JPH07275268A - Intraosseous implant - Google Patents

Abstract

PURPOSE:To provide a self-tappable intrasseous implant with excellent intraosseous maintaining force and excellent affinity to bone by forming a cutout shape part, provided at the end part surface of a male screw, into the smooth face in the intraosseous implant formed of a collar part and a body part having the roughened surface and the male screw. CONSTITUTION:In a cylinder type (screw type) double-system implant with a male screw provided at a body part 2, the maximum surface roughness of the whole surface of the body part 2 is to be 10-100mum, and a cutout shape part is provided at the end part surface of the male screw and formed into the smooth surface. The implant is formed of titanium, a titanium alloy or the oxide thereof or the complex thereof, and the body part 2 of the implant or the surface of the body part 2 is formed of bio-active material. The end part surface of the male screw is further provided with a through hole in such a way that the whole or part of the hole opening is included in the cutout shape part.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an endosseous implant used for dentistry and maxillofacial prosthesis.

[0002]

2. Description of the Related Art At present, there are two types of intraosseous implants (hereinafter referred to as implants) in the dental field, which are a cylinder type and a blade type. Cylinder type implants with a cylindrical appearance shape are roughly classified into three types: cylindrical, conical, and screw (including taper screw) type.
There are types. Further, the blade type has a plate-like appearance.

Further, there are a "two-time method" and a "one-time method" as a general method for implanting an implant in bone. In the two-step method, the implant is completely embedded in the bone at the time of implantation, and after several months, the gingiva is incised and a superstructure is attached to the upper end of the implant. On the other hand, in the one-time method, since the upper end of the implant penetrates the gingiva and is exposed in the oral cavity at the time of implantation, it is not necessary to incise the gingiva when the upper structure is attached to the implant.

Therefore, the length of the brim of the double implant is 0.5 to 2 mm, whereas the length of the single implant is about 5 to 10 mm. When the implant surface that comes into contact with bone after implantation is a relatively smooth machined surface, physical treatment (sandblasting method, thermal spraying method typified by plasma spraying, etc.), chemical treatment (acid etching, anode In some cases, the surface may be roughened by oxidation etc.) or their combination.

When the surface of the implant that comes into contact with the bone is roughened, food and miscellaneous bacteria intrude from the oral cavity, which easily causes infection and inflammation in the cervical part (upper part of the implant) of the implant, and bone resorption progresses. As a result, the implant may fall off. If the surface is smooth,
Even if food or bacteria in the oral cavity invades, it can be washed with a toothbrush, and infection and inflammation hardly occur.

Therefore, a portion having a smooth surface, which is generally called a "collar portion", is provided on the upper portion of the implant, and a "main body portion" having a roughened surface is provided below the portion. Maintaining the implant in the bone is generally based on a mechanical anchoring effect such as a screw, unevenness or protrusion. Implant materials include various metals such as titanium, titanium alloys and stainless steel, and various ceramics such as alumina and zirconia. Further, the body of the implant is composed of bioactive glass, bioactive crystallized glass, bioactive material such as hydroxyapatite, or the bioactive material is adhered to the surface of the body of the implant by a fusion method,
Attempts have also been made to increase the intraosseous maintenance power of the implant by coating it by various methods such as a thermal spraying method and an ion plating method and chemically bonding it.

There are two types of implanting methods for screw type implants. One is a method in which a screw hole (drilling hole) is drilled in the jawbone by using a tap, and a screw of an implant is screwed into the screw hole for implantation (tap implantation).
The other is a method in which a cylindrical or conical hole is bored in the jawbone and an implant provided with a self-tapping mechanism (for example, a cutting blade) is screwed into the hole to implant it (self-tap implantation).

Conventionally, there has been no implant having a roughened main body portion and a self-tapping mechanism (the reason will be described later).

[0009]

Immediately after implanting the implant, the bone and the implant surface are in close contact with each other, and
The less sway of the implant itself ensures that the bone contacts or joins the implant (providing superior intraosseous retention) and successful implant treatment. Self-tap implantation is advantageous because it easily causes this condition.

Further, the affinity with bone is improved by roughening the surface of the main body of the implant. However, conventionally, tap implantation has been performed in a screw-type implant with a roughened surface (it is difficult to obtain excellent intraosseous maintenance power). This is because the surface area becomes large due to the roughening and the resistance at the time of implantation becomes large, so that self-tap implantation cannot be performed.

It is an object of the present invention to provide an intraosseous implant capable of self-tapping, which has an excellent ability to maintain bone and has an excellent affinity with bone.

[0012]

Therefore, the first aspect of the present invention is to provide an intraosseous implant comprising "a collar portion and a main body portion having a roughened surface and having a male screw. An intraosseous implant characterized in that one or more notched portions are provided on the end surface of the male screw, and the notched portions are smooth surfaces (claim 1) "
I will provide a.

