JPH0827475A - Lubricating composition - Google Patents
Lubricating compositionInfo
- Publication number
- JPH0827475A JPH0827475A JP18683594A JP18683594A JPH0827475A JP H0827475 A JPH0827475 A JP H0827475A JP 18683594 A JP18683594 A JP 18683594A JP 18683594 A JP18683594 A JP 18683594A JP H0827475 A JPH0827475 A JP H0827475A
- Authority
- JP
- Japan
- Prior art keywords
- lubricating
- lubricating oil
- resin composition
- oil
- crosslinked resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、潤滑性組成物に関し、
特に軸受等の高温に晒される部品への適用が可能な潤滑
性組成物に関する。FIELD OF THE INVENTION The present invention relates to a lubricating composition,
In particular, the present invention relates to a lubricating composition that can be applied to parts exposed to high temperatures such as bearings.
【０００２】[0002]
【従来の技術】一般に軸受等の潤滑性が要求される部品
には、潤滑油や半固体状のグリース等の潤滑性組成物が
充填されている。しかしながら、これら潤滑性組成物は
潤滑油は勿論のこと、半固体状のグリースにおいても軸
受回転時の温度上昇に伴って流動化するため、これら潤
滑性組成物の飛散を防止するためにシール板等の密封部
材で充填部を密封しなければならず、構造が複雑にな
り、小型軸受等場合によっては密封部材を取り付けるこ
とができないこともある。2. Description of the Related Art In general, bearings and other parts requiring lubricity are filled with a lubricating composition such as lubricating oil or semi-solid grease. However, these lubricating compositions fluidize not only with the lubricating oil but also with semi-solid grease as the temperature rises during bearing rotation, so to prevent the scattering of these lubricating compositions, the sealing plate The filling portion must be sealed with a sealing member such as, which complicates the structure and may not be able to attach the sealing member depending on the case such as a small bearing.
【０００３】そこで密封部材を必要としない潤滑性組成
物として、潤滑油と樹脂とを混合して固形化させた潤滑
性組成物が開発され、実用化されている。この樹脂ベー
スの潤滑性組成物は、樹脂内に保持された潤滑油が樹脂
表面に滲み出て潤滑作用を発現するもので、例えば米国
特許第３７２９４１５号、同３５４７８１９号、同３５
４１０１１号各明細書には、潤滑油を含有するポリエチ
レンが記載されている。また、特公昭６３−２３２３９
号公報には、分子量として１×１０6 〜５×１０6 程度
の超高分子量のポリエチレンに、潤滑グリースを保持さ
せた潤滑性組成物が記載されている。Therefore, as a lubricating composition which does not require a sealing member, a lubricating composition in which a lubricating oil and a resin are mixed and solidified has been developed and put into practical use. This resin-based lubricating composition is one in which the lubricating oil retained in the resin exudes to the surface of the resin and exhibits a lubricating action. For example, US Pat. Nos. 3,729,415, 35,47819, and 35,
No. 41011 describes polyethylene containing a lubricating oil. In addition, Japanese Examined Japanese Patent Publication Sho 63-23239
The publication describes a lubricating composition in which a lubricating grease is held in ultrahigh molecular weight polyethylene having a molecular weight of about 1 × 10 6 to 5 × 10 6 .
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、上記ポ
リエチレンと潤滑油あるいはグリースとからなる潤滑性
組成物は、ポリエチレンは融点が低く、約８０℃ぐらい
から軟化し始め１３０〜１４０℃で完全に融解してしま
うので、８０℃以上の高温では使用できないという問題
点を抱えている。また、超高分子量ポリエチレンベース
の潤滑性組成物では、耐熱性能は改善されるものの、機
械的強度や成形性の点では充分満足できるものではな
く、軸受等に充填して使用した際に転動体の回転に伴い
変形や破壊を起こして充填部位から離脱してしまう。However, in the lubricating composition comprising polyethylene and lubricating oil or grease, polyethylene has a low melting point and begins to soften at about 80 ° C and completely melts at 130 to 140 ° C. Therefore, it has a problem that it cannot be used at a high temperature of 80 ° C. or higher. In addition, although the lubricating composition based on ultra-high molecular weight polyethylene has improved heat resistance, it is not sufficiently satisfactory in terms of mechanical strength and moldability. It will be deformed or destroyed as it rotates, and it will be separated from the filling part.
