JPH1036442A - Phenol-group-containing vinyl alcohol polymer - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain a modified vinyl alcohol polymer having a phenolic hydroxyl group and excellent functional properties and being useful as a textile size, a textile processing or the like by introducing a specified amount of specified phenolic-hydroxyl-containing units into a vinyl alcohol polymer. SOLUTION: This polymer is obtained by introducing 0.01-30mol% units each represented by formula I or II (wherein R<1> , R<2> , R<3> , R<4> and R<5> are each H, an 8C or lower hydrocarbon group which may contain a substituent; A is a divalent hydrocarbon group which may contain an atom such as nitrogen, oxygen or sulfur; S is a sulfur atom; and X is a monovalent group containing a phenolic hydroxyl) into a vinyl alcohol polymer mainly consisting of vinyl alcohol units. It can be produced by for example a method comprising reacting a copolymer of a vinyl ester monomer with an epoxy vinyl monomer (e.g. allyl glycidyl ether) with a phenolic-hydroxyl-containing thiol (e.g. 2- hydroxythiophenol) and hydrolyzing the product.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention relates to a novel modified vinyl alcohol-based polymer.

[0002]

2. Description of the Related Art Polyvinyl alcohol is one of the few crystalline water-soluble polymers that has excellent interfacial properties and strength properties. Therefore, polyvinyl alcohol is used as a stabilizer for paper processing, fiber processing and emulsions. It occupies an important position as a raw material for films and polyvinyl alcohol fibers. On the other hand, pursuit of high functionality by controlling crystallinity or improving specific performance by introducing a functional group has been pursued, and various types of so-called modified polyvinyl alcohol have been developed.

A vinyl alcohol polymer having a phenolic hydroxyl group is disclosed as an acetalized product with o-hydroxybenzaldehyde (Polymer Experiment 6, Polymer Reaction, p. 70, 1978, Kyoritsu Shuppan). However, since the phenolic hydroxyl group of the modified polyvinyl alcohol is linked by an acetal bond having low molecular mobility, the function of the phenolic hydroxyl group cannot be sufficiently used in many cases.

[0004]

SUMMARY OF THE INVENTION Under such circumstances, an object of the present invention is to provide a novel modified vinyl alcohol polymer which can sufficiently exhibit the function of a phenolic hydroxyl group.

[0005]

The present inventors have conducted intensive studies on such a novel modified vinyl alcohol-based polymer, and found that the unit represented by the following chemical formula (3) or (4) is 0.1.
The present inventors have found a vinyl alcohol polymer containing from 01 to 30 mol%, and have completed the present invention.

[0006]

Embedded image

[0007]

Embedded image

(Wherein R ¹ , R ² , R ³ , R ⁴ and R ⁵ represent a hydrogen atom or a hydrocarbon group having 8 or less carbon atoms which may have a substituent, A represents a nitrogen atom, Represents a divalent hydrocarbon group which may contain an oxygen atom or a sulfur atom, S represents a sulfur atom, and X represents a monovalent group containing a phenolic hydroxyl group.)

[0009]

BEST MODE FOR CARRYING OUT THE INVENTION The vinyl alcohol-based polymer of the present invention has a unit represented by Formula 3 or 4 in its molecular chain.
It is a vinyl alcohol-based polymer containing from 01 to 30 mol%, and there is no particular limitation on the distribution of the unit represented by the formula (3) or (4) in the polymer. When the content of the unit is 0.0
If it is less than 1 mol%, the effect of introduction is not sufficiently exhibited,
If it exceeds 30 mol%, a problem occurs in the storage stability (for example, gelation) of the vinyl alcohol-based polymer. A more preferred range of the content of the unit represented by Chemical Formula 3 or Chemical Formula 4 is
0.02 to 20 mol%, and a particularly preferred range is 0.1 to 2.0 mol%.
In the range from 0.5 to 15 mol%.

R ¹ in the unit represented by the formula (3) or (4),
R ² , R ³ , R ⁴ and R ⁵ are not particularly limited as long as they are a hydrogen atom or a hydrocarbon group having 8 or less carbon atoms which may have a substituent, but R ¹ is a hydrogen atom, R ² is a hydrogen atom or a methyl group, and R ³ , R ⁴ and R ⁵ are a hydrogen atom or 8 or less carbon atoms (preferably 6 or less carbon atoms)
Are preferably used. Note that R ³ and R ⁴ (or R ⁵ ) may form a ring together.

A in the unit represented by Formula 4 is a nitrogen atom,
The structure is not particularly limited as long as it is a divalent hydrocarbon group which may contain an oxygen atom or a sulfur atom.
_{-CH 2 OCH 2 -, - OCH} 2 -, - CONH-φ-
OCH ₂ —, —CONHCH ₂ —, —CONHCH ₂ O
CH ₂ —, —CONHCH ₂ OCH ₂ CH ₂ —, —CO
_{NHCH 2 OCH 2 CH 2 CH 2} -, - CONHCH 2
OCH ₂ CH ₂ CH ₂ CH _2- , -CONHCH ₂ -φ
(CH ₃ ) ₂ —CH ₂ — and the like are exemplified. (Note that φ means a phenylene group.)