The present invention secondly provides the "intraosseous implant according to claim 1 (claim 2)" in which the maximum surface roughness of the main body is 10 to 100 µm. Further, the present invention thirdly provides that "the implant is made of titanium, a titanium alloy, or an oxide thereof, or a complex thereof.
The described intraosseous implant (claim 3) "is provided.

A fourth aspect of the present invention provides an "intraosseous implant (claim 4)" characterized in that the body or the surface of the body of the implant is made of a bioactive material. To do. The fifth aspect of the present invention is that "one or more through holes are provided on the end surface of the male screw so that all or part of the mouth of the hole is included in the cutout-shaped portion. The intraosseous implant according to claims 1 to 4 (claim 5) "is provided.

Further, the present invention sixthly provides an "intraosseous implant (claim 6)" characterized in that a tip hole connected to the through hole is provided on the bottom surface of the tip of the implant. To do. In addition, in the seventh aspect of the present invention, "the number of the cutout-shaped portions is an even number, and the cutout-shaped portions are arranged so that the cutout-shaped portions are rotationally symmetric with respect to the center of the major axis of the implant. An intraosseous implant according to claims 1 to 6 (claim 7) "is provided.

In the eighth aspect of the present invention, "the tip of the implant is tapered and the taper angle is 5 to 1".
An intraosseous implant according to claims 1 to 7 (claim 8) "is provided.

[0017]

In the endosseous implant of the present invention, the surface of the main body portion 2 having the male screw 2 '(including the male screw 2'and not including the notch-shaped portion S) is roughened so that the male screw 2' One or more notch-shaped portions S are provided on the end surface, and the notch-shaped portions S are smooth surfaces (claim 1). It was confirmed by in-vitro and in-vivo tests that such an intraosseous implant can be self-tapped. In some cases, the collar portion 1 of the implant may not be provided.

As the shape of the male screw 2 ', for example, the height h of the screw thread is 0.2 to 0.4 mm and the pitch P of the screw thread is 0.8.
~ 1.7 mm, a straight line connecting the vertex 5 of the thread or the lowest point 5 of the top side 4 and the lowest point 6 of the bottom side 3 of the thread forms an angle θ with the bottom side 3 of the thread of 50 degrees or more and less than 90 degrees (or 60 degrees or more 75
However, the present invention is not limited to this. The direction 7 below the "lowermost point" is the direction in which the screw thread advances.

If the height h of the screw thread is too high, the implant cannot be implanted in a bone portion having a narrow bone width, and the resistance at the time of implantation is too large to successfully implant. On the other hand, when the height h of the screw thread is too low, the fixing force by the screw is too weak, the initial fixation of the implant becomes insufficient, and the implant holding force at the time of occlusion becomes small. And, at the end of implanting the implant, idle rotation may occur.

If the pitch P of the thread is too large, the distance (lead) that the thread will try to advance becomes too large when the implant is rotated once. Therefore, the resistance from the bone at the time of implanting the implant is too large, and the vibration at the time of screwing is very large, so that the implant cannot be successfully implanted. On the other hand, if the pitch P of the thread is too small, it takes a long time to implant the implant because the lead is small. Also,
Threaded bones are easily destroyed.

The angle θ formed by the straight line connecting the lowest point 5 of the apex or top side 4 of the screw thread and the lowest point 6 of the bottom side 3 of the screw thread with the bottom side 3 of the screw thread is 50 from the implant embedding experiment.
The range is preferably not less than 90 degrees and less than 90 degrees, and particularly not less than 60 degrees and 7
It has been found that a range of 5 degrees or less is preferable. The cross-sectional shape of the screw thread is not particularly limited, but basically, a shape having a small cross-sectional area requires less bone to be shaved at the time of implant implantation. In terms of sharpness, the triangular shape is superior to the trapezoidal, rectangular, and saw blade shapes.

Further, since both the tensile stress and the compressive stress are applied to the implant by the occlusal stress during the function of the implant, it is preferable that the cross-sectional shape of the screw thread is a balanced and symmetrical shape. This is because loads on the implant due to both tensile and compressive stresses can be reduced. Each side of the screw thread is not limited to a straight line and may be a curved line. Also,
The top portion of the screw thread is not limited to a point and may be a side. In addition, the top part of the screw thread is
It often has a straight side or a curved line with a curvature.

The maximum surface roughness of the main body 2 is 10 to 1
The thickness is preferably 00 μm (Claim 2), particularly 20
It is preferable that the thickness is ˜50 μm in order to improve the bone affinity and to reduce the resistance at the time of self-tap implantation. In this case, since the notch-shaped portion S is not roughened but has a smooth surface, such an intraosseous implant has an excellent self-tapping function.

