JPH0741042A - Capping material for press-through-pack and press-through-pack utilizing the capping material - Google Patents
Capping material for press-through-pack and press-through-pack utilizing the capping materialInfo
- Publication number
- JPH0741042A JPH0741042A JP20988393A JP20988393A JPH0741042A JP H0741042 A JPH0741042 A JP H0741042A JP 20988393 A JP20988393 A JP 20988393A JP 20988393 A JP20988393 A JP 20988393A JP H0741042 A JPH0741042 A JP H0741042A
- Authority
- JP
- Japan
- Prior art keywords
- press
- pack
- heat
- resin layer
- stretched polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、主として医薬品等の錠
剤の包装に使用するプレススルーパック用蓋材、及び該
蓋材を利用したプレススルーパックに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cover material for a press-through pack mainly used for packaging tablets such as pharmaceuticals, and a press-through pack using the cover material.
【０００２】[0002]
【従来の技術】医薬品等の錠剤を内容物とする包装体と
して、内容物収納用の凹部が形成されている合成樹脂製
の底材と、該底材における内容物収納用の凹部を閉塞す
る蓋材とからなり、蓋材として押圧破断が容易なアルミ
ニウム箔が使用されており、押圧によって蓋材を破断
し、包装体内の錠剤等の内容物の取り出しが行なえる所
謂プレススルーパックが利用されている。2. Description of the Related Art As a package containing tablets such as pharmaceuticals as contents, a bottom member made of synthetic resin in which a recess for storing contents is formed and a recess for storing contents in the bottom member are closed. A so-called press-through pack is used that consists of a lid material and uses an aluminum foil that is easy to press and rupture as the lid material and that can rupture the lid material by pressing and take out the contents such as tablets in the package. ing.
【０００３】なお、前記プレススルーパックの底材に
は、厚さ０．２〜０．４ｍｍ程度のポリ塩化ビニル樹
脂、ポリプロピレン樹脂、ポリエチレン樹脂等のプラス
チックシートに錠剤等の内容物収納用の凹部を賦形させ
たものを使用し、蓋材には、厚さ２０〜３０μ程度のア
ルミニウム箔にヒートシール層を積層した積層シートを
利用している。The bottom material of the press-through pack is a plastic sheet of polyvinyl chloride resin, polypropylene resin, polyethylene resin or the like having a thickness of about 0.2 to 0.4 mm, and a recess for storing contents such as tablets. Is used, and the lid material is a laminated sheet in which a heat seal layer is laminated on an aluminum foil having a thickness of about 20 to 30 μm.
【０００４】[0004]
【発明が解決しようとする課題】ところで、前記従来の
アルミニウム箔を蓋材とするプレススルーパックは、ア
ルミニウム箔自体が高価である、ピンホール等が発生し
易く防湿性に対する信頼性が完全ではない、不透明なた
めに蓋材側からの光等による内容物の自動検知を行なう
ことができない等の欠点を有する。By the way, in the above-mentioned press-through pack using the conventional aluminum foil as a cover material, the aluminum foil itself is expensive, pinholes and the like are apt to occur, and the reliability of moisture resistance is not perfect. Since it is opaque, it has the drawback that it cannot automatically detect the contents by light from the lid material side.
【０００５】さらに、アルミニウム箔を蓋材とするプレ
ススルーパックは、アルミニウム箔が不燃物であるた
め、焼却処理によって燃え残りが発生することから廃棄
処理上での問題点をも有する。特に、近年、地球環境保
護の観点からリサイクルが可能な素材または完全に焼却
し得る素材による包装体が望まれている。Further, the press-through pack having an aluminum foil as a cover material has a problem in waste disposal because the aluminum foil is a non-combustible material, and unburned residue is generated by incineration. In particular, in recent years, a package made of a recyclable material or a completely incinerable material has been desired from the viewpoint of protecting the global environment.
【０００６】これに対して本発明は、透明性、防湿性等
に優れ、しかも、廃棄処理が容易で、かつ、リサイクル
にも供し得るプレススルーパック用蓋材、及び該蓋材を
利用したプレススルーパックを提供する。On the other hand, the present invention is excellent in transparency, moisture proof, etc., is easy to dispose of, and can be recycled, and a press-through pack lid, and a press using the lid. Provide through pack.
