JPH0730634B2 - ALC makeup panel repair structure - Google Patents
ALC makeup panel repair structureInfo
- Publication number
- JPH0730634B2 JPH0730634B2 JP5071898A JP7189893A JPH0730634B2 JP H0730634 B2 JPH0730634 B2 JP H0730634B2 JP 5071898 A JP5071898 A JP 5071898A JP 7189893 A JP7189893 A JP 7189893A JP H0730634 B2 JPH0730634 B2 JP H0730634B2
- Authority
- JP
- Japan
- Prior art keywords
- cement mortar
- alc
- coating film
- decorative
- decorative panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】[0001]
【産業上の利用分野】本発明は、壁パネル等として使用
されるALC化粧パネルの補修構造に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a repair structure for an ALC decorative panel used as a wall panel or the like.
【0002】[0002]
【従来の技術】ALC(Autoclaved Lightweight Concr
ete)はオートクレーブ養生して製造される軽量気泡コン
クリートであり、軽量で取扱いが容易であるなど各種の
利点があるために、ALCは家屋の壁パネルなど化粧パ
ネルとして使用されている。しかし反面、ALCは多孔
体であるために脆く、欠け等の欠損が発生し易いという
欠点がある。2. Description of the Related Art ALC (Autoclaved Lightweight Concr
ete) is a lightweight cellular concrete produced by autoclave curing, and has various advantages such as being lightweight and easy to handle. Therefore, ALC is used as a decorative panel such as a wall panel of a house. However, on the other hand, since ALC is a porous material, it is fragile, and defects such as chipping easily occur.
【0003】そこで従来からこの欠損部にセメントモル
タルを充填して欠損部を埋め、次にセメントモルタルの
表面にアクリル樹脂系塗料等を塗装して化粧塗膜を形成
することによって、欠損部を補修することがおこなわれ
ている。Therefore, conventionally, the defective portion is repaired by filling the defective portion with cement mortar to fill the defective portion, and then coating the surface of the cement mortar with an acrylic resin paint or the like to form a decorative coating film. Is being done.
【0004】[0004]
【発明が解決しようとする課題】このように補修をおこ
なうにあたって、欠損部を埋めたセメントモルタルの表
面に塗装をして化粧塗膜を形成することによって補修部
分が目立たないようにしているのであるが、セメントモ
ルタルに対する化粧塗膜の密着性が悪く、セメントモル
タルから化粧塗膜が剥がれて補修箇所の外観が不良にな
るおそれがあるという問題があった。In carrying out repair in this way, the surface of cement mortar in which the defect is filled is coated to form a decorative coating film so that the repaired portion is inconspicuous. However, there is a problem in that the adhesiveness of the decorative coating film to the cement mortar is poor, and the decorative coating film may peel off from the cement mortar, resulting in a poor appearance at the repaired portion.
【0005】本発明は上記の点に鑑みてなされたもので
あり、補修部が外観不良になることを防ぐことができる
ALC化粧パネルの補修構造を提供することを目的とす
るものである。The present invention has been made in view of the above points, and an object of the present invention is to provide a repair structure for an ALC decorative panel which can prevent the repair portion from having a poor appearance.
【0006】[0006]
【課題を解決するための手段】本発明に係るALC化粧
パネルの補修構造は、ALC化粧パネル1の表面の欠損
部2にセメントモルタル3を充填し、この充填したセメ
ントモルタル3の表面にポリマーセメントモルタル4を
塗布すると共にこのポリマーセメントモルタル4の表面
に化粧塗膜5を施して成ることを特徴とするものであ
る。A repair structure for an ALC decorative panel according to the present invention comprises a cement mortar 3 filled in a defective portion 2 on the surface of an ALC decorative panel 1, and the surface of the filled cement mortar 3 is polymer cement. It is characterized in that the mortar 4 is applied and a decorative coating film 5 is applied to the surface of the polymer cement mortar 4.
