JPH08120850A - Waterproof sheet, and waterproofing therewith - Google Patents
Waterproof sheet, and waterproofing therewithInfo
- Publication number
- JPH08120850A JPH08120850A JP28580994A JP28580994A JPH08120850A JP H08120850 A JPH08120850 A JP H08120850A JP 28580994 A JP28580994 A JP 28580994A JP 28580994 A JP28580994 A JP 28580994A JP H08120850 A JPH08120850 A JP H08120850A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- organic solvent
- asphalt
- rubber
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【技術分野】本発明は、新規なアスファルト系の防水シ
ートとそれを用いた防水施工法に関する。TECHNICAL FIELD The present invention relates to a novel asphalt-based waterproof sheet and a waterproof construction method using the same.
【０００２】[0002]
【従来技術】従来防水の主流は、施工現場で２５０〜３
００℃に加熱したアスファルトを接着材として用いなが
らアスファルトルーフィングを積層一体化していく熱工
法であるが、アスファルトを溶解させる際にケムリ・匂
いが発生し、かつ高温アスファルトによる技能員のやけ
どの危険がある。2. Description of the Related Art The mainstream of conventional waterproofing is 250 to 3 at the construction site.
This is a thermal method in which asphalt roofing is laminated and integrated while using asphalt heated to 00 ° C as an adhesive material, but when melting asphalt, there is a scent and smell, and there is a risk of burns to technicians due to high temperature asphalt. is there.
【０００３】これらの問題を解決する有力な手段の一つ
に粘着材を設けたアスファルトルーフィングを剥離紙を
剥がして貼着していく自着工法がある。この工法の場
合、現場で発生する多量の剥離紙の取扱いが問題となっ
ている。One of the effective means for solving these problems is a self-adhesion method in which asphalt roofing provided with an adhesive is peeled off from the release paper and attached. In the case of this construction method, the handling of a large amount of release paper which is generated on site poses a problem.
【０００４】剥離紙を使用しない工法としては、施工時
に主として加硫ゴムや塩化ビニル系樹脂からなるシート
の裏面に、コンタクト型接着材を塗布し、オープンタイ
ムをとってから、予めコンタクト型接着材と同種のコン
タクト型接着材をプライマーとして塗っておいた下地に
貼着させる接着材工法がある。しかし、接着材工法も防
水シート本体への接着材塗布や、オープンタイムを要す
る点が煩わしく作業能率が低い。しかも、接着材の量も
技能員がローラー、刷毛等により塗布するためバラツキ
が大きく、接着信頼性に不安を残している。As a construction method which does not use release paper, a contact type adhesive is applied to the back surface of a sheet mainly made of vulcanized rubber or vinyl chloride resin at the time of construction, an open time is taken, and then the contact type adhesive is preliminarily used. There is an adhesive material construction method in which the same type of contact type adhesive material is applied as a primer to a base. However, the adhesive material construction method is also troublesome in that the adhesive material is applied to the main body of the waterproof sheet and that the open time is required, and the work efficiency is low. Moreover, the amount of the adhesive material varies greatly because the technician applies it with a roller, a brush or the like, and there remains concern about the adhesive reliability.
【０００５】加硫ゴムシートなどの防水シート裏面に予
め工場で接着材を塗布した製品もあるが、ロール状にま
いた場合、接着材を塗布していない面に接着材がブロッ
キングしてしまうため、剥離紙が必要となり、やはり、
剥離紙の取扱、廃棄の問題が残る。There is a product in which an adhesive is applied to the back surface of a waterproof sheet such as a vulcanized rubber sheet in advance at the factory. However, when the adhesive is applied in a roll, the adhesive may block the surface not applied with the adhesive. , Release paper is required, after all,
The problem of handling and discarding release paper remains.
【０００６】[0006]
【本発明の目的】本発明の目的は、施工現場で廃材（剥
離紙）が発生せず、かつ現場作業（オープンタイム不
要、プライマー不要）が少なくてすみ、効率良く防水層
が形成できる新規な防水シートとそれを用いた施工法を
提供する点にある。An object of the present invention is to provide a novel waterproof layer which does not generate waste materials (release paper) at the construction site, requires little on-site work (no open time, no primer), and can efficiently form a waterproof layer. The point is to provide a waterproof sheet and a construction method using it.
【０００７】[0007]
【目的を達成するための手段】本発明の第一は、上から
順に、ブロッキング防止層、アスファルト層、基材層、
アスファルト層、全面粘着層、有機溶剤可溶性のプラス
チックもしくはゴムよりなるフィルム層、よりなる積層
物であることを特徴とする防水シートに関する。The first aspect of the present invention is, in order from the top, an antiblocking layer, an asphalt layer, a substrate layer,
The present invention relates to a waterproof sheet, which is a laminate comprising an asphalt layer, an entire surface adhesive layer, a film layer made of an organic solvent-soluble plastic or rubber.
