JPH08120423A - Current collecting pantograph shoe material made of iron-base sintered alloy impregnated with lead, excellent in electric conductivity and wear resistance - Google Patents

Current collecting pantograph shoe material made of iron-base sintered alloy impregnated with lead, excellent in electric conductivity and wear resistance

Info

Publication number
JPH08120423A
JPH08120423A JP27714894A JP27714894A JPH08120423A JP H08120423 A JPH08120423 A JP H08120423A JP 27714894 A JP27714894 A JP 27714894A JP 27714894 A JP27714894 A JP 27714894A JP H08120423 A JPH08120423 A JP H08120423A
Authority
JP
Japan
Prior art keywords
impregnated
sintered alloy
lead
current collecting
wear resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP27714894A
Other languages
Japanese (ja)
Inventor
Masashi Koike
正志 小池
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Materials Corp
Original Assignee
Mitsubishi Materials Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Materials Corp filed Critical Mitsubishi Materials Corp
Priority to JP27714894A priority Critical patent/JPH08120423A/en
Publication of JPH08120423A publication Critical patent/JPH08120423A/en
Withdrawn legal-status Critical Current

Abstract

PURPOSE: To produce a current collecting pantograph shoe material made of Fe-base sintered alloy impregnated with lead, excellent in electric conductivity and wear resistance. CONSTITUTION: This current collecting pantograph shoe material is composed of an Fe-base sintered alloy impregnated with lead, prepared by impregnating Pb or Pb alloy into an Fe-base sintered alloy which has a composition consisting of, by weight, 5-30% TiSi2 and/or WSi2 as dispersed phase forming component, 0.1-7% of one or more elements among Ni, Cu, and Mn as matrix forming components, and the balance Fe with inevitable impurities and further containing, if necessary, either or both of 0.05-3% Cr and/or Mo and 0.05-0.5% C and also has 5-15% porosity.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】この発明は、すぐれた導電性と耐
摩耗性を有し、したがって高集電能力を可能とした状態
で、長期に亘ってすぐれた性能を発揮する鉛含浸Fe基
焼結合金製集電用パンタグラフすり板材に関するもので
ある。
BACKGROUND OF THE INVENTION The present invention relates to a lead-impregnated Fe-based calcinated which has excellent conductivity and wear resistance, and therefore exhibits excellent performance over a long period of time in a state where high current collecting capability is possible. The present invention relates to a pantograph sliding plate material for collecting electricity made of bonded gold.

【0002】[0002]

【従来の技術】従来、一般に電気車の集電用パンタグラ
フすり板材として、素地に硬質粒子が分散分布した組
織、並びに5〜30%の気孔率を有するFe基焼結合金
に、PbまたはPb合金を含浸してなる各種の鉛含浸F
e基焼結合金が提案され、実用に供されている。
2. Description of the Related Art Conventionally, a Pb or Pb alloy has been used as a pantograph sliding plate material for collecting current of an electric vehicle, in general, a Fe-based sintered alloy having a structure in which hard particles are dispersed and distributed in a substrate, and a porosity of 5 to 30%. Various lead-impregnated F impregnated with
An e-based sintered alloy has been proposed and put to practical use.

【0003】[0003]

【発明が解決しようとする課題】一方、近年の電気車の
大型化および多連結化、さらに高速化はめざましく、こ
れに伴ない、集電用パンタグラフすり板材には、できる
だけ多くの電流を取り入れることのできる特性、すなわ
ち高い導電性と、一段の耐摩耗性向上が要求されるが、
現在提案され、実用に供されている鉛含浸Fe基焼結合
金製集電用パンタグラフすり板材(以下、単に集電すり
板材という)においては、耐摩耗性にすぐれるものは導
電性が低く、反対に導電性の良好なものは耐摩耗性が劣
り、導電性と耐摩耗性の両特性を兼ね備えたものでない
ために、これらの要求に満足に対応することができない
のが現状である。
On the other hand, in recent years, electric vehicles have become larger and more connected, and the speed has been remarkably high. Accordingly, as much current as possible should be taken into the pantograph sliding plate material for current collection. The characteristics that can be achieved, namely high conductivity and further improvement in wear resistance are required,
Among the lead-impregnated Fe-based sintered alloy current collector pantograph siding plates (hereinafter simply referred to as current collecting siding plates) that have been proposed and are in practical use, those with excellent wear resistance have low conductivity, On the other hand, a material having good conductivity has poor wear resistance and does not have both conductivity and wear resistance, so that it is not possible to satisfy these requirements at present.