X in the unit represented by Formula 3 or 4 is
The structure is not particularly limited as long as it is a monovalent group containing a phenolic hydroxyl group. For example, -ph-OH (1,2
-), -Ph-OH (1,3-), -ph-OH (1,
_{4 -), - CH 2 -ph} -OH (1,2 -), - CH 2
-Ph-OH (1,3 -), - CH 2 -ph-OH
_{(1,4 -), - CH 2} CH 2 -ph-OH (1,2
_{-), - CH 2 CH 2} -ph-OH (1,3 -), - C
H ₂ CH ₂ -ph-OH (1,4-), -ph (C
_{H 3) -OH (1,2,3 -)} , - ph (CH 3) -O
H (1,2,4 -), - ph (CH 3) -OH (1,
2,5 -), - ph (CH 3) -OH (1,2,6
-), -Nph-OH (1,2-), -nph-OH
(1,4-), -nph-OH (1,8-) and the like and alkali metal salts thereof and the like are exemplified. (In addition, ph means a phenyl group, and nph means a naphthalene group.)

The vinyl alcohol polymer of the present invention substantially comprises a vinyl alcohol unit or a vinyl alcohol unit and a vinyl ester unit, except for the unit represented by the formula (3) or (4). Examples of the vinyl ester unit include vinyl formate, vinyl acetate, vinyl propionate, vinyl pivalate, vinyl trifluoroacetate, and vinyl 2-ethylhexanoate.

[0014] Further, other monomer units may be contained as long as the gist of the present invention is not impaired.
Examples of such units are ethylene, propylene, 1
Olefins such as butene and isobutene; acrylic acid, methacrylic acid, crotonic acid, (phthalic anhydride) phthalic acid,
Unsaturated acids such as (anhydride) maleic acid and (anhydride) itaconic acid or salts thereof or mono- or dialkyl esters having 1 to 18 carbon atoms; acrylamide, 1 to 1 carbon atoms
18 acrylamides such as N-alkylacrylamide, N, N-dimethylacrylamide, 2-acrylamidopropanesulfonic acid or a salt thereof, acrylamidopropyldimethylamine or an acid salt thereof or a quaternary salt thereof; methacrylamide, having 1 to 18 carbon atoms N-
Methacrylamides such as alkyl methacrylamide, N, N-dimethylmethacrylamide, 2-methacrylamidopropanesulfonic acid or a salt thereof, methacrylamidopropyldimethylamine or an acid salt or a quaternary salt thereof; N-vinylpyrrolidone, N- N-vinyl amides such as vinyl formamide and N-vinyl acetamide; vinyl cyanides such as acrylonitrile and methacrylonitrile; vinyl ethers such as alkyl vinyl ether having 1 to 18 carbon atoms, hydroxyalkyl vinyl ether and alkoxy alkyl vinyl ether; Vinyl halides such as vinyl, vinylidene chloride, vinyl fluoride, vinylidene fluoride, and vinyl bromide; vinyl silanes such as trimethoxyvinyl silane; allyl acetate; allyl chloride; Alcohol, dimethyl allyl alcohol, and the like.

The molecular weight of the vinyl alcohol polymer of the present invention is not particularly limited. The range of 2 to 10,000 cp is preferred. The vinyl alcohol content is 10 to 99.9 mol%, preferably 50 to 99.9 mol%.

The vinyl alcohol polymer of the present invention can be obtained, for example, by a method of reacting a thiol having a phenolic hydroxyl group with a copolymer of a vinyl ester monomer and a vinyl monomer having an epoxy group, followed by hydrolysis. Can be.

Examples of the vinyl monomer having an epoxy group include allyl glycidyl ether, methallyl glycidyl ether, butadiene monoepoxide, 1,2-epoxy-5-hexene, 1,2-epoxy-7-octene,
1,2-epoxy-9-decene, 8-hydroxy-6,
7-epoxy-1-octene, 8-acetoxy-6,7
-Epoxy-1-octene, N- (2,3-epoxy)
Propylacrylamide, N- (2,3-epoxy) propylmethacrylamide, 4-acrylamidophenylglycidyl ether, 3-acrylamidophenylglycidylether, 4-methacrylamidophenylglycidylether, 3-methacrylamidophenylglycidylether, N-glycid Xymethylacrylamide,
N-glycidoxymethyl methacrylamide, N-glycidoxyethyl acrylamide, N-glycidoxyethyl methacrylamide, N-glycidoxypropyl acrylamide, N-glycidoxypropyl methacrylamide,
N-glycidoxybutyl acrylamide, N-glycidoxybutyl methacrylamide, 4-acrylamidomethyl-2,5-dimethyl-phenylglycidyl ether,
4-methacrylamidomethyl-2,5-dimethyl-phenylglycidyl ether, acrylamidopropyldimethyl (2,3-epoxy) propylammonium chloride, methacrylamidopropyldimethyl (2,3-epoxy) propylammonium chloride, glycidyl methacrylate, etc. Used.