【０００８】本発明の第二は、上から順に、ブロッキン
グ防止層、アスファルト層、基材層、アスファルト層、
有機溶剤に対して不溶性のプラスチックフィルム層、粘
着材がない部分が連通している部分粘着層、有機溶剤可
溶性のプラスチックもしくはゴムよりなるフィルム層、
よりなる積層物であることを特徴とする防水シートに関
する。The second aspect of the present invention is, in order from the top, an antiblocking layer, an asphalt layer, a substrate layer, an asphalt layer,
A plastic film layer insoluble in an organic solvent, a partial adhesive layer in which a part without an adhesive material is in communication, a film layer made of an organic solvent-soluble plastic or rubber,
The present invention relates to a waterproof sheet, which is a laminate made of
【０００９】本発明の第三は、上から順に、有機溶剤可
溶性のプラスチックもしくはゴムよりなるフィルムより
なるブロッキング防止層、全面粘着層、アスファルト
層、基材層、アスファルト層、全面粘着層、有機溶剤可
溶性のプラスチックもしくはゴムよりなるフィルム層、
よりなる積層物であることを特徴とする防水シートに関
する。The third aspect of the present invention is, in order from the top, an anti-blocking layer consisting of a film made of an organic solvent-soluble plastic or rubber, an overall adhesive layer, an asphalt layer, a base material layer, an asphalt layer, an overall adhesive layer, an organic solvent. A film layer made of soluble plastic or rubber,
The present invention relates to a waterproof sheet, which is a laminate made of
【００１０】本発明の第四は、上から順に有機溶剤可溶
性のプラスチックもしくはゴムよりなるフィルムよりな
るブロッキング防止層、全面粘着層、アスファルト層、
基材層、アスファルト層、有機溶剤に対して不溶性のプ
ラスチックフィルム層、粘着材がない部分が連通してい
る部分粘着層、有機溶剤可溶性のプラスチックもしくは
ゴムよりなるフィルム層、よりなる積層物であることを
特徴とする防水シートに関する。A fourth aspect of the present invention is, in order from the top, an anti-blocking layer consisting of a film made of an organic solvent-soluble plastic or rubber, a full surface adhesive layer, an asphalt layer,
A laminate comprising a base material layer, an asphalt layer, a plastic film layer insoluble in an organic solvent, a partial adhesive layer in which parts without an adhesive are in communication, a film layer made of an organic solvent-soluble plastic or rubber, The present invention relates to a waterproof sheet.
【００１１】本発明の第五は、（ａ）有機溶剤単独 あるいは （ｂ）アスファルト、改質アスファルトおよび前
記有機溶剤可溶性のプラスチックもしくはゴムよりなる
フィルムに対して親和性と接着性に優れたゴムまたはプ
ラスチックよりなる群から選ばれた１種以上の材料の有
機溶剤溶液 を、請求項１または２記載の防水シートの有機溶剤可溶
性のプラスチックもしくはゴムよりなるフィルム層に塗
布しながら、あるいは下地に塗布しながら、請求項１ま
たは２記載の防水シートにおける有機溶剤可溶性のプラ
スチックもしくはゴムよりなるフィルム層を下地に向け
て接着していくことを特徴とする防水工法に関する。A fifth aspect of the present invention is a rubber excellent in affinity and adhesiveness with respect to (a) an organic solvent alone or (b) a film made of asphalt, modified asphalt and the organic solvent-soluble plastic or rubber, or An organic solvent solution of at least one material selected from the group consisting of plastics is applied to the undercoat layer of the waterproof sheet according to claim 1 or 2 while being applied to the organic solvent soluble plastic or rubber film layer. However, the present invention relates to a waterproofing method characterized in that a film layer made of an organic solvent-soluble plastic or rubber in the waterproof sheet according to claim 1 or 2 is adhered toward a base.
【００１２】本発明の第六は、請求項３または４記載の
防水シートを請求項５記載の防水工法で施工した後、そ
の表面に （ａ）有機溶剤単独 あるいは （ｂ）アスファルト、改質アスファルトおよび前
記有機溶剤可溶性のプラスチックもしくはゴムよりなる
フィルムに対して親和性と接着性に優れたゴムまたはプ
ラスチックよりなる群から選ばれた１種以上の材料の有
機溶剤溶液 を塗布しながら、請求項１記載の防水シートの有機溶剤
可溶性のプラスチックフィルム面を下に向けて接着する
ことを特徴とする防水工法に関する。In a sixth aspect of the present invention, after applying the waterproof sheet according to claim 3 or 4 by the waterproof method according to claim 5, (a) an organic solvent alone or (b) asphalt or modified asphalt. And applying an organic solvent solution of at least one material selected from the group consisting of rubber or plastic having excellent affinity and adhesiveness to the organic solvent-soluble plastic or rubber film. The present invention relates to a waterproofing method, characterized in that an organic solvent-soluble plastic film surface of the waterproof sheet is bonded downward.
【００１３】前記本発明はいずれも粘着層面を、有機溶
剤に対して速やかに溶融するプラスチックフィルムでも
って被覆し、該フィルムを有機溶剤または粘着性成分を
含む有機溶剤溶液によって溶解させ、溶剤が完全に揮発
する以前に（フィルムが溶解状態を呈している間に）、
下地に貼着することにより貼着層面が下地に直接接触か
つ密着し、溶剤の揮発とともに短時間で所定の接着力を
発現させることをねらったものである。In any of the above inventions, the surface of the adhesive layer is coated with a plastic film which is rapidly melted in an organic solvent, and the film is dissolved by an organic solvent or an organic solvent solution containing an adhesive component, and the solvent is completely removed. Before it volatilizes (while the film is in the molten state),
By sticking to the base, the surface of the adhesive layer is brought into direct contact and close contact with the base, and it is aimed to develop a predetermined adhesive force in a short time as the solvent volatilizes.
【００１４】粘着層は、下地面から発生する水蒸気によ
る防水層のフクレが懸念されない場合は全面粘着層で良
い（第一発明）が、そうでない場合（第二発明）は粘着
層がない部分が互いに全て連通した状態になるように粘
着材が部分的に施された構成を適用する。この場合、粘
着部分のみにフィルムを被覆することはできないので、
フィルムを全面にわたって被覆することになるが、粘着
材がない部分のプラスチックフィルムが溶剤で溶解した
後、その溶剤によって、粘着層の下のアスファルト層が
溶解し、下地にブロッキングしフクレ防止効果が低下す
る不安がある。そのため、アスファルト層と粘着層との
間に溶剤に不溶のプラスチックフィルム層を設ける必要
がある。The pressure-sensitive adhesive layer may be a full-scale pressure-sensitive adhesive layer (first invention) when there is no concern of blistering of the waterproof layer due to water vapor generated from the underlying surface, but in other cases (second invention), there is no pressure-sensitive adhesive layer. A structure in which an adhesive material is partially applied so that they are all in communication with each other is applied. In this case, it is not possible to coat the film only on the adhesive part,
The film covers the entire surface, but after the plastic film in the part without the adhesive is dissolved in the solvent, the asphalt layer below the adhesive layer is dissolved by the solvent, blocking the base and reducing the anti-blister effect. I am worried about Therefore, it is necessary to provide a plastic film layer insoluble in a solvent between the asphalt layer and the adhesive layer.