【0004】[0004]

【課題を解決するための手段】そこで、本発明者等は、
上述のような観点から、導電性および耐摩耗性にすぐれ
た集電すり板材を開発すべく研究を行なった結果、集電
すり板材を、重量%で(以下、組成に関する%は重量%
を示す)、分散相形成成分として、TiおよびWのけい
化物(以下、それぞれTiSi2およびWSi2 で示
す)のうちの1種または2種:5〜30%、以下いずれ
も素地形成成分として、Ni,Cu,およびMnのうち
の1種または2種以上:0.1〜7%、を含有し、さら
に必要に応じて、(a) Crおよび/またはMo:
0.05〜3%、(b) C:0.05〜0.5%、以
上(a)および/または(b)を含有し、残りがFeと
不可避不純物からなる組成、並びに、5〜15%の気孔
率、を有するFe基焼結合金に、PbまたはPb合金を
含浸してなる鉛含浸Fe基焼結合金で構成すると、上記
分散相を構成するTiSi2 およびWSi2 は、表1に
示される通り、素地の主要成分であるFeと近似した低
い比抵抗を有し、かつ相対的に高い硬さを有し、さらに
Fe基合金素地との密着性にもすぐれていることから、
この結果の集電すり板材は、きわめて導電性のすぐれた
ものとなるばかりでなく、すぐれた耐摩耗性を発揮する
という研究結果を得たのである。
Therefore, the present inventors have
From the above viewpoints, as a result of research to develop a current collecting strip material excellent in conductivity and wear resistance, the current collecting strip material is expressed in% by weight (hereinafter,% relating to composition is% by weight).
As a dispersed phase forming component, one or two kinds of silicides of Ti and W (hereinafter, respectively represented by TiSi 2 and WSi 2 ): 5 to 30%, and below as a base forming component, One or more of Ni, Cu, and Mn: 0.1 to 7%, and (a) Cr and / or Mo:
0.05 to 3%, (b) C: 0.05 to 0.5%, a composition containing the above (a) and / or (b), the balance being Fe and inevitable impurities, and 5 to 15 When a Fe-based sintered alloy having a porosity of 10% is used to form a lead-impregnated Fe-based sintered alloy impregnated with Pb or a Pb alloy, the TiSi 2 and WSi 2 constituting the dispersed phase are As shown, it has a low specific resistance similar to that of Fe, which is the main component of the base material, and has a relatively high hardness, and also has excellent adhesion to the Fe-based alloy base material,
The result of this study is that the current collecting strip material not only has extremely excellent electrical conductivity but also exhibits excellent wear resistance.

【0005】[0005]

【表1】 [Table 1]

【0006】この発明は、上記の研究結果にもとづいて
なされたものであって、分散相形成成分として、TiS
2 および/またはWSi2 :5〜30%、以下いずれ
も素地形成成分として、Ni,Cu,およびMnのうち
の1種または2種以上:0.1〜7%、を含有し、さら
に必要に応じて、(a) Crおよび/またはMo:
0.05〜3%、(b) C:0.05〜0.5%、以
上(a)および/または(b)を含有し、残りがFeと
不可避不純物からなる組成、並びに、5〜15%の気孔
率、を有するFe基焼結合金に、PbまたはPb合金を
含浸してなる鉛含浸Fe基焼結合金で構成してなる、導
電性および耐摩耗性にすぐれた集電すり板材に特徴を有
するものである。
The present invention was made based on the results of the above research, and TiS was used as a dispersed phase forming component.
i 2 and / or WSi 2: 5 to 30%, or less both as a matrix forming component, Ni, Cu, and one or more of Mn: 0.1 to 7%, containing further required (A) Cr and / or Mo:
0.05 to 3%, (b) C: 0.05 to 0.5%, a composition containing the above (a) and / or (b), the balance being Fe and inevitable impurities, and 5 to 15 Of a Fe-based sintered alloy having a porosity of 100% and a lead-impregnated Fe-based sintered alloy impregnated with Pb or a Pb alloy, having excellent conductivity and wear resistance. It has characteristics.

