JPH09286707A - Powdery cosmetic for body - Google Patents
Powdery cosmetic for bodyInfo
- Publication number
- JPH09286707A JPH09286707A JP12258896A JP12258896A JPH09286707A JP H09286707 A JPH09286707 A JP H09286707A JP 12258896 A JP12258896 A JP 12258896A JP 12258896 A JP12258896 A JP 12258896A JP H09286707 A JPH09286707 A JP H09286707A
- Authority
- JP
- Japan
- Prior art keywords
- powder
- cosmetic
- powdery
- present
- amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明はボディーパウダー、ファ
ンシーパウダー等の、ボディー用粉末化粧料に関し、透
明感があり、さらさらした、なめらかな感触でかつ耐衝
撃性が良好なボディー用粉末化粧料に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to body powder cosmetics such as body powders and fancy powders, and to a body powder cosmetic having a transparent feeling, a dry, smooth feel, and good impact resistance. .
【0002】[0002]
【従来の技術】従来より、透明感があり、さらさらした
感触のボディー化粧料を得るためには、シリカ、ナイロ
ン、ポリエチレン、PMMA等の球状の粉末を配合した
り、低粘度のシリコーンオイルを配合することを行って
いた。2. Description of the Related Art Conventionally, in order to obtain a body cosmetic having a transparent feeling and a dry feel, a spherical powder such as silica, nylon, polyethylene, PMMA, or a low-viscosity silicone oil has been added. I was doing what I was doing.
【0003】[0003]
【発明が解決しようとする課題】しかしながら、これら
を配合したボディー化粧料は耐衝撃性が悪く、中味が崩
れやすいという欠点があり、また使用時におけるさらさ
ら感、なめらかさにおいて劣っているという欠点を有し
ていた。本発明は、前記従来技術の課題に鑑みなされた
ものであり、その目的は、皮膚に塗布した際、透明感、
さらさら感、なめらかな感触にすぐれ、耐衝撃性が良好
なボディー用粉末化粧料を提供することにある。However, the body cosmetics containing them have the drawbacks of poor impact resistance and easy collapse of their contents, and also have the drawback of being inferior in dryness and smoothness during use. Had. The present invention has been made in view of the above-mentioned problems of the prior art, and its object is to provide a transparent feeling when applied to the skin,
An object of the present invention is to provide a powdery cosmetic for a body which has a smooth feel and a smooth feel and has good impact resistance.
【0004】[0004]
【課題を解決するための手段】前記目的を達成するため
に本発明者らは鋭意研究を重ね、特に粉体素材と油分に
注目して検討した結果、特定の粒径の粉末と、比較的粘
度の高いシリコーンオイルを配合した場合に透明感があ
り、さらさら感となめらかさに優れ、耐衝撃性が良好な
ボディー化粧料が得られることを見出し、本発明を完成
するに至った。[Means for Solving the Problems] In order to achieve the above-mentioned object, the inventors of the present invention have conducted extensive studies, and as a result of paying particular attention to the powder material and oil content, the results show that The present inventors have found that a body cosmetic having a transparent feeling when blended with a highly viscous silicone oil, having an excellent silky feel and smoothness, and having good impact resistance can be obtained, and completed the present invention.
【0005】すなわち、本発明のボディー用粉末化粧料
は、粉末成分を70〜99重量%配合する化粧料におい
て、平均粒径が4μm以上の粉末を粉末成分の70%以
上配合し、かつ粘度が500cs以上のジメチルポリシ
ロキサンを化粧料全量に対して1〜10重量%配合する
ことを特徴とするボディー用粉末化粧料である。That is, the powdery cosmetic for a body of the present invention is a cosmetic in which 70 to 99% by weight of the powder component is blended, and powder having an average particle size of 4 μm or more is blended in 70% or more of the powder component and the viscosity is. A powdery cosmetic for a body, which comprises 1 to 10% by weight of dimethylpolysiloxane of 500 cs or more based on the total amount of the cosmetic.
