JPH10151405A - Method for working surface of formed polystyrene - Google Patents
Method for working surface of formed polystyreneInfo
- Publication number
- JPH10151405A JPH10151405A JP32910596A JP32910596A JPH10151405A JP H10151405 A JPH10151405 A JP H10151405A JP 32910596 A JP32910596 A JP 32910596A JP 32910596 A JP32910596 A JP 32910596A JP H10151405 A JPH10151405 A JP H10151405A
- Authority
- JP
- Japan
- Prior art keywords
- glass fiber
- mesh
- fiber mesh
- base material
- solidified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、発泡スチロールの
表面の施工方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for constructing a surface of polystyrene foam.
【0002】[0002]
【従来の技術】従来より、例えば、バルコニー等の支柱
上部や梁の装飾のための装飾物は型を作成し、この型に
石こうを流し込んで所定の形に成型すると共に、この石
こうを所定の位置に取り付けていた。しかし、上記した
従来の方法は、型を作るためにコスト高になると共に、
施工期間も長くなり、又、重量が大であるため、取り付
けに多くの人手と手間が必要であるという欠点があっ
た。2. Description of the Related Art Conventionally, for example, decorations for decorating upper portions of pillars and beams, such as balconies, are made into a mold, and plaster is poured into the mold and molded into a predetermined shape. Had been mounted in position. However, the above-mentioned conventional method increases the cost for making the mold,
Since the construction period is long and the weight is large, there is a drawback that a large number of people and labor are required for installation.
【0003】[0003]
【発明が解決しようとする課題】この発明は上記した点
に鑑みてなされたものであり、その目的とするところ
は、発泡スチロールの表面をグラスファイバーメッシュ
と下地剤とでコーティングし、下地剤により所定の強度
をもたせるようにすると共にグラスファイバーメッシュ
を用いることにより柔軟性を持つようにして、クラック
等生じないようにした軽くて所定の強度を有する新規の
発泡スチロールの表面の施工方法を提供するものであ
る。DISCLOSURE OF THE INVENTION The present invention has been made in view of the above points, and an object of the present invention is to coat the surface of styrofoam with a glass fiber mesh and a base material, and to apply a predetermined amount to the base material. In order to provide a new method of applying a surface of a new styrofoam having a light and predetermined strength so as to have a strength and to have flexibility by using a glass fiber mesh so as not to cause cracks and the like. is there.
【0004】[0004]
【課題を解決するための手段】上記課題を解決するた
め、本発明の発泡スチロールの表面の施工方法は、発泡
スチロールの表面をグラスファイバーメッシュで覆い前
記グラスファイバーメッシュ上にアクリルとこのアクリ
ルに対し10〜20重量%のセメントを混入して攪拌し
た下地材を塗布又は吹き付け乾燥させ固化せしめたこと
を特徴とする。In order to solve the above-mentioned problems, the present invention provides a method for applying a surface of styrofoam to cover the surface of styrofoam with a glass fiber mesh, and apply acrylic on the glass fiber mesh and 10 to 10% of the acrylic. It is characterized in that a base material mixed with 20% by weight of cement and stirred is applied or sprayed and dried to be solidified.
【0005】又、前記固化させた下地剤上に、更に、グ
ラスファイバーメッシュと下地材とからなるコーティン
グ層を少なくとも一層以上形成したことを特徴とする。[0005] Further, at least one coating layer comprising a glass fiber mesh and a base material is further formed on the solidified base material.
【0006】[0006]
【発明の実施の形態】図1乃至図5は本発明の発泡スチ
ロールの表面の施工方法を説明する図である。図におい
て、1は、例えば、熱線を用いて所定の形状に切断し形
成した発泡スチロールからなるベース材であり、このベ
ース材1の表面2には、グラスファイバーをナッシュ状
にしたグラスファイバーメッシュ3が置かれ、更に、ベ
ース材1とグラスファイバーメッシュ3上に下地剤4
が、コテ塗り、又は、吹き付けにより塗布される。上記
下地剤4は液状のアクリル樹脂に粉状のセメントを10
〜20重量%混入して攪拌したものである。なお、必要
に応じこれに砂を混入させてもよい。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS FIGS. 1 to 5 are views for explaining a method for applying a surface of a polystyrene foam according to the present invention. In the drawing, reference numeral 1 denotes a base material made of, for example, styrofoam cut and formed into a predetermined shape using a hot wire, and a glass fiber mesh 3 in which glass fibers are made into a Nash shape is formed on a surface 2 of the base material 1. Placed on the base material 1 and the glass fiber mesh 3
Is applied by ironing or spraying. The base material 4 is composed of 10 parts of powdery cement in liquid acrylic resin.
2020% by weight was mixed and stirred. In addition, you may mix sand with this as needed.
【0007】さて、この状態で約1昼夜程度放置し、下
地剤4を乾燥させると、下地剤4は固化し、コーティン
グ層5が形成される。この状態では、下地剤4が、固化
することによりコーティング層5は堅く、強度を有して
いる。更に、グラスファイバーメッシュ3の作用によ
り、柔軟性を有し、従って、例えば、板状の発泡スチロ
ールを曲げてもクラックは発生しない。この上に装飾仕
上げ剤6を塗布又は吹き付けて、所定の装飾物が形成さ
れる。When the undercoating agent 4 is dried in this state for about one day and night, the undercoating agent 4 is solidified and the coating layer 5 is formed. In this state, the base layer 4 is solidified, so that the coating layer 5 is hard and has strength. Further, the glass fiber mesh 3 has flexibility due to the action of the glass fiber mesh, and therefore, for example, cracks do not occur even when a plate-like styrofoam is bent. The decorative finish 6 is applied or sprayed thereon to form a predetermined decorative product.
