JPH07278782A - Method for carburizing TiAl-based intermetallic compound - Google Patents
Method for carburizing TiAl-based intermetallic compoundInfo
- Publication number
- JPH07278782A JPH07278782A JP7617494A JP7617494A JPH07278782A JP H07278782 A JPH07278782 A JP H07278782A JP 7617494 A JP7617494 A JP 7617494A JP 7617494 A JP7617494 A JP 7617494A JP H07278782 A JPH07278782 A JP H07278782A
- Authority
- JP
- Japan
- Prior art keywords
- tial
- intermetallic compound
- carburizing
- based intermetallic
- hydrocarbon gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
(57)【要約】
【目的】 ＴｉＡｌ基金属間化合物に炭化水素ガスによ
る浸炭処理を行い、耐摩耗性、強度等の機能を付与した
ＴｉＡｌ金属間化合物を安価に製造する方法を提供す
る。
【構成】 ＴｉＡｌ基金属間化合物の表面酸化膜を除去
した後、９５０℃以上１３００℃以下の条件下におい
て、炭化水素ガスと反応させ、表面からの炭化反応によ
り、チタンカーバイドを生成させることを特徴とする浸
炭処理方法。浸炭処理ガスとしての炭化水素ガスとして
Ｃ3 Ｈ8 を用いることを特徴とする浸炭処理方法。浸炭
処理の際、保持時間を１時間以上１００時間以下の範囲
において、保持時間によってチタンカーバイド反応層厚
さを制御することを特徴とする浸炭処理方法。
【効果】 本発明によりＴｉＡｌ基金属間化合物の表面
を浸炭により硬化させ、耐摩耗性に優れたＴｉＡｌ基金
属間化合物を安価に、かつ大量に提供できる。本発明
は、ＴｉＡｌ金属間化合物の表面処理方法としても広く
応用できる。(57) [Abstract] [PROBLEMS] To provide a method for inexpensively producing a TiAl intermetallic compound in which a TiAl-based intermetallic compound is carburized with a hydrocarbon gas to impart functions such as wear resistance and strength. [Structure] After removing the surface oxide film of the TiAl-based intermetallic compound, it is reacted with a hydrocarbon gas under conditions of 950 ° C. or higher and 1300 ° C. or lower, and titanium carbide is generated by a carbonization reaction from the surface. Carburizing method. A carburizing method using C 3 H 8 as a hydrocarbon gas as a carburizing gas. In the carburizing treatment, the carburizing method is characterized in that the titanium carbide reaction layer thickness is controlled by the holding time within a holding time range of 1 hour or more and 100 hours or less. According to the present invention, the surface of a TiAl-based intermetallic compound is hardened by carburization, and a TiAl-based intermetallic compound having excellent wear resistance can be provided inexpensively and in a large amount. The present invention can be widely applied as a surface treatment method for TiAl intermetallic compounds.
Description
【０００１】[0001]
【産業上の利用分野】本発明は耐熱材料として有望なＴ
ｉＡｌ基金属間化合物に関するものである。ＴｉＡｌ基
金属間化合物は、比強度の高い高温耐熱材料として自動
車あるいは航空機用エンジン等に応用が検討されてい
る。さらに、その表面を硬化させることにより、ベアリ
ングあるいはエンジンバルブ等の摺動部材に使用でき
る。FIELD OF THE INVENTION The present invention is a promising T material as a heat resistant material.
The present invention relates to an iAl-based intermetallic compound. The TiAl-based intermetallic compound is being studied for application to automobiles, aircraft engines, etc. as a high temperature heat resistant material having high specific strength. Further, by hardening the surface, it can be used as a sliding member such as a bearing or an engine valve.
