JPH07157729A - Fabric laminate and its production and fabric label printer - Google Patents
Fabric laminate and its production and fabric label printerInfo
- Publication number
- JPH07157729A JPH07157729A JP5305445A JP30544593A JPH07157729A JP H07157729 A JPH07157729 A JP H07157729A JP 5305445 A JP5305445 A JP 5305445A JP 30544593 A JP30544593 A JP 30544593A JP H07157729 A JPH07157729 A JP H07157729A
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- adhesive
- cloth
- sheet
- roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、主に衣服等に接着可能
なラベル、ワッペン等に用いられる布帛に関するもので
あり、さらに詳しくは、アイロン等の熱により、容易に
衣服等に接着可能な布帛に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cloth mainly used for labels and patches that can be adhered to clothes and the like, and more specifically, it can be easily adhered to clothes and the like by heat of an iron or the like. It relates to cloth.
【０００２】[0002]
【従来の技術】従来、衣服等に付けるラベル等は、洗濯
耐久性が要求されるため、縫いつけにより取り付けられ
るものが多く、一部で熱融着により接着されているもの
があるにすぎない。2. Description of the Related Art Conventionally, labels attached to clothes and the like are required to have durability against washing, so that many of them are attached by sewing, and some of them are only attached by heat fusion.
【０００３】[0003]
【発明が解決しようとする課題】しかし、縫いつけで
は、取り付けに非常に手間がかかる、糸のほつれがで
る、薄いラベルではしわがよる等の問題がある。However, there are problems in that sewing requires a great deal of labor for attachment, frayed threads, wrinkles in thin labels, and the like.
【０００４】また、熱融着樹脂により接着されるラベル
については、充分な洗濯耐久性を得るためには熱融着樹
脂層をかなり厚くしなければならず、厚くて硬いものに
なってしまうといった問題がある。また、特開平３−２
６０１４９号公報には、ワッペン生地として用いられる
編物、織物に熱溶融性合成樹脂フイルムを重ねて加熱押
圧機で加熱押圧して上記熱溶融性合成樹脂フイルムをあ
る程度溶融して上記編物、織物と融着する方法が開示さ
れているが、この場合でも充分な洗濯耐久性を持たせる
ためには熱溶融性合成樹脂フイルムを厚くする必要があ
り、また薄い布帛の場合はこの方法でも硬く殆どフイル
ム状のラベル等になってしまうという問題がある。Further, in the case of a label that is adhered by a heat-sealing resin, the heat-sealing resin layer must be made considerably thick in order to obtain sufficient washing durability, and it becomes thick and hard. There's a problem. In addition, JP-A-3-2
No. 60149 gazette discloses that a knitted fabric used as a patch fabric, a woven fabric and a heat-melting synthetic resin film are overlapped and heated and pressed by a heating press machine to melt the heat-melting synthetic resin film to some extent to melt the knitted fabric and the woven fabric. Although a method of wearing is disclosed, even in this case, it is necessary to thicken the heat-meltable synthetic resin film in order to have sufficient washing durability, and in the case of thin cloth, this method is hard and almost film-like. There is a problem that it becomes the label etc.
【０００５】本発明はかかる従来技術の諸欠点に鑑み創
案されたものであり、その目的は、熱による接着が可能
でかつその接着力の洗濯耐久性が充分な、ラベル、ワッ
ペン等に用いられる布帛積層体を提供することにある。The present invention was devised in view of the above-mentioned drawbacks of the prior art, and an object thereof is to be used for a label, a patch or the like which can be adhered by heat and whose adhesive strength is sufficient for washing durability. It is to provide a fabric laminate.
【０００６】[0006]
【課題を解決するための手段】かかる本発明の目的を達
成するため以下の構成をとる。すなわち、本発明の布帛
積層体は、布帛の片面に、その全面を覆うようにシート
状熱融着接着剤を粘着層を介して積層したことを特徴と
するものである。To achieve the above object of the present invention, the following constitution is adopted. That is, the fabric laminate of the present invention is characterized in that a sheet-shaped heat-sealing adhesive is laminated on one surface of the fabric so as to cover the entire surface thereof via an adhesive layer.
