JPH08122320A - Substance measuring utensil, its manufacture and ion measuring utensil - Google Patents

Abstract

PURPOSE: To analyze and extract a substance in a solution simply and in a short time by a method wherein a water-soluble polymer phase is filled into a part between organic phases having a three-dimensional network structure which is formed by dissolving a non-water-soluble polymer in a hardly-water- soluble volatile organic solvent. CONSTITUTION: A non-water-soluble polymer such as a polyvinyl chloride-based polymer, a styrene-based polymer or the like is dissolved in a hardly-water- soluble volatile organic solvent (an organic solvent) such as dioctyl phthalate, o-nitrophenyloctyl-ether or the like, and organic phases having a three- dimensional network structure whose viscosity and physical strength are suitable for use as a substance-measuring utensil are generated. A water-soluble polymer such as polyethylene glycol or the like is filled into a part between the organic phases so that a sample to be measured is permeated quickly into the part between the organic phases. Although various filling methods are available, a method in which, after the organic solvent, the non-water-soluble polymer and the water-soluble polymer have been dissolved in the organic solving medium, they are coated on a support so as to be dried is most suitable.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a substance measuring instrument which can be used for detecting and quantifying various substances in a solution, and an ion measuring instrument using the same.

[0002]

2. Description of the Related Art In the field of analytical chemistry, various substances in a solution, particularly in an aqueous solution, are measured and used for medical purposes, production activities, environmental protection and the like. For example, it is known that useful information regarding the pathological condition of a patient can be obtained by measuring the ion concentration in serum and urine of the human body. Further, monitoring of harmful heavy metals in waste liquid discharged as a result of production activities of companies and measurement of the concentration of surfactant contained in domestic wastewater are required for environmental protection.
There are no other examples, but the measurement of substances in solution is indispensable to our lives.

The method of measuring a substance in a solution varies depending on the substance to be measured, and there are many methods. Among them, there is a method called a colorimetric method for measuring a change in absorption or fluorescence spectrum induced by a substance to be measured. In the colorimetric method, the substance to be measured in an aqueous solution is extracted and separated into an organic solvent, and it is generated by the interaction between the substance to be measured that has moved to the organic solvent and the coloring reagent previously added to water or the organic solvent. Quantification is often performed from the amount of change in absorption or fluorescence spectrum.

Extraction separation is an operation performed to separate a substance from one of two kinds of liquid to the other.
Generally, two kinds of solutions that do not mix with each other are put into a separating funnel, shaken and mixed, and then only the solution on the side where the substance to be measured has moved is taken out. Therefore, in the measurement of the colorimetric method that requires extraction and separation operation, a dedicated tool for extraction and separation is required. In order to make up for this drawback, it is known to use a film made of a poorly water-soluble and hardly volatile organic solvent in which a water-insoluble polymer is added instead of the organic solvent. For example, “Analytical Chemistry” Vol. 40 (1991)
(Pp. 227-231), using a film in which bathocuproine, which forms a complex with a monovalent copper ion to form a color, is dissolved in a water-insoluble polymer and a sparingly water-soluble sparingly volatile organic solvent. Is contacted with an aqueous solution containing an unknown concentration of monovalent copper ions to extract and separate the copper ions into the film to develop the color of bathocuproine in the film and to measure the copper ion concentration from the film's absorbance. Has been.
However, in the extraction / separation operation, since the substance transfer in which the measurement target substance in the aqueous solution moves into the poorly water-soluble hardly-volatile organic solvent is essential, Has the disadvantage that it becomes rate-determining and the measurement takes a very long time.

A method for analyzing ions by a colorimetric method based on the principle of causing absorption or a change in fluorescence spectrum due to movement of a substance to be measured is disclosed in JP-A-59-211864, JP-A-59-231452 and JP-A-60. -194360. These are ion concentration measuring instruments composed of various ionophores and poorly water-soluble and hardly volatile organic solvents containing dyes called reporter substances. When these measuring tools are brought into contact with a measurement sample aqueous solution containing ions, which is a substance to be measured, the ions are moved into the film and the absorption spectrum or the fluorescence spectrum of the dye is changed. Also in this method, it is known that the rate at which ions diffuse in the film is rate-determining. It is known that reducing the film thickness to about several μm is an effective method. However, this method is not practical because it has a drawback that the rate of color change increases, but the obtained color change amount decreases.

Various approaches have been developed to overcome the above drawbacks. For example, Japanese Unexamined Patent Publication No. 60-194360 describes an ion concentration measuring instrument in which a porous carrier is loaded with a poorly water-soluble and hardly volatile organic solvent containing various ionophores and a pH-sensitive dye called a reporter substance. This is an attempt to solve both problems of color change rate and color change amount by thinly coating a surface of a porous carrier such as filter paper with an ionophore and a poorly water-soluble and hardly volatile organic solvent containing a reporter substance. It was We could solve this problem to some extent. However, a measuring tool using these porous carriers requires a step of fixing the porous carrier on a support at an accurate position when manufacturing, and it is difficult or extremely difficult to mass-produce it. It still had the drawback of being expensive. Therefore, it has been desired to develop a method having the same effect without using a porous carrier.

