JPH0748778A - Ground covered with artificial lawn - Google Patents
Ground covered with artificial lawnInfo
- Publication number
- JPH0748778A JPH0748778A JP5194497A JP19449793A JPH0748778A JP H0748778 A JPH0748778 A JP H0748778A JP 5194497 A JP5194497 A JP 5194497A JP 19449793 A JP19449793 A JP 19449793A JP H0748778 A JPH0748778 A JP H0748778A
- Authority
- JP
- Japan
- Prior art keywords
- artificial lawn
- ground
- artificial
- lawn
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、人工芝生製グラウンド
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an artificial lawn ground.
【０００２】[0002]
【従来の技術】従来より、アスファルトやセメントなど
の基礎層に直接もしくはクッション層を介して人工芝生
を敷設した人工芝生製グラウンドが知られている。ま
た、その人工芝生に砂を散布した人工芝生製グラウンド
も知られている。2. Description of the Related Art Conventionally, there is known an artificial lawn-made ground in which an artificial lawn is laid directly on a foundation layer such as asphalt or cement or through a cushion layer. In addition, an artificial lawn-made ground in which sand is sprayed on the artificial lawn is also known.
【０００３】このような人工芝生製グラウンドを構成す
る人工芝生としては、基布にポリアミド繊維とポリプロ
ピレン繊維を混合して撚り合わせ、所定のパイル長に植
毛して芝葉を形成したものが使用されている（例えば、
実公平４−３７９２３号公報参照）。As an artificial lawn that constitutes such an artificial lawn ground, there is used an artificial lawn in which polyamide fibers and polypropylene fibers are mixed and twisted in a base cloth and flocked to a predetermined pile length to form turf leaves. (For example,
(See Japanese Utility Model Publication No. 4-37923).
【０００４】[0004]
【発明が解決しようとする課題】ところで、このような
人工芝生を用いた人工芝生製グラウンドは、足がひっか
りやすく、特にスタッドを有するサッカーシューズの場
合にこの傾向が顕著となって足への負担が大きいという
問題があった。By the way, the artificial lawn-made ground using such an artificial lawn is prone to catching the foot, and this tendency becomes remarkable especially in the case of a soccer shoe having a stud. There was a problem that the burden was heavy.
【０００５】本発明は、このような問題点に鑑みてなさ
れたもので、足のひっかりを少なくしてプレー性を改善
することのできる人工芝生製グラウンドを提供するもの
である。The present invention has been made in view of the above problems, and provides an artificial lawn ground capable of improving playability by reducing the possibility of the foot being caught.
【０００６】[0006]
【課題を解決するための手段】本発明は、ポリアミド繊
維とポリエチレン繊維とを撚り合わせて基布に植毛した
人工芝生を直接もしくはクッション層を介して基礎層に
敷設したことを特徴とするものである。The present invention is characterized in that an artificial lawn in which polyamide fibers and polyethylene fibers are twisted together and flocked to a base cloth is laid directly or through a cushion layer on a base layer. is there.
【０００７】[0007]
【作用】基礎層に直接もしくはクッション層を介して敷
設した人工芝生は、ポリアミド繊維で立毛させて地面よ
り浮き上がらせるとともに、ポリエチレン繊維で表面の
摩擦抵抗を低減させる。The artificial lawn laid directly on the foundation layer or through the cushion layer is raised with polyamide fibers to lift it from the ground, and polyethylene fibers to reduce the frictional resistance of the surface.
【０００８】この結果、スタッドを有するシューズで競
技しても足のひっかりが少なくなり、プレー性を改善す
ることができる。As a result, even if a player wears a shoe having studs, the foot is less likely to be caught and the playability can be improved.
【０００９】[0009]
【実施例】以下、本発明の具体的な実施例について説明
する。EXAMPLES Specific examples of the present invention will be described below.
