JPH0880977A - Easily openable retort pouch - Google Patents
Easily openable retort pouchInfo
- Publication number
- JPH0880977A JPH0880977A JP6243459A JP24345994A JPH0880977A JP H0880977 A JPH0880977 A JP H0880977A JP 6243459 A JP6243459 A JP 6243459A JP 24345994 A JP24345994 A JP 24345994A JP H0880977 A JPH0880977 A JP H0880977A
- Authority
- JP
- Japan
- Prior art keywords
- retort
- film
- pouch
- laminated
- biaxially stretched
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、直線的引き裂き性のよ
いレトルト適性のある積層包材に関するもので、その積
層包材の使用により、手で容易に開封できるレトルト用
パウチ又はスタンディングパウチを提供しようとするも
のである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a retort-appropriate laminated packaging material having good linear tearability, and provides a retort pouch or a standing pouch that can be easily opened by hand by using the laminated packaging material. Is what you are trying to do.
【０００２】[0002]
【従来の技術】従来より、レトルト用包装体として、主
に下記の構成の積層包材が使用されている。即ち、表面
層には、二軸延伸ポリエチレンテレフタレート（以下Ｐ
ＥＴとする）や二軸延伸ポリプロピレン（以下ＯＰＰと
する）、ガスバリヤー層には、アルミニウム箔（以下Ａ
ｌ箔とする）、内面のヒートシール層には、未延伸ポリ
プロピレン（以下ＣＰＰとする）や直鎖状低密度ポリエ
チレン（以下ＬＬＤＰＥとする）、そして中間層に耐衝
撃性や自立性（起立性）を良くするために、二軸延伸ナ
イロン（以下ＯＮとする）が使用されている。従って、
積層材の層構成としては以下のものが知られている。 ・ＰＥＴ（又はＯＰＰ）／ＯＮ／ＣＰＰ（又はＬＬＤＰ
Ｅ） ・ＰＥＴ（又はＯＰＰ）／ＯＮ／Ａｌ箔／ＣＰＰ（又は
ＬＬＤＰＥ）2. Description of the Related Art Conventionally, a laminated packaging material having the following structure has been mainly used as a retort packaging body. That is, a biaxially stretched polyethylene terephthalate (hereinafter referred to as P
ET), biaxially oriented polypropylene (hereinafter referred to as OPP), the gas barrier layer, aluminum foil (hereinafter referred to as A
l foil), the heat seal layer on the inner surface is unstretched polypropylene (hereinafter referred to as CPP) or linear low-density polyethylene (hereinafter referred to as LLDPE), and the intermediate layer is impact resistant and self-supporting (standing property). ), Biaxially stretched nylon (hereinafter referred to as ON) is used. Therefore,
The following are known as the layer structure of the laminated material.・ PET (or OPP) / ON / CPP (or LLDP)
E) ・ PET (or OPP) / ON / Al foil / CPP (or LLDPE)
【０００３】しかし、上記積層材を使用してレトルト用
包装体を作製した場合、内容物を取り出す際に、手で直
線的に引き裂き、内容物をこぼさずに開封することは非
常に困難であった。即ち、従来のＯＮで作製したレトル
トパウチは、開封の際に、直線的に引き裂かれず、表側
と裏側の積層材が所定の位置よりずれて、股裂き状態で
引き裂かれるので、内容物がこぼれ易いという問題があ
った。また、レトルトパウチの場合、レトルト時の破袋
防止や流通時の破袋防止のため、ＣＰＰの厚さを５０μ
ｍ以上とし、包装材全体の厚さを８０μｍ以上とするの
で、手での開封は困難であった。However, in the case where a retort package is manufactured using the above-mentioned laminated material, it is very difficult to tear the contents linearly by hand to take out the contents without spilling. It was That is, the conventional retort pouch made by ON is not linearly torn at the time of opening, and the laminated materials on the front side and the back side are displaced from a predetermined position and are torn in a crotch tear state, so that the contents are easily spilled. There was a problem. In the case of a retort pouch, the thickness of CPP should be 50μ in order to prevent bag breakage during retort and during distribution.
