘着テープに関する。A second aspect of the present invention is that a comparative tracking index (CTI value) measured according to IEC-112 is 6%.
The present invention relates to the tracking-resistant pressure-sensitive adhesive tape having a voltage of 00 V or more. Similarly, the third aspect of the present invention relates to the tracking-resistant pressure-sensitive adhesive tape, wherein the pressure-sensitive adhesive layer is made of an acrylic pressure-sensitive adhesive. Similarly, the fourth aspect of the present invention relates to the tracking-resistant pressure-sensitive adhesive tape, wherein the insulating substrate is made of a polyester film.
【０００６】[0006]
【発明の実施の形態】本発明の耐トラッキング性粘着テ
ープの中間層に用いられる合成樹脂は、ポリウレタン系
合成樹脂、塩酢ビ系合成樹脂、アクリル系合成樹脂及び
ポリオレフィン系合成樹脂から選ばれた少なくとも１種
の合成樹脂を主成分とする合成樹脂である。ポリウレタ
ン系合成樹脂としては、通常のポリウレタン樹脂を主成
分とする合成樹脂が使用でき、また、塩酢ビ系合成樹脂
としては、塩化ビニルと酢酸ビニル及び／又は無水マレ
イン酸との共重合体を主成分とするものが使用される。BEST MODE FOR CARRYING OUT THE INVENTION The synthetic resin used for the intermediate layer of the tracking-resistant pressure-sensitive adhesive tape of the present invention is selected from polyurethane-based synthetic resin, polyvinyl chloride-based synthetic resin, acrylic-based synthetic resin and polyolefin-based synthetic resin. It is a synthetic resin containing at least one kind of synthetic resin as a main component. As the polyurethane-based synthetic resin, a synthetic resin containing a usual polyurethane resin as a main component can be used. As the polyvinyl chloride-based synthetic resin, a copolymer of vinyl chloride and vinyl acetate and / or maleic anhydride can be used. What is used as a main component is used.
【０００７】アクリル系合成樹脂としては、（メタ）ア
クリル酸のＣ1 〜Ｃ12エステルやアクリル酸等の酸モノ
マーの重合体、又はこれらの酸モノマーと共重合可能な
他の単量体との共重合体を主成分とする合成樹脂が挙げ
られ、ポリオレフィン系合成樹脂としては、エチレンと
酢酸ビニル共重合体を主成分とする合成樹脂（ＥＶＡ）
あるいはエチレン−アクリル酸共重合体系樹脂などがあ
げられる。As the acrylic synthetic resin, a polymer of an acid monomer such as a C 1 -C 12 ester of (meth) acrylic acid or acrylic acid, or a copolymer of another monomer copolymerizable with these acid monomers can be used. Synthetic resins containing a copolymer as a main component are exemplified. As the polyolefin-based synthetic resin, a synthetic resin containing an ethylene / vinyl acetate copolymer as a main component (EVA) is used.
Alternatively, an ethylene-acrylic acid copolymer resin may be used.
【０００８】これらの合成樹脂に各種の添加剤、助剤、
フィラー、有機系又は無機系の顔料等を配合して溶剤に
溶解したものを使用することができる。さらに印刷イン
キや、この印刷インキから顔料を除いたもの等を添加し
た合成樹脂も使用することができる。[0008] Various additives, auxiliaries,
A mixture of a filler, an organic or inorganic pigment, and the like dissolved in a solvent can be used. Further, a synthetic resin to which a printing ink or a material obtained by removing a pigment from the printing ink or the like can be used.
【０００９】本発明の耐トラッキング性粘着テープの粘
着剤層には、通常の絶縁性粘着テープに使用されている
粘着剤のうち、アクリル系及びゴム系の粘着剤が使用で
き、特にアクリル系粘着剤を使用することが好ましい。In the pressure-sensitive adhesive layer of the tracking-resistant pressure-sensitive adhesive tape of the present invention, among the pressure-sensitive adhesives used for ordinary insulating pressure-sensitive adhesive tapes, acrylic and rubber-based pressure-sensitive adhesives can be used. It is preferred to use agents.
【００１０】本発明の耐トラッキング性粘着テープに使
用されるテープ基材としては、ポリエステルフィルムが
使用される。さらにポリエステルフィルムの少なくとも
片面をコロナ放電処理等のいわゆる易接着性処理したポ
リエステルフィルム等を使用することができる。なお、
本発明で使用できるポリエステルフィルムとはポリエチ
レンテレフタレートフィルムであり、そのフィルム厚さ
は、通常５〜１８０μの範囲から選択される。A polyester film is used as the tape substrate used in the tracking-resistant pressure-sensitive adhesive tape of the present invention. Further, it is possible to use a polyester film or the like in which at least one surface of the polyester film is subjected to a so-called easy adhesion treatment such as a corona discharge treatment. In addition,
The polyester film that can be used in the present invention is a polyethylene terephthalate film, and the thickness of the film is generally selected from the range of 5 to 180 µ.