【０００７】また、本発明の布帛積層体の製造方法は、
布帛またはシート状熱融着接着剤の片面に粘着剤を塗工
して両者を積層することを特徴とするものであるまた、
本発明の布帛ラベルプリンターは、少なくとも、布帛ロ
ールとシート状熱融着接着剤ロールとを有し、熱転写法
またはインクジェット法またはドットインパクト法で画
像を布帛上に形成する工程と、布帛または熱融着接着剤
フイルムの片面に粘着剤を塗工する工程と、布帛と熱融
着接着剤フイルムとを粘着剤を介して積層する工程とを
有することを特徴とするものである。The method for producing a fabric laminate of the present invention is
It is characterized in that a pressure-sensitive adhesive is applied to one surface of a cloth or sheet heat-sealing adhesive to laminate the both.
The fabric label printer of the present invention has at least a fabric roll and a sheet-shaped heat-fusion adhesive roll, and a step of forming an image on the fabric by a thermal transfer method, an inkjet method, or a dot impact method; It is characterized by including a step of applying an adhesive on one surface of the adhesive adhesive film and a step of laminating a cloth and a heat-fusion adhesive film via the adhesive.
【０００８】また、本発明の布帛ラベルプリンターは、
少なくとも、布帛ロールとシート状熱融着接着剤ロール
とを有し、かつその内の少なくとも一方の片面には粘着
層を有しており、熱転写法またはインクジェット法また
はドットインパクト法で画像を布帛上に形成する工程
と、布帛とシート状熱融着接着剤とを粘着剤を介して積
層する工程とを有することを特徴とするものである。Further, the fabric label printer of the present invention is
At least a cloth roll and a sheet-shaped heat-sealing adhesive roll are provided, and at least one of them has an adhesive layer, and an image is formed on the cloth by a thermal transfer method, an inkjet method, or a dot impact method. And a step of laminating the cloth and the sheet-shaped heat-sealing adhesive via a pressure-sensitive adhesive.
【０００９】また、本発明の布帛ラベルプリンターは、
少なくとも、布帛とシート状熱融着接着剤とを粘着層を
介して積層した積層布帛ロールを有し、その布帛面に、
熱転写法またはインクジェット法またはドットインパク
ト法で画像を布帛上に形成することを特徴とするもので
ある。Further, the fabric label printer of the present invention is
At least a laminated fabric roll having a fabric and a sheet-shaped heat-sealing adhesive laminated via an adhesive layer, and on the fabric surface thereof,
An image is formed on a cloth by a thermal transfer method, an inkjet method, or a dot impact method.
【００１０】[0010]
【作用】本発明で用いられる布帛は、特に限定されず、
綿、絹などの天然繊維、ポリアミド系、ポリエステル系
などの合成繊維からなる織物、編み物、不織布などが用
いられるが、寸法安定性の点から織物が好ましく、ま
た、熱可塑性合成繊維、特にポリエステル系繊維を用い
るのが、強度、接着性の点から好ましい。繊維の太さは
特に限定されないが、単繊維度が０．０００１デニール
以上１デニール以下の極細繊維から主としてなる布帛
は、平面平滑性に優れ、また柔軟性に優れており、また
ラベル等に用いる場合は印刷時に非常に鮮明な画像が得
られるので好ましい。また、ポリアミド繊維およびポリ
エステル繊維の２種類の極細繊維をよく混繊した布帛
は、緻密な表面、ひいては平滑性に優れた表面を有する
ため好ましい。また、極細布帛表面に高速の流体流処理
（ウォータージェットパンチ）を施し、極細繊維どうし
を開繊および／または交絡せしめ、表面を緻密化するの
も好ましい方法である。また、カレンダー加工も表面平
滑性が向上するため好ましい処理である。これら極細繊
維の製造方法は特に限定されず、通常の各種技術を用い
ることができる。The cloth used in the present invention is not particularly limited,
Woven fabrics, knits, non-woven fabrics, etc. made of natural fibers such as cotton and silk, synthetic fibers such as polyamide and polyester are used, but woven fabrics are preferred from the viewpoint of dimensional stability, and thermoplastic synthetic fibers, especially polyester fibers. It is preferable to use fibers in terms of strength and adhesiveness. The thickness of the fiber is not particularly limited, but a fabric mainly composed of ultrafine fibers having a monofilament degree of 0.0001 denier or more and 1 denier or less has excellent flatness smoothness and flexibility, and is used for labels and the like. In this case, a very clear image can be obtained during printing, which is preferable. A fabric in which two types of ultrafine fibers such as polyamide fibers and polyester fibers are well mixed is preferable because it has a dense surface and, in turn, a surface having excellent smoothness. It is also a preferred method to subject the surface of the ultrafine fabric to a high-speed fluid flow treatment (water jet punch) to open and / or entangle the ultrafine fibers to densify the surface. Further, calendering is also a preferable treatment because it improves the surface smoothness. The method for producing these ultrafine fibers is not particularly limited, and various ordinary techniques can be used.