【０００５】本発明の目的は、以上の問題点を解決する
ことにあり、高温での使用が可能であり、しかも機械的
強度や成形性、潤滑油の保持量に優れた潤滑性組成物を
提供することにある。An object of the present invention is to solve the above problems, and to provide a lubricating composition which can be used at high temperature and which is excellent in mechanical strength, moldability and lubricating oil retention amount. To provide.
【０００６】[0006]
【課題を解決するための手段】上記目的を達成するため
に、本発明の潤滑性組成物は、ポリプロピレンとエチレ
ン・プロピレン・非共役ジエン三元共重合体とを混合し
且つ架橋してなる架橋樹脂組成物と、潤滑油あるいは該
潤滑油を基油とするグリースとからなる混合物、あるい
はポリプロピレン、ポリエチレンおよびエチレン・プロ
ピレン・非共役ジエン三元共重合体とを混合し且つ架橋
してなる架橋樹脂組成物と、潤滑油あるいは該潤滑油を
基油とするグリースとからなる混合物を、前記架橋樹脂
組成物の融解温度以上に加熱し、しかる後冷却固化して
得られることを特徴とする。また、本発明の潤滑性組成
物は、前記非共役ジエンがジシクロペンタジエン、エチ
リデンノルボルネン、１，４−ヘキサジエンの少なくと
も１つであることを特徴とする。In order to achieve the above object, the lubricating composition of the present invention comprises a crosslinked mixture of polypropylene and ethylene / propylene / non-conjugated diene terpolymer. A cross-linked resin obtained by mixing and cross-linking a resin composition and a mixture of a lubricating oil or a grease containing the lubricating oil as a base oil, or polypropylene, polyethylene and an ethylene / propylene / non-conjugated diene terpolymer It is characterized by being obtained by heating a mixture of a composition and a lubricating oil or a grease containing the lubricating oil as a base oil to a temperature above the melting temperature of the crosslinked resin composition, followed by cooling and solidification. Further, the lubricating composition of the present invention is characterized in that the non-conjugated diene is at least one of dicyclopentadiene, ethylidene norbornene and 1,4-hexadiene.
【０００７】[0007]
【作用】本発明に係る潤滑性組成物は、ポリプロピレン
あるいはポリプロピレンとポリエチレンとの混合物と、
エチレン・プロピレン・非共役ジエン三元共重合体（以
下、単に三元共重合体と呼ぶ）とを混合し且つ架橋して
なる架橋樹脂組成物と、潤滑油またはグリースとの溶融
混合物を冷却して固化させたものである。この潤滑性組
成物においては、架橋樹脂組成物が固化して所望の形状
を維持するとともに、その内部に潤滑油やグリースが保
持される。その際、架橋樹脂組成物の三次元構造あるい
は網目構造の微細空間中に潤滑油やグリースが取り込ま
れるために、潤滑油やグリースは架橋樹脂組成物全体に
わたり均一に、しかも多量に含有、保持される。また、
保持された潤滑油やグリースが徐々に滲み出すために、
長期にわたって安定した潤滑性を維持することができ
る。また、本発明に係る潤滑性組成物は、ポリプロピレ
ンあるいはポリプロピレンとポリエチレンとの混合物
と、前記三元共重合体とを混合し且つ架橋してなる架橋
樹脂組成物の融点は１６０〜１７０℃と高く、またその
軟化点も１３０〜１５０℃と高いので、従来のポリエテ
レンベースの潤滑性組成物では使用できなかった高温
（約１２０〜１４０℃）でも軟化せずに形状保持が可能
となり、機械的強度を維持した状態で長期間にわたり安
定した潤滑を保つことができる。The lubricating composition according to the present invention comprises polypropylene or a mixture of polypropylene and polyethylene,
A melted mixture of a cross-linked resin composition obtained by mixing and cross-linking ethylene / propylene / non-conjugated diene terpolymer (hereinafter, simply referred to as “terpolymer”) and a melted mixture of lubricating oil or grease is cooled. It was solidified. In this lubricating composition, the crosslinked resin composition is solidified to maintain a desired shape, and the lubricating oil or grease is retained therein. At that time, since the lubricating oil or grease is taken into the three-dimensional structure or the fine space of the network structure of the crosslinked resin composition, the lubricating oil or grease is uniformly contained and retained in a large amount throughout the crosslinked resin composition. It Also,
Since the retained lubricating oil or grease gradually exudes,
Stable lubricity can be maintained for a long period of time. Further, the lubricating composition according to the present invention has a high melting point of 160 to 170 ° C. of a crosslinked resin composition obtained by mixing and crosslinking polypropylene or a mixture of polypropylene and polyethylene and the terpolymer. Moreover, since its softening point is as high as 130 to 150 ° C., it is possible to retain the shape without softening even at a high temperature (about 120 to 140 ° C.) which cannot be used in the conventional polyethylene-based lubricating composition, and it is mechanically It is possible to maintain stable lubrication for a long period of time while maintaining strength.
