JPH0995648A - Pressure-sensitive adhesive recording sheet - Google Patents
Pressure-sensitive adhesive recording sheetInfo
- Publication number
- JPH0995648A JPH0995648A JP7252548A JP25254895A JPH0995648A JP H0995648 A JPH0995648 A JP H0995648A JP 7252548 A JP7252548 A JP 7252548A JP 25254895 A JP25254895 A JP 25254895A JP H0995648 A JPH0995648 A JP H0995648A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- recording sheet
- adhesive layer
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、インクジェット記録が
可能で、かつ記録された記録の定着性が良好な感圧接着
性記録シートに関するものである。ここで感圧接着性記
録シートとは、通常状態では粘着性、接着性ともに示さ
ず加圧時に接着性を示し、加圧接着後に剥離可能な感圧
接着層を有する記録シートのことである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure-sensitive adhesive recording sheet which is capable of ink jet recording and has good fixability of the recorded record. Here, the pressure-sensitive adhesive recording sheet refers to a recording sheet having a pressure-sensitive adhesive layer that exhibits neither adhesiveness nor adhesiveness in a normal state, exhibits adhesiveness under pressure, and can be peeled off after pressure-bonding.
【０００２】[0002]
【従来の技術】近年、感圧接着性記録シートを用いた２
つ折りはがきや３つ折りはがきの用途が拡大している。
これらの感圧接着性記録シートは、支持体に通常状態で
は粘着性、接着性ともに示さず加圧時に接着性を示す感
圧接着剤を塗布して感圧接着層を形成させ、シートを折
り畳むことにより感圧接着層同士を対面させた状態で圧
力により接着させるものであり、加圧時の接着は接着後
に剥離可能にもできるし、剥離不能なまでに接着するこ
とも可能である。はがきの親展通信内容（暗証番号、会
員番号、請求金額、預金残高など）は剥離可能な感圧接
着面に印字し、圧力により貼合せた後、受取人が剥離す
ることにより内容を確認できる。2. Description of the Related Art Recently, a pressure-sensitive adhesive recording sheet has been used.
The applications of 3-fold postcards and 3-fold postcards are expanding.
In these pressure-sensitive adhesive recording sheets, a support is coated with a pressure-sensitive adhesive that exhibits neither adhesiveness nor adhesiveness in a normal state but exhibits adhesiveness when pressed, and a pressure-sensitive adhesive layer is formed, and the sheet is folded. As a result, the pressure-sensitive adhesive layers are adhered to each other by pressure in a state of being faced to each other. Adhesion at the time of pressurization can be peelable after the adhesion or can be performed before the separation is possible. The contents of confidential communication (postal code number, membership number, billing amount, deposit balance, etc.) on postcards can be printed on the peelable pressure-sensitive adhesive surface, pasted by pressure, and then the recipient can confirm the contents.
【０００３】このような感圧接着性記録シートは、感圧
接着層の上に印字して別の感圧接着層と加圧により貼合
せ、かつ再度それぞれを剥離して内容を確認するため、
印字した内容が対面の感圧接着層に転写するという、い
わゆる裏写り、インク写りの問題があった。このような
裏写りの現象を避けるために、印字した後にインク（ま
たはトナー）を熱で定着する印字方式（電子写真、レー
ザープリンターなど）が採用されている。Such a pressure-sensitive adhesive recording sheet is printed on the pressure-sensitive adhesive layer, laminated with another pressure-sensitive adhesive layer by pressure, and peeled again to confirm the contents.
There is a problem of so-called show-through and ink transfer in which the printed content is transferred to the pressure-sensitive adhesive layer on the opposite side. In order to avoid such a show-through phenomenon, a printing method (electrophotography, laser printer, etc.) in which ink (or toner) is fixed by heat after printing is adopted.
【０００４】しかしながら、このような熱定着の方式は
印字面（感圧接着面）および紙自体に過度の熱を与え、
その水分を奪うため、感圧接着層が乾燥し圧着性が低下
するという問題や、やはり過度の加熱により感圧接着層
を構成する接着成分の一部が熱分解し、異臭を発生して
作業環境を悪化させるという問題があった。However, such a heat fixing method gives excessive heat to the printing surface (pressure-sensitive adhesive surface) and the paper itself,
Since the moisture is taken away, the pressure-sensitive adhesive layer dries and the pressure-bonding property deteriorates. Again, excessive heating causes some of the adhesive components that make up the pressure-sensitive adhesive layer to be thermally decomposed, causing an offensive odor and causing work. There was a problem of deteriorating the environment.
【０００５】一方、インクジェット記録方式は、種々の
作動原理によりインクの微小液滴を飛翔させて紙などの
記録シートに付着させ、画像・文字などの記録を行なう
ものであるが、高速、低騒音、多色化が容易、記録パタ
ーンの融通性が大きい、現像−定着が不要等の特徴があ
り、漢字を含め各種図形及びカラー画像等の記録装置と
して種々の用途に於いて急速に普及している。さらに、
多色インクジェット記録方式により形成される画像は、
製版方式による多色印刷やカラー写真方式による印画に
比較して、遜色のない記録を得ることが可能である。
又、作成部数が少なくて済む用途に於いては、写真技術
によるよりも安価であることからフルカラー画像記録分
野にまで広く応用されつつある。On the other hand, the ink jet recording system is one in which minute droplets of ink are ejected and adhered to a recording sheet such as paper according to various operating principles to record images, characters, etc., but at high speed and low noise. It has features such as easy multicoloring, great flexibility in recording patterns, and no need for development-fixing. It has rapidly spread in various applications as a recording device for various figures and color images including Chinese characters. There is. further,
The image formed by the multi-color inkjet recording method is
Compared to multicolor printing by plate making method and printing by color photographic method, it is possible to obtain recording comparable to that.
In addition, in applications requiring a small number of copies, it is being widely applied to the field of full-color image recording because it is cheaper than the photographic technique.
【０００６】このように、非常に手軽でありながら、高
度な記録ができるインクジェット記録方式は圧着葉書に
使用するのに以下の点で有効である。As described above, the ink jet recording method, which is very convenient and enables high-level recording, is effective in the following points when it is used for a pressure-bonded postcard.