【００１１】本発明で用いられるシート状熱融着接着剤
は、接着温度において熱可塑性を有するものならば特に
限定されず、ポリエステル樹脂系、ポリアミド樹脂系、
塩化ビニール樹脂系等のシート、フイルムが用いられ
る。特に、ポリエステル樹脂系は、接着の耐洗濯性に優
れているため好ましい。The sheet-shaped heat-sealing adhesive used in the present invention is not particularly limited as long as it has thermoplasticity at the bonding temperature, and polyester resin type, polyamide resin type,
Sheets and films made of vinyl chloride resin are used. In particular, a polyester resin system is preferable because it has excellent adhesion washing resistance.
【００１２】本発明で用いられるシート状熱融着接着剤
の厚みは、布帛の種類により異なるが、１０μm 以上２
００μm 以下であるのが好ましく、より好ましくは１５
μm以上１５０μm 以下であるのがよく、さらに好まし
くは２０μm 以上１００μm以下であるのがよい。１０
μm 未満では接着力が不十分であり、また２００μmを
こえると接着剤が布帛表面や端面からしみ出し易くなる
ため好ましくない。The thickness of the sheet-like heat-sealing adhesive used in the present invention varies depending on the type of cloth, but is 10 μm or more 2
It is preferably not more than 00 μm, more preferably 15
The thickness is preferably in the range of from μm to 150 μm, more preferably from 20 μm to 100 μm. 10
If the thickness is less than μm, the adhesive strength is insufficient, and if it exceeds 200 μm, the adhesive easily exudes from the surface or end face of the fabric, which is not preferable.
【００１３】本発明の粘着層で用いられる粘着剤として
は、布帛とシート状熱融着接着剤とを貼り合わすことが
できるものならば特に限定されず、ポリクロロプレン
系、ニトリルゴム系、アクリルゴム系、スチレン−ブタ
ジエン共重合ゴム系などの合成ゴム系、再生ゴム系、天
然ゴム系などのゴム系粘着剤、ポリエステル系、ポリア
ミド系、アクリル系などのレジン系、またはエマルジョ
ン系粘着剤の単体または混合物が用いられる。粘着剤の
粘着強さは、特に限定されないが、５ g／cm以上１kg/c
m 以下であるのがよく、好ましくは５ g／cm以上８００
g／cm以下、さらに好ましくは８ g／cm以上６００ g／
cm以下であるのがよい。粘着強さが５ g／cm未満では、
布帛とシート状熱融着接着剤との接着が充分でなく、１
Kg／cmをこえると粘着剤の効果が強すぎて、該布帛と衣
服等の生地との接着性が悪くなるため好ましくない。The pressure-sensitive adhesive used in the pressure-sensitive adhesive layer of the present invention is not particularly limited as long as it can bond a cloth and a sheet-shaped heat-sealing adhesive, and it is a polychloroprene-based, nitrile rubber-based or acrylic rubber. System, synthetic rubber system such as styrene-butadiene copolymer rubber system, reclaimed rubber system, rubber system adhesive system such as natural rubber system, polyester system, polyamide system, resin system such as acrylic system, or emulsion system adhesive alone or A mixture is used. The adhesive strength of the adhesive is not particularly limited, but is 5 g / cm or more and 1 kg / c
m or less, preferably 5 g / cm or more and 800
g / cm or less, more preferably 8 g / cm or more and 600 g /
It should be below cm. If the adhesive strength is less than 5 g / cm,
Insufficient adhesion between the fabric and the sheet-shaped heat-sealing adhesive
If it exceeds Kg / cm, the effect of the pressure-sensitive adhesive is too strong, and the adhesiveness between the cloth and the cloth such as clothes is deteriorated, which is not preferable.