【００１０】図１には、本発明の人工芝生製グラウンド
１の第１実施例が示されている。この人工芝生製グラウ
ンド１は、基礎層２に人工芝生３が敷設された後、砂散
布機によって砂４が散布されて形成されている。そし
て、人工芝生３は、ポリプロピレン製基布５に５０００
デニール（以下単位記号Ｄで表わす）のポリアミド製ス
プリットヤーン６（太線で示す）と５０００Ｄの高密度
ポリエチレン製スプリットヤーン７（細線で示す）を撚
糸し、糸重量１．８Kg／m 2 、パイル長２５mmになるよ
うに植毛して芝葉を形成したものである。また、砂３
は、粒径２mm以下のものが使用され、３０Kg／m 2 の割
合で散布されている。FIG. 1 shows a first embodiment of an artificial lawn ground 1 according to the present invention. The artificial lawn ground 1 is formed by laying an artificial lawn 3 on a foundation layer 2 and then spraying sand 4 with a sand spreader. The artificial lawn 3 is made of a polypropylene base cloth 5 and 5000.
Polyamide split yarn 6 (denoted by thick line) of denier (denoted by unit D below) and high-density polyethylene split yarn 7 of 5000D (denoted by thin line) are twisted into a yarn weight of 1.8 Kg / m 2 , pile length The turf leaves are formed by planting hair so that the length becomes 25 mm. Also, sand 3
Has a particle size of 2 mm or less and is sprayed at a rate of 30 kg / m 2 .
【００１１】この人工芝生製グラウンド１をＪＩＳ Ａ
５７０５附属書床材の滑り試験方法（斜め引張形）を参
考に試験した。すなわち、滑り片としてスタッドを有す
るサッカーシューズの足先部を取り付け、８０Kgの荷重
を掛けて引っ張ったところ、この人工芝生製グラウンド
１の滑り抵抗係数は０．７であった。This artificial lawn ground 1 is JIS A
The test was carried out with reference to the slip test method (oblique tension type) of the floor material of Annex 5705. That is, when the foot portion of a soccer shoe having a stud as a slide piece was attached and pulled with a load of 80 kg, the slip resistance coefficient of this artificial grass ground 1 was 0.7.
【００１２】なお、サッカーなどの競技を行う場合、滑
り抵抗係数は０．４〜０．７が最適値とされている。When playing a game such as soccer, the optimum value of the slip resistance coefficient is 0.4 to 0.7.
【００１３】また、図２に示した人工芝生製グラウンド
１の第２実施例は、ポリプロピレン製基布５に２５００
Ｄのポリアミド製スプリットヤーン６と２５００Ｄの高
密度ポリエチレン製スプリットヤーン７を撚糸し、糸重
量１．５Kg／m 2 、パイル長１３mmになるように植毛し
て芝葉を形成した人工芝生３を基礎層２に敷設して形成
したものである。The second embodiment of the artificial lawn ground 1 shown in FIG.
Based on an artificial lawn 3 formed by twisting a polyamide split yarn 6 of D and a high density polyethylene split yarn 7 of 2500D, and flocking hair to a yarn weight of 1.5 kg / m 2 and a pile length of 13 mm. It is formed by being laid on the layer 2.
【００１４】この人工芝生製グラウンド１について同上
の試験を行ったところ、その滑り抵抗係数は０．６であ
った。When the above-mentioned test was conducted on the artificial lawn ground 1, the slip resistance coefficient was 0.6.
