JPH1045843A - Diene-containing vinyl alcohol-based polymer - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain a vinyl alcohol-based polymer capable of exhibiting excellent reactivity caused by a conjugated diene structure by adding a conjugated diene structure-containing unit in a certain mol% of a specific range to the molecular chain. SOLUTION: This polymer contains 0. 01-30mol% of a unit of formula I (R<1> to R<5> are each H or a <=8C hydrocarbon group which may contain a substituent group; A is a bifunctional hydrocarbon group which may contain an N atom, an O atom or an S atom; X is a conjugated diene structure-containing monofunctional group) or formula II. The polymer is obtained, for example, by reacting a copolymer of a vinyl ester monomer and an epoxy group- containing vinyl monomer with a conjugated diene structure-containing thiol and hydrolyzing. Consequently, the polymer is excellent in reactivity derived from the conjugated diene and is usable as a fiber sizing agent, a fiber treating agent, clear coating, etc.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention relates to a novel modified vinyl alcohol-based polymer.

[0002]

2. Description of the Related Art Polyvinyl alcohol is one of the few crystalline water-soluble polymers that has excellent interfacial properties and strength properties. Therefore, polyvinyl alcohol is used as a stabilizer for paper processing, fiber processing and emulsions. It occupies an important position as a raw material for films and polyvinyl alcohol fibers. On the other hand, pursuit of high functionality by controlling crystallinity or improving specific performance by introducing a functional group has been pursued, and various types of so-called modified polyvinyl alcohol have been developed.

However, a vinyl alcohol-based polymer (or the polymer composition) excellent in cross-linking properties, particularly under mild conditions at low temperatures, has not necessarily been developed to a satisfactory polymer. There is a strong demand for a vinyl alcohol polymer having high reactivity.

[0004]

Under such circumstances, an object of the present invention is to provide a novel modified vinyl alcohol-based polymer having reactivity derived from a conjugated diene.

[0005]

The present inventors have conducted intensive studies on such a novel modified vinyl alcohol-based polymer, and found that the unit represented by the following chemical formula (3) or (4) is 0.1.
The present inventors have found a vinyl alcohol polymer containing from 01 to 30 mol%, and have completed the present invention.

[0006]

Embedded image

[0007]

Embedded image

(Wherein R ¹ , R ² , R ³ , R ⁴ and R ⁵ represent a hydrogen atom or a hydrocarbon group having 8 or less carbon atoms which may have a substituent, A represents a nitrogen atom, Represents a divalent hydrocarbon group which may contain an oxygen atom or a sulfur atom, S represents a sulfur atom, and X represents a monovalent group containing a conjugated diene structure.)

[0009]

BEST MODE FOR CARRYING OUT THE INVENTION The vinyl alcohol-based polymer of the present invention has a unit represented by Formula 3 or 4 in its molecular chain.
It is a vinyl alcohol-based polymer containing from 01 to 30 mol%, and there is no particular limitation on the distribution of the unit represented by the formula (3) or (4) in the polymer. When the content of the unit is 0.0
If it is less than 1 mol%, the effect of introduction is not sufficiently exhibited,
If it exceeds 30 mol%, a problem occurs in the storage stability (for example, gelation) of the vinyl alcohol-based polymer. A more preferable range of the content of the unit is 0.02 to 20 mol%, and a particularly preferable range is 0.05 to 15 mol%.

R ¹ in the unit represented by the formula (3) or (4),
R ² , R ³ , R ⁴ and R ⁵ are not particularly limited as long as they are a hydrogen atom or a hydrocarbon group having 8 or less carbon atoms which may have a substituent, but R ¹ is a hydrogen atom, R ² is a hydrogen atom or a methyl group, and R ³ , R ⁴ and R ⁵ are a hydrogen atom or 8 or less carbon atoms (preferably 6 or less carbon atoms)
Are preferably used. Note that R ³ and R
⁴ (or R ⁵ ) may form a ring together.