Since the total thickness of the packaging material is 80 μm or more, it is difficult to open the packaging material by hand.
【０００４】[0004]
【発明が解決しようとする課題】従来のレトルトパウチ
は手での開封が困難なため、開封時には鋏やナイフを使
用するか、又は、手で直線的に引き裂きができるように
するため、直線的引き裂き性に優れた延伸高密度ポリエ
チレン層を更に積層することが行われている。この場合
はコスト高になるという問題があった。また、ＰＥＴと
ＯＮ層に傷を付けることにより、直線的引き裂き性を良
くする手段を講じている場合もあるが、強度が低下し
て、レトルトパウチとしては十分な強度が得られないと
いう問題があった。Since the conventional retort pouch is difficult to open by hand, it is necessary to use scissors or a knife at the time of opening, or to make it possible to tear it linearly by hand. It has been practiced to further laminate a stretched high-density polyethylene layer having excellent tearability. In this case, there is a problem that the cost becomes high. In some cases, the PET and the ON layer are scratched to improve the linear tearability, but the strength is lowered, and there is a problem that sufficient strength cannot be obtained as a retort pouch. there were.
【０００５】本発明は、上記問題点を解決するために、
直線的引き裂き性に優れた二軸延伸特殊ナイロンフィル
ムを使用して、レトルト用積層材を作製し、この積層材
を用いてレトルト用パウチやスタンディングパウチを製
袋することにより、コスト面及び強度面を変えずに内容
物をこぼすことなく、手で容易に開封できるようにする
ことを目的とする。In order to solve the above problems, the present invention provides
A biaxially stretched special nylon film with excellent linear tearability is used to make a retort laminate, and a bag for retort pouches and standing pouches is made using this laminate to reduce costs and strength. The purpose is to make it easy to open by hand without changing the contents and without spilling the contents.
【０００６】[0006]
【課題を解決するための手段】二軸延伸ポリエチレンテ
レフタレートフィルム、金属箔、二軸延伸ナイロンフィ
ルム、未延伸ポリプロピレンフィルムの順に積層される
レトルト用積層包材であって、該二軸延伸ナイロンフィ
ルムが直線的引き裂き性に優れた二軸延伸ナイロンフィ
ルムである易開封性レトルト用積層包材とした。また、
直線的引き裂き性に優れた二軸延伸ナイロンフィルムと
最内層の未延伸ポリプロピレンフィルムをポリエステル
ポリウレタ系接着剤１乃至５ｇ／ｍ2 （乾燥状態）を用
いてラミネートし、該二軸延伸ナイロンフィルムと未延
伸ポリプロピレンフィルムのラミネート強度を８００ｇ
／１５ｍｍ幅以上として、積層包材が手で直線的に引き
裂くことができるようなレトルト用積層包材とした。更
に、前記引き裂き性に優れた積層材を使用してレトルト
用の平パウチやスタンディングパウチを作製することに
より、該パウチが手で容易に開封できるような易開封性
レトルトパウチとした。[Means for Solving the Problems] A laminated packaging material for a retort in which a biaxially stretched polyethylene terephthalate film, a metal foil, a biaxially stretched nylon film and an unstretched polypropylene film are laminated in this order, wherein the biaxially stretched nylon film is A biaxially stretched nylon film having excellent linear tearability was provided as a layered packaging material for an easy-open retort. Also,
A biaxially stretched nylon film having excellent linear tearability and an unstretched polypropylene film as the innermost layer were laminated with a polyester polyureta adhesive 1 to 5 g / m 2 (dry state), Laminate strength of stretched polypropylene film is 800g
/ 15 mm width or more, so that the laminated packaging material for a retort can be torn linearly by hand. Furthermore, a flat pouch or a standing pouch for a retort was produced using the above-mentioned laminated material having excellent tearability, thereby making the pouch easily openable by hand.