【0007】つぎに、この発明の集電すり板材におい
て、これを構成するFe基焼結合金の成分組成および気
孔率を上記の通りに限定した理由を説明する。 (a) TiSi2 およびWSi2 これらの成分は、Fe成分に近似した低い比抵抗を有す
るので、これの含有によってすり板材の導電性が低下す
ることなく、著しく高い状態に保持され、かつ相対的に
硬質なものなので、耐摩耗性の向上効果も著しく、した
がってこれらの成分の含有によってすり板材は高い導電
性とすぐれた耐摩耗性をもつようになるが、その含有量
が5%未満では所望の耐摩耗性を確保することができ
ず、一方その含有量が30%を越えると、すり板材の強
度が低下するようになることから、その含有量を5〜3
0%と定めた。なお、望ましくは5〜20%の含有がよ
い。
Next, the reason why the component composition and porosity of the Fe-based sintered alloy constituting the current collecting strip material of the present invention are limited as described above will be explained. (A) TiSi 2 and WSi 2 These components have a low specific resistance close to that of the Fe component, so the inclusion of these components does not reduce the conductivity of the slab material and is maintained at a significantly high state, and the relative Since it is extremely hard, the effect of improving wear resistance is also remarkable. Therefore, the inclusion of these components makes the slab material have high conductivity and excellent wear resistance, but if the content is less than 5%, it is desirable. Wear resistance cannot be ensured, and on the other hand, if the content exceeds 30%, the strength of the contact plate material will decrease, so the content should be 5 to 3
It was set to 0%. Incidentally, the content of 5 to 20% is desirable.

【0008】(b) Ni,Cu、およびMn これらの成分には、素地に固溶して、これを強化すると
共に、分散相を構成するTiSi2 およびWSi2 の素
地に対する密着性を向上させる作用があるが、その含有
量が0.1%未満では前記作用に所望の効果が得られ
ず、一方その含有量が7%を越えると靭性が低下するよ
うになることから、その含有量を0.1〜7%と定め
た。望ましくは1.5〜4%の含有がよい。
(B) Ni, Cu, and Mn These components act to form a solid solution in the matrix to strengthen it and improve the adhesion of the dispersed phases of TiSi 2 and WSi 2 to the matrix. However, if the content is less than 0.1%, the desired effect is not obtained on the other hand, and if the content exceeds 7%, the toughness decreases, so the content is set to 0%. It was set at 1 to 7%. Desirably, the content is 1.5 to 4%.

【0009】(c) CrおよびMo これらの成分には、素地に固溶して、これの強度を一段
と向上させると共に、耐熱性を向上させ、もってすり板
材の耐摩耗性向上に寄与する作用があるので、必要に応
じて含有されるが、その含有量が0.05%未満では前
記作用に所望の効果が得られず、一方その含有量が3%
を越えると、TiSi2 およびWSi2の素地に対する
密着性が低下し、この結果として耐摩耗性の低下をもた
らすようになることから、その含有量を0.05〜3%
と定めた。望ましくは0.3〜1.5%の含有がよい。
(C) Cr and Mo These components have the function of forming a solid solution in the matrix to further improve the strength and heat resistance of the matrix and thereby contribute to the improvement of the wear resistance of the ground sheet material. Therefore, it is contained as necessary, but if the content is less than 0.05%, the desired effect on the above-mentioned action cannot be obtained, while the content is 3%.
When the content exceeds 0.05%, the adhesion of TiSi 2 and WSi 2 to the base material is lowered, and as a result, the wear resistance is lowered, so that the content is 0.05 to 3%.
I decided. Desirably, the content is 0.3 to 1.5%.

【0010】(d) C C成分には、素地に固溶して、これを強化し、かつ焼結
性を向上させる作用があるので、必要に応じて含有され
るが、その含有量が0.05%未満では前記作用に所望
の効果が得られず、一方その含有量が0.5%を越える
と靭性が低下するようになることから、その含有量を
0.05〜0.5%と定めた。望ましくは0.1〜0.
3%の含有がよい。
(D) C The C component has a function of forming a solid solution in the matrix to strengthen it and improve the sinterability, so that it is contained as necessary, but its content is 0. If the content is less than 0.05%, the desired effect cannot be obtained, while if the content exceeds 0.5%, the toughness decreases, so the content is set to 0.05 to 0.5%. I decided. Desirably 0.1 to 0.
3% content is good.