【０００７】[0007]
【課題を解決するための手段】本発明は、１軸延伸ポリ
プロピレン系フィルムの一方の面に熱溶着性能を有する
樹脂層からなるヒートシール層を積層した後、前記１軸
延伸ポリプロピレン系フィルム側に電子線を照射したプ
レススルーパック用蓋材からなる。According to the present invention, a uniaxially stretched polypropylene film is laminated on one surface with a heat-sealing layer made of a resin layer having a heat-welding property, and then the uniaxially stretched polypropylene film is provided with a heat seal layer. It consists of a lid material for a press-through pack that is irradiated with an electron beam.
【０００８】また本発明は、１軸延伸ポリプロピレン系
フィルムの一方の面に熱溶着性能を有する樹脂層からな
るヒートシール層を積層した後、前記１軸延伸ポリプロ
ピレン系フィルム側に電子線を照射し、さらに、該電子
線の照射面に、ガスバリヤー性能を有するバリヤー層を
形成したプレススルーパック用蓋材からなる。Further, according to the present invention, a heat-sealing layer made of a resin layer having a heat-welding property is laminated on one surface of a uniaxially stretched polypropylene film, and then the uniaxially stretched polypropylene film side is irradiated with an electron beam. Further, it comprises a cover material for a press-through pack in which a barrier layer having a gas barrier property is formed on the surface irradiated with the electron beam.
【０００９】また本発明は、１軸延伸ポリプロピレン系
フィルムに電子線を照射した後、該１軸延伸ポリプロピ
レン系フィルムの一方の面に熱溶着性能を有する樹脂層
からなるヒートシール層を積層したプレススルーパック
用蓋材からなる。Further, according to the present invention, the uniaxially stretched polypropylene film is irradiated with an electron beam, and then a heat-sealing layer made of a resin layer having heat welding performance is laminated on one surface of the uniaxially stretched polypropylene film. It consists of a lid material for through packs.
【００１０】さらに本発明は、１軸延伸ポリプロピレン
系フィルムに電子線を照射した後、該１軸延伸ポリプロ
ピレン系フィルムの一方の面に熱溶着性能を有する樹脂
層からなるヒートシール層を積層すると共に、他方の面
に、ガスバリヤー性能を有するバリヤー層を形成したプ
レススルーパック用蓋材からなる。Further, according to the present invention, after the uniaxially stretched polypropylene film is irradiated with an electron beam, a heat seal layer composed of a resin layer having a heat welding property is laminated on one surface of the uniaxially stretched polypropylene film. A cover material for a press-through pack having a barrier layer having a gas barrier property formed on the other surface.
【００１１】さらに本発明は、「ポリプロピレン系樹脂
層／ガスバリヤー性能を有するバリヤー層／ポリプロピ
レン系樹脂層」の積層構成を有する１軸延伸ポリプロピ
レン系積層フィルムの一方の面に熱溶着性能を有する樹
脂層からなるヒートシール層を積層した後、前記１軸延
伸ポリプロピレン系積層フィルム側に電子線を照射した
プレススルーパック用蓋材からなる。The present invention further relates to a resin having a heat-welding performance on one surface of a uniaxially stretched polypropylene-based laminated film having a laminated structure of "polypropylene-based resin layer / barrier layer having gas barrier performance / polypropylene-based resin layer". After laminating a heat-sealing layer consisting of layers, the uniaxially stretched polypropylene-based laminated film side is irradiated with an electron beam to form a press-through pack cover material.
【００１２】さらにまた本発明は、「ポリプロピレン系
樹脂層／ガスバリヤー性能を有するバリヤー層／ポリプ
ロピレン系樹脂層」の積層構成を有する１軸延伸ポリプ
ロピレン系積層フィルムに電子線を照射した後、該１軸
延伸ポリプロピレン系積層フィルムの一方の面に熱溶着
性能を有する樹脂層からなるヒートシール層を積層した
プレススルーパック用蓋材からなる。Furthermore, the present invention further comprises the step of irradiating an electron beam on a uniaxially stretched polypropylene-based laminated film having a laminated structure of "polypropylene-based resin layer / barrier layer having gas barrier performance / polypropylene-based resin layer", A cover material for a press-through pack in which a heat-sealing layer made of a resin layer having a heat-welding property is laminated on one surface of an axially stretched polypropylene-based laminated film.