【０００８】以下、本発明に係る潤滑性組成物をより詳
細に説明する。前記三元共重合体を構成するエチレン、
プロピレン並びに非共役ジエンの配合割合は特に限定さ
れるものではないが、一般にエチレンとプロピレンとの
共重合比において、プロピレンの量が３０モル％以下に
なると結晶化して機械的強度が向上する。従って、機械
的強度の向上のためには、エチレン含有量を高めること
が好ましい。また、前記三元共重合体を構成する非共役
ジエンは、ジシクロペンタジエン、エチリデンノルボル
ネン、１，４−ヘキサジエンが好ましく、これらジエン
類を単独で、あるいは混合して使用することができる。
これらの共役ジエンの配合割合も特に限定されるもので
はないが、通常５〜２６モル％の範囲内であり、１０〜
１２モル％が標準的な値である。Hereinafter, the lubricating composition according to the present invention will be described in more detail. Ethylene constituting the terpolymer,
The mixing ratio of propylene and non-conjugated diene is not particularly limited, but generally, in the copolymerization ratio of ethylene and propylene, when the amount of propylene is 30 mol% or less, crystallization is performed and mechanical strength is improved. Therefore, it is preferable to increase the ethylene content in order to improve the mechanical strength. The non-conjugated diene constituting the terpolymer is preferably dicyclopentadiene, ethylidene norbornene or 1,4-hexadiene, and these dienes can be used alone or in combination.
The blending ratio of these conjugated dienes is not particularly limited, but is usually within the range of 5 to 26 mol%,
12 mol% is a standard value.
【０００９】架橋樹脂組成物のもう一方の構成成分は、
ポリプロピレンあるいはポリプロピレンとポリエチレン
との混合物であるが、ポリプロピレンとポリエチレンと
の混合物を使用する場合には、ポリエチレンの割合がポ
リプロピレンに対して８０重量％以下であることが好ま
しい。ポリエチレンの割合が多くなると機械的強度が増
加して好ましいが、他方において、耐熱性（軟化点）が
低下するために、上記範囲とすることが好ましい。The other component of the crosslinked resin composition is
It is polypropylene or a mixture of polypropylene and polyethylene, but when a mixture of polypropylene and polyethylene is used, the proportion of polyethylene is preferably 80% by weight or less with respect to polypropylene. When the proportion of polyethylene is large, the mechanical strength is increased, which is preferable, but on the other hand, the heat resistance (softening point) is lowered, so that the above range is preferable.
【００１０】架橋樹脂組成物は、ポリプロピレンあるい
はポリプロピレンとポリエチレンとの混合物と、三元共
重合体とを混合して架橋させることにより得られる。架
橋は、有機過酸化物によって行われたものであり、ポリ
エチレンと三元共重合体は架橋状態となるのに対し、ポ
リプロピレンは架橋と同時に崩壊（高分子の切断）も起
こるので部分架橋状態となっている。The crosslinked resin composition is obtained by mixing polypropylene or a mixture of polypropylene and polyethylene with a terpolymer and crosslinking the mixture. Cross-linking is performed by organic peroxide, and polyethylene and terpolymer are in a cross-linked state, while polypropylene is disintegrated (cutting of polymer) at the same time as cross-linking. Has become.