【0011】(e) 気孔率 その割合が5%未満では、Fe基焼結合金に含浸される
PbまたはPb合金の割合が少なすぎて、このPbおよ
びPb合金によってもたらされるすぐれた潤滑性を確保
することができず、一方その割合が15%を越えると、
Fe基焼結合金の強度、すなわちすり板材の強度が低下
するばかりでなく、耐アーク性も低下するようになるこ
とから、その割合を5〜15%と定めた。望ましくは7
〜12%がよい。
(E) Porosity If the proportion is less than 5%, the proportion of Pb or Pb alloy impregnated in the Fe-based sintered alloy is too small, and the excellent lubricity provided by this Pb and Pb alloy is secured. If the percentage exceeds 15%,
Since not only the strength of the Fe-based sintered alloy, that is, the strength of the ground sheet material, but also the arc resistance is deteriorated, the ratio is set to 5 to 15%. Preferably 7
~ 12% is good.

【0012】[0012]

【実施例】つぎに、この発明の集電すり板材を実施例に
より具体的に説明する。原料粉末として、いずれも1〜
150μmの範囲内の所定の平均粒径を有するTiSi
2 粉末、WSi2 粉末、Ni粉末、Cu粉末、およびM
n粉末、さらにいずれも80メッシュ以下の所定の粒度
を有するアトマイズ鉄粉、Fe−Cr合金(Cr:65
%含有)粉末、Fe−Mo合金(Mo:65%含有)粉
末、および325メッシュ以下の粒度を有する黒鉛粉末
を用意し、これら原料粉末を表2,3に示される配合組
成に配合し、混合した後、3〜6ton /cm2 の範囲内の
所定の圧力で圧粉体にプレス成形し、この圧粉体を、ア
ンモニア分解ガス雰囲気中、1130〜1200℃の範
囲内の所定温度に1時間保持の条件で焼結して、実質的
に配合組成と同一の成分組成並びに表2,3に示される
気孔率をもったFe基焼結合金A〜Tを形成し、ついで
これらのFe基焼結合金A〜Tに、表4に示す通り純鉛
またはPb−30%Snの組成をもったPb合金を含浸
させることにより、幅:25mm×長さ:80mm×厚さ:
10mmの寸法をもった本発明集電すり板材1〜17およ
び比較集電すり板材1〜3をそれぞれ製造した。なお、
比較集電すり板材1〜3は、分散相を構成するTiSi
2 およびWSi2 の含有量がこの発明の範囲から低い方
に外れた組成をもつものである。
EXAMPLES Next, the current collecting strip material of the present invention will be specifically described by way of examples. As raw material powder, 1 to
TiSi having a predetermined average particle size within the range of 150 μm
2 powder, WSi 2 powder, Ni powder, Cu powder, and M
n powder, further atomized iron powder having a predetermined particle size of 80 mesh or less, Fe-Cr alloy (Cr: 65
%) Powder, Fe-Mo alloy (Mo: 65% content) powder, and graphite powder having a particle size of 325 mesh or less, and these raw material powders are blended in the blending composition shown in Tables 2 and 3 and mixed. After that, the green compact is press-molded at a predetermined pressure within the range of 3 to 6 ton / cm 2 , and the green compact is heated to a predetermined temperature within the range of 1130 to 1200 ° C. for 1 hour in an atmosphere of ammonia decomposition gas. Sintering was carried out under the condition of holding to form Fe-based sintered alloys A to T having substantially the same composition as the compounding composition and the porosities shown in Tables 2 and 3, and then these Fe-based sintered alloys were formed. By impregnating the binding metals A to T with pure lead or a Pb alloy having a composition of Pb-30% Sn as shown in Table 4, width: 25 mm x length: 80 mm x thickness:
The current collecting strips 1 to 17 of the present invention and the comparative current collecting strips 1 to 3 each having a size of 10 mm were manufactured. In addition,
Comparative current collecting strip materials 1 to 3 are TiSi forming a dispersed phase.
2 and WSi 2 have a composition outside the scope of the present invention.