【００１４】本発明において粘着層の厚みは、薄いほど
好ましく、具体的には０．０１μm以上３０μm 以下で
あるのが良く、さらに好ましくは０．０５μm 以上１５
μm以下であるのが良い。０．０１μm 未満では粘着が
充分でなく、また３０μm をこえると熱接着時に粘着剤
が布帛にしみ出し易くなるため好ましくない。In the present invention, the thinner the pressure-sensitive adhesive layer is, the more preferable it is. Specifically, the thickness is preferably 0.01 μm or more and 30 μm or less, and more preferably 0.05 μm or more and 15 μm or more.
It should be less than μm. If it is less than 0.01 μm, the tackiness is not sufficient, and if it exceeds 30 μm, the tackiness agent easily exudes to the cloth during heat bonding, which is not preferable.
【００１５】本発明においてシート状熱融着接着剤は、
布帛の片面に実質的にその全面を覆うように積層する。
シート状熱融着接着剤が小さすぎると、布帛が剥がれ易
く、大きすぎると布帛よりはみでた部分で汚れがついた
り、粘着したりするため好ましくない。In the present invention, the sheet-shaped heat-sealing adhesive is
The fabric is laminated on one side so as to cover substantially the entire surface.
If the sheet-shaped heat-sealing adhesive is too small, the cloth is easily peeled off, and if it is too large, it is unfavorable because stains or sticking may occur on a portion squeezed from the cloth.
【００１６】本発明における布帛積層体において、布帛
とシート状熱融着接着剤とは粘着層を介して積層され
る。従来から行われている粘着層を介さずに布帛とシー
ト状熱融着接着剤を重ねて加圧加熱して積層体を得る方
法では、シート状熱融着接着剤の布帛への浸透状態がば
らつくため、安定した接着力が得られない。In the fabric laminate of the present invention, the fabric and the sheet-shaped heat-sealing adhesive are laminated via an adhesive layer. In the conventional method of stacking a fabric and a sheet-shaped heat-sealing adhesive without applying an adhesive layer and pressurizing and heating to obtain a laminate, the state of penetration of the sheet-shaped heat-sealing adhesive into the fabric is As it varies, stable adhesive strength cannot be obtained.
【００１７】本発明においては、布帛に文字、絵または
識別マーク等の画像を形成することができる。これら
は、識別ラベル、ネームラベル、ケアラベル、ワッペン
等として用いることができる。In the present invention, images such as characters, pictures or identification marks can be formed on the cloth. These can be used as identification labels, name labels, care labels, patches, etc.
【００１８】本発明における布帛積層体は、布帛または
シート状熱融着接着剤の片面に粘着剤を塗工して両者を
積層することにより製造することができる。粘着剤は、
シート状熱融着接着剤に塗工する方が、塗液がしみこま
ないこと、腰があり塗工しやすいことなどから好まし
い。あらかじめ粘着剤を塗布した粘着剤付シート状熱融
着接着剤を用いることもできる。この場合、離型シート
が粘着面に積層されていても良い。The fabric laminate of the present invention can be produced by applying a pressure-sensitive adhesive to one side of a fabric or sheet-like heat-sealing adhesive and laminating both. The adhesive is
It is preferable to apply it to a sheet-shaped heat-sealing adhesive because the coating liquid does not soak into the adhesive and it is elastic and easy to apply. It is also possible to use a sheet-like heat-sealing adhesive with a pressure-sensitive adhesive, which has been previously coated with a pressure-sensitive adhesive. In this case, the release sheet may be laminated on the adhesive surface.