A in the unit represented by Formula 4 is a nitrogen atom,
The structure is not particularly limited as long as it is a divalent hydrocarbon group which may contain an oxygen atom or a sulfur atom.
_{-CH 2 OCH 2 -, - OCH} 2 -, - CONH-φ-
OCH ₂ —, —CONHCH ₂ —, —CONHCH ₂ O
CH ₂ —, —CONHCH ₂ OCH ₂ CH ₂ —, —CO
_{NHCH 2 OCH 2 CH 2 CH 2} -, - CONHCH 2
OCH ₂ CH ₂ CH ₂ CH _2- , -CONHCH ₂ -φ
(CH ₃ ) ₂ —CH ₂ — and the like are exemplified. (Note that φ means phenylene.)

X in the unit represented by Formula 3 or 4 is
The structure is not particularly limited as long as the group is a monovalent group having a conjugated diene structure.

[0013]

Embedded image

[0014]

Embedded image

[0015]

Embedded image

[0016]

Embedded image

The vinyl alcohol polymer of the present invention substantially comprises a vinyl alcohol unit or a vinyl alcohol unit and a vinyl ester unit, except for the unit represented by the formula (3) or (4). Examples of the vinyl ester unit include vinyl formate, vinyl acetate, vinyl propionate, vinyl pivalate, vinyl trifluoroacetate, and vinyl 2-ethylhexanoate.

Further, other monomer units may be contained as long as the gist of the present invention is not impaired.
Examples of such units are ethylene, propylene, 1
Olefins such as butene and isobutene; acrylic acid, methacrylic acid, crotonic acid, (phthalic anhydride) phthalic acid,
Unsaturated acids such as (anhydride) maleic acid and (anhydride) itaconic acid or salts thereof or mono- or dialkyl esters having 1 to 18 carbon atoms; acrylamide, 1 to 1 carbon atoms
18 acrylamides such as N-alkylacrylamide, N, N-dimethylacrylamide, 2-acrylamidopropanesulfonic acid or a salt thereof, acrylamidopropyldimethylamine or an acid salt thereof or a quaternary salt thereof; methacrylamide, having 1 to 18 carbon atoms N-
Methacrylamides such as alkyl methacrylamide, N, N-dimethylmethacrylamide, 2-methacrylamidopropanesulfonic acid or a salt thereof, methacrylamidopropyldimethylamine or an acid salt or a quaternary salt thereof; N-vinylpyrrolidone, N- N-vinyl amides such as vinyl formamide and N-vinyl acetamide; vinyl cyanides such as acrylonitrile and methacrylonitrile; vinyl ethers such as alkyl vinyl ether having 1 to 18 carbon atoms, hydroxyalkyl vinyl ether and alkoxy alkyl vinyl ether; Vinyl halides such as vinyl, vinylidene chloride, vinyl fluoride, vinylidene fluoride, and vinyl bromide; vinyl silanes such as trimethoxyvinyl silane; allyl acetate; allyl chloride; Alcohol, dimethyl allyl alcohol, and the like.

Although the molecular weight of the vinyl alcohol polymer of the present invention is not particularly limited, it is represented by the viscosity of a 4% dimethyl sulfoxide (DMSO) solution of the polymer at 20 ° C. (measured with a B-type viscometer). The range of 2 to 10,000 cp is preferred. The vinyl alcohol content is 10 to 99.9 mol%, preferably 50 to 99.9 mol%.

The vinyl alcohol polymer of the present invention can be obtained, for example, by a method comprising reacting a thiol having a conjugated diene structure with a copolymer of a vinyl ester monomer and a vinyl monomer having an epoxy group, followed by hydrolysis. Can be.

Examples of the vinyl monomer having an epoxy group include allyl glycidyl ether, methallyl glycidyl ether, butadiene monoepoxide, 1,2-epoxy-5-hexene, 1,2-epoxy-7-octene,
1,2-epoxy-9-decene, 8-hydroxy-6,
7-epoxy-1-octene, 8-acetoxy-6,7
-Epoxy-1-octene, N- (2,3-epoxy)
Propylacrylamide, N- (2,3-epoxy) propylmethacrylamide, 4-acrylamidophenylglycidyl ether, 3-acrylamidophenylglycidylether, 4-methacrylamidophenylglycidylether, 3-methacrylamidophenylglycidylether, N-glycid Xymethylacrylamide,
N-glycidoxymethyl methacrylamide, N-glycidoxyethyl acrylamide, N-glycidoxyethyl methacrylamide, N-glycidoxypropyl acrylamide, N-glycidoxypropyl methacrylamide,
N-glycidoxybutyl acrylamide, N-glycidoxybutyl methacrylamide, 4-acrylamidomethyl-2,5-dimethyl-phenylglycidyl ether,
4-methacrylamidomethyl-2,5-dimethyl-phenylglycidyl ether, acrylamidopropyldimethyl (2,3-epoxy) propylammonium chloride, methacrylamidopropyldimethyl (2,3-epoxy) propylammonium chloride, glycidyl methacrylate, etc. Used.