【0006】以下、本発明の構成について詳述する。本
発明に係る粉末の平均粒径は、沈降法で測定した積算重
量に基づいた50%径である。具体的には島津−マイク
ロメリティックス社性のセディグラフ5000−01型
で測定したものである。平均粒径が大きいほど透明性が
あり、図縁がよく、さらさら感が向上する。粒径として
は、4μm以上が好ましい。4μmを下回ると、隠蔽性
が高くなり、白っぽくなるため透明感が悪くなり好まし
くない。粒子径は大きい方がさらさら感に優れるが、4
0μmを越えるとざらつきがでるので好ましくない。The structure of the present invention will be described in detail below. The average particle diameter of the powder according to the present invention is 50% diameter based on the integrated weight measured by the sedimentation method. Specifically, it was measured with a sedigraph 5000-01 type manufactured by Shimadzu-Micromeritics. The larger the average particle size is, the more transparent it is, the better the border is, and the smoother the feeling is improved. The particle size is preferably 4 μm or more. When it is less than 4 μm, the hiding property becomes high and the color becomes whitish, resulting in poor transparency, which is not preferable. The larger the particle size, the better the dryness, but
If it exceeds 0 μm, it is not preferable because it is rough.
【0007】本発明で用いられる平均粒径が4μm以上
の粉末は、化粧品用に用いられる粉末はいずれも使用で
き、マイカ、タルク等の粘土鉱物、炭酸カルシウム、硫
酸バリウム等の無機塩、ナイロン、ポリエチレン、PM
MA等の高分子粉末などがあげられるが、中でも特に合
成マイカはさらさら感、なめらかさ、透明感の点で優れ
るため、特に好ましい。合成マイカには溶融法で合成し
たフッ素金雲母、カリ4ケイ素雲母等があげられる。そ
のほかにも固相反応法、水熱合成法等の方法でも作るこ
とができる。これらの化合物は鉱塊であったり、凝集物
であるために粉砕が必要である。粉砕に当たって、ハン
マーミルのような衝撃粉砕を用いる方法、水を加えてス
ラリー状態にして撹拌により摩砕する方法等があげられ
るがいずれでもかまわない。また合成マイカを使うメリ
ットとしては原料に高純度なものを使用すれば、純白な
粉末となり肌に透明感を与えることができる。これらの
本発明のボディー用粉末化粧料に用いる粉末は必要に応
じて、溌水、溌油、親水処理等を行ってから用いても良
い。The powder having an average particle size of 4 μm or more used in the present invention may be any powder used for cosmetics, such as clay minerals such as mica and talc, inorganic salts such as calcium carbonate and barium sulfate, nylon, Polyethylene, PM
Examples thereof include polymer powders such as MA. Among them, synthetic mica is particularly preferable because it is excellent in smoothness, smoothness and transparency. Examples of synthetic mica include fluorine phlogopite mica and potassium 4-silicon mica synthesized by the melting method. Besides, it can be prepared by a solid-phase reaction method, a hydrothermal synthesis method, or the like. These compounds are lumps or agglomerates and therefore require grinding. For the pulverization, a method of using impact pulverization such as a hammer mill, a method of adding water to prepare a slurry state and agitating by stirring, and the like can be used, but any method may be used. In addition, as a merit of using synthetic mica, if a high-purity material is used as a raw material, it becomes a pure white powder and can give a transparent feeling to the skin. These powders for use in the powdery cosmetics for a body of the present invention may be subjected to water repellent, oil repellent, hydrophilic treatment, etc. before use.
【0008】本発明における粉末成分の配合量は、70
重量%〜99重量%である。平均粒径4μm以上の粉末
の配合量は、粉末成分中の70%以上が好ましい。70
重量%を下回ると製品の外観、皮膚に塗布した際に白っ
ぽくなり、透明感が得られないので好ましくない。In the present invention, the blending amount of the powder component is 70
% By weight to 99% by weight. The compounding amount of the powder having an average particle size of 4 μm or more is preferably 70% or more in the powder component. 70
When the content is less than 10% by weight, the appearance of the product becomes whitish when applied to the skin and a transparent feeling cannot be obtained, which is not preferable.