【０００２】[0002]
【従来の技術】ＴｉＡｌ基金属間化合物は比重が約３．
９で、高温強度、耐クリープ特性に優れており、軽量耐
熱材料として航空機への応用を目指して研究開発がなさ
れている。しかしながら、ＴｉＡｌ基金属間化合物は常
温における変形能に乏しく、室温での延性改善について
多くの研究がなされてきた。最近、ＴｉＡｌ基金属間化
合物にＭｎを添加して、常温における延性を２〜３％に
改善した例が、辻本らによって報告された（特開昭６１
−４１７４０号公報）。その他、ＴｉＡｌ基金属間化合
物に第三元素、第四元素を添加して特性を改善した例が
報告されている（例えば、米国特許第４８４２８１９号
明細書（Ｃｒ添加）、同第４８５７２６８号明細書（Ｖ
添加））。2. Description of the Related Art A TiAl-based intermetallic compound has a specific gravity of about 3.
No. 9, excellent in high temperature strength and creep resistance, and research and development is being carried out aiming at application to aircraft as a lightweight heat resistant material. However, the TiAl-based intermetallic compound has poor deformability at room temperature, and many studies have been conducted on improving ductility at room temperature. Recently, Tsujimoto et al. Reported an example in which ductility at room temperature was improved to 2 to 3% by adding Mn to a TiAl-based intermetallic compound (JP-A-61).
No. 41740). In addition, examples in which a third element and a fourth element are added to a TiAl-based intermetallic compound to improve the characteristics have been reported (for example, U.S. Pat. No. 4,842,819 (Cr added) and U.S. Pat. No. 4,857,268). (V
Addition)).
【０００３】ＴｉＡｌ基金属間化合物の製造方法として
は、プラズマアーク溶解法、高周波溶解法、急冷粉末
法、自己燃焼法等が知られている。合金設計した所望の
成分を調整した合金を急冷凝固によって粉末化し、その
後ＨＩＰで成型体にした例が報告されている（米国特許
第４８４２８１９号明細書）。さらに、複合化方法とし
て、反応焼結を行ってＴｉＢ2 とＡｌの複合粉末を形成
し、複合粉末をＴｉＡｌ等金属間化合物に添加した製造
方法が提案されている（米国特許第４７５１０４８号明
細書）。As a method for producing a TiAl-based intermetallic compound, a plasma arc melting method, a high frequency melting method, a quenching powder method, a self-combustion method and the like are known. It has been reported that an alloy having desired alloy-designed components was powdered by rapid solidification and then formed into a molded body by HIP (US Pat. No. 4,842,819). Further, as a compounding method, there has been proposed a manufacturing method in which a compound powder of TiB 2 and Al is formed by performing reactive sintering, and the compound powder is added to an intermetallic compound such as TiAl (US Pat. No. 4,751,048). ).
【０００４】ＴｉＡｌ基金属間化合物の製造方法におい
ては、ＴｉとＡｌの素粉末を目標組成の割合で混合し、
その後反応焼結によってＴｉＡｌ基金属間化合物を製造
する方法が広く行われている。ＴｉＡｌバルク材をさら
に表面処理を行い、表面の機能を向上させる試みは耐酸
化性の改善を目指して行ったものがほとんどである。例
えば、低酸素分圧下において熱処理を行い、ＴｉＡｌ表
面にＡｌ2 Ｏ3 被膜をつける方法（特開平２−２９４４
５８号公報）。また、ＰＶＤあるいはＣＶＤによってＳ
ｉＣ等の被膜を形成する方法が提案されている。In the method for producing a TiAl-based intermetallic compound, elementary powders of Ti and Al are mixed in a target composition ratio,
A method of producing a TiAl-based intermetallic compound by reactive sintering is widely performed thereafter. Most attempts to further improve the function of the surface by further subjecting the TiAl bulk material to surface treatment have been made with the aim of improving oxidation resistance. For example, a method of heat-treating under a low oxygen partial pressure to form an Al 2 O 3 coating on the TiAl surface (JP-A-2-2944).
No. 58). In addition, S by PVD or CVD
A method of forming a film such as iC has been proposed.