[0007]

SUMMARY OF THE INVENTION A substance measuring instrument capable of performing a measurement having both a response speed and a response amount which are practically sufficient, for example, when used in a colorimetric method, a practically sufficient color development speed and color change amount can be obtained. The purpose is to develop a material measuring tool that can perform combined measurements and an ion measuring tool that uses this.

[0008]

[Means for Solving the Problems] The inventors of the present invention have conducted extensive studies to develop a material measuring instrument that can solve such problems. As a result, when the water-soluble polymer phase and the organic phase formed by dissolving the water-insoluble polymer in the poorly water-soluble and hardly volatile organic solvent have a specific structure, they exhibit sufficient performance to solve the above problems. I found what to do.

That is, the present invention comprises (A) an organic phase obtained by dissolving a water-insoluble polymer in a poorly water-soluble, hardly volatile organic solvent, and (B)
A substance measuring device comprising a water-soluble polymer phase, wherein (A) the organic phase has a three-dimensional network structure and (B) the water-soluble polymer phase is filled between the (A) organic phases. And a substance measuring tool in which the substance measuring tool is laminated on a support.

Another aspect of the present invention is that (A) an ionophore complexed with an ion or a ionophore complexed with an ion, which interacts with a poorly water-soluble poorly volatile organic solvent to form a detectable response by complexing with the ion. A dye exhibiting a detectable response, and an organic phase formed by dissolving a water-insoluble polymer and (B) a water-soluble polymer phase, and (A) the organic phase has a three-dimensional network structure. ) An ion measuring instrument characterized in that (B) a water-soluble polymer phase is filled between organic phases, and the ion measuring instrument is further laminated on a support.

Still another invention is to apply a solution of a poorly water-soluble hardly volatile organic solvent, a water-insoluble polymer and a water-soluble polymer dissolved in an organic solvent onto a support, and then to make the poorly water-soluble Measurement of the above-mentioned substance characterized in that the organic solvent is evaporated under the condition that the precipitation of the organic phase consisting of the volatile organic solvent and the water-insoluble polymer starts prior to or simultaneously with the precipitation of the water-soluble polymer. It is a manufacturing method of the ingredient.

The organic phase constituting the substance measuring device of the present invention basically comprises a poorly water-soluble hardly volatile organic solvent and a water-insoluble polymer.

The poorly water-soluble and hardly volatile organic solvent (hereinafter simply referred to as an organic solvent) means that it is hardly soluble in water and has a high boiling point.
It refers to an organic compound that does not have an ionizable functional group and is liquid at room temperature. The organic solvent is used to extract the substance to be measured in the measurement sample and to dissolve the dye or the like necessary for the measurement. Specifically, it is desirable that the boiling point is 100 degrees Celsius or more and the amount of the organic solvent that can be dissolved in 1 liter of water is about 1 g or less for stable measurement.

Specific examples of the organic solvent preferably used include high-boiling point esters such as dibutyl adipate and dioctyl phthalate, and high-boiling point ethers such as o-nitrophenyl octyl ether and diphenyl ether.

As the water-insoluble polymer, a polymer which can be dissolved in the above organic solvent and is insoluble in water is used. The water-insoluble polymer is dissolved in the above organic solvent to give viscosity and physical strength suitable for use as a substance measuring tool.

Examples of water-insoluble polymers that are preferably used include polyvinyl chloride, polyvinyl chloride-based polymers such as ethylene-vinyl chloride copolymer, vinyl chloride-vinylidene chloride copolymer, vinylidene chloride and the like. Examples include vinylidene chloride-based polymers, methacrylic acid ester-based polymers such as polymethylmethacrylate, and styrene-based polymers such as polystyrene. The degree of polymerization of the water-insoluble polymer can be used without any particular limitation. Generally, if the average degree of polymerization of 500 or more is used, the organic solvent becomes self-supporting, which is preferable. It is preferable that the concentration of the molecule in the organic solvent is equal to or lower than the upper limit of the solubility thereof, and the organic solvent is in a range showing the self-supporting property, because the substance measuring tool can be easily handled. The concentration range varies depending on the type of the water-insoluble polymer and organic solvent used, but generally, the water-insoluble polymer is added to the organic solvent in an amount of 5 to 5.
It is preferable to use it by dissolving it in 100% by weight. The method for dissolving the water-insoluble polymer in the organic solvent is not particularly limited, and usually the water-insoluble polymer is dissolved in the organic solvent while gradually being added.

The water-soluble polymer phase constituting the present invention basically consists of a water-soluble polymer. The water-soluble polymer is used for facilitating rapid penetration of the measurement sample between the organic phases of the three-dimensional network structure.