【００１５】粘着層は溶剤で活性化されるのでさほど厚
くする必要はないが、０．３〜１．０ｍｍ、好ましくは
０．４〜０．６ｍｍである。The pressure-sensitive adhesive layer is activated by a solvent, so it does not need to be so thick, but it is 0.3 to 1.0 mm, preferably 0.4 to 0.6 mm.
【００１６】前記粘着材層を構成する粘着材は合成樹脂
や合成ゴム、天然ゴム、再生ゴム等を主原料として調合
された汎用の粘着材であることができる。なお、本発明
はアスファルト防水工法に関することからアスファルト
に合成高分子物質を添加して得られる粘着材が望まし
い。粘着材の具体例を示すと、つぎのような組成にする
ことができる。 ＳＢＳ（スチレン・ブタジエン・ス チレン・ブロック共重合体） １０〜３０重量部とくに２０重量部 石油樹脂（粘着付与剤） ５〜２０重量部とくに１０重量部 アスファルト ３０〜７０重量部とくに４０重量部 プロセスオイル １０〜４０重量部とくに３０重量部The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer may be a general-purpose pressure-sensitive adhesive prepared by using synthetic resin, synthetic rubber, natural rubber, recycled rubber or the like as a main raw material. Since the present invention relates to an asphalt waterproofing method, an adhesive material obtained by adding a synthetic polymer substance to asphalt is desirable. Specific examples of the adhesive material can have the following compositions. SBS (styrene / butadiene / styrene / block copolymer) 10 to 30 parts by weight, especially 20 parts by weight Petroleum resin (tackifier) 5 to 20 parts by weight, especially 10 parts by weight Asphalt 30 to 70 parts by weight, especially 40 parts by weight Process Oil 10-40 parts by weight, especially 30 parts by weight
【００１７】使用する有機溶剤は、使用する有機溶剤可
溶性のプラスチックまたはゴムよりなるフィルム層をま
たたく間に溶解すること及び粘着層、アスファルト層に
拡散して揮散することが好ましいので、一般に芳香族系
炭化水素やハロゲン化炭化水素が好ましいが、これに限
定されるものではない。とりわけ、毒性の少ないソルベ
ントナフサ、トルエン、キシレン、シクロヘキサンある
いは混合溶剤等が使用できるが、アスファルト類と相溶
性のあるものが好ましく揮発性・毒性の点でトルエンが
特に好ましい。同一施工現場で火気の使用が見込まれる
場合には不燃性であるハロゲン化炭化水素系が推奨で
き、毒性の少ないジクロルペンタン、トリクロルエチレ
ンなどが好ましい。The organic solvent to be used is preferably dissolved in the organic solvent-soluble plastic or rubber film layer in a short time, and is preferably diffused and volatilized in the adhesive layer and the asphalt layer. Hydrogen and halogenated hydrocarbons are preferable, but not limited thereto. In particular, solvent naphtha, toluene, xylene, cyclohexane, or a mixed solvent having low toxicity can be used, but those having compatibility with asphalts are preferable, and toluene is particularly preferable from the viewpoint of volatility and toxicity. If fire is expected to be used at the same construction site, non-flammable halogenated hydrocarbons can be recommended, and dichloropentane, trichlorethylene, etc., which are less toxic, are preferred.
【００１８】有機溶剤単独ではなく、アスファルト、改
質アスファルトおよび前記有機溶剤可溶性のプラスチッ
クもしくはゴムよりなるフィルムに対して親和性と接着
性に優れたゴムまたはプラスチックよりなる群から選ば
れた１種以上の材料の有機溶剤溶液を用いるとそれ自身
が適度の粘性および初期接着力を有するので、施工直後
でも防水シート本体を仮固定する力が発現する。初期接
着力が非常に小さい場合には防水シートがロール状に巻
かれた状態で市場に供給されているため、往々にしてシ
ート端部がその巻きぐせを反映してハネや浮きが発生す
るが、この有機溶剤溶液を使用すれば、初期接着力が充
分発揮されるので、このようなハネや浮きを完全に防止
することができる。とくにプラスチックフィルムがポリ
スチレンやポリエステル（ポリエチレンテレフタレー
ト；ＰＥＴ）の場合には、クロロプレンやＮＢＲなどの
有機溶剤溶液が好ましい。One or more selected from the group consisting of rubber or plastic having excellent affinity and adhesiveness to asphalt, modified asphalt, and a film made of the above-mentioned organic solvent-soluble plastic or rubber, not the organic solvent alone. When an organic solvent solution of the above material is used, the solution itself has an appropriate viscosity and an initial adhesive force, so that a force for temporarily fixing the waterproof sheet main body is developed even immediately after construction. If the initial adhesive strength is very small, the tarpaulin is supplied to the market in a rolled state, so the edges of the sheet often reflect the curl and cause splashing or floating. When this organic solvent solution is used, the initial adhesive strength is sufficiently exerted, so that such splashing and floating can be completely prevented. Particularly when the plastic film is polystyrene or polyester (polyethylene terephthalate; PET), an organic solvent solution such as chloroprene or NBR is preferable.
【００１９】粘着層面を被覆する有機溶剤可溶性のプラ
スチックもしくはゴムよりなるフィルムとしては、有機
溶剤に対して溶解性の高いポリスチレン、アクリル樹
脂、アセタール樹脂、ポリ塩化ビニル、ポリブタジエ
ン、塩素化ポリエチレン等が挙げられるが、これに限定
されるものではない。しかし前述の例示した溶剤を用い
る場合には、これらの溶剤に対してポリスチレンが最も
すみやかに溶解するので特に好ましい。As the film made of an organic solvent-soluble plastic or rubber for coating the surface of the adhesive layer, polystyrene, acrylic resin, acetal resin, polyvinyl chloride, polybutadiene, chlorinated polyethylene and the like, which have high solubility in organic solvents, can be mentioned. However, the present invention is not limited to this. However, when the above-exemplified solvents are used, polystyrene is most preferably dissolved in these solvents, which is particularly preferable.