【００１９】本発明の布帛ラベルプリンターにおける画
像形成方法は、特に限定されず、通常用いられる熱転写
法、インクジェット法、ドットインパクト法が挙げられ
る。特に熱転写法は、にじみ等が少なく、鮮明な画像が
得られるため好ましい。これら画像を形成するインク
は、特に限定されず、カーボンブラック等を含有した顔
料系や染料系のものが用いられる。特に、耐洗濯、耐摩
擦等の堅牢性が必要な場合は、染料系のインクを用いる
のが好ましい。この場合に用いられる染料は、分散染
料、塩基性染料等特に限定されないが、昇華堅牢性の高
い染料を用いるのが好ましく、具体的には、昇華性であ
って昇華温度が１８０℃以上３００℃以下、好ましくは
２００℃以上２５０℃以下であるのがよい。昇華温度が
１８０℃未満では、印字画像の堅牢性が悪くなり、３０
０℃を超えると、布帛への染着が充分行われなくなるた
め好ましくない。なお、本発明でいう昇華温度とは、昇
華性染料の蒸気圧（昇華圧）が外圧に等しくなる温度を
指す。The image forming method in the cloth label printer of the present invention is not particularly limited, and examples thereof include a thermal transfer method, an ink jet method and a dot impact method which are usually used. In particular, the thermal transfer method is preferable because a clear image can be obtained with less bleeding. The ink for forming these images is not particularly limited, and pigment-based or dye-based ink containing carbon black or the like is used. In particular, dye-based ink is preferably used when fastness such as washing resistance and abrasion resistance is required. The dye used in this case is not particularly limited, such as a disperse dye and a basic dye, but it is preferable to use a dye having a high sublimation fastness. Specifically, it is sublimable and has a sublimation temperature of 180 ° C. or higher and 300 ° C. Hereafter, it is preferably 200 ° C. or higher and 250 ° C. or lower. If the sublimation temperature is less than 180 ° C, the fastness of the printed image will be poor, and
When the temperature exceeds 0 ° C, the dyeing on the fabric is not sufficiently performed, which is not preferable. The sublimation temperature in the present invention means a temperature at which the vapor pressure (sublimation pressure) of the sublimable dye becomes equal to the external pressure.
【００２０】次に本発明の布帛積層体および布帛ラベル
プリンターの例を図面で説明するが、もちろんこれらに
限定されない。Next, examples of the fabric laminate and the fabric label printer of the present invention will be explained with reference to the drawings, but of course the present invention is not limited thereto.
【００２１】図１は、本発明の布帛積層体の１例であ
る。図１において、布帛１とシート状熱融着接着剤３は
粘着層２を介して積層されている。FIG. 1 is an example of the fabric laminate of the present invention. In FIG. 1, the cloth 1 and the sheet-shaped heat-sealing adhesive 3 are laminated via an adhesive layer 2.
【００２２】図２は、本発明の布帛ラベルプリンターの
１例の側面概略図である。図２において、図１の布帛積
層体をロールにした積層布帛ロール４に印字機構５で画
像を形成し、カット機構６でカットしてラベル７とす
る。FIG. 2 is a schematic side view of an example of the fabric label printer of the present invention. In FIG. 2, an image is formed by a printing mechanism 5 on a laminated fabric roll 4 obtained by rolling the fabric laminated body of FIG. 1 and cut by a cutting mechanism 6 to obtain a label 7.
【００２３】図３は、本発明の布帛ラベルプリンターの
他の１例の側面概略図である。図３において、布帛ロー
ル８に印字機構７で画像を形成し、粘着剤付シート状熱
融着接着剤ロール９とラミネートロール１０で積層して
カット機構６でカットしてラベル７とする。FIG. 3 is a schematic side view of another example of the fabric label printer of the present invention. In FIG. 3, an image is formed on the cloth roll 8 by the printing mechanism 7, laminated by the sheet-shaped heat-sealing adhesive roll 9 with an adhesive and the laminating roll 10, and cut by the cutting mechanism 6 to obtain the label 7.
【００２４】図４は、本発明の布帛ラベルプリンターの
他の１例の側面概略図である。図４において、布帛ロー
ル８に印字機構７で画像を形成し、一方シート状熱融着
接着剤ロール１１には粘着加工機構１２で片面に粘着剤
を塗布し、両者をラミネートロール１０で積層してカッ
ト機構６でカットしてラベル７とする。FIG. 4 is a schematic side view of another example of the fabric label printer of the present invention. In FIG. 4, an image is formed on the cloth roll 8 by the printing mechanism 7, while on the sheet-shaped heat-sealing adhesive roll 11, the adhesive is applied on one side by the adhesive processing mechanism 12, and both are laminated by the laminating roll 10. The label 7 is cut by the cutting mechanism 6.