【0009】本発明で用いられるジメチルポリシロキサ
ンは、その粘度が500cs以上である。500cs以
下では耐衝撃性が十分でなく、またなめらかな感触もで
ない。500cs以上の粘度のジメチルポリシロキサン
は1種を単独で使用しても良く、またいくつかのジメチ
ルポリシロキサンの混合物でも良い。500cs以上の
粘度のジメチルポリシロキサンはボディー用粉末化粧料
において、全油分中の60%以上配合することが使用感
の点で好ましい。60%以下ではなめらかな感触が出に
くく、好ましくない。The dimethylpolysiloxane used in the present invention has a viscosity of 500 cs or more. If it is 500 cs or less, the impact resistance is not sufficient, and there is no smooth feel. The dimethylpolysiloxane having a viscosity of 500 cs or more may be used alone, or may be a mixture of several dimethylpolysiloxanes. Dimethylpolysiloxane having a viscosity of 500 cs or more is preferably blended in the body powder cosmetics in an amount of 60% or more based on the total oil content in terms of usability. If it is 60% or less, it is difficult to obtain a smooth feel, which is not preferable.
【0010】本発明の化粧料には、上記の必須成分の他
に本発明の効果を損なわない範囲で、通常化粧料、医薬
部外品等に用いられる成分を配合することができる。例
えば、水、油分、保湿剤、界面活性剤、分散剤、防腐
剤、香料、薬剤、増粘剤等の従来公知の任意の成分を配
合することができる。In addition to the above-mentioned essential components, the cosmetics of the present invention may contain components usually used in cosmetics, quasi-drugs and the like, as long as the effects of the present invention are not impaired. For example, water, oil, a moisturizer, a surfactant, a dispersant, a preservative, a fragrance, a drug, a thickener, and the like can be added to any conventionally known component.
【0011】[0011]
【実施例】次に実施例をあげて本発明をより詳細に説明
する。本発明がこれにより限定されるものではない。配
合量はすべて重量%である。Next, the present invention will be described in more detail with reference to examples. The present invention is not limited to this. All amounts are by weight.
【0012】実施例に先立ち評価方法について説明す
る。本発明の化粧料の性能は、専門パネル20名による
5段階官能評価を行い、20名の平均値に基づき評価し
た。The evaluation method will be described prior to the examples. The performance of the cosmetics of the present invention was evaluated on the basis of the average value of 20 persons by performing a 5-level sensory evaluation by 20 persons of a specialized panel.
【0013】透明感、さらさら感、なめらかな感触 1.ない 2.あまりない 3.普通 4.ある 5.非常にある 20名の点数の平均値を以下のように点数化した。 ◎ 4.5以上5.0まで ○ 3.5以上4.5未満 □ 2.5以上3.5未満 △ 1.5以上2.5未満 × 1.0以上1.5未満 Transparency, dryness, and smooth feel 1. Not 2. Not so much 3. Normal 4. Yes 5. The average value of the scores of 20 people who were very high was scored as follows. ◎ 4.5 to 5.0 up ○ 3.5 to less than 4.5 □ 2.5 to less than 3.5 △ 1.5 to less than 2.5 × 1.0 to less than 1.5
【0014】耐衝撃性 中皿にプレス成型したものを容器にいれ、鉄板上に10
個落としたときの破損した個数を測定した。結果は以下
に示す記号で示した。 ◎ 破損個数0〜1個 ○ 破損個数2〜3個 □ 破損個数4〜5個 △ 破損個数6〜7個 × 破損個数8〜10個 Impact-resistant middle plate press-molded into a container and placed on an iron plate for 10 minutes.