【００２０】前記フィルムの厚さは薄い方が早く溶解す
るので好ましいが、取り扱い時の破損の回避を考慮すれ
ば通常８〜３０μ、特に好ましくは１２〜２０μである
が、これに限定されるものではない。It is preferable that the thickness of the above-mentioned film is thin because it dissolves quickly. However, in consideration of avoidance of breakage during handling, it is usually 8 to 30 μ, and particularly preferably 12 to 20 μ, but it is not limited to this. is not.
【００２１】本発明のブロッキング防止層は、プラスチ
ック層またはゴム層であることもできるし、鉱物粉粒な
どの微粒子体層であることもできる。前記プラスチック
層またはゴム層としては、ポリエチレン、ポリプロピレ
ン、エチレン−酢酸ビニル共重合体、ポリスチレン、ポ
リエチレンテレフタレート、ポリブタジエンなどのフィ
ルムを挙げることができるが、一般的にポリエチレン、
ポリプロピレンおよびポリエチレンテレフタレートが比
較的安価で好適である。ブロッキング防止層として、プ
ラスチック層やゴム層を用いる場合には、ブロッキング
防止層とアスファルト層との接着性を確実にするため、
アンカーコート層を設けたり、コロナ放電処理や、さら
にコロナ放電処理した上にアンカーコート層を設け接着
性を改良することが好ましい。また、ブロッキング防止
層の耐候性を向上させるために、ブロッキング防止層を
構成する組成物中に紫外線防止剤、安定剤および／また
は濃色顔料を配合することができる。あるいはブロッキ
ング防止層を複層構造とし、表面層を耐候性プラスチッ
ク層とすることもできる。例えば、紫外線安定剤と濃色
染顔料を含むポリウレタン系インクを用いて表面層を形
成することができる。The anti-blocking layer of the present invention may be a plastic layer or a rubber layer, or may be a fine particle layer such as mineral powder. Examples of the plastic layer or the rubber layer include polyethylene, polypropylene, ethylene-vinyl acetate copolymer, polystyrene, polyethylene terephthalate, and polybutadiene films, but generally polyethylene,
Polypropylene and polyethylene terephthalate are relatively inexpensive and suitable. When using a plastic layer or a rubber layer as the anti-blocking layer, in order to ensure the adhesiveness between the anti-blocking layer and the asphalt layer,
It is preferable to provide an anchor coat layer, perform corona discharge treatment, or further perform an corona discharge treatment and then provide an anchor coat layer to improve adhesion. Further, in order to improve the weather resistance of the anti-blocking layer, an ultraviolet protective agent, a stabilizer and / or a dark pigment can be added to the composition constituting the anti-blocking layer. Alternatively, the antiblocking layer may have a multilayer structure and the surface layer may be a weather resistant plastic layer. For example, the surface layer can be formed by using a polyurethane-based ink containing an ultraviolet stabilizer and a dark dye / pigment.
【００２２】[0022]
実施例１（請求項１および５に対応：図１参照） ブロッキング防止層として、 ポリウレタン系インクを塗布したポリエ チレンテレフタレート（ＰＥＴ）フィルム ：厚さ １２μｍ アスファルト層２として、 改質アスファルト ：厚さ０．３ｍｍ 組成 ＳＢＳ １３ｗｔ％ ストレートアスファルト（１８０〜２００）８７ｗｔ％ 基材層３として、 ポリエステル不織布（ポリエステルスパンボンド） １２０ｇ／ｍ2 アスファルト層４として、 前記２のアスファルト層と同一のもの ：厚さ０．３ｍｍ 全面粘着層５として、 下記組成の粘着材 ：厚さ０．５ｍｍ ＳＢＳ ２５ｗｔ％ 粘着付与剤 ２０ｗｔ％ プロセスオイル ２０ｗｔ％ ストレートアスファルト（１８０〜２００）３５ｗｔ％ 有機溶剤可溶性プラスチックフィルム層６として、 ポリスチレンフィルム ：厚さ ２０μｍ 前記層構成の防水シートをポリスチレンフィルム面を上
にして仮敷きし、ウールローラー刷毛を用いてキシレン
を１００ｇ／ｍ2塗布し、すぐにひっくりかえして下地
に貼着した。Example 1 (corresponding to claims 1 and 5: see FIG. 1) Polyethylene terephthalate (PET) film coated with polyurethane-based ink as an anti-blocking layer: thickness 12 μm Asphalt layer 2, modified asphalt: thickness 0 0.3 mm composition SBS 13 wt% straight asphalt (180 to 200) 87 wt% As the base material layer 3, polyester nonwoven fabric (polyester spun bond) 120 g / m 2 Asphalt layer 4, the same as the asphalt layer 2 above: Thickness 0 .3 mm Adhesive material having the following composition as the entire surface adhesive layer 5: thickness 0.5 mm SBS 25 wt% tackifier 20 wt% process oil 20 wt% straight asphalt (180 to 200) 35 wt% organic solvent soluble plastic film layer 6 Lenfilm: a waterproof sheet having a thickness of 20μm wherein the layer structure is laid provisionally in the above polystyrene film surface, xylene was 100 g / m 2 applied with a wool roller brush, was stuck to the substrate is turned over immediately.
【００２３】実施例２（請求項１と５に対応） 下地に トルエン１５％ ジクロルメタン５５％ ７０ｗｔ％ クロロプレン ３０ｗｔ％ よりなる組成の有機溶剤（粘度：１３００ｃｐｓ／２５
℃）を１００ｇ／ｍ2の割合で塗布しながら、実施例１
の構成の防水シートをプラスチックフィルム層を下にし
て下地に接着した。Example 2 (corresponding to claims 1 and 5) An organic solvent having a composition of 15% toluene, 55% dichloromethane 55% 70 wt% chloroprene 30 wt% as a base (viscosity: 1300 cps / 25)
While ° C.) was applied at a rate of 100 g / m 2, Example 1
The waterproof sheet having the above constitution was adhered to the substrate with the plastic film layer facing down.