【００２５】[0025]
【実施例】以下実施例により本発明を具体的に説明する
が、本発明はこれらの実施例に限定されない。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples.
【００２６】実施例１ 布帛として０．０６デニールの極細ポリエステルフィラ
メント繊維からなる高密度織物布帛（融点２５５〜２６
０℃）を、シート状熱融着接着剤としてポリエステル系
熱融着型接着剤フイルム（融点１１４℃）をそれぞれ用
い、シート状熱融着接着剤の片面にアクリル系粘着剤を
塗布した後、常温で両者を積層し布帛積層体を得た。Example 1 As a cloth, a high density woven cloth (melting point: 255 to 26) composed of 0.06 denier ultrafine polyester filament fibers.
0 ° C.) is used as a sheet-shaped heat-sealing adhesive and a polyester-based heat-sealing adhesive film (melting point 114 ° C.) is used, and an acrylic pressure-sensitive adhesive is applied to one side of the sheet-shaped heat-sealing adhesive, Both were laminated at room temperature to obtain a fabric laminate.
【００２７】この布帛積層体ををラベルサイズに１００
枚カットし、１７０℃、１．５Kg／cm2 、１０秒の条件
で綿布にそれぞれ貼り付けたところ、１００回以上の熱
水洗濯、ドライ洗濯後でもまったく剥がれなかった。This fabric laminate is made to have a label size of 100.
The pieces were cut and attached to a cotton cloth under conditions of 170 ° C., 1.5 kg / cm 2 , and 10 seconds, respectively, and no peeling occurred even after 100 times of hot water washing and dry washing.
【００２８】比較例１ 実施例１の布帛およびシート状熱融着接着剤を１４０℃
で加熱加圧して貼り合わせて布帛積層体を得た。Comparative Example 1 The fabric of Example 1 and the sheet-like heat-sealing adhesive were mixed at 140 ° C.
Then, the mixture was heated and pressed to obtain a fabric laminate.
【００２９】得られた布帛積層体をラベルサイズに１０
０枚カットし、実施例１と同様の条件で綿布に貼り付け
たところ、１００回の熱水洗濯、ドライ洗濯後では、約
５０枚のラベルが全部または一部で剥がれた。The obtained fabric laminate was labeled with a label size of 10
When 0 sheets were cut and attached to a cotton cloth under the same conditions as in Example 1, about 50 sheets of labels were peeled off in whole or in part after 100 times of hot water washing and dry washing.
【００３０】[0030]
【発明の効果】本発明は上述のごとく構成したので、生
地と熱により簡便に接着でき、その接着についての耐洗
濯性、耐摩擦性等の優れた布帛積層体が容易に得られ、
これは識別ラベル、ネームラベル、ケアラベル、ワッペ
ン等に好適に用いることができる。EFFECTS OF THE INVENTION Since the present invention is constructed as described above, it is possible to easily bond the cloth to the cloth by heat, and it is possible to easily obtain a cloth laminate excellent in washing resistance, abrasion resistance and the like for the adhesion.
It can be suitably used for identification labels, name labels, care labels, patches, etc.
【図１】本発明の布帛積層体の１例である。FIG. 1 is an example of a fabric laminate of the present invention.
【図２】本発明の布帛ラベルプリンターの１例である。FIG. 2 is an example of a fabric label printer of the present invention.
【図３】本発明の布帛ラベルプリンターの１例である。FIG. 3 is an example of a fabric label printer of the present invention.
【図４】本発明の布帛ラベルプリンターの１例である。FIG. 4 is an example of a fabric label printer of the present invention.