【0007】[0007]
【作用】ALC化粧パネル1の欠損部2に充填したセメ
ントモルタル3の表面にポリマーセメントモルタル4を
塗布すると共にこのポリマーセメントモルタル4の表面
に化粧塗膜5を施すようにしているので、ポリマーセメ
ントモルタル4によってセメントモルタル3への化粧塗
膜5の密着性を高めることができる。The polymer cement mortar 4 is applied to the surface of the cement mortar 3 filled in the defective portion 2 of the ALC decorative panel 1, and the decorative coating film 5 is applied to the surface of the polymer cement mortar 4 so that the polymer cement mortar 4 is applied. The mortar 4 can enhance the adhesion of the decorative coating film 5 to the cement mortar 3.
【0008】[0008]
【実施例】以下本発明を実施例によって詳述する。AL
C化粧パネル1は、必要に応じて補強筋を予めセットし
た型枠内にセメントスラリーを流し込んでオートクレー
ブ中で養生することによってALC板9を製造すると共
にALC板9の表面に無機塗料等を塗布して無機塗膜等
の化粧塗膜10で化粧することによって、作成されるも
のである。EXAMPLES The present invention will be described in detail below with reference to examples. AL
The C decorative panel 1 manufactures the ALC plate 9 by pouring the cement slurry into a mold in which reinforcing bars are set in advance and curing in an autoclave as necessary, and at the same time, applies an inorganic paint or the like to the surface of the ALC plate 9. Then, it is created by applying makeup with a makeup coating film 10 such as an inorganic coating film.
【0009】このALC化粧パネル1に物が当たったり
してその表面に欠損部2が生じた際に、欠損部2を補修
するにあたっては、まず欠損部2にセメントモルタル3
を充填して養生硬化させる。セメントモルタル3は表面
がALC化粧パネル1の化粧塗膜10の面よりもやや凹
んだレベルになるように欠損部2に充填されるものであ
る。このセメントモルタル3はセメントに骨材を混合し
て調製されるものであり、養生が1〜3日程度で終わる
ようにセメントとして早強セメントを用いるのが好まし
い。また骨材としては、パーライトや発泡頁岩、川砂な
どを用いることができるが、ALC化粧パネル1は軽量
のALCで形成されているために、骨材として軽量のパ
ーライトや発泡頁岩を用いてセメントモルタル3を軽量
化して、ALC化粧パネル1と重量上の物性を均一化す
るのが好ましい。このセメントモルタルのセメントと骨
材の配合比率は、重量比でセメント:骨材=40〜6
0:60〜40が好ましく、また水/セメント比は、W
/C=40〜80重量%が好ましい。When a defect 2 is formed on the surface of the ALC decorative panel 1 due to something hitting it, when repairing the defect 2, first the cement mortar 3 is applied to the defect 2.
To cure and cure. The cement mortar 3 is filled in the defect portion 2 so that the surface thereof is slightly recessed from the surface of the decorative coating film 10 of the ALC decorative panel 1. This cement mortar 3 is prepared by mixing cement with aggregate, and it is preferable to use early-strength cement as the cement so that the curing is completed in about 1 to 3 days. Further, as the aggregate, perlite, foamed shale, river sand, etc. can be used. However, since the ALC decorative panel 1 is made of lightweight ALC, cement mortar is made by using lightweight perlite or foamed shale as the aggregate. It is preferable to reduce the weight of 3 and make the physical properties of the ALC decorative panel 1 uniform in weight. The mixing ratio of cement and aggregate in this cement mortar is cement: aggregate = 40 to 6 by weight ratio.
0: 60-40 is preferable, and the water / cement ratio is W
/ C = 40 to 80% by weight is preferable.