Examples of the thiol having a conjugated diene structure include the thiols shown in Chemical formulas 9 to 12, and esters such as acetates and benzoates thereof can also be used.

[0023]

Embedded image

[0024]

Embedded image

[0025]

Embedded image

[0026]

Embedded image

In the production of the vinyl alcohol polymer of the present invention, a reaction between a thiol group or a thioester group and an epoxy group is used. It is carried out in a solvent that dissolves or swells the compound having a group. Examples of such a solvent include alcohols such as methanol, ethanol, n-propyl alcohol and n-butyl alcohol; aromatics such as benzene, toluene and xylene; ethers such as tetrahydrofuran, dioxane and diethyl ether; and n-hexane. And the like, and used alone or as a mixture. The reaction conditions vary depending on the structure of the epoxy group and the structure of the thiol or thioester. However, in general, when a solvent is used, the polymer concentration is 5 to 90%, and the concentration of the thiol group or thioester group / epoxy group concentration is 1.0 to 1.0%.
The reaction temperature is 0 to 250 ° C. and the reaction time is 0.01 to 20 hours at a molar ratio of 5.0. Here, in the reaction with thiol, a basic compound such as a tertiary amine (eg, triethylamine, pyridine, etc.), phosphine (eg, tributylphosphine, triphenylphosphine, etc.), sodium hydroxide, tetraethylammonium hydroxide, sodium methylate, etc. In the reaction with the thioester, quaternary ammonium salts such as tributylammonium chloride and tributylammonium bromide are effective as reaction catalysts. In order to prevent thiol oxidation, the reaction system may be degassed or replaced with nitrogen, or an antioxidant may be added.

For the hydrolysis subsequent to the reaction between the thiol group or the thioester group and the epoxy group, a saponification reaction using a basic catalyst or an acid catalyst, which is generally used in the saponification of a polyvinyl ester, can be applied as it is. That is, using a basic catalyst such as sodium hydroxide, potassium hydroxide or sodium methylate or an acidic catalyst such as p-toluenesulfonic acid, the reaction is carried out using alcohol or glycol such as methanol, ethanol, propanol, butanol or ethylene glycol as a solvent. Is performed. In this case, a solvent such as tetrahydrofuran, dioxane, dimethyl sulfoxide, diethylene glycol dimethyl ether, toluene, acetone, or water is appropriately mixed and used in order to improve the solubility of the vinyl ester polymer and the catalyst. The conditions of the saponification reaction are appropriately adjusted depending on the structure of the vinyl ester polymer to be used and the desired degree of saponification of the vinyl alcohol polymer. Usually, the saponification is carried out at a catalyst concentration / vinyl ester unit concentration (molar ratio) = 0.00
1-1.2, reaction temperature: 20-180 ° C, reaction time:
It is performed in the range of 0.1 to 20 hours.

The vinyl alcohol polymer containing a unit represented by the formula (3) or (4) obtained by the present invention can be used as a fiber paste, a fiber treating agent, a fiber processing agent, Binders for paper coating agents such as clear coating and clay coating, paper processing agents such as binders for thermal paper overcoating, dispersants for organic and inorganic pigments, polymerization dispersion stabilizers for emulsions, polymerization dispersion stabilizers for PVC, ceramics For binders, image forming materials, photosensitive resins, raw materials for polyvinyl acetal such as formal resins and butyral resins, films, fibers, etc., utilizing the reactivity of conjugated dienes, alone or with unmodified PVA or other modified PVA , Starch (and its modified products), cellulose derivatives, gums, gelatin, casein and other polymers Combination with a plasticizer, is utilized in combination with the crosslinking agent such as bismaleimide.

[0030]

EXAMPLES The present invention will be described more specifically with reference to Synthesis Examples and Examples, which should not be construed as limiting the present invention. “Parts” and “%” in Synthesis Examples and Examples represent “parts by weight” and “% by weight”, respectively, unless otherwise specified.