【０００７】 一般に圧着葉書の圧着面への印字はレ
ーザープリンターや電子写真方式など加熱定着型の記録
が用いられるが、この加熱定着工程で圧着面を構成する
感圧接着剤が劣化し、圧着性が低下するという問題があ
る。裏面にも加熱定着方式の記録法方で印字した場合、
加熱定着工程を２度通ることになり、圧着面の劣化はよ
り激しくなる。Generally, a heat-fixing type recording such as a laser printer or an electrophotographic method is used for printing on the pressure-bonding surface of a pressure-bonding postcard, but the pressure-sensitive adhesive constituting the pressure-bonding surface is deteriorated in this heat-fixing step, and the pressure-bonding property is deteriorated. There is a problem that When printing on the back side with the recording method of heat fixing method,
The heat-fixing process is passed twice, and the pressure-bonded surface is more deteriorated.
【０００８】 このため、印字は非加熱定着方式の方
が好ましく、その点からインクジェット記録方式は適し
ている。しかし、一般に用いられる圧着葉書では、イン
クジェット記録用インクが非加熱定着方式であるため、
圧着時に記録の上に重ね合わされる面に記録部の定着不
足のインクが転写してしまい、剥離時、記録が大変読み
とり難くなってしまう。Therefore, the non-heat fixing method is preferable for printing, and the inkjet recording method is suitable in that respect. However, in a commonly used pressure-bonded postcard, since the ink jet recording ink is a non-heat fixing method,
Insufficiently fixed ink in the recording portion is transferred to the surface that is superposed on the recording during pressure bonding, and the recording becomes very difficult to read when peeling.
【０００９】[0009]
【発明が解決しようとする課題】本発明が解決しようと
する課題は、感圧接着性記録シートに印字・圧着・剥離
を行った際、印字した内容が反対面の感圧接着層に転写
するという問題をインクジェット記録された記録の定着
性を向上させることにより発生させない感圧接着性記録
シートを提供することである。The problem to be solved by the present invention is to transfer the printed contents to the pressure-sensitive adhesive layer on the opposite surface when the pressure-sensitive adhesive recording sheet is printed / pressed / peeled. SUMMARY OF THE INVENTION It is an object of the present invention to provide a pressure-sensitive adhesive recording sheet which does not cause such a problem by improving the fixability of ink-jet recorded records.
【００１０】[0010]
【課題を解決するための手段】本発明者らは、上述した
問題点を解決するため鋭意研究の結果、以下の様な感圧
接着性記録シートを見い出した。The present inventors have found the following pressure-sensitive adhesive recording sheet as a result of earnest research for solving the above-mentioned problems.
【００１１】すなわち、通常状態では粘着性、接着性と
もに示さず加圧時に接着性を示す感圧接着層を支持体の
少なくとも片面に有し、加圧時の接着が接着後に剥離可
能である感圧接着性記録シートにおいて、該感圧接着層
がカチオン性コロイド粒子を該感圧接着層内の粘着剤成
分に対し２５〜５００重量％含有することを特徴とする
感圧接着性記録シートの発明である。That is, a pressure-sensitive adhesive layer which does not exhibit tackiness or adhesiveness under normal conditions but exhibits adhesiveness under pressure is provided on at least one surface of the support, and the adhesiveness under pressure can be peeled off after adhesion. In the pressure-sensitive adhesive recording sheet, the pressure-sensitive adhesive layer contains the cationic colloid particles in an amount of 25 to 500% by weight based on the pressure-sensitive adhesive component in the pressure-sensitive adhesive layer. Is.
【００１２】以下、本発明を詳細に説明する。Hereinafter, the present invention will be described in detail.
【００１３】本発明に適用されるカチオン性コロイド粒
子は、水中に懸濁分散してコロイド状をなしているもの
であり、動的光散乱法により測定されるコロイド状態に
おける平均粒子径が３００ｎｍ以下であり、該粒子表面
が正に帯電した粒子を指し、例えば、ベーマイト、擬ベ
ーマイト等のアルミナゾルやコロイダルアルミナ、或い
は特公昭47ー26959号公報に開示されているようにコロイ
ド状シリカ粒子表面をアルミナコーティングした粒子等
が挙げられる。平均粒子径が３００ｎｍを超えると、該
コロイド粒子の表面積が減少するために、インクの定着
性が低下し、感圧接着層の塗工量を増やす必要が生じ
る。The cationic colloidal particles used in the present invention are suspended and dispersed in water to form a colloidal state, and have an average particle size of 300 nm or less in a colloidal state measured by a dynamic light scattering method. The particle surface refers to positively charged particles, for example, alumina sol such as boehmite, pseudo-boehmite or colloidal alumina, or the colloidal silica particle surface is alumina as disclosed in JP-B-47-26959. Examples thereof include coated particles. When the average particle diameter exceeds 300 nm, the surface area of the colloid particles decreases, so that the fixing property of the ink decreases and it becomes necessary to increase the coating amount of the pressure-sensitive adhesive layer.
【００１４】また、粒子表面の電荷がカチオンであるこ
とにより、電気的な相互作用によってインク中の染料成
分を感圧接着層に定着させることが可能となる。さら
に、コロイド粒子自体には溶媒成分を吸収するだけの容
量がないことから、溶媒成分は感圧接着層を透過して、
支持体に浸透することになる。支持体においては、溶媒
成分の面方向への拡散や深さ方向への浸透が生じても染
料成分が含まれていないために色彩性や鮮鋭性に影響が
無く、従って、インクの吸収と定着を同時に機能させる
ために必要な空隙量は不要となる。しかしながら、イン
ク受理層における溶媒成分の浸透が遅くなると、感圧接
着層においてインクが滞留してインクの拡散が生じるこ
とになるから溶媒成分の浸透は速くなければならない。Further, since the charges on the surface of the particles are cations, the dye component in the ink can be fixed on the pressure-sensitive adhesive layer by an electric interaction. Furthermore, since the colloidal particles themselves do not have the capacity to absorb the solvent component, the solvent component permeates the pressure-sensitive adhesive layer,
It will penetrate the support. In the support, even if the solvent component diffuses in the plane direction or penetrates in the depth direction, since the dye component is not contained, the color and sharpness are not affected, and therefore, the absorption and fixing of the ink There is no need for the amount of voids required for the two to function at the same time. However, when the permeation of the solvent component in the ink receiving layer is slow, the ink is retained in the pressure-sensitive adhesive layer to cause the diffusion of the ink. Therefore, the permeation of the solvent component must be fast.