As a method for roughening the surface of the main body 2, sandblasting, thermal spraying such as plasma spraying, acid etching, anodic oxidation, etc., physical methods, chemical methods,
Alternatively, there is a method of using them in combination, but the method is not limited to these. The notch-shaped portion S may be masked before roughening the surface of the main body portion, or the notch-shaped portion S may be provided by machining or the like after the roughening treatment.

Materials for the implant include various metals such as stainless steel and various ceramics such as alumina and zirconia. Titanium, titanium alloys, oxides thereof, or composites thereof having excellent biocompatibility. Is preferred (claim 3). Also, the body 2 of the implant
Alternatively, it is preferable that the surface of the main body 2 is made of a bioactive material (claim 4). For example, by using a bioactive material such as bioactive glass, bioactive crystallized glass, or hydroxyapatite for the body portion 2 that comes into contact with bone, or the surface of the body portion 2 made of the various metals or ceramics as the bioactive material. By covering the surface of the implant, the intraosseous maintenance power of the implant can be improved.

It is preferable that one or more through-holes H1 are provided on the end surface of the male screw so that all or part of the mouth of the hole is included in the cutout portion S (claim 5). Since the bone fragments carved by the self-tapping function of the implant according to the present invention enter the through hole H1, the carved bone fragments are not sandwiched between the bone and the implant and serve as a bone resorption source. Further, bone is regenerated in the through hole H1 and the functionality of the implant is further improved.

It is preferable that the through hole H1 is provided perpendicularly to the long axis of the implant, from the viewpoint of both function and manufacturing. It is preferable to provide a tip hole H2 connected to the through hole H1 on the bottom surface of the tip of the implant (claim 6). The tip hole H2 is not connected to the post hole. By providing the tip hole H2, the scraped bone fragments are likely to enter the tip hole H2 and the through hole H1, and bone regeneration is likely to occur in the tip hole H2 and the through hole.

The tip bottom surface may or may not be roughened. Further, it is preferable that the tip hole H2 is provided in parallel with the long axis of the implant because it is more functional and easy to manufacture. It is preferable that the through hole H1 and / or the tip hole H2, particularly the tip hole H2 have a circular vertical cross-sectional shape because it is more functional and easy to manufacture.

If one tip hole H2 is provided and the center of the hole is aligned with the center of the long axis of the implant, it is more functional,
It is preferable because it is easy to manufacture. Further, it is preferable for regeneration of the bone that the inner surfaces of the through hole H1 and the tip hole H2 are roughened, but even if the inner surface is not roughened, a functional surface of accommodating the scraped bone fragments is provided. Then there is no problem.

If the number of the notch-shaped portions S is an even number,
It is preferable to provide each notch-shaped portion S such that each notch-shaped portion S is rotationally symmetrical with respect to the long axis center of the implant (claim 7). If the notch-shaped portions S are rotationally symmetrical to each other with respect to the center of the long axis of the implant, they are provided at even-numbered locations (especially 2, 4 or 8 locations), and stability and operability at the time of self-tapping implantation are improved. It is excellent and easy to manufacture.

Further, when the through hole H1 is provided in the notched portion S, the vertical cross-sectional shape of the through hole H1 is a circle, and the center of the circle overlaps the line of the edge E of the notched portion S. , The scraped bone pieces easily enter the through hole H1, and the operability at the time of self-tapping is excellent,
It is preferable because it is easy to manufacture. The tip of the implant is tapered, and the taper angle (cone angle) α is 5
It is preferably 15 °. At the tip of the implant,
Providing a conical portion that tapers in the distal direction (tapering the tip) facilitates insertion of the implant into the perforation cavity.

When the taper angle is 5 ° or less, it becomes difficult to insert the implant into the perforation fossa, and when the taper angle is 15 ° or more, the tip of the implant becomes an acute angle, and when occlusal force is applied to the implant, stress is concentrated on the tip. It is not preferable because it is easy to do. As described above, the intraosseous implant according to the present invention has a roughened main body surface, and since self-tap implantation is easy, it has excellent intraosseous maintenance power and affinity with bone. There is.

When the bone is very hard, by tapping a part of the entrance of the perforation fossa formed in the hard bone before self-tap implantation (tap implantation is also used), It will be easier to perform self-tapping after that.
In this case, since the surface of the main body is roughened, sufficient bone-implant contact can be obtained even with a part of tapped bone.

Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited thereto.