【0008】なお更に、強度を増す必要が有る場合に
は、図4に示すようにコーティング層5の上に更にグラ
スファイバーメッシュ3と下地剤4からなるコーティン
グ層7を設けるとよい。勿論、コーティング層は2〜3
層と多層にしてもよい。If it is necessary to further increase the strength, a coating layer 7 made of a glass fiber mesh 3 and a base material 4 may be further provided on the coating layer 5 as shown in FIG. Of course, the coating layer is 2-3
Layers and multilayers may be used.
【0009】図5は実際にビルの外壁のデコレーション
に本発明を適用した例を示す図である。図5のデコレー
ション11は発泡スチロールを直方体に形成し、側面1
2と正面13を本発明の方法を用いてコーティングした
ものであり外壁8に設けられた出入口14を囲むように
デコレーション11が外壁8に接着剤を用いて取り付け
られている。FIG. 5 is a view showing an example in which the present invention is applied to decoration of an outer wall of a building. The decoration 11 shown in FIG.
The decoration 11 is attached to the outer wall 8 using an adhesive so as to surround the entrance 14 provided in the outer wall 8.
【0010】上記説明では、建築物の外壁の装飾(デコ
レーション)を例に説明したが、軽く、又、所定の形を
容易に、しかも、安価に短時間で作ることができること
から、例えば、演劇の舞台やテレビスタジオで短時間使
用する背景を構成するものや、その他の飾り物、置物等
に広く適用することができる。又、置物等の表面形状が
複雑な場合には、グラスファイバーメッシュ3を使用し
ない方がよい場合もあるが、このようにしても特に支障
がない。In the above description, the decoration of the outer wall of a building has been described as an example. However, since it is possible to make a predetermined shape easily, inexpensively and in a short time, for example, a theater, It can be widely applied to things that constitute a background that is used for a short time on a stage or a television studio, and other decorations and ornaments. Further, when the surface shape of the ornament or the like is complicated, it may be better not to use the glass fiber mesh 3, but this does not cause any particular problem.
【0011】[0011]
【発明の効果】本発明に係る発泡スチロールの表面の施
工方法によれば、上述のように構成したので、以下のよ
うな効果を奏する。 (1) 下地剤は乾燥するとモルタルと同様な強度を有する
から、軽くて、強度を有する材料になる。しかも、グラ
スファイバーメッシュを用いることにより、柔軟性もあ
るため、クラックも発生しにくい。According to the styrofoam surface construction method according to the present invention, the following effects can be obtained because of the above-described configuration. (1) Since the base material has the same strength as mortar when dried, it becomes a light and strong material. In addition, the use of the glass fiber mesh has flexibility, so that cracks hardly occur.
【0012】(2) 内部は発泡スチロールのため軽く、搬
入、施工作業が容易であり、従って作業能率も向上す
る。 (3) 切断も容易であるため、現場合わせが極めて容易で
ある。(2) Since the interior is made of styrofoam, it is light and easy to carry in and carry out, so that work efficiency is improved. (3) Since cutting is easy, site adjustment is extremely easy.
【図1】所定の形状に切断した発泡スチロールの斜視図
である。FIG. 1 is a perspective view of a polystyrene foam cut into a predetermined shape.
【図2】メッシュを貼りつけている状態を示す図であ
る。FIG. 2 is a diagram showing a state where a mesh is attached.
【図3】図2のA−A断面図である。FIG. 3 is a sectional view taken along line AA of FIG. 2;
【図4】本発明の他の実施の形態を示す断面図である。FIG. 4 is a cross-sectional view showing another embodiment of the present invention.
【図5】本発明の他の実施の形態を示す斜視図である。FIG. 5 is a perspective view showing another embodiment of the present invention.
【符号の説明】 1 ベース材 2 表面 3 グラスファイバーメッシュ 4 下地剤 5,7 コーティング層 8 外壁 11 デコレーション 14 出入口[Description of Signs] 1 Base material 2 Surface 3 Glass fiber mesh 4 Base agent 5, 7 Coating layer 8 Outer wall 11 Decoration 14 Doorway
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 FI B32B 27/30 B32B 27/30 B A E04F 13/18 E04F 13/18 C ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI B32B 27/30 B32B 27/30 B A E04F 13/18 E04F 13/18 C
Claims (2)
ーメッシュで覆い前記グラスファイバーメッシュ上にア
クリルとこのアクリルに対し10〜20重量%のセメン
トを混入して攪拌した下地材を塗布又は吹き付け乾燥さ
せ固化せしめたことを特徴とする発泡スチロールの表面
の施工方法。1. A surface of styrofoam is covered with a glass fiber mesh, and acrylic and 10 to 20% by weight of cement are mixed with the acrylic on the glass fiber mesh, and a stirred base material is applied or sprayed to be dried and solidified. A method for constructing a styrofoam surface.
スファイバーメッシュと下地材とからなるコーティング
層を少なくとも一層以上形成したことを特徴とする請求
項1記載の発泡スチロールの表面の施工方法。2. The method according to claim 1, wherein at least one or more coating layers comprising a glass fiber mesh and a base material are further formed on the solidified base material.