The water-soluble polymer is a polymer that can be dissolved in water, and the water-soluble polymer has a solubility of 50.
It is desirable to use wt% or more. If the water-soluble polymer is not present, the measurement sample cannot spread to every corner of the organic solvent, so that the measurement time required when the substance measuring tool is used for measurement becomes long. It is desirable to use a water-soluble polymer that is hardly soluble in an organic solvent. The effect of the present invention can be obtained even when using a substance that dissolves in an organic solvent, but in that case, when the measurement sample and the substance measuring tool of the present invention are brought into contact with a significant deformation, stable measurement cannot be performed. There are cases. Further, considering the easiness of handling when used as a substance measuring tool, it is desirable to use one having a degree of polymerization which becomes a solid state at room temperature. The amount of water-soluble polymer is 5 with respect to the total amount including organic solvent and water-insoluble polymer.
The range of 0 to 100% by weight is desirable for promoting the permeation of the measurement sample while maintaining an appropriate physical strength.

Examples of water-soluble polymers that can be preferably used include polyether polymer compounds such as polyethylene glycol and polypropylene glycol, polyvinylpyrrolidone, polyvinyl alcohol and polyacrylamide.

The fact that the organic phase of the present invention has a three-dimensional network structure can be confirmed by observing, with an electron microscope or the like, the portion remaining after washing the water-soluble polymer with water.

Various methods can be used for allowing the water-soluble polymer phase to exist in a packed state between the organic phases having a three-dimensional network structure. The most preferably used method is as follows. Is.

That is, the organic solvent, the non-water-soluble polymer and the water-soluble polymer are all dissolved in the organic solvent, and thereafter, the solution is coated on the support and dried. Along with the evaporation of the organic solvent, the water-soluble polymer phase and the organic phase formed by dissolving the water-insoluble polymer in the organic solvent undergo microphase separation, and the water-soluble polymer phase has a three-dimensional network structure. Precipitates in a state of being filled.

As the organic solvent used in the above method, any organic solvent, water-insoluble polymer and water-soluble polymer can be used without any limitation. Organic solvents that can be used differ depending on the selected organic solvent, water-insoluble polymer, and combination of water-soluble polymers, but examples include ethers such as tetrahydrofuran, and halogenated alkyls such as dichloromethane, chloroform, and dichloroethane. . The amount of organic solvent used cannot be unconditionally specified because it depends on the solubility of the selected organic solvent, water-insoluble polymer, and water-soluble polymer, but it cannot be specified unconditionally. It is general that the amount of one of the polymers is equal to or more than that of the organic solvent.

In the above-mentioned precipitation method, a uniform and good structure is obtained when the precipitation of the organic phase consisting of the organic solvent and the water-insoluble polymer begins prior to or simultaneously with the precipitation of the water-soluble polymer phase. be able to. It is more preferable that the organic phase is produced under the condition that the precipitation of the organic phase starts first. On the contrary, if the water-soluble polymer deposition begins before the organic phase deposition,
The obtained substance measuring tool is not uniform and has many voids, and is not suitable for measurement by a colorimetric method.

The precipitation order of the organic phase and the water-soluble polymer phase can be controlled by controlling the solubility of the organic solvent that dissolves both phases in the organic phase and the water-soluble polymer phase. This control of solubility is generally controlled by the polarity of the organic solvent. Generally, the organic solvent and the water-insoluble polymer that constitute the organic phase have a property that they are easily dissolved in an organic solvent having a low polarity, and conversely, the water-soluble polymer is easily dissolved in an organic solvent having a high polarity. Therefore, if an organic solvent having a high polarity is used, the precipitation of the organic phase having a low solubility starts first. Therefore, the precipitation of the organic phase composed of the organic solvent and the water-insoluble polymer can be started before the precipitation of the water-soluble polymer phase.

The polarity of the organic solvent can be controlled by mixing two or more kinds of organic solvents or water. Examples of suitable use include tetrahydrofuran with about 0.1% water, chloroform with 1% methanol, and the like. Further, even when the ionophore and the dye are dissolved in the organic phase, the order of precipitation can be controlled by the same method without any problem.

Specific examples of a substance measuring instrument having a good structure include o-nitrophenyl octyl ether as an organic solvent, polymethyl methacrylate as a water-insoluble polymer, and polyethylene glycol (average as a water-soluble polymer). It can be prepared by dissolving these in tetrahydrofuran, using a molecular weight of about 6000), coating them on a glass plate, and leaving them to stand at room temperature for drying. At this time, if a small amount of water is present in tetrahydrofuran, the precipitation of polyethylene glycol will be delayed and the above structure can be obtained with good reproducibility. The precipitation of the organic phase consisting of the organic solvent and the water-insoluble polymer starts before the precipitation of the water-soluble polymer phase, because the colored organic phase or the organic phase in which the dye is dissolved causes the colored precipitation. It can be known by the precipitation of the substance.

The principle and method of using an organic phase obtained by dissolving an ionophore, which forms a detectable response by forming a complex with an ion, in an organic solvent for measuring the ion concentration are well known, and "Analytical Chemistry" Vol. 40 (1991). Year) 227 to 231 have the description. The principle of using an organic phase formed by dissolving an ionophore that forms a complex with an ion, a dye that exhibits a detectable response by interacting with the complex formation, and a water-insoluble polymer in an organic solvent for measuring the ion concentration The method is also known, and Japanese Patent Laid-Open No. 59-211864, “Analytical Science” 1990 715-7
For example, see page 20. As the ionophore and dye used in the present invention, those described in these documents can be used without any problems.