１ ：布帛 ２ ：粘着層 ３ ：シート状熱融着接着剤 ４ ：積層布帛ロール ５ ：印字機構 ６ ：カット機構 ７ ：ラベル ８ ：布帛ロール ９ ：粘着剤付シート状熱融着接着剤ロール １０：ラミネートロール １１：シート状熱融着接着剤ロール １２：粘着加工機構 1: Fabric 2: Adhesive layer 3: Sheet-like heat-fusion adhesive 4: Laminated fabric roll 5: Printing mechanism 6: Cutting mechanism 7: Label 8: Fabric roll 9: Sheet-like heat-fusion adhesive roll with adhesive 10 : Laminating roll 11: Sheet-shaped heat-sealing adhesive roll 12: Adhesive processing mechanism
フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０９Ｊ 7/02 ＪＫＺ Ｂ４１Ｊ 3/407 3/36 Ｔ Ｄ０３Ｄ 1/00 Ｅ 7199−3Ｂ Ｇ０９Ｆ 3/00 Ｇ 7429−5Ｇ 3/02 Ｈ 7429−5Ｇ Continuation of the front page (51) Int.Cl. 6 Identification number Office reference number FI technical display location C09J 7/02 JKZ B41J 3/407 3/36 T D03D 1/00 E 7199-3B G09F 3/00 G 7429- 5G 3/02 H 7429-5G
Claims (9)
ート状熱融着接着剤を粘着層を介して積層したことを特
徴とする布帛積層体。1. A fabric laminate, wherein a sheet-shaped heat-sealing adhesive is laminated on one side of a fabric so as to cover the entire surface thereof via an adhesive layer.
度０．００１デニール以上１デニール以下の超極細繊維
からなることを特徴とする請求項１記載の布帛積層体。2. The fabric laminate according to claim 1, wherein the fibers constituting the fabric are mainly composed of ultrafine fibers having a monofilament degree of 0.001 denier or more and 1 denier or less.
像を形成せしめたことを特徴とする請求項１または２記
載の布帛積層体。3. The fabric laminate according to claim 1, wherein the fabric is formed with an image such as a character, a picture or an identification mark.
に粘着剤を塗工して両者を積層することを特徴とする布
帛積層体の製造方法。4. A method for producing a fabric laminate, which comprises applying a pressure-sensitive adhesive to one surface of a fabric or sheet-shaped heat-sealing adhesive to laminate the both.
着接着剤ロールとを有し、熱転写法またはインクジェッ
ト法またはドットインパクト法で画像を布帛上に形成す
る工程と、布帛または熱融着接着剤フイルムの片面に粘
着剤を塗工する工程と、布帛と熱融着接着剤フイルムと
を粘着剤を介して積層する工程とを有することを特徴と
する布帛ラベルプリンター。5. A step of forming an image on a cloth by a thermal transfer method, an ink jet method or a dot impact method, which has at least a cloth roll and a sheet-shaped heat-sealing adhesive roll, and the cloth or the heat-sealing adhesive. A fabric label printer comprising: a step of applying an adhesive on one surface of the film; and a step of laminating a fabric and a heat-fusion adhesive film via the adhesive.
着接着剤ロールとを有し、かつその内の少なくとも一方
の片面には粘着層を有しており、熱転写法またはインク
ジェット法またはドットインパクト法で画像を布帛上に
形成する工程と、布帛とシート状熱融着接着剤とを粘着
剤を介して積層する工程とを有することを特徴とする布
帛ラベルプリンター。6. A thermal transfer method, an inkjet method, or a dot impact method, which has at least a fabric roll and a sheet-shaped heat-sealing adhesive roll, and has an adhesive layer on at least one side thereof. And a step of laminating the cloth and the sheet-shaped heat-sealing adhesive via an adhesive, the cloth label printer.
剤とを粘着層を介して積層した積層布帛ロールを有し、
その布帛面に、熱転写法またはインクジェット法または
ドットインパクト法で画像を布帛上に形成することを特
徴とする布帛ラベルプリンター。7. A laminated fabric roll having at least a fabric and a sheet-shaped heat-sealing adhesive laminated via an adhesive layer,
A cloth label printer, characterized in that an image is formed on the cloth surface by a thermal transfer method, an inkjet method or a dot impact method.
する請求項５、６または７記載の布帛ラベルプリンタ
ー。8. The fabric label printer according to claim 5, 6 or 7, wherein an image is formed with a dye.
徴とする請求項５、６、７または８記載の布帛ラベルプ
リンター。9. The fabric label printer according to claim 5, wherein the image is formed by a thermal transfer method.