【００１１】一方、本発明で用いることのできる潤滑油
は、極性の低い潤滑油の方が保持量並びに保持力の点で
有利であり、具体的にはオクタデシルジフェニルエーテ
ル等のアルキルフェニルエーテル油、エイコシルナフタ
レン等のアルキルナフタレン油、鉱油、ポリα−オレフ
ィン油等が適当である。また、本発明においては、前記
潤滑油の代わりに該潤滑油を基油とするグリースを使用
することができる。その場合、潤滑油にリチウム石けん
等の公知の金属石けん類、ウレア化合物あるいはベント
ナイト等を増ちょう剤として適量添加して調合される。On the other hand, among the lubricating oils that can be used in the present invention, a lubricating oil having a low polarity is more advantageous in terms of the amount of holding and the holding power, and specifically, alkyl phenyl ether oil such as octadecyl diphenyl ether, eicosane, etc. Alkylnaphthalene oil such as silnaphthalene, mineral oil, poly α-olefin oil and the like are suitable. Further, in the present invention, instead of the lubricating oil, grease having the lubricating oil as a base oil can be used. In that case, a known amount of a metallic soap such as lithium soap, a urea compound or bentonite is added to the lubricating oil as a thickener to prepare the mixture.
【００１２】前記架橋樹脂組成物と前記潤滑油あるいは
グリースとの配合割合は、潤滑性組成物を１００重量％
とした時に、架橋樹脂組成物が２０〜９０重量％、潤滑
油あるいはグリースが１０〜８０重量％であることが好
ましい。架橋樹脂組成物が２０重量％未満の場合は、固
化後の機械的強度が低く、形状保持が困難となる。ま
た、架橋樹脂組成物が９０重量％を越えた場合は、潤滑
性組成物としての潤滑油またはグリースの量が絶対的に
不足し、潤滑性を長期間維持できない。The blending ratio of the crosslinked resin composition and the lubricating oil or grease is 100% by weight of the lubricating composition.
It is preferable that the crosslinked resin composition is 20 to 90% by weight and the lubricating oil or grease is 10 to 80% by weight. If the crosslinked resin composition is less than 20% by weight, the mechanical strength after solidification is low, and it becomes difficult to maintain the shape. On the other hand, when the cross-linked resin composition exceeds 90% by weight, the amount of lubricating oil or grease as the lubricating composition is absolutely insufficient, and the lubricity cannot be maintained for a long time.
【００１３】本発明に係る潤滑性組成物は、前記架橋樹
脂組成物と前記潤滑油あるいはグリースとを主成分とす
るものであるが、潤滑性組成物の機械的強度の補強や、
成形性向上の目的で下記のような充填材を添加してもよ
い。例えば、炭酸カルシウム、炭酸マグネシウム、チタ
ン酸カリウムウィスカーやホウ酸アルミニウムウィスカ
ー等の無機ウィスカー類、あるいはガラス繊維やアスベ
スト、金属繊維等の無機繊維類及びこれらを布状に編組
したもの、また有機化合物では、カーボンブラック、黒
鉛粉末、カーボン繊維、アラミド繊維やポリエステル繊
維、あるいはポリイミドやポリベンゾイミダゾール等の
各種熱硬化性樹脂を添加することができる。更に、潤滑
性組成物の熱伝導性を向上させる目的で、カーボン繊
維、金属繊維、黒鉛粉末、金属粉末、ＺｎＯ粉末等を添
加してもよい。The lubricating composition according to the present invention is mainly composed of the crosslinked resin composition and the lubricating oil or grease.
The following fillers may be added for the purpose of improving moldability. For example, calcium carbonate, magnesium carbonate, inorganic whiskers such as potassium titanate whiskers and aluminum borate whiskers, or glass fibers, asbestos, inorganic fibers such as metal fibers and those braided into a cloth shape, or organic compounds , Carbon black, graphite powder, carbon fiber, aramid fiber or polyester fiber, or various thermosetting resins such as polyimide or polybenzimidazole can be added. Further, carbon fibers, metal fibers, graphite powder, metal powder, ZnO powder and the like may be added for the purpose of improving the thermal conductivity of the lubricating composition.