The number of pieces damaged when dropped was measured. The results are shown by the symbols shown below. ◎ Number of breakage 0 to 1 ○ Number of breakage 2 to 3 □ Number of breakage 4 to 5 △ Number of breakage 6 to 7 × Number of breakage 8 to 10
【0015】以下に本発明にかかる具体的なボディー化
粧料について説明する。 実施例1〜3、比較例1〜4 ボディーパウダーSpecific body cosmetics according to the present invention will be described below. Examples 1-3, Comparative Examples 1-4 Body powder
【0016】[0016]
【表1】 ──────────────────────────────────── 実施例 比較例 ──────────────────── 1 2 3 1 2 3 4 5 ──────────────────────────────────── (1)タルク(10μm) 80 − 80 30 80 80 80 − (2)合成フッ素金雲母(5μm) − 80 − − − − − − (2’)合成フッ素金雲母(2μm) − − − − − − − 80 (3)タルク(2μm) 10 10 10 60 10 10 10 − (4)流動パラフィン − − 3 − − − 5 − (5)ジメチルポリシロキサン (900cs) 8 8 5 8 − 15 3 3 (6)ジメチルポリシロキサン (100cs) − − − − 8 − − − (7)顔料 適量適量適量 適量適量適量適量適量 (8)香料 適量適量適量 適量適量適量適量適量 (製法)(1)〜(3)、(7)をヘンシェルミキサー
で混合し、これに(4)〜(6)、(8)を混合したも
のを添加、混合、粉砕しこれを中皿に成型しボディーパ
ウダーを得た。[Table 1] ──────────────────────────────────── Examples Comparative examples ────── ────────────── 1 2 3 1 2 3 4 5 ──────────────────────────── ──────── (1) Talc (10 μm) 80-80 30 80 80 80- (2) Synthetic Fluoro phlogopite (5 μm) -80 − − − − − − (2 ′) Synthetic fluorophlogopite ( 2 μm) − − − − − − − 80 (3) Talc (2 μm) 10 10 10 60 10 10 10 − (4) Liquid paraffin − − 3 − − − − 5 − (5) Dimethyl polysiloxane (900 cs) 8 85 8-15 3 3 (6) Dimethyl polysiloxane (100cs) − − − − − 8 − − − (7) Pigment Suitable amount Suitable amount Suitable amount Suitable amount Suitable amount Suitable amount Suitable amount (8) Perfume Suitable amount Suitable amount Suitable amount Suitable amount Suitable amount Suitable amount (Production ) (1) to (3) and (7) are mixed with a Henschel mixer, and the mixture of (4) to (6) and (8) is added, mixed and crushed to form an intermediate plate. I got body powder.
【0017】[0017]
【表2】 ─────────────────────────────────── 実施例 比較例 ──────────────────── 1 2 3 1 2 3 4 5 ──────────────────────────────────── 透明感 ◎ ◎ ○ △ ◎ △ □ △ さらさら感 ◎ ◎ ○ △ ○ △ □ □ なめらかな感触 ○ ◎ ○ □ △ ○ □ □ 耐衝撃性 ◎ ◎ ○ ◎ × ○ ○ ○ ──────────────────────────────────── 上表に示すように本発明のボディーパウダーは優れてい
ることがわかる。[Table 2] ─────────────────────────────────── Examples Comparative examples ─────── ───────────── 1 2 3 1 2 3 4 5 ────────────────────────────── ─────── Transparency ◎ ◎ ○ △ ◎ △ □ △ Smoothness ◎ ◎ ○ △ ○ △ □ □ Smooth feeling ○ ◎ ○ □ △ ○ □ □ □ Impact resistance ◎ ◎ ○ ◎ × ○ ○ ○ ─ ─────────────────────────────────── As shown in the table above, the body powder of the present invention is excellent. I understand.