【０００５】さらに、Ｔｉ−Ａｌ系ベアリング材料とし
て、酸化、窒化、浸炭等硬化処理した材料が提案されて
いる（特開平３−４４４３６号公報）が、浸炭処理方法
はグラファイト微粉充填層中１０００℃で行ったもので
あり、製造方法は詳しく述べられていない。Further, as a Ti-Al bearing material, a material that has been hardened by oxidation, nitriding, carburizing, etc. has been proposed (Japanese Patent Laid-Open No. 3-44436), but the carburizing method is 1000 ° C. in a fine graphite powder packed bed. The manufacturing method has not been described in detail.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、ＴｉＡｌ基
金属間化合物に取扱いが容易なガスによる浸炭処理を行
い、耐摩耗性、強度等の機能を付与したＴｉＡｌ基金属
間化合物を安価に製造する方法を提供することを目的と
するものである。DISCLOSURE OF THE INVENTION According to the present invention, a TiAl-based intermetallic compound is produced at low cost by subjecting a TiAl-based intermetallic compound to carburizing treatment with a gas that is easy to handle, and imparting functions such as wear resistance and strength. The purpose is to provide a method of doing so.
【０００７】[0007]
【課題を解決するための手段】本発明の要旨とするとこ
ろは、ＴｉＡｌ基金属間化合物の表面酸化膜を除去した
後、９５０℃以上１３００℃以下の条件下において、炭
化水素ガスと反応させ、表面からの炭化反応により、チ
タンカーバイドを生成させることを特徴とするＴｉＡｌ
基金属間化合物の浸炭処理方法にあり、さらに炭化水素
ガスとしてＣ3Ｈ8 を用いることを特徴とし、また浸炭
処理の際、炭化水素ガスとの反応保持時間を１時間以上
１００時間以下の範囲において、保持時間によってチタ
ンカーバイド反応層厚さを制御することを特徴とする。The gist of the present invention is that after removing the surface oxide film of a TiAl-based intermetallic compound, it is reacted with a hydrocarbon gas under conditions of 950 ° C. or higher and 1300 ° C. or lower, TiAl characterized by producing titanium carbide by carbonization reaction from the surface
A method for carburizing a base intermetallic compound, further characterized by using C 3 H 8 as a hydrocarbon gas. Further, during the carburizing treatment, the reaction holding time with the hydrocarbon gas is in the range of 1 hour to 100 hours. In the above, the thickness of the titanium carbide reaction layer is controlled by the holding time.
【０００８】[0008]
【作用】本発明では、ＴｉＡｌ基金属間化合物にチタン
カーバイド層を安価に生成させるという課題対して、ガ
ス浸炭処理方法により生成させることを基本とするもの
である。ＴｉＡｌ基金属間化合物は、通常アルミナ酸化
膜とチタン酸化膜によって覆われている。従って、浸炭
処理を行う際にこれらの酸化物を除去し、清浄な表面と
する必要がある。表面から酸化膜を除去する方法はＡｒ
ガスによるスパッタ等が用いられるが、同一炉内で表面
酸化膜を除去するには、水素ガス雰囲気中で加熱するこ
とが有効である。The present invention is based on the problem of forming a titanium carbide layer on a TiAl-based intermetallic compound at a low cost by using a gas carburizing method. The TiAl-based intermetallic compound is usually covered with an alumina oxide film and a titanium oxide film. Therefore, it is necessary to remove these oxides during the carburizing process to obtain a clean surface. The method of removing the oxide film from the surface is Ar
Although gas sputtering or the like is used, heating in a hydrogen gas atmosphere is effective for removing the surface oxide film in the same furnace.