【００１４】また、潤滑油やグリースの保持量および保
持力を向上させる目的で、高吸油性高分子を配合するこ
ともできる。この高吸油性高分子は、分子間に油を取り
込んだり（吸着型吸油材）、あるいは繊維状の形態を採
る場合には該繊維間に毛細管現象により油を吸収保持
（貯蔵型吸油材）する性質を有する高分子であり、具体
的な物質名としてはポリスチレン、ポリウレタン、ポリ
メタクリル酸エステル等のアクリル樹脂あるいはポリノ
ルボルネン等を挙げることができる。これら高吸油性高
分子は単独でも、数種類混合して使用することもでき
る。混合して使用する場合、その組み合わせや混合割合
により、潤滑性組成物の潤滑油やグリースの保持量を自
由に調整することができる。Further, for the purpose of improving the holding amount and holding power of lubricating oil or grease, a highly oil-absorbing polymer can be blended. This highly oil-absorbing polymer absorbs oil between molecules (adsorption-type oil-absorbing material), or when it takes a fibrous form, absorbs and holds oil by capillary action between the fibers (storage-type oil-absorbing material). It is a polymer having properties, and concrete substance names include acrylic resins such as polystyrene, polyurethane, polymethacrylic acid ester, and polynorbornene. These highly oil-absorbent polymers can be used alone or in combination of several kinds. When mixed and used, the amount of lubricating oil or grease in the lubricating composition can be freely adjusted depending on the combination and the mixing ratio.
【００１５】本発明に係る潤滑性組成物は、例えば以下
の方法により製造される。先ず、前記配合割合で潤滑油
あるいはグリース中に前記架橋樹脂組成物、並びに必要
に応じて各種添加物を加えて均一に混合し、該混合物を
架橋樹脂組成物の融解温度以上の温度、例えば１７０〜
１８０℃で一様に溶解させる。次いで、この溶融混合物
を適当な金型に充填し、冷却して固化させる（射出成
形）ことにより潤滑性組成物が得られる。The lubricating composition according to the present invention is produced, for example, by the following method. First, the crosslinked resin composition, and if necessary, various additives are added to the lubricating oil or grease in the above-mentioned mixing ratio and mixed uniformly, and the mixture is heated to a temperature not lower than the melting temperature of the crosslinked resin composition, for example 170. ~
Dissolve uniformly at 180 ° C. Then, the melted mixture is filled in an appropriate mold and cooled to solidify (injection molding) to obtain a lubricating composition.
【００１６】このようにして得られる潤滑性組成物は、
内部に潤滑油あるいはグリースが潤滑性組成物中に均一
に保持され、また表面に潤滑油あるいはグリースが滲み
出たケーキ状の固形物で、金型形状に成形される。本発
明に係る潤滑性組成物は、成形性や形状保持性に優れる
ために、潤滑作用を必要とする部位の形状に合わせて成
形して、そのまま装着して使用することができる。例え
ば、玉軸受、ころ軸受等の転がり軸受、リニアガイド、
ボールねじ等の直動軸受の中の潤滑部材にグリース等の
代用として、しかも密封部材を必要とすることなく用い
ることができる。また、それ自体単独ですべり軸受とし
て用いることができる。The lubricating composition thus obtained is
Lubricating oil or grease is uniformly held in the lubricating composition inside, and a cake-like solid substance with lubricating oil or grease exuded on the surface is molded into a mold shape. Since the lubricating composition according to the present invention is excellent in moldability and shape-retaining property, it can be molded according to the shape of the part requiring a lubricating action and then used as it is. For example, rolling bearings such as ball bearings and roller bearings, linear guides,
It can be used as a substitute for grease or the like as a lubricating member in a linear motion bearing such as a ball screw, and without using a sealing member. It can also be used as a plain bearing by itself.
【００１７】[0017]
【実施例】以下の実施例により、本発明に係る潤滑性組
成物をより明確にすることができる。但し、本発明は以
下の実施例に限定されることなく、適宜変更することが
できる。[Examples] The following examples can clarify the lubricating composition according to the present invention. However, the present invention is not limited to the following examples and can be modified as appropriate.