【０００７】[0007]
【作用】本発明によれば、二軸延伸ポリエチレンテレフ
タレートフィルム、アルミニウム箔、二軸延伸ナイロン
フィルム、未延伸ポリプロピレンフィルムからなるレト
ルト用積層材において、該二軸延伸ナイロンフィルムを
直線的引き裂き性に優れた二軸延伸特殊ナイロンフィル
ムにすることにより、該積層包材が手で直線的に引き裂
くことができるようなレトルト用積層材を作製すること
ができる。また、前記引き裂き性に優れた積層材を使用
して、レトルト用平パウチやスタンディングパウチを作
製することにより、内容物をこぼすことなく、手で容易
に開封できるレトルト用平パウチやスタンディングパウ
チを得ることができる。According to the present invention, in a retort laminate comprising a biaxially stretched polyethylene terephthalate film, an aluminum foil, a biaxially stretched nylon film and an unstretched polypropylene film, the biaxially stretched nylon film is excellent in linear tearability. By using the biaxially stretched special nylon film, it is possible to prepare a laminated material for retort in which the laminated packaging material can be torn linearly by hand. Further, by using the above-mentioned laminated material having excellent tearability, a flat pouch for standing or a standing pouch for retort can be prepared to obtain a flat pouch for standing or a standing pouch that can be easily opened by hand without spilling the contents. be able to.
【０００８】[0008]
【実施例】以下、実施例に基づいて、図面を参照にしな
がら本発明を詳細に説明する。図１は本発明の引き裂き
性に優れた積層材の層構成を示す断面図である。図２は
本発明のレトルト用平パウチの斜視図であり、図３はそ
のパウチの層構成を示す断面図である。The present invention will be described in detail below with reference to the drawings based on the embodiments. FIG. 1 is a cross-sectional view showing a layer structure of a laminated material having excellent tearability according to the present invention. FIG. 2 is a perspective view of a flat pouch for a retort according to the present invention, and FIG. 3 is a cross-sectional view showing a layer structure of the pouch.
【０００９】本発明は、レトルト用平パウチやスタンデ
ィングパウチ包材に、直線的引き裂き性に優れた二軸延
伸特殊ナイロン（以下易引裂き性ＯＮとする）フィルム
を使用することにより、該積層包材に手で直線的に引き
裂くことができる機能を付与し、内容物をこぼさずに手
で開封できるようにしたことを特徴とする。The present invention uses a biaxially stretched special nylon (hereinafter referred to as easy tear ON) film having excellent linear tearability as a flat pouch for retort or a standing pouch packaging material. The feature is that it can be torn linearly by hand so that the contents can be opened by hand without spilling.
【００１０】本発明の易開封性レトルト包材は、図１に
示すように、外側よりＰＥＴフィルム１１、アルミニウ
ム箔１２、易引裂き性ＯＮフィルム１３、ＣＰＰフィル
ム１４より構成される。そして、表面層は耐熱性のある
ＰＥＴフィルムを使用し、バリヤー層としてアルミニウ
ム箔等の金属箔を用い、中間層には直線的引き裂き性を
付与するために、直線的引き裂き性に優れた二軸延伸特
殊ナイロンフィルムを使用し、更に、ヒートシール層と
して耐熱性のあるＣＰＰを使用した。As shown in FIG. 1, the easily openable retort packaging material of the present invention comprises a PET film 11, an aluminum foil 12, an easily tearable ON film 13, and a CPP film 14 from the outside. A heat-resistant PET film is used for the surface layer, a metal foil such as aluminum foil is used for the barrier layer, and a linear tearability is imparted to the intermediate layer. A stretched special nylon film was used, and further heat resistant CPP was used as a heat seal layer.