【００１３】さらにまた本発明は、錠剤収納用の凹部が
形成されている合成樹脂製の底材と、該底材における錠
剤収納用の凹部を閉塞するプレススルーパック用蓋材と
からなるプレススルーパックにおいて、プレススルーパ
ック用蓋材が前記した各プレススルーパック用蓋材から
なる。Further, according to the present invention, a press-through comprising a synthetic resin bottom material in which a concave portion for tablet storage is formed and a press-through pack lid material for closing the concave portion for tablet storage in the bottom material. In the pack, the cover material for press-through pack is composed of the above-mentioned cover material for press-through pack.
【００１４】本発明のプレススルーパック用蓋材及び該
蓋材を利用したプレススルーパックにおいて、蓋材に使
用される１軸延伸ポリプロピレン系フィルムまたは１軸
延伸ポリプロピレン系積層フィルムにおけるポリプロピ
レン系樹脂には、プロピレン重合体、またはプロピレン
と共重合可能なモノマー例えばエチレンやブテン等とプ
ロピレンとの共重合体が使用される。In the cover material for a press-through pack of the present invention and the press-through pack using the cover material, the polypropylene resin in the uniaxially stretched polypropylene film or the uniaxially stretched polypropylene laminated film used for the cover material is , A propylene polymer, or a copolymer of propylene and a monomer copolymerizable with propylene, such as ethylene or butene.
【００１５】１軸延伸ポリプロピレン系フィルムまたは
１軸延伸ポリプロピレン系積層フィルムは、製膜原料に
よって得られた所定の原反を、１軸方向に延伸して配向
させたものであり、延伸倍率３〜１５程度のものが好適
である。The uniaxially stretched polypropylene-based film or the uniaxially stretched polypropylene-based laminated film is obtained by stretching a predetermined material obtained from a film-forming raw material in a uniaxial direction and orienting it. The thing of about 15 is suitable.
【００１６】本発明のプレススルーパック用蓋材は、熱
溶着性能を有する樹脂層によるヒートシール層を利用し
て、真空圧空成形体等からなるプレススルーパックの底
材に熱溶着され、プレススルーパックに形成される。The lid material for a press-through pack of the present invention is heat-welded to the bottom material of a press-through pack composed of a vacuum-pressure air-molded body or the like by using a heat-sealing layer made of a resin layer having a heat-welding performance, and press-through. Formed in a pack.
【００１７】ヒートシール層には、例えばポリエチレン
やポリプロピレン等のオレフィン系樹脂層、ポリエステ
ル系樹脂層、ウレタン変性ポリエステル系樹脂層等の汎
用のヒートシール層が利用される。As the heat seal layer, a general heat seal layer such as an olefin resin layer such as polyethylene or polypropylene, a polyester resin layer, a urethane-modified polyester resin layer or the like is used.
【００１８】また、ガスバリヤー性能を有するバリヤー
層には、ポリ塩化ビニリデン樹脂やエチレン−ビニルア
ルコール共重合体樹脂等による樹脂層、シリカ等の無機
物による蒸着層等が利用される。Further, as the barrier layer having a gas barrier property, a resin layer made of polyvinylidene chloride resin, ethylene-vinyl alcohol copolymer resin or the like, a vapor deposition layer made of an inorganic material such as silica or the like is used.