Examples of the thiol having a phenolic hydroxyl group include 2-hydroxythiophenol, 3-hydroxythiophenol, 4-hydroxythiophenol, and 2-hydroxythiophenol.
Hydroxymethylthiophenol, 3-hydroxymethylthiophenol, 4-hydroxymethylthiophenol, 2- (2-hydroxyethyl) thiophenol, 3
-(2-hydroxyethyl) thiophenol, 4- (2
-Hydroxyethyl) thiophenol, 3-hydroxy-2-methylthiophenol, 4-hydroxy-2-methylthiophenol, 5-hydroxy-2-methylthiophenol, 6-hydroxy-2-methylthiophenol, 2-hydroxy-1-mercapto Naphthalene, 4-
Examples thereof include hydroxy-1-mercaptonaphthalene, 8-hydroxy-1-mercaptonaphthalene, and alkali metal salts thereof. Further, esters such as these acetates and benzoates can also be used.

In the production of the vinyl alcohol polymer of the present invention, a reaction between a thiol group or a thioester group and an epoxy group is used. It is carried out in a solvent that dissolves or swells the compound having a group. Examples of such a solvent include alcohols such as methanol, ethanol, n-propyl alcohol and n-butyl alcohol; aromatics such as benzene, toluene and xylene; ethers such as tetrahydrofuran, dioxane and diethyl ether; and n-hexane. And the like, and used alone or as a mixture. The reaction conditions vary depending on the structure of the epoxy group and the structure of the thiol or thioester. However, in general, when a solvent is used, the polymer concentration is 5 to 90%, and the concentration of the thiol group or thioester group / epoxy group concentration is 1.0 to 1.0%.
The reaction temperature is 0 to 250 ° C. and the reaction time is 0.01 to 20 hours at a molar ratio of 5.0. Here, in the reaction with thiol, a basic compound such as a tertiary amine (eg, triethylamine, pyridine, etc.), phosphine (eg, tributylphosphine, triphenylphosphine, etc.), sodium hydroxide, tetraethylammonium hydroxide, sodium methylate, etc. In the reaction with the thioester, quaternary ammonium salts such as tributylammonium chloride and tributylammonium bromide are effective as reaction catalysts. In order to prevent thiol oxidation, the reaction system may be degassed or replaced with nitrogen, or an antioxidant may be added.

For the hydrolysis subsequent to the reaction between the thiol group or thioester group and the epoxy group, a saponification reaction using a basic catalyst or an acid catalyst, which is commonly used in the saponification of polyvinyl ester, can be applied as it is. That is, using a basic catalyst such as sodium hydroxide, potassium hydroxide or sodium methylate or an acidic catalyst such as p-toluenesulfonic acid, the reaction is carried out using alcohol or glycol such as methanol, ethanol, propanol, butanol or ethylene glycol as a solvent. Is performed. In this case, a solvent such as tetrahydrofuran, dioxane, dimethyl sulfoxide, diethylene glycol dimethyl ether, toluene, acetone, or water is appropriately mixed and used in order to improve the solubility of the vinyl ester polymer and the catalyst. The conditions of the saponification reaction are appropriately adjusted depending on the structure of the vinyl ester polymer to be used and the desired degree of saponification of the vinyl alcohol polymer. Usually, the saponification is carried out at a catalyst concentration / vinyl ester unit concentration (molar ratio) = 0.00
1-1.2, reaction temperature: 20-180 ° C, reaction time:
It is performed in the range of 0.1 to 20 hours.

The vinyl alcohol-based polymer containing the unit represented by Chemical formula 3 or Chemical formula 4 obtained by the present invention may be a fiber sizing agent, a fiber treating agent, a fiber processing agent, a clear coating,
Binder for paper coating agent such as clay coating, paper processing agent such as binder for overcoating of thermal paper, dispersant for organic and inorganic pigments, polymerization dispersion stabilizer for emulsion, polymerization dispersion stabilizer for PVC, binder for ceramics, Utilizing the reactivity of phenolic hydroxyl groups for image forming materials, photosensitive resins, raw materials for polyvinyl acetal such as formal resins and butyral resins, films, fibers, etc., alone or in combination with unmodified PVA or other modified PVA , Starch (and modified products thereof), cellulose derivatives, gums, gelatin, casein, and other polymers, combined with plasticizers, and used with crosslinking agents such as epoxy compounds and isocyanates.