【0010】このようにALC化粧パネル1の欠損部2
にセメントモルタル3を充填して養生硬化させた後、欠
損部2内においてセメントモルタル3の表面にポリマー
セメントモルタル4を塗布して硬化させる。ポリマーセ
メントモルタル(樹脂モルタル)4はエポキシ樹脂やア
クリル樹脂等の樹脂をセメントに混合して調製されるも
のであり、セメントモルタル3の表面に1〜3mm程度
の厚みで塗布して、熱風や赤外線等で50〜100℃に
加熱しつつ4〜10分程養生することによって硬化させ
ることができる。As described above, the defective portion 2 of the ALC decorative panel 1
After the cement mortar 3 is filled in and cured and hardened, the polymer cement mortar 4 is applied to the surface of the cement mortar 3 in the defect portion 2 and hardened. The polymer cement mortar (resin mortar) 4 is prepared by mixing a resin such as an epoxy resin or an acrylic resin with cement, and is applied to the surface of the cement mortar 3 with a thickness of about 1 to 3 mm to obtain hot air or infrared rays. It can be hardened by aging for 4 to 10 minutes while heating at 50 to 100 ° C.
【0011】このようにポリマーセメントモルタル4を
塗布して下地調整した後に、ポリマーセメントモルタル
4の表面に塗装を施す。この塗装は無機塗料やフッ素樹
脂系塗料などを用いておこなうことができるものであ
り、例えば20〜150g/m 2 の塗布量で塗布して、
30〜60分自然乾燥させるかあるいは50〜100℃
の温風で5〜10分間乾燥させることによって、化粧塗
膜5を形成することができる。この化粧塗膜5は欠損部
2に充填したセメントモルタル3を隠して化粧するため
のものであり、ALC化粧パネル1の表面に施した化粧
塗膜10と同じ色のものを用いるのが一般的であり、化
粧塗膜5,10の各表面が面一になるように塗装をおこ
なうようにしてある。また、化粧塗膜5を無機塗料やフ
ッ素樹脂系塗料を塗布して形成するようにすれば、これ
らは耐候性に優れているために長期に亘ってセメントモ
ルタル3を化粧することができるものである。Thus, the polymer cement mortar 4 is
After applying and adjusting the base, polymer cement mortar
The surface of 4 is painted. This paint is inorganic paint or fluorine
It can be done using oil-based paint.
For example, 20 to 150 g / m 2Apply with the application amount of
Allow to air dry for 30-60 minutes or 50-100 ° C
Make-up by drying with warm air for 5-10 minutes
The film 5 can be formed. This decorative coating 5 has a defect
To hide the cement mortar 3 filled in 2 for makeup
And the makeup applied to the surface of the ALC decorative panel 1.
It is common to use the same color as the coating film 10.
Paint so that the surfaces of the decorative coatings 5 and 10 are flush with each other.
It's done like this. In addition, the makeup paint film 5 is applied to an inorganic paint or a film.
If it is formed by applying a fluorine resin-based paint, this
Since they have excellent weather resistance,
Lutar 3 can be put on.
【0012】このようにして、図1に示すようにALC
化粧パネル1の欠損部2にセメントモルタル3を充填す
ると共にセメントモルタル3の表面にポリマーセメント
モルタル4を介して化粧塗膜5を設けることによって補
修をおこなうことができるものであり、ポリマーセメン
トモルタル4はセメントモルタル3に対しても、化粧塗
膜5に対しても密着性が良好であるために、化粧塗膜5
がポリマーセメントモルタル4から剥がれるようなこと
を防止することができるものである。In this way, as shown in FIG.
The defect portion 2 of the decorative panel 1 is filled with cement mortar 3 and a decorative coating film 5 is provided on the surface of the cement mortar 3 via the polymer cement mortar 4 for repairing. Has good adhesion to both the cement mortar 3 and the decorative coating film 5.
Can be prevented from coming off from the polymer cement mortar 4.