In the present invention, an ionophore is a compound having the property of forming a complex with a specific cation.
A dye which has the ability to form a complex with a specific metal ion, causes a change in the electron orbital state by forming a complex with the metal ion, and causes a change in the absorption spectrum or fluorescence spectrum of the complex is It can be used as an ionophore to complex and show a detectable response. Examples of such ionophores include nitrosoaminophenols, diethylaminophenols, porphyrins and phenoxazines.

As the ionophore which can be used in the combination of the ionophore of the present invention which forms a complex with an ion and a dye which exhibits a detectable response by interacting with the complex formation, several known cyclic peptides can be used. Compounds, cyclic or acyclic polyether derivatives, potand derivatives, calixarene derivatives and the like.

Specific examples of ionophores that can be suitably used by forming a complex with an ion and exhibiting a detectable response include 3'-nitro-4'- with respect to potassium ions.
(2,4,6-Trinitrophenylamino) benzo-18-crown-6, 4 '-(2,6-dinitro-4-trifluoromethylphenyl) aminobenzo-15-crown-5, etc. are converted into copper ions. In contrast, bathocuproine and the like, iron ions such as 2-nitroso-5-N, N-dipropylaminophenol and other nitrosoaminophenols, and nickel and zinc ions, 2- (5-bromo- Diethylaminophenols such as 2-pyridylazo) -5-diethylaminophenol are phenoxazines such as [9- (diethylamino) -5-octadecanoylimino-5H-benzo [a] phenoxazine] for hydrogen ions. , [5-octadecanoyloxy-2- (4-nitrophenylazo) phenol] and other azophenols.

On the other hand, a specific example of an ionophore which can be preferably used in the combination of an ionophore that forms a complex with an ion and a dye that exhibits a detectable response by interacting with the complex formation is a lithium ionophore. Is 6,6-dibenzyl-1,4,8,11-tetraoxacyclotetradecane, 2,9-dibutyl-1,10-phenanthroline, and the like; and sodium ionophore is 5,11,17,23-tetra-t. -Butyl-25,26,27,28- tetrakis (ethoxycarbonyl) -methoxy-calix [4] arene, bis [(12-
Crown-4) methyl] methyl dodecyl malonate etc .;
Valinomycin as potassium ionophore, 2, 3-
Naphtho-1,4,7,10,13-pentaoxacyclopentadeca-2-
Ene, bis [(benzo-15-crown-5) -4'-methyl] pimelate, valinomycin and the like; as a calcium ionophore, diethyl-N, N '-[(4R, 5R) -4,5-dimethyl-1 , 8-Dioxo-3,6-dioxaoctamethylene] bis (12-methylaminododecanoate) and the like; magnesium ionophores include N, N'-diheptyl-N, N'-dimethylaspartamide and the like, Benzo-15-thiacrown for copper ions
-4-There are ether etc.

Of course, there are other compounds known to form a complex with a cation, and these can also be used. For references on ionophores, see “Cation Bindi” edited by Yoshihisa Inoue, George W. Gokel.
ng by Macrocycles "(MARCEL DEKKER INCORPORATION
1990), "Application of Functional Macrocycles to Analytical Chemistry", edited by Hiroyuki Takeda (published by IPC, Inc. in 1990) ANALYTICAL CHEMISTRY 60
Volume 2013-2016 (1988), "Analytical Chemistry" 23 Vol 141
2-1430 pages (1974) and so on.

As a dye (hereinafter referred to as a reporter dye) that interacts with an ionophore that forms a complex with the above-mentioned ion and exhibits a detectable response, there is a series of dyes called a pH indicator or a pH-sensitive dye. .

Since the reporter dye used in the present invention is solubilized and contained in an organic solvent, a substance having extremely small water solubility is used. Because of its easy availability and the degree of color response when used as an ion measuring tool, pKa
Reporter dyes of 5 to 10 are preferably used.

Specific examples of the reporter dye include phenolphthalein derivatives such as phenolphthalein and tetrabromophenolphthalein, 2,6-dichloroindophenol, 2,6-dibromo-3'-methylindophenol and the like. Examples include indophenol derivatives and triphenylmethane dye derivatives such as Victoria Pure Blue.

The ionophore and reporter dyes can be dissolved in organic solvents up to the upper limit of their solubility. At this time, it is known that the molar ratio of the ionophore to the reporter dye is preferably 1: 1 based on the principle. In general, the concentrations of the ionophore and the reporter dye in the organic solvent are preferably in the range of 0.1 to 200 mM in consideration of the sensitivity at the time of measurement.

In the present invention, the organic phase formed by dissolving a water-insoluble polymer in an organic solvent has a three-dimensional network structure, and the organic phase has a three-dimensional network structure such as sponge and sponge. It means having. Various substances having the same structure are used as different substances as water-absorbing substances or for filtering and separating. A method for producing a substance composed of a water-insoluble polymer having a three-dimensional network structure is disclosed in JP-A-2-30244.
9, JP-A-58-104940, JP-A-47-4593 and the like. These conventional substances having a three-dimensional network structure mainly consist of a water-insoluble polymer in order to achieve high strength, and generally do not add an organic solvent. Further, even if an organic solvent is added, no one filled with a water-soluble polymer is known. The organic phase in which the water-insoluble polymer is dissolved in the organic solvent of the three-dimensional network structure of the present invention is mainly composed of the organic solvent for performing the extraction operation, and the water-insoluble polymer is appropriate. There is a fundamental difference in that it is added in order to impart a proper viscosity and physical strength.