(Synthesis Example of Vinyl Ester Polymer Having Epoxy Group) Synthesis Example 1 405 parts of vinyl acetate monomer, allyl glycidyl ether 11 were placed in a reactor equipped with a stirrer, a reflux condenser, a nitrogen inlet tube and a thermometer. Parts and 30 parts of methanol,
Degas by bubbling nitrogen gas for 15 minutes. Separately, an initiator solution was prepared by dissolving 4.5 parts of 2,2′-azoisobutyronitrile in 15 parts of methanol, and the mixture was purged with nitrogen by bubbling nitrogen gas. Start raising the temperature of the reactor until the internal temperature reaches 6
When the temperature reached 0 ° C., a separately prepared initiator solution was added to initiate polymerization. Polymerization was carried out at 60 ° C. for 4 hours, and the polymerization was stopped by cooling. At this time, the solid content concentration was 54.8%. Subsequently, unreacted vinyl acetate monomer was removed while occasionally adding methanol at 30 ° C. under reduced pressure, and a methanol solution of polyvinyl acetate copolymer (concentration: 44.5%)
I got A part of this methanol solution was put into ether to recover the polymer, which was purified by reprecipitation twice with acetone-ether, and then dried at 40 ° C. under reduced pressure. The purified polymer was subjected to proton NMR (GSX-270, manufactured by JEOL) and intrinsic viscosity measurement in acetone (JIS) using CDCl ₃ as a solvent to calculate the viscosity average molecular weight. Is a polyvinyl acetate copolymer having a viscosity average molecular weight of 80 × 10 ³ containing 2.1 mol% of

Synthesis Examples 2 to 7 In the same manner as in Synthesis Example 1, except that the type and amount of vinyl ester monomer, the amount of methanol, the type and amount of initiator, and the removal of unreacted vinyl ester monomer were partially n-butanol. , Etc.) to obtain a vinyl ester polymer having an epoxy group shown in Table 1.

[0033]

[Table 1]

Example 1 100 parts of a methanol solution (concentration: 44.5%) of the polymer having an epoxy group obtained in Synthesis Example 1 was placed in a reactor equipped with a stirrer, a reflux condenser, a nitrogen inlet, and a thermometer. After weighing and bubbling nitrogen gas for 15 minutes, a solution prepared by dissolving 2.9 parts of furfuryl mercaptan and 0.03 part of sodium hydroxide in 48 parts of methanol was charged. 5 with stirring
After reacting at 0 ° C for 2 hours, cool to 40 ° C and
40% of a methanol solution of sodium hydroxide having a concentration of 10% was added to perform saponification. After leaving at 40 ° C. for 5 hours, the mixture was pulverized, neutralized by adding 8 parts of acetic acid, and washed with methanol using a Soxhlet extractor for 48 hours or more.
After drying for 0 hour or more, a modified vinyl alcohol-based polymer was obtained. IR and proton NMR (d ₆ -D
(MSO), the epoxy group had completely disappeared, and the introduction of a 2.1 mol% furan ring group was confirmed.
The vinyl alcohol content was 97.0 mol%. Further, a 4% DMSO solution of the polymer was prepared, and the viscosity was measured at 20 ° C. to find that it was 59.8 cp.

Examples 2 to 7 In the same manner as in Example 1, a modified polyvinyl alcohol having a furan ring group was obtained. Table 2 shows the synthesis conditions and results.

[0036]

[Table 2]

FM: furfuryl mercaptan VA: vinyl alcohol unit

[0038]

According to the present invention, a vinyl alcohol polymer having a conjugated diene structure with high reactivity is provided.

Claims (2)

[Claims] 1. A vinyl alcohol polymer containing 0.01 to 30 mol% of a unit represented by the following chemical formula 1 or 2. Embedded image Embedded image (Where R ¹ , R ² , R ³ , R ⁴ and R ⁵ represent a hydrogen atom or a hydrocarbon group having 8 or less carbon atoms which may have a substituent, and A represents a nitrogen atom, an oxygen atom or (Represents a divalent hydrocarbon group which may contain a sulfur atom, S represents a sulfur atom, and X represents a monovalent group containing a conjugated diene structure.) 2. The polyvinyl alcohol-based polymer according to claim 1, wherein X is a monovalent group containing a furan ring.