【００１５】本発明におけるカチオン性コロイド粒子の
感圧接着層への含有量は感圧接着層内の粘着剤成分に対
して２５〜５００重量％が好ましい。カチオン性コロイ
ド粒子の含有量が２５重量％より少ないとインクジェッ
ト記録用インクの重ね合わされた反対面への転写の割合
が増加してしまうし、５００重量％より多くともインク
ジェット記録用インクの転写を防ぐ効果に変化が無いば
かりか感圧接着層の接着力を著しく低下させてしまう。The content of the cationic colloid particles in the pressure-sensitive adhesive layer in the present invention is preferably 25 to 500% by weight based on the pressure-sensitive adhesive component in the pressure-sensitive adhesive layer. When the content of the cationic colloid particles is less than 25% by weight, the transfer rate of the ink jet recording ink to the opposite surface on which the ink is superposed increases, and when it is more than 500% by weight, the transfer of the ink jet recording ink is prevented. Not only does the effect remain unchanged, but the adhesive force of the pressure-sensitive adhesive layer is significantly reduced.
【００１６】また、本発明における感圧接着性記録シー
トの感圧接着層には、カチオン性コロイド粒子と共に公
知の顔料を１種類以上用いることができる。カチオン性
コロイド粒子と顔料を併用することにより、インクジェ
ット記録用インクの溶媒成分も感圧接着層中に浸透され
ることになる。顔料としては、例えば、軽質炭酸カルシ
ウム、重質炭酸カルシウム、カオリン、タルク、硫酸カ
ルシウム、硫酸バリウム、二酸化チタン、酸化亜鉛、硫
化亜鉛、炭酸亜鉛、サチンホワイト、珪酸アルミニウ
ム、ケイソウ土、珪酸カルシウム、珪酸マグネシウム、
合成非晶質シリカ、擬ベーマイト、水酸化アルミニウ
ム、アルミナ、リトポン、ゼオライト、加水ハロイサイ
ト、炭酸マグネシウム、水酸化マグネシウムなどの無機
顔料、スチレン系プラスチックピグメント、アクリル系
プラスチックピグメント、ポリエチレン、マイクロカプ
セル、尿素樹脂、メラミン樹脂、小麦澱粉などの有機顔
料などが挙げられる。Further, in the pressure-sensitive adhesive layer of the pressure-sensitive adhesive recording sheet of the present invention, one or more known pigments may be used together with the cationic colloid particles. By using the cationic colloid particles and the pigment in combination, the solvent component of the inkjet recording ink is also permeated into the pressure-sensitive adhesive layer. Examples of the pigment include light calcium carbonate, heavy calcium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth, calcium silicate, and silicic acid. magnesium,
Inorganic pigments such as synthetic amorphous silica, pseudo-boehmite, aluminum hydroxide, alumina, lithopone, zeolite, hydrohaloysite, magnesium carbonate, magnesium hydroxide, styrene plastic pigment, acrylic plastic pigment, polyethylene, microcapsule, urea resin , Organic pigments such as melamine resin and wheat starch.
【００１７】上記の中でも、インクジェット記録用イン
クの吸収性を向上させるために感圧接着層中に含有する
顔料としては、多孔性無機顔料が好ましく、多孔性合成
非晶質シリカ、多孔性炭酸マグネシウム、多孔性アルミ
ナなどが挙げられ、特に細孔容積の大きい多孔性合成非
晶質シリカが好ましい。さらに好ましくは給油度が２０
ｍｌ／１００ｇ以上の顔料である。また、接着性を制御
する目的の顔料としては、シリカ、カオリン、クレー、
炭酸カルシウム、水酸化アルミニウム、酸化チタン、酸
化亜鉛、メラミン樹脂粒子、ベンゾグアナミン樹脂粒
子、澱粉粒子などが挙げられ、特に平均粒子径の大きい
小麦澱粉が接着性制御の効果が大きく好ましい。Among the above, as the pigment contained in the pressure-sensitive adhesive layer for improving the absorptivity of the ink for ink jet recording, a porous inorganic pigment is preferable, and porous synthetic amorphous silica or porous magnesium carbonate is used. , Porous alumina, and the like, and porous synthetic amorphous silica having a large pore volume is particularly preferable. More preferably the refueling degree is 20
It is a pigment of 100 ml / ml or more. Further, as the pigment for controlling the adhesiveness, silica, kaolin, clay,
Examples thereof include calcium carbonate, aluminum hydroxide, titanium oxide, zinc oxide, melamine resin particles, benzoguanamine resin particles, and starch particles. Wheat starch having a large average particle size is particularly preferable because it has a large effect of controlling adhesion.
【００１８】本発明の支持体には原紙、合成樹脂フィル
ムなどを用いることが可能であるが、原紙が経済的にも
特性的にも適して用いられる。A base paper, a synthetic resin film or the like can be used for the support of the present invention, but the base paper is preferably used both economically and characteristically.
【００１９】本発明に用いられる原紙は、木材パルプと
顔料を主成分として構成される。木材パルプとしては、
ＬＢＫＰ、ＮＢＫＰなどの化学パルプ、ＧＰ、ＰＧＷ、
ＲＭＰ、ＴＭＰ、ＣＴＭＰ、ＣＭＰ、ＣＧＰなどの機械
パルプ、ＤＩＰなどの古紙パルプなどのパルプを含み、
必要に応じて従来公知の顔料やバインダーおよびサイズ
剤や定着剤、歩留まり向上剤、カチオン化剤、紙力増強
剤などの各種添加剤を１種以上用いて混合し、長網抄紙
機、円網抄紙機、ツインワイヤ抄紙機などの各種装置で
支持体の製造が可能であり、酸性、中性、アルカリ性で
抄造できる。The base paper used in the present invention is mainly composed of wood pulp and pigment. As wood pulp,
Chemical pulp such as LBKP and NBKP, GP, PGW,
Including mechanical pulp such as RMP, TMP, CTMP, CMP, CGP, pulp such as waste paper pulp such as DIP,
If necessary, various additives such as conventionally known pigments and binders, sizing agents, fixing agents, retention aids, cationizing agents, and paper strength enhancers are mixed and used to prepare a Fourdrinier paper machine and cylinder. The support can be produced by various devices such as a paper machine and a twin wire paper machine, and can be made by acid, neutral and alkaline papermaking.