【００１１】以下に、表面層、中間層、シール層を構成
する樹脂について更に詳細に説明する。表面層には、従
来から耐熱性の点でレトルト用に多く使用されているＰ
ＥＴフィルムを使用した。表面層には、ＰＥＴフィルム
の他に、従来レトルト包材に使用されているＯＰＰフィ
ルムやＯＮフィルムも使用できる。積層材に直線的引き
裂き性を付与するために、中間層に直線的引き裂き性に
優れた二軸延伸特殊ナイロンフィルムを使用した。この
引き裂き性に優れた二軸延伸ナイロンフィルムとして
は、出光石油化学（株）製の「ユニアスロン」が好適で
ある。The resins constituting the surface layer, the intermediate layer and the seal layer will be described in more detail below. The surface layer is made of P, which has been widely used for retort due to its heat resistance.
ET film was used. For the surface layer, in addition to the PET film, an OPP film or an ON film which is conventionally used for a retort packaging material can be used. In order to impart linear tearability to the laminated material, a biaxially stretched special nylon film having excellent linear tearability was used for the intermediate layer. "Uniathlon" manufactured by Idemitsu Petrochemical Co., Ltd. is suitable as the biaxially stretched nylon film having excellent tearability.
【００１２】前記ユニアスロンは出光石油化学（株）製
の二軸延伸特殊ナイロンフィルムであり、ナイロン樹脂
の持つ特性である優れた強度を保持し、更に、フィルム
の流れ方向（ｍachine direction：ＭＤ）に優れた直線
カット性を有するフィルムである。このユニアスロンを
使用することにより、積層材の直線的引き裂き性がよく
なるため、従来のＯＮ仕様のレトルトパウチのような股
裂き現象は生じず、従来のレトルト包材の欠点が解消さ
れ、開封時に内容物をこぼすことなく、手で容易に開封
できるレトルト包材を得ることができる。The Uniathlon is a biaxially stretched special nylon film manufactured by Idemitsu Petrochemical Co., Ltd., which retains the excellent strength characteristic of the nylon resin, and further, in the machine direction (MD) of the film. It is a film having excellent linear cutting properties. By using this Uniathlon, the linear tearability of the laminated material is improved, so the cleaving phenomenon unlike the conventional ON specification retort pouch does not occur, the drawbacks of the conventional retort packaging material are eliminated, and the contents when opened It is possible to obtain a retort packaging material that can be easily opened by hand without spilling an item.
【００１３】また、ユニアスロンは従来の二軸延伸ナイ
ロン（ＯＮ）に比べて剛性が約３０％も高いので、スタ
ンディングパウチ等の自立袋用には好適であり、レトル
ト用スタンディングパウチの易開封包材としても使用で
きる。フィルムの厚さは１０〜３０μｍのものが使用で
きるが、１５〜２５μｍのものが好適である。Further, since uniathlon has a rigidity that is about 30% higher than that of conventional biaxially stretched nylon (ON), it is suitable for a self-standing bag such as a standing pouch, and an easy-open packaging material for a standing pouch for a retort. Can also be used as A film having a thickness of 10 to 30 μm can be used, but a film having a thickness of 15 to 25 μm is preferable.
【００１４】中間層のガスバリヤー層としては、アルミ
ニウム箔が通常使用されるが、アルミニウムと亜鉛の合
金箔等その他の金属箔も使用できる。Aluminum foil is usually used as the gas barrier layer of the intermediate layer, but other metal foils such as aluminum-zinc alloy foil can also be used.
【００１５】最内面のシール層には、未延伸ポリプロピ
レン（ＣＰＰ）を使用し、レトルト耐性のあるものにし
た。また、ハイレトルト用には融点が１４５〜１６５℃
のものを選定し、ハイレトルトにも耐性のある積層材と
した。For the innermost seal layer, unstretched polypropylene (CPP) was used to make it resistant to retort. Also, the melting point is 145 to 165 ° C for high retort.
Was selected as the laminated material that is resistant to high retorts.