【0018】実施例4〜5 ベビーパウダーExamples 4-5 Baby powder
【0019】[0019]
【表3】 ────────────────────────────────── 実施例 実施例 4 5 ────────────────────────────────── (1)タルク(10μm) 80 0 (2)合成フッ素金雲母(5μm) 9 90 (3)亜鉛華 3 3 (4)ジメチルポリシロキサン (1000cs)* 8 7 ────────────────────────────────── * ジメチルポリシロキサン5000cs:6cs=7:3の混合物 (製法)(1)〜(3)をヘンシェルミキサーで混合
し、これに(4)添加、混合、粉砕しこれを中皿に成型
しベビーパウダーを得た。[Table 3] ────────────────────────────────── Example Example 45 5 ─────── ──────────────────────────── (1) Talc (10 μm) 80 0 (2) Synthetic fluorine phlogopite (5 μm) 9 90 ( 3) Zinc white 3 3 (4) Dimethyl polysiloxane (1000cs) * 8 7 ───────────────────────────────── ── * Mixture of dimethylpolysiloxane 5000cs: 6cs = 7: 3 (Production method) (1) to (3) are mixed with a Henschel mixer, and (4) is added, mixed and crushed into a medium dish. Got baby powder.
【0020】実施例4、5のベビーパウダーは透明感が
あり、さらさらした感触となめらかな感触をもってい
た。また、耐衝撃性にも優れていた。The baby powders of Examples 4 and 5 had a transparent feeling, and had a dry feel and a smooth feel. It was also excellent in impact resistance.
【0021】実施例6 芳香パウダー (1)合成フッ素金雲母(5μm) 96 (2)顔料 1 (3)ジメチルポリシロキサン(1000cs) 2 (4)香料 1 (製法)(1)、(2)をヘンシェルミキサーで混合
し、これに(3)、(4)を添加、混合、粉砕しこれを
容器に充填し芳香パウダー中皿に成型しを得た。Example 6 Aroma Powder (1) Synthetic Fluor phlogopite (5 μm) 96 (2) Pigment 1 (3) Dimethyl polysiloxane (1000 cs) 2 (4) Perfume 1 (Production method) (1), (2) The mixture was mixed with a Henschel mixer, and (3) and (4) were added thereto, mixed and crushed, and the mixture was filled in a container and molded into an aroma powder medium dish to obtain.
【0022】実施例6の芳香パウダーは透明感があり、
さらさらした感触となめらかな感触をもっていた。The aroma powder of Example 6 has a transparent feeling,
It had a silky feel and a smooth feel.
【0023】[0023]
【発明の効果】本発明のボディー用粉末化粧料は、皮膚
上に塗布した際、透明感があり、さらさらした感触とな
めらかな感触を持ち、また、耐衝撃性にも優れるもので
ある。EFFECTS OF THE INVENTION The powdery cosmetic composition for a body of the present invention has a transparent feeling when applied on the skin, has a dry feel and a smooth feel, and is also excellent in impact resistance.
Claims (4)
料において、平均粒径が4μm以上の粉末を粉末成分中
の70%以上配合することを特徴とするボディー用粉末
化粧料。1. A cosmetic composition containing 70 to 99% by weight of a powder component, wherein 70% or more of powder particles having an average particle diameter of 4 μm or more is contained in the powder component.
リシロキサンを化粧料全量に対して1〜10重量%配合
することを特徴とする請求項1記載のボディー用粉末化
粧料。2. The powder cosmetic for body according to claim 1, further comprising dimethylpolysiloxane having a viscosity of 500 cs or more in an amount of 1 to 10% by weight based on the total amount of the cosmetic.
油分中の60%以上である請求項1、2記載のボディー
用粉末化粧料。3. The powdery cosmetic for a body according to claim 1, wherein the content of the dimethylpolysiloxane is 60% or more of the total oil content.
母である請求項1〜3記載のボディー用粉末化粧料。4. The powder cosmetics for body according to claim 1, wherein the powder having an average particle size of 4 μm or more is synthetic mica.