JPH07118097B2 - Optical recording medium - Google Patents
Optical recording mediumInfo
- Publication number
- JPH07118097B2 JPH07118097B2 JP62178949A JP17894987A JPH07118097B2 JP H07118097 B2 JPH07118097 B2 JP H07118097B2 JP 62178949 A JP62178949 A JP 62178949A JP 17894987 A JP17894987 A JP 17894987A JP H07118097 B2 JPH07118097 B2 JP H07118097B2
- Authority
- JP
- Japan
- Prior art keywords
- optical recording
- recording medium
- adhesive
- melt adhesive
- plastomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は光ビームにより記録、再生が行なえる光記録媒
体に関し、とくに光ディスクおよび光カードなどに用い
られる改善された光記録媒体に関する。Description: TECHNICAL FIELD The present invention relates to an optical recording medium capable of recording and reproducing by a light beam, and more particularly to an improved optical recording medium used for optical disks and optical cards.
従来より、ガラス、アクリル樹脂、ポリカーボネート、
エポキシ樹脂等の基板に対し、磁気光学効果やフォトク
ロミズム、あるいはアモルファスと結晶間の相転移等を
利用して光記録層を設けた２枚の記録媒体、または記録
媒体と保護基板とを記録層を包み込むような形で貼り合
わせた構造の光記録媒体が提案されている。Conventionally, glass, acrylic resin, polycarbonate,
Two recording media provided with an optical recording layer, such as a magneto-optical effect, photochromism, or phase transition between amorphous and crystalline, or a recording medium and a protective substrate are used as a recording layer for an epoxy resin substrate. There has been proposed an optical recording medium having a structure in which the optical recording medium and the optical recording medium are bonded together in a wrapped manner.
この記録媒体の接着には、通常、米国特許明細書第4503
531号に記載されているようなホットメルト接着剤が使
われていた。Adhesion of this recording medium is usually carried out according to US Pat.
Hot melt adhesives such as those described in 531 were used.
このタイプの接着剤は、他の物に比べ接着作業が簡単で
溶剤型接着剤のように記録媒体を侵すこともないため、
光記録媒体の接着剤としては非常に優れている。This type of adhesive is easier to bond than other objects and does not attack the recording medium like solvent-based adhesives.
It is a very good adhesive for optical recording media.
しかしながら、このタイプの接着剤は熱可塑性エラスト
マーとタッキファイヤーとの組合せか、あるいはこれに
軟化剤を加えた構成からなり、接着剤と言うよりはむし
ろホットメルト粘着剤に属し、一応何にでも良く粘着す
るが凝集力が小さく、クリープし易く、耐熱性の面から
も充分とは言えなかった。However, this type of adhesive consists of a combination of a thermoplastic elastomer and a tackifier, or a composition in which a softening agent is added to it, and it belongs to a hot-melt pressure-sensitive adhesive rather than an adhesive. Although it was tacky, the cohesive force was small, it easily creeped, and it was not sufficient in terms of heat resistance.
特に最近では光記録媒体に磁気ディスク並の高速性をも
たせたいという要求が高まり、高速回転に耐える光記録
媒体を開発することが必要になってきた。また動作時の
環境温度も55℃程度を保障することが必要となってき
た。In particular, recently, there has been an increasing demand for optical recording media to have high-speed performance comparable to that of magnetic disks, and it has become necessary to develop optical recording media that can withstand high-speed rotation. In addition, it has become necessary to ensure that the operating environment temperature is about 55 ° C.
しかし、高温中でディスクを高速回転すると、ディスク
を接着している前記ホットメルト接着剤が軟化し、クリ
ープし易くなり、接着剤がディスクの端面から食み出し
たり、剥離したりするという問題が発生していた。However, when the disk is rotated at a high speed in a high temperature, the hot melt adhesive that adheres the disk is softened and easily creeps, and there is a problem that the adhesive oozes out from the end surface of the disk or peels off. Had occurred.
本発明の目的は、凝集力が高く、耐熱クリープ特性のす
ぐれたホットメルト接着剤を使用することにより、信頼
性の高い光記録媒体を提供することにある。An object of the present invention is to provide an optical recording medium having high reliability by using a hot melt adhesive having high cohesive force and excellent heat-resistant creep characteristics.
本発明の光記録媒体は、少なくとも一方の基板に光記録
層を形成した一対の基板を、ブロック状熱可塑性エラス
トマー、熱可塑性プラストマーおよびタッキファイヤー
をベースとするホットメルト接着剤により貼り合せてな
ることを特徴とする。The optical recording medium of the present invention comprises a pair of substrates each having an optical recording layer formed on at least one substrate, which are bonded together by a hot melt adhesive based on a block-shaped thermoplastic elastomer, a thermoplastic plastomer and a tackifier. Is characterized by.