【０００９】試料温度は９５０℃以上１３００℃以下の
範囲に限定する。試料温度を９５０℃以上とする理由
は、９５０℃未満の場合、炭化物生成の反応が遅く、実
用的でないからである。従って、浸炭反応温度としては
９５０℃以上が必要である。一方、試料温度を１３００
℃以下に限定する理由は、ＴｉＡｌ基金属間化合物を１
３００℃超の温度に長時間保持すると、組織が粗大化し
て機械的特性の低下を招くからである。上記温度範囲
は、ＴｉＡｌ基金属間化合物の熱処理温度と同じ温度範
囲であり、熱処理による組織制御と浸炭処理を同時に行
うことが可能である。The sample temperature is limited to the range of 950 ° C. or higher and 1300 ° C. or lower. The reason why the sample temperature is set to 950 ° C. or higher is that when the temperature is lower than 950 ° C., the reaction of carbide formation is slow and it is not practical. Therefore, the carburization reaction temperature needs to be 950 ° C. or higher. On the other hand, set the sample temperature to 1300
The reason for limiting the temperature to below ℃ is 1 for the TiAl-based intermetallic compound.
This is because if the temperature is kept above 300 ° C. for a long time, the structure becomes coarse and the mechanical properties are deteriorated. The above temperature range is the same temperature range as the heat treatment temperature of the TiAl-based intermetallic compound, and it is possible to simultaneously carry out the structure control by the heat treatment and the carburizing treatment.
【００１０】炭化水素ガスとしては、好ましくはＣ3 Ｈ
8 ガスが使用されるが、ＣＨ4 、Ｃ 2 Ｈ6 、Ｃ4 Ｈ10等
が使用できる。ＴｉＡｌ基金属間化合物表面において式
（１）に示す反応が継続して起こる必要がある。 Ｃ3 Ｈ8 ＋３Ｔｉ → ３ＴｉＣ＋４Ｈ2 …… （１） 炭化水素ガスは好ましくは１気圧でガス流量を制御する
方法が最も実用的であるが、１Ｔｏｒｒまでの減圧雰囲
気下、あるいは１気圧以上の加圧雰囲気下においても式
（１）の反応は起こる。従って、浸炭は表面において炭
化水素が分解する式（１）の反応が律速ではなく、Ｔｉ
Ａｌ中の炭素の拡散あるいはＴｉおよびＡｌの拡散が浸
炭処理プロセスを律速している。The hydrocarbon gas is preferably C3H
8Gas is used, but CHFour, C 2H6, CFourHTenetc
Can be used. Formula on the surface of TiAl-based intermetallic compound
The reaction shown in (1) must continue to occur. C3H8+ 3Ti → 3TiC + 4H2 (1) The hydrocarbon gas preferably controls the gas flow rate at 1 atm.
The method is the most practical, but in a reduced pressure atmosphere up to 1 Torr
Formula under air or under pressure of 1 atm or more
The reaction (1) occurs. Therefore, carburizing is
The reaction of the formula (1) in which hydrogen fluoride decomposes is not rate-limiting
Diffusion of carbon in Al or diffusion of Ti and Al
The rate of the charcoal treatment process is limited.
【００１１】浸炭処理の際、保持時間を１時間以上１０
０時間以内に限定した理由は実用上の問題であり、１時
間未満の保持時間では反応が均質化しないからであり、
また１００時間を超える保持時間は経済的でないからで
ある。一定温度で浸炭処理を行った場合、反応層厚さを
０．１μｍから１００μｍ程度までコントロールするこ
とができる。反応層厚さと保持時間の関係は、拡散方程
式から式（２）で示される。During the carburizing treatment, the holding time is 1 hour or more and 10
The reason for limiting to 0 hours or less is a practical problem, and the reaction is not homogenized at a holding time of less than 1 hour,
Also, holding time of more than 100 hours is not economical. When the carburizing treatment is performed at a constant temperature, the thickness of the reaction layer can be controlled from 0.1 μm to 100 μm. The relationship between the reaction layer thickness and the retention time is expressed by the equation (2) from the diffusion equation.