【００２０】原紙は、金属ロールと合成樹脂ロールから
なるカレンダー装置を用いてオンマシン処理しても良
い。その際、オフマシン処理しても良く、処理後に、さ
らにマシンカレンダー、スーパーカレンダーなどでカレ
ンダー処理を施して平坦性をコントロールしても良い。The base paper may be subjected to on-machine processing by using a calendering device composed of a metal roll and a synthetic resin roll. At that time, off-machine processing may be performed, and after processing, flatness may be controlled by further performing calendar processing using a machine calendar, a super calendar, or the like.
【００２１】本発明でいうインクジェット記録用インク
は、下記の着色剤、液媒体、その他の添加剤からなる記
録液体である。The ink jet recording ink referred to in the present invention is a recording liquid containing the following colorant, liquid medium and other additives.
【００２２】着色剤としては、直接染料、酸性染料、塩
基性染料、反応性染料あるいは食品用色素などの水溶性
染料が挙げられる。Examples of the colorant include water-soluble dyes such as direct dyes, acid dyes, basic dyes, reactive dyes and food dyes.
【００２３】インクの溶媒としては、水および水溶性の
各種有機溶剤、例えば、メチルアルコール、エチルアル
コール、ｎ−プロピルアルコール、イソプロピルアルコ
ール、ｎ−ブチルアルコール、 sec−ブチルアルコー
ル、tert−ブチルアルコール、イソブチルアルコールな
どの炭素数１〜４のアルキルアルコール類；ジメチルホ
ルムアミド、ジメチルアセトアミドなどのアミド類；ア
セトン、ジアセトンアルコールなどのケトンまたはケト
ンアルコール類；テトラヒドロフラン、ジオキサンなど
のエーテル類；ポリエチレングリコール、ポリプロピレ
ングリコールなどのポリアルキレングリコール類；エチ
レングリコール、プロピレングリコール、ブチレングリ
コール、トリエチレングリコール、1,2,6 −ヘキサント
リオール、チオジグリコール、ヘキシレングリコール、
ジエチレングリコールなどのアルキレン基が２〜６個の
アルキレングリコール類；グリセリン、エチレングリコ
ールメチルエーテル、ジエチレングリコールメチル（ま
たはエチル）エーテル、トリエチレングリコールモノメ
チルエーテルなどの多価アルコールの低級アルキルエー
テル類などが挙げられる。As the solvent of the ink, water and various water-soluble organic solvents such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol and isobutyl are used. Alkyl alcohols having 1 to 4 carbon atoms such as alcohols; amides such as dimethylformamide and dimethylacetamide; ketones or ketone alcohols such as acetone and diacetone alcohol; ethers such as tetrahydrofuran and dioxane; polyethylene glycol, polypropylene glycol, etc. Polyalkylene glycols; ethylene glycol, propylene glycol, butylene glycol, triethylene glycol, 1,2,6-hexanetriol, thiodiglycol Le, hexylene glycol,
Alkylene glycols having 2 to 6 alkylene groups such as diethylene glycol; and lower alkyl ethers of polyhydric alcohols such as glycerin, ethylene glycol methyl ether, diethylene glycol methyl (or ethyl) ether, and triethylene glycol monomethyl ether.
【００２４】これらの多くの水溶性有機溶剤の中でも、
ジエチレングリコールなどの多価アルコール、トリエチ
レングリコールモノメチルエーテル、トリエチレングリ
コールモノエチルエーテルなどの多価アルコールの低級
アルキルエーテルが好ましい。その他の添加剤として
は、例えば、ｐＨ調節剤、金属封鎖剤、防カビ剤、粘度
調整剤、表面張力調整剤、湿潤剤、界面活性剤、および
防錆剤などが挙げられる。Among many of these water-soluble organic solvents,
Polyhydric alcohols such as diethylene glycol, and lower alkyl ethers of polyhydric alcohols such as triethylene glycol monomethyl ether and triethylene glycol monoethyl ether are preferred. Other additives include, for example, a pH adjusting agent, a sequestering agent, an antifungal agent, a viscosity adjusting agent, a surface tension adjusting agent, a wetting agent, a surfactant, and a rust preventive agent.
【００２５】本発明に用いられる感圧接着層を構成する
感圧接着剤は、通常状態では粘着性も接着性も示さない
が、強い圧力により接着可能となるものであり、ラベル
や粘着テープに用いている通常粘着性のある感圧接着剤
とは異なるものである。本発明でいう感圧接着剤、感圧
接着層とは、前者の通常状態では粘着性も接着性も示さ
ないが、強い圧力により接着可能となるものに限定す
る。感圧接着層同士を重ね合わせて圧力を加えることで
接着することが可能で、感圧接着層の接着性の制御、あ
るいは加える圧力の加減により、接着後に剥離可能に接
着させることも、接着後に剥離不能なまでに強接着させ
ることも可能である。一般の３つ折り葉書において、印
字内容を確認するために剥離可能に接着する面と、印字
内容を設けず剥離不能に強接着する面は、このような感
圧接着性の違いを利用したものである。The pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer used in the present invention does not exhibit adhesiveness or adhesiveness in a normal state, but it can be adhered by a strong pressure, and can be applied to a label or an adhesive tape. It is different from the normally tacky pressure sensitive adhesives used. The pressure-sensitive adhesive and the pressure-sensitive adhesive layer in the present invention are limited to those which can be adhered by a strong pressure although they do not exhibit tackiness or adhesiveness in the former normal state. The pressure-sensitive adhesive layers can be bonded by overlapping them and applying pressure.By controlling the adhesiveness of the pressure-sensitive adhesive layers or adjusting the applied pressure, it is possible to make them peelable after bonding, or after bonding. It is also possible to make strong adhesion so that it cannot be peeled off. In general tri-fold postcards, the surface that adheres releasably to confirm the print content and the surface that does not provide the print content and that strongly adheres non-separably make use of this difference in pressure-sensitive adhesiveness. is there.
【００２６】本発明の感圧接着層に用いられる感圧接着
剤としては、天然ゴム、変性天然ゴム、スチレン−ブタ
ジエンゴム、アクリロニトリル−ブタジエンゴムなどの
合成ゴム、エチレン−酢酸ビニル共重合体樹脂、アクリ
ル酸エステル樹脂、塩化ビニル系樹脂、塩化ビニリデン
系樹脂などが溶液あるいはエマルジョンの形で用いられ
る。The pressure-sensitive adhesive used in the pressure-sensitive adhesive layer of the present invention includes natural rubber, modified natural rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber and other synthetic rubber, ethylene-vinyl acetate copolymer resin, Acrylic ester resin, vinyl chloride resin, vinylidene chloride resin, etc. are used in the form of solution or emulsion.