【００１６】本発明のレトルト用積層包材は、上記フィ
ルム及び金属箔を使用して常法に従って製造することが
できる。例えば、ドライラミネーション法、ウェットラ
ミネーション法、押し出しラミネーション法等により、
或いはこれらの方法を組み合わせることにより製造する
こができる。The laminated packaging material for a retort according to the present invention can be manufactured by a conventional method using the above film and metal foil. For example, by dry lamination method, wet lamination method, extrusion lamination method,
Alternatively, it can be produced by combining these methods.
【００１７】中でもドライラミネーション法が好まし
く、この場合の接着剤としてポリエステルポリウレタン
系の接着剤が用いられる。コート量は乾燥状態で０．５
〜１０ｇ／ｍ2 の範囲で使用されるが、引き裂き性を重
視した場合、１〜５ｇ／ｍ2 が好ましい。ポリエステル
ポリウレタン系接着剤からなる接着剤層は伸びが少な
く、引き裂き性に優れた二軸延伸ナイロンと未延伸ポリ
プロピレンの接着強度が８００ｇ／１５ｍｍ幅以上と強
いため、積層材を構成する各フィルムの引き裂きに追随
して引き裂かれるので、引き裂き性を重視した積層材の
接着剤としては優れたものである。又、耐熱性に優れる
ため、レトルト包材に適したものである。積層材の引き
裂き強度としては、ＪＩＳ−Ｐ８１１６に準じて引き裂
き強度を測定した場合、１００ｇ以下が良好である。Among them, the dry lamination method is preferable, and a polyester polyurethane adhesive is used as the adhesive in this case. Coat amount is 0.5 in dry state
It is used in the range of 10 to 10 g / m 2 , but 1 to 5 g / m 2 is preferable when tearability is important. The adhesive layer made of polyester polyurethane-based adhesive has low elongation and the tear strength of biaxially stretched nylon and unstretched polypropylene with excellent tearability is as strong as 800 g / 15 mm width or more. It is an excellent adhesive for a laminated material that emphasizes tearability, because it is torn following the above. Moreover, since it has excellent heat resistance, it is suitable as a retort packaging material. The tear strength of the laminated material is preferably 100 g or less when the tear strength is measured according to JIS-P8116.
【００１８】次に、具体的な実施例に従って本発明を更
に詳しく説明する。 （実施例）厚さ１２μｍの二軸延伸ポリエチレンテレフ
タレート（以下ＰＥＴとする）フィルム（東洋紡績
（株）製〔エスペットＴ４１０２〕）の片面に印刷加工
を行い、その印刷面にポリエステルポリウレタン系接着
剤（武田薬品工業（株）製〔タケラックＡ５１５／Ａ−
５０〕）を４ｇ／ｍ2 （乾燥状態）塗布し、厚さ９μｍ
のアルミニウム箔（以下Ａｌとする）をドライラミネー
ション法によりラミネートして積層フィルムを作製し
た。Next, the present invention will be described in more detail with reference to specific examples. (Example) A biaxially-stretched polyethylene terephthalate (hereinafter referred to as PET) film having a thickness of 12 μm ([Espet T4102] manufactured by Toyobo Co., Ltd.) was printed on one side, and a polyester polyurethane adhesive was applied to the printed side. (Takelac A515 / A- manufactured by Takeda Pharmaceutical Co., Ltd.
50]) is applied at 4 g / m 2 (dry state), and the thickness is 9 μm.
The aluminum foil (hereinafter referred to as Al) was laminated by a dry lamination method to prepare a laminated film.
【００１９】次に、前記積層フィルムのＡｌ面に、厚さ
１５μｍのユニアスロン（以下易引裂き性ＯＮとする）
フィルム（出光石油化学（株）製）と厚さ６０μｍの未
延伸ポリプロピレン（以下ＣＰＰとする）フィルム（昭
和電工（株）製〔アロマーＵ〕）を順次ドライラミネー
ション法で積層して、下記仕様の積層材を作製した。・
ＰＥＴ12μｍ／Ａｌ 9μｍ／易引裂き性ＯＮ15μｍ／Ｃ
ＰＰ60μｍ（内面）Next, on the Al surface of the laminated film, a uniathlon having a thickness of 15 μm (hereinafter referred to as easy tearing ON).