【００１１】本発明の耐トラッキング性粘着テープの基
材と粘着剤層の間に設けられる中間層の厚さは通常０．
５μｍ〜１００μｍの範囲内で選択される。ＣＴＩ値６
００Ｖ以上の耐トラッキング性を確保するためには、
０．５μｍ以上であることが好ましい。また、耐トラッ
キング性粘着テープを巻回使用する場合には１００μｍ
を越えないことが有利である。The thickness of the intermediate layer provided between the base material and the pressure-sensitive adhesive layer of the tracking-resistant pressure-sensitive adhesive tape of the present invention is usually 0.1.
It is selected within a range of 5 μm to 100 μm. CTI value 6
In order to secure the tracking resistance of 00V or more,
It is preferably 0.5 μm or more. When a tracking-resistant adhesive tape is used for winding, 100 μm
Is advantageously not exceeded.
【００１２】本発明の耐トラッキング性粘着テープは、
通常の絶縁性粘着テープの製造方法に従って製造するこ
とができる。たとえば、コロナ放電処理等の易接着処理
されていて粘着剤層が塗工される面の背面を公知の離型
剤で処理することができるし、粘着剤塗工側の中間層面
を公知の下塗剤やアンカー剤で処理することもできる。The tracking-resistant pressure-sensitive adhesive tape of the present invention comprises:
It can be manufactured according to a normal method for manufacturing an insulating pressure-sensitive adhesive tape. For example, the back surface of the surface on which the pressure-sensitive adhesive layer is coated, which has been subjected to easy adhesion treatment such as corona discharge treatment, can be treated with a known release agent, or the intermediate layer surface on the pressure-sensitive adhesive-coated side can be coated with a known undercoat. It can also be treated with an agent or an anchoring agent.
【００１３】本発明の耐トラッキング性粘着テープは、
基材と粘着剤層との間に中間層が配置されており、該中
間層は、そのＣＴＩ値が６００Ｖ以上となるように材
料、層の厚さ等が選択されている。上記構成の本発明の
耐トラッキング性粘着テープは、従来の絶縁性粘着テー
プに比べて沿面距離を低減することができるので、電源
トランス等の小型化、軽量化を実現することが可能とな
る。また、絶縁テープ幅を小さくすることができること
から、コイルの巻き付けが大きく取れるようになり、ト
ランスの容量を向上させることが可能である。The tracking-resistant pressure-sensitive adhesive tape of the present invention comprises:
An intermediate layer is disposed between the base material and the pressure-sensitive adhesive layer, and the material and thickness of the intermediate layer are selected so that the CTI value is 600 V or more. The tracking-resistant pressure-sensitive adhesive tape of the present invention having the above-described configuration can reduce the creepage distance as compared with the conventional insulating pressure-sensitive adhesive tape, so that it is possible to reduce the size and weight of the power transformer and the like. Further, since the width of the insulating tape can be reduced, it is possible to increase the winding of the coil, and it is possible to improve the capacity of the transformer.
【００１４】[0014]
【実施例】以下に、実施例及び比較例にしたがって本発
明の耐トラッキング性粘着テープをより詳細に説明する
が、本発明はこれらの実施例によって限定されるもので
はない。各実施例及び比較例で使用した耐トラッキング
性試験法、中間層用合成樹脂、粘着剤及び基材フィルム
はつぎの通りである。 （１）耐トラッキング性試験法：ＩＥＣ ｐｕｂ．１１
２法に準拠。 （２）中間層用の合成樹脂： Ａ ウレタン系合成樹脂：大日本インキ社製 ＸＳ−６
５３ Ｂ ウレタン／塩酢ビ系合成樹脂：大日本インキ社製
ＸＮ−３９７ Ｃ アクリル系合成樹脂：メチルアクリレート６５部／
エチルアクリレート３０部／アクリル酸５部からなる重
量平均分子量５０万のアクリル共重合体。 Ｄ ポリエステル系合成樹脂：バイロン５００（東洋紡
績社製 軟化点１１４℃）５０部とバイロン１０３（東
洋紡績社製 軟化点１５８℃）５０部を混合してなるも
の。 （３）アクリル系粘着剤Ａ：ブチルアクリレート９５部
とアクリル酸５部からなる重量平均分子量５５万のアク
リルポリマーにタッキファイヤーとしてテルペンフェノ
ール（荒川化学社製 ＹＳポリスター２１００）を１０
部配合してなるもの。 （４）アクリル系粘着剤Ｂ：ブチルアクリレート９５部
とアクリル酸５部からなる重量平均分子量５５万のアク
リルポリマーに難燃剤としてＦＧ−２０００（帝人化成
社製）５５部及びＣＲＰ（大八化学社製）４５部を配合
したもの。 （５）基材フィルム：東レ社製のポリエステルフィルム
「ルミラーＳ１５Ａ」EXAMPLES Hereinafter, the tracking-resistant pressure-sensitive adhesive tape of the present invention will be described in more detail with reference to Examples and Comparative Examples, but the present invention is not limited to these Examples. The tracking resistance test method, the synthetic resin for the intermediate layer, the pressure-sensitive adhesive and the base film used in each Example and Comparative Example are as follows. (1) Tracking resistance test method: IEC pub. 11
Conforms to two laws. (2) Synthetic resin for intermediate layer: A Urethane-based synthetic resin: XS-6 manufactured by Dainippon Ink and Chemicals, Inc.