【００２７】また、本発明の感圧接着層には、粘着付与
剤としてロジン系樹脂およびその誘導体、テルペン系樹
脂、クマロインデン系樹脂、キシレン系樹脂、アルキル
フェノール系樹脂、石油樹脂などを接着性、耐ブロッキ
ング性、耐熱性を損なわない範囲で併用できる。さら
に、剥離性を制御する目的で離型剤を併用することも可
能で、例えば、各種パラフィン、ワックス、脂肪酸また
はその誘導体、高級アルコール類、金属石鹸類、シリコ
ーン樹脂類などを接着性を損なわない範囲で用いること
ができる。In the pressure-sensitive adhesive layer of the present invention, a rosin-based resin and its derivative, a terpene-based resin, a coumaroindene-based resin, a xylene-based resin, an alkylphenol-based resin, a petroleum resin or the like is used as a tackifier for adhesion and resistance. It can be used in combination as long as the blocking property and heat resistance are not impaired. Further, it is also possible to use a release agent in combination for the purpose of controlling the releasability, for example, does not impair the adhesiveness of various paraffins, waxes, fatty acids or derivatives thereof, higher alcohols, metal soaps, silicone resins and the like. Can be used in a range.
【００２８】本発明の感圧接着層には、さらに、その他
の添加剤として、分散剤、増粘剤、流動性改良剤、消泡
剤、抑泡剤、発泡剤、浸透剤、着色染料、着色顔料、蛍
光増白剤、紫外線吸収剤、酸化防止剤、防腐剤、防バイ
剤、耐水化剤、湿潤紙力増強剤、乾燥紙力増強剤、帯電
防止剤、老化防止剤、などを適宜配合することもでき
る。In the pressure-sensitive adhesive layer of the present invention, further, as other additives, a dispersant, a thickener, a fluidity improver, an antifoaming agent, a foam suppressor, a foaming agent, a penetrating agent, a coloring dye, Coloring pigments, optical brighteners, UV absorbers, antioxidants, preservatives, anti-bacterial agents, water resistance agents, wet paper strength enhancers, dry paper strength enhancers, antistatic agents, anti-aging agents, etc. It can also be blended.
【００２９】本発明の感圧接着性記録シートは、折り目
にあたる部分に切れ込み部分や圧縮線を入れ、折り畳み
やすくすることは何等差し支えない。また、得られた感
圧接着性記録シートは、１枚の記録シートを折り畳んで
一体化することも、２枚の記録シートを重ね合わせて一
体化することも可能である。In the pressure-sensitive adhesive recording sheet of the present invention, there is no problem in forming a cut portion or a compression line at the portion corresponding to the fold so that it can be easily folded. Further, the obtained pressure-sensitive adhesive recording sheet can be formed by folding one recording sheet and integrating it, or by superposing two recording sheets on each other and integrating them.
【００３０】裏面にも感圧接着層（表面の感圧接着層と
区別する場合には、表面の感圧接着剤により得られる接
着性よりも強いということで感圧強接着層と呼ぶ）を設
けた両面感圧接着性記録シートにおいては、同様に１枚
の記録シートを２つに、あるいは３つに折り畳んで一体
化することも、２枚以上の記録シートを重ね合わせて一
体化することも可能である。感圧接着性記録シートを圧
着するには重ね合った感圧接着剤が接着する程度の圧力
で圧着を行うことができる。A pressure-sensitive adhesive layer is also provided on the back surface (in the case of being distinguished from the pressure-sensitive adhesive layer on the front surface, it is called a pressure-sensitive adhesive layer because it is stronger than the adhesiveness obtained by the pressure-sensitive adhesive on the surface). In the case of the double-sided pressure-sensitive adhesive recording sheet, similarly, one recording sheet may be folded into two or three to be integrated, or two or more recording sheets may be overlapped and integrated. It is possible. For pressure-bonding the pressure-sensitive adhesive recording sheet, the pressure-sensitive adhesive recording sheet can be pressure-bonded with pressure enough to bond the pressure-sensitive adhesives.
【００３１】本発明の剥離性の感圧接着性記録シート
は、本発明の感圧接着性記録シートを感圧接着層同士が
重なるように２層に重ね合わせ圧着して得られるもので
ある。両面に感圧接着層を設けた両面感圧接着性記録シ
ートを用いれば３つ折り葉書のように、感圧接着性記録
シートを３重に重ね合わせて一体化することも可能であ
る。The releasable pressure-sensitive adhesive recording sheet of the present invention is obtained by superposing two layers of the pressure-sensitive adhesive recording sheet of the present invention so that the pressure-sensitive adhesive layers overlap each other and press-bonding them. If a double-sided pressure-sensitive adhesive recording sheet provided with pressure-sensitive adhesive layers on both sides is used, the pressure-sensitive adhesive recording sheets can also be triple-layered and integrated like a trifold postcard.
【００３２】感圧接着性記録シートを用いた剥離性葉書
を作製する場合も、２枚の感圧接着性記録シートを重ね
合わせて圧着するか、１枚の再剥離可能な感圧接着性記
録シートを”く”の字状に折り曲げてから圧着させる印
字部分全面を隠ぺいする方法（２つ折りはがき）、ある
いは”Ｌ”字状に折り曲げて印字情報の一部のみを隠ぺ
いする方法、１枚の両面感圧接着性記録シートを”Ｚ”
字状に折り曲げて圧着する方法（３つ折りはがき）など
いずれの方法を用いても差し支えない。Also in the case of producing a peelable postcard using a pressure-sensitive adhesive recording sheet, two pressure-sensitive adhesive recording sheets are superposed and pressure-bonded, or one removable pressure-sensitive adhesive recording sheet is used. Bending the sheet into a "U" shape and then crimping it to conceal the entire print area (two-fold postcard), or to fold it into an "L" shape to conceal only part of the print information. Double sided pressure sensitive adhesive recording sheet "Z"
Any method such as a method of bending in a letter shape and crimping (three-fold postcard) may be used.