【００２４】評価 実施例１，２ともにその後接着力を測定したが、粘着材
の持っている本来の接着力が施工後、わずか約３時間で
発現したことは驚くべきことであった（１８０°ピーリ
ングテスト、テストスピード １００ｍｍ／ｍｉｎ）。 １ｈｒ後ピーリング強度 ０．３ｋｇ／ｃｍ ３ｈｒ後ピーリング強度 １．２ｋｇ／ｃｍ ２４ｈｒ後ピーリング強度 １．３ｋｇ／ｃｍ フランク＊ １．３ｋｇ／ｃｍ ＊（粘着層面にハクリシを設け、ハクリシ除去して貼り
合わせ粘着材の本来の接着力とした。）Evaluation In both Examples 1 and 2, the adhesive strength was measured thereafter, and it was surprising that the original adhesive strength of the adhesive material was developed only about 3 hours after the construction (180 °). Peeling test, test speed 100 mm / min). Peeling strength after 1 hr 0.3 kg / cm Peeling strength after 3 hr 1.2 kg / cm Peeling strength after 24 hr 1.3 kg / cm Frank * 1.3 kg / cm * (Provide the adhesive on the adhesive layer surface to remove the adhesive and apply the adhesive The original adhesive strength of the material.)
【００２５】実施例３（請求項２と５に対応：図２参
照） ブロッキング防止層１として、 ウレタン系インク塗布した二軸延伸 ポリプロピレンフィルム ：厚さ １２μｍ アスファルト層２として、 改質アスファルト ：厚さ０．３ｍｍ 組成 ＳＢＳ １３ｗｔ％ ストレートアスファルト（１８０〜２００）８７ｗｔ％ 基材層３として、 ポリエステル不織布（ポリエステルスパンボンド） １２０ｇ／ｍ2 アスファルト層４として、 改質アスファルト層 ：厚さ０．３ｍｍ 組成 ＳＢＳ １３ｗｔ％ ストレートアスファルト（１８０〜２００）８７ｗｔ％ 有機溶剤不溶性プラスチックフィルム層７として、 ポリエステル（ＰＥＴ）フィルム ：厚さ ２０μｍ 部分粘着層５’として、 ストライプ状の粘着層 ：厚さ０．５ｍｍ 有機溶剤可溶性プラスチックフィルム層６として、 ポリスチレンフィルム ：厚さ ２０μｍ 前記構成の防水シートを実施例１と同様の方法で下地に
施工した。ただし、施工に当ってはすべての防水層にお
いて粘着材が塗布されていない部分が連通するように注
意深く作業を行う必要がある。時間経過に伴う粘着力の
発現は実施例１と２と同じであり、かつ実施例３のもの
は下地に湿気が残っていても、この湿分がストライプ状
の非粘着層を通って放散されるので、防水層のフクレは
発生しない。Example 3 (corresponding to claims 2 and 5: see FIG. 2) As the anti-blocking layer 1, biaxially stretched polypropylene film coated with urethane ink: thickness 12 μm asphalt layer 2, modified asphalt: thickness 0.3 mm composition SBS 13 wt% straight asphalt (180 to 200) 87 wt% As the base material layer 3, polyester nonwoven fabric (polyester spun bond) 120 g / m 2 Asphalt layer 4, modified asphalt layer: thickness 0.3 mm Composition SBS 13 wt% Straight asphalt (180 to 200) 87 wt% As an organic solvent insoluble plastic film layer 7, a polyester (PET) film: 20 μm in thickness As a partial adhesive layer 5 ′, a striped adhesive layer: 0.5 mm in organic solvent soluble Plastic As the film layer 6, a polystyrene film: it was constructed on the base with a thickness 20μm the configuration similar manner tarpaulin Example 1. However, in the construction, it is necessary to carefully perform work so that all the waterproof layers are connected to the parts to which the adhesive is not applied. The development of adhesive force with the passage of time is the same as in Examples 1 and 2, and in Example 3, even if moisture remains on the substrate, this moisture is diffused through the striped non-adhesive layer. Therefore, blistering of the waterproof layer does not occur.
【００２６】実施例４（請求項３と６に対応：図３参
照） ブロッキング防止層１として、 ポリスチレンフィルム ：厚さ ２０μｍ 全面粘着層８として、 下記組成の粘着材料 ：厚さ０．５ｍｍ ＳＢＳ ２５ｗｔ％ 粘着付与剤 ２０ｗｔ％ プロセスオイル ２０ｗｔ％ ストレートアスファルト（１８０〜２００）３５ｗｔ％ アスファルト層２として、 改質アスファルト ：厚さ０．３ｍｍ 組成 ＳＢＳ １３ｗｔ％ ストレートアスファルト（１８０〜２００）８７ｗｔ％ 基材層３として、 ポリエステルスパボンド １２０ｇ／ｍ2 アスファルト層４として、 改質アスファルト層 ：厚さ０．３ｍｍ 組成 ＳＢＳ １３ｗｔ％ ストレートアスファルト（１８０〜２００）８７ｗｔ％ 全面粘着層５として、 下記組成の粘着材 ：厚さ０．５ｍｍ ＳＢＳ ２５ｗｔ％ 粘着付与剤 ２０ｗｔ％ プロセスオイル ２０ｗｔ％ ストレートアスファルト（１８０〜２００）３５ｗｔ％ 有機溶剤可溶性プラスチックフィルム層６として、 ポリスチレンフィルム ：厚さ ２０μｍ 前記防水シートＡを実施例１と同様の手法で下地１０に
貼着した。ついで、このようにして形成された第一層目
の防水シートの表面層であるポリスチレン層（ブロッキ
ング防止層）面にトルエンを１００ｇ／ｍ2の割合で塗
布しなら、実施例１の防水シートＢを更に第２層目とし
て貼着し、防水を一層完全なものとした。防水シートＡ
の最上層と防水シートＢの最下層は一体化してポリスチ
レンの層９を形成した。Example 4 (corresponding to claims 3 and 6: see FIG. 3) As a blocking prevention layer 1, a polystyrene film: a thickness of 20 μm An adhesive material having the following composition as an entire surface adhesive layer 8: a thickness of 0.5 mm SBS 25 wt % Tackifier 20 wt% Process oil 20 wt% Straight asphalt (180-200) 35 wt% Asphalt layer 2 Modified asphalt: Thickness 0.3 mm Composition SBS 13 wt% Straight asphalt (180-200) 87 wt% Base material layer 3 As polyester spobond 120 g / m 2 asphalt layer 4, modified asphalt layer: thickness 0.3 mm composition SBS 13 wt% straight asphalt (180 to 200) 87 wt% as overall adhesive layer 5, adhesive material with the following composition: thickness 0.5 mm SBS 2 wt% Tackifier 20 wt% Process oil 20 wt% Straight asphalt (180 to 200) 35 wt% As an organic solvent-soluble plastic film layer 6, polystyrene film: thickness 20 μm The waterproof sheet A is used as a base 10 in the same manner as in Example 1. I stuck it on. Then, if toluene is applied at a rate of 100 g / m 2 to the surface of the polystyrene layer (antiblocking layer) which is the surface layer of the first-layer waterproof sheet thus formed, the waterproof sheet B of Example 1 is obtained. Was further adhered as a second layer to make waterproofing more complete. Tarpaulin A
The uppermost layer and the lowermost layer of the waterproof sheet B were integrated to form a polystyrene layer 9.