以下、本発明をさらに詳しく説明すると、本発明に使用
するホットメルト接着剤は、ブロック状熱可塑性エラス
トマー、タッキファイヤー、必要に応じて添加される軟
化剤等の添加物からなる従来公知の組成（前出米国特許
明細書）に対し熱可塑性プラストマーを加えた点が改良
点である。Hereinafter, the present invention will be described in more detail. The hot-melt adhesive used in the present invention is a conventionally known composition comprising additives such as a block-shaped thermoplastic elastomer, a tackifier, and a softening agent added as necessary. The improvement is that a thermoplastic plastomer is added to the above-mentioned US patent specification).
まず、ブロック状熱可塑性エラストマーとしては、構造
式Ａ−Ｂ−ＡまたはＢ−Ａ−Ｂ（ただしＡは分子量2000
〜12500のポリエチレンポリマーブロック、Ｂは分子量1
000〜250000のポリブタジエン、ポリイソプレンまたは
エチレン−ブチレン共重合体ブロックを示す）で表わさ
れるエラストマーで、それぞれ単独でも混合物として用
いてもよい。さらに、ポリイソプレン、スチレンゴム、
ブタジエンゴム、ブチルゴム等の合成ゴム、ポリエチレ
ン、ポリプロピレン等のオレフィン系樹脂、エチレン−
酢酸ビニル共重合体等のオレフィン系共重合体などと混
合して用いることもできる。First, as the block-shaped thermoplastic elastomer, a structural formula A-B-A or B-A-B (where A is a molecular weight of 2000
~ 12500 polyethylene polymer block, B has molecular weight 1
000 to 250,000 polybutadiene, polyisoprene or ethylene-butylene copolymer block), which may be used alone or as a mixture. In addition, polyisoprene, styrene rubber,
Synthetic rubber such as butadiene rubber and butyl rubber, olefin resin such as polyethylene and polypropylene, ethylene-
It can also be used as a mixture with an olefin-based copolymer such as a vinyl acetate copolymer.
また、タッキファイヤーとしては、ロジン（高分子化ロ
ジン、水素化ロジン、ロジンエステル等の変成ロジンも
含む）や石油樹脂、テルペン、フェノール樹脂、クマロ
ン樹脂などを挙げることができる。Examples of tackifiers include rosin (including modified rosin such as polymerized rosin, hydrogenated rosin, and rosin ester), petroleum resin, terpene, phenol resin, coumarone resin, and the like.
次に必要に応じて使用される軟化剤としては、プロセス
オイル、パラフィン、カスターオイル、ポリブテン、ポ
リイソプレンなどが挙げられる。Next, as a softening agent used as needed, process oil, paraffin, castor oil, polybutene, polyisoprene and the like can be mentioned.
さらに軟化剤以外の添加剤としては、CaCO3，BaSO4，Ti
O2，タルク，クレー等の充填剤、DOP,DBP,BBP等の可塑
剤、ヒンダード、フエトル等の酸化防止剤がある。Furthermore, as additives other than the softening agent, CaCO 3 , BaSO 4 , Ti
There are fillers such as O 2 , talc and clay, plasticizers such as DOP, DBP and BBP, and antioxidants such as hindered and petroleum.
最後に、本発明のみそである熱可塑性エラストマーとし
ては、ポリエステルが好ましいが、これ以外にもポリプ
ロピレン、ポリアミド、ポリメチルメタクリレートなど
を挙げることができる。Lastly, as the thermoplastic elastomer of the present invention, polyester is preferable, but polypropylene, polyamide, polymethylmethacrylate, etc. may be mentioned as well.
本発明のホットメルト接着剤の配合割合については、一
般にブロック状熱可塑性エラストマ100部（重合基準、
以下同じ）に対しタッキファイヤー50〜600部、軟化剤
０〜100部、そして熱可塑性プラストマーを５〜200部と
するのが好ましい。Regarding the blending ratio of the hot melt adhesive of the present invention, generally 100 parts of a block thermoplastic elastomer (polymerization standard,
The same shall apply hereinafter), preferably 50 to 600 parts of tackifier, 0 to 100 parts of softener, and 5 to 200 parts of thermoplastic plastomer.
この熱可塑性プラストマーの配合量が５部未満である
と、ホットメルト接着剤の耐熱可塑性向上に効果がな
く、また200部を越えると、オープンタイムが短くなっ
て作業しずらいという問題が生じる。If the blending amount of this thermoplastic plastomer is less than 5 parts, there is no effect in improving the heat resistance of the hot melt adhesive, and if it exceeds 200 parts, the open time becomes short and the work becomes difficult.
次に、本発明に使用するホットメルト接着剤の軟化点は
100℃以上であることが好ましい。この軟化点を100℃以
上とするのは、ディスク動作中における上限温度を55℃
までと保障した場合、ディスクを連続動作させたときに
これ未満の軟化点をもつ接着剤では、ディスク端面から
食み出したり剥離が発生するためである。Next, the softening point of the hot melt adhesive used in the present invention is
It is preferably 100 ° C. or higher. This softening point is 100 ℃ or higher because the maximum temperature during disk operation is 55 ℃.
This is because, if the above is assured, an adhesive having a softening point lower than this when operating the disk continuously will stick out or peel off from the end surface of the disk.