53B urethane / vinyl chloride-based synthetic resin: manufactured by Dainippon Ink and Chemicals, Inc.
XN-397 C acrylic synthetic resin: methyl acrylate 65 parts /
An acrylic copolymer having a weight average molecular weight of 500,000, comprising 30 parts of ethyl acrylate / 5 parts of acrylic acid. D Polyester-based synthetic resin: A mixture of 50 parts of Byron 500 (softening point: 114 ° C., manufactured by Toyobo Co., Ltd.) and 50 parts of Byron 103 (softening point: 158 ° C., manufactured by Toyobo Co., Ltd.). (3) Acrylic pressure-sensitive adhesive A: Terpene phenol (YS Polystar 2100 manufactured by Arakawa Chemical Co., Ltd.) was used as a tackifier in an acrylic polymer having a weight average molecular weight of 550,000 comprising 95 parts of butyl acrylate and 5 parts of acrylic acid.
Parts are mixed. (4) Acrylic pressure-sensitive adhesive B: 55 parts of FG-2000 (manufactured by Teijin Chemicals Ltd.) and CRP (Daihachi Chemical Co., Ltd.) as a flame retardant for an acrylic polymer having a weight average molecular weight of 550,000 composed of 95 parts of butyl acrylate and 5 parts of acrylic acid Manufactured by the company) 45 parts. (5) Base film: Toray's polyester film "Lumirror S15A"
【００１５】実施例１ 片面に離型剤を塗布した厚さ５０μの前記東レ社製のポ
リエステルフィルムの他面側に、中間層として前記ウレ
タン系合成樹脂（大日本インキ株式会社製ＸＳ−６５
３）を厚さ２μとなるように塗布し、この中間層面に前
記アクリル系粘着剤Ａを厚さ３０μとなるように塗工し
て粘着テープを製造した。このようにして製造された厚
さ８２μの粘着テープを３７層積層して厚さ約３ｍｍの
試験片（一片の大きさ５０ｍｍ）を作成し、ＩＥＣｐｕ
ｂ．１１２法に準拠してＣＴＩ値を測定した。結果を表
１に示す。Example 1 The urethane-based synthetic resin (XS-65 manufactured by Dai Nippon Ink Co., Ltd.) was used as an intermediate layer on the other side of the 50 μm-thick polyester film coated with a release agent on one side.
3) was applied to a thickness of 2 μ, and the acrylic pressure-sensitive adhesive A was applied to the intermediate layer surface to a thickness of 30 μ to produce an adhesive tape. 37 pressure-sensitive adhesive tapes having a thickness of 82 μ thus manufactured are laminated to form a test piece (one piece size: 50 mm) having a thickness of about 3 mm.
b. The CTI value was measured according to the 112 method. Table 1 shows the results.
【００１６】実施例２ 中間層用の合成樹脂としてウレタン系合成樹脂に代え
て、前記ウレタン／塩酢ビ系合成樹脂を使用した以外
は、実施例１と同様にして粘着テープ試験片を作成し、
ＣＴＩ値を測定した。結果を表１に示す。Example 2 An adhesive tape test piece was prepared in the same manner as in Example 1 except that the urethane / vinyl chloride-based synthetic resin was used as the synthetic resin for the intermediate layer instead of the urethane-based synthetic resin. ,
CTI values were measured. Table 1 shows the results.