【００１２】Ｔ∞√Ｄｔ …… （２） Ｔ：反応層厚さ Ｄ：ＴｉＡｌ中の炭素の拡散係数 ｔ：保持時間 図１に１０６０℃における反応層厚さと保持時間の関係
を示す。保持時間によってＴｉＣの反応層厚さを制御す
ることが可能である。ＴｉＡｌ基金属間化合物表面にＴ
ｉＣ膜を浸炭反応によって生成させた試料は高温部での
摺動部材として適応でき、ＴｉＣ厚さは目的部位によっ
て異なる。本発明によりＴｉＣ反応層厚さを浸炭処理温
度保持時間で制御できることが明らかとなった。T ∞ √Dt (2) T: thickness of reaction layer D: diffusion coefficient of carbon in TiAl t: retention time FIG. 1 shows the relationship between the reaction layer thickness and the retention time at 1060 ° C. It is possible to control the reaction layer thickness of TiC by the holding time. T on the surface of TiAl-based intermetallic compound
The sample produced by the carburizing reaction of the iC film can be applied as a sliding member at a high temperature part, and the TiC thickness varies depending on the target site. According to the present invention, it was revealed that the TiC reaction layer thickness can be controlled by the carburizing temperature holding time.
【００１３】[0013]
実施例１ Ｔｉ−４８．１ａｔ％Ａｌ組成を持つ金属間化合物をプ
ラズマアーク溶解によって溶製し、インゴットを得た。
インゴットの酸素量は３００ｗｔｐｐｍであった。イン
ゴット材を１３００℃、１５００気圧、４時間のＨＩＰ
処理を行い、ＨＩＰ処理材から２５×２５×５ｍｍの板
状試験片を採取した。板状試験片はエメリー研磨を行
い、さらにアルミナ粒子によって研磨を行い、鏡面仕上
げを行った。Example 1 An ingot was obtained by melting an intermetallic compound having a Ti-48.1 at% Al composition by plasma arc melting.
The oxygen content of the ingot was 300 wtppm. HIP ingot material at 1300 ° C, 1500 atm for 4 hours
After the treatment, a plate-like test piece of 25 × 25 × 5 mm was taken from the HIP-treated material. The plate-shaped test piece was subjected to emery polishing, and further polished with alumina particles to be mirror-finished.
【００１４】反応炉中に試料をセットし、Ｎ2 ガス雰囲
気中で昇温速度毎分２０℃で１０６０℃まで昇温を行っ
た。表面に形成された酸化物を取り除くために、Ｈ2 ガ
ス雰囲気（１Ｔｏｒｒ）にし、高電圧をかけてグロー放
電を起こさせた。次に、雰囲気をＣ3 Ｈ8 に置換し、Ｃ
3 Ｈ8 を１気圧で毎分１０ｃｃの流量で保持した。保持
時間は３０時間とした。３０時間経過後、炉内をＡｒガ
ス（１Ｔｏｒｒ）に置換し、高電圧を印可した。Ａｒイ
オンによるスパッタリング効果によって表面に生成した
浸炭層の最表面部分を取り除き、ＴｉＣが最表面になる
ように表面処理を行った。The sample was set in a reaction furnace and heated up to 1060 ° C. at a heating rate of 20 ° C./min in an N 2 gas atmosphere. In order to remove the oxide formed on the surface, a H 2 gas atmosphere (1 Torr) was applied, and a high voltage was applied to cause glow discharge. Next, the atmosphere is replaced with C 3 H 8 and C
3 H 8 was held at 1 atmosphere at a flow rate of 10 cc / min. The holding time was 30 hours. After 30 hours, the inside of the furnace was replaced with Ar gas (1 Torr), and a high voltage was applied. The outermost surface portion of the carburized layer formed on the surface by the sputtering effect of Ar ions was removed, and surface treatment was performed so that TiC became the outermost surface.
【００１５】この結果、ＴｉＡｌ基金属間化合物板材表
面にＴｉＣ層１２μｍを浸炭処理によって生成させるこ
とができた。図２に試料断面の組織写真を示す。 実施例２ 実施例１と同一組成を持つＴｉＡｌ基金属間化合物を実
施例１と同様な試験方法で前処理を行い、１０６０℃、
１０時間、Ｃ3 Ｈ8 ガス中にて浸炭処理を行った。その
結果、７μｍのＴｉＣ層が生成した。As a result, a TiC layer of 12 μm could be formed on the surface of the TiAl-based intermetallic compound plate by carburizing. FIG. 2 shows a structural photograph of the cross section of the sample. Example 2 A TiAl-based intermetallic compound having the same composition as in Example 1 was pretreated by the same test method as in Example 1, and 1060 ° C.