本発明に用いるホットメルト接着剤は耐熱性が確実に向
上するが、その理由は、ブロック状熱可塑性エラストマ
ーに比べ熱可塑性プラストマーが明確な軟化点をもって
いるため、該プラストマーを添加した方が軟化点以下の
温度では粘度が急激に上昇し、その結果、光記録媒体の
使用温度範囲（〜55℃）内ではクリープや凝集剥離が生
じにくくなるからだと考えられる。The heat resistance of the hot-melt adhesive used in the present invention is definitely improved, because the thermoplastic plastomer has a clear softening point as compared with the block-like thermoplastic elastomer, and therefore the addition of the plastomer has a softening point. It is considered that the viscosity sharply increases at the following temperatures, and as a result, creep and cohesive peeling are less likely to occur within the operating temperature range (up to 55 ° C) of the optical recording medium.
つぎに実施例に基づいて本発明をさらに具体的に説明す
る。Next, the present invention will be described more specifically based on examples.
実施例１ 第１図に示す貼り合せ構造の光磁気記録媒体を次のよう
にして作製した。Example 1 A magneto-optical recording medium having a laminated structure shown in FIG. 1 was produced as follows.
外周130mmφ、内周15mmφのドーナツ状ポリカーボネー
ト基板1,1′上にスパッタリングによりSiC層（下引層）
2,2′、GdTbTeCo層（記録層）3,3′、SiC層（保護層）
4,4′を積層した構造体２枚を、表１に示すホットメル
ト接着剤層５を介して貼り合せ、55℃の恒温槽内で回転
耐久試験（毎分1800回転、1000時間）を行い、接着剤槽
５の変化を調べた。SiC layer (undercoat layer) by sputtering on donut-shaped polycarbonate substrate 1, 1'with 130 mmφ outer circumference and 15 mmφ inner circumference
2,2 ', GdTbTeCo layer (recording layer) 3,3', SiC layer (protective layer)
Two structures with 4,4 'laminated are pasted together via the hot melt adhesive layer 5 shown in Table 1, and a rotation endurance test (1800 rpm, 1000 hours) is performed in a thermostatic chamber at 55 ° C. The change of the adhesive agent tank 5 was investigated.
表１の結果から、軟化点が同じ接着剤で比較すると、ベ
ースポリマーがエラストマー単独のものよりポリエステ
ルのようなプラストマーを添加した接着剤の方が、耐熱
性が向上していることが分る。 From the results shown in Table 1, when comparing adhesives having the same softening point, it can be seen that the adhesive having a plastomer such as polyester improved in heat resistance, as compared with an adhesive having a base polymer alone.
また、ディスクの保障温度55℃での比較では、プラスト
マーを加えた接着剤は軟化点が100℃以上であれば接着
剤層に変化がみられないことから、ディスク用接着剤と
して信頼性が高いものと言える。In addition, in comparison with the guarantee temperature of the disc of 55 ° C, the adhesive with plastomer does not show any change in the adhesive layer if the softening point is 100 ° C or higher, so it is highly reliable as a disc adhesive. Can be said to be a thing.
以上で明らかなごとく、本発明の光記録媒体は基板を貼
り合せる接着剤として熱可塑性プラストマーを加えた組
成のホットメルト接着剤が使用されるため、耐熱性が改
善され、高温中で使用しても接着剤のクリープが防止さ
れ、ディスク等の端面からの食み出しや剥離等の現象も
効果的に防止され、安価で且つ高い信頼性をはくするこ
とができる。As is clear from the above, since the optical recording medium of the present invention uses a hot melt adhesive having a composition containing a thermoplastic plastomer as an adhesive for bonding substrates, the heat resistance is improved and Also, the creep of the adhesive is prevented, and the phenomenon such as leaching or peeling from the end surface of the disk or the like is effectively prevented, and the cost is low and the reliability is high.
第１図は本発明の一実施例である光記録媒体の構造を模
式的に示した側断面図である。 1,1′…ポリカーボネート基板、2,2′…下引き層、3,
3′…記録層、4,4′…保護層、５…ホットメルト接着剤
層。FIG. 1 is a side sectional view schematically showing the structure of an optical recording medium which is an embodiment of the present invention. 1, 1 '... Polycarbonate substrate, 2, 2' ... Undercoat layer, 3,
3 '... recording layer, 4, 4' ... protective layer, 5 ... hot melt adhesive layer.
Claims (3)
た一対の基板を、ブロック状熱可塑性エラストマー、熱
可塑性プラストマーおよびタッキファイヤーをベースと
するホットメルト接着剤により貼り合せてなることを特
徴とする光記録媒体。1. A pair of substrates each having an optical recording layer formed on at least one of the substrates are bonded by a hot-melt adhesive based on a block-shaped thermoplastic elastomer, a thermoplastic plastomer and a tackifier. Optical recording medium.
以上である特許請求の範囲第（１）項記載の光記録媒
体。2. The softening point of the hot melt adhesive is 100.degree.
The optical recording medium according to claim 1 above.
系の樹脂である特許請求の範囲第（１）項記載の光記録
媒体。3. The optical recording medium according to claim 1, wherein the thermoplastic plastomer is a polyester resin.