【００１９】本発明のプレススルーパック用蓋材の具体
的な積層構成は、例えば、 (1) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／印刷層 (2) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／ポリ塩化ビニリデン樹脂層／印刷層 (3) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／エチレン−ビニルアルコール共重合体樹脂層／印刷
層 (4) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／シリカの蒸着層／印刷層 (5) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／シリカの蒸着層／印刷層／１軸延伸ポリプロピレン
系フィルム (6) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／エチレン−ビニルアルコール共重合体樹脂層／印刷
層／ポリエチレン樹脂層 (7) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／ポリ塩化ビニリデン樹脂層／ポリエチレン樹脂層／
印刷層 (8) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／ポリ塩化ビニリデン樹脂層／印刷層／ポリエチレン
樹脂層 (9) ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／シリカの蒸着層／ポリエチレン樹脂層／印刷層 (10)ヒートシール層／１軸延伸ポリプロピレン系フィル
ム／シリカの蒸着層／印刷層／ポリエチレン樹脂層 (11)ヒートシール層／ポリプロピレン系樹脂層・エチレ
ン−ビニルアルコール共重合体樹脂層・ポリプロピレン
系樹脂層の３層構成からなる１軸延伸ポリプロピレン系
積層フィルム／印刷層 (12)ヒートシール層／ポリプロピレン系樹脂層・ポリ塩
化ビニリデン樹脂層・ポリプロピレン系樹脂層の３層構
成からなる１軸延伸ポリプロピレン系積層フィルム／印
刷層等である。A specific laminated structure of the cover material for a press-through pack of the present invention is, for example, (1) heat seal layer / uniaxially stretched polypropylene film / printing layer (2) heat seal layer / uniaxially stretched polypropylene system Film / Polyvinylidene chloride resin layer / Printing layer (3) Heat seal layer / Uniaxially stretched polypropylene film / Ethylene-vinyl alcohol copolymer resin layer / Printing layer (4) Heat seal layer / Uniaxially stretched polypropylene film / Silica vapor deposition layer / printing layer (5) Heat seal layer / uniaxially oriented polypropylene film / silica vapor deposition layer / printing layer / uniaxially oriented polypropylene film (6) Heat sealing layer / uniaxially oriented polypropylene film / ethylene -Vinyl alcohol copolymer resin layer / printing layer / polyethylene resin layer (7) Heat seal layer / uniaxially stretched polypropylene System film / polyvinylidene chloride resin layer / polyethylene resin layer /
Print layer (8) Heat seal layer / uniaxially oriented polypropylene film / polyvinylidene chloride resin layer / printing layer / polyethylene resin layer (9) Heat seal layer / uniaxially oriented polypropylene film / silica vapor deposition layer / polyethylene resin layer / Printing layer (10) Heat seal layer / Uniaxially stretched polypropylene film / Silica vapor deposition layer / Printing layer / Polyethylene resin layer (11) Heat seal layer / Polypropylene resin layer-Ethylene-vinyl alcohol copolymer resin layer- Uniaxially stretched polypropylene-based laminated film consisting of three layers of polypropylene-based resin layer / printing layer (12) Heat-sealing layer / polypropylene-based resin layer, polyvinylidene chloride resin layer, polypropylene-based resin layer It is a stretched polypropylene-based laminated film / printing layer.
【００２０】プレススルーパック用蓋材に必要に応じて
付される印刷インキによる印刷層は、商品名、製造，販
売会社名、プレススルーパック内の内容物の取り出し方
法を表示するマークや文字等であり、内容物に接するこ
とのない部分に付される。The printing layer made of printing ink, which is optionally attached to the cover material for the press-through pack, is a product name, a manufacturing or sales company name, a mark or a character indicating the method of taking out the contents from the press-through pack, etc. It is attached to the part that is not in contact with the contents.
【００２１】また、本発明のプレススルーパックにおい
て利用される底材には、従来のプレススルーパックに使
用されている底材と全く同様のものを利用し得る。The bottom material used in the press-through pack of the present invention may be the same as the bottom material used in the conventional press-through pack.
【００２２】[0022]
【実施例】本発明のプレススルーパック用蓋材及び該蓋
材を利用したプレススルーパックの具体的な構成を実施
例に基づいて説明する。EXAMPLE A concrete structure of a cover material for a press-through pack of the present invention and a press-through pack using the cover material will be described based on examples.