In the present invention, the water-soluble polymer phase is filled between the organic phases of the three-dimensional network structure,
The measurement sample quickly penetrates into the micropores of the organic phase having a three-dimensional network structure. In addition, since the organic phase has a three-dimensional network structure, it can have a thickness of several μm or less.
The transfer of the substance to be measured into the organic phase can be completed promptly. Further, when the water-soluble polymer in the organic phase having a three-dimensional network structure has fine pores having a diameter of 500 μm or less, a uniform structure can be obtained. The uniform structure is preferable because it enables more accurate measurement.

The substance measuring device of the present invention can be used for measurement as it is, but it should be laminated on a support in consideration of operability in measurement, use in combination with a reagent such as pH buffer, and the like. You can The laminating method is not particularly limited, and a known method can be used. A preferred example is a method of preparing the substance measuring device of the present invention in advance and adhering it with an appropriate adhesive, double-sided tape or the like. A solution prepared by dissolving an organic solvent, a water-insoluble polymer and a water-soluble polymer in an organic solvent is applied on a support,
As described above, there is a method of drying the organic phase obtained by dissolving the water-insoluble polymer in the organic solvent under the condition that the organic phase is precipitated in a three-dimensional network structure. The concentration of the substance can be measured. A specific example will be described below.

At present, the concentration of the surfactant in the aqueous solution is measured by adding a coloring substance that specifically binds or forms a complex with the surfactant to the aqueous solution, and the surfactant and the coloring substance are both added. It is carried out by extracting from the aqueous solution into a water-insoluble extract, and then measuring the degree of coloring of the extract. Such a method is shown in Japanese Industrial Standards (JIS K 0102 -1986 factory drainage test method), and a methylene blue absorptiometric method, a tetrathiocyanocobaltate (II) acid absorptiometric method and the like are described. Each of these methods has a drawback in that it takes a lot of time and labor because it involves an operation of putting two kinds of liquids in a container and then shaking and mixing for extraction.

The above-mentioned measurement can be carried out using the substance measuring tool of the present invention on the same principle. Taking the methylene blue absorptiometry as an example, it is as follows. That is, when a certain amount of methylene blue is added to a certain amount of the measurement sample aqueous solution and dropped into the substance measuring instrument of the present invention, the ion pair of methylene blue and anionic surfactant is extracted and separated in the organic phase of the substance measuring instrument. To be done. After that, wash away the measurement sample aqueous solution adhering to the substance measuring tool using ion-exchanged water or the like,
The degree of coloring of the remaining organic phase is measured. The degree of coloring can be measured visually or by measuring the amount of transmitted light and the amount of reflected light. As described above, when the substance measuring device of the present invention is used, a specific substance can be measured by a simple operation.

Further, according to the present invention, a water-soluble polymer between organic phases having a three-dimensional network structure formed by dissolving an ionophore showing a detectable response by forming a complex with an ion in an organic solvent and a water-insoluble polymer. When using an ion measuring device having a phase filled therein, the measurement can be performed as follows.

Taking bathocuproine as an ionophore for copper ions as an example, it is as follows.
An aqueous solution of a measurement sample containing copper ions is dropped to an ion measuring instrument in which a water-soluble polymer phase is filled between organic phases having a three-dimensional network structure formed by dissolving bathocuproine and a water-insoluble polymer in an organic solvent. . The measurement sample aqueous solution quickly permeates the entire ion measuring instrument, and copper ions are extracted into the organic phase by bathocuproine existing in the organic phase of the ion measuring instrument. Since the organic phase has a three-dimensional network structure, the film thickness is very thin, and this extraction is performed quickly. Bathocuproine causes a change in its absorption spectrum due to the complex formation with the extracted copper ion. After a certain period of time, the concentration of copper ions contained in the measurement sample aqueous solution was measured by washing away the measurement sample aqueous solution adhering to the ion measuring instrument using ion-exchanged water and measuring the coloring degree of the remaining organic phase. I can know. The conventional membrane extraction method took several hours to complete the response,
With the ion measuring instrument of the present invention, the response can be completed within a few minutes.

Furthermore, between the organic phase of the three-dimensional network structure formed by dissolving the ionophore capable of forming an ion complex, the reporter dye and the water-insoluble polymer in the organic solvent of the present invention,
When the ion measuring tool is filled with the water-soluble polymer phase, the measurement can be performed as follows.