A film (manufactured by Idemitsu Petrochemical Co., Ltd.) and a 60 μm thick unstretched polypropylene (hereinafter referred to as CPP) film (manufactured by Showa Denko KK [Aromar U]) were sequentially laminated by a dry lamination method, and the following specifications were obtained. A laminated material was produced.・
PET 12μm / Al 9μm / Easy tearing ON 15μm / C
PP 60 μm (inner surface)
【００２０】比較例として、易引裂き性ＯＮ及び従来の
二軸延伸ナイロン（以下ＯＮとする）フィルム（興人
（株）製〔ボニールＲＸ〕）を使用して、実施例と同様
の方法で下記仕様の積層材を作製した。いずれもＣＰＰ
が内面である。 （比較例１） ・ＰＥＴ12μｍ／易引裂き性ＯＮ15μｍ／Ａｌ 9μｍ／
ＣＰＰ60μｍ （比較例２） ・易引裂き性ＯＮ15μｍ／Ａｌ 9μｍ／ＣＰＰ60μｍ （比較例３） ・ＰＥＴ12μｍ／ＯＮ15μｍ／Ａｌ 9μｍ／ＣＰＰ60μ
ｍ （比較例４） ・ＰＥＴ12μｍ／Ａｌ 9μｍ／ＯＮ15μｍ／ＣＰＰ60μ
ｍAs a comparative example, an easily tearable ON and a conventional biaxially stretched nylon (hereinafter referred to as ON) film ([Bonil RX] manufactured by Kojin Co., Ltd.) were used in the same manner as in the following examples. A laminated material having the specifications was produced. Both are CPP
Is the inside. (Comparative Example 1) PET 12 μm / easily tearing ON 15 μm / Al 9 μm /
CPP 60 μm (Comparative Example 2) -Easy tearability ON 15 μm / Al 9 μm / CPP 60 μm (Comparative Example 3) -PET 12 μm / ON 15 μm / Al 9 μm / CPP 60 μ
m (Comparative Example 4) ・ PET 12 μm / Al 9 μm / ON 15 μm / CPP 60 μ
m
【００２１】実施例及び比較例１〜４で作製した積層材
について、積層材を流れ方向（ＭＤ）に引き裂き、引き
裂き量が１００ｍｍのとき、最初の位置からどれ位のズ
レが生じるかを測定し、以下のような試験結果が得られ
た。 With respect to the laminated materials produced in Examples and Comparative Examples 1 to 4, the laminated materials were torn in the machine direction (MD), and when the amount of tear was 100 mm, how much deviation from the initial position occurred was measured. The following test results were obtained.
【００２２】また、実施例及び比較例１〜４で作製した
積層材を用いて、図２に示すように、易引裂きＯＮ及び
ＯＮの流れ方向（ＭＤ）が袋の横方向になるように平パ
ウチ２を作製した。袋サイズは１３０×１５０ｍｍと
し、シール部３の幅は１０ｍｍとした。図３は実施例の
積層材を用いて、図２のような平パウチ２を作製したと
きのＸ−Ｘにおける断面図である。Further, using the laminated materials produced in Examples and Comparative Examples 1 to 4, as shown in FIG. 2, the easy-tearing ON and the flat flow direction (MD) of ON is in the lateral direction of the bag. Pouch 2 was prepared. The bag size was 130 × 150 mm, and the width of the seal portion 3 was 10 mm. FIG. 3 is a cross-sectional view taken along line XX when the flat pouch 2 as shown in FIG. 2 is manufactured using the laminated material of the example.
【００２３】前記パウチ２に水１２０ｃｃを充填し、上
部をヒートシールして密封し、これをレトルト釜にて、
１２０℃、３０分間加熱殺菌を行って、冷却後各サンプ
ルについて、外観検査、落下試験、引裂き性試験、引裂
き強度、シール強度、ラミネート強度、突き刺し強度等
の測定を行った。The pouch 2 is filled with 120 cc of water, and the upper portion is heat-sealed and hermetically sealed.