【００２３】参考例１〜参考例４ 厚さ２５μの１軸延伸ポリプロピレンフィルム（延伸倍
率：６）に、［表１］の所定欄に記載した強度の電子線
を照射することにより、本発明のプレススルーパック用
蓋材に使用する１軸延伸ポリプロピレンフィルムを得
た。Reference Example 1 to Reference Example 4 A uniaxially stretched polypropylene film (stretching ratio: 6) having a thickness of 25 μm was irradiated with an electron beam having the intensity described in the predetermined column of [Table 1] to obtain the present invention. A uniaxially stretched polypropylene film used as a cover material for a press-through pack was obtained.
【００２４】電子線の照射後の１軸延伸ポリプロピレン
フィルムのＪＩＳ Ｋ ６７３４による引張強さ（ｋｇ
ｆ／ｍｍ2 ）と引張破壊伸び（％）を［表１］に併記す
る。Tensile strength (kg) according to JIS K 6734 of uniaxially stretched polypropylene film after electron beam irradiation
f / mm 2 ) and tensile fracture elongation (%) are also shown in [Table 1].
【００２５】[0025]
【表１】 [Table 1]
【００２６】参考例５〜参考例８ 「ポリプロピレン樹脂層／エチレン−ビニルアルコール
共重合体樹脂層／ポリプロピレン樹脂層」からなる３層
共押し出しフィルムを１軸延伸して配向させた厚さ２５
μの積層フィルム（延伸倍率：６）に、［表２］の所定
欄に記載した強度の電子線を照射することにより、本発
明のプレススルーパック用蓋材に使用する１軸延伸ポリ
プロピレン系積層フィルムを得た。Reference Example 5 to Reference Example 8 A three-layer coextruded film composed of "polypropylene resin layer / ethylene-vinyl alcohol copolymer resin layer / polypropylene resin layer" is uniaxially stretched to have a thickness of 25.
A monoaxially oriented polypropylene-based laminate used for the cover material for a press-through pack of the present invention is obtained by irradiating a laminated film (stretching ratio: 6) of μ with an electron beam having the intensity described in the predetermined column of [Table 2]. I got a film.
【００２７】電子線の照射後の１軸延伸ポリプロピレン
フィルムのＪＩＳ Ｋ ６７３４による引張強さ（ｋｇ
ｆ／ｍｍ2 ）と引張破壊伸び（％）を［表２］に併記す
る。Tensile strength (kg) according to JIS K 6734 of uniaxially stretched polypropylene film after electron beam irradiation
f / mm 2 ) and tensile fracture elongation (%) are also shown in [Table 2].
【００２８】[0028]
【表２】 [Table 2]
【００２９】実施例１〜８ ［図１］において、厚さ２５０μのポリプロピレンシー
トを成形用素材とする真空圧空成形により、錠剤収納用
の独立した複数の凹部２を有する底材３を得た。In Examples 1 to 8 [FIG. 1], a bottom material 3 having a plurality of independent recesses 2 for storing tablets was obtained by vacuum pressure forming using a polypropylene sheet having a thickness of 250 μ as a molding material.
【００３０】続いて、前記底材３の凹部２に錠剤Ｍを収
納した後、プレススルーパック用蓋材６を、シールヘッ
ド温度１３０℃、シール時間１秒、シール圧３ｋｇｆ／
ｃｍ2 のシール条件によって熱溶着し、本発明の実施例
品であるプレススルーパック１を得た。Subsequently, after the tablets M are stored in the recesses 2 of the bottom material 3, the press-through pack lid material 6 is sealed with a seal head temperature of 130 ° C., a sealing time of 1 second, and a sealing pressure of 3 kgf /.
Heat welding was performed under a sealing condition of cm 2 to obtain a press-through pack 1 as an example product of the present invention.