An example of measuring potassium ion in an aqueous solution using valinomycin as an ionophore for potassium and 2,6-dibromo-3′-methoxyindophenol as a reporter dye is as follows. Ions formed by filling a water-soluble polymer phase between organic phases of a three-dimensional network structure formed by dissolving valinomycin, 2,6-dibromo-3'-methoxyindophenol and a water-insoluble polymer in an organic solvent The measurement sample aqueous solution is dropped onto the measuring tool. At this time, the pH of the measurement sample aqueous solution needs to be kept constant by using a pH buffer or the like. The measurement sample aqueous solution quickly permeates the entire ion measuring instrument, and potassium ions are extracted and separated into the organic phase by valinomycin existing in the organic phase of the ion measuring instrument, and at the same time, 2,6-dibromo-3'-methoxy. Indophenol releases hydrogen ions into the measurement sample aqueous solution to develop color. The more potassium ions in the measurement sample aqueous solution, the more potassium ions extracted into the film, and the more amount of the reporter dye that develops color.
As a result, the coloring of the measuring tool according to the amount of potassium ion in the measurement sample aqueous solution is observed, and the concentration of potassium ion can be known from the degree of coloring of the ion measuring tool. Since the organic phase has a three-dimensional network structure, it has a very thin film thickness, and this extraction and release is rapid, and the time required for measurement is short.

Of course, the substance measuring device of the present invention can be applied to other known measuring principles for performing extraction or ion exchange using an organic solvent or a non-water-soluble organic solvent. In either case, there is a feature that measurement can be performed in a short time and with a simple operation.

[0048]

The substance measuring device of the present invention is such that the water-soluble polymer phase is filled between organic phases having a three-dimensional network structure in which a water-insoluble polymer is dissolved in a poorly water-soluble and hardly volatile organic solvent. Due to its basic structure, the sample to be measured can quickly permeate the entire material measuring tool, and the small thickness of the organic phase allows the substance to be measured to move quickly from the sample to the organic phase. It has the feature of being exposed. Therefore, it also has a feature that the extraction and separation operation, which has conventionally required a complicated operation, can be performed by a simple operation in a short time.

Therefore, in the case of highly urgent measurement, that is, in the measurement of blood ion concentration in the field of emergency medical care or in the operating room, a great advantage is brought about. Further, even in general clinical tests, the number of serum or urine specimens to be measured within a limited time is increased, which improves work efficiency and facilitates diagnosis. In addition, because the measurement is complicated, the measurement, which was conventionally performed only in the laboratory, can be performed at the measurement sampling site, and the measurement result can be quickly known.

Further, the substance measuring device of the present invention does not use a conventional porous carrier, and therefore can be manufactured by a simple process. Therefore, it has a feature that it can be manufactured at low cost. From the above points, the industrial value of the present invention is extremely large.

[0051]

EXAMPLES In order to describe the present invention more specifically, examples and comparative examples will be described below, but the present invention is not limited to these examples.

Example 1 In 10 ml of tetrahydrofuran, 300 mg of polyvinyl chloride (average degree of polymerization of 1000) as a water-insoluble polymer, 700 mg of dioctyl sebacate as an organic solvent, and 10 g of polyethylene glycol (average molecular weight of 4000) as a water-soluble polymer were dissolved. Then
This was applied on a transparent polypropylene sheet with a doctor blade to a thickness of 600 μm. When left to stand at room temperature and dried for 1 hour, it gradually began to turn cloudy and finally a white film-like product was obtained.
A material measuring device was obtained by cutting into squares and having a white film-like material fixed to a transparent polypropylene sheet.

This material measuring tool was immersed in 100 ml of ion-exchanged water for 3 minutes, and the organic phase remaining on the transparent polypropylene sheet was observed with an electron microscope. The photograph taken at this time is shown in FIG. It was confirmed that a three-dimensional network structure was formed by the organic phase.

Example 2 Analysis of Nonionic Surfactant 1.5 ml of 0.30M ammonium tetrathiocyanocobaltate (II) aqueous solution was added to 10 ml of various concentrations of heptaoxyethylene dodecyl ether, which is a nonionic surfactant. Stir for 1 minute. 20 μl of this aqueous solution was dropped on the substance measuring instrument of Example 1, and 1 minute later, the substance measuring instrument was washed with about 2 ml of ion-exchanged water. Table 1 shows the results of measuring the amount of reflected light at 330 nm of the material measuring tool using the reflected light amount measuring device shown in FIG. It was shown that the nonionic surfactant can be quantified by a simple operation using the substance measuring instrument of the present invention.

[0055]

[Table 1] Example 3 Ion measuring tool for zinc ion In 10 ml of tetrahydrofuran, 300 mg of polyvinyl chloride (average polymerization degree: 1000) as a water-insoluble polymer, 700 mg of dioctyl sebacate as an organic solvent, 10 g of polyvinylpyrrolidone as a water-soluble polymer, zinc ion 2- (5-Bromo-2-pyridylazo) -5-diethylaminophenol 7.3 mg (21 μmol) was dissolved as an ionophore for use in 600 μm with a doctor blade on a transparent polypropylene sheet.
It was applied thickly. When left at room temperature and dried for 1 hour, it gradually began to become cloudy and finally a reddish brown film was obtained. The film was cut into 1 cm square pieces together with a transparent polypropylene sheet,
An ion measuring device having a film-like material fixed to a transparent polypropylene sheet was obtained. When the ion measuring instrument thus obtained is washed with ion-exchanged water, only an organic phase portion colored reddish brown can be obtained. As shown in Example 1, this organic phase portion had a three-dimensional network structure.