【００２７】本発明の実施態様を以下に列挙する。 １ 上から順に、ブロッキング防止層、アスファルト
層、基材層、アスファルト層、全面粘着層、有機溶剤可
溶性のプラスチックもしくはゴムよりなるフィルム層、
よりなる積層物であることを特徴とする防水シート。 ２ 上から順に、ブロッキング防止層、アスファルト
層、基材層、アスファルト層、有機溶剤に対して不溶性
のプラスチックフィルム層、粘着材がない部分が連通し
ている部分粘着層、有機溶剤可溶性のプラスチックもし
くはゴムよりなるフィルム層、よりなる積層物であるこ
とを特徴とする防水シート。 ３ 上から順に、有機溶剤可溶性のプラスチックもしく
はゴムよりなるフィルムよりなるブロッキング防止層、
全面粘着層、アスファルト層、基材層、アスファルト
層、全面粘着層、有機溶剤可溶性のプラスチックもしく
はゴムよりなるフィルム層、よりなる積層物であること
を特徴とする防水シート。 ４ 上から順に、有機溶剤可溶性のプラスチックもしく
はゴムよりなるフィルムよりなるブロッキング防止層、
全面粘着層、アスファルト層、基材層、アスファルト
層、有機溶剤に対して不溶性のプラスチックフィルム
層、粘着材がない部分が連通している部分粘着層、有機
溶剤可溶性のプラスチックもしくはゴムよりなるフィル
ム層、よりなる積層物であることを特徴とする防水シー
ト。 ５ 前記有機溶剤に対して不溶性のプラスチックフィル
ム層がポリエステルフィルム層である前項２または４記
載の防水シート。 ６ 前記ブロッキング防止層が有機溶剤可溶性のプラス
チックもしくはゴムよりなるフィルムである前項１，
２，３，４または５記載に防水シート。 ７ 前記ブロッキング防止層と有機溶剤可溶性のプラス
チックもしくはゴムよりなるフィルム層が共にポリスチ
レンフィルムである前項１，２，３，４または５記載の
防水シート。 ８ 有機溶剤を、前項１または２記載の防水シートの有
機溶剤可溶性のプラスチックもしくはゴムよりなるフィ
ルム層に塗布しながら、あるいは下地に塗布しながら、
前項１または２記載の防水シートにおける有機溶剤可溶
性のプラスチックもしくはゴムよりなるフィルム層を下
地に向けて接着していくことを特徴とする防水工法。 ９ アスファルト、改質アスファルトおよび前記
有機溶剤可溶性のプラスチックもしくはゴムよりなるフ
ィルムに対して親和性と接着性に優れたゴムまたはプラ
スチックよりなる群から選ばれた１種以上の材料の有機
溶剤溶液を、前項１または２記載の防水シートの有機溶
剤可溶性のプラスチックもしくはゴムよりなるフィルム
層に塗布しながら、あるいは下地に塗布しながら、前項
１または２記載の防水シートにおける有機溶剤可溶性の
プラスチックもしくはゴムよりなるフィルム層を下地に
向けて接着していくことを特徴とする防水工法。 １０ 前項３または４記載の防水シートを前項８または
９記載の防水工法で施工した後、その表面に有機溶剤を
塗布しながら、前項１または３記載の防水シートの有機
溶剤可溶性のプラスチックもしくはゴムよりなるフィル
ム面を下に向けて貼着することを特徴とする防水工法。 １１ 前項３または４記載の防水シートを前項８または
９記載の防水工法で施工した後、その表面にアスファル
ト、改質アスファルトおよび有機溶剤可溶性のプラスチ
ックフィルムに対して親和性と接着性に優れたゴムまた
はプラスチックよりなる群から選ばれた１種以上の材料
を溶解した有機溶剤溶液を塗布しながら、前項１または
３記載の防水シートの有機溶剤可溶性のプラスチックも
しくはゴムよりなるフィルム面を下に向けて貼着するこ
とを特徴とする防水工法。 １２ 前項３または４のブロッキング防止層が有機溶剤
可溶性のプラスチックもしくはゴムよりなるフィルムで
ある防水シートを使用する前項１０または１１記載の防
水工法。 １３ 前項３または４のブロッキング防止層と有機溶剤
可溶性のプラスチックもしくはゴムよりなるフィルム層
が共にポリスチレンフィルムである防水シートを前項８
または９記載の防水工法で施工した後、その表面に有機
溶剤を塗布しながら、前項６または７記載の防水シート
の有機溶剤可溶性のプラスチックもしくはゴムよりなる
フィルム面を下に向けて貼着することを特徴とする防水
工法。 １４ 前項３または４のブロッキング防止層と有機溶剤
可溶性のプラスチックもしくはゴムよりなるフィルム層
が共にポリスチレンフィルムである防水シートを前項８
または９記載の防水工法で施工した後、その表面にアス
ファルト、改質アスファルトおよび有機溶剤可溶性のプ
ラスチックフィルムに対して親和性と接着性に優れたゴ
ムまたはプラスチックよりなる群から選ばれた１種以上
の材料を溶解した有機溶剤溶液を塗布しながら、前項６
または７記載の防水シートの有機溶剤可溶性のプラスチ
ックもしくはゴムよりなるフィルム面を下に向けて貼着
することを特徴とする防水工法。The embodiments of the present invention are listed below. 1 In order from the top, anti-blocking layer, asphalt layer, base material layer, asphalt layer, overall adhesive layer, film layer made of organic solvent-soluble plastic or rubber,
A waterproof sheet, which is a laminate made of 2 In order from the top, anti-blocking layer, asphalt layer, base material layer, asphalt layer, plastic film layer insoluble in organic solvent, partial adhesive layer in which no adhesive is present, organic solvent-soluble plastic or A waterproof sheet comprising a film layer made of rubber and a laminate made of the film layer. 3 From the top in order, an anti-blocking layer composed of a film made of an organic solvent-soluble plastic or rubber,
A waterproof sheet which is a laminate comprising a full-scale adhesive layer, an asphalt layer, a base material layer, an asphalt layer, a full-scale adhesive layer, a film layer made of an organic solvent-soluble plastic or rubber. 4 In order from the top, an anti-blocking layer made of a film made of an organic solvent-soluble plastic or rubber,
Full-scale adhesive layer, asphalt layer, base material layer, asphalt layer, plastic film layer insoluble in organic solvent, partial adhesive layer in which parts without adhesive material are in communication, film layer made of organic solvent-soluble plastic or rubber A waterproof sheet, which is a laminate made of 5. The waterproof sheet according to item 2 or 4, wherein the plastic film layer insoluble in the organic solvent is a polyester film layer. 6 The blocking prevention layer is a film made of an organic solvent-soluble plastic or rubber.
A waterproof sheet as described in 2, 3, 4 or 5. 7. The waterproof sheet according to the above 1, 2, 3, 4 or 5, wherein both the blocking prevention layer and the film layer made of an organic solvent-soluble plastic or rubber are polystyrene films. 8 While applying the organic solvent to the film layer made of the organic solvent-soluble plastic or rubber of the waterproof sheet according to the above 1 or 2, or while applying it to the base,