[0035]

Example A cylinder type (screw type) two-step implant with a length of 10 mm and a collar 1 of 2 mm in which a male thread 2'having a valley diameter of 2.7 mm is provided in the main body 2, Height h is 0.25 mm, pitch P of screw thread is 1 mm,
The apex of the thread or the lowest point 5 of the top 4 and the bottom 3 of the thread
The straight line connecting the lowest point 6 of the screw thread to the base 3 of the screw thread is 75 degrees, and the cone angle α of the tip is 10 degrees.
Entire surface (including the male screw 2'and the notched portion S)
Has a maximum surface roughness of 20 to 50 μm.

Next, two notch-shaped portions S are provided on the end surface of the male screw 2 ', so that both notched-shaped portions S are 180 ° rotationally symmetrical to each other with respect to the longitudinal center of the implant. It was Next, a cylindrical through hole H1 having a hole diameter of 1.2 mm was provided so that the center of the hole overlapped with the line of the edge E of the notched portion S. Further, a cylindrical tip hole H2 having a diameter of 1 mm is connected to the through hole H1 on the bottom surface of the tip of the implant.
Implant A was prepared by providing the center of the hole so as to coincide with the long axis of the implant. The through hole H1 and the tip hole H2 are connected to each other at right angles.

Further, an implant B having a roughened cutout portion S of the implant A was separately prepared. Implants A and B were self-tapped in the jawbone of a pig, and the situation was qualitatively evaluated. The evaluation results are shown in Table 1. In addition,
After forming a straight hole equal to the root diameter of the male screw 2 ′ in advance in the jawbone, the straight hole portion that comes into contact with the collar portion 1 of the implant in the implanted state was enlarged in a mortar shape by a counter sink.

The evaluation was carried out with a male screw 2'at the time of implant implantation.
Can be easily inserted (easy to bite), the implant can be inserted straight without being shaken during screwing (straightness), the bone can be cut smoothly without resistance during screwing (resistance), or during implant implantation. Whether it was possible to recognize that the plant had been implanted to an appropriate depth (feeling of termination), and a comprehensive evaluation of these was performed.

As a result of the above, the implant A having the notch-shaped portion S as a smooth surface was equivalent to the implant B having the roughened portion S in the straightness and the feeling of finish, but was easily biteable. It was excellent in overall resistance, small in resistance and excellent in resistance, and was excellent overall.

[0040]

[Table 1]

[0041]

INDUSTRIAL APPLICABILITY As described above, the intraosseous implant according to the present invention has a roughened main body surface and has an excellent self-tapping function. It has excellent properties. That is, the intraosseous implant according to the present invention improves the bone affinity by roughening the surface of the main body portion, and provides the notched portion S having a smooth surface on the end surface of the male screw 2 ′. , Easy self-implantation,
The operability can be surely improved and the success rate of the implant can be improved.

[Brief description of drawings]

FIG. 1A is a side view and FIG. 1B is a bottom view of an implant according to an embodiment.

FIG. 2 is a schematic diagram illustrating the shape of a male screw 2 ′ provided on the main body 2 of the implant.

[Explanation of symbols]

 1 ... Collar part of intraosseous implant 2 ... Main part of intraosseous implant 2 '... Male screw provided on the main body 3 ... Base of male screw thread 4 ... Male screw Crest 5 ... Lowest point on top of male thread 6 ... Lowest point on bottom of male thread 7 ... Implant tip direction (travel direction of thread) S ... Notch part provided on the end surface of the male screw E ... Edge of notch part S H1 ... Through hole H2 ... Tip hole α ... Taper angle (cone angle) of implant tip and above

Claims (8)

[Claims] 1. An intraosseous implant comprising a collar portion and a body portion having a roughened surface and having a male screw, wherein one or more cuts are formed on the end surface of the male screw. An intraosseous implant characterized in that a notched portion is provided and the notched portion is a smooth surface. 2. The maximum surface roughness of the main body is 10 to 10.
The intraosseous implant according to claim 1, which has a diameter of 0 μm. 3. The intraosseous implant according to claim 1, wherein the implant is made of titanium, a titanium alloy, an oxide thereof, or a composite thereof. 4. The body of the implant or the surface of the body is made of a bioactive material.
The intraosseous implant according to 3. 5. The one or more through-holes are provided on the end surface of the male screw so that all or part of the mouth of the hole is included in the cutout-shaped portion. 1 to
The intraosseous implant according to 4. 6. The intraosseous implant according to claim 5, wherein a tip hole connected to the through hole is provided on the bottom surface of the tip of the implant. 7. The number of the cutout-shaped portions is an even number,
7. The intraosseous implant according to claim 1, wherein each notch-shaped portion is provided so that each notch-shaped portion is rotationally symmetrical with respect to the center of the long axis of the implant. 8. The intraosseous implant according to claim 1, wherein a tip portion of the implant has a tapered shape and a taper angle is 5 to 15 °.