Example 4 Measurement of Zinc Ion The ion measuring instrument prepared in Example 3 was attached to the reflected light quantity measuring device shown in FIG.
l was added dropwise. The amount of reflected light at a wavelength of 553 nm was measured, and the absorbance was calculated based on the amount of reflected light at a zinc chloride concentration of 0 mM. The results are shown in Fig. 3. Also, the time required to reach a certain amount of reflected light was measured. The time required was within the range of 15 to 20 seconds.

Comparative Example 1 In 10 ml of tetrahydrofuran, 300 mg of polyvinyl chloride (average polymerization degree: 1000) as a water-insoluble polymer, 700 mg of dioctyl sebacate as an organic solvent, and 2- (5-bromo-2-) as an ionophore for zinc ions. Pyridylazo) -5-diethylaminophenol 7.3 mg (21 μmol) was dissolved and this was placed on a transparent polypropylene sheet with a doctor blade.
It was applied to a thickness of 600 μm. Let stand at room temperature for 1 hour to dry,
A transparent reddish brown film-like material was obtained. This film-like material was cut into 1 cm square pieces together with a transparent polypropylene sheet to obtain a measuring tool in which the film-like material was fixed to the transparent polypropylene sheet.

By using this measuring instrument in the same manner as in Example 4, various zinc chloride concentration aqueous solutions were measured. However, a certain amount of reflected light was not reached even after 5 minutes had passed since the aqueous solution was dropped, so that measurement could not be performed.

Comparative Example 2 The measuring device prepared in Example 3 was washed with ion-exchanged water and then dried to remove the water-soluble polymer, and the water-insoluble polymer was dissolved in an organic solvent having a three-dimensional network structure. The measuring tool which consists of it was produced. This measuring tool was operated in the same manner as in Example 4 to measure various zinc chloride concentration aqueous solutions. However, even after dropping the aqueous solution, the aqueous solution does not penetrate into the micropores of the measuring tool,
Almost no color change was seen. The measurement could not be performed because the amount of reflected light did not reach a certain amount even after 5 minutes.

From Examples 3 and 4, Comparative Example 1 and Comparative Example 2,
It was shown that the water-soluble polymer needs to be filled between the organic phases of the three-dimensional network structure in order to perform the measurement in a short time.

Comparative Example 3 A tetrahydrofuran solution was coated on a transparent polypropylene sheet with the same composition and operation as in Example 3, and was rapidly dried using a blower. The solution became cloudy rapidly. After that, it was dried for 1 hour to obtain an opaque reddish brown film-like material. This film-like material was cut into 1 cm squares together with a transparent polypropylene sheet to obtain a measuring tool in which lumps were fixed to the transparent polypropylene sheet.

Using this measuring instrument, the same procedure as in Example 4 was carried out to measure various zinc chloride concentration aqueous solutions. The results are shown in Fig. 4. The drop of the aqueous solution opened some holes of about 0.1 mm in the measuring tool, and some parts did not allow the light to pass through the film, so the response obtained was very small, indicating that it was not suitable for measurement. It was

From Examples 3, 4 and Comparative Example 3, in the production of the substance measuring device of the present invention laminated on a support, an organic phase comprising at least a poorly water-soluble and hardly volatile organic solvent and a water-insoluble polymer was used. It was shown that it is necessary to perform the precipitation operation under the condition that the precipitation of water begins before the precipitation of the water-soluble polymer, and to fill the water-soluble polymer phase between the organic phases of the three-dimensional network structure. .

Example 5 Ion measuring tool for sodium ion: 10 ml of chloroform, 300 mg of polystyrene as a water-insoluble polymer, 600 mg of o-nitrophenyl octyl ether as an organic solvent, and 10 g of polyethylene glycol (average molecular weight of 6000) as a water-soluble polymer. 5,11,17,23-tetra-t-butyl-25,26,27,28-tetrakis (ethoxycarbonyl) -methoxy-calix as sodium ionophore
[4] Allene 18.4 mg (18.4 μmol), 2,6-dibromo-3'-methoxyindophenol 7.1 mg (18.4 μmol) as a dye were dissolved and applied on a transparent polypropylene sheet with a doctor blade to a thickness of 600 μm. did. When left to stand at room temperature and dried, the turbidity gradually increased, and finally a brown-white film was obtained. This film was cut into 1 cm square pieces with a transparent polypropylene sheet, and a brown-white film was obtained. To obtain an ion measuring device fixed to a transparent polypropylene sheet.

Example 6 The ion measuring instrument prepared in Example 5 was mounted on the reflected light quantity measuring apparatus shown in FIG. 2, and 2-morpholinoethanesulfonic acid 10 mM buffer solution (pH 5.5 with water) having various sodium chloride concentrations was used. (Prepared with potassium oxide) 25 μl was added dropwise. The amount of reflected light at a wavelength of 670 nm was measured, and the absorbance was calculated based on the amount of reflected light when the sodium chloride concentration was 0 mM. The results are shown in Fig. 5. From FIG. 5, it can be seen that sodium ion can be measured at 10 to 0.1 mM. Also, the time required to reach a certain amount of reflected light was measured. The time required was within the range of 15 to 20 seconds.