A waterproofing method, characterized in that a film layer made of an organic solvent-soluble plastic or rubber in the waterproof sheet according to the above 1 or 2 is adhered toward a substrate. 9. An organic solvent solution of one or more materials selected from the group consisting of rubber or plastic having excellent affinity and adhesion to asphalt, modified asphalt, and a film comprising the organic solvent-soluble plastic or rubber, The organic solvent-soluble plastic or rubber of the waterproof sheet according to the above 1 or 2 while being applied to the film layer of the organic solvent-soluble plastic or rubber of the waterproof sheet according to 1 or 2 above or while being applied to the base. A waterproofing method characterized by adhering the film layer to the base. 10 After applying the waterproof sheet according to the above 3 or 4 by the waterproof method according to the above 8 or 9, while applying an organic solvent on the surface thereof, from the organic solvent-soluble plastic or rubber of the waterproof sheet according to the above 1 or 3 A waterproofing method characterized by sticking the film surface facing downward. 11. A rubber having excellent affinity and adhesiveness to the asphalt, modified asphalt, and organic solvent-soluble plastic film on the surface after applying the waterproof sheet according to the above 3 or 4 by the waterproof method according to the above 8 or 9. Alternatively, while applying an organic solvent solution in which at least one material selected from the group consisting of plastics is dissolved, the film surface made of the organic solvent-soluble plastic or rubber of the waterproof sheet according to the above 1 or 3 is directed downward. Waterproofing method characterized by sticking. [12] The waterproof method according to [10] or [11] above, wherein the blocking prevention layer according to [3] or [4] is a waterproof sheet that is a film made of an organic solvent-soluble plastic or rubber. 13 A waterproof sheet according to the above item 3 or 4, wherein the anti-blocking layer and the film layer made of an organic solvent-soluble plastic or rubber are both polystyrene films.
Or, after applying the waterproofing method described in 9 above, while applying the organic solvent to the surface, stick the film of the waterproof sheet according to 6 or 7 described above, which is made of plastic or rubber soluble in organic solvent, facing downward. Waterproof construction method characterized by. 14 A waterproof sheet in which the anti-blocking layer of 3 or 4 and the film layer made of an organic solvent-soluble plastic or rubber are both polystyrene films is used.
Or one or more selected from the group consisting of rubber or plastic having excellent affinity and adhesion to the asphalt, modified asphalt, and plastic film soluble in organic solvent on the surface after applying the waterproofing method described in 9. While applying the organic solvent solution in which the material of
Alternatively, the waterproofing method is characterized in that the waterproof sheet is attached with the film surface made of an organic solvent-soluble plastic or rubber facing downward.
【００２８】[0028]
１ 廃材（剥離紙）が発生しない。 ２ 溶剤として、アスファルトを添加せず有機溶剤のみ
を使用する場合には、溶剤の容器は内部が汚れることが
ないので、繰り返し使用が可能であり、かつ廃棄の際の
コストも汚染物がないので低廉である。 ３ 従来の剥離紙使用のタイプを用いて施工する場合
は、下地面にプライマー塗布を行った後、防水シートを
接着していたが、本発明では、プライマー塗布のかわり
に有機溶剤のみを塗布すれば良いから、その分安価にな
る。1 No waste material (release paper) is generated. 2 As the solvent, when only organic solvent is used without adding asphalt, the inside of the solvent container is not contaminated, so it can be used repeatedly, and the cost at the time of disposal is free from contaminants. It is inexpensive. 3 When applying with a conventional release paper type, the primer sheet was applied to the base surface and then the waterproof sheet was adhered. However, in the present invention, only the organic solvent should be applied instead of the primer application. It's good, so it's cheaper.
【図１】実施例１の防水シートの断面図である。FIG. 1 is a cross-sectional view of a waterproof sheet according to a first embodiment.