After heating and sterilizing at 120 ° C. for 30 minutes, the samples were cooled and then the appearance test, drop test, tearability test, tear strength, seal strength, laminate strength, puncture strength, etc. were measured.
【００２４】試験結果は表１に示すとおりで、実施例で
作製した積層材は直線的引き裂き性が最も良好で、且つ
レトルト包材として必要なその他の物性は従来のＯＮと
同等であり、易開封性レトルト包材として非常に優れて
いることが実証された。また、前記積層材を使用したレ
トルトパウチは、レトルト適性は従来のレトルト包材と
変わらず、開封性が非常に優れていることが判明した。The test results are shown in Table 1. The laminated materials produced in the examples have the best linear tearability, and the other physical properties required for the retort packaging material are the same as those of the conventional ON, and the easy tearability is obtained. It has been proved to be very excellent as an openable retort packaging material. Further, it was found that the retort pouch using the above-mentioned laminated material has retort suitability as good as that of the conventional retort packaging material, and that the retort pouch is very excellent in opening property.
【００２５】[0025]
【表１】 [Table 1]
【００２６】（注） （１） 引裂き性試験は、レトルト後のパウチを手で横
方向に開封したとき、表側と裏側で引き裂き線がずれて
股裂きの状態となるので、その股裂きの大中小を比較し
たものである。また、手で開封したときの引き裂き強さ
を判定した。 （２） サンプルをレトルト殺菌後、３℃に７日間保存
し、１２０ｃｍの高さから連続して袋の底から落下す
る。１袋当たり最大３０回落下し、計５袋落下して全破
袋数を算出する。平均破袋率＝全破袋数／総落下回数と
する。 （３） 引裂き強度は、ＪＩＳ−Ｐ８１１６のエルメン
ドルフ引裂き強度の測定法に準じて、パウチの開封方向
（積層フィルムのＴＤ方向）について、パウチが引き裂
かれるときの強度を測定した。単位はｇである。 （４） シール強度及びラミネート強度は、厚生省告示
２０号に準じて、サンプル１５ｍｍ幅におけるシール強
度とラミネート強度を測定した。単位はｋｇ／１５ｍｍ
である。 （５） 突き刺し強度は、厚生省告示２０号に準じて、
先端０．５Ｒ、直径１ｍｍの針により積層フィルムの突
き刺し強度を測定した。単位はｋｇである。(Note) (1) In the tearability test, when the pouch after retort is opened in the lateral direction by hand, the tear lines are deviated between the front side and the back side, resulting in a crotch tearing condition. It is a comparison of small and medium. Further, the tear strength when opened by hand was determined. (2) The sample is sterilized by retort, stored at 3 ° C. for 7 days, and continuously dropped from the bottom of the bag from a height of 120 cm. A maximum of 30 times is dropped per bag, and a total of 5 bags are dropped to calculate the total number of broken bags. Average bag breakage rate = total bag breakage / total number of drops. (3) Tear strength was measured according to the method for measuring Elmendorf tear strength of JIS-P8116 in the opening direction of the pouch (TD direction of the laminated film), at which the pouch was torn. The unit is g. (4) The seal strength and the laminate strength were measured according to the Ministry of Health and Welfare Notification No. 20 by measuring the seal strength and the laminate strength in a width of 15 mm of the sample. The unit is kg / 15mm
Is. (5) The piercing strength is based on the Ministry of Health and Welfare Notification No. 20,
The puncture strength of the laminated film was measured with a needle having a tip of 0.5R and a diameter of 1 mm. The unit is kg.