Comparative Example 4 In 10 ml of tetrahydrofuran, 300 mg of polyvinyl chloride (average polymerization degree: 1000) as a water-insoluble polymer and o as an organic solvent
-Nitrophenyl octyl ether 600 mg, 5,11,17,23-tetra-t-butyl-25,26,2 as sodium ionophore
7,28- Tetrakis (ethoxycarbonyl) -methoxy-calix [4] arene 18.4mg (18.4μmol), 2,6 as dye
-Dibromo-3'-methoxyindophenol 7.1 mg (18.4 μm
ol) was dissolved and this was applied onto a transparent polypropylene sheet with a doctor blade to a thickness of 600 μm. It was left to stand at room temperature and dried to obtain a measuring instrument as a uniform transparent brown film.

The measuring device manufactured in this manner was attached to the reflected light quantity measuring device shown in FIG. 2, and 2-morpholinoethanesulfonic acid 10 mM buffer solution (pH 5.5) having various sodium chloride concentrations was used.
(Prepared with potassium hydroxide) was added dropwise. Wavelength 670
The amount of reflected light in nm was measured, but a constant amount of reflected light was not reached even after 3 minutes. It was not possible to carry out the measurement under the same conditions as in Example 6, which had a slow response speed.

From Example 6 and Comparative Example 5, it was shown that the ion measuring tool of the present invention can be used for quick measurement.

Comparative Examples 5 to 10 and Examples 7 to 227 Non-water-soluble polymers shown in Table 2, organic solvents, water-soluble polymers,
Using the same sodium ionophore and dye as in Example 5, the same operation as in Example 5 was carried out to produce an ion measuring instrument for sodium ions. The prepared measuring tool was attached to the reflected light quantity measuring device shown in Fig. 2, and the sodium chloride concentration was 10 mM.
25 μl of 2-morpholinoethanesulfonic acid 10 mM buffer (prepared with potassium hydroxide to pH 5.5) was added dropwise. Wavelength 670nm
The amount of reflected light was measured, and the time until the amount of reflected light became constant at that time was measured. The results are shown in Table 2. As can be seen from Examples 5 to 10, no prompt response was obtained even if any of the water-insoluble polymer, the organic solvent, and the water-soluble polymer was lacking. In addition, Examples 7 to 22 showed that a quick response was obtained in the combination of various water-insoluble polymers, organic solvents, and water-soluble polymers.

[0070]

[Table 2]

[0071]

[Table 3]

[Brief description of drawings]

FIG. 1 is an electron micrograph of the structure of the organic phase after the substance measuring device manufactured in Example 1 was washed with ion-exchanged water.

FIG. 2 is a diagram showing a configuration of a reflected light amount measuring device used in Examples and Comparative Examples.

FIG. 3 is a diagram showing the relationship between the measured zinc ion concentration and the measured absorbance in Example 4.

FIG. 4 is a diagram showing a relationship between a measured zinc ion concentration and a measured absorbance in Comparative Example 3.

5 is a diagram showing the relationship between the measured sodium ion concentration and the measured absorbance in Example 6. FIG.

[Explanation of symbols]

1 xenon lamp 2 condensing lens 3 projecting optical fiber 4 units (quartz plate) 5 white reflecting plate 6 substance measuring tool of the present invention 7 light receiving optical fiber 8 instant multi-photometer (MCPD-10 manufactured by Otsuka Electronics Co., Ltd.)
00 type) 9 Data processing device (Otsuka Electronics Co., Ltd.)

Claims (5)

[Claims] 1. An (A) organic phase obtained by dissolving a water-insoluble polymer in a sparingly water-soluble sparingly volatile organic solvent and (B) a water-soluble polymer phase, wherein (A) the organic phase is three-dimensional. 1. A substance measuring device having a network structure, wherein (A) an organic phase is filled with (B) a water-soluble polymer phase. 2. A substance measuring instrument comprising the substance measuring instrument according to claim 1 laminated on a support. 3. A poorly water-soluble hardly volatile organic solvent, a water-insoluble polymer and a water-soluble polymer dissolved in an organic solvent are applied on a support, and then the poorly water-soluble hardly volatile organic solvent is applied. 3. The organic solvent is evaporated under the condition that the precipitation of the organic phase consisting of the water-insoluble polymer and the precipitation of the water-soluble polymer start before or simultaneously with the precipitation of the water-soluble polymer.
A method for manufacturing the described substance measuring tool. 4. (A) An ionophore that forms a detectable response by forming a complex with an ion or an ionophore that forms a complex with an ion in a poorly water-soluble and hardly volatile organic solvent and an ionophore that forms a complex with the ion, and is detectable by interacting with the complex formation A dye showing a response, and an organic phase formed by dissolving a water-insoluble polymer and (B) a water-soluble polymer phase, and (A) the organic phase has a three-dimensional network structure and the (A) organic phase An ion measuring tool characterized in that (B) is filled with a water-soluble polymer phase. 5. An ion measuring instrument comprising the ion measuring instrument according to claim 4 laminated on a support.