【００３３】本発明の感圧接着性記録シートを用いた圧
着体は、内部の印字情報の非公開性が完全であり、感圧
接着剤の剥離可能な接着性を利用して２面の感圧接着性
記録シートを剥離して内部の記録を読む事が出来、且つ
一旦剥離した感圧接着性記録シートは再接着しないた
め、情報の秘守性が高いものである。The pressure-sensitive adhesive body using the pressure-sensitive adhesive recording sheet of the present invention has complete non-disclosure of the printing information inside, and the releasable adhesiveness of the pressure-sensitive adhesive is utilized to obtain two-sided feeling. Since the pressure-sensitive adhesive recording sheet can be peeled off to read the internal record, and the pressure-sensitive adhesive recording sheet once peeled off is not re-bonded, the confidentiality of information is high.
【００３４】感圧接着層の塗工量はその接着方法により
異なるが、良好な接着性およびインクジェット記録性を
確保する目的から、５〜４０ｇ/ｍ2の範囲内であること
が好ましい。接着層の塗工量がこの範囲より小さいと、
接着性が不足するために貼合せが弱い。この範囲より大
きくとも、紙の走行に支障を来すばかりか経済的にコス
トアップの要因となる。The coating amount of the pressure-sensitive adhesive layer varies depending on the bonding method, but it is preferably in the range of 5 to 40 g / m 2 for the purpose of ensuring good adhesiveness and ink jet recording property. If the coating amount of the adhesive layer is smaller than this range,
Bonding is weak due to lack of adhesiveness. If it is larger than this range, it not only hinders the running of the paper but also causes a cost increase economically.
【００３５】本発明の感圧接着層を塗工する方法として
は、例えば、グラビアコーター、グラビアオフセットコ
ーター、バーコーター、ロールコーター、エアナイフコ
ーター、Ｕコンマコーター、ＡＫＫＵコーター、スムー
ジングコーター、マイクログラビアコーター、リバース
ロールコーター、４本あるいは５本ロールコーター、ブ
レードコーター、ディップコーター、落下カーテンコー
ター、スライドコーター、ダイコーター、溶融押しだし
ダイなど如何なる塗工方法を用いてもよい。Examples of the method for applying the pressure-sensitive adhesive layer of the present invention include gravure coater, gravure offset coater, bar coater, roll coater, air knife coater, U comma coater, AKKU coater, smoothing coater, microgravure coater, Any coating method such as a reverse roll coater, a four roll roll coater, a five roll roll coater, a blade coater, a dip coater, a falling curtain coater, a slide coater, a die coater, and a melt extrusion die may be used.
【００３６】[0036]
【作用】本発明の感圧接着性記録シートは、カチオン性
コロイド粒子を該感圧接着層内の粘着剤成分に対し２５
〜５００重量％含有しているため、インクジェット記録
用インクのシートへの定着が良好であり、圧着後に剥離
してもインクジェット記録用インクが反対面に転写する
ことがほとんどない。In the pressure-sensitive adhesive recording sheet of the present invention, the cationic colloid particles are added to the pressure-sensitive adhesive component in the pressure-sensitive adhesive layer at 25%.
Since it is contained in an amount of up to 500% by weight, the ink jet recording ink is well fixed to the sheet, and the ink jet recording ink hardly transfers to the opposite surface even when peeled off after pressure bonding.
【００３７】[0037]
【実施例】以下、実施例により本発明を詳しく説明する
が、本発明の内容は、実施例に限られるものではない。
また、実施例において示す「部」および「％」は、特に
明示しない限り乾燥重量部および乾燥重量％を示す。The present invention will be described in detail below with reference to examples, but the contents of the present invention are not limited to the examples.
In addition, "parts" and "%" shown in the examples mean dry parts by weight and dry% by weight, unless otherwise specified.
【００３８】実施例１アクリル 酸エステル系エマルシ゛ョン（日本合成ゴム社製、AE-923） １００部カチオン 性コロイタ゛ルシリカ（日産化学工業社製、スノーテックスAK-ZL） ３５０部 上記配合（粘着剤成分に対しカチオン性コロイド粒子が
３５０重量％加えられている）により感圧接着剤を調整
後、支持体として坪量９４ｇ/ｍ2の上質紙の片面に乾燥
塗工量１０ｇ/ｍ2でエアナイフコーターにより塗工し、
乾燥して目的とする感圧接着性記録シートを得た。Example 1 Acrylic ester emulsion (AE-923, manufactured by Japan Synthetic Rubber Co., Ltd.) 100 parts Cationic colloidal silica (Snowtex AK-ZL, manufactured by Nissan Chemical Industries, Ltd.) 350 parts The above composition (to the adhesive component) after adjusting the pressure sensitive adhesive by against the cationic colloidal particles are added 350 wt%), by an air knife coater at a basis weight 94 g / dry on one surface of woodfree paper having m 2 coating weight 10 g / m 2 as a support Coated,
After drying, a target pressure-sensitive adhesive recording sheet was obtained.
【００３９】実施例２アクリル 酸エステル系エマルシ゛ョン（日本合成ゴム社製、AE-923） １００部カチオン 性コロイタ゛ルシリカ（日産化学工業社製、スノーテックスAK-ZL） ２５０部 合成非晶質シリカ（徳山曹達社製、ファインシルX37B） ６０部 上記配合（粘着剤成分に対しカチオン性コロイド粒子が
２５０重量％加えられている）により感圧接着剤を調整
後、支持体として坪量９４ｇ/ｍ2の上質紙の片面に乾燥
塗工量１０ｇ/ｍ2でエアナイフコーターにより塗工し、
乾燥して目的とする感圧接着性記録シートを得た。Example 2 Acrylic ester emulsion (AE-923, manufactured by Japan Synthetic Rubber Co., Ltd.) 100 parts Cationic colloidal silica (Snowtex AK-ZL, manufactured by Nissan Chemical Industries, Ltd.) 250 parts Synthetic amorphous silica (Tokuyama) Fine Sil X37B manufactured by Soda Co., Ltd. 60 parts After adjusting the pressure-sensitive adhesive by the above-mentioned composition (250% by weight of cationic colloid particles is added to the pressure-sensitive adhesive component), the support has a basis weight of 94 g / m 2 . Coated on one side of wood free paper with an air knife coater at a dry coating weight of 10 g / m 2 .
After drying, a target pressure-sensitive adhesive recording sheet was obtained.
【００４０】実施例３ 実施例１において、カチオン性コロイド粒子としてのカ
チオン性コロイダルシリカを５００部にした以外は、実
施例１と同様にして目的とする感圧接着性記録シートを
得た。Example 3 A target pressure-sensitive adhesive recording sheet was obtained in the same manner as in Example 1 except that the amount of the cationic colloidal silica as the cationic colloid particles was changed to 500 parts.