【0013】[0013]

【表2】 [Table 2]

【0014】[0014]

【表3】 [Table 3]

【0015】[0015]

【表4】 [Table 4]

【0016】この結果得られた各種集電すり板材につい
て加速摩耗試験を行なった。加速摩耗試験は、モータの
水平回転軸に中心を固定することにより直立支持された
外径:2.2mの円板の前記固定側とは反対側面に、模
擬トロリ線として外径:2m×幅:5mm×厚さ:15mm
の硬銅リング(JIS・C1100・BB−H)を50
mm偏心して取付けた装置を用い、上記硬銅リングの直径
線上の両側にそれぞれ集電すり板材を4kgの押付力で長
さ:80mm×幅:25mmの寸法面を面接触させ、上記模
擬トロリ線と集電すり板材間に200Aの電流を流しな
がら、上記円板の回転を5分で220km/hrの回転速度
に上げ、この速度に5分間保持した後、5分かけて停止
を1サイクルとし、これを4回繰り返すことにより行な
い、集電すり板材の比摩耗量と相手材である模擬トロリ
線の摩耗深さを測定した。この測定結果を表4に示し
た。また表4には導電性を評価する目的で集電すり板材
の比抵抗の測定結果も示した。
An accelerated wear test was conducted on the various current collecting strips obtained as a result. The accelerated wear test was carried out by fixing the center of the motor to the horizontal axis of rotation of the motor. The disc was supported upright on the side opposite to the fixed side of the disc with an outer diameter of 2.2 m. : 5 mm x thickness: 15 mm
50 hard copper rings (JIS / C1100 / BB-H)
Using a device mounted eccentrically, the current collecting strips are pressed on both sides of the diameter line of the hard copper ring with a pressing force of 4 kg to bring the dimension surfaces of length: 80 mm × width: 25 mm into surface contact, and then the simulated trolley wire. While passing a current of 200 A between the collector and the current collecting plate material, the rotation speed of the disk is increased to 220 km / hr in 5 minutes, and the speed is maintained for 5 minutes. This was repeated four times to measure the specific wear amount of the current collecting strip material and the wear depth of the simulated trolley wire as the mating material. The measurement results are shown in Table 4. In addition, Table 4 also shows the measurement results of the specific resistance of the current collecting strip material for the purpose of evaluating the conductivity.

【0017】[0017]

【発明の効果】表2〜4に示される結果から、本発明集
電すり板材1〜17は、硬質のTiSi2 およびWSi
2 の含有にもかかわらず高い導電性を有し、かつ低い相
手攻撃性ですぐれた耐摩耗性を示すのに対して、比較集
電すり板材1〜3に見られるように、Fe基焼結合金の
硬質相を構成するTiSi2 および/またはWSi2
この発明の範囲が外れた低い含有量であると所望のすぐ
れた耐摩耗性を確保することができないことが明らかで
ある。上述のように、この発明の集電すり板材は、すぐ
れた導電性と耐摩耗性を具備するので、電気車の著しい
進歩にも十分満足に対応することがてきるなど工業上有
用な効果をもたらすものである。
From the results shown in Tables 2 to 4, the current collecting contact strip materials 1 to 17 of the present invention are hard TiSi 2 and WSi.
Despite having a content of 2 , it has high electrical conductivity, and exhibits excellent wear resistance with low opponent attacking property, while it can be seen from the comparative current collecting strip materials 1 to 3 that Fe-based firing bonding is performed. When TiSi 2 and / or WSi 2 constituting the hard phase of gold has a low content outside the scope of the present invention, it is apparent that the desired excellent wear resistance cannot be ensured. As described above, the current collecting strip material of the present invention has excellent electrical conductivity and wear resistance, and therefore has industrially useful effects such as being able to sufficiently satisfy the remarkable progress of electric vehicles. To bring.

フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 B60L 5/00 A C22C 33/02 G 38/16 38/50 Continuation of the front page (51) Int.Cl. 6 Identification code Office reference number FI Technical display location B60L 5/00 AC22C33 / 02G 38/16 38/50

Claims (4)