【図２】実施例３の防水シートの断面図である。FIG. 2 is a sectional view of a waterproof sheet according to a third embodiment.
【図３】実施例４の防水工法により得られた下地面に施
工された防止構造の断面図である。FIG. 3 is a cross-sectional view of a preventive structure constructed on a base surface obtained by the waterproof method of Example 4.
１ ブロッキング防止層 ２ アスファルト層 ３ 基材層 ４ アスファルト層 ５ 全面粘着層 ５’ 部分粘着層 ６ 有機溶剤可溶性のプラスチックもしくはゴムよりな
るフィルム層 ７ 有機溶剤不溶性プラスチックフィルム層 ８ 全面粘着層 ９ ポリスチレン層 １０ 下地1 Blocking Prevention Layer 2 Asphalt Layer 3 Base Layer 4 Asphalt Layer 5 Full Adhesive Layer 5'Partial Adhesive Layer 6 Film Layer Made of Organic Solvent-Soluble Plastic or Rubber 7 Organic Solvent-Insoluble Plastic Film Layer 8 Full Adhesive Layer 9 Polystyrene Layer 10 Groundwork
───────────────────────────────────────────────────── フロントページの続き (72)発明者 真有 勝義 東京都足立区小台１丁目３番１号 田島ル ーフィング株式会社内 (72)発明者 町田 繁 東京都足立区小台１丁目３番１号 田島ル ーフィング株式会社内 ─────────────────────────────────────────────────── ─── Continuation of front page (72) Inventor Katsuyoshi Maari 1-3-1, Kodai, Adachi-ku, Tokyo Tajima Roofing Co., Ltd. (72) Inventor Shigeru Machida 1-3-1, Kodai, Adachi-ku, Tokyo No. within Tajima Roofing Co., Ltd.
Claims (6)
ィルム層、よりなる積層物であることを特徴とする防水
シート。1. A laminate comprising an anti-blocking layer, an asphalt layer, a base layer, an asphalt layer, a full-scale adhesive layer, a film layer made of an organic solvent-soluble plastic or rubber, and a laminate in this order from the top. Tarpaulin.
ィルム層、よりなる積層物であることを特徴とする防水
シート。2. An anti-blocking layer, an asphalt layer, a base material layer, an asphalt layer, a plastic film layer insoluble to an organic solvent, a partial adhesive layer in which no adhesive material is in communication, and an organic solvent in this order from the top. A waterproof sheet, which is a laminate comprising a film layer made of soluble plastic or rubber.
ィルムよりなるブロッキング防止層、 全面粘着層、 アスファルト層、 基材層、 アスファルト層、 全面粘着層、 有機溶剤可溶性のプラスチックもしくはゴムよりなるフ
ィルム層、よりなる積層物であることを特徴とする防水
シート。3. An anti-blocking layer consisting of a film made of an organic solvent-soluble plastic or rubber, a full surface adhesive layer, an asphalt layer, a base material layer, an asphalt layer, an entire adhesive layer, an organic solvent soluble plastic or rubber in order from the top. A waterproof sheet comprising a film layer made of, and a laminate made of.
ィルムよりなるブロッキング防止層、 全面粘着層、 アスファルト層、 基材層、 アスファルト層、 有機溶剤に対して不溶性のプラスチックフィルム層、 粘着材がない部分が連通している部分粘着層、 有機溶剤可溶性のプラスチックもしくはゴムよりなるフ
ィルム層、よりなる積層物であることを特徴とする防水
シート。4. An anti-blocking layer consisting of a film made of an organic solvent-soluble plastic or rubber, a full surface adhesive layer, an asphalt layer, a base layer, an asphalt layer, an organic solvent insoluble plastic film layer, in order from the top. A waterproof sheet characterized by being a laminate comprising a partial adhesive layer in which parts without an adhesive material are in communication, a film layer made of an organic solvent-soluble plastic or rubber.
記有機溶剤可溶性のプラスチックもしくはゴムよりなる
フィルムに対して親和性と接着性に優れたゴムまたはプ
ラスチックよりなる群から選ばれた１種以上の材料の有
機溶剤溶液 を、請求項１または２記載の防水シートの有機溶剤可溶
性のプラスチックもしくはゴムよりなるフィルム層に塗
布しながら、あるいは下地に塗布しながら、請求項１ま
たは２記載の防水シートにおける有機溶剤可溶性のプラ
スチックもしくはゴムよりなるフィルム層を下地に向け
て接着していくことを特徴とする防水工法。5. A group consisting of (a) an organic solvent alone or (b) asphalt, modified asphalt, and a rubber or plastic excellent in affinity and adhesion to a film made of the organic solvent-soluble plastic or rubber. An organic solvent solution of one or more selected materials is applied to the film layer made of the organic solvent-soluble plastic or rubber of the waterproof sheet according to claim 1 or 2, or while being applied to a base. Alternatively, a waterproofing method characterized in that a film layer made of an organic solvent-soluble plastic or rubber in the waterproof sheet according to 2 is adhered toward a base.
求項５記載の防水工法で施工した後、その表面に （ａ）有機溶剤単独 あるいは （ｂ）アスファルト、改質アスファルトおよび前
記有機溶剤可溶性のプラスチックもしくはゴムよりなる
フィルムに対して親和性と接着性に優れたゴムまたはプ
ラスチックよりなる群から選ばれた１種以上の材料の有
機溶剤溶液 を塗布しながら、請求項１記載の防水シートの有機溶剤
可溶性プラスチックフィルム面を下に向けて接着するこ
とを特徴とする防水工法。6. After applying the waterproof sheet according to claim 3 or 4 by the waterproof method according to claim 5, (a) an organic solvent alone or (b) asphalt, modified asphalt and the organic solvent-soluble material. The waterproof sheet according to claim 1, which is coated with an organic solvent solution of one or more materials selected from the group consisting of rubber or plastic having excellent affinity and adhesiveness to the plastic or rubber film of 1. A waterproofing method characterized in that the organic solvent-soluble plastic film surface is bonded downward.