【００１８】〔実施例１〕ポリプロピレンとエチレン・
プロピレン・非共役ジエン三元共重合体とからなる架橋
樹脂組成物〔三井石油化学工業（株）製：ミラストマー
Ｍ４８００Ｎ〕４．０ｇと、ジアルキルジフェニルエ
ーテル型潤滑油〔（株）松村石油研究所製：モレスコハ
イルーブＬＢＸ−１００〕６．０ｇとを混合し、１７０
℃に加熱して均一に溶解させて、溶融混合物を得た。そ
して、この溶融混合物を、５０℃に保温された金型に射
出して成形した。得られた固体は、潤滑油（ジアルキル
ジフェニルエーテル型潤滑油）を均一に保持した状態で
固化したポリプロピレンとエチレン・プロピレン・非共
役ジエン三元共重合体とを混合してなる架橋樹脂組成物
であり、比較的高い機械強度を有し、その表面に潤滑油
が徐々に滲み出してくるような白色の固形物であった。
また、前記溶融混合物を、５０℃に保温された６３０５
型玉軸受の内・外輪の間の転動体と保持器以外の空間に
充填し、同様の方法により射出成形させた後、この玉軸
受を１３０℃で３０００ｒｐｍで回転させて潤滑性を調
べたところ、２００時間経過時点でも、良好な潤滑性を
示した。[Example 1] Polypropylene and ethylene
Cross-linked resin composition consisting of propylene / non-conjugated diene terpolymer [manufactured by Mitsui Petrochemical Co., Ltd .: Mirastomer M4800N] 4.0 g and dialkyl diphenyl ether type lubricating oil [manufactured by Matsumura Petroleum Research Institute: Moresco High Lube LBX-100] 6.0 g was mixed, and 170
It heated at 0 degreeC and melt | dissolved uniformly, and the molten mixture was obtained. Then, this molten mixture was injected into a mold kept at 50 ° C. to be molded. The obtained solid is a crosslinked resin composition obtained by mixing polypropylene solidified in a state in which lubricating oil (dialkyldiphenyl ether type lubricating oil) is uniformly held and ethylene / propylene / non-conjugated diene terpolymer. It had a relatively high mechanical strength and was a white solid such that lubricating oil gradually exuded on its surface.
In addition, the molten mixture was heated to 6305
After filling the space between the rolling elements and the cage between the inner and outer races of the molded ball bearing and injection molding by the same method, this ball bearing was rotated at 3000 rpm at 130 ° C and the lubricity was examined. Even after the lapse of 200 hours, good lubricity was exhibited.
【００１９】〔実施例２〕実施例１の架橋樹脂組成物
を、ポリプロピレンとポリエチレンとの混合物と、エチ
レン・プロピレン・非共役ジエン三元共重合体とからな
る架橋樹脂組成物〔三井石油化学工業（株）製：ミラス
トマー ８０３２Ｎ〕に代えた以外は、実施例１と同様
にして潤滑性組成物を得た。得られた固体は、実施例１
と同様に、潤滑油（ジアルキルジフェニルエーテル型潤
滑油）を均一に保持した状態で固化したポリプロピレ
ン、ポリエチレンおよびエチレン・プロピレン・非共役
ジエン三元共重合体を混合してなる架橋樹脂組成物であ
り、比較的高い機械強度を有し、その表面に潤滑油が徐
々に滲み出してくるような白色の固形物であった。ま
た、同様に６３０５型玉軸受に組み込み、潤滑性を調べ
たところ、２００時間経過時点でも、良好な潤滑性を示
した。[Example 2] A crosslinked resin composition obtained by mixing the crosslinked resin composition of Example 1 with a mixture of polypropylene and polyethylene and an ethylene / propylene / non-conjugated diene terpolymer [Mitsui Petrochemical Industry] A lubricant composition was obtained in the same manner as in Example 1 except that the product was changed to Mirastomer 8032N manufactured by Co., Ltd. The obtained solid was obtained in Example 1
Similarly, a cross-linked resin composition obtained by mixing polypropylene, polyethylene, and ethylene / propylene / non-conjugated diene terpolymer copolymerized with lubricating oil (dialkyldiphenyl ether type lubricating oil) uniformly held, It had a relatively high mechanical strength, and was a white solid such that the lubricating oil gradually exuded on its surface. Further, when similarly incorporated into a 6305 type ball bearing and examined for lubricity, good lubricity was exhibited even after 200 hours had elapsed.