【0013】次に、厚み50mmのALC化粧パネル1
について、深さ20mm、幅30mmの欠損部2を補修
するときの具体例を示す。まず骨材(パーライト):セ
メント=60:40の重量比で混合すると共にさらにW
/C=60重量%になるように水を加えて混合すること
によってセメントモルタル3を調製し、欠損部2にこの
セメントモルタル3を充填して1日間養生した。次にポ
リマーセメントモルタル4として大日本塗料株式会社製
「釉元パテ」(主剤27重量部、硬化剤3重量部、セメ
ント4重量部、水1重量部)を用い、このポリマーセメ
ントモルタル4をセメントモルタル3の表面に1mmの
厚みで塗布し、80℃で5分間温風乾燥させた。そして
このポリマーセメントモルタル4の表面に大日本塗料株
式会社製フッ素樹脂塗料「Vフロン」を40g/m2 の
塗布量で塗布し、30分間自然乾燥させて化粧塗膜5を
設けた。Next, an ALC decorative panel 1 having a thickness of 50 mm
With respect to the above, a specific example of repairing the defective portion 2 having a depth of 20 mm and a width of 30 mm will be described. First, mix in a weight ratio of aggregate (perlite): cement = 60:40 and further mix W
Cement mortar 3 was prepared by adding water and mixing so that / C = 60% by weight, and the cement mortar 3 was filled in the defect portion 2 and cured for 1 day. Next, as the polymer cement mortar 4, "Glazed Putty" (27 parts by weight of main agent, 3 parts by weight of curing agent, 4 parts by weight of cement, 1 part by weight of water) manufactured by Dainippon Paint Co., Ltd. was used, and the polymer cement mortar 4 was cemented. It was applied to the surface of the mortar 3 with a thickness of 1 mm, and dried with warm air at 80 ° C. for 5 minutes. Then, a fluororesin paint "V CFC" manufactured by Dainippon Paint Co., Ltd. was applied on the surface of the polymer cement mortar 4 at a coating amount of 40 g / m 2 , and naturally dried for 30 minutes to form a decorative coating film 5.
【0014】このように補修するにあたって、化粧塗膜
5の剥離はみられなかった。比較のために、ポリマーセ
メントモルタル4を用いず、セメントモルタル3の表面
に化粧塗膜5を施すようにしたところ、化粧塗膜5は剥
離が発生し易いものであった。Upon repairing as described above, peeling of the decorative coating film 5 was not observed. For comparison, when the decorative coating film 5 was applied to the surface of the cement mortar 3 without using the polymer cement mortar 4, the decorative coating film 5 was easily peeled off.
【0015】[0015]
【発明の効果】上記のように本発明は、ALC化粧パネ
ルの表面の欠損部にセメントモルタルを充填し、この充
填したセメントモルタルの表面にポリマーセメントモル
タルを塗布すると共にこのポリマーセメントモルタルの
表面に化粧塗膜を施すようにしたので、ポリマーセメン
トモルタルによってセメントモルタルへの化粧塗膜の密
着性を高めることができ、化粧塗膜の剥離を防止して補
修部が外観不良になることを防ぐことができるものであ
る。INDUSTRIAL APPLICABILITY As described above, according to the present invention, the defective portion of the surface of the ALC decorative panel is filled with cement mortar, the surface of the filled cement mortar is coated with the polymer cement mortar, and the surface of the polymer cement mortar is coated. Since a decorative coating film is applied, the adhesion of the decorative coating film to the cement mortar can be improved by polymer cement mortar, and the peeling of the decorative coating film can be prevented to prevent the repaired part from having a poor appearance. Is something that can be done.
【図1】本発明の一実施例の断面図である。FIG. 1 is a sectional view of an embodiment of the present invention.
1 ALC化粧パネル 2 欠損部 3 セメントモルタル 4 ポリマーセメントモルタル 5 化粧塗膜 1 ALC decorative panel 2 Missing part 3 Cement mortar 4 Polymer cement mortar 5 Decorative coating film
Claims (1)
ントモルタルを充填し、この充填したセメントモルタル
の表面にポリマーセメントモルタルを塗布すると共にこ
のポリマーセメントモルタルの表面に化粧塗膜を施して
成ることを特徴とするALC化粧パネルの補修構造。1. A cement mortar is filled in the defect portion of the surface of an ALC decorative panel, and the polymer cement mortar is applied to the surface of the filled cement mortar and a decorative coating film is applied to the surface of the polymer cement mortar. ALC decorative panel repair structure characterized by: