JPH0723421Y2 - Inner seal material for container mouth sealing - Google Patents
Inner seal material for container mouth sealingInfo
- Publication number
- JPH0723421Y2 JPH0723421Y2 JP1990113165U JP11316590U JPH0723421Y2 JP H0723421 Y2 JPH0723421 Y2 JP H0723421Y2 JP 1990113165 U JP1990113165 U JP 1990113165U JP 11316590 U JP11316590 U JP 11316590U JP H0723421 Y2 JPH0723421 Y2 JP H0723421Y2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- container
- seal
- sealing
- back surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 「産業上の利用分野」 本考案は、例えば、コーヒー粉末，クリーム粉末，味
塩，化学調味料等が充填されている容器の口部を密封す
るためのインナーシール材に関するものである。[Detailed Description of the Invention] "Industrial field of application" The present invention is, for example, an inner seal material for sealing the mouth of a container filled with coffee powder, cream powder, taste salt, chemical seasoning and the like. It is about.
「従来の技術」 コーヒー粉末やクリーム粉末等が充填されているガラス
壜等の容器の口部には、内填物を湿気から保護する目的
で容器口部密封用のインナーシール材が取り付けられて
いる。"Prior Art" The mouth of a container such as a glass bottle filled with coffee powder or cream powder is equipped with an inner seal material for sealing the mouth of the container in order to protect the filling from moisture. There is.
この容器口部密封用のインナーシール材は、リシール層
の裏面とシール層の表面との間の接着強度が易剥離性と
されており、例えば、リシール層と、該リシール層の裏
面に対して離型性を有する剥離性樹脂層からなる表面層
を具備するシール層とを、リシール層の裏面とシール層
の表面との間で接着させた積層シートや、リシール層と
シール層とをワックスによって接着させた積層シート等
を、円板状に打ち抜き成形して得られた板状体が利用さ
れており、キャップの裏面内側にインナーシール材を係
止させる工程と、キャップを容器口部に嵌合させなが
ら、キャップの裏面内側に係止されているインナーシー
ル材の裏面を容器口部に対して接着させる工程とによっ
て、シール層の裏面が容器口部に接着されている。The inner sealing material for sealing the mouth of the container is such that the adhesive strength between the back surface of the reseal layer and the surface of the seal layer is easy to peel off. For example, for the reseal layer and the back surface of the reseal layer, A seal layer having a surface layer composed of a releasable resin layer having releasability is adhered between the back surface of the reseal layer and the front surface of the seal layer, or the reseal layer and the seal layer are waxed. A plate-shaped body obtained by punching and molding a bonded laminated sheet etc. into a disc shape is used, and the step of locking the inner seal material inside the back surface of the cap and fitting the cap to the mouth of the container. The back surface of the seal layer is bonded to the container opening portion by a step of bonding the back surface of the inner seal material, which is locked to the inside of the back surface of the cap, to the container opening portion while being combined.
前記インナーシール材は、容器口部に嵌合されているキ
ャップを取り除く操作によって、リシール層とシール層
とに分離し、シール層のみが容器口部に接着されたまま
残る。The inner seal material is separated into a reseal layer and a seal layer by an operation of removing the cap fitted to the container mouth, and only the seal layer remains adhered to the container mouth.
なお、リシール層とシール層との間の分離は、リシール
層と、該リシール層の裏面に対して離型性を有する剥離
性樹脂層からなる表面層を具備するシール層とを、リシ
ール層の裏面とシール層の表面との間で接着させた積層
シートによるインナーシール材、例えば、第２図〜第３
図に例示されるように、板紙による表面層21とポリオレ
フィン系樹脂による裏面層22とをワックス層23を介して
積層させたリシール層24と、前記リシール層24の裏面層
22に対して離形性を有する剥離性樹脂層25を表面層とし
て具備するシール層26との積層構成によるインナーシー
ル材27の場合には、容器口部29に嵌合しているキャップ
30を取り除く操作によって、リシール層24の裏面とシー
ル層26の表面との間の界面で分離する。Incidentally, the separation between the reseal layer and the seal layer is performed by separating the reseal layer from the reseal layer and a seal layer having a surface layer made of a releasable resin layer having releasability with respect to the back surface of the reseal layer. Inner seal material by a laminated sheet adhered between the back surface and the surface of the seal layer, for example, FIGS.
As illustrated in the drawing, a reseal layer 24 in which a front surface layer 21 made of paperboard and a back surface layer 22 made of a polyolefin resin are laminated via a wax layer 23, and a back surface layer of the reseal layer 24.
In the case of an inner seal material 27 having a laminated structure with a seal layer 26 having a releasable resin layer 25 having a releasability with respect to 22, as a surface layer, a cap fitted to a container mouth 29.
The operation of removing 30 separates at the interface between the back surface of the reseal layer 24 and the surface of the seal layer 26.
そして、剥離性樹脂層25とアルミニュウム箔等の金属箔
31と裏面層をなしているグラシン紙28とからなるシール
層26が容器口部29に残り、リシール層24はキャップ30の
裏面に係止したままになって、内填物の取り出しの際に
シール層26を容器口部29から剥離した後でも、依然とし
てキャップ30のパッキングの作用を果たし、容器内部の
内填物を密封している。Then, the peelable resin layer 25 and a metal foil such as an aluminum foil.
A seal layer 26 composed of 31 and glassine paper 28 forming the back surface layer remains in the container mouth portion 29, and the reseal layer 24 remains locked on the back surface of the cap 30 to remove the inner filler. Even after the sealing layer 26 is peeled off from the container opening 29, the cap 30 still functions as a packing and seals the inner filler inside the container.
また、リシール層の裏面とシール層の表面とをワックス
層で接着させたインナーシール材の場合には、ワックス
層内の破壊によって、リシール層とシール層とに分離す
る。Further, in the case of an inner seal material in which the back surface of the reseal layer and the surface of the seal layer are adhered with a wax layer, the reseal layer and the seal layer are separated by breaking the inside of the wax layer.
「考案が解決しようとする課題」 ところで、容器口部密封用インナーシール材は、キャッ
プの回動によってリシール層とシール層とを分離させた
後に、容器口部に接着されているシール層を剥離，除去
してから、内填物の取り出しを行なうが、シール層によ
る防湿作用をそのまま利用し得るように、シール層の１
部分のみを分離，除去することがしばしば行なわれる。[Problems to be solved by the invention] By the way, in the inner sealing material for sealing the container mouth, the reseal layer and the seal layer are separated by the rotation of the cap, and then the seal layer adhered to the container mouth is peeled off. , The internal filler is taken out after the removal, but in order to use the moisture-proof effect of the seal layer as it is,
Often, only parts are separated and removed.
しかるに、シール層には、該シール層による優れた防湿
性が得られるように、金属箔とプラスチックフィルムと
の積層材が使用されているのが普通であり、かかる積層
材によるシール層の１部分のみを指先の操作によって破
断，除去すると、該積層材の手切れ性の悪さのために、
例えば、第４図に示されるように、シール層40の開口部
41の切り口42が乱雑になり、直線状の切り口が得られな
く、また、粉・粒状の内填物が、開口部41の縁辺部をな
す切り口42に付着する等の見苦しさを与える。However, it is usual that a laminated material of a metal foil and a plastic film is used for the seal layer so that excellent moisture resistance by the seal layer can be obtained. If only the only one is broken and removed by the operation of the fingertip, the laminated material has poor hand-cutability,
For example, as shown in FIG. 4, the opening of the sealing layer 40
The cut 42 of 41 becomes messy, a straight cut cannot be obtained, and the powdered / granular filling material adheres to the cut 42 forming the edge portion of the opening 41, giving an unsightly appearance.
これに対して、本考案は、キャップの回動によって、容
器口部に接着されているインナーシール材をリシール層
とシール層とに分離した後に、容器口部に接着している
シール層の１部のみを、指先で破断，除去する際の手切
れ性が良好で、縁部がすっきりした状態の開口部をシー
ル層の１部に、きわめて容易に形成し得る容器口部密封
用インナーシール材を提供する。On the other hand, according to the present invention, by rotating the cap, the inner seal material adhered to the container mouth is separated into the reseal layer and the seal layer, and then the seal layer adhered to the container mouth is Inner seal material for sealing the mouth of a container, which has good hand-cutability when breaking and removing only part of the container with a fingertip, and which can very easily form an opening with a clean edge in one part of the sealing layer. I will provide a.
「課題を解決するための手段」 本考案の容器口部密封用インナーシール材は、従来のイ
ンナーシール材と同様に、リシール層の裏面とシール層
の表面との間が易剥離性とされており、シール層の裏面
が容器口部に接着されるものであって、シール層を構成
する積層構成中に、上，下の両面にポリエチレンの押し
出し樹脂層が積層されている１軸延伸ポリエチレンフィ
ルムが組み込まれた構成からなる。[Means for Solving the Problems] The inner seal material for sealing the container mouth portion of the present invention has an easy peeling property between the back surface of the reseal layer and the surface of the seal layer, like the conventional inner seal material. A uniaxially stretched polyethylene film in which the back surface of the seal layer is adhered to the mouth of the container, and a polyethylene extruded resin layer is laminated on both upper and lower surfaces in the laminated structure constituting the seal layer. Is built in.
本考案の容器口部密封用インナーシール材中のリシール
層は、板紙を主体として形成されているのが普通であ
り、キャップの裏面内周面側に係合されて、キャップに
パッキングの作用をもたらす。The reseal layer in the inner sealing material for sealing the mouth of the container of the present invention is usually formed mainly of paperboard, and is engaged with the inner surface of the back surface of the cap so that the cap functions as a packing. Bring
また、シール層は、その裏面が容器口部に接着されて、
容器内の内填物に対する防湿性を保持するものであっ
て、例えば、シール層の裏面層が熱接着性樹脂層によっ
て形成され、しかも、シール層中に金属箔が積層されて
いるような場合には、高周波誘導加熱によるシール層中
の金属箔の発熱と、前記裏面層をなす熱溶着性樹脂層の
熱溶着能とを利用して、インナーシール材と容器口部と
の間の接着を行ない得る。In addition, the back surface of the sealing layer is adhered to the mouth of the container,
For keeping moisture resistance against the filling material in the container, for example, in the case where the back surface layer of the seal layer is formed of a heat-adhesive resin layer, and further the metal foil is laminated in the seal layer. The heat generated by the high-frequency induction heating of the metal foil in the seal layer and the heat-welding ability of the heat-welding resin layer forming the back surface layer are used to bond the inner seal material and the container mouth. I can do it.
なお、シール層における裏面層と金属箔とが隣接するよ
うな場合には、裏面層たる熱接着性樹脂層は、金属箔に
対する接着性において優れた性質を有する酸変性ポリエ
チレン樹脂、例えば、エチレンと、アクリル酸やメタク
リル酸等のカルボン酸系モノマーと、（メタ）アクリル
酸エチル，（メタ）アクリル酸ブチル等とによる３元共
重合体樹脂、エチレン−酢酸ビニル共重合体樹脂、さら
には、アイオノマー樹脂等の酸変性エチレン系共重合体
樹脂で、カルボキシル基換算量で３〜25モル％程度のカ
ルボキシル基を具備する酸変性エチレン系共重合体樹脂
を主成分とする熱接着性樹脂で形成されていることが好
ましい。When the back surface layer of the seal layer and the metal foil are adjacent to each other, the heat-adhesive resin layer as the back surface layer is an acid-modified polyethylene resin having excellent properties in adhesion to the metal foil, for example, ethylene. , A terpolymer resin composed of a carboxylic acid-based monomer such as acrylic acid or methacrylic acid and ethyl (meth) acrylate, butyl (meth) acrylate, an ethylene-vinyl acetate copolymer resin, and an ionomer An acid-modified ethylene-based copolymer resin such as a resin, which is formed of a heat-adhesive resin whose main component is an acid-modified ethylene-based copolymer resin having about 3 to 25 mol% of carboxyl groups in terms of carboxyl groups. Preferably.
また、シール層における裏面層が熱接着性樹脂層で形成
されている場合には、該樹脂層自体の安定性、および、
高周波誘導加熱法で接着されるインナーシール材と容器
口部との間の熱接着部の安定性等の点から、厚さ20〜10
0μ程度に形成されていることが好ましい。Further, when the back surface layer of the seal layer is formed of a thermoadhesive resin layer, the stability of the resin layer itself, and
From the viewpoint of the stability of the heat-bonded part between the inner seal material and the container mouth, which are bonded by the high-frequency induction heating method, the thickness is 20 to 10
It is preferably formed to have a thickness of about 0 μ.
さらに、シール層における裏面層がグラシン紙によって
形成されている場合には、インナーシール材と容器口部
との間の接着は糊付けによってなされる。Further, when the back surface layer of the seal layer is made of glassine paper, the adhesion between the inner seal material and the container mouth is made by gluing.
本考案の容器口部密封用インナーシール材において、シ
ール層中に積層されているところの、上，下の両面にポ
リエチレンの押し出し樹脂層が積層されている１軸延伸
ポリエチレンフィルムは、シール層に対して方向性のあ
る良好な手切れ性をもたらすものであり、厚さ15〜50μ
程度の１軸延伸ポリエチレンフィルムの上，下の両面に
ポリエチレンの押し出し樹脂層が積層されている状態
で、シール層中に積層されている。In the inner sealing material for sealing the mouth of the container of the present invention, the uniaxially stretched polyethylene film having the polyethylene extruded resin layer laminated on both the upper and lower surfaces, which is laminated in the sealing layer, is used as the sealing layer. 15 to 50μ thickness
Extruded resin layers of polyethylene are laminated on both upper and lower surfaces of the uniaxially stretched polyethylene film, and are laminated in the seal layer.
「考案の作用」 本考案の容器口部密封用インナーシール材は、リシール
層の裏面とシール層の表面との間が易剥離性とされてお
り、シール層の裏面が容器口部に接着される積層シート
からなるものであり、シール層中に積層されているとこ
ろの、上，下の両面にポリエチレンの押し出し樹脂層が
積層されている１軸延伸ポリエチレンフィルムの存在に
よって、該１軸延伸ポリエチレンフィルムの延伸方向と
同一方向に破断する操作に対して、優れた手切れ性が奏
される。[Advantage of the Invention] The inner sealing material for sealing the container mouth portion of the present invention has an easy peeling property between the back surface of the reseal layer and the surface of the seal layer, and the back surface of the seal layer is adhered to the container mouth portion. The uniaxially-stretched polyethylene film is formed by the presence of a uniaxially-stretched polyethylene film in which a polyethylene extruded resin layer is laminated on both upper and lower surfaces of the uniaxially-stretched polyethylene film. Excellent hand-cutting property is exhibited against an operation of breaking in the same direction as the stretching direction of the film.
なお、シール層中に積層されているところの、上，下の
両面にポリエチレンの押し出し樹脂層が積層されている
１軸延伸ポリエチレンフィルムの延伸方向を表示する矢
印を、シール層の表面に印刷表示し、矢印方向への易破
断性を説明する等によって、内填物の消費者に対しての
便宜が図れる。It should be noted that an arrow indicating the stretching direction of the uniaxially stretched polyethylene film having polyethylene extruded resin layers laminated on both upper and lower sides of the layer laminated in the seal layer is printed on the surface of the seal layer. However, by explaining the easy breakability in the direction of the arrow and the like, it is possible to make the internal filler convenient for the consumer.
「実施例」 以下本考案の容器口部密封用インナーシール材の具体的
な構成を、図面に基づいて、その製造実施例を以って説
明する。[Examples] Hereinafter, a specific configuration of the inner seal material for sealing the container mouth portion of the present invention will be described with reference to the drawings and manufacturing examples thereof.
実施例１ 第１図において、表面に印刷模様ｍを有する坪量30.5g/
m2のグラシン紙２に対して、印刷模様ｍ面にアンカーコ
ート剤を付した後、このグラシン紙２と、符号３で表示
される厚さ25μの１軸延伸ポリエチレンフィルム［三井
東圧（株）：ハイブロン］とを、両者の間に、厚さ20μ
のポリエチレン樹脂の押し出し樹脂層４を介して積層し
た。Example 1 In FIG. 1, the basis weight having a printed pattern m on the surface is 30.5 g /
An anchor coat agent is applied to the m-side of the printed pattern m 2 of glassine paper 2, and this glassine paper 2 and a uniaxially stretched polyethylene film 25 μm thick, which is indicated by reference numeral 3, [Mitsui Toatsu Co., Ltd. ): Hybron] and 20 μm in thickness between the two
The polyethylene resin was laminated through the extruded resin layer 4.
次いで、先の１軸延伸ポリエチレンフィルム３の表面
に、厚さ10μのAl箔５を、符号６で表示される厚さ20μ
のポリエチレンの押し出し樹脂層を介装させながら積層
した。Then, on the surface of the uniaxially stretched polyethylene film 3 described above, an Al foil 5 having a thickness of 10 μ and a thickness of 20 μ indicated by reference numeral 6 are formed.
The polyethylene extruded resin layer of was laminated.
さらに、Al箔５の表面に、絵柄印刷層ｎと、厚さ２μの
剥離性樹脂（硝化綿）層７とを順次形成し、シール層８
となる積層シートを得た。Further, a pattern printing layer n and a peeling resin (nitrified cotton) layer 7 having a thickness of 2 μm are sequentially formed on the surface of the Al foil 5, and a seal layer 8 is formed.
A laminated sheet was obtained.
続けて、シール層８となる積層シートの剥離性樹脂層７
の表面に、厚さ20μのポリエチレン樹脂層９を溶融押し
出しコート法によって積層した後、ワックス（20g/m2）
によるホットメルト接着剤層10を利用して乳栓ボール
（630g/m2）11を積層することによって、容器口部密封
用インナーシール材の前駆体である積層シートを得た。Subsequently, the peelable resin layer 7 of the laminated sheet to be the seal layer 8
A polyethylene resin layer 9 having a thickness of 20 μm is laminated on the surface of the sol by a melt extrusion coating method, and then wax (20 g / m 2 )
By using the hot-melt adhesive layer 10 according to 1. to laminate the embolic balls (630 g / m 2 ) 11, a laminated sheet which is a precursor of the inner sealing material for sealing the mouth of the container was obtained.
なお、インナーシール材の前駆体である積層シートにお
いては、厚さ20μのポリエチレン樹脂層９と、ワックス
（20g/m2）によるホットメルト接着剤層10と、乳栓ボー
ル（630g/m2）11との積層部分が、符号12で表示される
リシール層となる。In the laminated sheet which is the precursor of the inner seal material, the polyethylene resin layer 9 having a thickness of 20 μm, the hot melt adhesive layer 10 made of wax (20 g / m 2 ) and the embolic ball (630 g / m 2 ). The laminated portion with 11 becomes a reseal layer indicated by reference numeral 12.
得られたインナーシール材の前駆体である積層シート
を、直径7.5cmの円板状に打ち抜き加工し、第１図にて
符号１で表示される本考案の１実施例品たる容器口部密
封用インナーシール材を得た。The laminated sheet, which is the precursor of the obtained inner seal material, is punched into a disk shape with a diameter of 7.5 cm, and the container mouth portion, which is one embodiment of the present invention indicated by reference numeral 1 in FIG. 1, is sealed. An inner seal material for use was obtained.
「考案の効果」 本考案の容器口部密封用インナーシール材は、シール層
を構成する積層構成中に、上，下の両面にポリエチレン
の押し出し樹脂層が積層されている１軸延伸ポリエチレ
ンフィルムが積層されているので、シール層が前述の１
軸延伸ポリエチレンフィルムの延伸方向と同一方向に対
して優れた手切れ性を奏する。[Advantage of the Invention] The inner sealing material for sealing the container mouth portion of the present invention is a uniaxially stretched polyethylene film in which a polyethylene extrusion resin layer is laminated on both upper and lower surfaces in the laminated structure constituting the sealing layer. Since it is laminated, the sealing layer is
It exhibits excellent hand-cutting properties in the same direction as the stretched direction of the axially stretched polyethylene film.