【００３１】なお、プレススルーパック用蓋材６は、前
記各参考例によるフィルムのそれぞれに、印刷インキに
よる印刷層を付すことによって、１軸延伸ポリプロピレ
ンフィルムまたは１軸延伸ポリプロピレン系積層フィル
ム４を得た後、これらのフィルム４の印刷面の反対側
に、ポリエステル系ヒートシール剤またはウレタン変性
ポリエステル系ヒートシール剤によるヒートシール層５
を形成したものからなる。In the press-through pack cover 6, a uniaxially stretched polypropylene film or a uniaxially stretched polypropylene-based laminated film 4 is obtained by attaching a printing layer of printing ink to each of the films according to the above-mentioned reference examples. Then, a heat-sealing layer 5 made of a polyester heat-sealing agent or a urethane-modified polyester heat-sealing agent is provided on the side opposite to the printed surface of these films 4.
Is formed.
【００３２】得られたプレススルーパック１は、その全
体に亙って透明性に優れており、また、内容物である錠
剤Ｍを底材３側から押圧することによって蓋材６を破断
し、錠剤Ｍを包装体内から取り出す際の取り出し操作が
容易であった。The obtained press-through pack 1 is excellent in transparency as a whole, and the lid material 6 is broken by pressing the tablet M which is the content from the bottom material 3 side, The taking-out operation when taking out the tablet M from the package was easy.
【００３３】[0033]
【作用，効果】本発明のプレススルーパック用蓋材によ
れば、蓋材に利用されている１軸延伸ポリプロピレン系
フィルムまたは１軸延伸ポリプロピレン系積層フィルム
が、１軸方向に配向しており、しかも、電子線の照射に
より劣化している。このため、該フィルムの特性により
押圧で蓋材が容易に簾状に引き裂かれることから、的確
なプレススルー機能が奏される。According to the lid material for a press-through pack of the present invention, the uniaxially stretched polypropylene film or the uniaxially stretched polypropylene laminated film used for the lid material is uniaxially oriented, Moreover, it is deteriorated by the electron beam irradiation. For this reason, the lid material is easily torn in the shape of a blind due to the characteristics of the film, so that an accurate press-through function is achieved.
【００３４】また、前記プレススルーパック用蓋材は、
アルミニウム箔におけるようなピンホールの発生の危険
性が無く、防湿性においての信頼性が高く、内容物の保
存特性に優れた作用，効果を奏する。The lid material for the press-through pack is
There is no risk of pinholes as in the case of aluminum foil, the moisture resistance is highly reliable, and the storage characteristics of the contents are excellent.
【００３５】さらに、本発明のプレススルーパック用蓋
材は、透明性に優れた特性を有しているため、光等によ
る内容物の自動検知を行なうことができる。Further, since the cover material for a press-through pack of the present invention has excellent transparency, the contents can be automatically detected by light or the like.
【００３６】また、本発明のプレススルーパック用蓋材
は、焼却の際の残存物が無いために廃棄処理が容易であ
り、また、プラスチックス素材としてリサイクルが可能
なため、省資源の面でのメリットも有する。The cover material for a press-through pack of the present invention is easy to dispose because there is no residue at the time of incineration, and can be recycled as a plastics material, so that it is resource-saving. It also has the advantage of.
【００３７】本発明のプレススルーパックは、前記特性
を有するプレススルーパック用蓋材を利用するものであ
り、該蓋材による作用，効果の悉くがそのまま奏され
る。The press-through pack of the present invention utilizes the cover material for press-through pack having the above-mentioned characteristics, and the action and effect of the cover material can be exerted as it is.
【図１】プレススルーパックの１例を示す要部断面図で
ある。FIG. 1 is a sectional view of an essential part showing an example of a press-through pack.
１：プレススルーパック ２：底材に形成されている内容物収納用の凹部 ３：底材 ４：１軸延伸ポリプロピレン系フィルムまたは１軸延伸
ポリプロピレン系積層フィルム ５：ヒートシール層 ６：プレススルーパック用蓋材1: Press-through pack 2: Recess for storing contents formed in bottom material 3: Bottom material 4: 1-axis oriented polypropylene film or uniaxially-oriented polypropylene laminated film 5: Heat seal layer 6: Press-through pack Lid material
Claims (7)
一方の面に熱溶着性能を有する樹脂層からなるヒートシ
ール層を積層した後、前記１軸延伸ポリプロピレン系フ
ィルム側に電子線を照射したことを特徴とするプレスス
ルーパック用蓋材。1. A uniaxially stretched polypropylene-based film is laminated on one surface with a heat-sealing layer made of a resin layer having a heat-welding property, and then the uniaxially stretched polypropylene-based film is irradiated with an electron beam. Cover material for press through packs.