Carburizing was performed in C 3 H 8 gas for 10 hours. As a result, a 7 μm TiC layer was formed.
【００１６】比較例１ 実施例１と同一組成を持つＴｉＡｌ基金属間化合物を実
施例１と同様な試験方法で前処理を行い、９００℃、２
時間、Ｃ3 Ｈ8 ガス中にて浸炭処理を行った。その結
果、光学顕微鏡による断面観察では反応層の生成が認め
られなかった。実施例および比較例の結果を表１にまと
めて示す。Comparative Example 1 A TiAl-based intermetallic compound having the same composition as in Example 1 was pretreated by the same test method as in Example 1, and 900 ° C., 2
Carburizing was performed in C 3 H 8 gas for a period of time. As a result, the formation of the reaction layer was not observed in the cross-section observation with the optical microscope. The results of Examples and Comparative Examples are summarized in Table 1.
【００１７】[0017]
【表１】 [Table 1]
【００１８】[0018]
【発明の効果】本発明に従い、ＴｉＡｌ基金属間化合物
の表面に炭化水素ガスを用いて浸炭処理してＴｉＣを生
成させ、表面を硬化させることにより、耐摩耗性に優れ
たＴｉＡｌ基金属間化合物を安価にかつ大量に提供する
ことができる。なお、本発明はＴｉＡｌ基金属間化合物
の表面処理方法としても広く応用できる。INDUSTRIAL APPLICABILITY According to the present invention, the surface of a TiAl-based intermetallic compound is carburized with a hydrocarbon gas to produce TiC, and the surface is hardened to obtain a TiAl-based intermetallic compound having excellent wear resistance. Can be provided inexpensively and in large quantities. The present invention can be widely applied as a surface treatment method for TiAl-based intermetallic compounds.
【図面の簡単な説明】[Brief description of drawings]
【図１】１０６０℃における反応層厚さと保持時間の関
係を示す図である。FIG. 1 is a diagram showing a relationship between a reaction layer thickness and a holding time at 1060 ° C.
【図２】１０６０℃×３０時間浸炭処理したＴｉＡｌ金
属間化合物の断面組織写真である。FIG. 2 is a photograph of a cross-section structure of a TiAl intermetallic compound which has been carburized at 1060 ° C. for 30 hours.
Claims (3)
除去した後、９５０℃以上１３００℃以下の条件下にお
いて、炭化水素ガスと反応させ、表面からの炭化反応に
より、チタンカーバイドを生成させることを特徴とする
ＴｉＡｌ基金属間化合物の浸炭処理方法。1. After removing the surface oxide film of a TiAl-based intermetallic compound, it is reacted with a hydrocarbon gas under conditions of 950 ° C. or higher and 1300 ° C. or lower to generate titanium carbide by a carbonization reaction from the surface. A method for carburizing a TiAl-based intermetallic compound, comprising:
とを特徴とする請求項１記載のＴｉＡｌ基金属間化合物
の浸炭処理方法。2. The method for carburizing a TiAl-based intermetallic compound according to claim 1, wherein C 3 H 8 is used as the hydrocarbon gas.
以上１００時間以下の範囲において、保持時間によって
チタンカーバイド反応層厚さを制御することを特徴とす
る請求項１または２記載のＴｉＡｌ基金属間化合物の浸
炭処理方法。3. The TiAl group according to claim 1, wherein the titanium carbide reaction layer thickness is controlled by the retention time within a reaction retention time with a hydrocarbon gas of 1 hour or more and 100 hours or less. Carburizing method for intermetallic compounds.