【００４１】実施例４アクリル 酸エステル系エマルシ゛ョン（中央理化工業社製、リカホ゛ント゛AP-90） １００部カチオン 性コロイタ゛ルシリカ（日産化学工業社製、スノーテックスAK-ZL） ２５部 小麦澱粉（平均粒径２０μｍ） ７０部 上記配合（粘着剤成分に対しカチオン性コロイド粒子が
２５重量％加えられている）により感圧接着剤を調整
後、支持体として坪量９４ｇ/ｍ2の上質紙の片面に乾燥
塗工量１０ｇ/ｍ2でエアナイフコーターにより塗工し、
乾燥して目的とする感圧接着性記録シートを得た。Example 4 Acrylic ester emulsion (Rikabond AP-90 manufactured by Chuo Rika Kogyo Co., Ltd.) 100 parts Cationic colloidal silica (Snowtex AK-ZL manufactured by Nissan Chemical Co., Ltd.) 25 parts Wheat starch (average particle size) 20 μm) 70 parts After adjusting the pressure-sensitive adhesive by the above composition (25% by weight of cationic colloid particles was added to the pressure-sensitive adhesive component), dried as a support on one side of a high-quality paper of basis weight 94 g / m 2. Coating with an air knife coater at a coating amount of 10 g / m 2 ,
After drying, a target pressure-sensitive adhesive recording sheet was obtained.
【００４２】実施例５ 実施例４において、感圧接着剤の乾燥塗工量を５ｇ/ｍ2
にした以外は実施例４と同様にして目的とする感圧接着
性記録シートを得た。Example 5 In Example 4, the dry coating amount of the pressure sensitive adhesive was 5 g / m 2.
A target pressure-sensitive adhesive recording sheet was obtained in the same manner as in Example 4 except that the above was adopted.
【００４３】実施例６ 実施例４において、感圧接着剤の乾燥塗工量を４０ｇ/
ｍ2にした以外は実施例４と同様にして目的とする感圧
接着性記録シートを得た。Example 6 In Example 4, the dry coating amount of the pressure sensitive adhesive was 40 g /
A target pressure-sensitive adhesive recording sheet was obtained in the same manner as in Example 4 except that m 2 was used.
【００４４】実施例７アクリル 酸エステル系エマルシ゛ョン（中央理化工業社製、リカホ゛ント゛AP-37） １００部カチオン 性コロイタ゛ルシリカ（日産化学工業社製、スノーテックスAK-ZL） ５０部 合成非晶質シリカ（徳山曹達社製、ファインシルX37B） ３０部 でんぷん粒子 ２０部 上記配合（粘着剤成分に対しカチオン性コロイド粒子が
５０重量％加えられている）により感圧接着剤を調整
後、実施例１と同様にして目的とする感圧接着性記録シ
ートを得た。Example 7 Acrylic ester type emulsion (Rikabond AP-37 manufactured by Chuo Rika Kogyo Co., Ltd.) 100 parts Cationic colloidal silica (Snowtex AK-ZL manufactured by Nissan Chemical Co., Ltd.) 50 parts Synthetic amorphous silica ( Tokuyama Soda Co., Ltd., Finesil X37B) 30 parts Starch particles 20 parts After adjusting the pressure-sensitive adhesive by the above composition (cationic colloid particles are added at 50% by weight to the pressure-sensitive adhesive component), the same as in Example 1 Thus, a target pressure-sensitive adhesive recording sheet was obtained.
【００４５】実施例８ 実施例１で得た感圧接着性記録シートの非塗工面に実施
例１で得た感圧接着剤を乾燥塗工量１５ｇ/ｍ2でエアナ
イフコーターにより塗工し、乾燥して目的とする両面と
も感圧接着性を有する感圧接着性記録シートを得た。な
お、乾燥塗工量１５ｇ/ｍ2の面が感圧強接着面である。Example 8 The pressure-sensitive adhesive obtained in Example 1 was coated on the non-coated surface of the pressure-sensitive adhesive recording sheet obtained in Example 1 with an air knife coater at a dry coating amount of 15 g / m 2 . After drying, a target pressure-sensitive adhesive recording sheet having pressure-sensitive adhesive properties on both sides was obtained. The surface having a dry coating amount of 15 g / m 2 is a pressure-sensitive and strongly adhesive surface.
【００４６】比較例１ カチオン性コロイド粒子としてのカチオン性コロイダル
シリカを５５０部にした以外は、実施例１と同様にして
目的とする感圧接着性記録シートを得た。Comparative Example 1 A target pressure-sensitive adhesive recording sheet was obtained in the same manner as in Example 1 except that 550 parts of the cationic colloidal silica as the cationic colloid particles was used.
【００４７】比較例２ カチオン性コロイド粒子としてのカチオン性コロイダル
シリカを２０部にした以外は、実施例４と同様にして目
的とする感圧接着性記録シートを得た。Comparative Example 2 A target pressure-sensitive adhesive recording sheet was obtained in the same manner as in Example 4 except that 20 parts of the cationic colloidal silica as the cationic colloid particles was used.
【００４８】比較例３ カチオン性コロイダルシリカを非カチオン性コロイダル
シリカ（日産化学工業社製、スノーテックスYL）に変更した以外
は実施例１と同様にして目的とする感圧接着性記録シー
トを得た。Comparative Example 3 A target pressure-sensitive adhesive recording sheet was obtained in the same manner as in Example 1 except that the cationic colloidal silica was changed to a non-cationic colloidal silica (Snowtex YL manufactured by Nissan Chemical Industries, Ltd.). It was
【００４９】比較例４ カチオン性コロイダルシリカを合成非晶質シリカ（徳山
曹達社製、ファインシルX37B）に変更した以外は実施例１と同
様にして目的とする感圧接着性記録シートを得た。Comparative Example 4 A target pressure-sensitive adhesive recording sheet was obtained in the same manner as in Example 1 except that synthetic amorphous silica (Finesil X37B manufactured by Tokuyama Soda Co., Ltd.) was used instead of the cationic colloidal silica. .
【００５０】上記により作製した実施例１〜８および比
較例１〜４の感圧接着性記録シートについて、次に記載
した評価方法によって評価し、その結果を表１に示し
た。The pressure-sensitive adhesive recording sheets of Examples 1 to 8 and Comparative Examples 1 to 4 produced as described above were evaluated by the evaluation method described below, and the results are shown in Table 1.