このため、容器口部に接着されているインナーシール材
を、キャップの回動によって、リシール層とシール層と
に分離した後に、容器口部に残ったままになっているシ
ール層の１部分のみを指先で破断，除去する操作によ
り、第５図にて符号50で表示されるインナーシール材の
ように、開口縁部に乱雑さがなく、しかも、直線状をな
す切り口52による美麗な開口部51を、きわめて容易に形
成し得る。Therefore, after the inner seal material adhered to the container mouth is separated into the reseal layer and the seal layer by the rotation of the cap, only one part of the seal layer left in the container mouth remains. By the operation of breaking and removing with a fingertip, unlike the inner seal material indicated by reference numeral 50 in FIG. 5, there is no clutter at the opening edge, and a beautiful opening with a straight cut 52 is formed. 51 can be formed very easily.
したがって、シール層による優れた防湿性が得られるよ
うに、シール層の１部分のみを指先の操作によって分
離，除去することにより、直線状のすっきりした状態の
開口部を形成し得るため、商品に対する良好なイメージ
を消費者に与えられる。Therefore, in order to obtain the excellent moisture resistance by the seal layer, by separating and removing only one part of the seal layer by the operation of the fingertip, a linear and clear opening can be formed. Good images are given to consumers.
第１図は、本考案の容器口部密封用インナーシール材の
１実施例品を示す模型断面図、第２図は、従来の容器口
部密封用インナーシール材の模型断面図、第３図は、第
２図のインナーシール材が容器口部に接着されている容
器から、キャップを取り外したときの状態を示す模型断
面図、第４図は、容器口部に取り付けられている従来の
インナーシール材からキャップを取り外した後に、シー
ル層の１部を指先で破断した状態を説明する斜面図、第
５図は、容器口部に取り付けられている本考案のインナ
ーシール材からキャップを取り外した後に、シール層の
１部のみを指先で破断した状態を説明する斜面図であ
る。 １……容器口部密封用インナーシール材、３……シール
層８における１軸延伸ポリエチレンフィルム、４……１
軸延伸ポリエチレンフィルム３の下面に積層されている
ポリエチレンの押し出し樹脂層、６……１軸延伸ポリエ
チレンフィルム３の上面に積層されているポリエチレン
の押し出し樹脂層、８……シール層、12……リシール
層。FIG. 1 is a model cross-sectional view showing an example of an inner seal material for sealing a container mouth portion according to the present invention, and FIG. 2 is a model cross-sectional view of a conventional inner seal material for sealing a container mouth portion, FIG. 2 is a model cross-sectional view showing a state in which the cap is removed from the container in which the inner seal material of FIG. 2 is adhered to the container mouth, and FIG. 4 is a conventional inner member attached to the container mouth. After removing the cap from the seal material, a perspective view illustrating a state in which a part of the seal layer is broken by a fingertip, FIG. 5 shows the cap removed from the inner seal material of the present invention attached to the container mouth part. It is a perspective view explaining the state which fractured | ruptured only one part of a sealing layer with a fingertip later. 1 ... Inner seal material for sealing container mouth, 3 ... Uniaxially stretched polyethylene film in seal layer 8, 4 ... 1
Extruded polyethylene resin layer laminated on the lower surface of the axially stretched polyethylene film 3, 6 ... Extruded polyethylene resin layer laminated on the upper surface of the monoaxially stretched polyethylene film 3, 8 ... Seal layer, 12 ... Reseal layer.
Claims (1)
が易剥離性とされており、シール層の裏面が容器口部に
接着される容器口部密封用インナーシール材において、
上，下の両面にポリエチレンの押し出し樹脂層が積層さ
れている１軸延伸ポリエチレンフィルムがシール層内に
積層されていることを特徴とする容器口部密封用インナ
ーシール材。1. An inner seal material for sealing a container mouth, wherein the back surface of the reseal layer and the surface of the seal layer are easily peeled off, and the back surface of the seal layer is adhered to the mouth part of the container.
An inner seal material for sealing the mouth of a container, characterized in that a uniaxially stretched polyethylene film having polyethylene extruded resin layers laminated on both upper and lower sides is laminated in a seal layer.