一方の面に熱溶着性能を有する樹脂層からなるヒートシ
ール層を積層した後、前記１軸延伸ポリプロピレン系フ
ィルム側に電子線を照射し、さらに、該電子線の照射面
に、ガスバリヤー性能を有するバリヤー層を形成したこ
とを特徴とするプレススルーパック用蓋材。2. A uniaxially stretched polypropylene-based film is laminated on one surface with a heat-sealing layer made of a resin layer having a heat-welding property, and then the uniaxially stretched polypropylene-based film is irradiated with an electron beam, and further, A cover material for a press-through pack, characterized in that a barrier layer having a gas barrier property is formed on the surface irradiated with the electron beam.
電子線を照射した後、該１軸延伸ポリプロピレン系フィ
ルムの一方の面に熱溶着性能を有する樹脂層からなるヒ
ートシール層を積層したことを特徴とするプレススルー
パック用蓋材。3. A uniaxially stretched polypropylene-based film is irradiated with an electron beam, and then a heat-sealing layer made of a resin layer having a heat-welding property is laminated on one surface of the uniaxially-stretched polypropylene-based film. Press-through pack lid material.
電子線を照射した後、該１軸延伸ポリプロピレン系フィ
ルムの一方の面に熱溶着性能を有する樹脂層からなるヒ
ートシール層を積層すると共に、他方の面に、ガスバリ
ヤー性能を有するバリヤー層を形成したことを特徴とす
るプレススルーパック用蓋材。4. A uniaxially stretched polypropylene-based film is irradiated with an electron beam, and then a heat-sealing layer made of a resin layer having a heat-welding property is laminated on one surface of the uniaxially-stretched polypropylene-based film, while the other one is laminated. A cover material for a press-through pack, characterized in that a barrier layer having a gas barrier property is formed on the surface.
ー性能を有するバリヤー層／ポリプロピレン系樹脂層の
積層構成を有する１軸延伸ポリプロピレン系積層フィル
ムの一方の面に熱溶着性能を有する樹脂層からなるヒー
トシール層を積層した後、前記１軸延伸ポリプロピレン
系積層フィルム側に電子線を照射したことを特徴とする
プレススルーパック用蓋材。5. A heat seal comprising a resin layer having heat-welding performance on one surface of a uniaxially stretched polypropylene-based laminated film having a laminated structure of polypropylene resin layer / barrier layer having gas barrier performance / polypropylene resin layer. A lid material for a press-through pack, which comprises irradiating an electron beam on the uniaxially stretched polypropylene-based laminated film side after laminating the layers.
ー性能を有するバリヤー層／ポリプロピレン系樹脂層の
積層構成を有する１軸延伸ポリプロピレン系積層フィル
ムに電子線を照射した後、該１軸延伸ポリプロピレン系
積層フィルムの一方の面に熱溶着性能を有する樹脂層か
らなるヒートシール層を積層したことを特徴とするプレ
ススルーパック用蓋材。6. A uniaxially stretched polypropylene laminated film having a laminated structure of polypropylene resin layer / barrier layer having gas barrier performance / polypropylene resin layer is irradiated with an electron beam, and then the uniaxially stretched polypropylene laminated film. A cover material for a press-through pack, characterized in that a heat-sealing layer made of a resin layer having a heat-welding property is laminated on one surface.
合成樹脂製の底材と、該底材における内容物収納用の凹
部を閉塞するプレススルーパック用蓋材とからなるプレ
ススルーパックにおいて、前記プレススルーパック用蓋
材が請求項１〜請求項６のいずれかの１項に記載のプレ
ススルーパック用蓋材であることを特徴とするプレスス
ルーパック。7. A press through pack comprising: a synthetic resin bottom material having a recess for storing contents, and a press through pack lid member for closing the recess for storing contents in the bottom material. The press-through pack is a cover material for a press-through pack according to any one of claims 1 to 6.