【００２０】[0020]
【発明の効果】以上説明したように、本発明に係る潤滑
性組成物は、ポリプロピレンあるいはポリプロピレンと
ポリエチレンとの混合物と、エチレン・プロピレン・非
共役ジエン三元共重合体とを混合し且つ架橋してなる架
橋樹脂組成物と、潤滑油またはグリースとの溶融混合物
を冷却して固化させたものである。この潤滑性組成物に
おいては、架橋樹脂組成物が固化して所望の形状を維持
するとともに、その内部に潤滑油やグリースが保持され
る。その際、架橋樹脂組成物の三次元構造あるいは網目
構造の微細空間中に潤滑油やグリースが取り込まれるた
めに、潤滑油やグリースは架橋樹脂組成物全体にわたり
均一に、しかも多量に含有、保持される。また、保持さ
れた潤滑油やグリースが徐々に滲み出すために、長期に
わたって安定した潤滑性を維持することができる。ま
た、本発明に係る潤滑性組成物の融点は１６０〜１７０
℃と高く、またその軟化点も１３０〜１５０℃と高いの
で、従来のポリエテレンベースの潤滑性組成物では使用
できなかった高温（約１２０〜１４０℃）でも軟化せず
に形状保持が可能となり、機械的強度を維持した状態で
長期間にわたり安定した潤滑を保つことができる。As described above, the lubricating composition according to the present invention is obtained by mixing and crosslinking polypropylene or a mixture of polypropylene and polyethylene with an ethylene / propylene / non-conjugated diene terpolymer. A cross-linked resin composition obtained from the above, and a molten mixture of a lubricating oil or grease are cooled and solidified. In this lubricating composition, the crosslinked resin composition is solidified to maintain a desired shape, and the lubricating oil or grease is retained therein. At that time, since the lubricating oil or grease is taken into the three-dimensional structure or the fine space of the network structure of the crosslinked resin composition, the lubricating oil or grease is uniformly contained and retained in a large amount throughout the crosslinked resin composition. It In addition, since the retained lubricating oil or grease gradually exudes, stable lubricity can be maintained for a long period of time. The melting point of the lubricating composition according to the present invention is 160 to 170.
Since it has a high softening point of 130 to 150 ° C., it can retain its shape without softening even at a high temperature (about 120 to 140 ° C.) which cannot be used in the conventional polyethylene-based lubricating composition. It is possible to maintain stable lubrication for a long period of time while maintaining the mechanical strength.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ１０Ｎ 60:00 70:00 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 6 Identification code Office reference number FI technical display location C10N 60:00 70:00
Claims (3)
・非共役ジエン三元共重合体とを混合し且つ架橋してな
る架橋樹脂組成物と、潤滑油あるいは該潤滑油を基油と
するグリースとからなる混合物を、前記架橋樹脂組成物
の融解温度以上に加熱し、しかる後冷却固化して得られ
ることを特徴とする潤滑性組成物。1. A mixture comprising a crosslinked resin composition obtained by mixing polypropylene and ethylene / propylene / non-conjugated diene terpolymer and crosslinking, and a lubricating oil or a grease containing the lubricating oil as a base oil. Is heated above the melting temperature of the crosslinked resin composition, and then cooled and solidified to obtain a lubricating composition.
チレン・プロピレン・非共役ジエン三元共重合体を混合
し且つ架橋してなる架橋樹脂組成物と、潤滑油あるいは
該潤滑油を基油とするグリースとからなる混合物を、前
記架橋樹脂組成物の融解温度以上に加熱し、しかる後冷
却固化して得られることを特徴とする潤滑性組成物。2. A cross-linked resin composition obtained by mixing and cross-linking polypropylene, polyethylene and an ethylene / propylene / non-conjugated diene terpolymer, and a lubricating oil or a grease containing the lubricating oil as a base oil. A lubricating composition obtained by heating a mixture to a temperature above the melting temperature of the crosslinked resin composition and then cooling and solidifying the mixture.
エン、エチリデンノルボルネン、１，４−ヘキサジエン
の少なくとも１つであることを特徴とする請求項１また
は２記載の潤滑性組成物。3. The lubricating composition according to claim 1, wherein the non-conjugated diene is at least one of dicyclopentadiene, ethylidene norbornene and 1,4-hexadiene.