【００１５】さらに、図３に示した人工芝生製グラウン
ド１の第３実施例においては、人工芝生３は、ポリプロ
ピレン製基布５に５０００Ｄのポリアミド製スプリット
ヤーン６と５０００Ｄの高密度ポリエチレン製直毛糸ス
プリットヤーン７を撚糸し、糸重量１．８Kg／m 2 、パ
イル長２５mmになるように植毛して芝葉を形成した後、
裏打材をコーティングする際に加熱して高密度ポリエチ
レン製直毛糸スプリットヤーン７を収縮させたものであ
る。そして、この人工芝生３を基礎層２に敷設した後、
その人工芝生３に粒径２mm以下の砂４を３０Kg／m 2 の
割合で散布して人工芝生製グラウンド１を形成した。Further, in the third embodiment of the artificial lawn ground 1 shown in FIG. 3, the artificial lawn 3 comprises a polypropylene base cloth 5, a 5000D polyamide split yarn 6 and a 5000D high density polyethylene straight wool yarn. After split yarn 7 is twisted, the yarn weight is 1.8 Kg / m 2 , and the pile length is 25 mm, and after flocking to form lawn leaves,
This is a product in which the high-density polyethylene straight wool split yarn 7 is shrunk by heating when coating the backing material. And after laying this artificial lawn 3 on the foundation layer 2,
Sand 4 having a particle size of 2 mm or less was sprinkled on the artificial grass 3 at a rate of 30 kg / m 2 to form an artificial grass ground 1.
【００１６】この人工芝生製グラウンド１の滑り抵抗係
数は０．６であった。The slip resistance coefficient of this artificial lawn ground 1 was 0.6.
【００１７】なお、これらの実施例においては、人工芝
生３を直接基礎層２に敷設した人工芝生製グラウンド１
を例示したが、基礎層２にクッション層を敷設し、その
上に人工芝生３を敷設するようにしてもよい。In these examples, the artificial lawn ground 1 in which the artificial lawn 3 is laid directly on the foundation layer 2 is used.
Although the cushion layer is laid on the foundation layer 2, the artificial grass 3 may be laid on the cushion layer.
【００１８】次に、これら実施例と比較するため、従来
の人工芝生製グラウンドについて、その滑り抵抗係数を
測定した。Next, in order to make a comparison with these examples, the slip resistance coefficient of the conventional artificial lawn ground was measured.
【００１９】比較例１の人工芝生製グラウンドにおいて
使用された人工芝生は、ポリプロピレン製基布に４５０
Ｄのポリアミド製モノフィラメントを１２本収束すると
ともに撚糸し、糸重量１．５Kg／m 2 、パイル長１３mm
になるように植毛して芝葉を形成したものである。そし
て、この人工芝生を基礎層に敷設して人工芝生製グラウ
ンドを形成した。The artificial grass used in the artificial grass ground of Comparative Example 1 was a polypropylene base cloth with 450
Twelve polyamide monofilaments of D are bundled and twisted together, yarn weight 1.5 kg / m 2 , pile length 13 mm
The turf is formed by planting hair so that Then, this artificial grass was laid on the foundation layer to form an artificial grass ground.
【００２０】この人工芝生製グラウンドについて同上の
試験を行ったところ、その滑り抵抗係数は０．８であっ
た。When the above-mentioned test was conducted on this artificial lawn ground, the slip resistance coefficient was 0.8.
【００２１】比較例２の人工芝生製グラウンドにおいて
使用された人工芝生は、ポリプロピレン製基布に４５０
Ｄのポリアミド製モノフィラメントを６本収束したもの
と、４５０Ｄのポリプロピレン製モノフィラメントを６
本収束したものとを撚糸し、糸重量１．５Kg／m 2 、パ
イル長１３mmになるように植毛して芝葉を形成したもの
である。そして、この人工芝生を基礎層に敷設して人工
芝生製グラウンドを形成した。The artificial turf used in the artificial turf ground of Comparative Example 2 was made of polypropylene base cloth with 450
6 monofilaments made of polyamide D and 6 polypropylene monofilaments made of 450D
This converged yarn is twisted and flocked so that the yarn weight is 1.5 kg / m 2 and the pile length is 13 mm to form a turf leaf. Then, this artificial grass was laid on the foundation layer to form an artificial grass ground.
【００２２】この人工芝生製グラウンドの滑り抵抗係数
は０．９であった。The slip resistance coefficient of this artificial lawn ground was 0.9.