【００５１】〈転写性〉カラーインクジェットプリンタ
ー（商品名：ＭＪ−７００Ｖ２Ｃ、エプソン社製）で印
字を行い、ブラックインクで■を複数個印字した後、サ
ンプルをＺ字状に折り畳み、葉書大（１０ｃｍ×１５ｃ
ｍ）にした後、クリアランス可変の圧着ローラー（日本
エー・ディ・エム社製、ＳＰ４０１）を通過させて圧着
一体化させる。その後、貼合せ部を静かに剥がし、■の
反対面への転写の具合を目視で判定した。なお、評価基
準として、Ａは特性が良好、Ｂは実用上問題ない範囲で
良好、Ｃは実用上問題あり、Ｄは特性が不良を示す。実
施例２の両面感圧接着性記録シートでは感圧強接着面で
はなく感圧接着面について評価した。<Transferability> Printing was performed with a color ink jet printer (trade name: MJ-700V2C, manufactured by Epson Corporation), a plurality of black dots (1) were printed, and the sample was folded into a Z shape to give a postcard size (10 cm). × 15c
m), and then passed through a pressure-variable pressure-bonding roller (SP401, manufactured by Japan ADM Co., Ltd.) to perform pressure-bonding integration. After that, the bonded portion was gently peeled off, and the degree of transfer to the opposite surface of (3) was visually judged. As evaluation criteria, A shows good characteristics, B shows good results in practically acceptable range, C shows practical problems, and D shows poor characteristics. In the double-sided pressure-sensitive adhesive recording sheet of Example 2, the pressure-sensitive adhesive surface was evaluated, not the pressure-sensitive strong adhesive surface.
【００５２】〈インク受理性〉カラーインクジェットプ
リンター（商品名：ＭＪ−７００Ｖ２Ｃ、エプソン社
製）にてインクジェット記録を行ない、印字の鮮明さを
目視で判断した。鮮明な画像、印字が得られるものを
Ａ、やや鮮明さに欠けるが画像や印字の解読に支障のな
いものをＢ、画像がぼやけて不鮮明なものをＣで判定し
た。<Ink Receptivity> Ink jet recording was performed with a color ink jet printer (trade name: MJ-700V2C, manufactured by Epson Corporation), and the sharpness of the print was visually judged. A clear image and a print that can be obtained were judged as A, B which was slightly lacking in clarity but which did not hinder the decoding of the image and print, and C where an image was blurred and unclear.
【００５３】〈接着力〉作製直後の感圧接着性記録シー
トをＺ字状に折り畳み、葉書大（１０ｃｍ×１５ｃｍ）
にした後、クリアランス可変の圧着ローラー（日本エー
・ディ・エム社製、ＳＰ４０１）を通過させて圧着一体
化させる。圧着後、２５ｍｍの幅で短冊状に切り取り、
テンシロン万能引っ張り試験機で１８０゜剥離強度を測
定した。接着力は５０ｇｆ／２５ｍｍ未満では不十分で
ある。<Adhesive strength> A pressure-sensitive adhesive recording sheet immediately after preparation was folded into a Z shape, and a postcard size (10 cm × 15 cm)
After that, the pressure-sensitive adhesive roller (manufactured by Japan ADM Co., Ltd., SP401) having a variable clearance is passed through to perform pressure-bonding integration. After crimping, cut into strips with a width of 25 mm,
The 180 ° peel strength was measured with a Tensilon universal tensile tester. Adhesive strength below 50 gf / 25 mm is insufficient.
【００５４】[0054]
【表１】 [Table 1]
【００５５】表１の結果から明らかなように、カチオン
性コロイド粒子を含有することにより、感圧接着層への
インクジェット記録用インクの定着性が向上し、圧着・
剥離後のインクの重ね合わされた反対面への転写は著し
く減少する。しかし、カチオン性コロイド粒子も感圧接
着層への含有量が粘着剤成分に対し２５重量％より少な
くなると、インク転写の抑制効果が低下することが比較
例２より判る。また、５００重量％よりカチオン性コロ
イド粒子が多くなると著しく接着力を低下させることが
比較例１の結果より分かる。As is clear from the results shown in Table 1, by containing the cationic colloid particles, the fixing property of the ink for ink jet recording on the pressure-sensitive adhesive layer was improved and the pressure-sensitive adhesive layer was fixed.
The transfer of ink to the opposite superposed surface after stripping is significantly reduced. However, Comparative Example 2 shows that when the content of the cationic colloid particles in the pressure-sensitive adhesive layer is less than 25% by weight based on the pressure-sensitive adhesive component, the effect of suppressing ink transfer is reduced. Further, it can be seen from the results of Comparative Example 1 that the adhesive force is remarkably reduced when the amount of the cationic colloid particles is more than 500% by weight.
【００５６】[0056]
【発明の効果】本発明の感圧接着性記録シートは、イン
クジェット記録においてのインクジェット記録用インク
の定着性が良好なため、インクジェット記録を行った後
に圧着・剥離を行ってもインクが重ね合わされた反対面
へ転写することなく、内容を容易に判読することができ
る。Since the pressure-sensitive adhesive recording sheet of the present invention has good fixability of the ink for ink jet recording in ink jet recording, the ink is superposed even if pressure bonding / peeling is performed after ink jet recording. The contents can be easily read without being transferred to the opposite side.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ４１Ｍ 5/124 Ｂ４２Ｄ 15/02 ５０１Ｂ Ｂ４２Ｄ 15/02 ５０１ Ｂ４１Ｍ 5/16 １０１ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location B41M 5/124 B42D 15/02 501B B42D 15/02 501 B41M 5/16 101
Claims (1)
ず加圧時に接着性を示す感圧接着層を支持体の少なくと
も片面に有し、加圧時の接着が接着後に剥離可能である
感圧接着性記録シートにおいて、該感圧接着層がカチオ
ン性コロイド粒子を該感圧接着層内の粘着剤成分に対し
２５〜５００重量％含有することを特徴とする感圧接着
性記録シート。1. A feeling that a pressure-sensitive adhesive layer that does not exhibit tackiness or adhesiveness in a normal state but exhibits adhesiveness under pressure is provided on at least one surface of the support, and the adhesion under pressure is peelable after adhesion. In the pressure-sensitive adhesive recording sheet, the pressure-sensitive adhesive layer contains the cationic colloid particles in an amount of 25 to 500% by weight based on the pressure-sensitive adhesive component in the pressure-sensitive adhesive layer.