【００１７】実施例３ 中間層用の合成樹脂としてウレタン系合成樹脂に代え
て、前記ウレタン／塩酢ビ系合成樹脂を使用し、またア
クリル系粘着剤Ａに代えてアクリル系粘着剤Ｂを使用し
た以外は、実施例１と同様にして粘着テープ試験片を作
成し、ＣＴＩ値を測定した。結果を表１に示す。Example 3 As the synthetic resin for the intermediate layer, the urethane-based synthetic resin was used in place of the urethane-based synthetic resin, and the acrylic adhesive B was used in place of the acrylic adhesive A. An adhesive tape test piece was prepared in the same manner as in Example 1 except that the CTI value was measured. Table 1 shows the results.
【００１８】実施例４ 中間層用の合成樹脂としてウレタン系合成樹脂に代え
て、アクリル系合成樹脂を使用した以外は、実施例１と
同様にして粘着テープ試験片を作成し、ＣＴＩ値を測定
した。結果を表１に示す。Example 4 An adhesive tape test piece was prepared in the same manner as in Example 1 except that an acrylic synthetic resin was used in place of the urethane synthetic resin as the synthetic resin for the intermediate layer, and the CTI value was measured. did. Table 1 shows the results.
【００１９】比較例１ 中間層用の合成樹脂としてウレタン系合成樹脂Ａに代え
て、ポリエステル系合成樹脂Ｄを使用した以外は、実施
例１と同様にして粘着テープ試験片を作成し、ＣＴＩ値
を測定した。結果を表２に示す。 比較例２ 中間層用の合成樹脂を使用しない以外は、実施例１と同
様にして粘着テープ試験片を作成し、ＣＴＩ値を測定し
た。結果を表２に示す。 比較例３ アクリル系粘着剤Ａに代えて、アクリル系粘着剤Ｂを使
用した以外は、比較例２と同様にして試験片を作成し、
ＣＴＩ値を測定した。結果を表２に示す。Comparative Example 1 An adhesive tape test piece was prepared in the same manner as in Example 1 except that a polyester-based synthetic resin D was used instead of the urethane-based synthetic resin A as the synthetic resin for the intermediate layer, and the CTI value was measured. Was measured. Table 2 shows the results. Comparative Example 2 An adhesive tape test piece was prepared in the same manner as in Example 1 except that the synthetic resin for the intermediate layer was not used, and the CTI value was measured. Table 2 shows the results. Comparative Example 3 A test piece was prepared in the same manner as in Comparative Example 2, except that an acrylic pressure-sensitive adhesive B was used instead of the acrylic pressure-sensitive adhesive A.
CTI values were measured. Table 2 shows the results.
【００２０】[0020]
【表１】 [Table 1]
【００２１】[0021]
【表２】 [Table 2]
【００２２】[0022]
【発明の効果】表１の結果から、基材フィルムと粘着剤
層との間に中間層として特定の合成樹脂層を設けること
により、絶縁テープにＣＴＩ値６００Ｖ以上の耐トラッ
キング性を付与することができることが明らかである。From the results in Table 1, it can be seen that by providing a specific synthetic resin layer as an intermediate layer between the base film and the pressure-sensitive adhesive layer, the insulating tape can be given a tracking resistance of CTI value of 600 V or more. It is clear that can be done.
Claims (4)
タン系合成樹脂、塩酢ビ系合成樹脂、アクリル系合成樹
脂及びポリオレフィン系合成樹脂から選ばれた少なくと
も１種の合成樹脂を主成分とする中間層を設けたことを
特徴とする耐トラッキング性粘着テープ。At least one synthetic resin selected from the group consisting of a polyurethane-based synthetic resin, a polyvinyl chloride-based synthetic resin, an acrylic-based synthetic resin and a polyolefin-based synthetic resin is provided between an insulating base material and an adhesive layer. A tracking-resistant pressure-sensitive adhesive tape having an intermediate layer as a component.
Ｃ−１１２に準じて測定される比較トラッキング指数
（ＣＴＩ値）が６００Ｖ以上であることを特徴とする請
求項１記載の耐トラッキング性粘着テープ。2. The tracking-resistant pressure-sensitive adhesive tape is IE
The tracking-resistant pressure-sensitive adhesive tape according to claim 1, wherein a comparative tracking index (CTI value) measured according to C-112 is 600 V or more.
ることを特徴とする請求項１又は請求項２記載の耐トラ
ッキング性粘着テープ。3. The tracking-resistant pressure-sensitive adhesive tape according to claim 1, wherein the pressure-sensitive adhesive layer is made of an acrylic pressure-sensitive adhesive.
からなることを特徴とする請求項１〜請求項３のいずれ
か１項に記載の耐トラッキング性粘着テープ。4. The tracking-resistant pressure-sensitive adhesive tape according to claim 1, wherein the insulating substrate is made of a polyester film.