【００２３】また、比較例３の人工芝生製グラウンドに
おいて使用された人工芝生は、ポリプロピレン製基布に
４５０Ｄのポリアミド製モノフィラメントを２４本収束
するとともに撚糸し、糸重量１．８Kg／m 2 、パイル長
２５mmになるように植毛して芝葉を形成したものであ
る。そして、この人工芝生を基礎層に敷設した後、その
人工芝生に砂散布機を用いて粒径２mm以下の砂を３０Kg
／m 2 の割合で散布して人工芝生製グラウンドを形成し
た。The artificial lawn used in the artificial lawn ground of Comparative Example 3 was obtained by converging 24 filaments of 450D polyamide monofilament on a polypropylene base cloth and twisting the yarn, and the yarn weight was 1.8 Kg / m 2 , pile. The turf is formed by planting hair so that the length is 25 mm. Then, after laying this artificial lawn on the foundation layer, 30 kg of sand with a particle size of 2 mm or less is applied to the artificial lawn using a sand spreader.
/ M 2 was sprayed to form an artificial lawn ground.
【００２４】この人工芝生製グラウンドについて同上の
試験を行ったところ、その滑り抵抗係数は１．０であっ
た。When the above-mentioned test was conducted on the artificial lawn ground, the slip resistance coefficient was 1.0.
【００２５】一方、比較例４の人工芝生製グラウンドに
おいて使用された人工芝生は、ポリプロピレン製基布に
５０００Ｄのポリプロピレン製スプリットヤーンと５０
００Ｄのポリアミド製スプリットヤーンを撚糸し、糸重
量１．８Kg／m 2 、パイル長２５mmになるように植毛し
て芝葉を形成したものである。そして、この人工芝生を
基礎層に敷設した後、その人工芝生に砂散布機を用いて
粒径２mm以下の砂を３０Kg／m 2 の割合で散布して人工
芝生製グラウンドを形成した。On the other hand, the artificial lawn used in the artificial lawn ground of Comparative Example 4 was prepared by using a polypropylene base fabric and a polypropylene split yarn of 5000D and 50
A polyamide split yarn of 00D is twisted, and flocked so that the yarn weight is 1.8 Kg / m 2 and the pile length is 25 mm to form turf leaves. Then, after laying this artificial lawn on the foundation layer, sand having a particle size of 2 mm or less was sprinkled on the artificial lawn at a rate of 30 kg / m 2 to form an artificial lawn ground.
【００２６】この人工芝生製グラウンドの滑り抵抗係数
は１．１であった。The slip resistance coefficient of this artificial lawn ground was 1.1.
【００２７】また、比較例５の人工芝生製グラウンドに
おいて使用された人工芝生は、ポリプロピレン製基布に
１００００Ｄのポリプロピレン製スプリットヤーンを撚
糸し、糸重量１．８Kg／m 2 、パイル長２５mmになるよ
うに植毛して芝葉を形成したものである。そして、この
人工芝生を基礎層に敷設した後、その人工芝生に砂散布
機を用いて粒径２mm以下の砂を３０Kg／m 2 の割合で散
布して人工芝生製グラウンドを形成した。The artificial lawn used in the artificial lawn ground of Comparative Example 5 was obtained by twisting 10000D polypropylene split yarn on a polypropylene base cloth to give a yarn weight of 1.8 Kg / m 2 and a pile length of 25 mm. As described above, turf is formed by planting hair. Then, after laying this artificial lawn on the foundation layer, sand having a particle size of 2 mm or less was sprinkled on the artificial lawn at a rate of 30 kg / m 2 to form an artificial lawn ground.
【００２８】この人工芝生製グラウンドについて同上の
試験を行ったところ、その滑り抵抗係数は１．２であっ
た。When the above-mentioned test was conducted on this artificial lawn ground, the slip resistance coefficient was 1.2.