【００２７】[0027]
【発明の効果】本発明によれば、レトルト用包材に、直
線的引き裂き性に優れた二軸延伸特殊ナイロンフィルム
を使用することにより、該積層包材が手で直線的に引き
裂くことができるようなレトルト用積層材を作製するこ
とができる。また、前記引き裂き性に優れた積層材を使
用して、レトルト用平パウチやスタンディングパウチを
作製することにより、内容物をこぼすことなく、手で容
易に開封できるようになり、消費者の苦情を解消するこ
とができる。従って、従来のレトルト包材に新しい機能
を付与することになり、販路拡大に役立つ。According to the present invention, by using a biaxially stretched special nylon film having excellent linear tearability in a packaging material for retort, the laminated packaging material can be torn by hand in a linear manner. Such a retort laminated material can be produced. In addition, by using the above-mentioned laminated material having excellent tearability, a flat pouch for retort and a standing pouch can be easily opened by hand without spilling the contents, and consumer complaints can be obtained. It can be resolved. Therefore, a new function is added to the conventional retort packaging material, which is useful for expanding sales channels.
【図１】本発明によるレトルト用積層材の層構成を示す
の断面図である。FIG. 1 is a cross-sectional view showing a layer structure of a retort laminate material according to the present invention.
【図２】本発明によるレトルトパウチの斜視図である。FIG. 2 is a perspective view of a retort pouch according to the present invention.
【図３】本発明によるレトルトパウチの層構成を示す断
面図である。FIG. 3 is a cross-sectional view showing a layer structure of a retort pouch according to the present invention.
１ 積層材 ２ レトルトパウチ ３ シール部 ４ 積層材の流れ方向 １１ ＰＥＴフィルム １２ Ａｌ箔 １３ 易引裂き性ＯＮ １４ ＣＰＰフィルム DESCRIPTION OF SYMBOLS 1 Laminated material 2 Retort pouch 3 Seal part 4 Flow direction of laminated material 11 PET film 12 Al foil 13 Easy tearing ON 14 CPP film
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 27/08 9349−4Ｆ 27/34 9349−4Ｆ Ｂ６５Ｄ 30/02 33/00 Ｃ 81/34 // Ｂ２９Ｋ 23:00 77:00 Ｂ２９Ｌ 9:00 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location B32B 27/08 9349-4F 27/34 9349-4F B65D 30/02 33/00 C 81/34 / / B29K 23:00 77:00 B29L 9:00
Claims (3)
ィルム、金属箔、二軸延伸ナイロンフィルム、未延伸ポ
リプロピレンフィルムの順に積層されるレトルト用積層
包材であって、該二軸延伸ナイロンフィルムが直線的引
き裂き性に優れた二軸延伸ナイロンフィルムであること
を特徴とする易開封性レトルト用積層包材。1. A laminated packaging material for a retort in which a biaxially stretched polyethylene terephthalate film, a metal foil, a biaxially stretched nylon film, and an unstretched polypropylene film are laminated in this order, wherein the biaxially stretched nylon film is linearly tearable. A laminated packaging material for an easily openable retort, which is a biaxially stretched nylon film having excellent properties.
ロンフィルムと最内層の未延伸ポリプロピレンフィルム
をポリエステルポリウレタン系接着剤１乃至５ｇ／ｍ2
（乾燥状態）を用いてラミネートし、該二軸延伸ナイロ
ンフィルムと未延伸ポリプロピレンフィルムのラミネー
ト強度を８００ｇ／１５ｍｍ幅以上としたことを特徴と
する請求項１に記載のレトルト用積層包材。2. A biaxially stretched nylon film excellent in linear tearability and an unstretched polypropylene film as an innermost layer are used as a polyester polyurethane adhesive 1 to 5 g / m 2
The laminated packaging material for a retort according to claim 1, wherein the biaxially stretched nylon film and the unstretched polypropylene film are laminated using (dry state) to have a laminate strength of 800 g / 15 mm width or more.
を使用してパウチを作製することにより、該パウチが手
で容易に開封できるようにしたことを特徴とする易開封
性レトルトパウチ。3. An easily openable retort characterized in that a pouch is made by using the laminated packaging material according to claim 1 or 2, whereby the pouch can be easily opened by hand. Pouch.