[0022]

EXAMPLES The present invention will be described more specifically with reference to Synthesis Examples and Examples, which should not be construed as limiting the present invention. “Parts” and “%” in Synthesis Examples and Examples represent “parts by weight” and “% by weight”, respectively, unless otherwise specified.

(Synthesis Example of Vinyl Ester Polymer Having Epoxy Group) Synthesis Example 1 405 parts of vinyl acetate monomer and allyl glycidyl ether 11 were placed in a reactor equipped with a stirrer, a reflux condenser, a nitrogen inlet and a thermometer. Parts and 30 parts of methanol,
Degas by bubbling nitrogen gas for 15 minutes. Separately, an initiator solution was prepared by dissolving 4.5 parts of 2,2′-azoisobutyronitrile in 15 parts of methanol, and the mixture was purged with nitrogen by bubbling nitrogen gas. Start raising the temperature of the reactor until the internal temperature reaches 6
When the temperature reached 0 ° C., a separately prepared initiator solution was added to initiate polymerization. Polymerization was carried out at 60 ° C. for 4 hours, and the polymerization was stopped by cooling. At this time, the solid content concentration was 54.8%. Subsequently, unreacted vinyl acetate monomer was removed while occasionally adding methanol at 30 ° C. under reduced pressure, and a methanol solution of polyvinyl acetate copolymer (concentration: 44.5%)
I got A part of this methanol solution was put into ether to recover the polymer, which was purified by reprecipitation twice with acetone-ether, and then dried at 40 ° C. under reduced pressure. The purified polymer was subjected to proton NMR (GSX-270, manufactured by JEOL) and intrinsic viscosity measurement in acetone (JIS) using CDCl ₃ as a solvent to calculate the viscosity average molecular weight. Is a polyvinyl acetate copolymer having a viscosity average molecular weight of 80 × 10 ³ containing 2.1 mol% of

Synthetic Examples 2 to 7 In the same manner as in Synthetic Example 1 except that the type and amount of vinyl ester monomer, the amount of methanol, the type and amount of initiator, and the removal of unreacted vinyl ester monomer were partially n-butanol , Etc.) to obtain a vinyl ester polymer having an epoxy group shown in Table 1.

[0025]

[Table 1]

Example 1 100 parts of a methanol solution (concentration: 44.5%) of the polymer having an epoxy group obtained in Synthesis Example 1 was placed in a reactor equipped with a stirrer, a reflux condenser, a nitrogen inlet, and a thermometer. After weighing and bubbling nitrogen gas for 15 minutes, a solution prepared by dissolving 2.9 parts of 4-mercaptophenol and 0.46 part of sodium hydroxide in 48 parts of methanol was charged. After reacting at 50 ° C. for 2 hours with stirring, the mixture was cooled to 40 ° C.
Saponification was performed by adding 40 parts of a 0% sodium hydroxide methanol solution. After leaving at 40 ° C. for 5 hours, pulverized, neutralized by adding 8 parts of acetic acid, washed with methanol using a Soxhlet extractor for 48 hours or more, dried at 60 ° C. for 20 hours or more, and modified vinyl alcohol-based. A polymer was obtained. IR and proton NMR (d ₆ −
As a result of measurement of (DMSO), the epoxy group was completely disappeared, introduction of 2.1 mol% of a phenol group was confirmed, and the vinyl alcohol content was 96.5 mol%.
Also, a 4% DMSO solution of the polymer was prepared,
Was 60.1 cp.

Examples 2 to 7 In the same manner as in Example 1, a modified polyvinyl alcohol having a phenolic hydroxyl group was obtained. Table 2 shows the synthesis conditions and results.
Shown in

[0028]

[Table 2]

4-MPH: 4-mercaptophenol 2-MPH: 2-mercaptophenol 4-MEPH: 4- (2-mercapto) ethylphenol VA: vinyl alcohol unit

[0030]

According to the present invention, there is provided a vinyl alcohol polymer having a phenolic hydroxyl group which is excellent in functionality.

──────────────────────────────────────────────────続 き Continuation of the front page (51) Int.Cl. ⁶ Identification number Agency reference number FI Technical indication location C08F 228/02 MNR C08F 228/02 MNR

Claims (1)

[Claims] 1. A vinyl alcohol polymer containing 0.01 to 30 mol% of a unit represented by the following chemical formula 1 or 2. Embedded image Embedded image (Where R ¹ , R ² , R ³ , R ⁴ and R ⁵ represent a hydrogen atom or a hydrocarbon group having 8 or less carbon atoms which may have a substituent, and A represents a nitrogen atom, an oxygen atom or (S represents a divalent hydrocarbon group which may contain a sulfur atom, S represents a sulfur atom, and X represents a monovalent group containing a phenolic hydroxyl group.)