【特許請求の範囲】[Claims] 【請求項1】 重量%で、 分散相形成成分として、TiおよびWのけい化物のうち
の1種または2種:5〜30%、 素地形成成分として、Ni,Cu,およびMnのうちの
1種または2種以上:0.1〜7%、を含有し、残りが
同じく素地形成成分としてのFeと不可避不純物からな
る組成、並びに、 5〜15%の気孔率、を有するFe基焼結合金に、Pb
またはPb合金を含浸してなる鉛含浸Fe基焼結合金で
構成したことを特徴とする導電性および耐摩耗性にすぐ
れた鉛含浸Fe基焼結合金製集電用パンタグラフすり板
材。
1. By weight%, one or two of silicides of Ti and W as a dispersed phase forming component: 5 to 30%, and one of Ni, Cu, and Mn as a base forming component. Or a mixture of two or more kinds: 0.1 to 7%, the rest of which is a composition of Fe and unavoidable impurities as a base forming component, and a porosity of 5 to 15%. , Pb
Alternatively, a lead-impregnated Fe-based sintered alloy current collecting pantograph sliding plate material excellent in conductivity and wear resistance, characterized by being constituted by a lead-impregnated Fe-based sintered alloy impregnated with a Pb alloy.
【請求項2】 重量%で、 分散相形成成分として、TiおよびWのけい化物のうち
の1種または2種:5〜30%、 以下いずれも素地形成成分として、 Ni,Cu,およびMnのうちの1種または2種以上:
0.1〜7%、 Crおよび/またはMo:0.05〜3%、を含有し、
残りがFeと不可避不純物からなる組成、並びに、 5〜15%の気孔率、を有するFe基焼結合金に、Pb
またはPb合金を含浸してなる鉛含浸Fe基焼結合金で
構成したことを特徴とする導電性および耐摩耗性にすぐ
れた鉛含浸Fe基焼結合金製集電用パンタグラフすり板
材。
2. One or two kinds of silicides of Ti and W as a disperse phase forming component: 5 to 30%, all of which are Ni, Cu, and Mn as a base forming component. One or more of them:
0.1 to 7%, Cr and / or Mo: 0.05 to 3%,
A Fe-based sintered alloy having a composition in which the balance is Fe and inevitable impurities, and a porosity of 5 to 15%, Pb
Alternatively, a lead-impregnated Fe-based sintered alloy current collecting pantograph sliding plate material excellent in conductivity and wear resistance, characterized by being constituted by a lead-impregnated Fe-based sintered alloy impregnated with a Pb alloy.
【請求項3】 重量%で、 分散相形成成分として、TiおよびWのけい化物のうち
の1種または2種:5〜30%、 以下いずれも素地形成成分として、 Ni,Cu,およびMnのうちの1種または2種以上:
0.1〜7%、 C:0.05〜0.5%、を含有し、残りがFeと不可
避不純物からなる組成、並びに、 5〜15%の気孔率、を有するFe基焼結合金に、Pb
またはPb合金を含浸してなる鉛含浸Fe基焼結合金で
構成したことを特徴とする導電性および耐摩耗性にすぐ
れた鉛含浸Fe基焼結合金製集電用パンタグラフすり板
材。
3. By weight%, one or two of silicides of Ti and W as a dispersed phase forming component: 5 to 30%, all of which include Ni, Cu, and Mn as a matrix forming component. One or more of them:
A Fe-based sintered alloy containing 0.1 to 7%, C: 0.05 to 0.5%, and the balance of Fe and inevitable impurities, and a porosity of 5 to 15%. , Pb
Alternatively, a lead-impregnated Fe-based sintered alloy current collecting pantograph sliding plate material excellent in conductivity and wear resistance, characterized by being constituted by a lead-impregnated Fe-based sintered alloy impregnated with a Pb alloy.
【請求項4】 重量%で、 分散相形成成分として、TiおよびWのけい化物のうち
の1種または2種:5〜30%、 以下いずれも素地形成成分として、 Ni,Cu,およびMnのうちの1種または2種以上:
0.1〜7%、 Crおよび/またはMo:0.05〜3%、 C:0.05〜0.5%、を含有し、残りがFeと不可
避不純物からなる組成、並びに、 5〜15%の気孔率、を有するFe基焼結合金に、Pb
またはPb合金を含浸してなる鉛含浸Fe基焼結合金で
構成したことを特徴とする導電性および耐摩耗性にすぐ
れた鉛含浸Fe基焼結合金製集電用パンタグラフすり板
材。
4. One or two kinds of silicides of Ti and W as a dispersed phase forming component: 5 to 30% by weight, all of which are Ni, Cu, and Mn as a base forming component. One or more of them:
0.1 to 7%, Cr and / or Mo: 0.05 to 3%, C: 0.05 to 0.5%, with the balance being Fe and inevitable impurities, and 5 to 15 Fe-based sintered alloy having a porosity of
Alternatively, a lead-impregnated Fe-based sintered alloy current collecting pantograph sliding plate material excellent in conductivity and wear resistance, characterized by being constituted by a lead-impregnated Fe-based sintered alloy impregnated with a Pb alloy.
JP27714894A 1994-10-17 1994-10-17 Current collecting pantograph shoe material made of iron-base sintered alloy impregnated with lead, excellent in electric conductivity and wear resistance Withdrawn JPH08120423A (en)