【００２９】さらに、比較例６の人工芝生製グラウンド
における人工芝生は、ポリプロピレン製基布に１０００
０Ｄのポリアミド製スプリットヤーンを撚糸し、糸重量
１．８Kg／m 2 、パイル長２５mmになるように植毛して
芝葉を形成したものである。そして、この人工芝生を基
礎層に敷設した後、その人工芝生に砂散布機を用いて粒
径２mm以下の砂を３０Kg／m 2 の割合で散布して人工芝
生製グラウンドを形成した。Further, the artificial grass in the artificial grass ground of Comparative Example 6 was prepared by adding 1000 to polypropylene base cloth.
A 0D polyamide split yarn is twisted, and flocked so that the yarn weight is 1.8 kg / m 2 and the pile length is 25 mm to form turf leaves. Then, after laying this artificial lawn on the foundation layer, sand having a particle size of 2 mm or less was sprinkled on the artificial lawn at a rate of 30 kg / m 2 to form an artificial lawn ground.
【００３０】この人工芝生製グラウンドの滑り抵抗係数
は１．１であった。The slip resistance coefficient of this artificial lawn ground was 1.1.
【００３１】なお、これらの実施例においては、ポリア
ミド繊維とポリエチレン繊維とを撚り合わせて芝葉とし
た人工芝生を例示したが、ポリエチレン繊維に代えてポ
リエチレンとポリオレフィンとを共重合してなる繊維を
使用してもよい。In these examples, artificial lawn in which polyamide fibers and polyethylene fibers are twisted and turfed is illustrated, but fibers formed by copolymerizing polyethylene and polyolefin instead of polyethylene fibers are used. May be used.
【００３２】[0032]
【発明の効果】以上のように本発明によれば、ポリアミ
ド繊維とポリエチレン繊維とを撚り合わせて基布に植毛
した人工芝生を直接もしくはクッション層を介して基礎
層に敷設したことにより、ポリアミド繊維で立毛させて
地面より浮き上がらせるとともに、ポリエチレン繊維で
表面の摩擦抵抗を低減させることから、スタッドを有す
るシューズで競技しても足のひっかりが少なくなり、プ
レー性を改善することができる。As described above, according to the present invention, an artificial lawn in which polyamide fibers and polyethylene fibers are twisted and planted on a base fabric is laid directly or through a cushion layer on the base layer, whereby polyamide fibers are obtained. Since it is raised up from the ground and raised from the ground, and the friction resistance of the surface is reduced by polyethylene fiber, it is possible to improve the playability by reducing foot catching even when competing in shoes having studs.
【図１】本発明の人工芝生製グラウンドの第１実施例を
示す断面図である。FIG. 1 is a cross-sectional view showing a first embodiment of an artificial lawn ground according to the present invention.
【図２】本発明の人工芝生製グラウンドの第２実施例を
示す断面図である。FIG. 2 is a cross-sectional view showing a second embodiment of the artificial lawn ground according to the present invention.
【図３】本発明の人工芝生製グラウンドの第３実施例を
示す断面図である。FIG. 3 is a sectional view showing a third embodiment of the artificial lawn ground of the present invention.
１ 人工芝生製グラウンド ２ 基礎層 ３ 人工芝生 ４ 砂 ５ 基布 ６ ポリアミド繊維 ７ ポリエチレン繊維 1 Ground made of artificial grass 2 Foundation layer 3 Artificial grass 4 Sand 5 Base cloth 6 Polyamide fiber 7 Polyethylene fiber
Claims (1)
撚り合わせて基布に植毛した人工芝生を直接もしくはク
ッション層を介して基礎層に敷設したことを特徴とする
人工芝生製グラウンド。1. An artificial lawn ground, characterized in that an artificial lawn in which polyamide fibers and polyethylene fibers are twisted and planted on a base fabric is laid on a foundation layer directly or via a cushion layer.